JPH04231425A - 溶融アルミニウム濾過用セラミックスフィルター - Google Patents
溶融アルミニウム濾過用セラミックスフィルターInfo
- Publication number
- JPH04231425A JPH04231425A JP2415095A JP41509590A JPH04231425A JP H04231425 A JPH04231425 A JP H04231425A JP 2415095 A JP2415095 A JP 2415095A JP 41509590 A JP41509590 A JP 41509590A JP H04231425 A JPH04231425 A JP H04231425A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- ceramic filter
- molten aluminum
- parts
- bending strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【０００１】
【産業上の利用分野】本発明はアルミニウムまたはアル
ミニウム合金溶湯中に混入する非金属介在物等を濾過す
るために使用するセラミックスフィルターに関するもの
である。
ミニウム合金溶湯中に混入する非金属介在物等を濾過す
るために使用するセラミックスフィルターに関するもの
である。
【０００２】
【従来の技術およびその問題点】一般に、アルミニウム
またはアルミニウム合金溶湯中には非金属介在物等の異
物が混入しており、鋳造時にハードスポット等の加工上
のトラブルの原因となるため、これら異物は鋳造に先立
って除去し、鋳造品の品質を高め、後加工工程トラブル
を回避するようにしている。そのために従来から溶湯の
濾過処理が施されている。この溶湯の濾過に使用される
装置としては種々の形式のものがあるが、特公昭５２−
２２３２７号公報に記載されているように、ＳｉＯ２、
Ｂ２Ｏ３等の無機物質を結合材として用いて焼結したチ
ューブタイプのフィルターが一般的である。
またはアルミニウム合金溶湯中には非金属介在物等の異
物が混入しており、鋳造時にハードスポット等の加工上
のトラブルの原因となるため、これら異物は鋳造に先立
って除去し、鋳造品の品質を高め、後加工工程トラブル
を回避するようにしている。そのために従来から溶湯の
濾過処理が施されている。この溶湯の濾過に使用される
装置としては種々の形式のものがあるが、特公昭５２−
２２３２７号公報に記載されているように、ＳｉＯ２、
Ｂ２Ｏ３等の無機物質を結合材として用いて焼結したチ
ューブタイプのフィルターが一般的である。
【０００３】しかしながら、このような従来のフィルタ
ーでは熱間曲げ強度（８００℃）が３０ｋｇｆ／ｃｍ２
と低いため、高純度アルミニウム等のように溶湯温度が
高い溶湯の濾過には、濾過中にフィルターが圧壊する恐
れがあるため、不適であり、問題とされていた。
ーでは熱間曲げ強度（８００℃）が３０ｋｇｆ／ｃｍ２
と低いため、高純度アルミニウム等のように溶湯温度が
高い溶湯の濾過には、濾過中にフィルターが圧壊する恐
れがあるため、不適であり、問題とされていた。
【０００４】本発明は熱間曲げ強度が高く、溶湯温度の
高い特に高純度アルミニウム溶湯の濾過に極めて好適な
セラミックスフィルターを提供することを目的とするも
のである。
高い特に高純度アルミニウム溶湯の濾過に極めて好適な
セラミックスフィルターを提供することを目的とするも
のである。
【０００５】
【問題点を解決するための手段】本発明は、電融アルミ
ナ骨材粒子１００重量部に対し、３〜２５重量部の結合
材を配合してなり、該結合材が２〜６重量％のＳｉＯ２
，１〜１０重量％のＭｇＯ，１〜８重量％のＴｉＯ２，
残部Ａｌ２Ｏ３から構成したセラミックスフィルターに
より、前記問題点を解決したものである。
ナ骨材粒子１００重量部に対し、３〜２５重量部の結合
材を配合してなり、該結合材が２〜６重量％のＳｉＯ２
，１〜１０重量％のＭｇＯ，１〜８重量％のＴｉＯ２，
残部Ａｌ２Ｏ３から構成したセラミックスフィルターに
より、前記問題点を解決したものである。
【０００６】
【作用】本発明ではアルミナ骨材粒子１００重量部に対
して３〜２５重量部の結合材を配合することにより熱間
強度を高めかつ気孔率を適正値に保持し、結合材として
含有させるＳｉＯ２、ＭｇＯ、ＴｉＯ２、Ａｌ２Ｏ３の
配合割合を適正値とすることにより熱間曲げ強度を高め
ることができる。なお、結合材の配合比率が骨材粒子に
対し、３重量部未満では強度が保てず、逆に２５重量部
を超えると気孔率が低下して濾過量が不足する。好まし
くは結合材の配合比率を骨材粒子に対し、１０重量部〜
２２重量部とする。
して３〜２５重量部の結合材を配合することにより熱間
強度を高めかつ気孔率を適正値に保持し、結合材として
含有させるＳｉＯ２、ＭｇＯ、ＴｉＯ２、Ａｌ２Ｏ３の
配合割合を適正値とすることにより熱間曲げ強度を高め
ることができる。なお、結合材の配合比率が骨材粒子に
対し、３重量部未満では強度が保てず、逆に２５重量部
を超えると気孔率が低下して濾過量が不足する。好まし
くは結合材の配合比率を骨材粒子に対し、１０重量部〜
２２重量部とする。
【０００７】
【実施例】電融アルミナＷＡ骨材＃８０重量％、第１表
に示した組成の結合材２０重量％および穀物粉４重量％
とを混練し、所定形状に成形し、これを乾燥後、１６０
０〜１６５０℃で焼成し、フィルター試料とした。これ
ら試料を常温、および熱間（８００℃）で曲げ強度を測
定した。
に示した組成の結合材２０重量％および穀物粉４重量％
とを混練し、所定形状に成形し、これを乾燥後、１６０
０〜１６５０℃で焼成し、フィルター試料とした。これ
ら試料を常温、および熱間（８００℃）で曲げ強度を測
定した。
【０００８】曲げ強度は２点支持１点荷重方式で支持ス
パン９０ｍｍで行い、熱間曲げは試料を８００℃、２０
分間保持した雰囲気温度設定用電気炉中で行った。それ
らの結果を表１に併せて記載する。
パン９０ｍｍで行い、熱間曲げは試料を８００℃、２０
分間保持した雰囲気温度設定用電気炉中で行った。それ
らの結果を表１に併せて記載する。
【０００９】
【表１】
【００１０】表１において、試料１〜４番より、ＳｉＯ
２が多くなると常温での曲げ強度は向上するものの８０
０℃における熱間曲げ強度が低下することが分かる。ま
た、試料５〜８番より、ＭｇＯが０では熱間強度は低い
が、１０重量％以下の添加で熱間強度を向上させること
が分かる。しかし、１０重量％を超えるＭｇＯの添加は
気孔率を下げ、濾過量不足の可能性があり、実用的では
なくなる。さらに、試料９〜１４番より、ＴｉＯ２は３
〜５重量％で常温、熱間曲げ強度とも極大値を持つこと
が分かる。
２が多くなると常温での曲げ強度は向上するものの８０
０℃における熱間曲げ強度が低下することが分かる。ま
た、試料５〜８番より、ＭｇＯが０では熱間強度は低い
が、１０重量％以下の添加で熱間強度を向上させること
が分かる。しかし、１０重量％を超えるＭｇＯの添加は
気孔率を下げ、濾過量不足の可能性があり、実用的では
なくなる。さらに、試料９〜１４番より、ＴｉＯ２は３
〜５重量％で常温、熱間曲げ強度とも極大値を持つこと
が分かる。
【００１１】表１の結果より、本発明実施例組成のフィ
ルターでは、特に熱間曲げ強度がいずれも１００ｋｇｆ
／ｃｍ２以上の値を示すことが分かる。
ルターでは、特に熱間曲げ強度がいずれも１００ｋｇｆ
／ｃｍ２以上の値を示すことが分かる。
【００１２】
【発明の効果】以上のような本発明によれば、８００℃
熱間曲げ強度が１００ｋｇｆ／ｃｍ２以上と極めて大き
く、従って高純度アルミニウム溶湯等の濾過に使用して
もフィルターの破壊の可能性がより少なくなり、耐久性
および安全性に優れたセラミックスフィルターが得られ
る。
熱間曲げ強度が１００ｋｇｆ／ｃｍ２以上と極めて大き
く、従って高純度アルミニウム溶湯等の濾過に使用して
もフィルターの破壊の可能性がより少なくなり、耐久性
および安全性に優れたセラミックスフィルターが得られ
る。
Claims (1)
- 【請求項１】 溶融アルミニウム濾過に使用するセラ
ミックスフィルターにおいて、電融アルミナ骨材粒子１
００重量部に対し、３〜２５重量部の結合材を配合して
なり、該結合材が２〜６重量％のＳｉＯ２，１〜１０重
量％のＭｇＯ，１〜８重量％のＴｉＯ２，残部Ａｌ２Ｏ
３からなることを特徴とする溶融アルミニウム濾過用セ
ラミックスフィルター。