JPH10273579A - Polyacetal resin composition - Google Patents
Polyacetal resin compositionInfo
- Publication number
- JPH10273579A JPH10273579A JP8031697A JP8031697A JPH10273579A JP H10273579 A JPH10273579 A JP H10273579A JP 8031697 A JP8031697 A JP 8031697A JP 8031697 A JP8031697 A JP 8031697A JP H10273579 A JPH10273579 A JP H10273579A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- polyacetal resin
- hydroxide
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 優れた耐熱性を持ち、加熱変色が改良された
ポリアセタール樹脂組成物を提供する。
【解決手段】 (A) ポリアセタール樹脂 100重量部に対
し、(B) 立体障害性フェノール系酸化防止剤 0.001〜３
重量部、(C) アルカリ金属又はアルカリ土類金属の水酸
化物、有機酸のアルカリ金属塩、有機酸のアルカリ土類
金属塩から選ばれる少なくとも１種0.01〜５重量部と
(D) ホウ酸化合物 0.001〜３重量部を配合する。(57) [Problem] To provide a polyacetal resin composition having excellent heat resistance and improved heat discoloration. SOLUTION: (A) 100 parts by weight of polyacetal resin, (B) sterically hindered phenolic antioxidant 0.001 to 3
Parts by weight, (C) at least one selected from the group consisting of an alkali metal or alkaline earth metal hydroxide, an organic acid alkali metal salt and an organic acid alkaline earth metal salt, in an amount of 0.01 to 5 parts by weight.
(D) A boric acid compound is added in an amount of 0.001 to 3 parts by weight.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ポリアセタール樹
脂に立体障害性フェノール系酸化防止剤と特定の塩基性
化合物とホウ酸化合物を配合してなる、加熱時の変色が
少ないポリアセタール樹脂組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyacetal resin composition obtained by blending a polyacetal resin with a sterically hindered phenolic antioxidant, a specific basic compound and a boric acid compound and having little discoloration upon heating.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】ポリア
セタール樹脂は機械的性質、耐疲労性、耐摩擦・摩耗
性、耐薬品性、及び成形性に優れ、自動車、電気・電子
機器、その他の精密機械、建材配管等に利用されてい
る。これらの利用目的で使用されるポリアセタール樹脂
には、耐熱安定性を改善するために、無機又は有機の塩
基性化合物を添加することがしばしば行われる。しかし
ながら、この塩基性化合物は、樹脂組成物の溶融時ない
しは溶融温度以下での加熱時に、樹脂組成物を着色させ
やすいことが知られている。この着色を防止するため
に、蛍光増白剤の添加などがなされているが、満足でき
るものではなく、改善が望まれている。2. Description of the Related Art Polyacetal resins are excellent in mechanical properties, fatigue resistance, friction / wear resistance, chemical resistance, and moldability, and are used in automobiles, electric / electronic devices, and other precision products. It is used for machinery, building material piping, etc. In order to improve the heat resistance stability, an inorganic or organic basic compound is often added to the polyacetal resin used for these purposes. However, it is known that this basic compound tends to color the resin composition when the resin composition is melted or heated at a temperature lower than the melting temperature. In order to prevent this coloring, addition of a fluorescent whitening agent or the like has been made, but this is not satisfactory, and improvement is desired.
【０００３】[0003]
【課題を解決するための手段】本発明者等は、上記課題
に鑑み、優れた耐熱性を持ち、加熱変色が改良されたポ
リアセタール樹脂組成物を得るべく鋭意検討した。その
結果、立体障害性フェノール系酸化防止剤と特定の塩基
性化合物と特定の硼酸化合物をポリアセタール樹脂に添
加、溶融混練することによって、かかる問題が顕著に改
善されることを見出し、本発明を完成するに至った。即
ち、本発明は (A) ポリアセタール樹脂 100重量部に (B) 立体障害性フェノール系酸化防止剤 0.001〜３重量
部 (C) アルカリ金属又はアルカリ土類金属の水酸化物、有
機酸のアルカリ金属塩、有機酸のアルカリ土類金属塩か
ら選ばれる少なくとも１種0.01〜５重量部と (D) ホウ酸化合物 0.001〜３重量部を配合してなる、ポ
リアセタール樹脂組成物に関するものである。Means for Solving the Problems In view of the above problems, the present inventors have intensively studied to obtain a polyacetal resin composition having excellent heat resistance and improved heat discoloration. As a result, they have found that the problem is remarkably improved by adding a sterically hindered phenolic antioxidant, a specific basic compound and a specific boric acid compound to a polyacetal resin and melt-kneading the same, and completed the present invention. I came to. That is, the present invention relates to (A) 100 parts by weight of a polyacetal resin, (B) 0.001 to 3 parts by weight of a sterically hindered phenolic antioxidant, (C) a hydroxide of an alkali metal or an alkaline earth metal, and an alkali metal of an organic acid. The present invention relates to a polyacetal resin composition comprising 0.01 to 5 parts by weight of at least one selected from salts and alkaline earth metal salts of organic acids and 0.001 to 3 parts by weight of a (D) boric acid compound.
【０００４】[0004]
【発明の実施の形態】以下に本発明の構成成分について
説明する。本発明に用いられるポリアセタール樹脂(A)
とは、オキシメチレン基（-CH2O-）を主たる構成単位と
する高分子化合物で、オキシメチレン基以外に他の構成
単位を少量含有するポリアセタールコポリマー（例え
ば、ポリプラスチックス社製、“ジュラコン”）が好ま
しく、特にコモノマー成分を１〜30重量％共重合させて
なるポリアセタールコポリマーが優れた熱安定性、機械
的強度等を保持できるので好ましい。又、ポリアセター
ルコポリマーは、分子が線状のみならず、分岐構造、架
橋構造を有するものであってもよい。ポリアセタール樹
脂の粘度は成形が可能な限り特に限定されないが、ＭＩ
が１〜100g/min、特に５〜50 g/minのものが好ましい。
ポリアセタールコポリマーの製造に用いるコモノマー成
分は特に限定されないが、一般的に下記に示した一般式
を有するものが用いられる。BEST MODE FOR CARRYING OUT THE INVENTION The components of the present invention will be described below. Polyacetal resin (A) used in the present invention
Is a polymer compound having an oxymethylene group (—CH 2 O—) as a main structural unit, and a polyacetal copolymer containing a small amount of other structural units in addition to the oxymethylene group (for example, “Duracon” manufactured by Polyplastics Co., Ltd.) ") Is preferred, and a polyacetal copolymer obtained by copolymerizing 1 to 30% by weight of a comonomer component is particularly preferred because it can maintain excellent heat stability, mechanical strength and the like. The polyacetal copolymer may have not only a linear molecule but also a branched structure or a crosslinked structure. The viscosity of the polyacetal resin is not particularly limited as long as molding is possible.
Is preferably 1 to 100 g / min, particularly preferably 5 to 50 g / min.
The comonomer component used for producing the polyacetal copolymer is not particularly limited, but those having the following general formula are generally used.
【０００５】[0005]
【化１】 Embedded image
【０００６】〔但し、R1、R2、R3、R4は同一又は異なる
置換基であり、水素原子、アルキル基（１〜５個の炭素
を有し、０〜３個の水素がハロゲン原子で置換されたも
の、以下同じ、又は、ハロゲンで置換されたアルキル基
を意味し、R5はメチレン基、オキシメチレン基、夫々ア
ルキル基もしくはオキシメチレン基（この場合、p ＝０
〜３の整数）、-(CH2)q -OCH2 （q ＝１〜４の整数）又
は -(O-CH2-CH2) q -OCH2(q ＝１〜４の整数）で示され
る２価の基（この場合p ＝１）を示す。〕 該コモノマーとしては、エチレンオキシド、エピクロル
ヒドリン、1,3 −ジオキソラン、ジエチレングリコール
ホルマール、1,4 −ブタンジオールホルマール、1,3 −
ジオキサン、プロピレンオキシド等が挙げられる。Wherein R 1 , R 2 , R 3 , and R 4 are the same or different substituents, and each represents a hydrogen atom, an alkyl group (having 1 to 5 carbon atoms, and 0 to 3 hydrogen atoms being halogen atoms); R 5 represents a methylene group, an oxymethylene group, an alkyl group or an oxymethylene group, respectively (in this case, p = 0)
-3 integer), - (CH 2) q -OCH 2 (q = 1~4 integer) or - indicated by (O-CH 2 -CH 2) q -OCH 2 (q = 1~4 integer) (P = 1 in this case). Examples of the comonomer include ethylene oxide, epichlorohydrin, 1,3-dioxolan, diethylene glycol formal, 1,4-butanediol formal, and 1,3-
Dioxane, propylene oxide and the like.
【０００７】次に本発明において使用される(B) 立体障
害性フェノール系酸化防止剤としては、2,2'−メチレン
ビス（４−メチル−６−ｔ−ブチルフェノール）、1,6
−ヘキサンジオール−ビス〔３−（3,5 −ジ−ｔ−ブチ
ル−４−ヒドロキシフェニル）プロピオネート〕、ペン
タエリスリトールテトラキス〔３−（3,5 −ジ−ｔ−ブ
チル−４−ヒドロキシフェニル）プロピオネート〕、ト
リエチレングリコールビス〔３−（3,5 −ジ−ｔ−ブチ
ル−４−ヒドロキシフェニル）プロピオネート〕、1,3,
5 −トリメチル−2,4,6 −トリス（3,5 −ジ−ｔ−ブチ
ル−４−ヒドロキシベンジル）ベンゼン、ｎ−オクタデ
シル−３−（４’−ヒドロキシ−3',5'−ジ−ｔ−ブチ
ルフェニル）プロピオネート、4,4'−メチレンビス（2,
6 −ジ−ｔ−ブチルフェノール）、4,4'−ブチリデンビ
ス−（６−ｔ−ブチル−３−メチルフェノール）、ジ−
ステアリル−3,5 −ジ−ｔ−ブチル−４−ヒドロキシベ
ンジルホスホネート、２−ｔ−ブチル−６−（３−ｔ−
ブチル−５−メチル−２−ヒドロキシベンジル）−４−
メチルフェニルアクリレート、N,N'−ヘキサメチレンビ
ス（3,5 −ジ−ｔ−ブチル−４−ヒドロキシ−ヒドロシ
ンナマミド）が挙げられる。本発明において添加配合さ
れる(B) 酸化防止剤の添加量は、(A) 成分 100重量部に
対して 0.001〜３重量部が好ましく、特に好ましくは0.
03〜１重量部である。0.01重量部より過少の場合はポリ
アセタール樹脂の分解を抑制する効果が小さく、また、
３重量部より過大にしても増量の影響が見られず、経済
的にも不利となる。Next, (B) sterically hindered phenolic antioxidants used in the present invention include 2,2'-methylenebis (4-methyl-6-t-butylphenol) and 1,6
-Hexanediol-bis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate], pentaerythritol tetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate ], Triethylene glycol bis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate], 1,3,
5-trimethyl-2,4,6-tris (3,5-di-t-butyl-4-hydroxybenzyl) benzene, n-octadecyl-3- (4'-hydroxy-3 ', 5'-di-t -Butylphenyl) propionate, 4,4′-methylenebis (2,
6-di-t-butylphenol), 4,4′-butylidenebis- (6-t-butyl-3-methylphenol), di-
Stearyl-3,5-di-t-butyl-4-hydroxybenzylphosphonate, 2-t-butyl-6- (3-t-
Butyl-5-methyl-2-hydroxybenzyl) -4-
Methylphenyl acrylate and N, N'-hexamethylenebis (3,5-di-t-butyl-4-hydroxy-hydrocinnamamide). The amount of the (B) antioxidant added and blended in the present invention is preferably 0.001 to 3 parts by weight, particularly preferably 0.1 part by weight, per 100 parts by weight of the component (A).
03 to 1 part by weight. If the amount is less than 0.01 part by weight, the effect of suppressing the decomposition of the polyacetal resin is small, and
If the amount is more than 3 parts by weight, the effect of increasing the amount is not seen, and this is economically disadvantageous.
【０００８】次に本発明で用いられる(C) 成分は、アル
カリ金属又はアルカリ土類金属の水酸化物、有機酸のア
ルカリ金属塩、有機酸のアルカリ土類金属塩から選ばれ
る少なくとも１種であり、具体的には、ナトリウム、カ
リウム、マグネシウム、カルシウム、バリウム等の水酸
化物、並びにこれら金属の蓚酸塩、マロン酸塩、こはく
酸塩、アジピン酸塩、ステアリン酸塩の如き高級脂肪酸
及び水酸基等の置換基を有する置換高級脂肪酸の塩など
が挙げられる。本発明で使用されるアルカリ金属の水酸
化物としては水酸化リチウム、水酸化ナトリウム、水酸
化カリウムが挙げられるが、水酸化ナトリウム、水酸化
カリウムが好ましい。本発明で使用されるアルカリ土類
金属の水酸化物としては水酸化マグネシウム、水酸化カ
ルシウム、水酸化ストロンチウム、水酸化バリウムが挙
げられるが、水酸化マグネシウム、水酸化カルシウム、
水酸化ストロンチウムが好ましい。本発明で使用される
有機酸のアルカリ金属塩としては、酢酸ナトリウム、ア
ジピン酸ナトリウム、ラウリン酸ナトリウム、ステアリ
ン酸ナトリウム、モンタン酸ナトリウム、モンタン酸カ
リウム、ベヘン酸ナトリウム、ベヘン酸カリウム、安息
香酸ナトリウム、安息香酸カリウム、テレフタル酸ナト
リウム、テレフタル酸カリウム等が挙げられるが、ステ
アリン酸ナトリウム、モンタン酸カリウムが好ましい。
本発明で使用される有機のアルカリ土類金属塩として
は、酢酸マグネシウム、酢酸カルシウム、アジピン酸マ
グネシウム、アジピン酸カルシウム、ラウリン酸マグネ
シウム、ラウリン酸カルシウム、ステアリン酸マグネシ
ウム、ステアリン酸カルシウム、12−ヒドロキシステア
リン酸カルシウム、ステアリン酸ストロンチウム、ステ
アリン酸バリウム、パルミチン酸マグネシウム、パルミ
チン酸カルシウム、乳酸マグネシウム、乳酸カルシウ
ム、モンタン酸マグネシウム、モンタン酸カルシウム、
モンタン酸バリウム、ベヘン酸マグネシウム、ベヘン酸
カルシウム、ベヘン酸バリウム、安息香酸マグネシウ
ム、安息香酸カルシウム、安息香酸バリウム、テレフタ
ル酸マグネシウム、テレフタル酸カルシウム等が挙げら
れるが、ステアリン酸カルシウム、12−ヒドロキシステ
アリン酸カルシウム、ステアリン酸マグネシウム、パル
ミチン酸マグネシウム、パルミチン酸カルシウム、ベヘ
ン酸カルシウム、ベヘン酸マグネシウム、ステアリン酸
カルシウム／パルミチン酸カルシウム混合物、ステアリ
ン酸マグネシウム／パルミチン酸マグネシウム混合物が
好ましい。前記のアルカリ金属の水酸化物、アルカリ土
類金属の水酸化物、有機酸のアルカリ金属塩、有機酸の
アルカリ土類金属塩は無水塩であっても結晶水を含んで
いてもかまわない。又、(C) 成分の配合量は、(A) 成分
100重量部に対して0.01〜５重量部、好ましくは 0.5〜
３重量部である。0.01重量部未満では耐熱安定性或いは
ホルムアルデヒドガス捕捉には不十分であり、５重量部
を越えるとポリアセタールの分解が起こり、成形加工等
が困難となる。The component (C) used in the present invention is at least one selected from hydroxides of alkali metals or alkaline earth metals, alkali metal salts of organic acids, and alkaline earth metal salts of organic acids. Yes, specifically, hydroxides such as sodium, potassium, magnesium, calcium, barium and the like, and higher fatty acids such as oxalate, malonate, succinate, adipate, stearate and hydroxyl group of these metals. And the like, and salts of substituted higher fatty acids having a substituent such as Examples of the alkali metal hydroxide used in the present invention include lithium hydroxide, sodium hydroxide, and potassium hydroxide, and sodium hydroxide and potassium hydroxide are preferred. Examples of the alkaline earth metal hydroxide used in the present invention include magnesium hydroxide, calcium hydroxide, strontium hydroxide, barium hydroxide, magnesium hydroxide, calcium hydroxide,
Strontium hydroxide is preferred. Examples of the alkali metal salt of an organic acid used in the present invention include sodium acetate, sodium adipate, sodium laurate, sodium stearate, sodium montanate, potassium montanate, sodium behenate, potassium behenate, sodium benzoate, Examples include potassium benzoate, sodium terephthalate, potassium terephthalate and the like, with sodium stearate and potassium montanate being preferred.
Examples of the organic alkaline earth metal salt used in the present invention include magnesium acetate, calcium acetate, magnesium adipate, calcium adipate, magnesium laurate, calcium laurate, magnesium stearate, calcium stearate, calcium 12-hydroxystearate, Strontium stearate, barium stearate, magnesium palmitate, calcium palmitate, magnesium lactate, calcium lactate, magnesium montanate, calcium montanate,
Barium montanate, magnesium behenate, calcium behenate, barium behenate, magnesium benzoate, calcium benzoate, barium benzoate, magnesium terephthalate, calcium terephthalate, etc., include calcium stearate, calcium 12-hydroxystearate, Magnesium stearate, magnesium palmitate, calcium palmitate, calcium behenate, magnesium behenate, calcium stearate / calcium palmitate mixtures, magnesium stearate / magnesium palmitate mixtures are preferred. The alkali metal hydroxide, alkaline earth metal hydroxide, organic acid alkali metal salt, and organic acid alkaline earth metal salt may be anhydrous or contain crystallization water. The amount of component (C) is
0.01 to 5 parts by weight, preferably 0.5 to 5 parts by weight per 100 parts by weight
3 parts by weight. If the amount is less than 0.01 part by weight, heat resistance or formaldehyde gas trapping is insufficient. If the amount exceeds 5 parts by weight, polyacetal is decomposed, making molding and the like difficult.
【０００９】本発明で使用される(D) ホウ酸化合物とし
ては、オルトホウ酸、メタホウ酸及び四ホウ酸等のホウ
酸類、三酸化二ホウ素等の酸化ホウ素類などが挙げら
れ、市販品を用いることが出来る。また、その粒径等に
対して特に制限はない。本発明において添加配合される
(D) ホウ酸化合物の量は(A) 成分 100重量部に対して
0.001〜３重量部、好ましくは 0.005〜１重量部、特に
好ましくは、0.01〜0.5 重量部である。この添加量が、
過小の場合は充分なる効果が得られず、また過大の場合
には、変色抑制の効果が飽和に達し、むしろ熱安定性の
悪化を招き好ましくない。Examples of the boric acid compound (D) used in the present invention include boric acids such as orthoboric acid, metaboric acid and tetraboric acid, and boron oxides such as diboron trioxide. Commercially available products are used. I can do it. There is no particular limitation on the particle size and the like. It is added and blended in the present invention.
(D) The amount of the boric acid compound is based on 100 parts by weight of the component (A).
0.001 to 3 parts by weight, preferably 0.005 to 1 part by weight, particularly preferably 0.01 to 0.5 part by weight. This addition amount
If the amount is too small, a sufficient effect cannot be obtained, and if the amount is too large, the effect of suppressing discoloration reaches saturation, and the thermal stability is rather deteriorated, which is not preferable.
【００１０】本発明に用いるポリアセタール樹脂には、
更に公知の各種添加剤を配合し得る。例えば、各種の着
色剤、離型剤、核剤、帯電防止剤、その他の界面活性
剤、各種ポリマー等である。また、本発明の目的とする
組成物成形品の性能を大幅に低下させないような範囲で
あるならば、公知の無機、有機、及び金属等の繊維状、
板状、粉粒状等の充填剤を１種または２種以上複合させ
て配合することも可能である。このような充填剤の例と
しては、ガラス繊維、ガラスビーズ、タルク、マイカ、
ウォラストナイト、炭素繊維等が挙げられるが、何等こ
れらに限定されるものではない。The polyacetal resin used in the present invention includes:
Further, various known additives can be blended. For example, various coloring agents, release agents, nucleating agents, antistatic agents, other surfactants, various polymers, and the like. In addition, if it is within a range that does not significantly reduce the performance of the composition molded article aimed at the present invention, known inorganic, organic, and fibrous such as metal,
It is also possible to mix one or more of plate-like and powder-like fillers. Examples of such fillers include glass fiber, glass beads, talc, mica,
Examples include wollastonite and carbon fiber, but are not limited thereto.
【００１１】本発明の組成物の調製法は特に制限がな
く、従来の樹脂組成物調製法として一般に用いられてい
る公知の設備と方法により容易に調製される。例えば、
ｉ）各成分を混合した後、押出機により練込押出してペ
レットを調製し、しかる後に成形する方法、ii）一旦組
成の異なるペレットを調製し、そのペレットを所定量混
合して成形に供し、成形後に目的組成の成形品を得る方
法、iii)成形機に各成分の１または２種以上を直接仕込
む方法等、何れも使用できる。また、樹脂成分の一部を
細かい粉体としてこれ以外の成分と混合し添加すること
は、これらの成分の均一配合を行なう上で好ましい方法
である。また、本発明に係る樹脂組成物は、押出成形、
射出成形、圧縮成形、真空成形、吹込成形、発泡成形の
何れによっても成形可能である。The method of preparing the composition of the present invention is not particularly limited, and it can be easily prepared by known equipment and methods generally used as conventional resin composition preparation methods. For example,
i) mixing each component, kneading and extruding with an extruder to prepare pellets, and then molding, ii) once preparing pellets having a different composition, mixing a predetermined amount of the pellets, and subjecting them to molding; Any method can be used, such as a method of obtaining a molded article having a desired composition after molding, and iii) a method of directly charging one or more of each component to a molding machine. Mixing and adding a part of the resin component as a fine powder with other components is a preferable method for uniformly mixing these components. Further, the resin composition according to the present invention, extrusion molding,
It can be formed by any of injection molding, compression molding, vacuum molding, blow molding and foam molding.
【００１２】[0012]
【発明の効果】本発明によれば、耐熱性に優れ、加熱に
よる色相変化が小さいポリアセタール樹脂組成物を提供
することができる。According to the present invention, it is possible to provide a polyacetal resin composition having excellent heat resistance and a small change in hue upon heating.
【００１３】[0013]
【実施例】以下、実施例により本発明を更に具体的に説
明するが、本発明はこれらの実施例に限定されるもので
はない。 実施例１〜９及び比較例１〜10 ポリアセタール樹脂（ポリプラスチックス（株）製、ジ
ュラコンＭ90）100 重量部に、表１に示す各種塩基性化
合物、各種立体障害性フェノール化合物、各種ホウ酸化
合物を配合し、シリンダー温度 200℃の押出機で溶融混
練し、ペレット状の組成物を調製した。次いで、このペ
レット状の組成物から射出成形機を用いて試験片を作成
し、以下に示す物性を測定した。比較のため、塩基性化
合物を添加しない組成物、ホウ酸化合物を添加しない組
成物及び立体障害性フェノール化合物を添加しない組成
物を同様の方法で調製し、評価を行った。結果を表２に
示す。尚、測定評価方法は以下の通りである。 ＜色相安定性＞試験片を成形し、初期の色相（b 値）と
140℃で５日間加熱し色相（b 値）を日本電色工業
（株）製Ｚ−３００Ａ型カラーセンサーで測定した。EXAMPLES The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. Examples 1 to 9 and Comparative Examples 1 to 10 100 parts by weight of a polyacetal resin (manufactured by Polyplastics Co., Ltd., Duracon M90) were mixed with various basic compounds, various sterically hindered phenol compounds and various boric acid compounds shown in Table 1. Was melt-kneaded with an extruder having a cylinder temperature of 200 ° C. to prepare a pellet-shaped composition. Next, test pieces were prepared from the pellet-shaped composition using an injection molding machine, and the physical properties shown below were measured. For comparison, a composition without the addition of a basic compound, a composition without the addition of a boric acid compound, and a composition without the addition of a sterically hindered phenol compound were prepared in the same manner and evaluated. Table 2 shows the results. In addition, the measurement evaluation method is as follows. <Hue stability> A test piece was molded, and the initial hue (b value)
After heating at 140 ° C. for 5 days, the hue (b value) was measured with a Z-300A color sensor manufactured by Nippon Denshoku Industries Co., Ltd.
【００１４】[0014]
【表１】 [Table 1]
【００１５】[0015]
【表２】 [Table 2]
【００１６】注） B-1 ：ペンタエリスリチル−テトラキス〔３−（3,5 −
ジ−ｔ−ブチル−４−ヒドロキシフェニル）プロピオネ
ート〕 B-2 ：トリエチレングリコールビス〔３−（３−ｔ−ブ
チル−５−メチル−４−ヒドロキシフェニル）プロピオ
ネート C-1 ：水酸化マグネシウム C-2 ：水酸化カルシウム C-3 ：12ヒドロキシステアリン酸カルシウム D-1 ：オルトホウ酸 D-2 ：四ホウ酸Note) B-1: pentaerythrityl-tetrakis [3- (3,5-
Di-t-butyl-4-hydroxyphenyl) propionate] B-2: triethylene glycol bis [3- (3-t-butyl-5-methyl-4-hydroxyphenyl) propionate C-1: magnesium hydroxide C- 2: Calcium hydroxide C-3: Calcium 12 hydroxystearate D-1: Orthoboric acid D-2: Tetraboric acid
Claims (4)
部 (C) アルカリ金属又はアルカリ土類金属の水酸化物、有
機酸のアルカリ金属塩、有機酸のアルカリ土類金属塩か
ら選ばれる少なくとも１種0.01〜５重量部と (D) ホウ酸化合物 0.001〜３重量部を配合してなる、ポ
リアセタール樹脂組成物。(A) To 100 parts by weight of a polyacetal resin; (B) 0.001 to 3 parts by weight of a sterically hindered phenolic antioxidant; (C) Alkali metal or alkaline earth metal hydroxide; organic acid alkali metal. A polyacetal resin composition comprising 0.01 to 5 parts by weight of at least one selected from salts and alkaline earth metal salts of organic acids and 0.001 to 3 parts by weight of a boric acid compound (D).
金属の水酸化物が、水酸化マグネシウム、水酸化カルシ
ウム、水酸化カリウムから選ばれる１種である請求項１
記載のポリアセタール樹脂組成物。2. The alkali metal or alkaline earth metal hydroxide of component (C) is one selected from magnesium hydroxide, calcium hydroxide and potassium hydroxide.
The polyacetal resin composition according to the above.
水酸基を有する脂肪酸の１種とカルシウム、マグネシウ
ムの１種からなる脂肪酸金属塩である請求項１記載のポ
リアセタール樹脂組成物。3. The polyacetal resin composition according to claim 1, wherein the metal salt of the organic acid as the component (C) is a metal salt of a fatty acid or a fatty acid having a hydroxyl group and one of calcium and magnesium.
四ホウ酸、三酸化二ホウ素より選ばれた１種または２種
以上である請求項１記載のポリアセタール樹脂組成物。4. Component (D) is orthoboric acid, metaboric acid,
The polyacetal resin composition according to claim 1, wherein the composition is one or more selected from tetraboric acid and diboron trioxide.