HK27294A - Attrition resistant catalysts, catalyst precursors and catalyst supports - Google Patents

Attrition resistant catalysts, catalyst precursors and catalyst supports

Info

Publication number
HK27294A
HK27294A HK272/94A HK27294A HK27294A HK 27294 A HK27294 A HK 27294A HK 272/94 A HK272/94 A HK 272/94A HK 27294 A HK27294 A HK 27294A HK 27294 A HK27294 A HK 27294A
Authority
HK
Hong Kong
Prior art keywords
catalyst
sio2
particles
oxide
precursor
Prior art date
Application number
HK272/94A
Other languages
German (de)
English (en)
Inventor
Horacio Enrique Bergna
Original Assignee
E.I. Du Pont De Nemours And Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by E.I. Du Pont De Nemours And Company filed Critical E.I. Du Pont De Nemours And Company
Publication of HK27294A publication Critical patent/HK27294A/en

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
    • B01J23/002—Mixed oxides other than spinels, e.g. perovskite
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
    • B01J27/14—Phosphorus; Compounds thereof
    • B01J27/186—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
    • B01J27/195—Phosphorus; Compounds thereof with arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium with vanadium, niobium or tantalum
    • B01J27/198—Vanadium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
    • B01J37/0027—Powdering
    • B01J37/0045—Drying a slurry, e.g. spray drying
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/08—Heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2523/00—Constitutive chemical elements of heterogeneous catalysts

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Catalysts (AREA)
  • Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
  • Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
  • Furan Compounds (AREA)

Claims (12)

  1. Un procédé pour la production de particules de catalyseur ou de support de catalyseur résistantes à l'attrition comportant une couche superficielle riche en oxyde, le procédé consistant à :
    (a) former une suspension comprenant des particules de catalyseur, précurseur de catalyseur ou support de catalyseur dispersées dans une solution d'un soluté, les quantités relatives des particules et du précurseur d'oxyde étant choisies de telle manière que le poids de l'oxyde formé dans les étapes (b) et/ou (c) soit d'environ 3 à 15 % du poids total des particules et de l'oxyde formé ;
    (b) sécher par atomisation la suspension pour former des microsphères poreuses de particules de catalyseur, précurseur de catalyseur ou support de catalyseur résistantes à l'attrition ; et
    (c) calciner les microsphères séchées par atomisation, à une température élevée qui est inférieure à la température qui est sensiblement préjudiciable au catalyseur ou support de catalyseur, pour produire des particules de catalyseur ou de support de catalyseur résistantes à l'attrition comportant ladite couche superficielle riche en oxyde ; caractérisé en ce que le soluté de l'étape (a) comprend un précurseur d'oxyde dont la taille de particules n'est pas supérieure à 5 nm.
  2. Procédé de la revendication 1, dans lequel ladite couche superficielle riche en oxyde consiste en SiO₂ et la solution de soluté est une solution aqueuse d'acide silicique équivalent à un poids de SiO₂ ne dépassant pas 6 % en poids.
  3. Procédé de la revendication 2, dans lequel l'acide silicique est un acide polysilicique.
  4. Un procédé pour préparer des catalyseurs à l'oxyde de vanadium/phosphore résistants à l'attrition, qui consiste à :
    (a) former une suspension de particules de précurseur de catalyseur à l'oxyde de vanadium/phosphore dispersées dans une solution aqueuse d'acide silicique (c'est-à-dire un précurseur de SiO₂) équivalent à une concentration de SiO₂ ne dépassant pas environ 6 pour cent en poids, les quantités relatives des particules et de l'acide silicique étant choisies de telle manière que le poids de SiO₂ soit d'environ 3 à 15 % du poids total des particules et du SiO₂ dans le catalyseur résultant ;
    (b) sécher par atomisation la suspension pour former des microsphères poreuses ;
    (c) calciner les microsphères séchées par atomisation, à une température élevée qui est inférieure à la température qui est sensiblement précudiciable au catalyseur, pour produire des particules de catalyseur à l'oxyde de vanadium/phosphore contenant SiO₂ résistantes à l'attrition, comportant ladite couche superficielle riche en oxyde ; caractérisé en ce que la taille des particules de précurseur de SiO₂ dans l'étape (a) n'est pas supérieure à 5 nm.
  5. Particules de catalyseur ou support de catalyseur résistantes à l'attrition comportant une couche superficielle riche en oxyde et préparées par le procédé de la revendication 1.
  6. Particules de catalyseur ou support de catalyseur résistantes à l'attrition comportant une couche superficielle riche en oxyde et préparées par le procédé de la revendication 3.
  7. Particules de catalyseur à l'oxyde de vanadium/phosphore contenant SiO₂ résistantes à l'attrition comportant une couche superficielle riche en oxyde et préparées par le procédé de la revendication 4.
  8. Un catalyseur résistant à l'attrition qui comprend des microsphères poreuses comportant une enveloppe séchée par atomisation et calcinée comprenant du SiO₂, dans lequel le SiO₂ contenu dans l'enveloppe constitue 3 à 15 % en poids du poids total du catalyseur ; ledit catalyseur étant un catalyseur au molybdène à plusieurs composants et étant préparé par un procédé tel que revendiqué dans la revendication 1.
  9. Un catalyseur résistant à l'attrition qui comprend des microsphères poreuses ayant une taille de particules de 0,5 à 10 µm et ayant été formé avec un revêtement séché par atomisation et calciné comprenant du SiO₂, ledit catalyseur étant un catalyseur à l'oxyde de vanadium/phosphore et le SiO₂ contenu dans le revêtement constituant 10 à 15 % en poids du poids total du catalyseur, et étant préparé par un procédé tel que revendiqué dans la revendication 4.
  10. Procédé pour la production d'anhydride maléique par l'oxydation d'un hydrocarbure en présence du catalyseur de la revendication 7.
  11. Procédé de la revendication 9, dans lequel l'hydrocarbure est le n-butane qui est mélangé avec de l'air.
  12. Procédé pour la production d'acrylonitrile à partir de propylène et d'ammoniac en présence du catalyseur de la revendication 8.
HK272/94A 1985-11-27 1994-03-24 Attrition resistant catalysts, catalyst precursors and catalyst supports HK27294A (en)