PL155006B1 - Method of dyeing proteinous an/or polyamide fibre products - Google Patents
Method of dyeing proteinous an/or polyamide fibre productsInfo
- Publication number
- PL155006B1 PL155006B1 PL27496488A PL27496488A PL155006B1 PL 155006 B1 PL155006 B1 PL 155006B1 PL 27496488 A PL27496488 A PL 27496488A PL 27496488 A PL27496488 A PL 27496488A PL 155006 B1 PL155006 B1 PL 155006B1
- Authority
- PL
- Poland
- Prior art keywords
- parts
- dyeing
- agents
- bath
- polyamide
- Prior art date
Description
rzeczpospolita OPIS PATENTOWY POLSKARzeczpospolita PATENT DESCRIPTION POLAND
Patent dodatkowy do patentu nr Zgłoszono: 88 09 29 (P. 274964)Additional patent to patent no. Pending: 88 09 29 (P. 274964)
Int. Cl.5 D06P 1/10 D06P 3/02 C02J 3/20 Z/CQ9B 45/26Int. Cl. 5 D06P 1/10 D06P 3/02 C02J 3/20 Z / CQ9B 45/26
PierwszeństwoPriority
URZĄDOFFICE
PATENNOWYPATENNE
RPRP
Zgłoseenie ogłosznno: 90 04 02Application announced: 90 04 02
Opis paientowy opubiikownoo: 1992 02 228Customer description of the post office: 1992 02 228
HyiELfllJl δ fi Ó ί fiuHyiELfllJl δ fi Ó ί fiu
Twórcy wynalazku: Chrystian Przybylski, Anna Polka,Creators of the invention: Chrystian Przybylski, Anna Polka,
Wojciech Szafnicki, Mirosław MuszyńskiWojciech Szafnicki, Mirosław Muszyński
Uprawniony z patentu: Ośrodek Badawczo-Rozwojowy Przemysłu Barwników „Organika, Zgierz (Polska)Entitled by the patent: Research and Development Center of the Dye Industry "Organika, Zgierz (Poland)
Sposób barwienia wyrobów z włókien proteinowych i/lub poliamidowychA method of dyeing products made of protein and / or polyamide fibers
Przedmiotem wynalazku jest sposób barwienia wyrobów z włókien proteinowych i/lub poliamidowych na kolor szary.The subject of the invention is a method for dyeing protein and / or polyamide fiber products gray.
Znany sposób barwienia wyrobów z włókien proteinowych i/lub poliamidowych polega na poddaniu korzystnie wypranego wyrobu procesowi barwienia sulfonowymi barwnikami metalokomplekowymi 1:2 w obecności środków kwasowych bądź kwasotwórczych albo mieszanin tych środków oraz ewentualnie środków pomocniczych w podwyższonej temperaturze, a następnie płukaniu wybarwionego wyrobu oraz ewentualnej obróbce środkami wykańczającymi, zwłaszcza środkami o działaniu zmiękczającym i antyelektrostatycznym.The known method of dyeing products made of protein and / or polyamide fibers consists in subjecting the preferably washed product to a dyeing process with sulphonic metal complex dyes 1: 2 in the presence of acidic or acid-forming agents or mixtures of these agents and, possibly, auxiliaries at elevated temperature, and then rinsing the dyed product and, if necessary, treatment with finishing agents, especially with softening and antistatic agents.
Opracowano nowy azowy barwnik chromokompleksowy 1:2 o wzorze podanym na rysunku, w którym M i Mi są jednakowe względnie różne i odznaczają bezbarwne kationy. W wyniku przeprowadzonych badań ustalono, że nowy barwnik charakteryzuje się korzystnymi właściwościami kolorystycznymi i użytkowo-aplikacyjnymi w zastosowaniu do barwienia wyrobów z włókien proteinowych i/lub poliamidowych. Sposób otrzymywania barwnika jest między innymi przedmiotem odrębnego, równoczesnego zgłoszenia patentowego.A new 1: 2 azo chromocomplex dye with the formula shown in the figure was developed, wherein M and Mi are the same relatively different and have colorless cations. As a result of the conducted research, it was found that the new dye is characterized by favorable color and application and application properties when used for dyeing protein and / or polyamide fiber products. The method of obtaining the dye is, inter alia, the subject of a separate, simultaneous patent application.
Sposobem według wynalazku do barwienia wyrobów z włókien proteinowych i/lub poliamidowych stosuje się nowy azowy barwnik chromokompleksowy 1:2 o wzorze podanym na rysunku, najczęściej w postaci soli metali alkalicznych i ziem alkalicznych czy amonowych, ewentualnie podstawionychIn the process according to the invention, a new 1: 2 azo chromocomplex dye with the formula shown in the figure is used for dyeing protein and / or polyamide fiber products, most often in the form of alkali and alkaline earth or ammonium salts, optionally substituted
Proces barwienia sposobem według wynalazku jest prowadzony w obecności środków kwasowych i/lub kwasotwórczych, zwłaszcza takich jak kwas octowy bądź siarczan amonu, przy czym w barwieniu wełny i jedwabiu naturalnego nie jest konieczne stosowanie w czasie procesu środków pomocniczych. Jednakże środki wyrównujące o charakterze niejonowym wykazujące powinowactwo do barwników, przykładowo produkty addycji tlenku etylenu do mieszaniny amin tłuszczowych znane jako Rokamin S-22 albo SR-22, podnoszą komfort uzyskiwanych sposobem według wynalazku wybarwień wyrobów z włókien proteinowych. W przypadku użycia tych środków poleca się je stosować w ilości 0,5 - 1,0% w stosunku do masy barwionego wyrobu.The dyeing process according to the invention is carried out in the presence of acidic and / or acid-forming agents, such as acetic acid or ammonium sulphate, in particular, it is not necessary to use auxiliaries during the dyeing of wool and natural silk. However, non-ionic leveling agents having an affinity for dyes, for example addition products of ethylene oxide to a mixture of fatty amines, known as Rokamin S-22 or SR-22, improve the comfort of the dyeing of protein fiber products obtained by the method according to the invention. If these agents are used, it is recommended to use them in the amount of 0.5-1.0% of the weight of the colored product.
155 006155 006
W barwieniu mieszanek wełna/poliamid sposobem według wynalazku bez użycia środków pomocniczych otrzymuje się nieco silniejsze zabarwienie składnika poliamidowego. Dla równomiernego pokrycia obydwu składników należy zastosować pomocnicze środki wyrównujące, które blokują poliamid, np. środki będące kompozycją sulfonowanych i oksyetylowanych pochodnych alkilobenzenu wprowadzone na rynek pod nazwą Polanol S lub ST.In the dyeing of wool / polyamide blends according to the invention without the use of auxiliaries, a slightly stronger dyeing of the polyamide component is obtained. To ensure even coverage of both components, use leveling aids that block the polyamide, e.g., compositions of sulfonated and ethoxylated alkylbenzene derivatives marketed under the name Polanol S or ST.
Przy barwieniu sposobem według wynalazku wyrobów z włókien poliamidowych zaleca się stosowanie środków pomocniczych typu Rokamin względnie Polanol dla zneutralizowania tendencji nowego barwnika do ujawnienia pasiastości materiałowej.When dyeing polyamide fiber products according to the invention, it is advisable to use auxiliaries of the Rokamin or Polanol type to neutralize the tendency of the new dye to reveal material streaks.
Przy ewentualnej obróbce końcowej wybarwień uzyskiwanych sposobem według wynalazku jako środki o działaniu zmiękczającym i antyelektrostatycznym przykładowo mogą być użyte produkty przyłączenia tlenku etylenu do nasyconych kwasów tłuszczowych wprowadzono do obrotu jako Rokacety, zwłaszcza Rokacet S-7 bądź S-8.In the eventual post-treatment of the dyes obtained by the process according to the invention, the products with the addition of ethylene oxide to saturated fatty acids, for example, may be used as softening and antistatic agents.
Otrzymywane sposobem według wynalazku wybarwienia w interesującym kolorze szarym o odcieniu zielonym są intensywne oraz równe i posiadają bardzo dobre odporności na czynniki mokre, tarcie oraz światło. Dzięki dobrej rozpuszczalności nowego barwnika w zimnej i gorącej wodzie sposób według wynalazku może być realizowany metodą ciągłą, a także w barwieniu poliamidowej przędzy dywanowej metodą „Space dyeing“.The dyes obtained by the method according to the invention in an interesting gray color with a green shade are intense and even and have very good resistance to wet factors, abrasion and light. Due to the good solubility of the new dye in cold and hot water, the method according to the invention can be carried out in a continuous process as well as in the dyeing of polyamide carpet yarns by the "Space dyeing" method.
Wynalazek ilustrują, nie ograniczając jego zakresu, niżej podane przykłady, w których części i procenty oznaczają części i procenty wagowe, a stopnie temperatury podano w stopniach Celsjusza:The invention is illustrated without limiting its scope in the following examples in which parts and percentages are parts and percentages by weight and degrees of temperatures are in degrees Celsius:
Przykład 1100 części dzianiny poliamidowej o symbolu JE 44 barwi się w aparacie AHIBA w kąpieli o składzie: 0,6 części barwnika o wzorze podanym na rysunku, w którym M — M1 i oznacza atom sodu, 2,0 części siarczanu amonowego, 2,0 części kwasu octowego 40%, 0,5 części Rokaminu SR-22 i 4000 części wody. Krotność kąpieli 1:40. Dzianinę wprowadza się do kąpieli o temperaturze 50°. Kąpiel ogrzewa się w czasie 30 minut do wrzenia i utrzymuje się w tej temperaturze 45 minut.Example 1100 parts of a polyamide knit with the symbol JE 44 is dyed in the AHIBA apparatus in a bath composed of: 0.6 parts of the dye according to the formula shown in the figure, where M - M1 i represents sodium, 2.0 parts of ammonium sulphate, 2.0 parts of acetic acid 40%, 0.5 parts of Rokay SR-22 and 4000 parts of water. The ratio of the bath is 1:40. The knitted fabric is put into a bath at a temperature of 50 °. The bath is heated to boiling within 30 minutes and kept at this temperature for 45 minutes.
Następnie kąpiel schładza się do temperatury 70°. Wybarwioną dzianinę płucze się w ciepłej, a później w zimnej wodzie i suszy. Otrzymuje się intensywne, równomierne wybarwienie w kolorze szarym o odcieniu zielonym i dobrych odpornościach na czynniki mokre, tarcie i światło.The bath is then cooled to 70 °. The dyed fabric is rinsed in warm and then cold water and dried. An intense, even, gray, green tint with good resistance to wet agents, abrasion and light is obtained.
Przykład II. 100 części dzianiny poliamidowej o symbolu JE 44 barwi się w aparacie AHIBA w kąpieli o składzie: 0,2 części barwnika o wzorze podanym na rysunku, w którym M oznacza atom sodu, a M1 grupę amonową, 2,0 części siarczanu amonowego, 1,0 części kwasu octowego 40%, 0,5 części Rokaminu SR-22 i 4000 części wody. Krotność kąpieli 1:40. Dzianinę wprowadza się do kąpieli o temperaturze 50°. Kąpiel, ogrzewa się w czasie 45 minut do wrzenia i utrzymuje w tej temperaturze 45 minut. Następnie kąpiel schładza się do temperatury 70°. Wybarwioną dzianinę płucze się w ciepłej, a później w zimnej wodzie i suszy.Example II. 100 parts of polyamide knitted fabric with the symbol JE 44 is dyed in the AHIBA apparatus in a bath composed of: 0.2 parts of the dye according to the formula given in the figure, where M represents the sodium atom and M 1 is the ammonium group, 2.0 parts of ammonium sulphate, 1 .0 parts of acetic acid 40%, 0.5 parts of Rok R-22 and 4000 parts of water. The ratio of the bath is 1:40. The knitted fabric is put into a bath at a temperature of 50 °. The bath is heated to boiling within 45 minutes and kept at this temperature for 45 minutes. The bath is then cooled to 70 °. The dyed fabric is rinsed in warm and then cold water and dried.
Otrzymuje się równomierne wybarwienie w kolorze jasnej szarzeni o odcieniu zielonkawym i bardzo dobrych odpornościach na czynniki mokre i tarcie oraz dobrych odpornościach na światło.A uniform, light gray color with a greenish tinge is obtained, with very good wet and friction fastness, and good light fastness.
Przykład III. 100 części tkaniny wełnianej sukienkowej artykuł 9109 barwi się w aparacie AHIBA w kąpieli o składzie: 0,6 części barwnika o wzorze podanym na rysunku, w którym M oznacza atom sodu, a M1 atom potasu, 4,0 części kwasu octowego 40%, 0,5 części Rokaminu SR-22 i 4000 części wody. Krotność kąpieli 1:40. Tkaninę wprowadza się do kąpieli o temperaturze 40°, ogrzewa się w czasie 45 minut do wrzenia i utrzymuje w tej temperaturze w czasie 60 minut. Kąpiel schładza się do temperatury 60°. Tkaninę dokładnie płucze się w ciepłej wodzie i suszy.Example III. 100 parts of woolen cloth fabric, article 9109 is dyed in the AHIBA apparatus in a bath composed of: 0.6 parts of the dye according to the formula given in the figure, where M is sodium and M1 is potassium, 4.0 parts of acetic acid 40%, 0 , 5 parts of the SR-22 Year and 4000 parts of water. The ratio of the bath is 1:40. The fabric is placed in a bath at 40 ° C, heated to boiling for 45 minutes and kept at this temperature for 60 minutes. The bath is cooled down to a temperature of 60 °. The fabric is rinsed thoroughly in warm water and dried.
Otrzymuje się intensywne, równomierne wybarwienie w kolorze szarym o odcieniu zielonym i dobrych odpornościach na czynniki mokre, tarcie i światło.An intense, even, gray, green tint with good resistance to wet agents, abrasion and light is obtained.
Przykład IV. 100 części przędzy dywanowej, w skład której wchodzi: 70% wełny i 30% włókna poliamidowego, barwi się w aparacie AHIBA w kąpieli o składzie: 0,4 części barwnika o wzorze podanym na rysunku, w którym M oznacza atom sodu, a M1 atom wapnia, 2,0 części siarczanu amonowego, 4,0 części kwasu octowego 40%, 1,0 części Polanolu S i 4000 części wody. Krotność kąpieli 1:40. Przędzę wprowadza się do kąpieli o temperaturze 40°, ogrzewa w czasie 30 minut do temperatury wrzenia i utrzymuje w tej temperaturze w czasie 60 minut. Kąpiel schładza się do temperatury 60-70° i płucze się przędzę w ciepłej, a później w zimnej wodzie. Wypłukaną przędzę suszy się.Example IV. 100 parts of carpet yarn, consisting of: 70% wool and 30% polyamide fiber, are dyed in the AHIBA apparatus in a bath composed of: 0.4 parts of the dye according to the formula given in the figure, where M is sodium and M1 is calcium, 2.0 parts of ammonium sulfate, 4.0 parts of acetic acid 40%, 1.0 parts of Polanol S and 4000 parts of water. The ratio of the bath is 1:40. The yarn is introduced into a bath at 40 ° C, heated within 30 minutes to the boiling point and kept at this temperature for 60 minutes. The bath is cooled to a temperature of 60-70 ° and the yarn is rinsed in warm and then in cold water. The rinsed yarn is dried.
155 006155 006
Otrzymuje się wybarwienie w kolorze szarym o odcieniu zielonym i dobrych odpornościach na czynniki mokre, tarcie i światło. Włókna wełniane i poliamidowe są zabarwione w zbliżonej intensywności.A gray color with a green shade and good resistance to wet agents, abrasion and light is obtained. Wool and polyamide fibers are dyed with a similar intensity.
PrzykładV. 100 części jedwabiu naturalnego barwni się w aparacie AHIBA w kąpieli o składzie: 0,6 części barwnika o wzorze przedstawionym na rysunku, w którym M = M1 i oznacza atom sodu, 4,0 części kwasu octowego 40%, 0,5 części Rokaminu SR-22 i 4000 części wody. Krotność kąpieli 1:40. Tkaninę wprowadza się do kąpieli o temperaturze 40°, ogrzewa w czasie 45 minut do wrzenia i utrzymuje w tej temperaturze w czasie 60 minut. Następnie kąpiel schładza się do temperatury 60°. Tkaninę dokładnie płucze się w ciepłej, a później w zimnej wodzie i suszy.ExampleV. 100 parts of natural silk are dyed in the AHIBA apparatus in a bath composed of: 0.6 parts of the dye according to the formula shown in the figure, where M = M1 i denotes a sodium atom, 4.0 parts of acetic acid 40%, 0.5 parts of Rokumn SR -22 and 4000 parts of water. The ratio of the bath is 1:40. The fabric is placed in a bath at 40 ° C, heated to boiling for 45 minutes and kept at this temperature for 60 minutes. The bath is then cooled to 60 °. The fabric is rinsed thoroughly in warm and then cold water and dried.
Otrzymuje się równomierne wybarwnienie w kolorze szarym o odcieniu zielonym i dobrych odpornościach na czynniki mokre, tarcie i światło.A uniform gray with a green tinge is obtained and good resistance to wet agents, rubbing and light.
Claims (1)