JPS6056406A - マンネスマン穿孔法 - Google Patents

マンネスマン穿孔法

Info

Publication number
JPS6056406A
JPS6056406A JP58165135A JP16513583A JPS6056406A JP S6056406 A JPS6056406 A JP S6056406A JP 58165135 A JP58165135 A JP 58165135A JP 16513583 A JP16513583 A JP 16513583A JP S6056406 A JPS6056406 A JP S6056406A
Authority
JP
Japan
Prior art keywords
guide shoe
lubricant
shoe
aqueous solution
rolling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP58165135A
Other languages
English (en)
Inventor
Shigeru Sano
茂 佐野
Taku Ogawa
卓 小河
Tomoshige Shiyudo
首藤　知茂
Atsushi Umetsu
梅津　篤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Engineering Corp
Original Assignee
NKK Corp
Nippon Kokan Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NKK Corp, Nippon Kokan Ltd filed Critical NKK Corp
Priority to JP58165135A priority Critical patent/JPS6056406A/ja
Publication of JPS6056406A publication Critical patent/JPS6056406A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 この発明はマンネスマン穿孔法の改良に関する。
マンネスマン方式によって継目無鋼管を製造する場合、
二つの樽型の穿孔ロールが加熱鋼片の両側を挾んで回転
し且つガイドシューがその上下を挾んでガイドすること
によシ、該加熱鋼片を回転前進せしめ、その回転中心に
センタリングしたせん孔プラグを押込み穿孔している。
このマンネスマン穿孔におけるガイドシューはホローシ
ェルの品質保障及びガイドシューの原単位向上の要求か
ら材質的に合金化している。一方市場の要請から高合金
鋼片のマンネスマン穿孔の必要が生じてきた。そのため
従来材質のガイドシューを用いて高合金鋼をマンネスマ
ン穿孔するとガイドシュー表面に加熱鋼片が凝着し該加
熱鋼片表面がむしり取られ、その結果として製品表面に
は螺旋状の一条ないし数条の連続又は不連続の疵（所謂
シューマーク〕が発生する。
本発明はこのような加熱鋼片とガイドシューとの１焼着
き′”を防止するためなされたもので、それによシ表面
欠陥のない良質なホローシェルを製造できるようにした
ものである。
以下本発明の詳細な説明する。
本発明者らは、熱間圧延潤滑剤が圧延工具等に使用され
、その表面の摩擦係数を大幅に減少させるものであるこ
とに基づき、とｎをガイドシュー表面に適用することを
創案した。
この熱間圧延潤滑剤は、乾燥固化性媒体を含む水溶液（
スチレン、マイレン酸共重合物アンモニウム塩、ポリア
クリル酸アンモニウム塩、ロート油アンモニウム塩、非
置換若しくは置換アミノカルボン酸アンモニウム塩の１
種又は２種以上を水に配合したもの等）又は懸濁水（メ
チルメタクリレート、スチレン、ｔ−ブチルメタクリレ
ート、メチルアクリレート、アクリロニトリルの単独重
合物あるいは２種以上の共重合物又はこれら２１以上の
混合物等）中に微細黒鉛及び／又は微細固体アスファル
ト粒子を分散させたものである。
このうち、微細黒鉛及び微細固体アスファルト粒子に潤
滑作用があり、それによって加熱鋼片が摺動するガイド
シュー表面ｏ摩を係数を大幅に減少せしめることができ
ることになる。そのため本発明法はこの熱間圧延潤滑剤
をガイドシュー表面に塗布し、これを自然乾燥、熱風の
吹付は等による強制乾燥、あるいはガイドシュー表面の
含熱による短時間乾燥によシそこに固着せしめた後、こ
のガイドシューによシ加熱鋼片をガイドしながら穿孔せ
しめるようにしたものである。ガイドシュー表面に乾燥
固着した上記潤滑剤の固着膜内には微細黒鉛及び／又は
微細固体アスファルト粒子が取込まｎておシ、これらに
よシガイドシュー表面の摩擦係数を大幅に減少せしめる
ことができる。
以上の熱間圧延潤滑剤を未使用のガイドシュー表面に塗
布する場合はスプレ又はノ・ケ塗シによって行なう。そ
して自然乾燥後又は加熱等による強制乾燥後、これを使
用するようにすると良い。更に第１図に示すように使用
中の固定ガイドシュ−００α℃表面に上記潤滑剤を塗布
する場合は、実圧延時間の間のアイドルタイム間に、第
２図に示すようにスプレノズル翰Ｑ力から上下両固定ガ
イドシューαＱαカ表面にそれぞれ潤滑剤をスプレする
。又第３図に示すように回転式のディスクシューである
ガイドシュー（２）ａ埠に潤滑剤を塗布する場合、アイ
ドルタイム間にスプレノズル＠に）からそｎぞれ回転し
ているガイドシュー（２）α１表面にスプレする。以上
のようにして使用中のガイドシューαＯ乃至（２）表面
に潤滑剤を塗布するとガイドシュー１０乃至ａ３の含熱
によυ短時間に乾燥し、実圧延さ１しるまでの間に十分
固着した乾燥膜が形成さｎるため、そのままこれを使用
すると良い。尚、図中（１）は加熱鋼片、輪（３１）は
穿孔ロール、（４０）は穿孔プラグを告示している。
次に本発明法と従来法との効果について比較検討する。
本発明による効果は特に高Ｃｒ系の合金鋼の穿孔におい
て顕著に認められた。即ち、前述した従来の穿孔法にお
いてはガイドシューの焼着きが１パスないしせいぜい３
ノくスで発生し、これによりホローシェルには致命的な
外面欠陥が認めらｎた。−万、本発明の穿孔法によると
ガイドシューの焼着きは少なくとも１００パスの間は全
く発生せず、当然シェル外面は欠陥のない良質なものが
得ら扛た。今回はたまたま１００バスで一旦取り替えた
がガイドシュー表面の摩耗状況から判断して更に継続使
用可能であった。
そのｔ’ｔかマンネスマン穿孔におけるシェル外面品質
対策として、 ■穿孔中にスケールないし砂をロールと加熱鋼片の間に
落下する（特開昭５５−１２２６０４号） ■穿孔中にガイドシューとロールの間から液体潤滑油を
噴射する ■穿孔前にガイドシュー表面に食塩等を放置する 等が知られているが、倒れについても本発明法程の効果
はあげらｎ力かった。特に高合金鋼の穿孔の時には、普
通鋼の時よりその差が顕著であシ、本発明法の優位性が
明白に認めらｎた。
以上のような本発明法によれば、ガイドシニー表面に乾
燥固着せしめらｎた熱間圧延潤滑剤の潤滑作用によシ、
ガイドシュー表面の摩擦係数が大幅に減少せしめられる
ため、マンネスマン穿孔の際カロ熱鋼片と該ガイドシュ
ーとの焼着きを防止することができ、シューマーク等の
表面欠陥のない良質なホローシェルを製造することがで
きるという優れた効果を有している。
【図面の簡単な説明】
第１図は固定ガイドシューを使用するマンネスマン穿孔
の場合の一例を示す説明図、第２図はそのマンネスマン
穿孔の際本発明に係る熱間圧延潤滑剤の塗布工程を示す
説明図、第３図は回転ガイドシューを使用するマンネス
マン穿孔の際の熱間圧延潤滑剤の塗布工程を示す説明図
である。 図中ＱＯ（ｌυは固定ガイドシュー、（ロ）α葎は回転
式ガイドシュー、翰乃至幹はスグレノズルを各示す。

Claims (1)

    【特許請求の範囲】
  1. 乾燥固化性媒体を含む水溶液又は懸濁水中に微細黒鉛粒
    子及び／又は微細固形アスファルト粒子を分散せしめた
    熱間圧延潤滑剤をガイドシュー表面に塗布し、且っ販潤
    滑剤がガイドシュー表面に固着した後、このガイドシュ
    ーにょシ加熱細片をガイドしながら穿孔せしめるように
    したことを特徴とするマンネスマン穿孔法。
JP58165135A 1983-09-09 1983-09-09 マンネスマン穿孔法 Pending JPS6056406A (ja)