WO2017179913A2 - Composition de résine composite texturée de haute qualité et tôle d'acier galvanisé revêtue d'une composition de résine composite - Google Patents

Composition de résine composite texturée de haute qualité et tôle d'acier galvanisé revêtue d'une composition de résine composite Download PDF

Info

Publication number
WO2017179913A2
WO2017179913A2 PCT/KR2017/003974 KR2017003974W WO2017179913A2 WO 2017179913 A2 WO2017179913 A2 WO 2017179913A2 KR 2017003974 W KR2017003974 W KR 2017003974W WO 2017179913 A2 WO2017179913 A2 WO 2017179913A2
Authority
WO
WIPO (PCT)
Prior art keywords
composite resin
resin composition
steel sheet
coating film
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2017/003974
Other languages
English (en)
Korean (ko)
Other versions
WO2017179913A3 (fr
Inventor
조두환
강춘호
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Posco Holdings Inc
Original Assignee
Posco Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020160178224A external-priority patent/KR101867736B1/ko
Application filed by Posco Co Ltd filed Critical Posco Co Ltd
Priority to EP17782668.2A priority Critical patent/EP3444303B1/fr
Priority to CN201780023554.5A priority patent/CN109071924A/zh
Publication of WO2017179913A2 publication Critical patent/WO2017179913A2/fr
Publication of WO2017179913A3 publication Critical patent/WO2017179913A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une composition de résine composite comprenant 30 à 60 % en poids d'une résine de polyester modifié par de l'uréthane dans laquelle un type linéaire et un type à réticulation sont mélangés, 3 à 15 % en poids d'au moins un agent de durcissement qui est soit un agent de durcissement de type aziridine, soit un agent de durcissement de type mélamine, de 0,05 à 1,5 % en poids d'un catalyseur de durcissement acide, de 0,05 à 1,5 % en poids d'un catalyseur de durcissement de type amine, 0,1 à 15 % en poids d'un pigment inorganique coloré, le complément étant constitué d'un solvant. En outre, la présente invention concerne une tôle d'acier galvanisé revêtue de résine composite portant un film de revêtement de résine composite formé de la composition ci-dessus.
PCT/KR2017/003974 2016-04-12 2017-04-12 Composition de résine composite texturée de haute qualité et tôle d'acier galvanisé revêtue d'une composition de résine composite Ceased WO2017179913A2 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP17782668.2A EP3444303B1 (fr) 2016-04-12 2017-04-12 Composition de résine composite texturée de haute qualité et tôle d'acier galvanisé revêtue d'une composition de résine composite
CN201780023554.5A CN109071924A (zh) 2016-04-12 2017-04-12 高级质感的复合树脂组合物及涂覆有所述复合树脂组合物的镀锌钢板

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR10-2016-0044696 2016-04-12
KR20160044696 2016-04-12
KR10-2016-0178224 2016-12-23
KR1020160178224A KR101867736B1 (ko) 2016-04-12 2016-12-23 고급질감의 복합수지 조성물 및 상기 복합수지 조성물이 코팅된 아연도금강판

Publications (2)

Publication Number Publication Date
WO2017179913A2 true WO2017179913A2 (fr) 2017-10-19
WO2017179913A3 WO2017179913A3 (fr) 2018-08-02

Family

ID=60041677

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2017/003974 Ceased WO2017179913A2 (fr) 2016-04-12 2017-04-12 Composition de résine composite texturée de haute qualité et tôle d'acier galvanisé revêtue d'une composition de résine composite

Country Status (1)

Country Link
WO (1) WO2017179913A2 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3447417A1 (fr) * 2017-08-21 2019-02-27 LG Electronics Inc. Plaque extérieure d'un réfrigérateur et son procédé de fabrication
EP3473419A1 (fr) * 2017-10-20 2019-04-24 Société de Trefilerie d'Alsace SAS Dispositifs et procédés de revêtement de câbles

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04176367A (ja) * 1990-11-07 1992-06-24 Kawasaki Steel Corp 加工性の優れた艶消し塗装鋼板
JP3487924B2 (ja) * 1994-09-29 2004-01-19 新日本製鐵株式会社 塗装金属板用塗料組成物及び塗装金属板の製造方法
KR100618469B1 (ko) * 1998-10-29 2007-04-25 주식회사 새 한 광확산반사투과형 편광판_
KR20040065937A (ko) * 2003-01-16 2004-07-23 건설화학공업주식회사 코일코팅용 향기나는 텍스츄어 도료의 조성물 및 그도장강판
KR100915082B1 (ko) * 2007-09-11 2009-09-02 삼화페인트 공업주식회사 피씨엠용 주름형 Ｃｏｌｏｒ Ｔｅｘｔｕｒｅ 도료 조성물및 상기 조성물을 이용한 칼라 강판의 제조방법
KR101383008B1 (ko) * 2012-07-26 2014-04-08 주식회사 포스코 내이행성과 가공성이 우수한 흑색수지 조성물 및 흑색수지 코팅강판

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3447417A1 (fr) * 2017-08-21 2019-02-27 LG Electronics Inc. Plaque extérieure d'un réfrigérateur et son procédé de fabrication
US11383492B2 (en) 2017-08-21 2022-07-12 Lg Electronics Inc. Outer plate of refrigerator and method for manufacturing the same
EP3473419A1 (fr) * 2017-10-20 2019-04-24 Société de Trefilerie d'Alsace SAS Dispositifs et procédés de revêtement de câbles

Also Published As

Publication number Publication date
WO2017179913A3 (fr) 2018-08-02

Similar Documents

Publication Publication Date Title
WO2013009133A2 (fr) Composition de résine pour un traitement de surface et tôle d'acier revêtue de celle-ci
WO2014077632A1 (fr) Composition de peinture inorganique et procédé pour la formation d'un feuil de peinture inorganique à l'aide de celle-ci
WO2019124990A1 (fr) Composition de solution de traitement de surface pour tôle d'acier plaquée d'alliage de zinc par immersion à chaud ternaire, fournissant une excellente résistance à la corrosion et au noircissement, tôle d'acier plaquée d'alliage de zinc par immersion à chaud ternaire traitée en surface l'utilisant, et son procédé de fabrication
WO2022065922A1 (fr) Composition de résine composite ayant une excellentes résistance aux intempéries et d'excellentes caractéristiques de rayonnement thermique, une feuille d'acier revêtue de résine composite et un procédé de fabrication associé
WO2021060818A1 (fr) Composition de solution de traitement de surface de tôle d'acier galvanisée par immersion à chaud ternaire pour fournir une excellente résistance au noircissement et une excellente résistance aux alcalis, tôle d'acier galvanisée par immersion à chaud ternaire traitée en surface l'utilisant et son procédé de fabrication
WO2017030334A1 (fr) Composition d'encre pour une plaque d'acier d'impression à jet d'encre, plaque d'acier d'impression à jet d'encre utilisant cette dernière et procédé permettant de produire une plaque d'acier d'impression à jet d'encre
WO2013112018A1 (fr) Composition de résine de polycarbonate présentant d'excellentes propriétés en termes de coloration, de résistance aux chocs et de résistance aux éraflures
KR101867736B1 (ko) 고급질감의 복합수지 조성물 및 상기 복합수지 조성물이 코팅된 아연도금강판
WO2022085998A1 (fr) Composition de résine thermoplastique, son procédé de préparation et produit moulé la comprenant
WO2013062329A1 (fr) Tôle d'acier revêtue qui présente de meilleures propriétés de soudage, de résistance aux rayures et de résistance à la corrosion
WO2024167235A1 (fr) Composition photopolymérisable pour jet d'encre, film durci de celle-ci, et élément optique et dispositif d'affichage la comprenant
WO2017111561A1 (fr) Tôle d'acier revêtue d'alliage et procédé de fabrication s'y rapportant
WO2010008213A9 (fr) Composé à base de silane, procédé de préparation de ce dernier et composition d'agent de traitement de surface pour feuille de cuivre comprenant le composé à base de silane
WO2023055099A1 (fr) Résine thermoplastique et article moulé fabriqué à partir de celle-ci
WO2020159086A1 (fr) Film de résine polyamide et stratifié de résine l'utilisant
WO2022158831A1 (fr) Film stratifié plaqué de cuivre, élément électronique le comprenant, et procédé de fabrication de film stratifié plaqué de cuivre
KR20140014817A (ko) 내이행성과 가공성이 우수한 흑색수지 조성물 및 흑색수지 코팅강판
WO2022097872A1 (fr) Film de libération et son procédé de préparation
WO2022045737A1 (fr) Composition de résine photosensible positive
WO2012158001A2 (fr) Composition de peinture inorganique, procédé pour sa préparation et procédé de formation d'un film de revêtement inorganique
WO2010008214A2 (fr) Feuille de cuivre pour carte à circuit imprimé, procédé de préparation de cette dernière et stratifié plaqué de cuivre souple obtenu à l'aide d'un précurseur acide polyamique et d'une feuille de cuivre
WO2023277541A1 (fr) Pigment nacré multicolore à effet scintillant amélioré et procédé de préparation associé
WO2022203284A1 (fr) Monomère antibactérien, composition de polymère antibactérien comprenant le monomère antibactérien, film antibactérien obtenu à partir de la composition de polymère antibactérien, et article comprenant le film antibactérien
WO2025095371A1 (fr) Composition d'additif de peinture présentant une excellente propriété d'élimination de contamination et une excellente persistance d'élimination de contamination, et composition de peinture la comprenant
WO2024080498A1 (fr) Composition de résine thermoplastique, son procédé de production et article moulé la comprenant

Legal Events

Date Code Title Description
NENP Non-entry into the national phase in:

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2017782668

Country of ref document: EP

ENP Entry into the national phase in:

Ref document number: 2017782668

Country of ref document: EP

Effective date: 20181112

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17782668

Country of ref document: EP

Kind code of ref document: A2