JPS631264B2 - - Google Patents
Info
- Publication number
- JPS631264B2 JPS631264B2 JP57040396A JP4039682A JPS631264B2 JP S631264 B2 JPS631264 B2 JP S631264B2 JP 57040396 A JP57040396 A JP 57040396A JP 4039682 A JP4039682 A JP 4039682A JP S631264 B2 JPS631264 B2 JP S631264B2
- Authority
- JP
- Japan
- Prior art keywords
- composition
- cao
- tio
- present
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は破壊電圧が高くかつ寿命の長い温度補
償用誘電体磁器組成物に関する。 従来温度補償用誘電体磁器組成物として、例え
ばランタン、チタン、カルシウムおよびマグネシ
ウムの酸化物をそれぞれLa2O3、TiO2、CaO、
およびMgOに換算して、La2O33.0乃至250mol％
とTiO251.0乃至62.0mol％とCaO0.5乃至45.0mol
％とMgO1.0乃至45.0mol％とからなるLa2O3―
TiO2―CaO―MgO系組成物が公知となつてい
る。しかしながら、その結晶粒径は5μm以上で大
きく、積層コンデンサなどのように電界強度の大
きい製品には不適当である。すなわち、結晶粒径
が大きい場合には、結晶粒子１個あたりにかかる
電界強度は大きくなり、そため破壊電圧は低くな
り、寿命も短くなり、従つて信頼性が低下すると
いう欠点があつた。また、La2O3を含有している
ために、アルミナ・セツターを用いる必要があ
り、通常の誘電体磁器組成物で用いるジルコニ
ア・セツターと使い別けをしなければならないと
いう製造工程面での煩雑さがあつた。 本発明者らは上記の従来の組成物の欠点を解決
し、結晶粒径が5μm未満のきわめて微細であるの
で破壊電圧が高くかつ寿命が長く、しかもジルコ
ニア・セツターにて焼成可能な誘電体磁器組成物
を提供すべく検討した結果、酸化ジルコニウムを
添加すると、得られた誘電体磁器組成物の結晶粒
子が微細化し、しかも誘電率、Ｑ、温度特性を低
下させることがなく、更にジルコニア・セツター
にて焼成可能であることを見出し、本発明に到達
した。すなわち、本発明の要旨とするところは、
La2O3―TiO2―CaO―MgO系組成物を主成分と
し、ジルコニウムの酸化物をZrO2に換算して、
該主成分に対し0.1重量％乃至8.0重量％含有して
なる誘電体磁器組成物、にある。 本発明の組成物は上記構成によつて、実施例に
示すように、結晶粒径がきわめて微細であるの
で、積層コンデンサなどのように電界強度の大き
い製品には好適である。すなわち、結晶粒径が微
細であるので結晶粒子１個あたりにかかる電界強
度が小さくなり、それによつて破壊電圧が高くな
り、寿命はのびて信頼性が向上する。また、本発
明の組成物は、酸化ジルコニウムを含有しない従
来の組成物と同等の誘電率、Ｑ、温度特性を有
し、実用的であることは実施例が示す通りであ
る。 本発明の組成物の組成において、酸化ジルコニ
ウムの量が0.1重量％未満であると、結晶粒径が
5μm以上になるとともにジルコニア・セツターと
反応し、また、8.0重量％を起えると粒径5μm以
上の結晶が発生する。 本発明の組成物は、例えば、焼成後に本発明の
組成になるように秤取された原料配合物をボール
ミルで湿式混合・粉砕し、得られた混合・粉砕物
を脱水・乾燥後、所定の形状に加圧成形して焼成
することにより得ることができる。この場合、原
料として使用するランタン化合物はLa2O3、La2
（C2O4）3・9H2O、チタン化合物はTiO2、Ti2O3、
カルシウム化合物はCaO、CaCO3、マグネシウ
ム化合物はMgO、MgC2O4・2H2O、ジルコニア
化合物はZrO2、3ZrO2・6H2Oが好適である。 次に本発明を実施例によつてさらに具体的に説
明するが、本発明はその要旨を越えない限り以下
の実施例に限定されるものではない。 実施例 原料として、主成分であるLa2O3、TiO2、
CaO、MgO、並びに添加成分であるZrO2を、そ
れぞれ試薬１級のLa2O3、TiO2、CaO、MgOお
よびZrO2を用い、焼成後に次の表に示す配合比
になるよう秤取し、ボールミル中で20時間湿式混
合・粉砕し、脱水・乾燥後、成形圧力3ton／cm2で
直径16mm厚さ0.6mmの円板に加圧成形し、成形物
を次の表に示す焼成温度で１時間焼成し、試料番
号１〜７とした。 これら試料の結晶粒径は光学顕微鏡により倍率
400で観察し、容量値およびＱ値は試料の両面に
銀電極を焼付け、YHPデジタルLCRメータモデ
ル4274Aを使用し、測定温度25℃、測定電圧
1.0Vrms、測定周波数100KHzによる測定により
求めた。温度特性は25℃における容量値を基準と
し85℃における容量値にて算出した。これら物性
の測定結果を次の表に併せ示す。 得られた試料はいずれも次の表が示すように、
酸化ジルコニウム添加により結晶粒径が5.0μm未
満で、かつ実用的な誘電率、Ｑ値および温度特性
を有し、しかもジルコニア・セツターにて焼成可
能な誘電体磁器組成物であり、積層コンデンサの
ごとき電界強度の大きい製品には最適である。 【表】
償用誘電体磁器組成物に関する。 従来温度補償用誘電体磁器組成物として、例え
ばランタン、チタン、カルシウムおよびマグネシ
ウムの酸化物をそれぞれLa2O3、TiO2、CaO、
およびMgOに換算して、La2O33.0乃至250mol％
とTiO251.0乃至62.0mol％とCaO0.5乃至45.0mol
％とMgO1.0乃至45.0mol％とからなるLa2O3―
TiO2―CaO―MgO系組成物が公知となつてい
る。しかしながら、その結晶粒径は5μm以上で大
きく、積層コンデンサなどのように電界強度の大
きい製品には不適当である。すなわち、結晶粒径
が大きい場合には、結晶粒子１個あたりにかかる
電界強度は大きくなり、そため破壊電圧は低くな
り、寿命も短くなり、従つて信頼性が低下すると
いう欠点があつた。また、La2O3を含有している
ために、アルミナ・セツターを用いる必要があ
り、通常の誘電体磁器組成物で用いるジルコニ
ア・セツターと使い別けをしなければならないと
いう製造工程面での煩雑さがあつた。 本発明者らは上記の従来の組成物の欠点を解決
し、結晶粒径が5μm未満のきわめて微細であるの
で破壊電圧が高くかつ寿命が長く、しかもジルコ
ニア・セツターにて焼成可能な誘電体磁器組成物
を提供すべく検討した結果、酸化ジルコニウムを
添加すると、得られた誘電体磁器組成物の結晶粒
子が微細化し、しかも誘電率、Ｑ、温度特性を低
下させることがなく、更にジルコニア・セツター
にて焼成可能であることを見出し、本発明に到達
した。すなわち、本発明の要旨とするところは、
La2O3―TiO2―CaO―MgO系組成物を主成分と
し、ジルコニウムの酸化物をZrO2に換算して、
該主成分に対し0.1重量％乃至8.0重量％含有して
なる誘電体磁器組成物、にある。 本発明の組成物は上記構成によつて、実施例に
示すように、結晶粒径がきわめて微細であるの
で、積層コンデンサなどのように電界強度の大き
い製品には好適である。すなわち、結晶粒径が微
細であるので結晶粒子１個あたりにかかる電界強
度が小さくなり、それによつて破壊電圧が高くな
り、寿命はのびて信頼性が向上する。また、本発
明の組成物は、酸化ジルコニウムを含有しない従
来の組成物と同等の誘電率、Ｑ、温度特性を有
し、実用的であることは実施例が示す通りであ
る。 本発明の組成物の組成において、酸化ジルコニ
ウムの量が0.1重量％未満であると、結晶粒径が
5μm以上になるとともにジルコニア・セツターと
反応し、また、8.0重量％を起えると粒径5μm以
上の結晶が発生する。 本発明の組成物は、例えば、焼成後に本発明の
組成になるように秤取された原料配合物をボール
ミルで湿式混合・粉砕し、得られた混合・粉砕物
を脱水・乾燥後、所定の形状に加圧成形して焼成
することにより得ることができる。この場合、原
料として使用するランタン化合物はLa2O3、La2
（C2O4）3・9H2O、チタン化合物はTiO2、Ti2O3、
カルシウム化合物はCaO、CaCO3、マグネシウ
ム化合物はMgO、MgC2O4・2H2O、ジルコニア
化合物はZrO2、3ZrO2・6H2Oが好適である。 次に本発明を実施例によつてさらに具体的に説
明するが、本発明はその要旨を越えない限り以下
の実施例に限定されるものではない。 実施例 原料として、主成分であるLa2O3、TiO2、
CaO、MgO、並びに添加成分であるZrO2を、そ
れぞれ試薬１級のLa2O3、TiO2、CaO、MgOお
よびZrO2を用い、焼成後に次の表に示す配合比
になるよう秤取し、ボールミル中で20時間湿式混
合・粉砕し、脱水・乾燥後、成形圧力3ton／cm2で
直径16mm厚さ0.6mmの円板に加圧成形し、成形物
を次の表に示す焼成温度で１時間焼成し、試料番
号１〜７とした。 これら試料の結晶粒径は光学顕微鏡により倍率
400で観察し、容量値およびＱ値は試料の両面に
銀電極を焼付け、YHPデジタルLCRメータモデ
ル4274Aを使用し、測定温度25℃、測定電圧
1.0Vrms、測定周波数100KHzによる測定により
求めた。温度特性は25℃における容量値を基準と
し85℃における容量値にて算出した。これら物性
の測定結果を次の表に併せ示す。 得られた試料はいずれも次の表が示すように、
酸化ジルコニウム添加により結晶粒径が5.0μm未
満で、かつ実用的な誘電率、Ｑ値および温度特性
を有し、しかもジルコニア・セツターにて焼成可
能な誘電体磁器組成物であり、積層コンデンサの
ごとき電界強度の大きい製品には最適である。 【表】
Claims (1)
- １ La2O3―TiO2―CaO―MgO系組成物を主成
分とし、ジルコニウムの酸化物をZrO2に換算し
て、該主成分に対し0.1重量％乃至8.0重量％含有
してなる誘電体磁器組成物。