JPH025087B2 - - Google Patents

Info

Publication number
JPH025087B2
JPH025087B2 JP61123132A JP12313286A JPH025087B2 JP H025087 B2 JPH025087 B2 JP H025087B2 JP 61123132 A JP61123132 A JP 61123132A JP 12313286 A JP12313286 A JP 12313286A JP H025087 B2 JPH025087 B2 JP H025087B2
Authority
JP
Japan
Prior art keywords
bone
calcium phosphate
bone grafting
grafting material
particle size
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP61123132A
Other languages
English (en)
Other versions
JPS62281953A (ja
Inventor
Makoto Ogiso
Tetsuro Ogawa
Kenji Ichizuka
Masahide Inoe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pentax Corp
Original Assignee
Asahi Kogaku Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Kogaku Kogyo Co Ltd filed Critical Asahi Kogaku Kogyo Co Ltd
Priority to JP61123132A priority Critical patent/JPS62281953A/ja
Priority to CA000537654A priority patent/CA1340503C/en
Priority to GB8712130A priority patent/GB2192389B/en
Priority to DE19873717818 priority patent/DE3717818A1/de
Priority to FR878707499A priority patent/FR2607008B1/fr
Publication of JPS62281953A publication Critical patent/JPS62281953A/ja
Priority to US07/373,708 priority patent/US5064436A/en
Publication of JPH025087B2 publication Critical patent/JPH025087B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】 「技術分野」 本発明は、例えば口腔外科、整形外科などにお
いて、骨腫瘍、歯槽膿ろうなどで手術した後の骨
の欠損部を埋めるために使用される骨補填材およ
びその製造方法に関する。
「従来技術およびその問題点」 従来、かかる骨補填材としては、コバルトーク
ロム、チタン、ステンレスなどの金属や、アルミ
ナ、ジルコニア、三リン酸カルシウム、ハイドロ
オキシアパタイト、リン酸カルシウム系ガラスな
どのセラミツクスや、シリコン樹脂などの高分子
材料や、カーボンなどを材質とし、これらをブロ
ツク状、顆粒状などに形成したものが使用されて
いる。
この中でも、三リン酸カルシウム、ハイドロオ
キシアパタイト、リン酸カルシウム系ガラスなど
のリン酸カルシウム系材料は、骨と同様な成分か
らなるので生体親和性が極めて高く、近年、最も
注目されている材料である。
しかしながら、リン酸カルシウム系材料からな
る骨補填材を用いた場合においても、本来は異物
なので、充填した骨補填材の生体組織に近い部分
においては、新生骨との融着がなされるが、生体
組織から離れた部分においては、いわゆるカプセ
ル反応により、繊維性組織で取囲まれて軟質化す
ることが多かつた。このように、リン酸カルシウ
ム系材料を用いた場合でも、治癒力の不活発な部
位においては、カプセル反応による組織不適合性
が生じるという問題点があつた。
また、特開昭60−21763号には、孔径10〜100μ
ｍの連続気孔を有し、少なくとも100Kg／cm2の曲
げ強度をもつ水酸アパタイト焼結体からなる人工
骨材料が提案されている。
しかしながら、上記の人工骨材料においては、
少なくとも100Kg／cm2の曲げ強度を付与するため
に、気孔率を高めることができず、連続気孔は極
めて少ないものとなり、カプセル反応を有効に防
止することはできなかつた。
「発明の目的」 本発明の目的は、例えば生体組織から離れた治
癒力の不活発な部位においても、新生骨との融着
がなされ、カプセル反応が起こらないようにした
骨補填材料およびその製造方法を提供することに
ある。
「発明の構成」 本発明の骨補填材は、平均孔径0.01〜10μｍの
連続気孔を有し、かつその気孔が均一に分散して
いて、顆粒表面の100μm2範囲内に少なくとも１
つ以上存在するリン酸カルシウム系多孔質顆粒か
らなることを特徴とする。
また、本発明の骨補填材の製造方法は、平均粒
径0.01〜10μｍの有機可燃物粒子と平均粒径0.05
〜1μｍのリン酸カルシウム系粉末とを混合して
造粒し、この造粒物を焼成することを特徴とす
る。
生体内に取込まれた骨補填材に対するカプセル
反応は、骨補填材に付着したマクロフアージがこ
れを異物と判断することによつて誘起される。本
発明者らは、この作用をよく研究した結果、マク
ロフアージが付着した部位において、体液が流通
している状態である場合には、マクロフアージに
よつて異物と判断されることはなく、カプセル反
応を防止できることがわかつた。
本発明は、骨補填材に連続気孔を形成すること
により、骨補填材内部に体液を流通させ、カプセ
ル反応を防止して、新生骨との融着を促進できる
という事実に着眼してなされたものである。この
場合、マクロフアージにより異物と判断されない
ためには、連続気孔の孔径が重要であり、具体的
にはマクロフアージに比べて大きすぎない程度の
孔径とすることが必要となる。
このため、本発明では、平均孔径0.01〜10μｍ
の連続気孔を有するものが採用される。この場
合、平均孔径が0.01μｍ未満では、製造困難とな
ると共に、体液が流通しにくくなるのでカプセル
反応防止効果が充分に得られない。また、平均孔
径が10μｍを超えると、マクロフアージの大きさ
に比べて孔径が大きすぎるため、マクロフアージ
が付着した部位における体液流通がなされず、カ
プセル反応防止効果が充分に得られない。
本発明の好ましい態様においては、顆粒表面の
100μm2の範囲内に少なくとも一つ以上の連続気
孔を有する。このように、連続気孔が所定密度で
配列されていることにより、マクロフアージが付
着した箇所に連続気孔が位置する確率が高めら
れ、カプセル反応をより効果的に防止できる。
また、本発明の好ましい態様においては、連続
気孔の平均孔径は0.01〜1μｍとされる。平均孔径
を0.01〜1μｍとすることにより、マクロフアージ
が孔の上に乗つて付着する状態となり、カプセル
反応防止効果がより高められる。
さらに、本発明の好ましい態様においては、気
孔率が60〜90％とされる。気孔率が60％未満で
は、連続気孔になりにくく、体液の流通が充分に
なされない。一方、気孔率が90％を超えると、強
度が低下してくずれやすくなる傾向がある。
本発明において、骨補填材の顆粒の形状は、球
形、不定形など特に限定されない。また、顆粒の
大きさは、充填操作を容易にするため、平均径が
0.1〜１mmとなるようにすることが好ましい。顆
粒の平均径が0.1mm未満では体液によつて流され
やすくなり、１mmを超えると顆粒の間に隙間がで
きすぎて新生骨との融着がなされにくくなる。
本発明で使用するリン酸カルシウム系材料とし
ては、公知の各種のものが使用可能であるが、特
にハイドロオキシアパタイト、三リン酸カルシウ
ムなどが好ましい。原料としてのリン酸カルシウ
ム粉末は、例えば平均粒径１〜10μｍ程度のもの
が使用され、これをボールミルなどで粉砕して平
均粒径0.05〜1μｍ程度に調製すればよい。
また、有機可燃物粒子としては、ポリスチレ
ン、ポリビニルアルコール、ポリプロピレンなど
の合成樹脂ビーズや、セルロース、動物繊維など
を細かく切断したものなどが採用される。有機可
燃物粒子の平均粒径は、前述したような平均孔径
の連続気孔を形成するため、0.01〜10μｍとされ
る。
なお、上記のリン酸カルシウム系材料と有機可
燃物粒子とを混合して造粒するに際して、必要に
応じて結合剤として水、ポリビニルアルコールな
どを添加してもよい。
原料の配合組成は、リン酸カルシウム系粉末
100重量部に対して有機可燃物粒子30〜70重量％
が好ましい。有機可燃物粒子が30重量％未満では
充分な気孔率が得られず、70重量％を超えると気
孔率が大きくなりすぎて強度が低下する。
造粒方法としては、例えばリン酸カルシウム粉
末と有機可燃物粒子とを混合してスラリーとし、
これを乾燥してブロツク化し、さらに粉砕する方
法や、パン型造粒機などを用いて造粒する方法な
どが採用できる。
焼成条件は、特に限定されないが、例えば室温
から600℃程度まで50℃／Hr前後で昇温して有機
可燃物粒子を焼失させた後、さらに1200℃程度ま
で100℃／Hr前後で昇温し、1200℃程度で８時間
ほど保持することにより、焼結体を得ることがで
きる。
この骨補填材の使用に際しては、例えば骨補填
材を滅菌した後、滅菌ずみの生理食塩水と混合し
て骨欠損部に充填すればよい。これにより、骨補
填材と周囲の骨組織とが新生骨によつて融着し、
骨欠損部を治癒することができる。
「発明の実施例」 合成ハイドロオキシアパタイト粉末（粒径１〜
10μｍ）600ｇと、ポリスチレンビーズ「フアイ
ンパール」（商品名、住友化学工業株式会社製、
平均粒径6μｍ）400ｇとに、蒸留水2000mlを添加
し、ボールミルにて24時間混合分散し、平均粒径
0.6μｍのハイドロオキシアパタイトのスラリーを
得た。
シヤーレに上記スラリーを入れ、熱風循環式乾
燥機にて100℃で24時間乾燥し、乾燥ブロツクと
した。
この乾燥ブロツクを乳鉢にて粉砕して100〜
1000μｍの顆粒とし、電気炉にて焼成した。焼成
条件は、室温から600℃まで50℃／Hrで昇温し、
さらに1200℃まで100℃／Hrで昇温し、1200℃で
８時間保持した後、200℃／Hrの速度で降温する
ことによつて行なつた。
こうして得られたハイドロオキシアパタイトの
顆粒を、ステンレス製メツシユを用いて、粒径
300〜500μｍの範囲に調製した。
この骨補填材は、平均孔径4μｍ程度の連続気
孔を有するものであつた。この骨補填材の100倍
の電子顕微鏡写真を第１図に、1000倍の電子顕微
鏡写真を第２図に、10000倍の電子顕微鏡写真を
第３図に示す。
「発明の効果」 以上説明したように、本発明によれば、平均孔
径0.01〜10μｍの連続気孔を有するリン酸カルシ
ウム系多孔質顆粒からなるので、マクロフアージ
が付着した部位における体液流通がなされ、マク
ロフアージによる異物判断がなされないので、カ
プセル反応を効果的に防止でき、新生骨との融着
を良好にして、治癒を早めることができる。
【図面の簡単な説明】
第１図は本発明の実施例で得られた骨補填材の
粒子構造を示す100倍の電子顕微鏡写真、第２図
は同粒子構造を示す1000倍の電子顕微鏡写真、第
３図は同粒子構造を示す10000倍の電子顕微鏡写
真である。

Claims (1)

  1. 【特許請求の範囲】 １ 平均孔径0.01〜10μｍの連続気孔を有し、か
    つその気孔が均一に分散していて、顆粒表面の
    100μm2の範囲内に少なくとも１つ以上存在する
    リン酸カルシウム系多孔質顆粒からなることを特
    徴とする骨補填材。 ２ 平均粒径0.01〜10μｍの有機可燃物粒子と平
    均粒径0.05〜1μｍのリン酸カルシウム粉末とを混
    合して造粒し、この造粒物を焼成することを特徴
    とする骨補填材の製造方法。
JP61123132A 1986-05-28 1986-05-28 骨補填材 Granted JPS62281953A (ja)