WO2024256545A1 - Production d'un toron d'aluminium - Google Patents

Production d'un toron d'aluminium Download PDF

Info

Publication number
WO2024256545A1
WO2024256545A1 PCT/EP2024/066377 EP2024066377W WO2024256545A1 WO 2024256545 A1 WO2024256545 A1 WO 2024256545A1 EP 2024066377 W EP2024066377 W EP 2024066377W WO 2024256545 A1 WO2024256545 A1 WO 2024256545A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminium strand
cooling
press
die
cooling installation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2024/066377
Other languages
English (en)
Inventor
Dawid Nadolski
Elena Gerber
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Air Liquide Deutschland GmbH
Air Liquide SA
LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
Original Assignee
Air Liquide Deutschland GmbH
Air Liquide SA
LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Air Liquide Deutschland GmbH, Air Liquide SA, LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude filed Critical Air Liquide Deutschland GmbH
Priority to EP24733152.3A priority Critical patent/EP4727707A1/fr
Priority to CN202480040038.3A priority patent/CN121358551A/zh
Publication of WO2024256545A1 publication Critical patent/WO2024256545A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un dispositif (1) pour la production d'un toron d'aluminium (2), comprenant une presse (3), une installation de refroidissement (4) et une source de gaz liquide (5), la presse (3) comprenant une filière (6), un matériau de presse (7) pouvant être pressé à travers la filière (6) en un toron d'aluminium (2) dans la presse (3), l'installation de refroidissement (4) permettant de refroidir le toron d'aluminium (2) étant directement en aval de la filière (6), et l'installation de refroidissement (4) étant raccordée à la source de gaz liquide (5).
PCT/EP2024/066377 2023-06-14 2024-06-13 Production d'un toron d'aluminium Ceased WO2024256545A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP24733152.3A EP4727707A1 (fr) 2023-06-14 2024-06-13 Production d'un toron d'aluminium
CN202480040038.3A CN121358551A (zh) 2023-06-14 2024-06-13 铝绞线的生产

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102023115493.1 2023-06-14
DE102023115493.1A DE102023115493A1 (de) 2023-06-14 2023-06-14 Herstellung eines Aluminiumstrangs

Publications (1)

Publication Number Publication Date
WO2024256545A1 true WO2024256545A1 (fr) 2024-12-19

Family

ID=91580975

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2024/066377 Ceased WO2024256545A1 (fr) 2023-06-14 2024-06-13 Production d'un toron d'aluminium

Country Status (4)

Country Link
EP (1) EP4727707A1 (fr)
CN (1) CN121358551A (fr)
DE (1) DE102023115493A1 (fr)
WO (1) WO2024256545A1 (fr)

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1594455A (en) * 1976-10-15 1981-07-30 Michelin & Cie Plant for the manufacture of a wire by projecting a stream of liquid metal into a cooling medium
EP0210568B1 (fr) * 1985-08-02 1994-03-09 Linde Aktiengesellschaft Procédé d'extrusion, respectivement d'étirage
JPH07132318A (ja) * 1993-11-12 1995-05-23 Sumitomo Light Metal Ind Ltd アルミニウム押出材の冷却方法および冷却装置
EP0578607B1 (fr) * 1992-06-19 1997-01-08 Alusuisse Technology & Management AG Dispositif de pulvérisation pour le refroidissement de profilés
US20020170330A1 (en) * 2001-03-16 2002-11-21 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Cooling system for press quenching and method for press quenching with said cooling system
EP1837410B1 (fr) * 2006-03-21 2009-08-26 Linde AG Procédé et dispositif de réfrigération rapide de pièces d' ouvrage
DE102013010836A1 (de) * 2013-07-10 2015-01-15 Messer Group Gmbh Vorrichtung zum Strangpressen von Werkstücken, insbesondere aus Aluminiumlegierungen
KR102243544B1 (ko) * 2021-01-27 2021-04-22 주식회사 알코아 알루미늄 압출장치의 압출금형 자동 냉각장치
US20220152678A1 (en) * 2019-09-27 2022-05-19 Ube Machinery Corporation, Ltd. Extrusion press machine and platen for extrusion press machine

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CH540076A (de) * 1971-03-18 1973-08-15 Alusuisse Verfahren und Vorrichtung zum Strangpressen von Werkstücken insbesondere aus Aluminiumlegierungen
DE102017106969B4 (de) * 2017-03-31 2020-08-06 Wefa Singen Gmbh Verfahren zum Herstellen eines Strangpresswerkzeugs

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1594455A (en) * 1976-10-15 1981-07-30 Michelin & Cie Plant for the manufacture of a wire by projecting a stream of liquid metal into a cooling medium
EP0210568B1 (fr) * 1985-08-02 1994-03-09 Linde Aktiengesellschaft Procédé d'extrusion, respectivement d'étirage
EP0578607B1 (fr) * 1992-06-19 1997-01-08 Alusuisse Technology & Management AG Dispositif de pulvérisation pour le refroidissement de profilés
JPH07132318A (ja) * 1993-11-12 1995-05-23 Sumitomo Light Metal Ind Ltd アルミニウム押出材の冷却方法および冷却装置
US20020170330A1 (en) * 2001-03-16 2002-11-21 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Cooling system for press quenching and method for press quenching with said cooling system
EP1837410B1 (fr) * 2006-03-21 2009-08-26 Linde AG Procédé et dispositif de réfrigération rapide de pièces d' ouvrage
DE102013010836A1 (de) * 2013-07-10 2015-01-15 Messer Group Gmbh Vorrichtung zum Strangpressen von Werkstücken, insbesondere aus Aluminiumlegierungen
US20220152678A1 (en) * 2019-09-27 2022-05-19 Ube Machinery Corporation, Ltd. Extrusion press machine and platen for extrusion press machine
KR102243544B1 (ko) * 2021-01-27 2021-04-22 주식회사 알코아 알루미늄 압출장치의 압출금형 자동 냉각장치

Also Published As

Publication number Publication date
EP4727707A1 (fr) 2026-04-22
DE102023115493A1 (de) 2024-12-19
CN121358551A (zh) 2026-01-16

Similar Documents

Publication Publication Date Title
EP2072157B1 (fr) Procédé de refroidissement de bande d'acier laminée à chaud
CN107922988B (zh) 非接触式冷却钢板的方法以及用于该方法的设备
CN206204366U (zh) 热处理装置
EP1630253A1 (fr) Procédé pour la fabrication en ligne continue de revêtements rapides par pulvérisation cinétique
EP1999297A1 (fr) Pistolet de projection a gaz froid
KR19980702237A (ko) 강철 스트립의 연속 어닐링에 있어서의 1차 냉각 방법
WO2010122847A1 (fr) Procédé de production de tuyau sans soudure et appareil pour mettre en oeuvre ledit procédé
CN206204351U (zh) 热处理装置
EP1241273A2 (fr) Procédé et dispositif de refroidissement par jets
JP2022166196A (ja) 熱処理方法
US20170044643A1 (en) Method and apparatus for producing a steel strip
WO2024256545A1 (fr) Production d'un toron d'aluminium
CN102952929A (zh) 一种用于连续进行热处理的装置及热处理方法
US20070220906A1 (en) Method and Device for Rapid Cooling of Work Pieces
JP4507341B2 (ja) 鋼材の冷却方法
JPH0429615B2 (fr)
CN101370947B (zh) 用于在碳素钢内尤其是在带钢内连续生成贝氏体组织的方法和设备
JP2008221316A (ja) 連続鋳造鋳片の冷却方法
EP2656741B1 (fr) Procédé et dispositif destinés au refroidissement de produits
KR101867706B1 (ko) 냉각 장치
JP4066387B1 (ja) 棒鋼の制御冷却装置
US5902543A (en) Process and device for cooling an article
DE102008064083A1 (de) Vorrichtung und Verfahren zum Kühlen von Oberflächen
JP2002038219A (ja) マルテンサイト系ステンレス鋼管の製造方法
US7707841B2 (en) Phase cooling method and apparatus

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24733152

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2024733152

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2024733152

Country of ref document: EP

Effective date: 20260114

ENP Entry into the national phase

Ref document number: 2024733152

Country of ref document: EP

Effective date: 20260114

ENP Entry into the national phase

Ref document number: 2024733152

Country of ref document: EP

Effective date: 20260114

ENP Entry into the national phase

Ref document number: 2024733152

Country of ref document: EP

Effective date: 20260114

WWP Wipo information: published in national office

Ref document number: 2024733152

Country of ref document: EP