ES2493092T7 - Una piedra pómez granular así como un procedimiento para la producción de una piedra pómez granular - Google Patents

Una piedra pómez granular así como un procedimiento para la producción de una piedra pómez granular Download PDF

Info

Publication number
ES2493092T7
ES2493092T7 ES11706816.3T ES11706816T ES2493092T7 ES 2493092 T7 ES2493092 T7 ES 2493092T7 ES 11706816 T ES11706816 T ES 11706816T ES 2493092 T7 ES2493092 T7 ES 2493092T7
Authority
ES
Spain
Prior art keywords
pumice stone
granular pumice
well
production
sample
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
ES11706816.3T
Other languages
English (en)
Other versions
ES2493092T3 (es
Inventor
Markus Roos
Guido Runkel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rotec Rohstoff-Technik & Co KG GmbH
Rotec Rohstoff Technik & Co KG GmbH
Evonik Operations GmbH
Original Assignee
Rotec Rohstoff-Technik & Co KG GmbH
Rotec Rohstoff Technik & Co KG GmbH
Evonik Degussa GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rotec Rohstoff-Technik & Co KG GmbH, Rotec Rohstoff Technik & Co KG GmbH, Evonik Degussa GmbH filed Critical Rotec Rohstoff-Technik & Co KG GmbH
Application granted granted Critical
Publication of ES2493092T3 publication Critical patent/ES2493092T3/es
Publication of ES2493092T7 publication Critical patent/ES2493092T7/es
Active legal-status Critical Current

Description

imagen1
imagen2
imagen3
imagen4
imagen5
imagen6
E11706816
01-10-2015
Muestra :
I II III
Densidad aparente en fresco del mortero (kg/dm3):
1,27 1,27 1,22
Cuerpo de probeta prisma de mortero L x B x H (mm):
160x80x80 160x80x80 160x80x80
Peso en seco (g)
229 227 223
Densidad aparente en seco (kg/dm3):
0,224 0,221 0,218
Carga de rotura bajo flexión (kN):
0,487 0,408 0,449
Resistencia a la tracción con flexión (N/mm2):
0,143 0,12 0,132
Carga de rotura bajo compresión (kN):
4,39 3,56 4,52
Resistencia a la compresión (N/mm2):
0,7 0,6 0,71
Se midió por un lado el peso en seco de los cuerpos. Éste fue, en el caso del cuerpo de probeta que contenía la espuma silicática, de 229 g, en el caso del cuerpo de probeta que contenía la piedra pómez no tratada, de 227 g y, en el caso de los cuerpos de probeta que contenían la piedra pómez conforme al invento, de 223 g. Esto quiere decir que el cuerpo de probeta que contenía la piedra pómez conforme al invento era el más ligero de todos los cuerpos
5 de probeta.
Por lo demás se midió la densidad aparente en seco. Ésta fue, en el caso del cuerpo de probeta que contenía la espuma silicática de 0,224 kg/dm3, en el caso del cuerpo de probeta que contenía la piedra pómez no tratada, de 0,221 kg/dm3 y en el caso del cuerpo de probeta que contenía la piedra pómez conforme al invento, de 0,218 kg/dm3. Por consiguiente, el cuerpo de probeta que contenía la piedra pómez conforme al invento mostraba la más
10 baja densidad aparente en seco.
Luego se midieron la carga de rotura bajo flexión, la resistencia a la tracción con flexión, la carga de rotura bajo compresión así como la resistencia a la rotura. Los valores medidos han de tomarse en particular de la Tabla.
La carga de rotura de la muestra que contenía la espuma silicática fue de 0,487 kN. Mientras que la carga de rotura de la muestra que contenía la piedra pómez no tratada, con un valor de 0,408 kN, estaba situada manifiestamente
15 por debajo del valor de la muestra de espuma ligera silicática, la muestra que contenía la piedra pómez conforme al invento, con 0,449 kN, tenía un valor medido, que estaba situado aproximadamente en la región de la muestra de espuma ligera silicática.
La resistencia a la tracción con flexión de la muestra de espuma silicática fue de 0,143 N/mm2. También en este caso, la muestra que contenía la piedra pómez no tratada, con un valor de 0,12 N/mm2, estaba situada
20 manifiestamente por debajo, mientras que la muestra que contenía la piedra pómez conforme al invento, con un valor de 0,132 N/mm2, estaba situada de nuevo aproximadamente en la región de la muestra de espuma silicática.
En el caso de la carga de rotura bajo compresión la muestra que contenía la piedra pómez conforme al invento muestra el valor medido más alto con 4,52 kN, mientras que la muestra que contenía la espuma silicática tenía un
8
imagen7

Claims (1)

  1. imagen1
    imagen2
    imagen3
ES11706816.3T 2010-05-26 2011-03-04 Una piedra pómez granular así como un procedimiento para la producción de una piedra pómez granular Active ES2493092T7 (es)