WO2017160935A1 - Blanchiment à faible capital de pâte chimique - Google Patents

Blanchiment à faible capital de pâte chimique Download PDF

Info

Publication number
WO2017160935A1
WO2017160935A1 PCT/US2017/022443 US2017022443W WO2017160935A1 WO 2017160935 A1 WO2017160935 A1 WO 2017160935A1 US 2017022443 W US2017022443 W US 2017022443W WO 2017160935 A1 WO2017160935 A1 WO 2017160935A1
Authority
WO
WIPO (PCT)
Prior art keywords
chemical pulp
organomanganese
pulp
bleaching
complex
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2017/022443
Other languages
English (en)
Inventor
Prasad Y. Duggirala
Sergey M. Shevchenko
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ecolab USA Inc
Original Assignee
Ecolab USA Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ecolab USA Inc filed Critical Ecolab USA Inc
Publication of WO2017160935A1 publication Critical patent/WO2017160935A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne des procédés et des formulations de blanchiment pour des processus de blanchiment/délignification de pâte chimique. Les procédés de blanchiment utilisent du peroxyde et un complexe organo-manganèse dans des conditions caustiques aqueuses, augmentant l'efficacité de blanchiment du processus de blanchiment/délignification global. Une pâte chimique ayant une blancheur accrue peut être obtenue à des températures réduites et avec une durée de phase réduite, entraînant une consommation de produit chimique réduite et une efficacité énergétique améliorée.
PCT/US2017/022443 2016-03-16 2017-03-15 Blanchiment à faible capital de pâte chimique Ceased WO2017160935A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201662309282P 2016-03-16 2016-03-16
US62/309,282 2016-03-16

Publications (1)

Publication Number Publication Date
WO2017160935A1 true WO2017160935A1 (fr) 2017-09-21

Family

ID=58448621

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/022443 Ceased WO2017160935A1 (fr) 2016-03-16 2017-03-15 Blanchiment à faible capital de pâte chimique

Country Status (2)

Country Link
US (1) US20170268171A1 (fr)
WO (1) WO2017160935A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113338061A (zh) * 2021-05-27 2021-09-03 广州骏亚纺织科技有限公司 双氧水催化剂的组合物及其应用

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1246304A (fr) * 1982-09-29 1988-12-13 Cip Inc. Methode et dispositif de blanchiment de la pate a papier
US5244594A (en) * 1990-05-21 1993-09-14 Lever Brothers Company, Division Of Conopco, Inc. Bleach activation multinuclear manganese-based coordination complexes
US5938892A (en) * 1991-01-28 1999-08-17 Champion International Corporation Process for recycling bleach plant filtrate
WO2002022944A1 (fr) * 2000-09-14 2002-03-21 Atofina Procede de delignification et blanchiment par un oxydant et un catalyseur d'oxydoreduction
US20130126111A1 (en) * 2010-05-10 2013-05-23 Catexel Limited Freeness of paper products
US20140213436A1 (en) * 2005-05-27 2014-07-31 Conopco Inc., D/B/A Unilver Process of bleaching

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA1246304A (fr) * 1982-09-29 1988-12-13 Cip Inc. Methode et dispositif de blanchiment de la pate a papier
US5244594A (en) * 1990-05-21 1993-09-14 Lever Brothers Company, Division Of Conopco, Inc. Bleach activation multinuclear manganese-based coordination complexes
US5938892A (en) * 1991-01-28 1999-08-17 Champion International Corporation Process for recycling bleach plant filtrate
WO2002022944A1 (fr) * 2000-09-14 2002-03-21 Atofina Procede de delignification et blanchiment par un oxydant et un catalyseur d'oxydoreduction
US20140213436A1 (en) * 2005-05-27 2014-07-31 Conopco Inc., D/B/A Unilver Process of bleaching
US20130126111A1 (en) * 2010-05-10 2013-05-23 Catexel Limited Freeness of paper products

Also Published As

Publication number Publication date
US20170268171A1 (en) 2017-09-21

Similar Documents

Publication Publication Date Title
US4568420A (en) Multi-stage bleaching process including an enhanced oxidative extraction stage
US20110174451A1 (en) Process for Delignifying and Bleaching Chemical Pulp
US11840805B2 (en) High efficiency fiber bleaching process
FI105213B (fi) Menetelmä valkaistun massan valmistamiseksi lignoselluloosamateriaalista
CN104471146B (zh) 漂白纸浆的方法
Sevastyanova et al. Bleaching of eucalyptus kraft pulps with chlorine dioxide: Factors affecting the efficiency of the final D stage
US20170268171A1 (en) Low Capital Bleaching of Chemical Pulp
CA2916017C (fr) Procede de traitement des pates papetieres chimiques par traitement a l'ozone en presence d'ions magnesium
US4132589A (en) Delignification and bleaching of cellulose pulp
CA2327248A1 (fr) Procede de production de pate chimique blanchie respectueux de l'environnement
US11384480B2 (en) Method for bleaching paper pulp
JP5915263B2 (ja) パルプの製造方法
EP0902120A1 (fr) Procédé de blanchissement d'une pâte à papier avec de l'ozone et du dioxyde de chlore
US20120031575A1 (en) Pulp Bleaching and Alkaline Extraction Method
MXPA96002927A (en) Procedure for whitening pulp paste kr
US20030168190A1 (en) Method for controlling the delignfication and bleaching of a pulp suspension
US20030155086A1 (en) Process for bleaching a lignocellulosic pulp
Sharma et al. Environmental Impact of Application of Ozone Bleaching for Production of Pulp from Agro Based Fibrous Materials—An Innovative Approach
Isaza Ferro Catalyzed and non-catalyzed hypochlorous acid bleaching of kraft pulps
CA3049171C (fr) Procede de blanchiment d'une pate a papier
JP2003278087A (ja) パルプ処理法
CN116457529A (zh) 高卡伯纤维的氧处理
Zeinaly et al. The use of TAED in the last phase of CMP peroxide bleaching
JP2006283211A (ja) 化学パルプの漂白方法
Vitasari The Effect of Ozone Concentration on the Bleached Pulp Properties

Legal Events

Date Code Title Description
WA Withdrawal of international application
NENP Non-entry into the national phase

Ref country code: DE