PL441557A1 - Laminat magnez-szkło i sposób jego wytwarzania - Google Patents

Laminat magnez-szkło i sposób jego wytwarzania

Info

Publication number
PL441557A1
PL441557A1 PL441557A PL44155722A PL441557A1 PL 441557 A1 PL441557 A1 PL 441557A1 PL 441557 A PL441557 A PL 441557A PL 44155722 A PL44155722 A PL 44155722A PL 441557 A1 PL441557 A1 PL 441557A1
Authority
PL
Poland
Prior art keywords
thickness
magnesium
diethylenetriamine
weight
amount
Prior art date
Application number
PL441557A
Other languages
English (en)
Other versions
PL243177B1 (pl
Inventor
Monika Ostapiuk
Jarosław Bieniaś
Patryk Jakubczak
Magda Droździel-Jurkiewicz
Piotr Podolak
Original Assignee
Politechnika Lubelska
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Politechnika Lubelska filed Critical Politechnika Lubelska
Priority to PL441557A priority Critical patent/PL243177B1/pl
Publication of PL441557A1 publication Critical patent/PL441557A1/pl
Publication of PL243177B1 publication Critical patent/PL243177B1/pl

Abstract

Przedmiotem zgłoszenia jest laminat magnez-szkło i sposób jego wytwarzania. Laminat magnez-szkło, charakteryzuje się tym, że w części środkowej laminatu znajdują się cztery jednakowe warstwy samonaprawiające się (4) o grubości od 1,5 mm do 2,3 mm każda, składające się z włókien szklanych wypełnionych roztworem dietylenotriaminy składającym się z wody w ilości 10% wagowo i dietylenotriaminy w ilości 90% wagowo i połączonych żywicą epoksydową. Do zewnętrznych powierzchni skrajnych warstw samonaprawiających się (4) przylega adhezyjnie warstwa żywicy polimerowej (3) o grubości od 10 µm do 30 µm, która nałożona jest na warstwę ceramiczną (2) o grubości od 8 µm do 15 µm znajdującą się na arkuszu blachy (1) ze stopu magnezu o grubości od 0,3 mm do 0,5 mm. Sposób wytwarzania laminatu magnez-szkło, polega na tym, że na dwa arkusze blachy (1) ze stopu magnezu o grubości od 0,3 mm do 0,5 mm posiadające na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm nakłada się obustronnie warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm, po czym pozostawia się na czas 3 h w temperaturze 23°C. Następnie na jeden z arkuszy blachy (1) ze stopu magnezu o grubości od 0,3 mm do 0,5 mm posiadający na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm i warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm nakłada się kolejno cztery jednakowe warstwy włókien szklanych wypełnionych roztworem dietylenotriaminy składającym się z wody w ilości 10% wagowo i dietylenotriaminy w ilości 90% wagowo o grubości od 0,25 mm do 1 mm każda.
PL441557A 2022-06-27 2022-06-27 Laminat magnez-szkło i sposób jego wytwarzania PL243177B1 (pl)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PL441557A PL243177B1 (pl) 2022-06-27 2022-06-27 Laminat magnez-szkło i sposób jego wytwarzania

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PL441557A PL243177B1 (pl) 2022-06-27 2022-06-27 Laminat magnez-szkło i sposób jego wytwarzania

Publications (2)

Publication Number Publication Date
PL441557A1 true PL441557A1 (pl) 2023-01-02
PL243177B1 PL243177B1 (pl) 2023-07-10

Family

ID=84786793

Family Applications (1)

Application Number Title Priority Date Filing Date
PL441557A PL243177B1 (pl) 2022-06-27 2022-06-27 Laminat magnez-szkło i sposób jego wytwarzania

Country Status (1)

Country Link
PL (1) PL243177B1 (pl)

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL248762B1 (pl) * 2024-01-17 2026-01-26 Lubelska Polt Laminat metal-węgiel i sposób jego wytwarzania
PL248600B1 (pl) * 2024-01-17 2026-01-05 Lubelska Polt Laminat metal-węgiel i sposób jego wytwarzania
PL248599B1 (pl) * 2024-01-17 2026-01-05 Lubelska Polt Laminat metal-węgiel i sposób jego wytwarzania
PL245867B1 (pl) * 2024-01-17 2024-10-21 Lubelska Polt Laminat metal-szkło-węgiel i sposób jego wytwarzania
PL248601B1 (pl) * 2024-01-17 2026-01-05 Lubelska Polt Laminat metal-węgiel i sposób jego wytwarzania
PL245864B1 (pl) * 2024-01-17 2024-10-21 Lubelska Polt Laminat metal-szkło i sposób jego wytwarzania
PL245865B1 (pl) * 2024-01-17 2024-10-21 Lubelska Polt Laminat metal-szkło i sposób jego wytwarzania
PL245866B1 (pl) * 2024-01-17 2024-10-21 Lubelska Polt Laminat metal-szkło i sposób jego wytwarzania
PL248763B1 (pl) * 2024-01-17 2026-01-26 Lubelska Polt Laminat metal-węgiel-szkło i sposób jego wytwarzania
PL245863B1 (pl) * 2024-01-17 2024-10-21 Lubelska Polt Laminat metal-szkło i sposób jego wytwarzania

Also Published As

Publication number Publication date
PL243177B1 (pl) 2023-07-10

Similar Documents

Publication Publication Date Title
PL441554A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441553A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441552A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
CN113912301B (zh) 可弯折玻璃堆叠组件、制品及其制造方法
PL437402A1 (pl) Laminat tytan-szkło-węgiel i sposób jego wytwarzania
MY158938A (en) Manufacturing method of glass substrate for magnetic disk
PL243177B1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL437396A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441560A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
CN109605859A (zh) 一种蜂窝芯、蜂窝板及蜂窝芯制作方法
PL441558A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441561A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
WO2011142782A3 (en) Zone compensated multilayer laue lens and apparatus and method of fabricating the same
PL441559A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL441555A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
CS214020B1 (en) Laminated glass made body and method of its manufacture
CN210553438U (zh) 一种高冲深成型性能铝塑复合膜
PL451055A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL432777A1 (pl) Sposób wytwarzania laminatu magnez-węgiel
PL451054A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451052A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451051A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451053A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
CN221697239U (zh) 一种抗变形的复合多层板
PL437393A1 (pl) Laminat tytan-węgiel i sposób jego wytwarzania