PL441559A1 - Laminat tytan-szkło i sposób jego wytwarzania - Google Patents

Laminat tytan-szkło i sposób jego wytwarzania

Info

Publication number
PL441559A1
PL441559A1 PL441559A PL44155922A PL441559A1 PL 441559 A1 PL441559 A1 PL 441559A1 PL 441559 A PL441559 A PL 441559A PL 44155922 A PL44155922 A PL 44155922A PL 441559 A1 PL441559 A1 PL 441559A1
Authority
PL
Poland
Prior art keywords
thickness
titanium
layer
glass fibers
glass laminate
Prior art date
Application number
PL441559A
Other languages
English (en)
Other versions
PL243179B1 (pl
Inventor
Monika Ostapiuk
Jarosław Bieniaś
Patryk Jakubczak
Magda Droździel-Jurkiewicz
Piotr Podolak
Original Assignee
Politechnika Lubelska
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Politechnika Lubelska filed Critical Politechnika Lubelska
Priority to PL441559A priority Critical patent/PL243179B1/pl
Publication of PL441559A1 publication Critical patent/PL441559A1/pl
Publication of PL243179B1 publication Critical patent/PL243179B1/pl

Abstract

Przedmiotem zgłoszenia jest laminat tytan-szkło i sposób jego wytwarzania. Laminat tytan-szkło, charakteryzuje się tym, że w części środkowej laminatu znajdują się cztery jednakowe warstwy samonaprawiające się (4) o grubości od 1,5 mm do 2,3 mm każda, składające się z włókien szklanych wypełnionych diizocyjanianem izoforonu i połączonych żywicą epoksydową. Do zewnętrznych powierzchni skrajnych warstw samonaprawiających się (4) przylega adhezyjnie warstwa żywicy polimerowej (3) o grubości od 10 µm do 30 µm, która nałożona jest na warstwę ceramiczną (2) o grubości od 8 µm do 15 µm znajdującą się na arkuszu blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm. Sposób wytwarzania laminatu tytan-szkło, polega na tym, że na dwa arkusze blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm posiadające na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm nakłada się obustronnie warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm, po czym pozostawia się na czas 3 h w temperaturze 23°C. Następnie na jeden z arkuszy blachy (1) ze stopu tytanu o grubości od 0,3 mm do 0,5 mm posiadający na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm i warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm nakłada się kolejno cztery jednakowe warstwy włókien szklanych wypełnionych diizocyjanianem izoforonu o grubości od 0,25 mm do 1 mm każda. Każdą warstwę włókien szklanych laminuje się ręcznie żywicą epoksydową i otrzymuje się cztery jednakowe warstwy samonaprawiające się (4) o grubości od 1,5 mm do 2,3 mm każda, składające się z włókien szklanych wypełnionych diizocyjanianem izoforonu i połączonych żywicą epoksydową.
PL441559A 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania PL243179B1 (pl)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PL441559A PL243179B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PL441559A PL243179B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Publications (2)

Publication Number Publication Date
PL441559A1 true PL441559A1 (pl) 2023-01-02
PL243179B1 PL243179B1 (pl) 2023-07-10

Family

ID=84786796

Family Applications (1)

Application Number Title Priority Date Filing Date
PL441559A PL243179B1 (pl) 2022-06-27 2022-06-27 Laminat tytan-szkło i sposób jego wytwarzania

Country Status (1)

Country Link
PL (1) PL243179B1 (pl)

Also Published As

Publication number Publication date
PL243179B1 (pl) 2023-07-10

Similar Documents

Publication Publication Date Title
PL441557A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441554A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441552A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL441553A1 (pl) Laminat aluminium-szkło i sposób jego wytwarzania
PL437396A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
KR101445213B1 (ko) 마그네슘합금 허니콤 패널 및 그 생산 공정
PL447525A1 (pl) Laminat metal-szkło i sposób jego wytwarzania
PL447530A1 (pl) Laminat metal-węgiel i sposób jego wytwarzania
PL441555A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441561A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL441558A1 (pl) Laminat magnez-szkło i sposób jego wytwarzania
PL441560A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL451051A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451053A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451055A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL451052A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL437394A1 (pl) Laminat tytan-szkło i sposób jego wytwarzania
PL437395A1 (pl) Laminat magnez-szkło-węgiel i sposób jego wytwarzania
PL432777A1 (pl) Sposób wytwarzania laminatu magnez-węgiel
PL437393A1 (pl) Laminat tytan-węgiel i sposób jego wytwarzania
JP2021019055A (ja) セラミック電子部品および積層セラミックコンデンサの製造方法
PL451054A1 (pl) Laminat samonaprawiający się i sposób jego wytwarzania
PL437392A1 (pl) Laminat magnez-węgiel i sposób jego wytwarzania
PL447522A1 (pl) Laminat metal-szkło i sposób jego wytwarzania
TWI675747B (zh) 複合板材之疊層結構與其製造方法