PL441560A1 - Laminat tytan-szkło i sposób jego wytwarzania - Google Patents

Laminat tytan-szkło i sposób jego wytwarzania

Info

Publication number
PL441560A1
PL441560A1 PL441560A PL44156022A PL441560A1 PL 441560 A1 PL441560 A1 PL 441560A1 PL 441560 A PL441560 A PL 441560A PL 44156022 A PL44156022 A PL 44156022A PL 441560 A1 PL441560 A1 PL 441560A1
Authority
PL
Poland
Prior art keywords
thickness
titanium
layer
weight
glass laminate
Prior art date
Application number
PL441560A
Other languages
English (en)
Other versions
PL243180B1 (pl
Inventor
Monika Ostapiuk
Jarosław Bieniaś
Patryk Jakubczak
Magda Droździel-Jurkiewicz
Piotr Podolak
Original Assignee
Politechnika Lubelska
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Politechnika Lubelska filed Critical Politechnika Lubelska
Priority to PL441560A priority Critical patent/PL243180B1/pl
Publication of PL441560A1 publication Critical patent/PL441560A1/pl
Publication of PL243180B1 publication Critical patent/PL243180B1/pl

Abstract

Przedmiotem zgłoszenia jest laminat tytan-szkło i sposób jego wytwarzania. Laminat tytan-szkło, charakteryzuje się tym, że w części środkowej laminatu znajdują się cztery jednakowe warstwy samonaprawiające się (4) o grubości od 1,5 mm do 2,3 mm każda, składające się z włókien szklanych wypełnionych roztworem dietylenotriaminy składającym się z wody w ilości 10% wagowo i dietylenotriaminy w ilości 90% wagowo i połączonych żywicą epoksydową. Do zewnętrznych powierzchni skrajnych warstw samonaprawiających się (4) przylega adhezyjnie warstwa żywicy polimerowej (3) o grubości od 10 µm do 30 µm, która nałożona jest na warstwę ceramiczną (2) o grubości od 8 µm do 15 µm znajdującą się na arkuszu blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm. Sposób wytwarzania laminatu tytan-szkło, polega na tym, że na dwa arkusze blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm posiadające na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm nakłada się obustronnie warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm, po czym pozostawia się na czas 3 h w temperaturze 23°C. Następnie na jeden z arkuszy blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm posiadający na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm i warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm nakłada się kolejno cztery jednakowe warstwy włókien szklanych wypełnionych wodnym 10% wagowo roztworem dietylenotriaminy 90% wagowo o grubości od 0,25 mm do 1 mm każda.
PL441560A 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania PL243180B1 (pl)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PL441560A PL243180B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PL441560A PL243180B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Publications (2)

Publication Number Publication Date
PL441560A1 true PL441560A1 (pl) 2023-01-02
PL243180B1 PL243180B1 (pl) 2023-07-10

Family

ID=84786784

Family Applications (1)

Application Number Title Priority Date Filing Date
PL441560A PL243180B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Country Status (1)

Country Link
PL (1) PL243180B1 (pl)

Also Published As

Publication number Publication date
PL243180B1 (pl) 2023-07-10

Similar Documents

Publication Publication Date Title
PL441557A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441554A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441553A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441552A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
CN113943111B (zh) 可弯折玻璃堆叠组件、制品及其制造方法
JP6392363B2 (ja) イオン交換プロセスおよびそれにより得られる化学強化されたガラス基材
ATE532760T1 (de) Wabenstruktur und zugehöriges herstellungsverfahren
CN110446691A (zh) 具有工程应力分布的经涂覆的基于玻璃的制品及制造方法
PL441561A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
CN109605859A (zh) 一种蜂窝芯、蜂窝板及蜂窝芯制作方法
PL441558A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441559A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL441555A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL451055A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451054A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL437394A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL432777A1 (pl) Sposób wytwarzania laminatu magnez-węgiel
PL451052A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451051A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL437393A1 (pl) Laminat tytan-węgiel i sposób jego wytwarzania
PL451053A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL243180B1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL437397A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
TWI675747B (zh) 複合板材之疊層結構與其製造方法
TW202537816A (zh) 積層體、壓印用基板、複製模及其製造方法、以及壓印裝置