JPH0636406U

JPH0636406U - Ceramics band

Info

Publication number: JPH0636406U
Application number: JP7342292U
Authority: JP
Inventors: 節夫東海林
Original assignee: セイコー電子工業株式会社
Priority date: 1992-10-21
Filing date: 1992-10-21
Publication date: 1994-05-17

Abstract

(57)【要約】【目的】バンドを構成する駒と駒をつなぐ金属部の露
出の少ないセラミックスバンドを得る。【構成】ループとループを結ぶ平坦部を金属により一
体に構成し、平坦部を凹部を有するセラミックスで挟ん
で接合する、ループが露出しないようにセラミックの一
部を短くし、その空間に収納する。【効果】平坦部の露出が少なく、セラミックスと金属
の接合強度が高いセラミックスバンドが得られる。 (57) [Summary] [Purpose] To obtain a ceramic band in which the pieces constituting the band and the metal parts connecting the pieces are less exposed. [Structure] A flat portion that connects the loops is integrally formed of metal, and the flat portions are sandwiched and joined by ceramics having recesses. A part of the ceramics is shortened so that the loops are not exposed and the ceramics are stored in the space. . [Effect] A ceramic band in which the flat portion is less exposed and the bonding strength between the ceramic and the metal is high can be obtained.

Description

[Detailed description of the device]

【０００１】[0001]

[Industrial applications]

この考案は、セラミックスと金属の接合技術を用いたセラミックスバンドに関する。 The present invention relates to a ceramic band using a ceramic-metal joining technique.

【０００２】[0002]

[Prior art]

従来は、セラミックス部に図２に示すように逆テーパを有する溝を形成し、台形状の断面を有する金属を溝に差し込み、ろう材で固定していた。 Conventionally, a groove having an inverse taper is formed in the ceramic portion as shown in FIG. 2, and a metal having a trapezoidal cross section is inserted into the groove and fixed with a brazing material.

【０００３】[0003]

[Problems to be solved by the device]

従来の方法によると、セラミックスは金属より熱膨張係数が小さいためセラミックス部の端面に圧縮応力が加わり弱い外力によっても接合部が剥離する、金属部や接合部が表面に露出しデザイン面での制約があるという課題がある。 According to the conventional method, ceramics have a smaller coefficient of thermal expansion than metal, so compressive stress is applied to the end face of the ceramic part and the joint part is peeled off even by a weak external force. There is a problem that there are restrictions.

【０００４】そこで、本考案の目的はセラミックスと金属の接合部が剥離しないバンドを実現することにある。Therefore, an object of the present invention is to realize a band in which the bonded portion of ceramics and metal does not separate.

【０００５】[0005]

[Means for Solving the Problems]

上記課題を解決するために本考案では、セラミックスの駒のループとループを結ぶ平坦部を金属により一体に構成され、平坦部を凹部を有するセラミックスで挟み接合することを特徴とする。 In order to solve the above problems, the present invention is characterized in that a loop of a ceramic piece and a flat portion connecting the loops are integrally formed of metal, and the flat portion is sandwiched and joined by ceramics having a recess.

【０００６】[0006]

[Action]

本考案によれば、接合部が剥離せず、平坦部や接合部を表面に露出する事なくセラミックスの駒をつなぐことが可能となった。 According to the present invention, it is possible to connect ceramic pieces without peeling the joint and exposing the flat portion and the joint on the surface.

【０００７】[0007]

【Example】

以下に、本考案の実施例を図面に基づき説明する。（実施例１）図１（ａ）は、本考案の実施例を示すセラミックスバンドの一部を示すものである。図１（ｂ）は、そのセラミックスバンド駒の断面を示すものである。平坦部２の両端にはループ４を持ち、金属で一体に構成された結合部の平坦部２を凹部３を持った２枚のセラミックス１で挟み、ろう材５によって接合されている。このように構成すれば、温度が変化してもセラミックス１と平坦部２の伸縮の違いによる剥離は少なくなり、外力に対しても強くなった。表１は、本考案と従来方法の接合部の強度を比較した結果である。 Embodiments of the present invention will be described below with reference to the drawings. (Example 1) FIG. 1A shows a part of a ceramic band showing an example of the present invention. FIG. 1 (b) shows a cross section of the ceramic band piece. Loops 4 are provided at both ends of the flat portion 2, and the flat portion 2 of the connecting portion integrally formed of metal is sandwiched by two ceramics 1 having a concave portion 3 and joined by a brazing material 5. According to this structure, even if the temperature changes, the peeling due to the difference in expansion and contraction of the ceramic 1 and the flat portion 2 is reduced, and the ceramic 1 and the flat portion 2 are strong against external force. Table 1 shows the results of comparing the strength of the joint between the present invention and the conventional method.

【０００８】（表１） ―――――｜――――――――――― ｜せん断強度(Kg/mm²) ―――――｜――――――――――― 本考案｜ 15 (N=30) 従来方法｜ 4 (N=30) ―――――｜――――――――――― （実施例２）図３（ａ）は、本考案の他の実施例を示すセラミックスバンドの一部を示すものである。図３（ｂ）はそのセラミックスバンド駒の断面を示すものである。実施例１と同様にループ４を持った一体に構成された平坦部２を２枚のセラミックス１で挟むが、このときループの露出を極力抑えた方が外観上好ましいので、下面（腕に接触する面）のセラミックスを短くし、その内容６にループ４を収めるようにした。(Table 1) ――――― ｜ ―――――――――――― ｜ Shear strength (Kg / mm ² ) ――――― ｜ ―――――――――――― The present invention ｜ 15 (N = 30) Conventional method ｜ 4 (N = 30) ――――― ｜ ―――――――――――― (Example 2) FIG. 3A shows the present invention. This is a part of a ceramic band showing another embodiment. FIG. 3B shows a cross section of the ceramic band piece. As in Example 1, the flat portion 2 having the loop 4 and integrally formed is sandwiched between the two ceramics 1. At this time, it is preferable to minimize the exposure of the loop. The ceramic on the surface that contacts the arm was shortened so that the loop 4 was placed in the content 6.

【０００９】[0009]

[Effect of device]

以上本考案によれば、セラミックスバンドの駒をつなぐ平坦部を露出させることなく接続でき、更に平坦部とセラミックスの接合強度が飛躍的に向上するという効果がある。 As described above, according to the present invention, it is possible to make a connection without exposing the flat portion connecting the ceramic band pieces, and further, the bonding strength between the flat portion and the ceramic can be dramatically improved.

[Brief description of drawings]

【図１】（ａ）は本考案のセラミックスバンドの平坦部
である。（ｂ）は本考案のセラミックスバンド駒の断面
図である。FIG. 1 (a) is a flat portion of a ceramic band of the present invention. (B) is a sectional view of the ceramic band piece of the present invention.

【図２】（ａ）は従来のセラミックスバンド駒の断面図
である。（ｂ）は従来のセラミックスバンド駒の側面図
である。FIG. 2A is a sectional view of a conventional ceramic band piece. (B) is a side view of the conventional ceramic band piece.

【図３】（ａ）は本考案の他の実施例の平面図である。
（ｂ）は本考案の実施例の断面図である。FIG. 3A is a plan view of another embodiment of the present invention.
(B) is sectional drawing of the Example of this invention.

[Explanation of symbols]

１セラミックス２平坦部３凹部４ループ５ろう材７駒 1 Ceramics 2 Flat part 3 Recessed part 4 Loop 5 Brazing material 7 pieces

Claims

[Scope of utility model registration request]

1. In a band using ceramics,
A ceramic band characterized in that a loop of a piece forming a band and a flat portion connecting the loops are integrally made of metal, and the flat portion is sandwiched by ceramics having a recess and joined.