JPH09174784A - 防火室用の絶縁層 - Google Patents

防火室用の絶縁層

Info

Publication number
JPH09174784A
JPH09174784A JP8328456A JP32845696A JPH09174784A JP H09174784 A JPH09174784 A JP H09174784A JP 8328456 A JP8328456 A JP 8328456A JP 32845696 A JP32845696 A JP 32845696A JP H09174784 A JPH09174784 A JP H09174784A
Authority
JP
Japan
Prior art keywords
layer
insulating layer
composite insulating
thickness
iss
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP8328456A
Other languages
English (en)
Inventor
Hermann Seibert
ザイベルト ヘルマン
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Roehm GmbH Darmstadt
Original Assignee
Roehm GmbH Darmstadt
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Roehm GmbH Darmstadt filed Critical Roehm GmbH Darmstadt
Publication of JPH09174784A publication Critical patent/JPH09174784A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【課題】 防火室用の絶縁層 【解決手段】 本発明は、有利に造船において使用する
ための複合絶縁層ＩＳＳに関し、これは、 ｉ）金属薄板から成る外層ＡＳから、 ii）メラミン層ＭＳＳ iii）アルミニウム薄板層 iv）両側をフェノール樹脂プリプレグＰＮＰを用いて被
覆された、硬質フォームＨＳＳのコア層と組み合わされ
て構成されている。

Description

【発明の詳細な説明】
【０００１】
【発明の属する技術分野】本発明は、殊に造船における
防火室用の新規絶縁層に関する。
【０００２】
【従来の技術】防火室の提供は、従来から文明の発達に
伴う１つの課題である。化学工業は、無機ベースでも有
機ベースでも耐火材料を開発することにより決定的に防
火に貢献した（Kirk-Othmer, Encyclopedia of Chemica
l Technology, 3rd Ed. Vol. 10, 348-444, J. Wiley,
1980; ibidem Vol. 13, 598-605, J. Wiley, 1981 参
照）。
【０００３】個人の分野を超えて、防火は公共の分野で
も軍事的分野でも、特に比較的多数の人命の危険の観点
の下に発達した。
【０００４】場所的に固定的な交通の中心又は集まりの
中心地、例えば駅、ホテル、コンサートホール及び劇場
広間、講堂、教会、病院、銀行、公的及び民間の管理棟
等における以外に、人の集まりは、鉄道、航空交通及び
水上交通の分野においても発生する。最後の二つの交通
手段では、火災の場合の制限された避難の可能性の時機
は、比較的小さな又は比較的大きな災害でも常に一般的
意識の中で高められる大きな問題である。
【０００５】現代の大量輸送における特別な危険の潜在
性により、ここには当然、公的関心の重点が有り、この
ことは、特に制限的な立法及び厳しい国内的及び国際的
認可又は許可の実際に表れている。潜在的に危険にさら
されている空間をできるだけ最適に断熱することが、こ
れらの当然な防護措置に属する。
【０００６】断熱とは、通常、ある材料又は材料層の、
熱伝達に対する抵抗として定義されている（例えばＡＳ
ＴＭ Ｃ １６８参照）。
【０００７】造船においては、国際海事機構（ＩＭＯ）
が定めた火災規定が通用している。
【０００８】ＩＭＯは、客船、貨物船及び漁船は一定の
防火措置を施されていなければならないことを規定して
いる。ＩＭＯは、好適な絶縁層により高すぎる温度作用
から保護されるべき、船の種々の構造群を区別してい
る。決議Ａ．７５４（１８）の中に、これらの構造群が
記載されており、相応する絶縁層がどのような要求を満
たさなければならないかが規定されている。絶縁層に、
厳密に規定された経過に従って片側に温度を当てる。こ
れは、次のように行なう： 最初の５分の経過の後の温度５７６℃ 最初の１０分の経過の後の温度６７９℃ 最初の１５分の経過の後の温度７３８℃ 最初の３０分の経過の後の温度８４１℃ 最初の６０分の経過の後の温度９４５℃ この絶縁層の、熱源から逸らされた側面で、測定温度
は、その際１４０℃を超えてはならない。
【０００９】構造群及び熱適用の時間に応じて、次の分
類で区別する： Ａ−６０ ６０分＝最も厳しい試験 Ａ−３０ ３０分 Ａ−１５ １５分 Ａ−０ ０分 Ｂ−３０ ３０分 Ｂ−１５ １５分 Ｂ−０ ０分 Ｆ−３０ ３０分 Ｆ−１５ １５分 Ｆ−０ ０分 この技術は、反射性の金属外層及び鉱物綿内層を有する
多層の断熱材を起用するのが有利である（Kirk-Othmer,
Vol. 13, loc.cit., pg. 596 参照）。造船においては
現在、鋼板／岩綿／鋼板の構成を有する絶縁層が使用さ
れている。絶縁層への要求に応じて、個々の層の厚さは
異なり、それに伴い当然、総厚及び単位面積当たりの重
量は異なる。
【００１０】
【発明が解決しようとする課題】原則的に、そのような
絶縁層は高い単位面積当たりの重量を有するということ
がいえる。このことは、特にＡ−６０、Ａ−３０、Ｂ−
３０及びＦ−３０絶縁層に当てはまる。存在する絶縁層
の高い単位面積当たりの重量に基づいて、著しい重量問
題が生じ、大きな客船の場合の高すぎる重心位置により
付加的な問題が生じる。造船において、益々高速の船へ
の趨勢が観察されるので、防火絶縁の際にも、重量を節
減し、推進動力を節減し、エネルギー消費を引き下げる
ために軽量建造の解決策が求められている。
【００１１】前記の記載から、殊に当然、現行の安全規
程を満たさなければならない造船用の、より軽量な絶縁
層への技術の要望が明確になる。
【００１２】特に下記の要求を満足する絶縁層が求めら
れる： １．分類Ａ−６０、Ａ−３０、Ａ−１５／Ｂ−３０、Ｂ
−１５／Ｆ−３０、Ｆ−１５ ２．Ａ−６０に関する総厚＜８０ｍｍ ３．Ａ−６０に関する単位面積当たりの重量＜２０ｋｇ
／ｍ2 この絶縁層は、試験温度／試験時間の影響下でも、その
構造的特性を失うべきではない。
【００１３】使用される材料の選択は、第一に、炭素含
有材料、例えば有機合成ポリマーを原則的に可燃性とし
て分類しなければならないことにより制限されているよ
うである（Kirk-Othmer, Vol. 10, loc.cit., pg. 34
8）。但しアルミニウムも、好適な条件下では可燃性と
して分類するべきである。
【００１４】
【課題を解決するための手段】全く意想外に、本発明に
よる絶縁層は、造船技術の要求、殊にＩＭＯ規格Ａ−６
０による防火絶縁テストを満足することを見出した。本
発明による複合絶縁層ＩＳＳは、 ｉ）金属薄板、例えばアルミニウム薄板から成る、有利
に０.５ｍｍの層厚を有する外層ＡＳから、 ii）有利に４２ｍｍの層厚を有するメラミンフォーム層
ＭＳＳ、 iii）０.５ｍｍの層厚を有する金属薄板、例えばアルミ
ニウム薄板 iv）両側を、有利に０.３ｍｍ層厚のフェノール樹脂プ
リプレグＰＮＰを用いて被覆された、硬質フォームＨＳ
Ｓ、例えばポリ（メタ）アクリルイミドフォーム（ＰＭ
Ｉフォーム）ＰＭＩ−ＳＳの、有利に３０ｍｍの層厚を
有するコア層と組み合わされて構成されている。
【００１５】複合絶縁層ＩＳＳの層厚に関する基準値と
しては、２０±１ｋｇ／ｍ2、有利には１９ｋｇ／ｍ2の
単位面積当たりの重量の場合に、７０〜７５ｍｍ、特に
７３.６ｍｍの値である。
【００１６】絶縁層ＩＳＳの個々の層成分は、自体公知
である：本発明によるメラミンフォームＭＳＳとして
は、自体公知の市販品（Ullman′s Encyclopedia of In
dustrial Chemistry, 5th Ed., Vol. A11, pg. 453, VC
H 1988 参照）、例えば２１０ｋｇ／ｍ3の単位面積当た
りの重量を有する、ＧＬＡＳＩＳ ＡＢセロカー（Soer
aker）（スウェーデン）社の製品リコア（ＲＥＣＯＲ
Ｅ：登録商標）を使用することができる。メラミンフォ
ーム層ii）の厚さ及び密度を変化させることによって
も、層iv）の厚さ及び密度を変化させることによって
も、上記の全ての分類に関して、技術水準の系よりも著
しく軽い、重量最適化された構造を見出すことができ
る。
【００１７】層の組合せの硬質フォームコア層iv）とし
ては、ポリ（メタ）アクリルイミド、例えばＰＭＩフォ
ーム、ポリメチルメタクリレート（ＰＭＭＡ）、ポリ塩
化ビニル（ＰＶＣ）、アクリルニトリル−ブタジエン−
スチレンコポリマー（ＡＢＳ）、ポリカーボネート（Ｐ
Ｃ）をベースとする自体公知の硬質フォーム、更にポリ
オレフィン、アセチルセルロース、エポキシ樹脂、ポリ
スチレン、ポリエーテルイミド、ポリアミド、ポリイミ
ド、ポリフェニレンオキシド、ポリスルホン及びポリウ
レタンをベースとする硬質フォームがこれに該当する。
より詳細な記載は、例えば H.F. Mark et al., Encyclo
pedia of Polymer, Science & Engineering, Vol. 3, 1
-49, J. Wiley, 1985; Ullmann′s Encyclopedia of In
dustrialChemistry 5th Ed. Vol. A 11, 435-464, VCH
1988 又はドイツ特許（ＤＥ−Ａ）第４２０７０５７号
明細書から読み取ることができる。
【００１８】層iv）のプリプレグとしては、殊にフェノ
ール−ノボラック−プリプレグが効を奏した。
【００１９】本発明は、ポリメタクリルイミドフォーム
の例により詳述されている（Ullmann′s Encuyclopedia
A 11 loc.cit., pg. 456 参照）。
【００２０】ポリメタクリルイミドフォーム（ＰＭＩ−
ＳＳ）は、例えば英国特許（ＧＢ−Ａ）第１０７８４２
５号及び同第１０４５２２９号明細書中及びドイツ特許
（ＤＴ−ＰＳ）第１８１７１５６号明細書中に記載され
ている。それらは、特性単位としてイミド基を有する環
状構造体を含有している。それらの熱形状安定性（Waer
meformbestaendigkeit）（ＤＩＮ５３４２４による）
は、通常、１８０〜２２０℃の範囲にある。このような
ＰＭＩポリマーフォームは市販であり、Ｒｏｅｈｍ社の
商標名ロハセル（ＲＯＨＡＣＥＬＬ：登録商標）なる名
称で入手可能である。製品ロハセル５１Ｓを使用するの
が有利である。
【００２１】
【実施例】本発明の場合は、層iv）のポリメタクリルイ
ミドフォーム（ＰＭＩ−ＳＳ）の単位面積当たりの重量
は、通常、〜５２±１２ｋｇ／ｍ3である。
【００２２】層iv）の中に存在するような複合材料は、
記載のように、同様に自体公知である（B. Carlowitz H
rsg. Die Kunststoffe, Kunststoff-Handbuch, Bd. 1,
321,484, C. Hanser, 1990 参照）。
【００２３】ＰＭＩコア層の場合には、例えば英国特許
（ＧＢ）第２１３４８４５号、ドイツ特許（ＤＥ−Ａ）
第２９２７１２２号、同第３３０４８６２号；米国特許
（ＵＳ）第４３１６９３４号；ヨーロッパ特許（ＥＰ）
第０２２１６８号；ヨーロッパ特許（ＥＰ−Ａ）第３１
０５６１号明細書を拠り所とすることができる。
【００２４】層iv）の製造のためには、型の内側の、相
応して寸法決定されたフォーム板上にプリプレグ材を重
量に合わされた量で積層し、成形圧をかけるのが有利で
ある。このプリプレグの、繊維含有プラスチック材料
は、表面的に軟化し、隣接しているフォーム層の孔内で
層の固定が起こる。
【００２５】そのプリプレグが流れ、かつ硬化し始める
典型的な作業条件は、１Ｎ／ｍｍ2の圧力及び６０〜１
８０℃の範囲の温度である。加圧時間は、通常１２分〜
１２０分であり、特に有利な範囲は１２〜３０分であ
る。
【００２６】層iv）の成分として使用されるプリプレグ
は、通常のように、室温では固体状であり、加熱の際に
流動性である、場合によってはロープ状物、織物又はフ
リースの形の、埋め込まれた繊維を有する層状樹脂であ
る。これらの樹脂は、フェノール樹脂、例えばフェノー
ル−ノボラック−熱硬化性樹脂から成る（H.F. Market
al., Encyclopedia of Polymer Science & Engineerin
g, Vol. 11, 62-84, J. Wiley, 1988 参照）。
【００２７】複合絶縁層ＩＳＳの個々の層は、公知の方
法で継ぎ合わせるか又は共通の枠内で使用することがで
きる。
【００２８】本発明による複合絶縁層ＩＳＳは、既に記
載のように、技術水準の要求、殊にＩＭＯにより規定さ
れた基準を満たし、その際、層ii）及びiv）の層厚を変
えることにより、記載の全分類への適合に達することが
できる。
【００２９】
【発明の効果】本発明による複合絶縁層は、殊に造船の
厳しい規程を満足する防火室の提供を許す。これは、著
しい重量節減の可能性を意味しており、それに伴い、燃
料のより良好な利用及び船舶輸送における、より高い採
算性にも貢献する。

Claims (5)

    【特許請求の範囲】
  1. 【請求項１】 複合絶縁層ＩＳＳにおいて、 ｉ）金属薄板から成る外層から、 ii）メラミンフォーム層ＭＳＳ iii）金属薄板層 iv）両側をフェノール樹脂プリプレグＰＮＰで被覆され
    た、硬質フォームＨＳＳのコア層と組み合わされて構成
    されている複合絶縁層。
  2. 【請求項２】 層ｉ）及び／又は層iii）がアルミニウ
    ム薄板から成る、請求項１に記載の複合絶縁層ＩＳＳ。
  3. 【請求項３】 ２０±１ｋｇ／ｍ2の単位面積当たりの
    重量での複合絶縁層の総厚が７０〜７５ｍｍである、請
    求項１に記載の複合絶縁層ＩＳＳ。
  4. 【請求項４】 層ｉ）が約０.５ｍｍの層厚を有し、層i
    i）が約４２ｍｍの層厚を有し、層iii）が約０.５ｍｍ
    の層厚を有し、層iv）が約３０ｍｍの層厚及び各約０.
    ３ｍｍのプリプレグ層ＰＮＰを有する、請求項１から３
    のいずれかに記載の複合絶縁層ＩＳＳ。
  5. 【請求項５】 国際海事機構の造船における防火規定を
    満足する、請求項１から４のいずれかに記載の複合絶縁
    層ＩＳＳ。
JP8328456A 1995-12-20 1996-12-09 防火室用の絶縁層 Pending JPH09174784A (ja)