ATE328925T1 - Verfahren zur herstellung von flexiblem polyurethanschaum - Google Patents

Verfahren zur herstellung von flexiblem polyurethanschaum

Info

Publication number
ATE328925T1
ATE328925T1 AT01919914T AT01919914T ATE328925T1 AT E328925 T1 ATE328925 T1 AT E328925T1 AT 01919914 T AT01919914 T AT 01919914T AT 01919914 T AT01919914 T AT 01919914T AT E328925 T1 ATE328925 T1 AT E328925T1
Authority
AT
Austria
Prior art keywords
polyurethane foam
flexible polyurethane
catalyst
mass
producing flexible
Prior art date
Application number
AT01919914T
Other languages
English (en)
Inventor
Yoshinori Toyota
Hiroshi Wada
Takayuki Sasaki
Akio Horie
Kayoko Sugiyama
Hiromitsu Takeyasu
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Application granted granted Critical
Publication of ATE328925T1 publication Critical patent/ATE328925T1/de

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4866—Polyethers having a low unsaturation value
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/4009—Two or more macromolecular compounds not provided for in one single group of groups C08G18/42 - C08G18/64
    • C08G18/4072—Mixtures of compounds of group C08G18/63 with other macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4804—Two or more polyethers of different physical or chemical nature
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/6552—Compounds of group C08G18/63
    • C08G18/6558—Compounds of group C08G18/63 with compounds of group C08G18/32 or polyamines of C08G18/38
    • C08G18/6564—Compounds of group C08G18/63 with compounds of group C08G18/32 or polyamines of C08G18/38 with compounds of group C08G18/3203
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0008—Foam properties flexible
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0041—Foam properties having specified density
    • C08G2110/0058—≥50 and <150kg/m3
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0083—Foam properties prepared using water as the sole blowing agent
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2350/00—Acoustic or vibration damping material

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyurethanes Or Polyureas (AREA)
AT01919914T 2000-04-14 2001-04-12 Verfahren zur herstellung von flexiblem polyurethanschaum ATE328925T1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2000114330 2000-04-14

Publications (1)

Publication Number Publication Date
ATE328925T1 true ATE328925T1 (de) 2006-06-15

Family

ID=18626150

Family Applications (1)

Application Number Title Priority Date Filing Date
AT01919914T ATE328925T1 (de) 2000-04-14 2001-04-12 Verfahren zur herstellung von flexiblem polyurethanschaum

Country Status (10)

Country Link
US (1) US6653362B2 (de)
EP (1) EP1273605B1 (de)
JP (1) JP5332073B2 (de)
KR (1) KR100663682B1 (de)
CN (1) CN1261477C (de)
AT (1) ATE328925T1 (de)
AU (1) AU772300B2 (de)
CA (1) CA2406114A1 (de)
DE (1) DE60120390T2 (de)
WO (1) WO2001079323A1 (de)

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3181279B2 (ja) * 1999-09-03 2001-07-03 東洋ゴム工業株式会社 シートクッションパッド
US6866915B2 (en) * 2000-01-11 2005-03-15 Tempur World, Llc Cushion
JP4715002B2 (ja) * 2001-02-27 2011-07-06 旭硝子株式会社 軟質ポリウレタンフォームの製造方法
WO2002100916A1 (en) * 2001-05-24 2002-12-19 Mitsui Takeda Chemicals, Inc. Process for producing flexible polyurethane foams and apparatus for producing flexible polyurethane foams
EP1283231A1 (de) 2001-08-06 2003-02-12 Asahi Glass Company Ltd. Polyurethanweichschaum, sein Verfahren zur Herstellung und Material-System zu seiner Herstellung
JP2008195962A (ja) * 2001-11-29 2008-08-28 Asahi Glass Co Ltd 軟質ポリウレタンフォームとその製造方法
JP5151461B2 (ja) * 2001-11-30 2013-02-27 旭硝子株式会社 軟質ポリウレタンフォームの製造方法およびその用途
EP1316573B1 (de) * 2001-11-30 2007-07-18 Asahi Glass Co., Ltd. Polyurethanweichschaum und Verfahren zur Herstellung
AU2002357617A1 (en) * 2001-12-21 2003-07-09 Asahi Glass Company, Limited Low-resilience flexible polyurethane foam and process for producing the same
US7530127B2 (en) 2002-05-24 2009-05-12 Dan-Foam Aps Pillow and method of manufacturing a pillow
NZ554159A (en) 2002-05-24 2008-10-31 Tempur World Llc Comfort pillow
WO2005028535A1 (ja) * 2003-09-19 2005-03-31 Asahi Glass Company, Limited 軟質ポリウレタンフォームおよびその製造方法
ATE509051T1 (de) * 2003-11-26 2011-05-15 Asahi Glass Co Ltd Polyurethanweichschaumstoff, herstellungsverfahren dafür und automobilsitz damit
JP4750369B2 (ja) * 2004-03-31 2011-08-17 三洋化成工業株式会社 軟質ポリウレタンフォームの製造方法
JP4910702B2 (ja) * 2004-11-18 2012-04-04 旭硝子株式会社 軟質ポリウレタンフォームの製造方法
CN101061155B (zh) * 2004-11-24 2010-07-21 旭硝子株式会社 软质聚氨酯泡沫塑料、其制造方法以及汽车用座垫
KR101292900B1 (ko) * 2005-04-21 2013-08-02 아사히 가라스 가부시키가이샤 저반발성 연질 폴리우레탄폼 및 그 제조 방법
EP1884528A4 (de) * 2005-05-25 2012-07-25 Asahi Glass Co Ltd Polyurethanweichschaumstoff, herstellungsverfahren dafür und autositz mit dem polyurethanweichschaumstoff
JP5266757B2 (ja) * 2005-05-25 2013-08-21 旭硝子株式会社 軟質ポリウレタンフォームの製造方法
WO2006126611A1 (ja) * 2005-05-25 2006-11-30 Asahi Glass Company, Limited 軟質ポリウレタンフォームおよびその製造方法、該軟質ポリウレタンフォームを用いた自動車用シート
US7469437B2 (en) 2005-06-24 2008-12-30 Tempur-Pedic Management, Inc. Reticulated material body support and method
WO2007018129A1 (ja) * 2005-08-05 2007-02-15 Asahi Glass Company, Limited 軟質ポリウレタンフォーム、その製造方法および自動車用シート
EP1991608A4 (de) * 2006-02-23 2011-07-20 Robert N Clausi Hoch gefülltte verbundwerkstoffe
TW200801060A (en) * 2006-02-28 2008-01-01 Asahi Glass Co Ltd Flexible polyurethane foam and process for producing the same
US8656537B2 (en) 2006-04-20 2014-02-25 Dan Foam Aps Multi-component pillow and method of manufacturing and assembling same
KR20090082177A (ko) 2006-10-25 2009-07-29 아사히 가라스 가부시키가이샤 연질 폴리우레탄 폼의 제조 방법
JP5303885B2 (ja) 2007-09-18 2013-10-02 旭硝子株式会社 軟質ポリウレタンフォームの製造方法および軟質ポリウレタンフォーム
CN101809053B (zh) * 2007-09-28 2012-09-26 旭硝子株式会社 软质聚氨酯泡沫及热压成形品的制造方法以及热压成形品
DE102008000266A1 (de) * 2008-02-11 2009-08-13 Evonik Goldschmidt Gmbh Die Erfindung betrifft die Verwendung von Schaumstabilisatoren, die auf Basis nachwachsender Rohstoffe hergestellt werden, zur Herstellung von Polyurethanschäumen
JP5838154B2 (ja) * 2010-04-19 2015-12-24 株式会社ブリヂストン シートパッド用ポリウレタンフォーム
KR20130094688A (ko) * 2010-04-30 2013-08-26 아사히 가라스 가부시키가이샤 폴리옥시알킬렌폴리올, 폴리머 분산 폴리올, 및 연질 폴리우레탄폼, 그리고 이들의 제조 방법
PL3044247T3 (pl) * 2013-09-13 2021-03-08 Dow Global Technologies Llc Pianka poliuretanowa modyfikowana pod względem palności na bazie PI
KR20170134407A (ko) * 2015-04-08 2017-12-06 쉘 인터내셔날 리써취 마트샤피지 비.브이. 폴리올 및 폴리우레탄에 관한 개선
KR101737764B1 (ko) 2015-05-29 2017-05-19 주식회사 빅스 바이오 폴리올을 사용한 미세기공형 폼시트용 폴리우레탄 수지조성물
DK3133097T3 (da) * 2015-08-17 2022-12-19 Evonik Operations Gmbh Fremstilling af blødt polyurethanskum med forbedret hårdhed
KR102761328B1 (ko) 2015-12-21 2025-02-04 쉘 인터내셔날 리써취 마트샤피지 비.브이. 폴리우레탄 폼을 제조하는 방법
US10793692B2 (en) * 2018-10-24 2020-10-06 Covestro Llc Viscoelastic flexible foams comprising hydroxyl-terminated prepolymers
EP3940012A1 (de) * 2020-07-16 2022-01-19 Evonik Operations GmbH Stickstofffreie und stickstoffarme vernetzende additive für kaltblockweichschaum mit verbesserten kompressions- und alterungseigenschaften

Family Cites Families (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2616055B2 (ja) 1988-10-25 1997-06-04 旭硝子株式会社 ポリウレタン弾性フォームの製造方法
WO1990004613A1 (fr) 1988-10-25 1990-05-03 Asahi Glass Company Ltd. Mousse de polyurethane elastique et procede de production
JP2910778B2 (ja) 1990-06-29 1999-06-23 旭硝子株式会社 ポリエーテル類の製造方法
JP2653236B2 (ja) 1990-10-05 1997-09-17 旭硝子株式会社 ポリエーテル化合物の製造方法
JP3128914B2 (ja) 1991-12-18 2001-01-29 東ソー株式会社 アリルクロライドの製造方法
US5437822A (en) 1992-01-29 1995-08-01 Asahi Glass Company Ltd. Method for producing a skin-formed polyurethane foam molded product
JP3344824B2 (ja) 1994-05-20 2002-11-18 三井化学株式会社 軟質高弾性ポリウレタンフォームの製造方法
JP3083235B2 (ja) 1994-04-12 2000-09-04 三井化学株式会社 ポリマーポリオール、その製造方法および軟質高弾性ポリウレタンフォームの製造方法
JP3504789B2 (ja) 1994-12-08 2004-03-08 三井化学株式会社 軟質高弾性ポリウレタン発泡体
JPH08231677A (ja) * 1995-02-28 1996-09-10 Asahi Glass Co Ltd 高弾性ポリウレタンフォームの製造法
JP3680339B2 (ja) * 1995-02-28 2005-08-10 旭硝子株式会社 高弾性ポリウレタンフォームの製造方法
JPH0931153A (ja) * 1995-07-21 1997-02-04 Asahi Glass Co Ltd 高弾性ポリウレタンフォームの製法
JPH0952932A (ja) 1995-08-09 1997-02-25 Sanyo Chem Ind Ltd 軟質ポリウレタンモールドフォームの製造方法
JP3074252B2 (ja) 1995-08-22 2000-08-07 三洋化成工業株式会社 軟質ポリウレタンフォームの製造方法
US5700847A (en) * 1995-12-04 1997-12-23 Arco Chemical Technology, L.P. Molded polyurethane foam with enhanced physical properties
CZ351996A3 (en) 1995-12-07 1997-06-11 Shell Int Research Polyol formulation for preparing flexible polyurethane foam similar to latex
US5668191A (en) 1995-12-21 1997-09-16 Arco Chemical Technology, L.P. One-shot cold molded flexible polyurethane foam from low primary hydroxyl polyols and process for the preparation thereof
US5605939A (en) * 1996-01-26 1997-02-25 Arco Chemical Technology, L.P. Poly(oxypropylene/oxyethylene) random polyols useful in preparing flexible high resilience foam with reduced tendencies toward shrinkage and foam prepared therewith
JPH09263621A (ja) 1996-03-27 1997-10-07 Takeda Chem Ind Ltd 高弾性軟質ポリウレタンフォームの製造方法
JPH10251508A (ja) 1997-03-12 1998-09-22 Sanyo Chem Ind Ltd 軟質ポリウレタンフォームの製造方法
JP3905638B2 (ja) 1997-05-28 2007-04-18 三井化学株式会社 ポリオキシアルキレンポリオール及びその誘導体、並びに、該ポリオキシアルキレンポリオールの製造方法
JPH11140154A (ja) 1997-08-19 1999-05-25 Mitsui Chem Inc 高耐久軟質ポリウレタンフォームの製造方法
JP3703262B2 (ja) 1997-08-19 2005-10-05 三井化学株式会社 ポリオキシアルキレンポリオール、軟質ポリウレタンフォーム及び非発泡ポリウレタンの製造方法
JP3880699B2 (ja) 1997-08-20 2007-02-14 三井化学ポリウレタン株式会社 軟質ポリウレタンフォームの製造方法
JP3297366B2 (ja) * 1997-12-05 2002-07-02 三洋化成工業株式会社 軟質ポリウレタンフォームの製造方法及びポリオール組成物
US6008263A (en) * 1998-04-03 1999-12-28 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
US6051622A (en) * 1998-09-17 2000-04-18 Arco Chemical Technology, L.P. Low resilience, low frequency molded polyurethane foam

Also Published As

Publication number Publication date
DE60120390D1 (de) 2006-07-20
KR100663682B1 (ko) 2007-01-02
DE60120390T2 (de) 2007-05-16
JP5332073B2 (ja) 2013-11-06
CN1261477C (zh) 2006-06-28
US20030045595A1 (en) 2003-03-06
WO2001079323A1 (fr) 2001-10-25
EP1273605A1 (de) 2003-01-08
AU4691101A (en) 2001-10-30
EP1273605B1 (de) 2006-06-07
KR20020095205A (ko) 2002-12-20
CA2406114A1 (en) 2001-10-25
AU772300B2 (en) 2004-04-22
EP1273605A4 (de) 2004-10-20
US6653362B2 (en) 2003-11-25
CN1423669A (zh) 2003-06-11

Similar Documents

Publication Publication Date Title
ATE328925T1 (de) Verfahren zur herstellung von flexiblem polyurethanschaum
ATE430770T1 (de) Polyurethanweichschaumstoff mit geringer rückprallelastizität und herstellungsverfahren dafür
ATE497983T1 (de) Verfahren zur herstellung von polyurethanweichschaumstoffen
DE69924056D1 (de) Polyolmischung zur Herstellung von Polyurethanschaumstoff und daraus hergestellter Schaumstoff
EP0403066A3 (de) CO2-geblasene Integralschäume.
ATE373031T1 (de) Verfahren zur herstellung von emissionsarmen polyurethan-weichschaumstoffen
ATE367411T1 (de) Polyurethanweichschaum und verfahren zur herstellung
ATE341572T1 (de) Polyurethanweichschaum und verfahren zur herstellung
BRPI0400127A (pt) Espuma de poliuretano, semi-flexìvel ou rìgida e processo para sua produção
ATE287421T1 (de) Mit permanentgas geblähte mikrozelluläre polyurethan-elastomere
ES2110647T3 (es) Procedimiento para la obtencion de plasticos celulares de poliuretano.
DE60214937D1 (de) Verfahren zur Herstellung eines polymerdispergierten Polyols
WO2003042268A1 (en) Process for producing synthetic resin foam
DE59800060D1 (de) Verfahren zur Herstellung von Polyurethan-Hartschaumstoffen mit geringer Wärmeleitfähigkeit
BRPI0408677A (pt) espumas de poliuretano de baixa emissão de amina e processo para prepará-las
BR0011066A (pt) Poliol de alto peso molecular, processo de preparação de uma espuma de poliuretano, e, espuma
HUP0303259A2 (hu) Továbbfejlesztett eljárás poliéter-poliolok előállítására
ATE438670T1 (de) Verfahren zur herstellung von polyurethan- weichschaumstoffen
DE69016429D1 (de) Polyisocyanat-Zusammensetzungen sowie ihre Verwendung zur Herstellung von Polyurethan-Weichschaumstoffen.
ATE338781T1 (de) Verfahren zur herstellung von polyurethan- prepolymeren in gegenwart eines katalysators
TW336240B (en) A method of producing rigid foamed plastics containing urethane groups
ATE276307T1 (de) Verfahren zur herstellung von polyurethan- hartschaumstoffen mit verringerter rohdichte
RU2142968C1 (ru) Композиция для получения эластичного пенополиуретана методом формования
DE59405154D1 (de) Verfahren zum Herstellen von Formteilen und Füllungen aus Polyurethan-Hart-und Weichschaumstoffen
ATE115156T1 (de) Verfahren zur herstellung von hochelastischen polyurethan-weichschaumstoffen und deren verwendung als polstermaterial.

Legal Events

Date Code Title Description
RER Ceased as to paragraph 5 lit. 3 law introducing patent treaties