JPS5974457A - カイロ - Google Patents
カイロInfo
- Publication number
- JPS5974457A JPS5974457A JP57186346A JP18634682A JPS5974457A JP S5974457 A JPS5974457 A JP S5974457A JP 57186346 A JP57186346 A JP 57186346A JP 18634682 A JP18634682 A JP 18634682A JP S5974457 A JPS5974457 A JP S5974457A
- Authority
- JP
- Japan
- Prior art keywords
- ammonium
- iron
- kairo
- sulfur
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
利用したカイロ、たとえば使い捨てカイロに関する。さ
らに詳しくは、含イオウ含チッ素化合物が配合されてな
るカイロに関する。
らに詳しくは、含イオウ含チッ素化合物が配合されてな
るカイロに関する。
一般に、鉄の空気酸化を利用するカイロには、鉄粉、水
、金属中性塩、炭素質物質、保水剤などが配合されてい
る。
、金属中性塩、炭素質物質、保水剤などが配合されてい
る。
しかしながら、鉄の空気酸化という反応自体本来激しい
ものではないため、暖房効果が生じ始める温度（約６０
〜４０°０）に達するまで約９０分もかかり、緊急なば
あいには役に立たないことがある。さらに寒冷地におい
てはより発熱開始時の温度の立上りがわるくなり、使用
に耐えないときもある。
ものではないため、暖房効果が生じ始める温度（約６０
〜４０°０）に達するまで約９０分もかかり、緊急なば
あいには役に立たないことがある。さらに寒冷地におい
てはより発熱開始時の温度の立上りがわるくなり、使用
に耐えないときもある。
またこの種のカイロは、貯蔵中の酸化反応を防ぐために
空気を遮断するべく、酸素不透過性の袋に密封されてい
る。しかしながら、鉄と水との反応は進行し、その結果
水素が発生している。この水素の発生により、爆発の危
険が生ずるほか袋がふくらみ、貯蔵に大きな問題が生じ
ている。
空気を遮断するべく、酸素不透過性の袋に密封されてい
る。しかしながら、鉄と水との反応は進行し、その結果
水素が発生している。この水素の発生により、爆発の危
険が生ずるほか袋がふくらみ、貯蔵に大きな問題が生じ
ている。
水素の発生抑制のために、従来水酸化ナトリウム、炭酸
ナトリウムなどのアルカリ性物質を配合することが行な
われている。ところがそのようなアルカリ性物質の配合
は発熱開始時の立上りをわるくするため、好ましいもの
ではない。
ナトリウムなどのアルカリ性物質を配合することが行な
われている。ところがそのようなアルカリ性物質の配合
は発熱開始時の立上りをわるくするため、好ましいもの
ではない。
本発明者らは、発熱開始時の立上りを改善すると共に水
素の発生をも抑制しうるカイロをうるべく鋭意研究を重
ねた結果、含イオウ含チッ素化合物を配合するときは値
上の目的を達成しうろことを見出し、本発明を完成した
。
素の発生をも抑制しうるカイロをうるべく鋭意研究を重
ねた結果、含イオウ含チッ素化合物を配合するときは値
上の目的を達成しうろことを見出し、本発明を完成した
。
本発明に用いる含イオウ含チッ素化合物としては、たと
えば硫化アンモニウム、チオ硫酸アンモニウム、硫酸ア
ンモニウム、ＥＫ硫ｍアンモニウム、スルファミン酸ア
ンモニウム、テトラメチルチウラムジスルフィド、チオ
尿素、ジエチルジチオカルバミン酸ナトリウムなどがあ
げられる。
えば硫化アンモニウム、チオ硫酸アンモニウム、硫酸ア
ンモニウム、ＥＫ硫ｍアンモニウム、スルファミン酸ア
ンモニウム、テトラメチルチウラムジスルフィド、チオ
尿素、ジエチルジチオカルバミン酸ナトリウムなどがあ
げられる。
それらのうち硫化アンモニウム、チオ硫１９アンモニウ
ム、ＭＫＭアンモニウム、チオ尿素、よび水素ガス発生
抑制効果の両方にとくにすぐれている。
ム、ＭＫＭアンモニウム、チオ尿素、よび水素ガス発生
抑制効果の両方にとくにすぐれている。
本発明において含イオウ含チッ累化合物は鉄１００部（
重量部、以下同様）に対し、６０部以下、とくに０．０
５〜１．０部配合することが好ましい。
重量部、以下同様）に対し、６０部以下、とくに０．０
５〜１．０部配合することが好ましい。
使用する鉄粉としては、たとえば還元鉄粉やアトマイズ
法によりえられる鉄粉などがあげられる。それらのうち
還元鉄粉がとくに好ましい。
法によりえられる鉄粉などがあげられる。それらのうち
還元鉄粉がとくに好ましい。
鉄の空気酸化によって生ずる熱を利用するカイロには、
前記のごとく鉄のほかに水、金属中性塩、炭素質物質、
保水剤などの成分が配合されているが、本発明において
も同様の成分が配合される。
前記のごとく鉄のほかに水、金属中性塩、炭素質物質、
保水剤などの成分が配合されているが、本発明において
も同様の成分が配合される。
金属中性塩としては塩化す） ＩＪウム、塩化カリウム
、塩化カルシウムなどがあげられるが、価格その他の点
から塩化す】・リウムが好ましい。
、塩化カルシウムなどがあげられるが、価格その他の点
から塩化す】・リウムが好ましい。
炭素質物質は酸化触媒として用いるものであり、たとえ
ば活性炭粉が好ましいが、適宜ヤシ殻炭粉などに置き換
えてもよい。保水剤としては、木屑、バーミキュライト
、繊維粉、高吸水性樹脂またはそれらの混合物があげら
れる。
ば活性炭粉が好ましいが、適宜ヤシ殻炭粉などに置き換
えてもよい。保水剤としては、木屑、バーミキュライト
、繊維粉、高吸水性樹脂またはそれらの混合物があげら
れる。
これらの配合割合は、鉄粉１００部に対して水２０〜７
０部、炭素質物質０．１〜８０部、金属中性塩１〜２０
部、保水剤１〜５００部とするのが好ましい。
０部、炭素質物質０．１〜８０部、金属中性塩１〜２０
部、保水剤１〜５００部とするのが好ましい。
また要すれば酸化剤を適当量配合してもよい。
それら各成分の混合は、全成分を一度に混合してもよい
が、まず鉄粉と含イオウ含チッ素化合物とを均一に混合
し、ついでこの混合物と他の成分とを混合するのが好ま
しい。
が、まず鉄粉と含イオウ含チッ素化合物とを均一に混合
し、ついでこの混合物と他の成分とを混合するのが好ま
しい。
以上の混合物を封入する袋体としては、通常通気性を有
する内袋と非通気性の外袋からなるものが用いられる。
する内袋と非通気性の外袋からなるものが用いられる。
本発明のカイロに用いる外袋としては、非通気性のもの
であればそのほかの制限はなく、ラミネートされている
ものでもよい。好ましいものとしては、たとえばＯＦＦ
、ａｐｐ 、ポリ塩化ビニリデンなどにより防湿処理さ
れたナイロン、ポリエステル、ポリプロピレンフィルム
、サラにはアルミ箔またはアルミ蒸着されたプラスチッ
クフィルムなどがあげられる。
であればそのほかの制限はなく、ラミネートされている
ものでもよい。好ましいものとしては、たとえばＯＦＦ
、ａｐｐ 、ポリ塩化ビニリデンなどにより防湿処理さ
れたナイロン、ポリエステル、ポリプロピレンフィルム
、サラにはアルミ箔またはアルミ蒸着されたプラスチッ
クフィルムなどがあげられる。
この種のカイｐの内袋は通常不織布が用いられているが
、通気性を有するものであればよく、たとえば布、紙な
ども用いられつる。
、通気性を有するものであればよく、たとえば布、紙な
ども用いられつる。
つぎに実施例をあげて本発明の詳細な説明するが、本発
明はかかる実施例のみに限定されるものではない。
明はかかる実施例のみに限定されるものではない。
実施例１〜１６および比較例１〜６
還元鉄粉２Ｑ０７に第１表に示す化合物を同表に示す量
で２４〜６０°０にて均一に混合した。
で２４〜６０°０にて均一に混合した。
えられた混合物２５りと水１０．５ｇ、塩化ナトリウム
１．５りおよび木屑１０．５ｇとを充分混合したのち通
気性の袋体に封入し、それらの立上り状態を調べた。
１．５りおよび木屑１０．５ｇとを充分混合したのち通
気性の袋体に封入し、それらの立上り状態を調べた。
袋体としてはナイロン不織布の内面にポリエチレンをラ
ミネートしたものの中央部に４．３ｍｎ＋幅、６ＩｗＩ
間隔で片面３６０個穿孔（０，３ｍｍ径の針使用）した
８０ｍｍＸ１２０ｍｍのものを用いた。
ミネートしたものの中央部に４．３ｍｎ＋幅、６ＩｗＩ
間隔で片面３６０個穿孔（０，３ｍｍ径の針使用）した
８０ｍｍＸ１２０ｍｍのものを用いた。
測定は封入後、ただちに数十回振り、毛布４枚を重ねた
上におき、熱電対を挾んだ上に毛布２枚を重ね、室内温
度が約８８０に保たれた室内で行なった。
上におき、熱電対を挾んだ上に毛布２枚を重ね、室内温
度が約８８０に保たれた室内で行なった。
それらの結果を第１表に示す。
つぎに実施例１．３．７．１０．１１．１６および比較
例１．２．６でそれぞれえられた鉄粉混合物３０７、水
１２ｇ、塩化ナトリウム１．５ｇ、バーミキュライト２
．５９、活性炭（ＩＣ−５０、成田薬品工業■製）２．
Ｅｌｇ、ヤシ殻炭７りおよび高吸水性樹脂（サンウェッ
ト ＩＭ −３００、三洋化成工業■Ｈ）ｏ、ａｇｐを
、全成分を均一に混合したのち非通気性のアルミ箔製の
袋体に充填し真空密封して水素ガスの発生を調べた。
例１．２．６でそれぞれえられた鉄粉混合物３０７、水
１２ｇ、塩化ナトリウム１．５ｇ、バーミキュライト２
．５９、活性炭（ＩＣ−５０、成田薬品工業■製）２．
Ｅｌｇ、ヤシ殻炭７りおよび高吸水性樹脂（サンウェッ
ト ＩＭ −３００、三洋化成工業■Ｈ）ｏ、ａｇｐを
、全成分を均一に混合したのち非通気性のアルミ箔製の
袋体に充填し真空密封して水素ガスの発生を調べた。
えられた密封体を乾燥炉で８８〜８９°０で８時間加熱
して水素ガスの発生の度合を調べた。さらに６５〜４０
°０にて３カ月間保存し、水素ガスの発生の度合を調べ
た。それらの結果を第２表に示す。
して水素ガスの発生の度合を調べた。さらに６５〜４０
°０にて３カ月間保存し、水素ガスの発生の度合を調べ
た。それらの結果を第２表に示す。
ガス発生の度合は、つぎの基準で肉眼により観察評価し
た。
た。
◎：まったく変化なし
○：殆んど変化なし
×：袋体がふくれ、破裂したものもある第 ２
表 第１〜２表から明らかなごとく、含イオウ含チッ素化合
物を配合したときは立上り時間を半減せしめることがで
き、しかも水素ガスが発生することもない。
表 第１〜２表から明らかなごとく、含イオウ含チッ素化合
物を配合したときは立上り時間を半減せしめることがで
き、しかも水素ガスが発生することもない。
一方、チッ素原子を含まない含イオウ化合物である硫化
ナトリウムを配合したときは、水素ガスの発生を抑制す
ることはできたが立上りは逆にわるくなり、またイオウ
原子を含まない含チツ素化合物である尿素を配合したと
きは、立上りは改善されず、しかも水素ガスの発生も抑
制することができなかった。
ナトリウムを配合したときは、水素ガスの発生を抑制す
ることはできたが立上りは逆にわるくなり、またイオウ
原子を含まない含チツ素化合物である尿素を配合したと
きは、立上りは改善されず、しかも水素ガスの発生も抑
制することができなかった。
Claims (1)
- １ 含イオウ含チッ素化合物が配合されてなる鉄の空気
酸化を利用するカイロ。