PL2762600T3 - Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania - Google Patents

Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania

Info

Publication number
PL2762600T3
PL2762600T3 PL12834953T PL12834953T PL2762600T3 PL 2762600 T3 PL2762600 T3 PL 2762600T3 PL 12834953 T PL12834953 T PL 12834953T PL 12834953 T PL12834953 T PL 12834953T PL 2762600 T3 PL2762600 T3 PL 2762600T3
Authority
PL
Poland
Prior art keywords
hot
steel sheet
galvanized steel
dip galvanized
producing same
Prior art date
Application number
PL12834953T
Other languages
English (en)
Inventor
Masafumi Azuma
Chisato Wakabayashi
Takayuki Nozaki
Manabu Takahashi
Nobuhiro Fujita
Original Assignee
Nippon Steel & Sumitomo Metal Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corporation filed Critical Nippon Steel & Sumitomo Metal Corporation
Publication of PL2762600T3 publication Critical patent/PL2762600T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
PL12834953T 2011-09-30 2012-09-28 Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania PL2762600T3 (pl)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2011217108 2011-09-30
JP2011218046 2011-09-30
EP12834953.7A EP2762600B1 (en) 2011-09-30 2012-09-28 Hot-dip galvanized steel sheet and process for producing same
PCT/JP2012/075215 WO2013047820A1 (ja) 2011-09-30 2012-09-28 溶融亜鉛めっき鋼板及びその製造方法

Publications (1)

Publication Number Publication Date
PL2762600T3 true PL2762600T3 (pl) 2019-09-30

Family

ID=47995843

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12834953T PL2762600T3 (pl) 2011-09-30 2012-09-28 Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania

Country Status (14)

Country Link
US (1) US10407760B2 (pl)
EP (1) EP2762600B1 (pl)
JP (1) JP5569647B2 (pl)
KR (3) KR101935112B1 (pl)
CN (1) CN103827341B (pl)
BR (1) BR112014007500A2 (pl)
CA (1) CA2850044C (pl)
ES (1) ES2732799T3 (pl)
MX (1) MX373591B (pl)
PL (1) PL2762600T3 (pl)
RU (1) RU2566131C1 (pl)
TW (1) TWI500780B (pl)
WO (1) WO2013047820A1 (pl)
ZA (1) ZA201402259B (pl)

Families Citing this family (75)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BR112014007500A2 (pt) * 2011-09-30 2017-04-04 Nippon Steel & Sumitomo Metal Corp folha de aço galvanizada por imersão a quente e método de fabricação da mesma
JP6246621B2 (ja) * 2013-05-08 2017-12-13 株式会社神戸製鋼所 引張強度が１１８０ＭＰａ以上の強度−曲げ性バランスに優れた溶融亜鉛めっき鋼板もしくは合金化溶融亜鉛めっき鋼板
MX386196B (es) * 2013-08-02 2025-03-18 Jfe Steel Corp Lámina de acero de alta resistencia que tiene alto módulo de young y método para la fabricación de la misma.
EP2998415B1 (en) 2013-08-02 2017-09-06 JFE Steel Corporation High-strength, high-young's modulus steel plate, and manufacturing method thereof
JP5821912B2 (ja) 2013-08-09 2015-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
HUE046359T2 (hu) 2013-12-11 2020-03-30 Arcelormittal Martenzites acél töréssel szembeni késleltetett ellenállással, valamint gyártási eljárás
WO2015185956A1 (en) * 2014-06-06 2015-12-10 ArcelorMittal Investigación y Desarrollo, S.L. High strength multiphase galvanized steel sheet, production method and use
PL3492608T3 (pl) 2014-07-03 2020-08-24 Arcelormittal Sposób wytwarzania niepowlekanej blachy stalowej o ultrawysokiej wytrzymałości oraz wytworzona blacha
MX2017005507A (es) 2014-11-05 2017-06-20 Nippon Steel & Sumitomo Metal Corp Hoja de acero galvanizad por inmersion en caliente.
WO2016072477A1 (ja) 2014-11-05 2016-05-12 新日鐵住金株式会社 溶融亜鉛めっき鋼板
BR112017007973A2 (pt) 2014-11-05 2017-12-19 Nippon Steel & Sumitomo Metal Corp folha de aço galvanizada por imersão a quente
CN107148488B (zh) * 2015-01-07 2020-02-07 Posco公司 拉伸强度为1300Mpa以上的超高强度镀覆钢板及其制造方法
JP6082451B2 (ja) * 2015-03-18 2017-02-15 株式会社神戸製鋼所 熱間プレス用鋼板およびその製造方法
JP6453140B2 (ja) * 2015-03-31 2019-01-16 株式会社神戸製鋼所 切断端面の耐遅れ破壊性に優れた高強度鋼板およびその製造方法
EP3309273B1 (en) * 2015-06-11 2021-05-26 Nippon Steel Corporation Galvannealed steel sheet and method for manufacturing same
JP6460239B2 (ja) 2015-07-13 2019-01-30 新日鐵住金株式会社 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP6460238B2 (ja) 2015-07-13 2019-01-30 新日鐵住金株式会社 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
TWI551695B (zh) * 2015-07-13 2016-10-01 新日鐵住金股份有限公司 鋼板、熔融鍍鋅鋼板及合金化熔融鍍鋅鋼板以及其等之製造方法
JP6724320B2 (ja) * 2015-09-10 2020-07-15 日本製鉄株式会社 伸びと穴広げ性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
JP2017075394A (ja) * 2015-10-16 2017-04-20 株式会社神戸製鋼所 高強度溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法
KR101758485B1 (ko) 2015-12-15 2017-07-17 주식회사 포스코 표면품질 및 점 용접성이 우수한 고강도 용융아연도금강판 및 그 제조방법
JP6164280B2 (ja) * 2015-12-22 2017-07-19 Ｊｆｅスチール株式会社 表面外観および曲げ性に優れるＭｎ含有合金化溶融亜鉛めっき鋼板およびその製造方法
JP2017115205A (ja) * 2015-12-24 2017-06-29 日新製鋼株式会社 めっき密着性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ合金めっき鋼板の製造方法
UA119946C2 (uk) * 2015-12-29 2019-08-27 Арселорміттал Спосіб виробництва надвисокоміцної листової сталі, підданої цинкуванню з відпалюванням, і одержана листова сталь, піддана цинкуванню з відпалюванням
KR102170060B1 (ko) * 2016-01-27 2020-10-26 제이에프이 스틸 가부시키가이샤 고항복비형 고강도 아연 도금 강판 및 그의 제조 방법
KR101767818B1 (ko) 2016-03-08 2017-08-11 주식회사 포스코 소부경화성 및 내시효성이 우수한 용융 아연계 도금강판 및 그 제조방법
US11560606B2 (en) 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
JP7186694B2 (ja) 2016-05-10 2022-12-09 ユナイテッド ステイツ スチール コーポレイション 高強度鋼製品及び該製品を製造するためのアニーリング工程
CN105925887B (zh) * 2016-06-21 2018-01-30 宝山钢铁股份有限公司 一种980MPa级热轧铁素体贝氏体双相钢及其制造方法
CN105908089B (zh) * 2016-06-28 2019-11-22 宝山钢铁股份有限公司 一种热浸镀低密度钢及其制造方法
WO2018011978A1 (ja) 2016-07-15 2018-01-18 新日鐵住金株式会社 溶融亜鉛めっき鋼板
TWI613300B (zh) * 2016-09-06 2018-02-01 新日鐵住金股份有限公司 高強度冷軋鋼板
JP6798556B2 (ja) * 2016-09-13 2020-12-09 日本製鉄株式会社 鋼板
MX2019005168A (es) 2016-11-04 2019-10-02 Nucor Corp Acero multifase laminado en frío de resistencia ultra alta.
US11021776B2 (en) 2016-11-04 2021-06-01 Nucor Corporation Method of manufacture of multiphase, hot-rolled ultra-high strength steel
KR101889181B1 (ko) * 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
MX391277B (es) 2016-12-27 2025-03-21 Jfe Steel Corp Lámina de acero galvanizado de alta resistencia y método para producir la misma.
MX2019007660A (es) * 2017-01-25 2019-08-29 Nippon Steel Corp Lamina de acero.
US10895002B2 (en) 2017-01-30 2021-01-19 Nippon Steel Corporation Steel sheet
BR112019006502A2 (pt) * 2017-01-31 2019-08-13 Nippon Steel & Sumitomo Metal Corp chapa de aço
KR102312464B1 (ko) 2017-02-10 2021-10-13 제이에프이 스틸 가부시키가이샤 고강도 아연 도금 강판 및 그 제조 방법
CN107287542A (zh) * 2017-05-18 2017-10-24 当涂县宏宇金属炉料有限责任公司 一种加强热浸镀锌钢板防腐蚀性能的处理工艺
DE102017218704A1 (de) 2017-10-19 2019-04-25 Thyssenkrupp Ag Verfahren zur Herstellung eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils
WO2019092467A1 (en) * 2017-11-08 2019-05-16 Arcelormittal A galvannealed steel sheet
WO2019092468A1 (en) 2017-11-08 2019-05-16 Arcelormittal A hot-dip coated steel sheet
KR102333410B1 (ko) 2017-11-15 2021-12-02 닛폰세이테츠 가부시키가이샤 고강도 냉연 강판
WO2019122965A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
KR102020411B1 (ko) 2017-12-22 2019-09-10 주식회사 포스코 가공성이 우수한 고강도 강판 및 이의 제조방법
KR102031454B1 (ko) 2017-12-24 2019-10-11 주식회사 포스코 저온 밀착성과 가공성이 우수한 용융아연도금강판 및 그 제조방법
WO2019130713A1 (ja) 2017-12-27 2019-07-04 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
PT3749790T (pt) * 2018-02-07 2024-08-23 Tata Steel Nederland Tech Bv Aço de alta resistência laminado a quente ou laminado a frio e recozido, e método para a sua produção
KR102467656B1 (ko) * 2018-03-30 2022-11-17 닛폰세이테츠 가부시키가이샤 강판 및 그 제조 방법
CN111936650B (zh) 2018-03-30 2022-04-08 杰富意钢铁株式会社 高强度镀锌钢板、高强度部件和它们的制造方法
WO2019194251A1 (ja) * 2018-04-03 2019-10-10 日本製鉄株式会社 鋼板及び鋼板の製造方法
WO2020058748A1 (en) 2018-09-20 2020-03-26 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2020065381A1 (en) * 2018-09-28 2020-04-02 Arcelormittal Hot rolled steel sheet and a method of manufacturing thereof
KR102222614B1 (ko) * 2018-11-27 2021-03-05 주식회사 포스코 수소취성 저항성이 우수한 초고강도 냉연강판 및 그 제조 방법
EP3992314A4 (en) * 2019-06-28 2023-07-19 Nippon Steel Corporation GALVANISED STEEL
JP2021014605A (ja) * 2019-07-10 2021-02-12 株式会社神戸製鋼所 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
WO2021026437A1 (en) * 2019-08-07 2021-02-11 United States Steel Corporation High ductility zinc-coated steel sheet products
CN110564928A (zh) * 2019-10-18 2019-12-13 山东钢铁集团日照有限公司 一种生产不同屈服强度级别热镀锌dp980钢的方法
KR102321301B1 (ko) * 2019-12-09 2021-11-02 주식회사 포스코 내해수성이 우수한 구조용 강판 및 이의 제조방법
WO2021161679A1 (ja) 2020-02-13 2021-08-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN112267069B (zh) * 2020-09-30 2022-03-29 江苏省沙钢钢铁研究院有限公司 2100MPa级镀锌钢丝用盘条及其制造方法
KR102502605B1 (ko) * 2020-12-18 2023-02-24 주식회사 포스코 표면품질과 전기저항 점용접성이 우수한 고강도 용융아연도금 강판 및 그 제조방법
KR102457023B1 (ko) * 2020-12-21 2022-10-21 주식회사 포스코 표면품질과 점 용접성이 우수한 고강도 용융아연도금 강판 및 그 제조방법
WO2022138395A1 (ja) * 2020-12-24 2022-06-30 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板およびその製造方法
CN117242199B (zh) * 2021-04-27 2026-01-09 日本制铁株式会社 钢焊接构件
US12534790B2 (en) * 2021-05-21 2026-01-27 Nippon Steel Corporation Hot dip galvannealed steel sheet
US20240344165A1 (en) 2021-08-27 2024-10-17 Nippon Steel Corporation Steel sheet and press-formed article
CN114107818B (zh) * 2021-11-19 2023-03-28 本钢板材股份有限公司 一种1000MPa级热镀锌双相钢及其生产方法
CN114875336A (zh) * 2022-05-31 2022-08-09 山东钢铁集团日照有限公司 一种增塑性热镀锌复相钢的生产调控方法
MY206044A (en) * 2024-03-28 2024-11-26 Wei Dat Steel Wire Sdn Bhd Steel Product and Its Producing Method Thereof

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59219473A (ja) 1983-05-26 1984-12-10 Nippon Steel Corp カラ−エツチング液及びエツチング方法
JPH11293383A (ja) * 1998-04-09 1999-10-26 Nippon Steel Corp 水素性欠陥の少ない厚鋼板およびその製造方法
JP3882474B2 (ja) 2000-07-06 2007-02-14 住友金属工業株式会社 金属板の熱間プレス成形方法
BR0210265B1 (pt) * 2001-06-06 2013-04-09 folha de aÇo galvanizado ou galvanelado com imersço a quente.
KR100748736B1 (ko) 2003-03-31 2007-08-13 신닛뽄세이테쯔 카부시키카이샤 합금화 용융 아연 도금 강판 및 그 제조 방법
EP1612288B9 (en) 2003-04-10 2010-10-27 Nippon Steel Corporation A method for producing a hot-dip zinc coated steel sheet having high strength
JP4192051B2 (ja) * 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
BRPI0621421B8 (pt) * 2006-01-30 2019-05-21 Nippon Steel & Sumitomo Metal Corp chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada e recozida e métodos de produção das mesmas
JP4837459B2 (ja) * 2006-06-30 2011-12-14 新日本製鐵株式会社 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2007270176A (ja) * 2006-03-30 2007-10-18 Nippon Steel Corp 表面外観及びめっき密着性に優れた合金化溶融亜鉛めっき鋼板
JP4411326B2 (ja) 2007-01-29 2010-02-10 株式会社神戸製鋼所 リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4894863B2 (ja) 2008-02-08 2012-03-14 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5438302B2 (ja) * 2008-10-30 2014-03-12 株式会社神戸製鋼所 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法
KR101501048B1 (ko) * 2009-03-03 2015-03-10 헥사곤 테크놀로지 에이에스 압력 릴리프 밸브용 형상 기억 합금 트리거
JP4737319B2 (ja) * 2009-06-17 2011-07-27 Ｊｆｅスチール株式会社 加工性および耐疲労特性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JP5435340B2 (ja) * 2009-07-17 2014-03-05 富士ゼロックス株式会社 蓋装置および画像形成装置
US20110019800A1 (en) * 2009-07-24 2011-01-27 Martin Spahn X-ray detector for recording x-ray images and x-ray recording system
JP5499663B2 (ja) * 2009-11-30 2014-05-21 新日鐵住金株式会社 機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法
MX360965B (es) * 2009-11-30 2018-11-23 Nippon Steel & Sumitomo Metal Corp Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma.
CA2782777C (en) * 2010-01-13 2014-11-18 Nippon Steel Corporation High tensile steel sheet superior in formability and method of manufacturing the same
BR112014007500A2 (pt) * 2011-09-30 2017-04-04 Nippon Steel & Sumitomo Metal Corp folha de aço galvanizada por imersão a quente e método de fabricação da mesma

Also Published As

Publication number Publication date
US10407760B2 (en) 2019-09-10
TWI500780B (zh) 2015-09-21
KR101951081B1 (ko) 2019-02-21
CA2850044C (en) 2016-08-23
CN103827341B (zh) 2016-08-31
EP2762600A1 (en) 2014-08-06
MX2014003716A (es) 2014-06-23
MX373591B (es) 2020-05-15
CA2850044A1 (en) 2013-04-04
JPWO2013047820A1 (ja) 2015-03-30
KR20140068122A (ko) 2014-06-05
ES2732799T3 (es) 2019-11-26
KR20160075850A (ko) 2016-06-29
US20140234657A1 (en) 2014-08-21
JP5569647B2 (ja) 2014-08-13
BR112014007500A2 (pt) 2017-04-04
KR101935112B1 (ko) 2019-01-03
WO2013047820A1 (ja) 2013-04-04
ZA201402259B (en) 2015-04-29
RU2566131C1 (ru) 2015-10-20
CN103827341A (zh) 2014-05-28
KR20160075849A (ko) 2016-06-29
EP2762600A4 (en) 2015-09-23
EP2762600B1 (en) 2019-04-17
TW201319268A (zh) 2013-05-16

Similar Documents

Publication Publication Date Title
PL2762579T3 (pl) Blacha stalowa cienka cynkowana na gorąco o dużej wytrzymałości i sposób jej wytwarzania
ZA201402259B (en) Hot-dip galvanized steel sheet and manufacturing method thereof
EP2811047A4 (en) FIREPLATED STEEL PLATE AND METHOD OF MANUFACTURING THEREOF
PL2738280T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości mająca doskonałą zginalność oraz sposób jej wytwarzania
PL2835440T3 (pl) Blacha stalowa cienka walcowana na gorąco i cynkowana z przeżarzaniem zanurzeniowo na gorąco oraz sposób jej wytwarzania
ZA201402256B (en) High-strength hot-dip galvanized steel sheet
PL2716783T3 (pl) Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania
ZA201402216B (en) Galvanized steel sheet and method of manufacturing the same
PL2692895T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
AU2012276644A1 (en) High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof
ZA201400359B (en) Hot-dip plated cold-rolled steel sheet and process for producing same
ZA201307002B (en) Hot-rolled steel sheet and associated production method
PL2738276T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości i blacha stalowa cienka o dużej wytrzymałości mająca doskonałą formowalność oraz sposób ich wytwarzania
ZA201404813B (en) Cold-rolled steel sheet and method for producing cold-rolled steel sheet
PL2918696T3 (pl) Stopowa blacha stalowa cienka cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
PL2653582T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
ZA201400360B (en) Method for producing col-rolled steel sheet
ZA201402308B (en) Alloyed hot-dip galvanized steel sheet
PL2803744T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
EP2762584A4 (en) HOT-ROLLED STEEL SHEET, AND METHOD FOR MANUFACTURING THE SAME
PL2610357T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
PL2944705T3 (pl) Stopowa blacha stalowa cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
EP2548664A4 (en) Process for producing hot-rolled steel sheet and process for producing hot-dip galvanized steel sheet
EP2796584A4 (en) HIGH STRENGTH STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME
SG2014007579A (en) Molten zn-al alloy-plated steel sheet and manufacturing method thereof