JPH0732481A - 含フッ素樹脂系フィルムの接合方法及び接合機械 - Google Patents

含フッ素樹脂系フィルムの接合方法及び接合機械

Info

Publication number
JPH0732481A
JPH0732481A JP5202043A JP20204393A JPH0732481A JP H0732481 A JPH0732481 A JP H0732481A JP 5202043 A JP5202043 A JP 5202043A JP 20204393 A JP20204393 A JP 20204393A JP H0732481 A JPH0732481 A JP H0732481A
Authority
JP
Japan
Prior art keywords
joining
film
fluororesin
fluorine
bonding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP5202043A
Other languages
English (en)
Inventor
Noriyuki Miyai
紀之 宮井
Hiroyuki Yamauchi
弘之 山内
Isamu Harasawa
勇 原沢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Carbide Industries Co Inc
Original Assignee
Nippon Carbide Industries Co Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Carbide Industries Co Inc filed Critical Nippon Carbide Industries Co Inc
Priority to JP5202043A priority Critical patent/JPH0732481A/ja
Publication of JPH0732481A publication Critical patent/JPH0732481A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【目的】 従来全く不可能とされていた含フッ素樹脂系
フィルムの接合をいずれの人でも、容易で、確実でさら
に安全に作用する含フッ素樹脂系フィルムの効果的な接
合方法が得られる。 【構成】 含フッ素樹脂系フィルムを互がいに連続的に
接合する方法において、予め前記フィルムを予熱し、次
いで２００℃以上の温度で０.５kg/cm2以上の圧力の
下、１秒間以上加熱圧着して後、冷却することを特徴と
した含フッ素樹脂系フィルムの接合方法。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、含フッ素樹脂系フィル
ムの接合方法及び接合機械に関する。
【０００２】
【従来の技術】従来よりフィルムの接合方法は種々提案
されている。例えば塩化ビニル樹脂、ポリエチレン樹脂
及びポリ酢酸ビニル樹脂フィルム等の農業用フィルムで
は、加熱ヒーター、もしくは高周波ウエルダー等によ
り、フィルムを接合している。
【０００３】しかしながら、これら接合方法では、含フ
ッ素樹脂系フィルムを効率的に接合することはできず、
業界からは、これら含フッ素樹脂系フィルムの新規な接
合方法の開発が望まれていた。
【０００４】
【発明が解決しようとする課題】本発明の目的は前述の
課題を解決すべくなされたものであり、従来より全く知
られていなかった新規な含フッ素樹脂系フィルムの接合
方法を提供することを目的とするものである。
【０００５】
【課題を解決するための手段】本発明は、前述の課題を
解決すべくなされたものであり、含フッ素樹脂系フィル
ムを互がいに連続的に接合する方法において、予め前記
フィルムを予熱し、次いで２００℃以上の温度で０.５k
g/cm2以上の圧力の下、１秒間以上加熱圧着した後、冷
却することを特徴とした含フッ素樹脂系フィルムの接合
方法を提供することを目的とするものである。
【０００６】しかして、本発明によれば、従来全く不可
能とされていた含フッ素樹脂系フィルムの接合をいずれ
の人でも容易で、確実でさらに安全に作用する含フッ素
樹脂系フィルムの効果的な接合方法が得られるのであ
る。以下、本発明の構成要因について、さらに詳細に説
明する。
【０００７】本発明において、含フッ素樹脂とは、フッ
素を含むオレフインの重合によって得られる合成樹脂を
総称するものであり、本発明では一般にフッ素含有量が
４５重量％以上、特に５０重量％以上のものが好適に使
用される。そのようなフッ素樹脂としては、例えばエチ
レン−テトラフルオロエチレン系共重合体、エチレン−
クロロトリフルオロエチレン系共重合体、ヘキサフルオ
ロプロピレン−テトラフルオロエチレン系共重合体、パ
ーフルオロアルキルビニルエーテル−テトラフルオロエ
チレン系共重合体、、ポリフッ化ビニリデン、ポリフッ
化ビニル等が挙げられ、本発明では、これらのいずれで
も使用可能であるが、中でも、エチレン−テトラフルオ
ロエチレン系共重合体が好適である。
【０００８】エチレン−テトラフルオロエチレン系共重
合体は、エチレン及びテトラフルオロエチレンを主体と
し（エチレン／テトラフルオロエチレンのモル比は一般
に４０／６０〜６０／４０にある）、そして必要によ
り、これに少量（通常１０モル％以下）の第３のコモノ
マー成分を共重合させたものであり、本発明では殊に、
エチレン／テトラフルオロエチレンの含有モル比が４０
／６０〜６０／４０、好ましくは４５／５５〜５５／４
５の範囲内にあり、且つ式CH2=CH-CnF2n+1（ここで、n
は２〜１０の整数である）で示されるパーフルオロアル
キルビニルモノマー単位（例えば、CH2=CH-C4H9またはC
H2=CH-C6H13から誘導される単位）の含有量が０.１〜１
０モル％、好ましくは０.３〜５モル％の範囲内にある
エチレン−テトラフルオロエチレン系共重合体が好適に
使用される。このエチレン−テトラフルオロエチレン系
共重合体はそれ自体既知のものであり、例えば特公昭５
９−５０１６３号公報に記載の方法で製造することがで
き、また、市販品として旭硝子(株)より「アフロン Ｃ
ＯＰ」なる商品名で市販されているものを使用すること
もできる。
【０００９】以上に述べたフッ素樹脂からのフィルムの
成形はそれ自体公知の方法に従い、例えば押出成形法、
インフレーション成形法等により行なうことができる。
【００１０】また、本発明に於いて「予熱工程」とは、
次工程に於けるフィルムの昇温を容易にするための前提
条件であり、その予熱条件は１５０℃以上、１秒以上が
好ましく、具体的には、１５０℃〜２５０℃、１〜３秒
間の範囲で、特に好ましくは２００℃、１秒間である。
【００１１】次の「加熱圧着工程」は、フィルムの接合
すべき部分を熔融乃至熔融状態に近い温度まで加熱して
圧着するもので、その加熱圧着条件は２００℃以上、圧
力０.５kg/cm2以上、１秒間以上の加熱圧着が好まし
く、具体的には、２５０〜３００℃、０.５〜２kg/c
m2、１〜３秒間で、特に好ましくは、２８０℃、１kg/c
m2、１.５秒間である。
【００１２】最後の「冷却工程」は接合部分の接合をよ
り確実にするための工程であり、その冷却条件は、１０
〜５０℃１〜４秒間で、具体的には空冷及び水冷等によ
り目的を達成し得また、上記各工程に於ける温度、処理
時間、圧力等は、接合すべき含フッ素樹脂系フィルムの
樹脂組成、厚み、要求される接合強度及び生産性などを
考慮して適切な条件が選定されることは言うまでもな
い。
【００１３】次に本発明に於ける含フッ素樹脂系フィル
ムの接合機械とは前記３工程即ち予熱、加熱圧着、冷却
の各操作を基本的要素とし、且つこれらを連続的に行な
うものである。
【００１４】ここに於いて加熱方式に制約はないが、電
気ヒーターを内蔵した熱板に、フッ素樹脂処理したガラ
スクロスを介して、含フッ素樹脂系フィルムを接触させ
て加熱する方式が好ましい。
【００１５】このようにして接合された含フッ素樹脂系
フィルムは施設園芸用ハウスに対する被覆材として、フ
イルムの張設工事の簡略化、安定した張設状態の実現を
もたらし、業界に大きく寄与するものである。
【００１６】以下、実施例を以つて更に詳しく説明する
が、本発明は実施例にのみ限定されるものでないことは
言うまでもない。
【００１７】
【実施例】
実施例Ａ（含フッ素樹脂フィルムの調整） 含フッ素樹脂の代表としてエチレン−テトラフルオロエ
チレン共重合体（ＥＴＦＥ」の「アフロン ＣＯＰ」
（旭硝子(株)製）を選び、押出成形により、厚み２４
μ、６０μ、１６０μのフィルムを得た。
【００１８】実施例Ｂ（フィルムの接合） 接合すべき部分と重ね合わせた２枚のフィルムを、フッ
素樹脂処理したガラスクロスを介して、２枚の熱板の間
に挟み、先ず予熱し、次に加熱圧着し、冷却したのち、
所定の形状に裁断し試料を得た。フィルムの接合条件と
接合評価を表１に示した。
【００１９】
【表１】
【００２０】表１に示した物性値の測定方法は次の通り
である。接合強度の測定方法は、接合部（１８mm）を挟
んだダンベル型の試料（幅３mm）を作り、ＡＳＴＭ Ｄ
８８２に準拠した引張試験方法によった（引張速度２０
０mm／分）。
【００２１】接合したフィルムの実用性の評価基準は以
下に述べる通りである。 ○ 引張試験に於いて、接合部以外の部分（フィルム原
反）が破断する場合 × 引張試験に於いて、接合部が破断又は剥離する場合

Claims (5)

    【特許請求の範囲】
  1. 【請求項１】 含フッ素樹脂系フィルムを互がいに連続
    的に接合する方法において、予め前記フィルムを予熱
    し、次いで２００℃以上の温度で０.５kg/cm2以上の圧
    力の下、１秒間以上加熱圧着して後、冷却することを特
    徴とした含フッ素樹脂系フィルムの接合方法。
  2. 【請求項２】 該含フッ素樹脂がエチレン−テトラフル
    オロエチレン共重合体（ＥＴＦＥ）である請求項１記載
    の接合方法。
  3. 【請求項３】 該予熱条件が１５０℃以上の温度で１秒
    以上である請求項１記載の接合方法。
  4. 【請求項４】 該フィルムが農業用フィルムである請求
    項１〜３いずれか記載の接合方法。
  5. 【請求項５】 含フッ素樹脂系フィルムを互がいに連続
    的に接合する装置において、少なくとも予め１５０℃以
    上のフィルム予熱装置と、２００℃以上の温度で０.５k
    g/cm2以上の圧力の下、１秒間以上加熱圧着する加熱圧
    着装置と、さらに圧着後、フィルムを冷却する冷却装置
    とを具備してなることを特徴とする含フッ素樹脂系フィ
    ルムの接合機械。
JP5202043A 1993-07-23 1993-07-23 含フッ素樹脂系フィルムの接合方法及び接合機械 Pending JPH0732481A (ja)