JPH01200512A - 難燃性電気絶縁組成物 - Google Patents
難燃性電気絶縁組成物Info
- Publication number
- JPH01200512A JPH01200512A JP2470188A JP2470188A JPH01200512A JP H01200512 A JPH01200512 A JP H01200512A JP 2470188 A JP2470188 A JP 2470188A JP 2470188 A JP2470188 A JP 2470188A JP H01200512 A JPH01200512 A JP H01200512A
- Authority
- JP
- Japan
- Prior art keywords
- niobium
- inorganic
- fire
- niobium compound
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、燃焼時に有毒なハロゲン系ガスを発生しない
難燃性電気絶縁組成物、特に、電線・ケーブルの絶縁材
料やシース材料への適用に好適な難燃性電気絶縁組成物
に関するものである。
難燃性電気絶縁組成物、特に、電線・ケーブルの絶縁材
料やシース材料への適用に好適な難燃性電気絶縁組成物
に関するものである。
電線・ケーブルの絶縁材料やシース材料としては電気絶
縁性に優れたポリオレフィンが多く用いられてきている
。最近の趨勢として原子力発電所用電線・ケーブル、車
両用電線・ケーブル、船舶用電線・ケーブルに垂直トレ
イ燃焼試験レベルの高度の難燃性が要望されるようにな
ってきた。
縁性に優れたポリオレフィンが多く用いられてきている
。最近の趨勢として原子力発電所用電線・ケーブル、車
両用電線・ケーブル、船舶用電線・ケーブルに垂直トレ
イ燃焼試験レベルの高度の難燃性が要望されるようにな
ってきた。
ポリオレフィンを難燃化する方法としてはハロゲン含有
化合物等を混和する方法が一般に採用されてきている。
化合物等を混和する方法が一般に採用されてきている。
しかし、これらは燃焼時多量の煙を発生し、機器への腐
食性、人体への有害性等が問題になっている。特に、最
近は安全面からこの様なハロゲン系ガスを発生しないこ
とが要望されるようになってきている。
食性、人体への有害性等が問題になっている。特に、最
近は安全面からこの様なハロゲン系ガスを発生しないこ
とが要望されるようになってきている。
この様な情勢を踏まえ、発煙性、有毒性の非常に少ない
無機系難燃剤が注目されるようになってきた。
無機系難燃剤が注目されるようになってきた。
しかしながら、無機系難燃剤は難燃効果が小さいため、
単にポリマに混和しただけでは燃焼時に溶融滴下すると
いうドリップ現象がみられ、高度の難燃性を付与するこ
とは難しい。なお、高度の難燃性を付与するためには無
機系難燃剤を多量加えることも有効であるが、得られる
絶縁体やシースの引張特性の低下を招いたり、押出加工
性が低下するという問題がある。
単にポリマに混和しただけでは燃焼時に溶融滴下すると
いうドリップ現象がみられ、高度の難燃性を付与するこ
とは難しい。なお、高度の難燃性を付与するためには無
機系難燃剤を多量加えることも有効であるが、得られる
絶縁体やシースの引張特性の低下を招いたり、押出加工
性が低下するという問題がある。
本発明は上記に基いてなされたものであり、従来の問題
点を解消し、燃焼時にドリップを防止でき、難燃性を大
幅に向上し、垂直トレイ燃焼試験レベルに合格する高度
の難燃性を付与できると共に、有毒なハロゲン系ガスを
発生しない難燃性電気絶縁組成物の提供を目的とするも
のである。
点を解消し、燃焼時にドリップを防止でき、難燃性を大
幅に向上し、垂直トレイ燃焼試験レベルに合格する高度
の難燃性を付与できると共に、有毒なハロゲン系ガスを
発生しない難燃性電気絶縁組成物の提供を目的とするも
のである。
〔課題を解決するための手段及び作用）本発明の上記目
的はポリオレフィン１００重量部に対して、無機系難燃
剤を５０〜３００重量部およびニオブ又は無機ニオブ化
合物あるいは有機ニオブ化合物を０．５重量部以上含有
することを特徴とする難燃性電気絶縁組成物によって達
成される。
的はポリオレフィン１００重量部に対して、無機系難燃
剤を５０〜３００重量部およびニオブ又は無機ニオブ化
合物あるいは有機ニオブ化合物を０．５重量部以上含有
することを特徴とする難燃性電気絶縁組成物によって達
成される。
本発明において、ポリオレフィンとしては、エチレンプ
ロピレンコポリマ、エチレンプロビレコンジェンターポ
リマ、ポリエチレン、エチレン酢酸ビニルコポリマ、エ
チレンエチルアクリレートコポリマ、エチレンブテンコ
ポリマ、エチレンブテンジェンターポリマといったもの
があげられ、これらは単独使用または２種以上の併用が
可能である。
ロピレンコポリマ、エチレンプロビレコンジェンターポ
リマ、ポリエチレン、エチレン酢酸ビニルコポリマ、エ
チレンエチルアクリレートコポリマ、エチレンブテンコ
ポリマ、エチレンブテンジェンターポリマといったもの
があげられ、これらは単独使用または２種以上の併用が
可能である。
本発明において無機系難燃剤としては、水酸化アルミニ
ウム、水酸化マグネシウム、塩基性炭酸マグネシウム、
水酸化カルシウム、ハイドロタルサイト類等があげられ
る。無機系難燃剤の含有量は、ポリオレフィン１００重
量部に対して５０〜３００重量部の範囲とする必要があ
り、５０重量部未満では目的とする難燃性を付与できず
、３００重量部を越えると加工性が著しく低下して押出
成形が困難になる。
ウム、水酸化マグネシウム、塩基性炭酸マグネシウム、
水酸化カルシウム、ハイドロタルサイト類等があげられ
る。無機系難燃剤の含有量は、ポリオレフィン１００重
量部に対して５０〜３００重量部の範囲とする必要があ
り、５０重量部未満では目的とする難燃性を付与できず
、３００重量部を越えると加工性が著しく低下して押出
成形が困難になる。
本発明においては、無機系難燃剤に加えてニオブ又は無
機ニオブ化合物あるいは有機ニオブ化合物を併用するこ
とにより、燃焼時のドリップを防止でき、ＩＩ燃性を大
幅に向上できることが見出された。
機ニオブ化合物あるいは有機ニオブ化合物を併用するこ
とにより、燃焼時のドリップを防止でき、ＩＩ燃性を大
幅に向上できることが見出された。
無機ニオブ化合物として、二酸化ニオブ、三酸化ニオブ
、五酸化ニオブ、ニオブ酸リチウム、ニオブ酸ナトリウ
ム、硼化ニオブ、珪化ニオブ等がある。
、五酸化ニオブ、ニオブ酸リチウム、ニオブ酸ナトリウ
ム、硼化ニオブ、珪化ニオブ等がある。
有機ニオブ化合物としては、ペンタメトキシニオブ、ペ
ンタエトキシニオブ、ペンタ−１−プロポキシニオブ、
ペンクーｎ−ブトキシニオブ等がある。
ンタエトキシニオブ、ペンタ−１−プロポキシニオブ、
ペンクーｎ−ブトキシニオブ等がある。
これら、ニオブ、無機ニオブ化合物、有機ニオブ化合物
はポリオレフィン１００重量部に対して０．５重量部以
上配合する必要があり、０．５重量部未満では燃焼時の
ドリップを防止できず、難燃性が不充分となる。
はポリオレフィン１００重量部に対して０．５重量部以
上配合する必要があり、０．５重量部未満では燃焼時の
ドリップを防止できず、難燃性が不充分となる。
本発明においては、上記成分に加えて架橋剤、酸化防止
剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。架
橋剤としては、ジクミルパーオキサイド、３−ビス（ｔ
−ブチルパーオキシイソプロビル）べ、ンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、硫黄、エチレンジメタアクリレート、ジアリルフタレ
ート、ｐ−キノンジオキンム等を併用してもよい。また
、電子線等の電離性放射線による架橋の場合は、架橋助
剤としてトリメチロールプロパントリメリテート、トリ
アリルイソシアヌレート等の反応性のモノマを添加する
のが一般的である。酸化防止剤としでは、フェニル−α
−ナフチルアミン、Ｎ。
剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。架
橋剤としては、ジクミルパーオキサイド、３−ビス（ｔ
−ブチルパーオキシイソプロビル）べ、ンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、硫黄、エチレンジメタアクリレート、ジアリルフタレ
ート、ｐ−キノンジオキンム等を併用してもよい。また
、電子線等の電離性放射線による架橋の場合は、架橋助
剤としてトリメチロールプロパントリメリテート、トリ
アリルイソシアヌレート等の反応性のモノマを添加する
のが一般的である。酸化防止剤としでは、フェニル−α
−ナフチルアミン、Ｎ。
Ｎ −ジ−β−ナフチル−ｐ−フェニレンジアミン等の
アミン系酸化防止剤、２．６−ジーＬ−ブチル−４−メ
チルフェノール、ヒンダードフェノール等のフェノール
系酸化防止剤があげられる。
アミン系酸化防止剤、２．６−ジーＬ−ブチル−４−メ
チルフェノール、ヒンダードフェノール等のフェノール
系酸化防止剤があげられる。
本発明の実施例について説明する。但し、本発明は本実
施例にのみ限られるものではない。
施例にのみ限られるものではない。
第１表に示すような配合にしたがって各種成分を１００
″Ｃに保持された６インチロールに投入してロール混練
を行い、混練後１２０ ’Ｃに保持された４０ｍ／ｍ押
出１１（Ｌ／Ｄ＝２５）を用い、外径５．３鵬の絶縁線
心を３本撚合せた゛外周に２．０閣の厚さで押出被覆し
た。なお、実施例−１，４゜５および比較例−１につい
ては押出被覆に続いて１３ｋｇ／ｃｄの水蒸気雰囲気中
に３分間保持して架橋した。
″Ｃに保持された６インチロールに投入してロール混練
を行い、混練後１２０ ’Ｃに保持された４０ｍ／ｍ押
出１１（Ｌ／Ｄ＝２５）を用い、外径５．３鵬の絶縁線
心を３本撚合せた゛外周に２．０閣の厚さで押出被覆し
た。なお、実施例−１，４゜５および比較例−１につい
ては押出被覆に続いて１３ｋｇ／ｃｄの水蒸気雰囲気中
に３分間保持して架橋した。
各個で作製した絶縁電線についての評価結果は第１表の
下欄に示した通りである。
下欄に示した通りである。
なお、難燃性評価は次に基いて行った。長さ２ｍのケー
ブルを垂直に８本並べ、下から７万ＢＴＵの炎を２０分
間当て、自己消炎すれば合格であり、自己消炎せず全焼
するものは不合格である。
ブルを垂直に８本並べ、下から７万ＢＴＵの炎を２０分
間当て、自己消炎すれば合格であり、自己消炎せず全焼
するものは不合格である。
第１表からも明らかな通り、本発明に係わる実施例−１
〜６ではいずれも難燃性に合格し、押出加工性に優れて
いる。これに対し無機系Ｈ燃剤の含有量が規定値以下の
比較例−１では難燃性が不合格であり、規定値以上の比
較例−２では押出性が悪く成形不可能であった。また、
ニオブや無機ニオブ化合物あるいは有機ニオブ化合物の
含有量が０．５重量部以上という規定値以下の比較例−
３，４，５ではドリップが生じて難燃性が不合格となる
。
〜６ではいずれも難燃性に合格し、押出加工性に優れて
いる。これに対し無機系Ｈ燃剤の含有量が規定値以下の
比較例−１では難燃性が不合格であり、規定値以上の比
較例−２では押出性が悪く成形不可能であった。また、
ニオブや無機ニオブ化合物あるいは有機ニオブ化合物の
含有量が０．５重量部以上という規定値以下の比較例−
３，４，５ではドリップが生じて難燃性が不合格となる
。
以上説明してきた通り、本発明はポリオレフィン１００
重量部に対して無機系難燃剤５０〜３００重量部、およ
びニオブ又は無機ニオブ化合物あるいは有機ニオブ化合
物を０．５重量部以上含有することを特徴とする難燃性
電気絶縁組成物により、良好な押出加工性を維持しなが
ら、燃焼時のドリップを防止でき、高度の難燃性を付与
でき、しかも燃焼時に有毒なハロゲン系ガスを発生しな
いようになる。
重量部に対して無機系難燃剤５０〜３００重量部、およ
びニオブ又は無機ニオブ化合物あるいは有機ニオブ化合
物を０．５重量部以上含有することを特徴とする難燃性
電気絶縁組成物により、良好な押出加工性を維持しなが
ら、燃焼時のドリップを防止でき、高度の難燃性を付与
でき、しかも燃焼時に有毒なハロゲン系ガスを発生しな
いようになる。
Claims (1)
- （１）ポリオレフィン１００重量部に対して、無機系難
燃剤５０〜３００重量部およびニオブ又は無機ニオブ化
合物あるいは有機ニオブ化合物を０．５重量部以上含有
することを特徴とする難燃性電気絶縁組成物。