WO2005018902A1 - 中空成形品、中空成形品の製造方法および中空成形用金型 - Google Patents

中空成形品、中空成形品の製造方法および中空成形用金型 Download PDF

Info

Publication number
WO2005018902A1
WO2005018902A1 PCT/JP2004/011554 JP2004011554W WO2005018902A1 WO 2005018902 A1 WO2005018902 A1 WO 2005018902A1 JP 2004011554 W JP2004011554 W JP 2004011554W WO 2005018902 A1 WO2005018902 A1 WO 2005018902A1
Authority
WO
WIPO (PCT)
Prior art keywords
hollow
fluid
molded product
hollow molded
molded article
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2004/011554
Other languages
English (en)
French (fr)
Inventor
Yasuhiro Suzuki
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzuka Fuji Xerox Manufacturing Co Ltd
Original Assignee
Suzuka Fuji Xerox Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzuka Fuji Xerox Manufacturing Co Ltd filed Critical Suzuka Fuji Xerox Manufacturing Co Ltd
Publication of WO2005018902A1 publication Critical patent/WO2005018902A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

【課題】　溶融樹脂にガスを注入して製造する中空成形品には、一般にガスの流路としてリブが設けられている。しかし、このリブは、中空成形品の表面にヒケ、転写斑、中空部が形成される時の白化等の外観を悪化させるという問題点を有する。 【解決手段】　流体注入部から加圧流体を注入することにより内部に中空部を形成する中空成形品において、流体注入部から中空部に至る流体流路に対応する表面又は裏面の一部にシボ模様を形成することにより、シボ模様にガスチャンネルとしての機能を持たせた。

Description

明 細 書
中空成形品、中空成形品の製造方法および中空成形用金型
技術分野
[0001] 本発明は、金型キヤビティ内に射出された溶融樹脂中に加圧流体を注入 (圧入）す る中空成形法で成形され、表面にシボ模様を有する中空成形品、その製造方法、お よび中空成形品を製造するための中空成形用金型に関するものである。
背景技術
[0002] 中空成形法の 1つであるガスアシスト成形は、引け、反りのない中空成形品を製造 できることが知られている（例えば、特許文献 1参照）。
このガスアシスト成形では、成形品内に加圧流体を注入するための通路（以下、「ガ スチャンネル」と称す）として、成形品への流体注入部から、成形品を規定する基体 に、基体を規定する肉厚より幅、高さの大きなリブを形成するのが一般的である（例え ば、特許文献 2参照)。
[0003] しかし、このリブは、流体注入部から中空部が形成される領域 (以下、「中空部形成 領域」と称す）に至る成形品に若干のヒケゃ転写斑、中空部が形成される時の白化 等の外観を悪化させるという問題点がある。
また、機能上リブを設けることが困難な製品も多い。
[0004] そこで、リブを無くし、成形品の流体注入部から中空部形成領域までの外観を向上 させるため、流体注入部から中空部形成領域へと伸びる中空成形用金型のキヤビテ ィ面の所定領域に、断熱材を設けた中空成形用金型が提案されている (例えば、特 許文献 3参照)。
[0005] この中空成形用金型は、従来リブを形成していた位置に対応する金型キヤビティ位 置に断熱材を設けることにより、他の領域に充填された溶融樹脂よりも冷却を遅延さ せ、この冷却を遅延させた領域内に加圧流体を圧入してガスチャンネルを形成する というものである。
特許文献 1：特公昭 48 - 41264号公報
特許文献 2：特開平 6— 278155号公報 特許文献 3 :特開平 7— 52183号公報
発明の開示
発明が解決しょうとする課題
[0006] しかし、この断熱材は、金型材料よりも熱伝導率が低いものでなければならないの で、金型材料とは異なる材料を金型キヤビティ内に設けなければならないとレ、う問題 力 sある。
つまり、高温 低温の温度サイクルを繰り返し、かつ高圧 低圧（大気圧）の圧力サ イタルを繰り返す過酷な環境の金型キヤビティ内に、金型材料とは異なる材料の断熱 材を設けることは、断熱材の剥がれ、劣化等により金型のメンテナンス頻度を高め、 中空成形品の生産コストを高めるという問題がある。
[0007] 本発明は、このような従来の問題点に鑑みてなされたものであり、リブを設けず美観 を向上させ、かつ、金型キヤビティに金型材料とは異なる材料を設けず安価に、流体 注入部から中空部形成領域に至るガスチャンネルを形成し、確実に加圧流体を導く ことができるようにすることを目的とする。
課題を解決するための手段
[0008] 請求項 1に記載の中空成形品は、流体注入部から加圧流体を注入することにより 内部に中空部が形成され、表面及び/又は裏面の少なくとも一部にシボ模様が形成 された中空成形品において、流体注入部から中空部に至る流体流路に対応する表 面及び/又は裏面にシボ模様が線状に形成されていることにより、リブが無ぐ所望 の位置に加圧流体の流体流路を形成した外観および美観を高めた中空成形品とす ること力 sできるものである。
[0009] 請求項 2に記載の中空成形品は、流体流路を表面及び Z又は裏面に投影した形 状が、表面及び Z又は裏面に形成されたシボ模様が形成する形状と略同じであるこ とにより、リブが無ぐ所望の位置に加圧流体の流体流路を形成した外観および美観 を高めた中空成形品とすることができるものである。
[0010] 請求項 3に記載の中空成形品は、表面及び Z又は裏面に線状に形成されたシボ 模様を複数本とすることにより、中空部形成領域に十分な加圧流体を供給することが できるものである。 [0011] 請求項 4に記載の中空成形品は、流体注入部を複数にすることにより、中空部形成 領域に十分な加圧流体を供給することができるものである。
[0012] 請求項 5に記載の中空成形品の製造方法は、表面及び/又は裏面の少なくとも一 部にシボ模様が形成され、流体注入部から加圧流体を注入することにより内部に中 空部が形成された中空成形品の製造方法において、前記流体注入部の近傍からシ ボ模様を表面及び Z又は裏面に線状に形成し、流体注入部から加圧流体を注入す ることにより、線状に形成したシボ模様に沿って加圧流体を導き、所望の位置に中空 部を形成することにより、リブが無ぐ所望の位置に加圧流体の流体流路を形成した 外観および美観を高めた中空成形品を製造することができるものである。
[0013] 請求項 6に記載の中空成形品の製造方法は、表面及び/又は裏面に線状に形成 されたシボ模様を複数本とすることにより、中空部形成領域に十分な加圧流体を供 給すること力 Sできるものである。
[0014] 請求項 7に記載の中空成形品の製造方法は、流体注入部を複数とすることにより、 中空部形成領域に十分な加圧流体を供給することができるものである。
[0015] 請求項 8に記載の中空成形用金型は、金型キヤビティへの加圧流体の注入位置と 、この注入位置から加圧流体を導いて中空部を形成する中空部形成領域との間に 流体流路形成領域が設けられた中空成形用金型において、流体流路形成領域の金 型キヤビティ面に、注入位置から中空部形成領域へと伸びる所定領域までの間に成 形品にシボ模様を形成する処理が施されていることにより、リブが無ぐ所望の位置に 加圧流体の流体流路を形成した外観および美観を高めた中空成形品を製造するこ とができるものである。
発明の効果
[0016] 成形品にシボ模様を付することにより、リブによるガスチャンネルと同様な効果を得 ることができるため、材料費を低減し、美観が向上した中空成形品とその製造方法を 提供すること力 Sできる。
また、金型キヤビティ面に、成形品の一部または全部にシボ模様を形成する処理を 施すことにより、上記した中空成形品を容易に成形することができる中空成形金型を 提供すること力 Sできる。 発明を実施するための最良の形態
[0017] 〔シボ模様〕
本発明における、シボ模様とは、成形品の表面及び Z又は裏面に表れた細かい凹 凸により形成された模様をいう。例えば、梨地シボ、ゴマシボ、中皮シボ、小皮シボ、 皮シボ、木皮シボ、布目シボ、矢ガスリシボ、エジプトシボ、大エジプトシボ、石垣シボ 等が挙げられる。
〔シボ模様の作用〕
[0018] これらのシボ模様を成形品に形成するために、金型キヤビティ面に処理を施した場 合の作用について説明する。
シボの大きさにも左右される力 深さ 30 / m程度の梨地シボ（例えば、棚沢八光社 のシボパターン見本 TH—112— TH—121)を金型キヤビティ面に施すと、金型キヤビ ティ内の溶融樹脂の流動性を良くすることができる。
[0019] その理由は、シボ模様が施された金型キヤビティ面を溶融樹脂が流れると、シボ模 様を構成する凹凸と溶融樹脂との間に、複数の細かな気泡ができ、この気泡によって 断熱層（熱境膜と類似するもの）が形成されるからである。
この気泡は、図 1に示すように、シボ模様 1の凹部 (谷部） 2に存在する空気 3が溶融 樹脂 4の流動によって押し出されることなぐ溶融樹脂 4と金型 5との間に入る (残る）こ とにより形成される。
[0020] また、前記した梨地シボ等のシボ模様を、成形品の表面及び/又は裏面の少なく とも一部に形成することで、金型キヤビティ内の溶融樹脂の流動性を向上させること ができるため、溶融樹脂の冷却遅延によって中実成形時の保圧効果、ガスアシスト 成形時のガス保圧効果等を向上させることができる。
[0021] ここで、表面又は裏面にシボ模様を施すに際し、成形品が金型から離型する場合 の障害とならない箇所を選択する。離型の障害となりそうな箇所を選択せざるを得な い場合は、シボ模様に変えて、同様な断熱の作用効果を持つ熱伝導率の低い表面 処理 (ペインティング、コーティング）又は鍍金（プレーティング）を金型キヤビティ面に 採用することができる。例えば、 CVD、 PVDを用いた DLC、 TiN、 CrN、 A1N等のセ ラミックコート、弗素樹脂をサスペンジョンとした鍍金、シリコン樹脂、弗素樹脂を主成 分とした塗装等があげられる。
〔熱可塑性樹脂〕
[0022] 本発明において、中空成形品の材料として使用する熱可塑性樹脂としては、一般 的に成形に用いられてレ、る熱可塑性樹脂であれば種類を問わなレ、。
熱可塑性樹脂を例示すれば、スチレン系単量体を重合せしめて成るポリスチレン系 樹脂、例えばポリスチレン (PS)、耐衝撃性ポリスチレン（HIPS、 HiPS)、二トリル系 単量体、スチレン系単量体との共重合体であるスチレン系樹脂、例えば、アタリロニト リル .スチレン共重合体（AS)、二トリル系単量体 'スチレン系単量体 .ブタジエン系ゴ ムから成る樹脂、例えば、アクリロニトリル 'ブタジエン 'スチレン共重合体 (ABS、 Ab S)等のスチレン系樹脂、ポリエチレン（PE)、ポリプロピレン（PP)等に代表されるポリ ォレフィン系樹脂、ポリフエ二レンエーテル（PPE)、ポリカーボネート（PC)、ポリアミド (PA)、ポリスルフォン（PSF)、ポリエーテルイミド（PEI)、ポリメチルメタタリレート（P MMA)等のエンジニアリングプラスチック、ポリエチレンテレフタレート（PET)、ポリブ チレンテレフタレート（PBT)等のポリエステル樹脂、塩化ビエル（PVC)等のビニル 系樹脂等、或いは前記熱可塑性樹脂の二種以上の混合物である。
〔成形加工法〕
[0023] 本発明で使用される中空成形法は、旭化成工業の AGI、 GPI、 CGM、 H2M、出光 石油化学の GIM、新日鉄化学の PFP、英国のシンプレス、米国の GAIN Technol ogy、独国のエアーモールド、コンツールなどに代表されるガスアシスト成形法（中空 射出成形法）、及び米国の UCC法、 USM法、或いは、東芝機械と旭ダウとが開発し た TAF法、 EX— CELL—〇社法、へッティンガーの発泡成形や、 New— SF、 GCP法 、ァライドケミカル社の技法等、更に超臨界状態の気態（体)を用いた米国 トレクセ ル社の MuCell (ミューセル）や旭化成工業の AMOTECに代表される発泡成形法（ 発泡射出成形法）と前記ガスアシスト成形法と融合された方法、更には住友化学の S Pモーノレド、インモールド成形法との前記ガスアシスト成形法とを融合させた方法にも 適用される。
[0024] それ以外には、発泡射出成形、或いは従来から実施されている中実 (ソリッド)成形 への適用も可能で、溶融樹脂の流動面にシボ加工を施す事で溶融樹脂の流動性を 向上させることができる。
実施例 1
[0025] 図 2に示した上型 40と下型 41で形成されるキヤビティ 42に、溶融状態の成形用樹 脂を、樹脂注入部 43から射出し、ガスアシスト成形法により、図 3に示す中空成形品 20を得た。成形用樹脂として、東レ製の透明 ABS (トヨラック 920) (商品名）を使用し た。
[0026] 加圧流体としての窒素ガスの注入位置であるガス注入ピン 44及び 45 (流体注入部 22及び 23)から、成形品 20の中空部 24を形成する中空部形成領域 47に至る流体 流路形成領域 48における金型キヤビティ面には、成形品の表面にシボ模様を形成 する処理 46が施されてレ、る。
[0027] 本実施例においては、上型 40の金型キヤビティ面の一部に、中空成形品 20の表 面に 15mmの幅で線状の梨地シボ 21 (TH-115)を形成する加工が施されているた め、梨地シボ 21が形成された部分に沿って、流体流路 25が約 12— 16mmの幅で形 成されることを確認できた。つまり、成形品に形成された流体流路を、成形品の表面 に投影した形状が、成形品の表面に形成した梨地シボと略同じであつた。
[0028] 以上より、線状にシボ模様を施すことにより、シボ模様を施した部分の溶融樹脂の 冷却が遅くなり、シボ模様に沿って窒素ガスの流路が形成されることが確認できた。 実施例 2
[0029] 成形用樹脂としてトヨラック 920 (商品名）を金型キヤビティに射出し、ガスアシスト成 形により、図 4に示す中空成形品 30を得た。該中空成形品 30は、表面に 15mmの 幅で線状の梨地シボ 31 (TH-115)が施されており、流体注入部 32に図示しないガ ス注入ピンを設置し、窒素ガスを注入した。
その結果、線状に梨地シボ 31を施した部分に沿って、中空部が約 16— 20mmの 幅で形成されることを確認できた。すなわち、成形品にリブ等のガスチャンネルが設 けられていない場合でも、成形品にシボ模様を付することにより、リブによるガスチヤ ンネルと同様な、窒素ガスを導くという効果が得られることを確認できた。
実施例 3
[0030] トヨラック 920 (商品名）を成形材料として、金型キヤビティに射出し、図 5に示すよう に、ガスアシスト成形により、表面の半分に梨地シボ 12 (TH— 115)を施した板厚 3m mの中空成形品 10を得た。この中空成形品 10の裏面には、根元の厚さはリブが立 つている面（天肉）の 60%で、高さ 5mm、長さ 350mmのリブ 13が形成されている。 また、加圧流体としての窒素ガスは、流体注入部 14から注入した。
[0031] リブ 13付近での中空部 15が形成されている状態を確認した結果、シボ模様 12の ある部分では、中空部 15の幅が 18 30mmの広がりがあるのに対し、シボ模様 12 のない部分では、中空部 15の幅が 5— 8mmと極端に狭くなるのが確認された。窒素 ガスを、流体注入部 11から注入した場合も、同様な結果を得ることができた。
実施例 4
[0032] トヨラック 920 (商品名）を成形材料として、金型キヤビティに射出し、図 6に示すよう に、ガスアシスト成形により、表面の略半分に幅 15mmの線状の梨地シボ 51 (TH—1 15)を施し、表面の略半分に幅が 1. 5mmで高さが 5mmのリブ 54を設けた板厚 3m mの中空成形品 50を得た。加圧流体としての窒素ガスは、流体注入部 52から注入し た。
[0033] 窒素ガスは線状に形成されたシボ 51に沿って進み、かつリブ 54に到達後は、リブ 5 4に沿って進む。このため、中空部 53は、シボ 51およびリブ 54に沿って形成される。 この中空部 53の状態を確認した結果、シボ模様 51のある部分では、中空部 53の幅 力 S15 18mmの広がりがあるのに対し、リブ 54のある部分では、中空部 53の幅が 5 一 9mmと狭くなるのが確認された。
窒素ガスを、リブ 54の端部から注入した場合も、同様な結果を得ることができた。
[0034] 以上より、シボ模様は、溶融樹脂の温度を低下させにくいので、加圧流体の注入を 容易にするという作用効果があるといえる。
[0035] 前記した実施例は、説明のために例示したものであって、本発明としてはそれらに 限定されるものではなぐ特許請求の範囲、発明の詳細な説明および図面の記載か ら当業者が認識することができる本発明の技術的思想に反しない限り、変更および 付加が可能である。
[0036] 例えば、前記した実施例においては、シボ模様として直線状のものを示した力 こ れに限られず、線状のものであれば、曲線状のものでも良い。 産業上の利用可能性
[0037] 成形品にリブによるガスチャンネルが設けられていない場合でも、成形品にシボ模 様を付することにより、リブと同様な結果を得ることができるため、美観を向上させた中 空成形品に適用することができる。
図面の簡単な説明
[0038] [図 1]シボ模様の作用効果の説明図である。
[図 2]中空成形用金型を示した断面図である。 （実施例 1)
[図 3]中空成形品を示した斜視図である。 （実施例 1)
[図 4]中空成形品を示した斜視図である。 （実施例 2)
[図 5]中空成形品を示した斜視図である。 （実施例 3)
[図 6]中空成形品を示した斜視図である。 （実施例 4)
符号の説明
[0039] 20 中空成形品
21 シボ模様
22 流体注入部
23 流体注入部
24 中空部
25 流体流路
26 表面

Claims

請求の範囲
[1] 流体注入部から加圧流体を注入することにより内部に中空部が形成され、表面及 び/又は裏面の少なくとも一部にシボ模様が形成された中空成形品において、 前記流体注入部から前記中空部に至る流体流路に対応する前記表面及び Z又は 前記裏面に前記シボ模様が線状に形成されていることを特徴とする中空成形品
[2] 前記流体流路を前記表面及び/又は前記裏面に投影した形状が、前記表面及び
/又は前記裏面に形成されたシボ模様が形成する形状と略同じであることを特徴と する請求項 1に記載の中空成形品
[3] 前記表面及び/又は前記裏面に線状に形成された前記シボ模様が、複数本ある ことを特徴とする請求項 1又は請求項 2に記載の中空成形品
[4] 前記流体注入部が複数あることを特徴とする請求項 1、請求項 2又は請求項 3に記 載の中空成形品
[5] 表面及び/又は裏面の少なくとも一部にシボ模様が形成され、流体注入部から加 圧流体を注入することにより内部に中空部が形成された中空成形品の製造方法にお いて、
前記流体注入部の近傍からシボ模様を表面及び/又は裏面に線状に形成し、 前記流体注入部から加圧流体を注入することにより、前記線状に形成したシボ模 様に沿って加圧流体を導き、
所望の位置に中空部を形成することを特徴とする中空成形品の製造方法
[6] 前記表面及び/又は前記裏面に線状に形成された前記シボ模様が、複数本ある ことを特徴とする請求項 5に記載の中空成形品の製造方法
[7] 前記流体注入部が複数あることを特徴とする請求項 5又は請求項 6に記載の中空 成形品の製造方法
[8] 金型キヤビティへの加圧流体の注入位置と、該注入位置から前記加圧流体を導い て中空部を形成する中空部形成領域との間に流体流路形成領域が設けられた中空 成形用金型において、
流体流路形成領域の金型キヤビティ面に、前記注入位置から前記中空部形成領 域へと伸びる所定領域までの間にシボ模様を形成する処理が施されていることを特 徴とする中空成形用金型
PCT/JP2004/011554 2003-08-22 2004-08-11 中空成形品、中空成形品の製造方法および中空成形用金型 Ceased WO2005018902A1 (ja)