JPH11328733A - 貴金属反射層を備えた相変化光ディスク及びその光学的データ貯蔵システム - Google Patents

貴金属反射層を備えた相変化光ディスク及びその光学的データ貯蔵システム

Info

Publication number
JPH11328733A
JPH11328733A JP10334790A JP33479098A JPH11328733A JP H11328733 A JPH11328733 A JP H11328733A JP 10334790 A JP10334790 A JP 10334790A JP 33479098 A JP33479098 A JP 33479098A JP H11328733 A JPH11328733 A JP H11328733A
Authority
JP
Japan
Prior art keywords
optical disk
phase change
recording
reflective layer
change optical
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP10334790A
Other languages
English (en)
Inventor
Seong-Sue Kim
成洙 金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Samsung Electronics Co Ltd
Original Assignee
Samsung Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Samsung Electronics Co Ltd filed Critical Samsung Electronics Co Ltd
Publication of JPH11328733A publication Critical patent/JPH11328733A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【課題】 反復的に記録及び再生可能な相変化光ディス
クを提供する。 【解決手段】 ＤＶＤ−ＲＡＭとして用いられる高密度
相変化ディスクは熱伝導度、反射率及び融点が高い銅
（Ｃｕ）、銀（Ａｇ）及び金（Ａｕ）などの貴金属より
なる反射層を備える。従って、既存のＡｌ反射層を備え
た相変化光ディスクに比べてオーバーライト回数が大き
く向上され、記録しようとするトラックに隣接したトラ
ックに記録されたデータが消されるクロス消去現象も顕
著に減少される。

Description

【発明の詳細な説明】
【０００１】
【発明の属する技術分野】本発明は反復的に記録及び再
生可能な相変化光ディスクに係り、より詳しくは新たな
物質よりなる反射層を利用することによってオーバーラ
イト回数を増やし、ランド／グルーブ記録方式における
クロス消去（cross-erasing）を減らすことができる高
密度相変化光ディスク及びその光学的データ貯蔵システ
ムに関する。
【０００２】
【従来の技術】一般の相変化光ディスクは、図１に示し
たように、レーザー光が入射する側からその順の通り蒸
着（deposition）された基板及び多層薄膜を含み、多層
薄膜は基板側からその順の通り蒸着された第１誘電体
層、記録層、第２誘電体層及び反射層とから構成され
る。図１のような層構造を有する相変化光ディスクにお
いて、反射層は記録層を透過したレーザー光を再び記録
層側に反射させる。かかる反射層の反射機能により、デ
ィスクの反射率（reflectivity）及び光エネルギー効率
は高まり、反射層の有する高い熱伝導度により記録時に
溶融された記録層は急速に冷却される。その結果、記録
層内のマーク（marks）は結晶状態から非晶質状態に変
換されて相変化光ディスクに情報の記録が可能になる。
【０００３】従来は、このような相変化光ディスクの反
射層材料としてアルミニウム（Ａｌ）が使われた。アル
ミニウムよりなる反射層を備えた相変化光ディスクに対
して略１５０００回のオーバーライト（overwriting）
を行なう場合、ジッタ（jitter）が１５％を超える。ジ
ッタは再生信号の正確度を評価するのに使われるもので
あって、１５％以上のジッタを有する光ディスクは記録
媒体として使用し難い。
【０００４】また、アルミニウムよりなる反射層を備え
た相変化光ディスクにランド（land)/ク゛ルーフ゛(groove）記
録方式を利用する場合、オーバーライト回数が増えるほ
ど、予め記録されたデータの一部が損傷されることによ
るクロス消去（が大きく発生する。
【０００５】
【発明が解決しようとする課題】従って、本発明の目的
は、反射層の材料として新たな物質を使用し、Ａｌを反
射層として使用する既存の相変化光ディスクよりオーバ
ーライト回数を遥かに向上させることができる光ディス
クを提供するにある。本発明の他の目的は、相変化光デ
ィスクまたは磁気光ディスクのための光学的データ貯蔵
システムを提供するにある。
【０００６】
【課題を解決するための手段】前述した本発明の目的を
達成するための光ディスクは、基板と、前記基板の一表
面上に置かれた少なくとも１枚の薄膜を含み、前記薄膜
は、前記基板の上側に置かれた記録層と、前記記録層上
に置かれて１００ より大きくて３５０ より小さな厚
さを有する誘電体層と、及び前記誘電体層上に置かれて
金属よりなる反射層を含む。金属材料は望ましくは銅
（Ｃｕ）、銀（Ａｇ）及び金（Ａｕ）の中一つであり、
さらに望ましくは金である。
【０００７】本発明の他の目的を達成するための光学的
データ貯蔵システムは、基板と、前記基板の一表面上に
置かれた少なくとも１枚の薄膜を含み、前記薄膜は、前
記基板の上側に置かれた記録層と、前記記録層上に置か
れて１００ より大きくて３５０ より小さな厚さを有
する誘電体層と、前記誘電体層上に置かれ金属よりなる
反射層を含む光ディスク、及び前記光ディスクの記録時
に１０〜１２ｍＷのレーザーパワーを利用し、前記光デ
ィスクの再生時に１ｍＷのレーザーパワーを使用する光
ディスクドライブを含む。
【０００８】
【発明の実施の形態】以下、添付した図面に基づき本発
明の望ましい実施形態を詳述する。オーバーライト及び
クロス消去の両方は、相変化光ディスクを用いた４．７
ＧｂｙｔｅＤＶＤ−ＲＡＭの実現に主要な技術的な問題
として知られている。本発明では、このような問題が反
射層に大きく依存するに注目し、また新規な金属反射層
を利用して相変化光ディスクを製作することによってオ
ーバーライト回数を増やしながらもクロス消去を顕著に
減らすことができることを発見した。
【０００９】本発明により反射層の材料として提案され
たＣｕ、Ａｇ及びＡｕと、既存のＡｌの有する物理的な
特性を比較すると次の通りである。Ａｌは２．３７Ｗ／
ｃｍ／ｄｅｇ／ｓｅｃの熱伝導度（thermal conductivi
ty）を有する反面、Ｃｕ、Ａｇ及びＡｕは各々４．０１
Ｗ／ｃｍ／ｄｅｇ／ｓｅｃ、４．２９Ｗ／ｃｍ／ｄｅｇ
／ｓｅｃ及び３．１７Ｗ／ｃｍ／ｄｅｇ／ｓｅｃの熱伝
導度を持つ。言い換えれば、Ｃｕ、Ａｇ及びＡｕのよう
な貴金属はＡｌより３３％〜６９％程度さらに高い熱伝
導度を持つ。Ｃｕ、Ａｇ及びＡｕの融点３は各々略１０
８５℃、略９６１℃及び略８６５℃であるから、略６６
０．５℃の融点を有するＡｌより遥かに高い。従って、
反復記録時、反射層の劣化現象が防止されてオーバーラ
イト回数にともなうジッタの増加を顕著に減少させるこ
とができる。このような物質の屈折率、熱伝導度及び溶
融温度を整理すれば次の表１の通りである。
【００１０】
【表１】
【００１１】ここで、ｎは屈折率の数値、κは熱伝導
度、Ｔｍは絶対温度（Ｋ）単位で表現された溶融温度で
ある。従って、Ｃｕ、Ａｇ及びＡｕから選択された一つ
を相変化光ディスクの反射層として使用する場合、高い
熱伝導度を有する反射層は記録時に溶融された記録層か
ら熱を急速に奪うので、記録層は急速に冷却される。そ
の結果、反復記録時、ジッタ（jitter）増加の主原因の
物質流動（material flow）即ち、記録層内における熱
の不均一性により溶融された物質が移動する現象が抑制
される。ここで、ジッタとは、媒体に記録されたマーク
（mark）位置の外れ程度を示す量であって、再生信号の
正確度を表す。
【００１２】従って、温度が少なくても６５０℃以上、
記録時１０００℃まで上がる相変化光ディスクにおい
て、反射層として用いられるＣｕ、Ａｇ及びＡｕはＡｌ
より熱的に安定した特性を持つことになる。以上のよう
な特性によって、Ｃｕ、Ａｇ及びＡｕ中の選択された一
つよりなる反射層を有する相変化光ディスクはＡｌより
なる反射層を有する相変化光ディスクより良好なオーバ
ーライト特性及びクロス消去特性を持つ。
【００１３】一方、第２誘電体層は反射層に比べて相対
的に遥かに低い熱伝導度を持ち、反射層の反射率を適切
に調節するために使われる。Ｃｕ、Ａｇ及びＡｕ中の選
択された一つを反射層として使用する場合に、反射層及
び記録層間に位置した第２誘電体層は、望ましくは１０
０ より大きくて３５０ より小さな範囲の厚さを持
ち、従って、オーバーライト回数を一層増やすことがで
き、またクロス消去を一層減らすことができる。
【００１４】前述した本発明によるＣｕ、Ａｇ及びＡｕ
よりなる反射層を備えた相変化光ディスクら及び既存の
Ａｌよりなる反射層を有する相変化光ディスク間のオー
バーライト回数及びクロス消去に関連した特性を次の試
験例を通じて比較説明する。
【００１５】試験例 その各々がＡｌ、Ａｕ、Ａｇ及びＣｕよりなる反射層を
有する４枚の相変化光ディスクは、ランド／グルーブ記
録方式を利用できるようにトラックピッチ（track pitc
h）０．５８μｍのポリカーボネート（polycarbonate）
の基板を使用し、ＲＦ／ＤＣスパッタリング（sputteri
ng）により製作された。
【００１６】図２は試験のために製作された相変化光デ
ィスクの有する断層構造を示す図面である。図２におい
て、反射層は略１０００ の厚さを持つもので、前述し
たＡｌ、Ａｕ、Ａｇ及びＣｕの中一つより構成される。
基板の厚さは略０．６ｍｍであり、第１誘電体層及び第
２誘電体層はＺｎＳｉ（８０ａｔ．％）−ＳｉＯ２（２
０ａｔ．％）であり、第１誘電体層の厚さは略１２００
であり、第２誘電体層の厚さは略２００ である。記
録層はＧｅ２Ｓｂ２Ｔｅ５（化学的組成）でありその厚
さは２５０ である。
【００１７】Ａｌ、Ａｕ、Ａｇ及びＣｕ反射層を有する
４枚の相変化光ディスクを試験するために、１３．３、
１３．０、１４．５及び１５．２ｍＷの記録パワー、
５．０、５．２、６．５及び６．２ｍＷの消去パワーが
各々使われた。このような全てのパワーは１００回オー
バーライト以降に最小ジッタ値を持つように決定され
た。
【００１８】ジッタはオーバーライト回数１０５までに
対して測定された。クロス消去は隣接するランド及びグ
ルーブ中の一つに対してオーバーライト回数を増やしつ
つジッタ及びエンベロープの大きさを測定することによ
って評価された。このような全ての測定は、６８０ｎｍ
波長を持ち、ＰＵＬＳＴＥＣで製作されたＤＤＵ−１０
０の動的テスト機（dynamic tester）により、相変化光
ディスクの線速度６．１ｍ／ｓｅｃ、及びその１Ｔ
（Ｔ：信号周期）が３４．２７ｎｓｅｃの８−１４変調
（modulation）信号を使用して行われた。
【００１９】図３は溶融及び結晶化により初期化された
相変化光ディスクにおけるオーバーライト回数に対する
ジッタ変化を示す。溶融及び結晶化を用いて初期化され
た場合に、Ｃｕよりなる反射層を有する相変化光ディス
クは図３に示したように、６×１０４回のオーバーライ
トまで１２％より小さなジッタ値を持ち、１０５回のオ
ーバーライト以降に略１４．０％のジッタ値を持つ。一
方、Ａｌよりなる反射層を有する相変化光ディスクは１
５０００回のオーバーライトに対して略１５％のジッタ
値を持ち、１０５回のオーバーライト以降に略２６％の
ジッタ値を持つ。従って、本発明によって提案されたＣ
ｕ、Ａｇ及びＡｕよりなる反射層を有する光ディスクは
Ａｌよりなる反射層を有する既存の光ディスクに比べて
優れたオーバーライト能力（cyclabilities）を持つ。
【００２０】図４は隣接したランドまたはグルーブにお
いてオーバーライト回数を増やしつつ測定したジッタの
変化を示すもので、特にトラックピッチが０．５４μｍ
の基板を使用した場合のジッタ変化を示す。Ｃｕ、Ａｇ
及びＡｕから選択された一つよりなる反射層を有する相
変化光ディスクはＡｌよりなる反射層を有する相変化光
ディスクに比べて相当少ないジッタ値を保ち、このよう
なジッタは図４に示した全体オーバーライト範囲下で１
１％より小さな状態に維持される。したがって、Ｃｕ、
Ａｇ及びＡｕから選択された一つよりなる反射層を有す
る相変化ディスクはＡｌよりなる反射層を有する相変化
光ディスクに比べて、記録時隣接トラックのデータ損傷
が少なくなる。
【００２１】図５は赤色光領域におけるＡｌ、Ｃｕ、Ａ
ｇまたはＡｕよりなる単一層の反射率を示す。図５から
分かるように、Ｃｕ、Ａｇ及びＡｕはＡｌより高い反射
率を持つ。従って、Ａｌよりなる反射層を有する相変化
光ディスクに比べて、Ｃｕ、Ａｇ及びＡｕ中の一つより
なる反射層を有する相変化光ディスクは、記録層で多く
の光エネルギーの吸収が起きる一方、反射層では少ない
光エネルギーの吸収が起きる。
【００２２】図６は反射層に接した第２誘電体層が異な
る厚さを持つ場合、オーバーライト回数に対するジッタ
の変化を示すもので、特に、Ｃｕよりなる反射層を有す
る相変化光ディスクに対して測定したジッタの変化を示
す。
【００２３】図７はＡｌ反射層を有する相変化光ディス
クにおけるトラック間隔に対するクロス消去特性を示
す。この特性図は１９９６年ＩＳＯＭ（International
Symposium on Optical Memory）とＯＤＳ（Optical Dat
a Storage）の合同シンポジウム論文集３３ページに掲
載された日本松下社の論文に開示されたもので、トラッ
クピッチが０．７μｍ以下になる場合は１５％以上のジ
ッタが発生することを示す。即ち、記録する過程で隣接
トラックのデータが消去されることを示す。
【００２４】隣接トラックに記録する場合に関連して、
図４に示された特性図を図７のそれと比較してみれば、
Ａｌを反射層として使用した相変化光ディスクは図７の
結果と同様にジッタが５％程増加する。しかし、貴金属
反射層を有する相変化光ディスクの場合、ジッタの増加
量が顕著に減少し、特にＣｕ反射膜を使用した光ディス
クの場合、ジッタ増加量が２％以内となる。
【００２５】前述した試験例から分かるように、Ｃｕ、
Ａｇ、Ａｕ中からＡｕはその性能及び信頼度の両面を考
慮した場合の最適の材料である。前述した試験例におい
て、第１誘電体層、記録層、第２誘電体層及び反射層を
備えた単一薄膜を含む相変化光ディスクが説明された。
しかし、本発明はこのような薄膜を複数枚具備した相変
化光ディスクに対しても同一に適用できることは当業者
にとって明白である。
【００２６】一方、前述した貴金属反射層は光磁気（ma
gneto-optical）ディスクでも使用できる。光磁気ディ
スクの場合、大気温度（ambient temperature）で高い
磁気保磁力（magnetic coercivity）を有する光磁気層
は集束されたレーザービームによりその温度が上がる。
その結果、レーザービームが集束された部分の磁気保磁
力は落ち、光磁気層に情報を記録できる。従って、本発
明に係る貴金属反射層を基板、誘電体層、光磁気層、及
び反射層を有する光磁気ディスクの反射層として使用で
きる。
【００２７】図８は本発明に係る光ディスクドライブを
示す。図８に示された光ディスクドライブは光ピックア
ップ１０と、サーボ及び信号処理部２０を具備する。光
ピックアップ１０は光源１１０、ビーム分割器１２０、
対物レンズ１３０及び光検出器１４０を具備する。図８
のディスクドライブはロードされたディスク３０に対し
情報を記録及び／または再生する。ディスク３０はトラ
ックピッチが略０．６μｍ以下の相変化光ディスク、ま
たは光磁気ディスクである。
【００２８】サーボ及び信号処理部２０は、記録または
再生に適した電圧を光源１１０に供給する。サーボ及び
信号処理部２０からの電圧に応答する光源１１０は６９
０ｎｍ以下の波長を有するレーザー光を発生する。この
光源１１０は情報を読み出す場合よりは情報を記録する
場合に一層強い光ビームを発生する。従って、相変化光
ディスクに信号を記録する場合、ディスクにおけるレー
ザーパワーは１０〜１２ｍＷの範囲を持ち、相変化光デ
ィスクから信号を読み出す場合、ディスクにおけるレー
ザーパワーは略１ｍＶである。光ピックアップ技術に関
連した当業者にとって、光源１１０から出射されるレー
ザー光により形成される光経路は明白なことであるか
ら、その具体的な説明を省く。
【００２９】
【発明の効果】以上述べたように、本発明による相変化
光ディスクはＡｌの代りにＣｕ、Ａｇ及びＡｕなどのよ
うな貴金属よりなる反射層を備え、反射層に接した誘電
体層は１００ より大きくて３５０ より小さな厚さを
持つ。その結果、本発明による相変化光ディスクは１０
万回以上のオーバーライト回数についてそのジッタ値が
１５％を越えなく、ランド／グルーブ記録方式を利用す
る場合も既存のＡｌよりなる反射層を有する相変化光デ
ィスクに比べて遥かに優れたクロス消去特性を提供す
る。従って、本発明による相変化光ディスは４．７ＧＢ
ＤＶＤ−ＲＡＭディスクとして用いられる場合、Ａｌ
よりなる反射層を有する既存の相変化光ディスクに比べ
て記録媒体として一層高い信頼度を維持できる。
【図面の簡単な説明】
【図１】 一般の相変化光ディスクの構造を示す断面図
である。
【図２】 本発明の実験例の説明のための相変化光ディ
スクの構造を示した断面図である。
【図３】 Ａｌ、Ｃｕ、Ａｇ及びＡｕよりなる反射層を
有する相変化光ディスクに対するオーバーライト回数−
ジッタ特性の変化を示す図表である。
【図４】 ランド／グルーブ構造よりなる基板を有する
相変化光ディスクの隣接したランドまたはグルーブに対
するオーバーライト回数−ジッタ特性を示した図表であ
る。
【図５】 Ａｌ、Ｃｕ、Ａｇ及びＡｕよりなる単一層の
赤色光領域における波長−反射率特性を示す図表であ
る。
【図６】 反射層に接した第２誘電体層が異なる厚さを
持つ場合のオーバーライト回数に対するジッタの変化を
示す図表である。
【図７】 Ａｌ反射層を有する相変化光ディスクにおけ
るトラック間隔に対するクロス消去特性を示す図面であ
る。
【図８】 相変化光ディスク及び光磁気ディスクのため
の本発明に係る光ディスクドライブを示した図面であ
る。
【符号の説明】
１０ 光ピックアップ ２０ サーボ及び信号処理部 ３０ ディスク １１０ 光源 １２０ ビーム分割器 １３０ 対物レンズ １４０ 光検出器

Claims (18)

    【特許請求の範囲】
  1. 【請求項１】 光ディスクにおいて、 基板と、 前記基板の一表面上に置かれた少なくとも１枚の薄膜を
    含み、前記薄膜は、 前記基板の上側に置かれた記録層と、 前記記録層上に置かれ１００ より大きくて３５０ よ
    り小さな厚さを有する誘電体層と、 前記誘電体層上に置かれ金属よりなる反射層とを含む光
    ディスク。
  2. 【請求項２】 前記反射層は、銅（Ｃｕ）、金（Ａｕ）
    及び銀（Ａｇ）から選ばれた一つよりなる請求項１に記
    載の光ディスク。
  3. 【請求項３】 前記反射層は、望ましくは金であること
    を特徴とする請求項２に記載の光ディスク。
  4. 【請求項４】 前記光ディスクは、相変化ディスクであ
    ることを特徴とする請求項１に記載の光ディスク。
  5. 【請求項５】 前記誘電体層は、ＺｎＳｉ（８０ａｔ．
    ％）−ＳｉＯ２（２０ａｔ．％）よりなり、前記記録層
    はＧｅ２Ｓｂ２Ｔｅ５よりなる請求項４に記載の光ディ
    スク。
  6. 【請求項６】 前記相変化光ディスクにおけるトラック
    ピッチは、略０．６μｍ以下である請求項４に記載の光
    ディスク。
  7. 【請求項７】 ６９０ｎｍ以下の波長を有するレーザー
    光が、相変化光ディスクにおける情報の記録、消去また
    は再生のために用いられる請求項４に記載の光ディス
    ク。
  8. 【請求項８】 相変化光ディスクにおいて、 基板と、 前記基板の一表面上に置かれた少なくとも１枚の薄膜を
    含み、前記薄膜は、 前記基板上に置かれた第１誘電体層と、 前記第１誘電体層上に置かれた記録層と、 前記記録層上に置かれ１００ より大きくて３５０ よ
    り小さな厚さを有する誘電体層と、 前記誘電体層上に置かれ金属よりなる反射層を含む相変
    化光ディスク。
  9. 【請求項９】 前記反射層は、銅（Ｃｕ）、金（Ａｕ）
    及び銀（Ａｇ）から選ばれた一つよりなる請求項８に記
    載の相変化光ディスク。
  10. 【請求項１０】 トラックピッチは、略０．６μｍ以下
    である請求項８に記載の相変化光ディスク。
  11. 【請求項１１】 ６９０ｎｍ以下の波長を有するレーザ
    ー光が、情報の記録、消去または再生のために用いられ
    る請求項８に記載の相変化光ディスク。
  12. 【請求項１２】 光学的データ貯蔵システムにおいて、 基板、及び前記基板の一表面上に置かれた少なくとも１
    枚の薄膜を含み、前記薄膜は、前記基板の上側に置かれ
    た記録層と、前記記録層上に置かれ１００ より大きく
    て３５０ より小さな厚さを有する誘電体層、及び前記
    誘電体層上に置かれ金属よりなる反射層とを含む光ディ
    スクと、 前記光ディスクの記録時に１０〜１２ｍＷのレーザーパ
    ワーを利用し、前記光ディスクの再生時に１ｍＷのレー
    ザーパワーを使用する光ディスクドライブを含む光学的
    データ貯蔵システム。
  13. 【請求項１３】 前記反射層は、銅（Ｃｕ）、金（Ａ
    ｕ）及び銀（Ａｇ）から選ばれた一つよりなる請求項１
    ２に記載の光学的データ貯蔵システム。
  14. 【請求項１４】 前記光ディスクは、相変化光ディスク
    である請求項１３に記載の光学的データ貯蔵システム。
  15. 【請求項１５】 前記誘電体層は、ＺｎＳｉ（８０ａ
    ｔ．％）−ＳｉＯ２（２０ａｔ．％）よりなり、前記記
    録層は、Ｇｅ２Ｓｂ２Ｔｅ５よりなる請求項１４に記載
    の光学的データ貯蔵システム。
  16. 【請求項１６】 前記光ディスクにおけるトラックピッ
    チは、略０．６μｍ以下である請求項１５に記載の光学
    的データ貯蔵システム。
  17. 【請求項１７】 ６９０ｎｍ以下の波長を有するレー
    ザー光が、光ディスクにおける情報を記録、消去または
    再生のために用いられる請求項１３に記載の光学的デー
    タ貯蔵システム。
  18. 【請求項１８】 前記光ディスクは、光磁気ディスクで
    ある請求項１２に記載の光学的データ貯蔵システム。
JP10334790A 1997-11-25 1998-11-25 貴金属反射層を備えた相変化光ディスク及びその光学的データ貯蔵システム Pending JPH11328733A (ja)