US20090165700A1 - Inner crystallization crucible and pulling method using the crucible - Google Patents

Inner crystallization crucible and pulling method using the crucible Download PDF

Info

Publication number
US20090165700A1
US20090165700A1 US12/324,978 US32497808A US2009165700A1 US 20090165700 A1 US20090165700 A1 US 20090165700A1 US 32497808 A US32497808 A US 32497808A US 2009165700 A1 US2009165700 A1 US 2009165700A1
Authority
US
United States
Prior art keywords
crucible
glass layer
vitreous silica
pulling
equal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/324,978
Other languages
English (en)
Inventor
Hiroshi Kishi
Minoru Kanda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Japan Super Quartz Corp
Original Assignee
Japan Super Quartz Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Japan Super Quartz Corp filed Critical Japan Super Quartz Corp
Assigned to JAPAN SUPER QUARTZ CORPORATION reassignment JAPAN SUPER QUARTZ CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KANDA, MINORU, KISHI, HIROSHI
Publication of US20090165700A1 publication Critical patent/US20090165700A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B15/00—Single-crystal growth by pulling from a melt, e.g. Czochralski method
    • C30B15/10—Crucibles or containers for supporting the melt
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/02—Elements
    • C30B29/06—Silicon
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T117/00—Single-crystal, oriented-crystal, and epitaxy growth processes; non-coating apparatus therefor
    • Y10T117/10—Apparatus
    • Y10T117/1024—Apparatus for crystallization from liquid or supercritical state
    • Y10T117/1032—Seed pulling

Definitions

  • the present invention relates to a vitreous silica crucible used for pulling single-crystal silicon, and in particular, to a vitreous silica crucible providing a high yield of single-crystal silicon, which has a high density of the generated brown rings in the inner surface of the crucible upon pulling, and a high strength of the crucible, and hardly causes peeling of brown rings, and to a pulling method using the crucible.
  • Single-crystal silicon used as a semiconductor material is usually manufactured by a single crystallization method (Czochralski (CZ) method) by pulling up a single crystal silicon ingot from a molten silicon contained in a vitreous silica crucible.
  • the vitreous silica crucible including the silicon melt is brought into contact with a silicon melt at a temperature higher than a silicon melting point, and accordingly, the inner surface of the crucible is reacted with a silicon melt to generate uncounted numbers of crystal nuclei on the glass surface. A number of the generated crystal nuclei are degenerated according to the dissolution rate of the glass.
  • the remaining crystal nuclei grow on the surface of the glass and in a direction perpendicular to the surface to develop crystallized spots in the form of a ring as the pulling proceeds.
  • the peripheries of these spots are brown in color, and thus are called brown rings.
  • the inner part of the brown ring is a layer having no cristobalite layer or having a very thin cristobalite layer, if any.
  • the area of the brown ring expands. Further, the adjacent brown rings are fused to each other to maintain their growth. Also, the portion encircled by the brown ring is eroded causing an irregular elution surface to appear on the glass. If this elution surface appears on the glass, dislocation easily occurs on a single-crystal silicon, thereby interfering with the yield of the single crystal pulling.
  • JP-A No. 11-228291 describes a vitreous silica crucible in which by uniformly distributing the impurities which become the production nuclei of crystallized spots, at a lower concentration, the density of the crystallized spots produced in the inner surface of the crucible is controlled to 5 spots/cm 2 or less.
  • the brown ring on the inner surface of the crucible is related to vibration of the melt surface of the silicon melt. It has been pointed out that a small number of the brown rings make the vibration of the melt surface of the silicon melt easier. This vibration can be often found at an initial pulling step in the former part of the single crystal body upon formation of a shoulder by seeding. As a result, in some cases, a seeding operation required a certain period of time, or crystals were dislocated, and then became molten again causing so-called melt-back, or lowering the productivity. In order to solve this problem, JP-A No. 2005-320241 proposes a vitreous silica crucible, in which many brown rings are generated on an inner surface part that is underneath the initial melt surface position at a certain distance.
  • the present invention has been made to solve the above-described problems in conventional vitreous silica crucibles, and is intended to control the concentration of OH groups on a thin surface layer of the inner layer of the crucible, and thus to lower a dissolution rate of the vitreous silica of the thin surface layer, whereby the crystal nuclei of the brown ring readily remain. Also, concurrently, the concentration of OH groups in the underlying layer of the thin surface layer is controlled so as to allow easy growth of the crystal nuclei.
  • the present invention provides a vitreous silica crucible inhibiting the peeling of the brown ring.
  • the invention relates to a vitreous silica crucible which has solved the above-mentioned problems by employing the following constitutions, and to a pulling method using the vitreous silica crucible.
  • a vitreous silica crucible for pulling single-crystal silicon wherein the concentration of OH groups in the surface glass layer with a thickness of 100 ⁇ m from the inner surface of the crucible is 90 ppm or less, and the concentration of OH groups in the glass layer with a thickness of 1 mm from the inner surface of the crucible which is a portion at the lower side of the above layer is equal to or more than 90 ppm and equal to or less than 200 ppm.
  • the concentration of OH groups in the surface glass layer with a thickness of 100 ⁇ m from the inner surface of the crucible is 90 ppm or less in the vitreous silica crucible of the present invention, the dissolution rate of the surface glass layer is low. For this reason, the generated crystal nuclei grow into brown rings, thereby improving the strength of the crucible.
  • the density of the generated brown rings is 2 rings/cm 2 or more, and preferably 5 rings/cm 2 or more, under a common pulling condition. As such, since the generation density of the brown rings is high, the strength of the crucible is enhanced.
  • the concentration of OH groups in the glass layer of the underlying surface glass layer is equal to or more than 90 ppm and equal to or less than 200 ppm and crystallization easily occurs, the grown brown ring is difficult to be peeled off.
  • the peeling rate of the brown ring (a percentage of the peeled area/the inner area of the brown ring) under a common pulling condition is preferably 10% or less, and for this reason, the brown ring is difficult to be peeled off. Accordingly, the yield of the single-crystal silicon is enhanced.
  • the bubble content of the glass layer with a thickness of 1 mm from the inner surface of the crucible is preferably 0.1% or less in the vitreous silica crucible of the present invention, the number of the expanded bubbles is greatly reduced, and for this reason, the brown ring is more difficult to be peeled off.
  • FIG. 1 is a vertical cross-sectional view illustrating an embodiment of the vitreous silica crucible for pulling single-crystal silicon according to the present invention.
  • FIG. 2 is a horizontal cross-sectional view illustrating a vitreous silica crucible manufacturing device.
  • FIG. 3 is a vertical cross-sectional view illustrating a single-crystal silicon pulling step.
  • FIG. 4 is a flow chart illustrating a single-crystal silicon pulling step.
  • FIG. 1 is a cross-sectional view illustrating a first embodiment of the vitreous silica crucible for pulling single-crystal silicon according to the present invention.
  • a vitreous silica crucible C has a surface glass layer with a thickness of 100 ⁇ m from the inner surface of the crucible (hereinafter referred to as a first surface glass layer C 1 ), and a glass layer with a thickness of 1 mm from the inner surface of the crucible (hereinafter referred to as a second surface glass layer C 2 , or the underlying glass layer) which is a portion at the lower side of the above layer.
  • the first surface glass layer C 1 is a glass layer with a thickness of 100 ⁇ m from the inner surface of the crucible, and has a concentration of OH groups of 90 ppm or less.
  • the second surface glass layer C 2 is a glass layer with a thickness of 1 mm from the inner surface of the crucible that is at the lower side of the first surface glass layer C 1 , and has a concentration of OH groups of equal to or more than 90 ppm and equal to or less than 200 ppm.
  • the vitreous silica crucible is formed by melting vitreous silica powder (raw powder) in a crucible shape for vitrification.
  • vitreous silica powder as a raw material contains a trace amount of OH groups together with SiO 2 as a main component
  • the glass layer of the crucible contains more or less OH groups. If this concentration of OH groups is high, the viscosity of the glass is lowered, and OH groups are incorporated into the chains of the glass structure. Accordingly, the glass structure is easily cleaved, making the crystallization easier.
  • the concentration of OH groups in the glass layer is low, the viscosity of the glass is maintained, whereby the glass is hardly dissolved.
  • the present invention employs these two properties.
  • silanol produced by alkoxide hydrolysis remains usually in an amount of 50 ppm to a few hundred ppm.
  • the silanol-containing synthetic fused silica powder is used to prepare a surface glass layer of the vitreous silica crucible.
  • the vitreous silica crucible C used for pulling single-crystal silicon undergoes melting-damage by the reaction of the silicon melt with the crucible inner layer to be in contact therewith.
  • the amount of oxygen which generates from the inner wall of the crucible, dissolves into the molten silicon as a solid solution, and diffuses into the atmospheric gas from the molten silicon is increased in accordance with the following formula:
  • the concentration of OH groups in the first surface glass layer C 1 with a thickness of 100 ⁇ m from the inner surface of the crucible is 90 ppm or less. Accordingly, the dissolution rate of the first surface glass layer C 1 is low, and the generated crystal nuclei in the surface glass layer are hardly lost until the generated crystal nuclei sufficiently grow in a direction perpendicular to the surface. Thus, the density of the generated brown rings in the inner surface of the crucible upon pulling the single-crystal silicon is increased.
  • a second surface glass layer C 2 with a thickness of 1 mm from the inner surface of the crucible which is hereinafter referred to as a underlying glass layer
  • a concentration of OH groups of equal to or more than 90 ppm and equal to or less than 200 ppm.
  • the second surface glass layer C 2 has a higher concentration of OH groups than the first surface glass layer C 1 . Therefore, this underlying glass layer (a second surface glass layer C 2 ) is more easily crystallized than the first surface glass layer C 1 .
  • the grown crystal nuclei are not dissolved, and are increased in size to form a brown ring, and accordingly, the area of the brown ring in the inner surface of the crucible is increased, thereby improving the strength of the crucible. Also, since the brown ring is hardly dissolved and peeled, the yield of the single-crystal silicon is enhanced.
  • the first surface glass layer C 1 has a concentration of OH groups of 90 ppm or less. More preferably it is equal to or more than 30 ppm and equal to or less than 80 ppm, and particularly preferably equal to or more than 40 and equal to or less 70 ppm. If the first surface glass layer C 1 has a concentration of OH groups of more than 90 ppm, the fusion rate of the first surface glass layer C 1 is high, and it is possible that the generated crystal nuclei are lost by melting before they grow. On the other hand, if the concentration of OH groups is less than 1 ppm, there is a possibility that the density of brown rings per unit area will decrease. The reason of this can be presumed as follows.
  • the second surface glass layer C 2 has a concentration of OH groups of equal to or more than 90 ppm and equal to or less than 200 ppm, more preferably equal to or more than 95 ppm and equal to or less 170 ppm, and particularly preferably equal to or more than 100 ppm and equal to or less 150 ppm or less. If the second surface glass layer C 2 has a concentration of OH groups of less than 90 ppm, a preferable crystallization rate of the second surface glass layer C 2 cannot be obtained.
  • the second surface glass layer C 2 has a concentration of OH groups of more than 200 ppm, there is a possibility that the crucible deforms due to a decrease of the viscosity (hardness) of the vitreous silica supporting brown rings.
  • an infrared spectrophotometry (FT-IR) method can be used as for the method for measuring the concentration of OH groups.
  • the concentration of OH groups can be measured by obtaining an absorption spectrum at a wave length of 3672 nm absorbed by OH groups using a conventional FT-IR apparatus.
  • the first surface glass layer C 1 is a glass layer with a thickness of 100 ⁇ m from the inner surface of the crucible.
  • the second the surface glass layer C 2 is a glass layer with a thickness of 1 mm from the inner surface of the crucible that is a portion at the lower side of the first surface glass layer C 1 .
  • any thickness of the first surface glass layer C 1 and the second surface glass layer C 2 at an equivalent ratio to the above thickness can be used, other thicknesses may be applied.
  • the thicknesses of the surface glass layer C 1 and the second surface glass layer C 2 are uniformly distributed across the vitreous silica crucible.
  • a thick constitution may be applied around the lower portion of the vitreous silica crucible since it has a long contact time with the silicon melt.
  • the brown ring moving in a thickness direction perpendicular to the inner surface of the crucible has an apparent growth rate of 1 ⁇ m/hr or more.
  • the density of the generated brown rings is 2 rings/cm 2 or more, and preferably 5 rings/cm 2 or more.
  • a conventional common vitreous silica crucible has a brown ring density of about 1 ring/cm 2 . That is, the density of the brown ring in the vitreous silica crucible having a preferable shape according to the present invention is significantly higher, and thus it has an effect of improving the strength of the crucible.
  • the density of the brown ring preferably has an upper limit of 10 rings/cm 2 or less.
  • the brown ring moving in a thickness direction perpendicular to the inner surface of the crucible has an apparent growth rate of 1 ⁇ m/hr or more under the above-described common pulling conditions.
  • the apparent growth rate of the brown ring is defined by equation (2).
  • the growth rate of the brown ring and the dissolution rate of the brown ring can be determined by microscopy of the inner surface of the crucible at each step of the pulling, or by other methods.
  • the brown ring more preferably has an apparent growth rate of 2 ⁇ m/hr or more, and particularly preferably 4 ⁇ m/hr or more.
  • the upper limit of the apparent growth rate of the brown ring is preferably 20 ⁇ m/hr in terms of the preparation of single-crystal silicon.
  • the brown ring Since the apparent growth rate of the brown ring is 1 ⁇ m/hr or more in the vitreous silica crucible of the present invention, as described above, the brown ring is difficult to be peeled off. Accordingly, the peeling rate of the brown ring (a percentage of the peeled area/the inner area of the brown ring) is 10% or less under the above-described common pulling conditions. As the peeling rate lowers, the yield of the single-crystal silicon is further enhanced.
  • the bubble content in the glass layer with a thickness of 1 mm from the inner surface of the crucible is preferably 0.1% or less.
  • the vitreous silica crucible undergoes melting-damage in the glass layer with a thickness of 1 mm from the inner surface of the crucible, by its reaction with the silicon melt upon pulling single-crystal silicon. With a high amount of the bubbles contained in this part, the brown ring around the bubbles is easily peeled off owing to expansion of the bubbles.
  • the bubble content in this portion is low, and the number of the expanded bubbles is inhibited, and thus the brown ring is more difficult to be peeled off.
  • % in the bubble content represents % by volume.
  • Examples of the raw powder include synthetic fused silica powder and natural quartz powder.
  • the synthetic fused silica powder refers to powder consisting of synthetic fused silica
  • the synthetic fused silica refers to a chemically synthesized or prepared raw material, in which the synthetic fused silica powder is amorphous. Since the synthetic fused silica raw material is gas or liquid, it can be easily purified, and the synthetic fused silica powder can have a higher purity than the natural quartz powder. Examples of the synthetic fused silica raw materials include those derived from gas raw materials such as carbon tetrachloride and those derived from liquid raw materials such as silicon alkoxide. In the synthetic fused silica powder, it is possible that all the impurities are at 0.1 ppm or less.
  • the first surface glass layer C 1 and the second surface glass layer C 2 can be made of those containing a trace amount of OH groups together with SiO 2 as a main component among the synthetic fused silica powder.
  • the synthetic fused silica powder those obtained by a sol-gel method, and containing silanol produced by alkoxide hydrolysis usually in an amount of 50 ppm to 100 ppm, are preferable.
  • the residual amount of silanol can be controlled over a wide range of equal to or more than 0 ppm and equal to or less than 1000 ppm, but usually chlorine is contained in an amount of about 100 ppm or more. If alkoxides are used as a raw material, synthetic fused silica containing no chlorine can be easily prepared.
  • the “vitreous silica powder” can include, as long as it satisfies the above conditions, crystal, silica sand, and the like, including silicon dioxide (silica), not limited to vitreous silica, as well as powder of well-known materials as raw materials for a vitreous silica crucible.
  • silicon dioxide silicon dioxide
  • a synthetic fused silica having a low content of the silanol groups be used in the first surface glass layer C 1 .
  • a synthetic fused silica having a higher concentration of OH groups in the second surface glass layer C 2 as compared in the first surface glass layer C 1 be used in the second surface glass layer C 2 .
  • a synthetic fused silica having a content of silanol groups of equal to or more than 10 ppm and equal to or less than 120 ppm be used in the first surface glass layer C 1 .
  • a synthetic fused silica having a content of silanol groups of equal to or more than 80 ppm and equal to or less than 300 ppm or less be used in the second surface glass layer C 2 .
  • the synthetic fused silica to be used is not limited to those described above.
  • the concentrations of OH groups in the first surface glass layer C 1 and the second surface glass layer C 2 may be adjusted by varying the temperature gradient toward the outside upon heating. More silanol is removed by further heating the synthetic fused silica powder, thereby lowering the concentration of OH groups.
  • a crucible manufacturing device 1 having a rotary mold 10 for performing vacuum pulling is used, as shown in FIG. 2
  • the vitreous silica crucible manufacturing device 1 is roughly constituted of a mold 10 which has a melting space in the inner part for melting a vitreous silica powder and forming a vitreous silica crucible; a driving mechanism which rotates the mold 10 around the axis; and a plurality of carbon electrodes 13 which acts as an arc discharge means for heating the inner side of the mold 10 .
  • the mold 10 is formed of, for example, carbon, and a number of pressure-reducing passages 12 which are open to the surface of the inner part of the mold 10 are formed inside.
  • the pressure-reducing passage 12 is connected to a pressure-reducing mechanism, which thus allows suction of air from the inner surface of the mold 10 via the pressure-reducing passage 12 at the time of rotating the mold 10 .
  • the atmospheric pressure around the mold 10 can be subjected to depressurization or pressurization by an atmospheric pressure control device (not shown).
  • a plurality of electrodes 13 is provided as the arc discharge means at the upper side of the mold 10 in the vitreous silica crucible manufacturing device 1 .
  • the electrode 13 is formed of a combination of three electrodes.
  • the electrodes 13 are each fixed to a support 20 at the upper part of a furnace, and the support 20 is provided with a means (omitted in the figure) to vertically move the carbon electrode 13 .
  • the support 20 is provided with a supporting part 21 that supports the carbon electrode 13 while allowing setting of the distance D between the electrodes, a horizontally transferring means that allows the supporting part 21 to move in a horizontal direction T 2 , and a vertically transferring means that allows the plurality of supporting parts 21 and the respective horizontally transferring means to move integrally in a vertical direction T.
  • the supporting part 21 supports by allowing the carbon electrode 13 to move around an angle setting axis 22 , and is provided with a rotation means that controls the rotation angle of the angle setting axis 22 .
  • the angle direction T 3 of the carbon electrode 13 is controlled by the rotation means, as well as the horizontal position of the supporting part 21 being controlled by the horizontally transferring means and the height of the supporting part 21 also being controlled by the vertical transferring means.
  • the supporting part 21 and the like are shown at only the left end of the carbon electrode 13 in the figure, but other electrodes are also supported by the same constitution, and the height of each carbon electrode 13 can be controlled individually.
  • an arc electrode 13 provided on the upper side of the mold space is used to melt the vitreous silica powder by heating to achieve vitrification, vacuum pulling is performed upon melting by a depressurization mechanism via a pressure-reducing passage 12 , and the bubbles of the inner layer are sucked to form a transparent glass layer. After vitrification, it is cooled, and then taken out of the mold to obtain a vitreous silica crucible C.
  • the vitreous silica powder used in the second surface glass layer C 2 be laminated to approximately equal to or more than 0.5 mm and equal to or less than 5 mm. Also, it is preferable that the vitreous silica powder used in the first surface glass layer C 2 be laminated to approximately equal to or more than 1 mm and equal to or less than 2.5 mm.
  • FIG. 4 is a flow chart illustrating the single-crystal silicon pulling method using the vitreous silica crucible of the present embodiment.
  • FIG. 3 is a front cross-sectional view illustrating the pulling of single-crystal silicon using the vitreous silica crucible in the present embodiment.
  • the pulling of single-crystal silicon using the vitreous silica crucible C in the present embodiment is, for example, in accordance with the CZ (Czochralski) method.
  • the single-crystal silicon pulling method has a raw material filling step S 1 , an elevated-temperature melting step S 2 ; a necking step S 31 , a shoulder part forming step S 32 , a straight body part growing step S 33 , and a tail part forming step S 34 for removing single crystal from the melt by diameter shrinkage in a pulling step S 3 , as shown in FIG. 4 .
  • the vitreous silica crucible C is filled with the multi-crystal silicon mass, as a raw material.
  • the vitreous silica crucible C filled with the raw material is disposed in the single crystal-pulling furnace P, as shown in FIG. 3 . Thereafter, the pressure, the atmosphere, the temperature, and the time are adjusted to form a silicon melt S.
  • the atmospheric state in the single crystal-pulling furnace is such as, for example, a melting pressure of 1.33 to 26.66 kPa (10 torr to 200 torr).
  • an inert gas atmosphere such as an argon gas atmosphere, and the like is used.
  • a heating means, H as shown in FIG. 3 , the temperature is elevated from room temperature to a pulling temperature of equal to or more than 1400° C.
  • a seed crystal (single-crystal silicon) 30 is immersed in a silicon melt S as shown in FIG. 3 , and the seed crystal is slowly pulled up while rotating the crucible, thereby allowing the single-crystal silicon 2 to grow, with the seed crystal 30 being a nucleus.
  • the pressure may be a normal pressure of equal to or more than 500 torr and equal to or less than 760 torr, a slightly reduced pressure of equal to or more than 300 torr and equal to or less than 500 torr, or a reduced pressure of equal to or more than 20 torr and equal to or less than 300 torr.
  • a layer containing no bubble is required to be disposed with a thickness of about 5 mm from the inner side.
  • the density of the brown ring can be increased, and it can also be difficult to peel the generated brown ring.
  • a necking step S 31 in the pulling step S 3 dislocation by thermal impact is eliminated from the crystal surface to form a necking part 31 .
  • the shoulder part 32 is formed by diameter expansion; in the straight body part growing step S 33 , a single-crystal silicon 2 having a straight body part 33 taking a silicon wafer is grown; and in the tail part forming step S 34 , the single crystal is taken out from the melt by diameter shrinkage.
  • the gradient of the concentration of OH groups may increase in the thickness direction from the inner surface of the vitreous silica crucible to the outer surface of the vitreous silica crucible.
  • the gradient of the concentration of OH groups is preferably equal to or more than 15 and equal to or less than 400, more preferably equal to or more than 30 and equal to or less than 300, more preferably equal to or more than 60 and equal to or less than 100 or less.
  • the density of the generated brown rings in the inner surface of the crucible is high upon pulling, and the generated brown ring is difficult to be peeled off. Accordingly, by using the vitreous silica crucible of the present invention as a crucible for pulling single-crystal silicon, the yield of single crystallization can be enhanced.
  • a vitreous silica crucible (opening diameter 32 inches) having a concentration of OH groups and a bubble content as shown in Table 1 was prepared, and the pulling of single-crystal silicon was carried out using the vitreous silica crucible. These results are shown in Table 1.
  • the inner surface of the crucible has a low concentration of OH groups in the first surface glass layer, and a high density of the brown ring.
  • the underlying glass layer (the second surface glass layer) has a low concentration of OH groups
  • the apparent growth rate of the brown ring is low. Accordingly, the peeling rate of the brown ring is high.
  • the first surface glass layer has a high OH concentration, and the dissolution rate of glass is high. Accordingly, the density of the brown ring is low.
  • the apparent growth rate of the brown ring is low, the peeling rate of the brown ring is high.
  • the density of the brown ring is high, and the strength of the crucible is high. As a result, the crucible is not deformed. Also, the bubble content in the thickness portion that has undergone melt-damage is low, and the apparent growth rate of the brown ring is high. As a result, the peeling rate of the brown ring is low. Thus, the yield of the single crystallization is high.
  • the concentration of OH groups in Table 1 is a value measured by a infrared spectrophotometry (FT-IR) in the first surface glass layer and the second surface glass layer.
  • FT-IR infrared spectrophotometry
  • the bubble content (% by volume) in Table 1 was measured by taking a photographic image of the bubbles by an optical means for a portion with a thickness of 1 mm from the vitreous silica crucible inner layer, and then subjecting it to imaging.
  • the peeling rate in Table 1 was determined by measuring the peeled area and the inner area of the brown rings by taking photographs of the brown rings by a digital camera, and representing it as a percentage of the peeled area/the inner area of the brown ring.
  • the brown ring density in Table 1 was measured by image-processing of photograph of the inner surface of the crucibles taken by a digital camera. If neighboring brown rings are integrated to form one greater brown ring, in particular, on the inner bottom surface of the crucible which contacts the remaining molten silicon after pulling-up the single crystal silicon, the number of brown rings can be measured as follows. First, the average area per one brown ring is calculated by measuring diameters of independent (not integrated) brown rings in the same target region to be observed. Next, the area of each of the integrated brown rings is measured, and the number of brown rings included in the integrated brown ring is calculated by dividing the area of each of the integrated brown rings by the average area per one brown ring.
  • the deformation of crucible in Table 1 refers to a state of a vitreous silica crucible after preparation of single-crystal silicon for 200 hours using a vitreous silica crucible (opening diameter: 32 inch).
  • a case where deformation of a vitreous silica crucible is observed with the naked eye is evaluated as “Yes”, whereas a case where deformation of a vitreous silica crucible is not observed with the naked eye is evaluated as “No”.
  • the yield in Table 1 is a percentage of a mass of a straight body part capable of taking out a wafer of single-crystal silicon having neither crystal deformation nor impurities/the total mass of polysilicon introduced into a crucible. If this single crystallization rate is changed by 1% by mass, the wafer capable of being taken is changed by about 20 sheets.
  • the surface glass layer is a portion with a thickness of 100 ⁇ m from the inner surface of the crucible surface.
  • the underlying glass layer is at a lower side of the surface glass layer, which is a portion with a thickness of 1 mm from the inner surface of the vitreous silica crucible surface.
  • BR denotes a brown ring.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Crystals, And After-Treatments Of Crystals (AREA)
US12/324,978 2007-12-28 2008-11-28 Inner crystallization crucible and pulling method using the crucible Abandoned US20090165700A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2007339346A JP4995069B2 (ja) 2007-12-28 2007-12-28 内面結晶化ルツボおよび該ルツボを用いた引上げ方法
JP2007-339346 2007-12-28

Publications (1)

Publication Number Publication Date
US20090165700A1 true US20090165700A1 (en) 2009-07-02

Family

ID=40139193

Family Applications (1)

Application Number Title Priority Date Filing Date
US12/324,978 Abandoned US20090165700A1 (en) 2007-12-28 2008-11-28 Inner crystallization crucible and pulling method using the crucible

Country Status (3)

Country Link
US (1) US20090165700A1 (de)
EP (1) EP2075355B1 (de)
JP (1) JP4995069B2 (de)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090084308A1 (en) * 2005-11-30 2009-04-02 Japan Super Quartz Corporation Easily crystallizable vitreous silica member, vitreous silica crucible and method for manufacturing single-crystal silicon
US20100170298A1 (en) * 2009-01-08 2010-07-08 Japan Super Quartz Corporation Vitreous silica crucible manufacturing apparatus
US20110079047A1 (en) * 2009-10-02 2011-04-07 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US20110315072A1 (en) * 2010-06-25 2011-12-29 Japan Super Quartz Corporation Vitreous silica crucible and method of manufacturing the same, and method of manufacturing silicon ingot
US20120131954A1 (en) * 2009-08-12 2012-05-31 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US20120167623A1 (en) * 2010-12-31 2012-07-05 Japan Super Quartz Corporation Method and apparatus for manufacturing vitreous silica crucible
US9856576B2 (en) 2012-09-27 2018-01-02 Heraeus Quarzglas Gmbh & Co. Kg Pulling a semiconductor single crystal according to the Czochralski method
TWI815688B (zh) * 2022-05-27 2023-09-11 大陸商西安奕斯偉材料科技股份有限公司 一種用於生產單晶矽棒的石英坩堝、坩堝元件及拉晶爐
EP4244411A1 (de) * 2020-11-11 2023-09-20 GlobalWafers Co., Ltd. Verfahren zur herstellung eines einkristall-siliciumblocks mit reduzierter tiegelerosion

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5543909B2 (ja) * 2010-12-27 2014-07-09 コバレントマテリアル株式会社 シリカガラスルツボ
JP5557334B2 (ja) * 2010-12-27 2014-07-23 コバレントマテリアル株式会社 シリコン単結晶引上げ用シリカガラスルツボ
JP5978724B2 (ja) * 2012-04-06 2016-08-24 株式会社Sumco シリコン単結晶の製造方法
JP6743753B2 (ja) * 2017-04-27 2020-08-19 株式会社Sumco シリコン単結晶の引上げ方法
US12371812B2 (en) 2019-12-23 2025-07-29 Sumco Corporation Quartz glass crucible and manufacturing method thereof

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5989021A (en) * 1996-03-14 1999-11-23 Shin-Etsu Quartz Products Co., Ltd. Quartz crucible with large diameter for pulling single crystal and method of producing the same
US20020029737A1 (en) * 1998-05-25 2002-03-14 Shin Etsu Quartz Products Co., Ltd. Quartz glass crucible for pulling up silicon single crystal and production method therefor
US20030074920A1 (en) * 2000-05-31 2003-04-24 Yasuo Ohama Method for producing quartz glass crucible
US20030210731A1 (en) * 2002-03-14 2003-11-13 Japan Super Quartz Process and device for producing a quartz glass crucible by ring-like arc, and its quartz glass crucible
US6652934B1 (en) * 1999-06-01 2003-11-25 Toshiba Ceramics Co., Ltd. Silica glass crucible and method of fabricating thereof
US20060236916A1 (en) * 2003-05-01 2006-10-26 Heraeus Quarzglas Gmbh & Co. Kg Quartz glass crucible for pulling up silicon single crystal and method for manufacture thereof

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0764673B2 (ja) * 1990-01-10 1995-07-12 三菱マテリアル株式会社 石英ルツボの製造方法
JP4144060B2 (ja) * 1998-02-20 2008-09-03 株式会社Ｓｕｍｃｏ シリコン単結晶の育成方法
JP4233059B2 (ja) 2003-05-01 2009-03-04 信越石英株式会社 シリコン単結晶引上げ用石英ガラスルツボ及びその製造方法
JP4678667B2 (ja) * 2004-06-07 2011-04-27 信越石英株式会社 シリコン単結晶引上げ用石英ガラスルツボ及びその製造方法

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5989021A (en) * 1996-03-14 1999-11-23 Shin-Etsu Quartz Products Co., Ltd. Quartz crucible with large diameter for pulling single crystal and method of producing the same
US6136092A (en) * 1996-03-14 2000-10-24 Shin Etsu Quartz Products Co., Ltd. Quart crucible with large diameter for pulling single crystal and method of producing the same
US20020029737A1 (en) * 1998-05-25 2002-03-14 Shin Etsu Quartz Products Co., Ltd. Quartz glass crucible for pulling up silicon single crystal and production method therefor
US6652934B1 (en) * 1999-06-01 2003-11-25 Toshiba Ceramics Co., Ltd. Silica glass crucible and method of fabricating thereof
US20030074920A1 (en) * 2000-05-31 2003-04-24 Yasuo Ohama Method for producing quartz glass crucible
US20030210731A1 (en) * 2002-03-14 2003-11-13 Japan Super Quartz Process and device for producing a quartz glass crucible by ring-like arc, and its quartz glass crucible
US20060236916A1 (en) * 2003-05-01 2006-10-26 Heraeus Quarzglas Gmbh & Co. Kg Quartz glass crucible for pulling up silicon single crystal and method for manufacture thereof

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090084308A1 (en) * 2005-11-30 2009-04-02 Japan Super Quartz Corporation Easily crystallizable vitreous silica member, vitreous silica crucible and method for manufacturing single-crystal silicon
US20100170298A1 (en) * 2009-01-08 2010-07-08 Japan Super Quartz Corporation Vitreous silica crucible manufacturing apparatus
US8240169B2 (en) * 2009-01-08 2012-08-14 Japan Super Quartz Corporation Vitreous silica crucible manufacturing apparatus
US8739573B2 (en) * 2009-08-12 2014-06-03 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US20120131954A1 (en) * 2009-08-12 2012-05-31 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US20110079047A1 (en) * 2009-10-02 2011-04-07 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US8844321B2 (en) * 2009-10-02 2014-09-30 Japan Super Quartz Corporation Apparatus and method for manufacturing vitreous silica crucible
US9719188B2 (en) 2010-06-25 2017-08-01 Sumco Corporation Method of manufacturing a vitreous silica crucible having a transparent layer, bubble-containing layers, and a semi-transparent layer in its wall
US9157168B2 (en) * 2010-06-25 2015-10-13 Sumco Corporation Vitreous silica crucible having transparent layer, bubble-containing layer, and semi-transparent layer in its wall, method of manufacturing the same, and method of manufacturing silicon ingot
US20110315072A1 (en) * 2010-06-25 2011-12-29 Japan Super Quartz Corporation Vitreous silica crucible and method of manufacturing the same, and method of manufacturing silicon ingot
US20140283552A1 (en) * 2010-12-31 2014-09-25 Sumco Corporation Method for manufacturing vitreous silica crucible
US20120167623A1 (en) * 2010-12-31 2012-07-05 Japan Super Quartz Corporation Method and apparatus for manufacturing vitreous silica crucible
US9181121B2 (en) * 2010-12-31 2015-11-10 Sumco Corporation Method for manufacturing vitreous silica crucible
US9856576B2 (en) 2012-09-27 2018-01-02 Heraeus Quarzglas Gmbh & Co. Kg Pulling a semiconductor single crystal according to the Czochralski method
US10287705B2 (en) 2012-09-27 2019-05-14 Heraeus Quarzglas Gmbh & Co. Kg Pulling a semiconductor single crystal according to the Czochralski method and silica glass crucible suitable therefor
EP4244411A1 (de) * 2020-11-11 2023-09-20 GlobalWafers Co., Ltd. Verfahren zur herstellung eines einkristall-siliciumblocks mit reduzierter tiegelerosion
TWI815688B (zh) * 2022-05-27 2023-09-11 大陸商西安奕斯偉材料科技股份有限公司 一種用於生產單晶矽棒的石英坩堝、坩堝元件及拉晶爐

Also Published As

Publication number Publication date
JP2009161364A (ja) 2009-07-23
EP2075355B1 (de) 2012-05-16
JP4995069B2 (ja) 2012-08-08
EP2075355A3 (de) 2010-08-11
EP2075355A2 (de) 2009-07-01

Similar Documents

Publication Publication Date Title
EP2075355B1 (de) Innerer Kristallisierungstiegel und Ziehverfahren unter Verwendung des Tiegels
JP4166241B2 (ja) シリコン単結晶引上げ用石英ガラスルツボ及びその製造方法
JP4702898B2 (ja) シリコン単結晶引上げ用石英ガラスルツボの製造方法
EP2071059B1 (de) Hochreiner glasartiger Quarztiegel zum Ziehen eines Einkristall-Siliciumblocks mit großem Durchmesser
EP2267192B1 (de) Verfahren zur ziehung eines siliziumeinkristalles und verfahren zur herstellung eines quarzglastiegels
KR100731833B1 (ko) 실리콘 단결정 인상용 석영 그라스 도가니
KR101165703B1 (ko) 실리콘 단결정 인상용 석영 유리 도가니 및 그 제조 방법
EP2067883B1 (de) Verfahren zur Herstellung eines glasartigen Quarztiegels
US8163083B2 (en) Silica glass crucible and method for pulling up silicon single crystal using the same
KR100731831B1 (ko) 실리콘단결정 인상용 석영유리 도가니 및 그 제조방법
JP2005343774A (ja) シリコン単結晶引上げ用石英ガラスルツボ及びその製造方法
JP2010280567A (ja) シリカガラスルツボの製造方法
JP5741163B2 (ja) 石英ガラスルツボ及びその製造方法、並びにシリコン単結晶の製造方法
JP4549008B2 (ja) 水素ドープシリカ粉及びそれを用いたシリコン単結晶引上げ用石英ガラスルツボ
JP5685894B2 (ja) 石英ガラスルツボ及びその製造方法、並びにシリコン単結晶の製造方法
JP4931106B2 (ja) シリカガラスルツボ
WO2004094705A1 (ja) フッ化物結晶の製造装置
JP2000109391A (ja) 石英るつぼ
JP7280160B2 (ja) シリカガラスルツボ
JP4726138B2 (ja) 石英ガラスルツボ
EP2143831B1 (de) Verfahren zum Hochziehen von Siliziumeinkristallen unter Verwendung von Quarzglastiegeln.
JPH09278582A (ja) 単結晶の製造方法およびその装置
JP2012218980A (ja) 石英ガラスルツボ及びその製造方法、並びにシリコン単結晶の製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: JAPAN SUPER QUARTZ CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KISHI, HIROSHI;KANDA, MINORU;REEL/FRAME:022332/0832

Effective date: 20090211

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO PAY ISSUE FEE