JPH01177363A - 缶用光沢ドライ鍍金鋼板 - Google Patents

缶用光沢ドライ鍍金鋼板

Info

Publication number
JPH01177363A
JPH01177363A JP62336859A JP33685987A JPH01177363A JP H01177363 A JPH01177363 A JP H01177363A JP 62336859 A JP62336859 A JP 62336859A JP 33685987 A JP33685987 A JP 33685987A JP H01177363 A JPH01177363 A JP H01177363A
Authority
JP
Japan
Prior art keywords
dry
steel sheet
plating
cans
plated steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP62336859A
Other languages
English (en)
Inventor
Hiroshi Kagechika
影近　博
Tadahiko Mishima
三島　忠彦
Yoshinori Yomura
吉則 余村
Hiroshi Ishikawa
博司 石川
Naoyuki Oba
直幸 大庭
Yoshihiko Yasue
良彦 安江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Engineering Corp
Original Assignee
NKK Corp
Nippon Kokan Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NKK Corp, Nippon Kokan Ltd filed Critical NKK Corp
Priority to JP62336859A priority Critical patent/JPH01177363A/ja
Priority to US07/281,032 priority patent/US4897316A/en
Priority to CA000585522A priority patent/CA1315497C/en
Priority to EP88120936A priority patent/EP0322655A3/en
Publication of JPH01177363A publication Critical patent/JPH01177363A/ja
Priority to US07/404,841 priority patent/US4940522A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［産業上の利用分野］ この発明は、食缶や飲料缶その他の印刷缶用の材料に関
するものである。
［従来技術］ 食缶や飲料缶等缶詰に使われる缶、或は菓子や乾物等を
湿気から守るために使われる缶容器などは、錫鍍金鋼板
やクロム鍍金鋼板或はアルミニウムシート等の材料で作
られているが、殆どの缶容器は、その外側に印刷が施さ
れ外観を美しく仕上げられている。特に、贈り物、土産
物等の缶容器では、そのデザイン、色彩、色調によって
需要が左右されると言っても過言では無いほど、外観の
美しさは重要である。
この外観の美しさを得るために、印刷にあたっては、先
ず、ホワイトコーティングによって金属板特有の色相を
隠蔽し、その上に色刷りを施す方法と、逆に、金属の色
相や光沢を活し透明色インキで印刷される場合とがある
。しかし、どちらの場合も、金属板表面の鮮映性が要求
され、鮮映性が高いほど印刷色が鮮明で仕上がりが美し
く、鮮映性が低いとくすんだ色にしか仕上がらない。
しかしながら、従来の缶用鍍金鋼板では、上記の鮮映性
にもう一歩の不満を残しており、これを解消するには、
素地の表面性状、鍍金被膜形成のコントロール等の検討
を必要とするが、未だその技術は開発されていない。
一方、缶用付以外では、例えば、装飾用の鍍金では光沢
クロム鍍金、光沢ニッケル鍍金等のような方法もあるが
、これらは適正な鍍金条件の範囲が狭く、下地処理にも
複雑な工程を必要とし、安価で量産を求められる缶用材
には適用できない。
又、素地の粗さに注目し、これを平滑化するために塗料
を塗布しその上に金属のドライ鍍金を施す方法（特開昭
６Ｏ−６７６５３）なども提案されているが、電気溶接
ができなかったり、量産に不向きだったりして缶用材に
は向かない。
［発明が解決しようとする問題点１ 以上のように、従来の缶用の鍍金鋼板では、印刷により
美しい外観を得る為には鮮映性に不足し、従来の光沢鍍
金法は安価でなく量産には適さない。
このような問題を解決するために、この発明はなされた
もので、鮮映性の高い安価な缶用の光沢鍍金鋼板の提供
を目的とするものである。
［問題点を解決するための手段］ この発明は、鍍金鋼板において、表面粗度が中心線平均
粗さで０．１０μｍ以下の鋼板の表面にドライ鍍金層を
有することを特徴とする缶用光沢ドライ鍍金鋼板である
。
発明者らは、圧延技術の進歩により、近年、表面粗度の
小さな冷延鋼板が製造されるようになったことに着目し
て、鍍金原板の表面粗度と鍍金面の粗度、粗度と光沢、
光沢と鮮映性等の関係を調べた。その結果、原板表面粗
度の大きく異なる場合は、粗度の中心線平均粗さＲａが
小さくなる程、光沢、鮮映性ともに向上し、Ｒａが小さ
な範囲では、同じような光沢を呈する表面でもＲａが異
なったり、鮮映性が異なったりすることが判った。しか
し、同時に、これらの関係の中で、原板の表面粗度と鍍
金面の鮮映性との間には、相関が見られたことから、更
に、鍍金処理の種類別に検討を行った。その結果、平滑
な原板にドライ鍍金を施した鍍金鋼板は、鮮映性が格段
に優れていることが判明した。
この関係を第１図に示す。
原板の表面粗度は触針式粗度計でＪＩＳ　　Ｂ１２Ｏ３
のＲａで測定した。鮮映性は一定の間隔において描かれ
た白黒の縞模様を有する板を鮮映性を測定する試験板を
介して反射させ、反射された白黒の縞模様の識別の難易
により評価した。評価点は市販の鏡を１０としＲａが０
．２μｍの冷延鋼板を１とし、識別の難易に応じて１０
段階の感応評価をした。ここでは評価点が高い程鮮映性
が優れていることになる。第１図に原板の表面粗度と鮮
映性の関係を示す、横軸は原板の表面粗度、縦軸は鮮映
性を示す。図において実線で示されているのが鍍金面、
点線で示されているのが冷延鋼板面であり、原板のＲａ
が０．１μｍより小さくなると、急に鮮映性が高まって
くる。そしてその傾向は、原板面よりもドライ鍍金面の
方が遥かに顕著である。電気鍍金の場合は、上記したよ
うな明瞭な関係は見られず、原板のＲａが０．　１μｍ
より小さくなっても、鍍金面の鮮映性は左程向上しない
、従来の缶用鋼板では、Ｒａが０．１２〜３．０μｍの
冷延鋼板が使われており、しかも電気鍍金処理が施され
ていたために、鮮映性の低いものしか得られなかったの
である。
本発明のドライ鍍金層の組成は従来がら缶用鍍金鋼板あ
るいは缶用材料に使用されるＳｎ、Ｃｒ、Ｎｉ、ＡＩや
光沢電気鍍金において鍍金層の組成として用いられてい
る各種の単一金属あるいは合金のみならず広く単一金属
あるいは合金を選ぶことが出来る。本発明のドライ鍍金
層の厚さは０．０１μｍ未満では十分な鮮映性が得られ
ない。また鍍金層の厚さが増加すれば鮮映性が良好にな
るが、経済性の観点から５μｍを超えると実用的でない
、従って鍍金層の厚さは０．０１μｍ〜５μｍとするの
が好ましい。又かかるドライ鍍金層を形成する方法とし
てはＣＶＤあるいはイオンブレーティング、真空蒸着、
スパッター法等通常用いられているドライ鍍金方法を用
いることが出来る。
［作用］ 本発明において鋼板上に形成されたドライ鍍金層は鍍金
粒子が細かく被膜が滑らかであるので、光の乱反射が従
来の技術に比べて極めて少なくなり鮮明性に優れる。
［発明の実施例コ 鈑の表面粗度を種々に変えた鋼板に真空蒸着、イオンブ
レーティング、電気鍍金の三種のうち何れかの鍍金を施
し、鮮映性を調べた。ここにおいて真空蒸着処理は以下
の条件で行った。
真空度＋　６１０−６Ｔｏｒｒ 基板温度：２００℃ 蒸発方法：エレクトロンビーム加熱 基板−るつぼ距離：５０ｃｍ 又、イオンブレーティング処理は以下の条件で行った。
真空度：　６１０−６Ｔｏｒｒ 基板温度＝２００℃ 蒸発方法；エレクトロンビーム加熱 基板−るつぼ距離：５０ｃｍ バイアス電圧：　５００ｖ イオン化電流＝２５ｖ また電気鍍金はＳｎ鍍金及びＣｒ鍍金を行い、Ｓｎ鍍金
は通常のフェロスタン浴により鍍金を行った。
その結果を第２図に示す、第２図において、各印は次の
鍍金を表す。
◇・・・Ａ１を１．５μｍ真空蒸着したもの。
◆・・・ＡＩを０．１μｍイオンブレーティングしたも
の。
Δ・・・Ｓｎ０．５μｍ真空蒸着したもの。
ム・・・Ｃｒ　　Ｏ，０５μｍ５μｍ真空蒸もの。
○・・・Ｓｎ０．５μｍ電気鍍金したもの。
・・・・Ｃｒ　　Ｏ，０５μｍ電気鍍金したもの。
真空蒸着或はイオンブレーティングによるドライ鍍金を
施したものは、原板の表面粗度Ｒａが０．１μｍ以下に
なると鮮映性が顕著に向上してくるが、従来の電気鍍金
を施したものは、Ｓｎ鍍金、Ｃｒ鍍金ともに、ドライ鍍
金に比してその向上は僅かである。
従来の缶用鍍金鋼板は原板のＲａが０．１２μｍ乃至３
．０μｍであるので、鮮映性２程度である。これに比し
、Ｒａが０．１μｍ以下の原板にドライ鍍金を施す本発
明では、鮮映性は４〜６と顕著に向上している。
［発明の効果］ 以上のように、この発明によれば、表面粗度が一定値以
下の原板に、ドライ鍍金を施しであるので、従来にない
高い鮮映性を持つ鍍金鋼板となっており、これに印刷を
施すと、鮮明性の高い美しい外観が得られる。しかも、
何ら複雑な工程を経ること無く安価に製造される。缶製
品に豊かな彩りを与え、需要者の楽しみを穣成するこの
発明の効果は大きい。
【図面の簡単な説明】
第１図はこの発明を説明するための原板粗度と鮮映性と
の関係を示す図、第２図は発明の実施例における原板粗
度と鮮映性の関係図である。

Claims (1)

    【特許請求の範囲】
  1. 　鍍金鋼板において、表面粗度が中心線平均粗さで０．
    １０μｍ以下の鋼板の表面にドライ鍍金層を有すること
    を特徴とする缶用光沢ドライ鍍金鋼板。
JP62336859A 1987-12-29 1987-12-29 缶用光沢ドライ鍍金鋼板 Pending JPH01177363A (ja)