JPH08291242A - 高温加工に適したハロゲン含有樹脂組成物 - Google Patents
高温加工に適したハロゲン含有樹脂組成物Info
- Publication number
- JPH08291242A JPH08291242A JP12913795A JP12913795A JPH08291242A JP H08291242 A JPH08291242 A JP H08291242A JP 12913795 A JP12913795 A JP 12913795A JP 12913795 A JP12913795 A JP 12913795A JP H08291242 A JPH08291242 A JP H08291242A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- halogen
- parts
- carbon atoms
- pts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【構成】ハロゲン含有樹脂１００重量部に対して、
（ａ）ステアリン酸カルシウム０．１〜３重量部、
（ｂ）Ａ型ゼオライト類、ハイドロタルサイト類及び水
酸化マグネシウムの少なくとも一種０．０１〜２重量
部、（ｃ）一般式（１）で表される有機錫硫黄化合物
０．１〜３重量部及び（ｄ）一般式（２）および（３）
で表される有機錫硫黄化合物の少なくとも一種０．０１
〜３重量部を含有する高温加工に適したハロゲン含有樹
脂組成物。 【化１】 （Ｒ：アルキル基又はアルコキシカルボニル基，Ｒ1 ：
アルキル基、アルケニル基又はアラルキル基，Ｒ2 ：脂
肪酸又は芳香族酸の残基） 【効果】ハロゲン含有樹脂に、上記の（ａ）〜（ｄ）の
化合物を併用して添加すれば、熱安定性が良好で初期着
色性の少ない高温加工に適したハロゲン含有樹脂組成物
が得られる。
（ａ）ステアリン酸カルシウム０．１〜３重量部、
（ｂ）Ａ型ゼオライト類、ハイドロタルサイト類及び水
酸化マグネシウムの少なくとも一種０．０１〜２重量
部、（ｃ）一般式（１）で表される有機錫硫黄化合物
０．１〜３重量部及び（ｄ）一般式（２）および（３）
で表される有機錫硫黄化合物の少なくとも一種０．０１
〜３重量部を含有する高温加工に適したハロゲン含有樹
脂組成物。 【化１】 （Ｒ：アルキル基又はアルコキシカルボニル基，Ｒ1 ：
アルキル基、アルケニル基又はアラルキル基，Ｒ2 ：脂
肪酸又は芳香族酸の残基） 【効果】ハロゲン含有樹脂に、上記の（ａ）〜（ｄ）の
化合物を併用して添加すれば、熱安定性が良好で初期着
色性の少ない高温加工に適したハロゲン含有樹脂組成物
が得られる。
Description
【０００１】
【産業上の利用分野】本発明は、熱安定性と初期着色性
を改良した高温加工に適したハロゲン含有樹脂組成物に
関する。
を改良した高温加工に適したハロゲン含有樹脂組成物に
関する。
【０００２】
【従来の技術】ハロゲン含有樹脂は、熱及び光に対する
安定性に欠けるので、加熱成形加工を行う際に、脱ハロ
ゲン化水素に起因した熱分解を生じ易い。このため、成
形加工品が着色したり、物理的性質が低下するなどの弊
害が生ずる。かかる熱及び光に不安定なハロゲン含有樹
脂の欠点を補う為に、金属石鹸、有機錫化合物、有機亜
リン酸エステル類、エポキシ化合物、抗酸化剤、紫外線
吸収剤等が安定剤として使用されてきた。特に有機錫化
合物なかんずく有機錫メルカプトカルボン酸エステル類
は、ハロゲン含有樹脂に対する優れた安定剤として知ら
れている。
安定性に欠けるので、加熱成形加工を行う際に、脱ハロ
ゲン化水素に起因した熱分解を生じ易い。このため、成
形加工品が着色したり、物理的性質が低下するなどの弊
害が生ずる。かかる熱及び光に不安定なハロゲン含有樹
脂の欠点を補う為に、金属石鹸、有機錫化合物、有機亜
リン酸エステル類、エポキシ化合物、抗酸化剤、紫外線
吸収剤等が安定剤として使用されてきた。特に有機錫化
合物なかんずく有機錫メルカプトカルボン酸エステル類
は、ハロゲン含有樹脂に対する優れた安定剤として知ら
れている。
【０００３】
【発明が解決しようとする課題】しかし、これらの安定
剤も苛酷な加工条件（高温熱処理）下における樹脂の熱
劣化を防止するには不充分であり、樹脂の着色を防ぐこ
とができない。例えば、ジアルキル錫メルカプトカルボ
ン酸エステルとモノアルキル錫メルカプトカルボン酸エ
ステルの併用が提案されている（特公昭５１−３１２５
８号）が、初期着色において不充分であり、また、モノ
アルキル錫（２−メルカプトエチル脂肪酸）若しくは
〔モノアルキル錫（２−メルカプトエチル脂肪酸）〕サ
ルファイドとジアルキル錫（２−メルカプトエチル脂肪
酸）若しくは〔ジアルキル錫（２−メルカプトエチル脂
肪酸）〕サルファイドの併用（特公昭５８−４５４６１
号）では、熱安定性において不充分である。一方、有機
錫硫黄化合物とＡ型ゼオライト類を併用する特許出願と
して、特公昭５８−１８９３９号、特公昭６０−４５６
６０号が、有機錫硫黄化合物とハイドロタルサイト類を
併用するものとして特開昭５７−２０９９４３号、特公
平３−３７５７９号が、また有機錫硫黄化合物と水酸化
マグネシウムを併用するものとして特開昭５０−１３４
３９号、特開昭５０−３８７４４号、特開昭５０−５２
１６０号、特開昭５０−８８１５４号、特開昭５６−８
４３号、特開平３−１３７１４８号等があるも、いずれ
も満足な熱安定効果が得られない。当樹脂業界では、特
にハロゲン含有樹脂に有機錫硫黄化合物を配合した場合
の初期着色性および熱安定性の改良が望まれている。
剤も苛酷な加工条件（高温熱処理）下における樹脂の熱
劣化を防止するには不充分であり、樹脂の着色を防ぐこ
とができない。例えば、ジアルキル錫メルカプトカルボ
ン酸エステルとモノアルキル錫メルカプトカルボン酸エ
ステルの併用が提案されている（特公昭５１−３１２５
８号）が、初期着色において不充分であり、また、モノ
アルキル錫（２−メルカプトエチル脂肪酸）若しくは
〔モノアルキル錫（２−メルカプトエチル脂肪酸）〕サ
ルファイドとジアルキル錫（２−メルカプトエチル脂肪
酸）若しくは〔ジアルキル錫（２−メルカプトエチル脂
肪酸）〕サルファイドの併用（特公昭５８−４５４６１
号）では、熱安定性において不充分である。一方、有機
錫硫黄化合物とＡ型ゼオライト類を併用する特許出願と
して、特公昭５８−１８９３９号、特公昭６０−４５６
６０号が、有機錫硫黄化合物とハイドロタルサイト類を
併用するものとして特開昭５７−２０９９４３号、特公
平３−３７５７９号が、また有機錫硫黄化合物と水酸化
マグネシウムを併用するものとして特開昭５０−１３４
３９号、特開昭５０−３８７４４号、特開昭５０−５２
１６０号、特開昭５０−８８１５４号、特開昭５６−８
４３号、特開平３−１３７１４８号等があるも、いずれ
も満足な熱安定効果が得られない。当樹脂業界では、特
にハロゲン含有樹脂に有機錫硫黄化合物を配合した場合
の初期着色性および熱安定性の改良が望まれている。
【０００４】
【課題を解決するための手段】そこで、発明者等は、種
々検討の結果、ハロゲン含有樹脂に以下に示す（ａ）〜
（ｄ）の化合物を併用して添加することにより高温加工
に適したハロゲン含有樹脂組成物が得られることを見出
し、本発明に至った。
々検討の結果、ハロゲン含有樹脂に以下に示す（ａ）〜
（ｄ）の化合物を併用して添加することにより高温加工
に適したハロゲン含有樹脂組成物が得られることを見出
し、本発明に至った。
【０００５】本発明は、ハロゲン含有樹脂１００重量部
に対して、（ａ）ステアリン酸カルシウム０．１〜３重
量部、（ｂ）Ａ型ゼオライト類、ハイドロタルサイト類
及び水酸化マグネシウム（若しくは表面処理をした水酸
化マグネシウム）の少なくとも一種０．０１〜２重量
部、（ｃ）一般式（１）
に対して、（ａ）ステアリン酸カルシウム０．１〜３重
量部、（ｂ）Ａ型ゼオライト類、ハイドロタルサイト類
及び水酸化マグネシウム（若しくは表面処理をした水酸
化マグネシウム）の少なくとも一種０．０１〜２重量
部、（ｃ）一般式（１）
【０００６】
【化４】 （式中、Ｒは炭素数１〜１８の直鎖若しくは分枝を有す
るアルキル基又は炭素数１〜２０のアルコキシカルボニ
ルエチル基を、Ｒ1 は炭素数１〜３６の直鎖若しくは分
枝を有するアルキル基、アルケニル基又はアラルキル基
をそれぞれ示す）で表される有機錫硫黄化合物０．１〜
３重量部及び（ｄ）一般式（２）および（３）
るアルキル基又は炭素数１〜２０のアルコキシカルボニ
ルエチル基を、Ｒ1 は炭素数１〜３６の直鎖若しくは分
枝を有するアルキル基、アルケニル基又はアラルキル基
をそれぞれ示す）で表される有機錫硫黄化合物０．１〜
３重量部及び（ｄ）一般式（２）および（３）
【０００７】
【化５】
【０００８】
【化６】 （各式中、Ｒは炭素数１〜１８の直鎖若しくは分枝を有
するアルキル基又は炭素数１〜２０のアルコキシカルボ
ニルエチル基を、Ｒ2 は炭素数１〜２２の脂肪酸4 残基
又は芳香族酸の残基をそれぞれ示す）で表される有機錫
硫黄化合物の少なくとも一種０．０１〜３重量部を含有
する高温加工に適したハロゲン含有樹脂組成物である。
するアルキル基又は炭素数１〜２０のアルコキシカルボ
ニルエチル基を、Ｒ2 は炭素数１〜２２の脂肪酸4 残基
又は芳香族酸の残基をそれぞれ示す）で表される有機錫
硫黄化合物の少なくとも一種０．０１〜３重量部を含有
する高温加工に適したハロゲン含有樹脂組成物である。
【０００９】本発明によって安定化される塩素含有樹脂
としては、例えば、塩化ビニル樹脂や塩化ビニリデン樹
脂の如きハロゲン化ビニル単独重合体、ハロゲン化ビニ
ルを酢酸ビニル、エチレン、プロピレン、スチレン、イ
ソブチレン、塩化ビニリデン、無水マレイン酸、ブタジ
エン、イソプレン、メチルメタクリレ−ト、アクリロニ
トリル、ジアルキルマレ−トの如きコモノマ−の一種又
は二種以上と共重合させることによって形成されるよう
な共重合体、後塩素化塩化ビニル樹脂などが挙げられ
る。また、ハロゲン含有樹脂とアクリロニトリル・ブタ
ジエン・スチレン樹脂、メチルメタクリレ−ト・ブタジ
エン・スチレン樹脂、アクリロニトリル・塩素化ポリエ
チレン・スチレン共重合体樹脂、アクリルゴム・アクリ
ロニトリル・スチレン共重合体、アクリルゴム・メチル
メタクリレ−ト・アクリロニトリル共重合体樹脂、酢酸
ビニル・エチレン共重合樹脂、塩素化ポリエチレン、塩
化ゴムなどの耐衝撃改良樹脂とのポリマーブレンド樹脂
などを挙げることができる。
としては、例えば、塩化ビニル樹脂や塩化ビニリデン樹
脂の如きハロゲン化ビニル単独重合体、ハロゲン化ビニ
ルを酢酸ビニル、エチレン、プロピレン、スチレン、イ
ソブチレン、塩化ビニリデン、無水マレイン酸、ブタジ
エン、イソプレン、メチルメタクリレ−ト、アクリロニ
トリル、ジアルキルマレ−トの如きコモノマ−の一種又
は二種以上と共重合させることによって形成されるよう
な共重合体、後塩素化塩化ビニル樹脂などが挙げられ
る。また、ハロゲン含有樹脂とアクリロニトリル・ブタ
ジエン・スチレン樹脂、メチルメタクリレ−ト・ブタジ
エン・スチレン樹脂、アクリロニトリル・塩素化ポリエ
チレン・スチレン共重合体樹脂、アクリルゴム・アクリ
ロニトリル・スチレン共重合体、アクリルゴム・メチル
メタクリレ−ト・アクリロニトリル共重合体樹脂、酢酸
ビニル・エチレン共重合樹脂、塩素化ポリエチレン、塩
化ゴムなどの耐衝撃改良樹脂とのポリマーブレンド樹脂
などを挙げることができる。
【００１０】本発明で添加されるＡ型ゼオライト類は、
一般式（４）
一般式（４）
【化７】 （式中、Ｍは１価のカチオン又はそれと等量の多価カチ
オンであり、Ｎａ、Ｋ、ＮＨ4 、Ｃａ、Ｍｇ、Ｓｒ、Ｚ
ｎを示す）で表され、例えばＭが１価のカチオンである
場合には、Ｍ2 ＯはＮａ2 Ｏ、Ｋ2 Ｏ、（ＮＨ4 ）2 Ｏ
を表し、Ｍがそれと等量の多価カチオンである場合に
は、Ｍ2 ＯはＣａＯ、ＭｇＯ、ＳｒＯ、ＺｎＯを表す。
オンであり、Ｎａ、Ｋ、ＮＨ4 、Ｃａ、Ｍｇ、Ｓｒ、Ｚ
ｎを示す）で表され、例えばＭが１価のカチオンである
場合には、Ｍ2 ＯはＮａ2 Ｏ、Ｋ2 Ｏ、（ＮＨ4 ）2 Ｏ
を表し、Ｍがそれと等量の多価カチオンである場合に
は、Ｍ2 ＯはＣａＯ、ＭｇＯ、ＳｒＯ、ＺｎＯを表す。
【００１１】ハイドロタルサイト類は、一般式（５）
【化８】 （式中、Ｍ2+はＭｇまたはＭｇとＺｎの固溶体を、Ａn-
はＣｌ4 - 、ＣＯ3 2- 、ＳＯ4 2- などのｎ価のアニオン
を、ｘ及びｍは０＜ｘ＜０．５、０≦ｍ＜１を満足する
正の数をそれぞれ示す）で表されるマグネシウムとアル
ミニウムとからなる含水複塩化合物であり、天然物でも
合成品でもよく、これらは市販されている。
はＣｌ4 - 、ＣＯ3 2- 、ＳＯ4 2- などのｎ価のアニオン
を、ｘ及びｍは０＜ｘ＜０．５、０≦ｍ＜１を満足する
正の数をそれぞれ示す）で表されるマグネシウムとアル
ミニウムとからなる含水複塩化合物であり、天然物でも
合成品でもよく、これらは市販されている。
【００１２】表面処理をした水酸化マグネシウムは、水
酸化マグネシウム自体よりも分散性に優れ、表面処理剤
で処理をすることによって得られる。表面処理剤として
は、例えば高級脂肪酸類、アニオン系界面活性剤類、シ
ラン系カップリング剤類、チタネ−ト系カップリング剤
類、脂肪酸のグリセリンエステル類等を挙げることがで
き、具体例としてステアリン酸、オレイン酸、ラウリン
酸、１２−ヒドロキシステアリン酸等の高級脂肪酸類、
ステアリン酸ソ−ダ、オレイン酸ソ−ダ、ラウリルベン
ゼンスルホン酸ソ−ダ等のアニオン系界面活性剤類、ビ
ニルトリエトキシシラン、γ−メタクリロキシプロピル
トリエトキシシラン、イソプロピルトリイソステアロイ
ルチタネ−ト、イソプロピルトリデシルベンゼンスルホ
ニルチタネ−ト等のシラン系又はチタネ−ト系カップリ
ング剤類、グリセリンモノステアレ−ト、グリセリンモ
ノオレ−ト等の脂肪酸のグリセリンエステル類がある。
酸化マグネシウム自体よりも分散性に優れ、表面処理剤
で処理をすることによって得られる。表面処理剤として
は、例えば高級脂肪酸類、アニオン系界面活性剤類、シ
ラン系カップリング剤類、チタネ−ト系カップリング剤
類、脂肪酸のグリセリンエステル類等を挙げることがで
き、具体例としてステアリン酸、オレイン酸、ラウリン
酸、１２−ヒドロキシステアリン酸等の高級脂肪酸類、
ステアリン酸ソ−ダ、オレイン酸ソ−ダ、ラウリルベン
ゼンスルホン酸ソ−ダ等のアニオン系界面活性剤類、ビ
ニルトリエトキシシラン、γ−メタクリロキシプロピル
トリエトキシシラン、イソプロピルトリイソステアロイ
ルチタネ−ト、イソプロピルトリデシルベンゼンスルホ
ニルチタネ−ト等のシラン系又はチタネ−ト系カップリ
ング剤類、グリセリンモノステアレ−ト、グリセリンモ
ノオレ−ト等の脂肪酸のグリセリンエステル類がある。
【００１３】本発明で添加される一般式（１）で表され
る有機錫硫黄化合物としては、例えばジメチルスズビス
（イソオクチルメルカプトアセテート）、ジブチルスズ
ビス（２−エチルヘキシルメルカプトアセテート）、ジ
ブチルスズビス（イソオクチルメルカプトアセテー
ト）、ジオクチルスズビス（２−エチルヘキシルメルカ
プトアセテート）、ジオクチルスズビス（イソオクチル
メルカプトアセテート）、ジオクチルスズビス（イソノ
ニルメルカプトアセテート）、ジオクチルスズビス（デ
シルメルカプトアセテート）、ジオクチルスズビス（ド
デシルメルカプトアセテート）、ジオクチルスズビス
（テトラデシルメルカプトアセテート）、ジオクチルス
ズビス（ヘキサデシルメルカプトアセテート）、ジオク
チルスズビス（オクタデシルメルカプトアセテート）、
ジオクチルスズビス（Ｃ10〜18混合アルコールのメルカ
プトアセテート）、ジラウリルスズビス（２−エチルヘ
キシルメルカプトアセテート）、ジラウリルスズビス
（イソオクチルメルカプトアセテート）、ビス（ブトオ
キシカルボニルエチル）スズビス（イソオクチルメルカ
プトアセテート）などが挙げられる。
る有機錫硫黄化合物としては、例えばジメチルスズビス
（イソオクチルメルカプトアセテート）、ジブチルスズ
ビス（２−エチルヘキシルメルカプトアセテート）、ジ
ブチルスズビス（イソオクチルメルカプトアセテー
ト）、ジオクチルスズビス（２−エチルヘキシルメルカ
プトアセテート）、ジオクチルスズビス（イソオクチル
メルカプトアセテート）、ジオクチルスズビス（イソノ
ニルメルカプトアセテート）、ジオクチルスズビス（デ
シルメルカプトアセテート）、ジオクチルスズビス（ド
デシルメルカプトアセテート）、ジオクチルスズビス
（テトラデシルメルカプトアセテート）、ジオクチルス
ズビス（ヘキサデシルメルカプトアセテート）、ジオク
チルスズビス（オクタデシルメルカプトアセテート）、
ジオクチルスズビス（Ｃ10〜18混合アルコールのメルカ
プトアセテート）、ジラウリルスズビス（２−エチルヘ
キシルメルカプトアセテート）、ジラウリルスズビス
（イソオクチルメルカプトアセテート）、ビス（ブトオ
キシカルボニルエチル）スズビス（イソオクチルメルカ
プトアセテート）などが挙げられる。
【００１４】また、一般式（２）で表される有機錫硫黄
化合物としては、例えばモノメチルスズトリス（２−メ
ルカプトエチルオレイン酸）、モノブチルスズトリス
（２−メルカプトエチルカプリン酸）、モノオクチルス
ズトリス（２−メルカプトエチルトール油酸）、モノラ
ウリルスズトリス（２−メルカプトエチルステアリン
酸）、ブトオキシカルボニルエチルスズトリス（２−メ
ルカプトエチルオクチル酸）などが挙げられる。
化合物としては、例えばモノメチルスズトリス（２−メ
ルカプトエチルオレイン酸）、モノブチルスズトリス
（２−メルカプトエチルカプリン酸）、モノオクチルス
ズトリス（２−メルカプトエチルトール油酸）、モノラ
ウリルスズトリス（２−メルカプトエチルステアリン
酸）、ブトオキシカルボニルエチルスズトリス（２−メ
ルカプトエチルオクチル酸）などが挙げられる。
【００１５】一般式（３）で表される有機錫硫黄化合物
としては、例えばビス〔モノメチルスズビス（２−メル
カプトエチルオレイン酸）〕サルファイド、ビス〔モノ
ブチルスズビス（２−メルカプトエチル大豆油酸）〕サ
ルファイド、ビス〔モノオクチルスズビス（２−メルカ
プトエチルトール油酸）〕サルファイド、ビス〔モノラ
ウリルスズビス（２−メルカプトエチルオクチル酸）〕
サルファイド、ビス〔メトオキシカルボニルエチルスズ
（２−メルカプトエチルラウリン酸）〕サルファイドな
どが挙げられる。
としては、例えばビス〔モノメチルスズビス（２−メル
カプトエチルオレイン酸）〕サルファイド、ビス〔モノ
ブチルスズビス（２−メルカプトエチル大豆油酸）〕サ
ルファイド、ビス〔モノオクチルスズビス（２−メルカ
プトエチルトール油酸）〕サルファイド、ビス〔モノラ
ウリルスズビス（２−メルカプトエチルオクチル酸）〕
サルファイド、ビス〔メトオキシカルボニルエチルスズ
（２−メルカプトエチルラウリン酸）〕サルファイドな
どが挙げられる。
【００１６】本発明を構成する一般式（２）および
（３）で表される有機錫硫黄化合物については、添加剤
として一般式（２）および（３）で表される有機錫硫黄
化合物のうち少なくとも一種を含有していればよく、二
種とも含有していても差し支えない。
（３）で表される有機錫硫黄化合物については、添加剤
として一般式（２）および（３）で表される有機錫硫黄
化合物のうち少なくとも一種を含有していればよく、二
種とも含有していても差し支えない。
【００１７】さらに、本発明のハロゲン含有樹脂組成物
に対して、必要により、酸化防止剤、エポキシ化合物、
有機亜リン酸エステル、紫外線吸収剤、ホウ酸、ホウ酸
エステル、ホウ酸塩、三酸化アンチモン、滑剤、顔料、
充填剤、帯電防止剤、難燃剤、加工助剤、可塑剤等を添
加することができる。
に対して、必要により、酸化防止剤、エポキシ化合物、
有機亜リン酸エステル、紫外線吸収剤、ホウ酸、ホウ酸
エステル、ホウ酸塩、三酸化アンチモン、滑剤、顔料、
充填剤、帯電防止剤、難燃剤、加工助剤、可塑剤等を添
加することができる。
【００１８】
【実施例】つぎに、実施例を挙げて本発明を説明する
が、実施例中の部は重量部を示すものとする。
が、実施例中の部は重量部を示すものとする。
【００１９】実施例１〜８ 塩化ビニル樹脂（Ｇｅｏｎ１０３ＥＰ 日本ゼオン社
製）１００重量部、ステアリン酸カルシウム１．０重量
部、Ａ型ゼオライト（ミズカライザ−ＤＳ 水沢化学工
業社製）０．３重量部、ジオクチル錫ビス（イソオクチ
ルメルカプトアセテ−ト）０．５重量部、炭酸カルシウ
ム３．０重量部、酸化チタン０．３重量部及び一般式
（２）又は（３）で表される有機錫硫黄化合物０．５重
量部を添加し、１９０℃の混練ロールにて３分間混練
し、得られた厚さ０．５ｍｍのシ−トの一部を１９５℃
のオーブンに入れて、熱安定性試験を行って、白色から
黒化するまでを１０段階で評価した。また、シ−トの残
りの部分を、１８０℃で２５分間プレスして初期着色性
試験を行った。初期着色性の評価は、東京電色カラ−エ
−スＴＣ−ＰＴ３で黄色度（ＹＩ）を測定した。これら
の試験結果を第１表に示す。
製）１００重量部、ステアリン酸カルシウム１．０重量
部、Ａ型ゼオライト（ミズカライザ−ＤＳ 水沢化学工
業社製）０．３重量部、ジオクチル錫ビス（イソオクチ
ルメルカプトアセテ−ト）０．５重量部、炭酸カルシウ
ム３．０重量部、酸化チタン０．３重量部及び一般式
（２）又は（３）で表される有機錫硫黄化合物０．５重
量部を添加し、１９０℃の混練ロールにて３分間混練
し、得られた厚さ０．５ｍｍのシ−トの一部を１９５℃
のオーブンに入れて、熱安定性試験を行って、白色から
黒化するまでを１０段階で評価した。また、シ−トの残
りの部分を、１８０℃で２５分間プレスして初期着色性
試験を行った。初期着色性の評価は、東京電色カラ−エ
−スＴＣ−ＰＴ３で黄色度（ＹＩ）を測定した。これら
の試験結果を第１表に示す。
【００２０】
【表１】
【００２１】実施例９〜１３ 塩化ビニル樹脂（カネビニ−ルＳ−１００３ 鐘淵化学
工業社製）１００重量部、耐衝撃強化剤（カネエースＢ
−５６１ 鐘淵化学工業社製）１０重量部、ステアリン
酸カルシウム０．５重量部、ハイドロタルサイト（アル
カマイザ−２ 協和化学工業社製）０．５重量部、酸化
チタン０．３重量部及び一般式（１）乃至（３）で表さ
れる有機錫硫黄化合物２．０重量部を添加し、実施例１
〜８の場合と同様の試験を行い評価した。これらの試験
結果を第２表に示す。
工業社製）１００重量部、耐衝撃強化剤（カネエースＢ
−５６１ 鐘淵化学工業社製）１０重量部、ステアリン
酸カルシウム０．５重量部、ハイドロタルサイト（アル
カマイザ−２ 協和化学工業社製）０．５重量部、酸化
チタン０．３重量部及び一般式（１）乃至（３）で表さ
れる有機錫硫黄化合物２．０重量部を添加し、実施例１
〜８の場合と同様の試験を行い評価した。これらの試験
結果を第２表に示す。
【００２２】
【表２】
【００２３】実施例１４〜１７ 塩化ビニル樹脂（Ｇｅｏｎ１０２ＥＰ 日本ゼオン社
製）１００重量部、耐衝撃強化剤（ダイソラックＨ−１
３５ ダイソ−社製）８重量部、ステアリン酸カルシウ
ム０．３重量部、水酸化マグネシウム（キョ−ワスイマ
グＦ 協和化学工業社製）１．０重量部、酸化チタン
０．１重量部及び一般式（１）乃至（３）で表される有
機錫硫黄化合物１．５重量部を添加し、実施例１〜８の
場合と同様の試験を行い評価した。これらの試験結果を
第３表に示す。
製）１００重量部、耐衝撃強化剤（ダイソラックＨ−１
３５ ダイソ−社製）８重量部、ステアリン酸カルシウ
ム０．３重量部、水酸化マグネシウム（キョ−ワスイマ
グＦ 協和化学工業社製）１．０重量部、酸化チタン
０．１重量部及び一般式（１）乃至（３）で表される有
機錫硫黄化合物１．５重量部を添加し、実施例１〜８の
場合と同様の試験を行い評価した。これらの試験結果を
第３表に示す。
【００２４】
【表３】
【００２５】
【効果】第１表から、モノ有機錫アルキルメルカプトア
セテ−トを添加するよりも、モノ有機錫２−メルカプト
エチル脂肪酸を添加した場合の方が、ハロゲン含有樹脂
の熱安定性及び初期着色性が共に良好となることが窺え
る。また、第２表から、ジ有機錫２−メルカプトエチル
脂肪酸を添加するよりも、ジ有機錫アルキルメルカプト
アセテ−トを添加した場合の方が、当該樹脂の熱安定性
及び初期着色性が共に良好となる。さらに、第３表から
ビス（ジ有機錫２−メルカプトエチル脂肪酸）サルファ
イドを添加するよりも、ビス〔モノ有機錫ビス（２−メ
ルカプトエチル脂肪酸）〕サルファイドを添加した場合
の方が熱安定性及び初期着色性が良好となる。実施例１
〜１７の熱安定性試験及び初期着色性試験の結果から明
らかなように、ハロゲン含有樹脂に前記した（ａ）〜
（ｄ）の化合物を併用添加すれば、熱安定性が良好で初
期着色性の少ない高温加工に適したハロゲン含有樹脂組
成物が得られる。
セテ−トを添加するよりも、モノ有機錫２−メルカプト
エチル脂肪酸を添加した場合の方が、ハロゲン含有樹脂
の熱安定性及び初期着色性が共に良好となることが窺え
る。また、第２表から、ジ有機錫２−メルカプトエチル
脂肪酸を添加するよりも、ジ有機錫アルキルメルカプト
アセテ−トを添加した場合の方が、当該樹脂の熱安定性
及び初期着色性が共に良好となる。さらに、第３表から
ビス（ジ有機錫２−メルカプトエチル脂肪酸）サルファ
イドを添加するよりも、ビス〔モノ有機錫ビス（２−メ
ルカプトエチル脂肪酸）〕サルファイドを添加した場合
の方が熱安定性及び初期着色性が良好となる。実施例１
〜１７の熱安定性試験及び初期着色性試験の結果から明
らかなように、ハロゲン含有樹脂に前記した（ａ）〜
（ｄ）の化合物を併用添加すれば、熱安定性が良好で初
期着色性の少ない高温加工に適したハロゲン含有樹脂組
成物が得られる。
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｋ 5/58 ＫＪＣ Ｃ０８Ｋ 5/58 ＫＪＣ Ｃ０８Ｌ 23/28 ＫＦＲ Ｃ０８Ｌ 23/28 ＫＦＲ
Claims (1)
- 【請求項１】ハロゲン含有樹脂１００重量部に対して、
（ａ）ステアリン酸カルシウム０．１〜３重量部、
（ｂ）Ａ型ゼオライト類、ハイドロタルサイト類及び水
酸化マグネシウム（若しくは表面処理をした水酸化マグ
ネシウム）の少なくとも一種０．０１〜２重量部、
（ｃ）一般式（１） 【化１】 （式中、Ｒは炭素数１〜１８の直鎖若しくは分枝を有す
るアルキル基又は炭素数１〜２０のアルコキシカルボニ
ルエチル基を、Ｒ1 は炭素数１〜３６の直鎖若しくは分
枝を有するアルキル基、アルケニル基又はアラルキル基
をそれぞれ示す）で表される有機錫硫黄化合物０．１〜
３重量部及び（ｄ）一般式（２）および（３） 【化２】 【化３】 （各式中、Ｒは炭素数１〜１８の直鎖若しくは分枝を有
するアルキル基又は炭素数１〜２０のアルコキシカルボ
ニルエチル基を、Ｒ2 は炭素数１〜２２の脂肪酸の残基
又は芳香族酸の残基をそれぞれ示す）で表される有機錫
硫黄化合物の少なくとも一種０．０１〜３重量部を含有
する高温加工に適したハロゲン含有樹脂組成物。