JPH0442875A - 軽量無機質製品の製造方法 - Google Patents
軽量無機質製品の製造方法Info
- Publication number
- JPH0442875A JPH0442875A JP2149658A JP14965890A JPH0442875A JP H0442875 A JPH0442875 A JP H0442875A JP 2149658 A JP2149658 A JP 2149658A JP 14965890 A JP14965890 A JP 14965890A JP H0442875 A JPH0442875 A JP H0442875A
- Authority
- JP
- Japan
- Prior art keywords
- lightweight
- inorganic
- cement
- fly ash
- specific gravity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は軽量無機質製品の製造方法に関し、詳しくは
、無機質軽量発泡骨材を添加した常法配合における軽量
無機質製品の製造方法の改良に関する。
、無機質軽量発泡骨材を添加した常法配合における軽量
無機質製品の製造方法の改良に関する。
従来、無機質建材の軽量化をはかるため、セメント、珪
砂よりなるセメント配合物にパーライト、プラスバルー
ン等の無機質軽量発泡骨材を添加し、この添加物により
軽量化を達成することが種々行われている。
砂よりなるセメント配合物にパーライト、プラスバルー
ン等の無機質軽量発泡骨材を添加し、この添加物により
軽量化を達成することが種々行われている。
ところで、上記無機質軽量発泡骨材は添加すればするほ
ど軽量化は促進されるがこれと共に強度の低下も生し、
やがては建材として実用出来ない程度にまで強度が低下
する欠点があった。
ど軽量化は促進されるがこれと共に強度の低下も生し、
やがては建材として実用出来ない程度にまで強度が低下
する欠点があった。
従って、無機質建材における強度と軽量化は相反する関
係となり、建材の用途に応し何れかを犠牲としなければ
ならない問題があった。
係となり、建材の用途に応し何れかを犠牲としなければ
ならない問題があった。
（発明が解決しようとする課題〕
この発明は上記問題に鑑み、軽量化が達成できると同時
に強度の低下も防止し得る軽量無機質製品の製造方法を
提供することを目的としてなされたものである。
に強度の低下も防止し得る軽量無機質製品の製造方法を
提供することを目的としてなされたものである。
即ち、この発明の軽量無機質製品の製造方法はセメント
と珪砂との配合比が略１：１とされ、これに対し必要な
補強繊維、充填材を添加しさらに無機質軽量発泡骨材を
添加してなる常法による軽量無機質製品のセメント配合
において、無機質軽量発泡骨材の添加量の内そのｌ／４
〜１／２量をかさ比重０．５以下のフライアッシュに置
換することを特徴とするものである。
と珪砂との配合比が略１：１とされ、これに対し必要な
補強繊維、充填材を添加しさらに無機質軽量発泡骨材を
添加してなる常法による軽量無機質製品のセメント配合
において、無機質軽量発泡骨材の添加量の内そのｌ／４
〜１／２量をかさ比重０．５以下のフライアッシュに置
換することを特徴とするものである。
この発明において前提とするセメント配合そのものは従
来常法により実施されているものでこの点に特徴は無い
。
来常法により実施されているものでこの点に特徴は無い
。
この発明において、軽量化に使用する無機質軽量発泡骨
材としてはパーライト、シラスバルーン等の天然発泡軽
量骨材の他、人工軽量発泡骨材がある。
材としてはパーライト、シラスバルーン等の天然発泡軽
量骨材の他、人工軽量発泡骨材がある。
この発明において、軽量発泡骨材の添加量において、そ
の添加量の１／４〜１／２をかさ比重０．５以下のフラ
イアッシュに置換する。
の添加量の１／４〜１／２をかさ比重０．５以下のフラ
イアッシュに置換する。
このフライアッシュは５ｉ（ｈの他ＣａＯも多量に含む
ため反応性が高く、従ってパーライト等の粒径の大きい
発泡骨材の間隙においてセメント粒子と良く反応し発泡
骨材を取り囲む状態で強固なマトリックスを形成する。
ため反応性が高く、従ってパーライト等の粒径の大きい
発泡骨材の間隙においてセメント粒子と良く反応し発泡
骨材を取り囲む状態で強固なマトリックスを形成する。
一方、このフライアッシュとしてかさ比″１０．５以下
のものを用いれば、製品全体の軽量化にも寄与する。
のものを用いれば、製品全体の軽量化にも寄与する。
この発明においてフライアッシュを軽量発泡骨材の添加
量の１／４〜１／２Ｍ換するのは、１／４より少ない置
換量の場合は十分な建材強度が得られないからであり、
また１／２より多い置換量の場合はフライアッシュの水
和反応で生しる水和物質により返ってセメントマトリッ
クスの強度が損なわれるからである。
量の１／４〜１／２Ｍ換するのは、１／４より少ない置
換量の場合は十分な建材強度が得られないからであり、
また１／２より多い置換量の場合はフライアッシュの水
和反応で生しる水和物質により返ってセメントマトリッ
クスの強度が損なわれるからである。
次にこの発明の詳細な説明する。
軽量発泡骨材としてかさ比重０．２１のパーライトを、
またシリカ源としてかさ比重０．３７のフライアッシュ
を用意し、表１の配合として厚さ５Ｎ縦横３００１の試
験片を賦形し、オートクレーブにて養生した。
またシリカ源としてかさ比重０．３７のフライアッシュ
を用意し、表１の配合として厚さ５Ｎ縦横３００１の試
験片を賦形し、オートクレーブにて養生した。
試験片について比重及び強度試験を行ったところ表１下
欄に示す結果となった。
欄に示す結果となった。
表 １
骨材を使用して軽量無機質製品を製造する場合において
、フライアッシュの反応特性を利用しパーライトの軽量
化を損なうことなく製品の強度を量配合表中の数字は重
量％を示す。
、フライアッシュの反応特性を利用しパーライトの軽量
化を損なうことなく製品の強度を量配合表中の数字は重
量％を示す。
曲げ強度の単位はｋｇ／ｃｊ
表１より明らかなように、本願発明による場合、比重が
１．０２であるのに係わらずこれと時開等の比重である
比較例１に比べ強度が向上しているのが確認された。
１．０２であるのに係わらずこれと時開等の比重である
比較例１に比べ強度が向上しているのが確認された。
また比較例２．３より明らかなように比重に比し本願発
明は強度が優れることが判明した。
明は強度が優れることが判明した。
以上説明しように、この発明は無機質軽量発泡手続補正
書は劃 平成２年 ９月 １゜ ２゜ ３゜ 事件の表示 平成２年特許願第１４９６５８号 発明の名称 軽量無機質製品の製造方法 補正をする者 事件との間係 特許出願人 住所 大阪市浪速区敷津東−丁目２番４７号４、代理人
〒６６５ 住所 兵庫県宝塚市千種１丁目１２番３号６、補正の対
象 （１） 明細書の発明の詳細な説明の欄７、補正の内
容
書は劃 平成２年 ９月 １゜ ２゜ ３゜ 事件の表示 平成２年特許願第１４９６５８号 発明の名称 軽量無機質製品の製造方法 補正をする者 事件との間係 特許出願人 住所 大阪市浪速区敷津東−丁目２番４７号４、代理人
〒６６５ 住所 兵庫県宝塚市千種１丁目１２番３号６、補正の対
象 （１） 明細書の発明の詳細な説明の欄７、補正の内
容
Claims (1)
- （１）セメントと珪砂との配合比が略１：１とされ、こ
れに対し必要な補強繊維、充填材を添加しさらに無機質
軽量発泡骨材を添加してなる常法による軽量無機質製品
のセメント配合において、無機質軽量発泡骨材の添加量
の内その１／４〜１／２量をかさ比重０．５以下のフラ
イアッシュに置換することを特徴とする軽量無機質製品
の製造方法。