JPH02248496A - 潤滑グリース - Google Patents

潤滑グリース

Info

Publication number
JPH02248496A
JPH02248496A JP1071473A JP7147389A JPH02248496A JP H02248496 A JPH02248496 A JP H02248496A JP 1071473 A JP1071473 A JP 1071473A JP 7147389 A JP7147389 A JP 7147389A JP H02248496 A JPH02248496 A JP H02248496A
Authority
JP
Japan
Prior art keywords
grease
weight
base oil
vacuum
lubricity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP1071473A
Other languages
English (en)
Other versions
JPH0575797B2 (ja
Inventor
Kenjiro Obara
小原　建治郎
Kazuyuki Nakamura
和幸 中村
Yoshio Murakami
村上　義夫
Takao Soda
曽田　孝雄
Toshihiro Kanie
蟹江　敏広
Tamio Akata
民生 赤田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Matsumura Oil Research Corp
Japan Atomic Energy Agency
Original Assignee
Matsumura Oil Research Corp
Japan Atomic Energy Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsumura Oil Research Corp, Japan Atomic Energy Research Institute filed Critical Matsumura Oil Research Corp
Priority to JP1071473A priority Critical patent/JPH02248496A/ja
Priority to US07/496,700 priority patent/US5013466A/en
Publication of JPH02248496A publication Critical patent/JPH02248496A/ja
Publication of JPH0575797B2 publication Critical patent/JPH0575797B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［産業上の利用分野〕 本発明は、高温、高真空環境下において優れた潤滑性を
有するグリースに関する。より詳細に述べると、本発明
はアルキル置換テトラフェニルエーテルを基油とし、ベ
ントナイトを増稠剤として、二硫化モリブデン、二硫化
タングステンの少な（とも１種の固体潤滑剤を配合して
成る潤滑グリースに関する。
〔従来の技術〕
高温、高真空下で使用される機器類の駆動部分は、多数
の歯車、軸受等の機械要素から構成され、これらの円滑
な動作には潤滑剤の使用が不可欠である。
従来、高温・高真空用の潤滑剤としては、二硫化モリブ
デンに代表される固体潤滑剤を金属表面にコーティング
しての使用、および石油系潤滑油を基油とした石けん基
グリースと固体潤滑剤を組合せたグリースの使用が一般
的であった。
〔発明が解決しようとする課題〕
しかしながら、固体潤滑剤では潤滑膜と基材との密着強
度が比較的弱いため、高応力化の使用では剥離し易いと
いう欠点がある。また石油系潤滑油を基油とした石けん
基グリースと固体潤滑剤を組合せたグリースは、蒸発損
失、劣化損失、これらによる系内汚染が問題となる。
〔課題を解決するための手段〕
これらの問題を解決するためには、高温・高真空下で長
期間安定な潤滑性を保ち、かつ蒸発損失、劣化損失、こ
れらによる系内汚染を引き起こさないことが重要となる
。本発明は、以上述べた点を考慮して高温・高真空下で
優れた潤滑性を有するグリースの開発を目的としてなさ
れたものである。
このような条件下て優れた潤滑性を示すグリースを考え
る場合、基油は主に耐熱性、真空特性に、増稠剤、固体
潤滑剤は潤滑性に影響を及ぼし、それらを向上させるこ
とが必要である。また同時に、基油、増稠剤および固体
潤滑剤から形成されるグリース特有のゲル構造が高温・
高真空環境下で安定であることが重要である。
本発明者らは、まずアルキル置換テトラフェニルエーテ
ル、ベントナイト系増稠剤、二硫化モリブデンから成る
グリースを調製し、圧力１０−’Ｔｏｒｒ。
温度１００℃、１５０°Ｃでの損耗量を調べた結果、従
来の鉱油系グリースに比べて極めて少ない値を示し、試
験後の状態も安定であることを見いだした。
次に上記グリースについて、ＡＳＴＭ　Ｄ　２７１４．
３７０４に基づ（Ｂｌｏｃｋ　ｏｎ　Ｒｉｎｇ試験機を
用いて回転数１１００ｒｐ　、温度１５０°Ｃ１圧力０
．０１Ｔｏｒｒでの耐荷重能を調べたところ、鉱油系グ
リース、および鉱油系グリースに固体潤滑剤を配合した
グリース以上の潤滑性を有するということを見いだした
。同様に、回転数１１００ｒｐ＋、温度１５０℃、圧力
０．０１Ｔｏｒｒ、荷重５００ボンドでの耐久性の試験
を実施しこところ、従来の金属表面にコーティングした
二硫化モリブデンの約２倍の寿命時間を有することを見
いだした。
またアルキル置換テトラフェニルエーテルの置換基数が
１〜４個、置換基の炭素原子数が６〜２０個の場合は、
いずれも同様の挙動を示し、高温・高真空下で非常に優
れた潤滑性を有するグリースを与えることを見いだした
。
すなわち本発明は、上記の油を基油とし、これらにベン
トナイト系増稠剤、固体潤滑剤を組合せたときに優れた
耐熱・耐酸化性、真空特性、潤滑性を有するグリースが
得られ、高真空下でかつ高温下で使用される機器の潤滑
に優れた性能を発揮することを確認したことに基づく。
従って、本発明の包括的な目的は、アルキル置換テトラ
フェニルエーテルを基油とし、ベントナイト系増稠剤、
および二硫化モリブデン、二硫化タングステンを固体潤
滑剤として用いた高温・高真空下で優れた潤滑性を有す
る潤滑グリースを提供することである。しかして、本願
の発明に係る潤滑グリースは次の成分： （イ）下記成分から成る基油５５重量％乃至９０重量％ アルキル置換テトラフェニルエーテル、ただし置換基数
が１乃至４個、置換基の炭素原子数が６個乃至２０個で
あ、る。
（ロ）ベントナイト系増稠剤５重量％乃至２５重量％ （ハ）粒子径０．１μ■乃至２０μ−の二硫化モリブデ
ン、二硫化タングステンより成る群から選ばれる少なく
とも１種の固体潤滑剤５重量％乃至２０重量％ から成る。
〔作用〕
上記の本発明に係る潤滑グリースにおいて、得られたグ
リースに対して基油は約５５〜９０重量％、好ましくは
約６５〜７５重量％の割合で用いられる。
基油には、一般に蒸発抑止および劣化防止の目的で５重
量％以下の酸化防止剤を添加することが好ましく、基油
に溶解し、通常の保存状態で長期間変質しない任意のも
のであれば、フェノール系、アミン系、燐系、硫黄系の
いずれもが使用できる。
好ましくはフェノール系、硫黄系の酸化防止剤である。
使用できるフェノール系酸化防止剤の例として、オクタ
デシル３（３，５−ジ−ｔ−ブチル−４−ヒドロキシフ
ェニル）プロピオネート、２．２”−メチレンビス（４
−エチル−６−トブチルフエノール）　、１．３．５−
トリメチル−２，４，６−）リス（３，５−ジー【−ブ
チル−４ヒドロキシベンジル）ベンゼンがある。使用で
きる硫黄系酸化防止剤の例として、ジラウリルチオジプ
ロピオネート、ジステアリルチオジプロピオネート、２
−２°−チオジエチルビス［３−（３，５−ジ−ｔ−ブ
チル−４−ヒドロキシフェニル）プロピオネート１があ
る。
またアルキル置換テトラフェニルエーテル、もしくは酸
化防止剤を添加したアルキル置換テトラフェニルエーテ
ルにベントナイト系増稠剤を配合すると、高温・高真空
下で安定なゲル構造を形成し、適正な稠度を持ち、かつ
優れた潤滑性を有するグリースが得られることが明らか
となった。この場合、ベントナイト系増稠剤の配合量は
得られたグリースに対して約５〜２５重量％、好ましく
は約１０〜１７重量％である。一般に使用されているベ
ントナイト系増稠剤は、安定なゲル構造を形成するため
に若干量のゲル化補助剤を必要としたが、本発明におい
ては揮発性のゲル化補助剤を必要としないベントナイト
系増稠剤を使用し、真空特性および潤滑性の向上を見い
だした。
ゲル化補助剤を必要としないベントナイト系増稠剤とし
て、例えばベント（Ｂｅｎｔｏｎｅ：商標名）Ｓ［１−
１１同Ｓロー２、バラゲル（ＢＡＲＡＧｔｌＬ：商標名
）　３０００〔以上エヌ・エル・インダストリーズ社（
ＮＬ　Ｉｎｄｕｓｅｒｉｅｓ）製〕が使用できる。
潤滑グリースとして、最も大切な潤滑性に大きな影響を
与える成分である固体潤滑剤、は、粒子径０．１〜２０
μ騙の二硫化モリブデン、二硫化タングステンより成る
群から選ばれる微粒子の粉末である。使用できる二硫化
モリブデンの例として、モリコー）　（ＭＯＬＹＫＯＴ
Ｅ：商標名）マイクロサイズパウダー、同Ｚパウダー〔
以上ダウ・コーニング社（ＤＯＷ−Ｃｏｒｎｉｎｇ）製
〕およびモリサルファイド（ＭＯＬＹＳＵＬＦＩＤｔｈ
商標名）テクニカルグレード、同テクニカル・ファイン
グレード、同スーパー・ファイングレード〔以上フライ
マックス・モリブデン社（ＣＬＹＭＡＸ　ＭＯＬＹＢＤ
ＥＮＵＭ）製〕がある。使用できる二硫化タングステン
の例として、ミクロンパウダーＡ２ミクロンパウダーＢ
（日本潤滑剤社製）がある、これらの固体潤滑剤の量は
、得られたグリースに対して５〜２０重量％、好ましく
は１０〜１５重量％である。
〔実施例〕
上記本発明のグリースは、常法に従って容易に製造する
ことができる。例えば、本発明のグリースは次のように
して製造することができる。
即ち、所定量の基油と所定量の増稠剤および所定量の固
体潤滑剤を加え攪拌・混合する。混合は、常用のミキサ
ー、例えばダブルプラネタリ−ミキサーを用いて行なう
ことができる。混合は、通常室温〜ｉ００’ｃで行なわ
れるが、真空中での使用を考慮し、脱ガス操作を兼ねて
７０〜１００°Ｃの昇温下で行なうことが好ましい。混
合時間は、１〜３時間で十分である。
得られた混合物を次に常法に従って均質混合処理する。
この均質’ｔＨ合は、例えばマイコロイダーホぞジナイ
ザーあるいはロール処理によって行なうことができる。
均質混合温度および時間は、５０〜１２０’Ｃおよび１
０〜６０分である。この段階で基油と増稠剤間にゲル構
造が形成され、所望のグリースが得られる。
かくして、前記組成の成分の配合によって、後記実施例
で例証されるように、高温・高真空下での損耗量を抑え
、かつ優れた潤滑性を有する潤滑グリースが得られる。
以下、本発明に係るグリース４品（試作品１〜４）を試
作し、高温・真空中でのＩ員耗量、耐荷重能、耐久性に
ついて、一般に高温・真空中で優れた性能を示すと言わ
れ、広く使用されている従来品（比較品１〜３）との比
較試験を実施した詳細を説明する。それぞれの組成を第
１表にまとめて示した。ただし、これらの実施例は本発
明を説明するだめのものであって、本発明を限定するも
のではない。
（実施例１） ７４０ｇ　（Ｄアルキル置換テトラフェニルエーテル、
ただし炭素原子数１６個から成る置換基の数が２個のも
のを主成分とする置換基数１〜４個の油に３０ｇのオク
タデシル３（３，５−シートブチル−４−ヒドロキソフ
ェニル）プロピオネートを溶解させた基油と１６０ｇの
ベントナイト系増稠剤および１００ｇの二硫化モリブデ
ンを７０″Ｃで３時間攪拌・混合し、その後マイコロイ
ダー処理を行って、９５０ｇのグリースを得た（後記第
１表に示す試作品ｌとする）。
試作品ｌを高さ１７■鰯、内径８８．１ａｓ＋のステン
レス製シャーレに厚みが６−−になるように採り、真空
チャンバー中のヒーター上に静置し、圧力９Ｘ１０−’
Ｔｏｒｒｓ温度１００℃、１５０°Ｃでの２４．４８．
９６時間後の損耗量を測定した。得られた結果を後記第
２表に示す。
またＡＳＴＭ　ｏ　２７１４．３７０４の規格に基づく
旧ｏｃｋｏｎ　Ｒムｎｇ試験機を用いて、圧力０．０１
ＴｏｒｒＳｍ度１５０°Ｃ１回転数１００ｒｐ−で１分
間に２０ポンドの割合で荷重を加えた場合の耐荷重能を
測定した。試料はリング表面に約０．１ｇを均一に塗布
し、耐荷重は異常トルク上昇の発生で判定した。得られ
た結果を後記第３表に示す。
さらに同様の操作で、圧力０．０１Ｔｏｒｒ、温度１５
０℃、回転数１００ｒρ−１荷重５００ポンドの条件で
の耐久性を調べるため、焼付きまでの寿命時間を測定し
た。得られた結果を後記第４表に示す。
（実施例２） 実施例１の操作を用いて、試作品３の基油を炭素原子敞
１６個から成る置換基の数が１個のものを主成分とする
置換様数１〜３個のアルキル置換テトラフェニルエーテ
ルに代えたグリース（後記第１表に示す試作品２とする
）、試作品ｌの固体潤滑剤を二硫化タングステンに代え
たグリース（後記第１表に示す試作品３とする）、およ
び試作品４の固体潤滑剤を二硫化タングステンに代えた
グリース（後記第１表に示す試作品４とする）を調製し
た。また市販グリースとして、鉱油系グリース（後記第
１表に示す比較品１とする）、鉱油系グリースに固体潤
滑剤を配合したグリース（後記第１表に示す比較品２と
する）各選定した。これらを用いて実施例１と同様に測
定した結果を第２〜４表にまとめて示す。
（実施例３） 二硫化モリブデンを潤滑性試験用リングにコーティング
したもの（後記第１表に示す比較品３とする）について
、実施例１と同様の操作で焼付きまでの寿命時間を測定
した。得られた結果を第４表に示す。
第２表から明らかなように、本発明に係るグリースは、
一般に使用されている鉱油系グリースと比較して損耗量
が少なく、真空容器内の汚染を最小限に抑える結果を示
し、試験後の状態も良好であり優れた耐熱性、真空特性
を有していることを示している。
第３表の結果は、本発明に係るグリースは、市販グリー
スと比較して優れた潤滑性を有していることを示してい
る。この理由としては必ずしも明らかではないが、優れ
た耐熱性、真空特性を有する基油、増稠剤と適度な粒子
径、添加量の固体潤滑剤、さらにそれらから形成される
特殊なゲル構造が高温・高真空下において安定であった
ためと推察される。
また第４表の結果は、本発明に係るグリースは、金属表
面にコーティングした固体潤滑剤と比較して長期間安定
な潤滑性を保つことを示している。
グリース潤滑の場合、潤滑給脂が可能であるが、固体潤
滑剤は剥離等を起こすと再び回復しないため長期間の安
定性には問題がある。
以上の比較品と対比して、試作品１〜４のグリースは、
高温・真空下で潤滑性に優れていることが判る。
第１表 第２表 試験条件；試料をシャーレに厚さ６ｍｍに採り、圧力９
　Ｘ　１０−　”Ｔｏｒｒの真空チャンバー中に静置第
３表 第４表 試験条件： 温度１５０゛Ｃ１圧力０．０ＩＴｏｒｒ。
１００ｒｐ鴎、荷重２０ボンド／ｓｉｎ回転数 試験条件：温度１５０°Ｃ１圧力０．０ＩＴｏｒｒ、回
転数１１００ｒｐ、　荷重５００ポンド 〔発明の効果〕 本発明によれば、耐熱性、真空特性に優れる基油と特定
の増稠剤および特定の固体潤滑剤を組合セることにより
、高温・真空下で優れた潤滑性を示す潤滑グリースを得
ることができる。また、本発明に係るアルキル置換テト
ラフェニルエーテルは、その構造からも耐放射線性に優
れていることが明らかである。
従って、本発明の潤滑グリースは、高温・真空下で使用
される機器類の駆動部分、例えば歯車、軸受等のグリー
スとして優れた性能を発揮することができる。

Claims (1)

    【特許請求の範囲】
  1. （１）次の成分： （イ）下記成分から成る基油５５重量％乃至９０重量％ アルキル置換テトラフェニルエーテル、 ただし置換基数が１乃至４個、置換基の 炭素原子数が６個乃至２０個である。 （ロ）ベントナイト系増稠剤５重量％乃至２５重量％ （ハ）粒子径０．１μｍ乃至２０μｍの二硫化モリブデ
    ン、二硫化タングステンより成る群から 選ばれる少なくとも１種の固体潤滑剤５重 量％乃至２０重量％ から成ることを特徴とする潤滑グリース。
JP1071473A 1989-03-23 1989-03-23 潤滑グリース Granted JPH02248496A (ja)