JPH0547623B2 - - Google Patents
Info
- Publication number
- JPH0547623B2 JPH0547623B2 JP15295383A JP15295383A JPH0547623B2 JP H0547623 B2 JPH0547623 B2 JP H0547623B2 JP 15295383 A JP15295383 A JP 15295383A JP 15295383 A JP15295383 A JP 15295383A JP H0547623 B2 JPH0547623 B2 JP H0547623B2
- Authority
- JP
- Japan
- Prior art keywords
- gold
- aluminum
- coating
- purple
- platinum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
本発明は、指輪、ネツクレス、バンド、ブレス
レツト、時計側など、貴金属又は、貴金属合金を
使用した装飾用材料の製造方法に関するものであ
る。
レツト、時計側など、貴金属又は、貴金属合金を
使用した装飾用材料の製造方法に関するものであ
る。
従来、装飾用銀、白金、金またはそれらの合金
上に紫色を呈する金とアルミニウムから成る被膜
をめつきにより形成していたが、この被膜は紫色
しか示さないという欠点を有していた。
上に紫色を呈する金とアルミニウムから成る被膜
をめつきにより形成していたが、この被膜は紫色
しか示さないという欠点を有していた。
本発明は上記の欠点を解消せんがためになされ
たものであり、表面に赤紫色の金−アルミニウム
合金酸化被膜を有する種々の形状の装飾用材料の
製造方法を提供せんとするものである。
たものであり、表面に赤紫色の金−アルミニウム
合金酸化被膜を有する種々の形状の装飾用材料の
製造方法を提供せんとするものである。
本発明は、装飾用銀、白金、金またはそれらの
合金上に、拡散防止用の下地めつきをほどこし、
その後紫色の呈する金とアルミニウムから成る被
膜をめつきにより形成し、さらに酸化性雰囲気中
で熱処理し、前記被膜の表面を酸化させることを
特徴とするものである。
合金上に、拡散防止用の下地めつきをほどこし、
その後紫色の呈する金とアルミニウムから成る被
膜をめつきにより形成し、さらに酸化性雰囲気中
で熱処理し、前記被膜の表面を酸化させることを
特徴とするものである。
而して本発明の製造法において、金とアルミニ
ウムから成る被膜をめつきにて装飾用銀、白金、
金またはそれらの合金上に形成する理由は、装飾
品としての種々の形状に加工できるようにするた
めである。また、装飾用銀、白金、金またはそれ
らの合金上に拡散防止用の下地めつきをほどこす
理由は、最終装飾品として組み上げる際にろう付
け等の熱処理を行なうが、その熱処理により装飾
用銀、白金、金またはそれらの合金中に紫色を呈
する金とアルミニウムから成る被膜が拡散し、金
とアルミニウムから成る被膜の所定の膜厚あるい
は色調が得られなくなるため、あらかじめ拡散防
止用の下地めつきをすることにより装飾用銀、白
金、金またはそれらの合金中への金とアルミニウ
ムから成る被膜の拡散を防止するためであり、下
地めつきとしてはスパツタリング、化学めつきあ
るいは電気めつきなどの方法が用いられる。ま
た、装飾用銀、白金、金またはそれらの合金上に
金とアルミニウムから成る被膜を付着させた後、
酸化性雰囲気中で熱処理し、金とアルミニウムか
ら成る被膜の表面を酸化する理由は、熱処理する
前の色を赤紫色に変えるためと単なる紫色の金−
アルミニウム合金そのものによりさらに、耐食性
を向上させ且つ硬くするためである。
ウムから成る被膜をめつきにて装飾用銀、白金、
金またはそれらの合金上に形成する理由は、装飾
品としての種々の形状に加工できるようにするた
めである。また、装飾用銀、白金、金またはそれ
らの合金上に拡散防止用の下地めつきをほどこす
理由は、最終装飾品として組み上げる際にろう付
け等の熱処理を行なうが、その熱処理により装飾
用銀、白金、金またはそれらの合金中に紫色を呈
する金とアルミニウムから成る被膜が拡散し、金
とアルミニウムから成る被膜の所定の膜厚あるい
は色調が得られなくなるため、あらかじめ拡散防
止用の下地めつきをすることにより装飾用銀、白
金、金またはそれらの合金中への金とアルミニウ
ムから成る被膜の拡散を防止するためであり、下
地めつきとしてはスパツタリング、化学めつきあ
るいは電気めつきなどの方法が用いられる。ま
た、装飾用銀、白金、金またはそれらの合金上に
金とアルミニウムから成る被膜を付着させた後、
酸化性雰囲気中で熱処理し、金とアルミニウムか
ら成る被膜の表面を酸化する理由は、熱処理する
前の色を赤紫色に変えるためと単なる紫色の金−
アルミニウム合金そのものによりさらに、耐食性
を向上させ且つ硬くするためである。
次に本発明の製造方法による具体的な装飾用材
料の製造実施例について説明する。
料の製造実施例について説明する。
実施例 １
10mm×10mm×１mmの白金−パラジウム10重量％
板上にスパツタリング装置を用いてモルブデンを
1μの厚みだけ被膜し、さらにその上に金−アル
ミニウム22重量％合金のターゲツトを用いてスパ
ツタリング装置により紫色を呈した金−アルミニ
ウム合金を0.2mmの厚みだけ被膜した後、その板
を600℃で10分、大気中で熱処理を行なつたとこ
ろその白金−パラジウム10重量％板の表面はあざ
やかな赤紫色を呈し、その表面のビツカース硬さ
が、75から243に上昇し、硬化した。さらにこの
白金−パラジウム10重量％板を600℃で10分、真
空中で熱処理を行なつてもあざやかな赤紫色は変
化しなかつた。
板上にスパツタリング装置を用いてモルブデンを
1μの厚みだけ被膜し、さらにその上に金−アル
ミニウム22重量％合金のターゲツトを用いてスパ
ツタリング装置により紫色を呈した金−アルミニ
ウム合金を0.2mmの厚みだけ被膜した後、その板
を600℃で10分、大気中で熱処理を行なつたとこ
ろその白金−パラジウム10重量％板の表面はあざ
やかな赤紫色を呈し、その表面のビツカース硬さ
が、75から243に上昇し、硬化した。さらにこの
白金−パラジウム10重量％板を600℃で10分、真
空中で熱処理を行なつてもあざやかな赤紫色は変
化しなかつた。
実施例 ２
外径18mm、肉厚２mmのK18甲丸指輪上にスパツ
タリング装置を用いてモリブデンを1.5μの厚みだ
け被膜し、さらにその上に独立した金及びアルミ
ニウムのターゲツトを用いてスパツタリング装置
により金75重量％−アルミニウム25重量％から成
る被膜を0.2mmめつきした後、この指輪を400℃で
30分大気中で熱処理を行なつたところ、この指輪
の表面はあざやかな赤紫色を呈し、その表面のビ
ツカース硬さが、115から355に上昇し、硬化し
た。さらにこの指輪を500℃で10分、真空中で熱
処理を行なつてもあざやかな紫色は変化しなかつ
た。
タリング装置を用いてモリブデンを1.5μの厚みだ
け被膜し、さらにその上に独立した金及びアルミ
ニウムのターゲツトを用いてスパツタリング装置
により金75重量％−アルミニウム25重量％から成
る被膜を0.2mmめつきした後、この指輪を400℃で
30分大気中で熱処理を行なつたところ、この指輪
の表面はあざやかな赤紫色を呈し、その表面のビ
ツカース硬さが、115から355に上昇し、硬化し
た。さらにこの指輪を500℃で10分、真空中で熱
処理を行なつてもあざやかな紫色は変化しなかつ
た。
実施例 ３
10mm×10mm×１mmの金−銀12.5重量％−銅12.5
重量％板をワツト浴にて、浴温60％℃、電流密度
2A／dm2、めつき時間３分間めつきすることに
より、ニツケルを1μｍの厚みで被覆させた。さ
らにその後金−アルミニウム22重量％合金のター
ゲツトを用いてスパツタリング装置により0.3mm
の厚みで金−アルミニウム合金を被覆した。この
板を500℃で15分間、大気中で熱処理を行つたと
ころ、表面はあざやかな赤紫色を呈し、表面のビ
ツカース硬さは110から275に上昇した。
重量％板をワツト浴にて、浴温60％℃、電流密度
2A／dm2、めつき時間３分間めつきすることに
より、ニツケルを1μｍの厚みで被覆させた。さ
らにその後金−アルミニウム22重量％合金のター
ゲツトを用いてスパツタリング装置により0.3mm
の厚みで金−アルミニウム合金を被覆した。この
板を500℃で15分間、大気中で熱処理を行つたと
ころ、表面はあざやかな赤紫色を呈し、表面のビ
ツカース硬さは110から275に上昇した。
上記の説明で明らかなように本発明の製造法は
銀、白金、金またはそれらの合金の表面に拡散防
止用下地めつきをほどこした後、金とアルミニウ
ムからなる紫色の被膜を全面または部分的にめつ
きにより形成させた後、被膜の表面を酸化させる
ことにより種々の形状の赤紫色は赤紫色と他の色
の混じつた装飾材料を製造でき、またろう付等の
加熱によつても色調が変化しないので、従来の製
造法にとつて代わることのできる画期的なものと
言える。
銀、白金、金またはそれらの合金の表面に拡散防
止用下地めつきをほどこした後、金とアルミニウ
ムからなる紫色の被膜を全面または部分的にめつ
きにより形成させた後、被膜の表面を酸化させる
ことにより種々の形状の赤紫色は赤紫色と他の色
の混じつた装飾材料を製造でき、またろう付等の
加熱によつても色調が変化しないので、従来の製
造法にとつて代わることのできる画期的なものと
言える。
Claims (1)
- 【特許請求の範囲】 １ 装飾用銀、白金、金またはそれらの合金上
に、拡散防止用の下地めつきをほどこし、その後
紫色を呈する金とアルミニウムから成る被覆をめ
つきにより形成し、さらに酸化性雰囲気中で熱処
理し、前記被覆の表面を酸化させることを特徴と
する装飾用材料の製造方法。 ２ 前記の拡散防止用下地めつきとしては、金と
アルミニウムの拡散速度が遅いNiまたはMoとす
ることを特徴とする特許請求の範囲第１項記載の
装飾用材料の製造方法。