WO2010143777A1 - 저융점사를 포함하는 원단 - Google Patents

저융점사를 포함하는 원단 Download PDF

Info

Publication number
WO2010143777A1
WO2010143777A1 PCT/KR2009/004354 KR2009004354W WO2010143777A1 WO 2010143777 A1 WO2010143777 A1 WO 2010143777A1 KR 2009004354 W KR2009004354 W KR 2009004354W WO 2010143777 A1 WO2010143777 A1 WO 2010143777A1
Authority
WO
WIPO (PCT)
Prior art keywords
melting point
fabric
low melting
yarn
point yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2009/004354
Other languages
English (en)
French (fr)
Inventor
장후성
김성군
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Chemical Korea Inc
Original Assignee
Woongjin Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Woongjin Chemical Co Ltd filed Critical Woongjin Chemical Co Ltd
Publication of WO2010143777A1 publication Critical patent/WO2010143777A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 일반사와 저융점사를 포함하는 원단에 있어서, 상기 저융점사가 경사 및 위사 또는, 경사 또는 위사에 포함되거나; 상기 일반사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함되되, 상기 저융점사의 융착율이 30 내지 100%인 저융점사를 포함하는 원단으로 상기 범위의 융착율을 갖는 원단의 경우 실미끄러짐 정도가 0.1 내지 2.5mm인 저융점사를 포함하는 원단을 제공한다.

Description

저융점사를 포함하는 원단
본 발명은 저융점사가 포함된 원단에 관한 것으로서, 특히 저융점사의 융착율을 제어하여 형태안정성과 환경안정성이 동시에 만족될 수 있는 원단에 관한 것이다.
최근 원단은 의류용 뿐만 아니라 산업용, 생활용품용으로 그 용도를 확장하고 있다. 그 중 생활소재로서 원단이 스크린용으로 사용되고 있는데, 스크린(screen)은 일반적으로 창가리개용이나 프로젝터의 스크린으로 활용되고 이 중 창가리개용 스크린은 가정, 호텔, 레스토랑 기타 건물 등에서 내부의 사생활 보호 및 태양광 차단을 위해서 사용되고 있는 것을 지칭하는 것으로, 일정 폭의 원단을 제단하고, 롤로 감아서 창문에 고정시켜 사용자가 롤을 풀어서 창문을 가리거나 롤을 감아서 시야를 확보할 수 있도록 만든 제품이다. 이 제품은 롤, 판넬의 형태로 원단을 절단하여 롤 스크린(Roll Screen), 판넬 스크린(Panel Screen),버티칼 등의 명칭으로 불리고 있다.
상기 스크린 원단은 장폭으로 사용되는 관계로 경직성을 부여해야 한다. 이를 위하여 종래 스크린 원단의 표면을 폴리우레탄계 수지를 이용하여 코팅하여 원단 특유의 유연성을 확보하면서 경직성을 부여하여 왔다.
그러나 상기와 같은 방법은 공정상 코팅공정이 추가되어야 하고, 스크린 원단은 댁내에서 설치되고 사용되는 특성상 코팅물질이 VOC로 취급되어 실내환경오염의 문제를 야기하고 있다.
본 발명자들은 한편 폴리에스테르 섬유에 주목하는데 이는 상기 섬유의 물성이 강도가 높고, 내약품성이 있으며, 250 내지 255 ℃ 범위의 융점을 지녀 내열성이 우수하며, 신장 굴곡에 대하여는 탄성을 지니는 장점이 있어서 신사복지, 셔츠 등의 의류뿐만 아니라 산업용 재료로 용도가 다양하다는 점에 주목하였다.
그러나, 상기의 폴리에스테르는 비교적 융점이 높아 일반적으로 섬유 구조체를 경화시킬 때는 포르말린(포름알데히드 수용액)이라든가 유기용제를 함유한 접착제, 경질 수지(페놀 수지, 멜라닌 수지, 우레아 수지)를 사용한다. 이러한 유기 용제를 함유한 접착제는 원단의 내부까지 침투하지 않아 접착성도 낮고 완성되었을 때의 촉감이 거칠다. 또한, 휘발성이 강하고 인체에 유해한 물질이 대부분이며, 유독 가스 배출 등의 환경적으로 문제가 되어 왔다.
한편 이러한 문제점을 개선하기 위하여 저융점사를 포함시켜 제직된 원단을 열처리하여 상기 저융점사를 원단에 융착시킴으로서 코팅공정을 생략할 수 있는 기술이 제안되었다. 이러한 방식은 종래 코팅방식의 문제점을 개선할 수 있는 장점이 있기는 하나, 융착율에 따른 물성제어가 검토되지 못하여 다양한 제품군을 형성하지 못하고 필요한 용도에 따른 물성을 보유하지 못하는 문제점이 있다.
상기와 같은 문제점을 해결하기 위하여 본 발명의 목적은 휘발성 물질이 방출되지 않는 안정성이 높은 원단을 제공함에 있다.
또한 본 발명은 융착율에 따른 물성제어가 가능한 원단을 제공함에 있다.
또한 본 발명은 원단으로서의 유연성과 스크린용으로서의 경직성을 동시에 만족할 수 있는 원단을 제공함에 있다.
또한 본 발명은 원단이 유연성과 경직성을 동시에 만족할 수 있는 적절한 물성을 제공함에 있다.
상기와 같은 목적을 달성하기 위하여 본 발명은 일반사와 저융점사를 포함하는 원단에 있어서, 상기 저융점사가 경사 및 위사 또는, 경사 또는 위사에 포함되거나; 상기 일반사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함되되, 상기 저융점사의 융착율이 30 내지 100%인 저융점사를 포함하는 원단을 제공한다.
또한, 상기 범위의 융착율을 갖는 원단의 경우 실미끄러짐도가 0.1 내지 2.5mm인 저융점사를 포함하는 원단을 제공한다.
또한, 상기 원단의 올풀림강도(1올 기준)가 0.2 내지 3.5Kg인 저융점사를 포함하는 원단을 제공한다.
또한, 상기 원단의 올풀림강도(5mm 기준)가 10 내지 35Kg인 저융점사를 포함하는 원단을 제공한다.
또한, 상기 원단의 굽힘길이는 3 내지 10cm인 저융점사를 포함하는 원단을 제공한다.
또한, 상기 일반사와 저융점사는 50 : 50 내지 75 : 15 중량비로 이루어진 저융점사를 포함하는 원단을 제공한다.
또한, 상기 원단에는 난연사가 더 포함된 저융점사를 포함하는 원단을 제공한다.
또한, 상기 저융점사는 복합섬유로서, 시스부에는 저융점 폴리에스테르계 수지가, 코어부에는 난연성 폴리에스테르계 수지가 포함된 저융점사를 포함하는 원단을 제공한다.
또한, 본 발명은 난연사와 저융점사를 포함하는 원단에 있어서, 상기 저융점사가 경사 및 위사 또는, 경사 또는 위사에 포함되거나; 상기 난연사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함되되, 상기 저융점사의 융착율이 30 내지 100%인 저융점사를 포함하는 원단을 제공한다.
상술한 바와 같이 본 발명의 실시예에 따른 원단은 별도의 코팅공정을 채택하지 않으므로서 휘발성 물질이 방출되지 않아 친환경적인 산업용 자재로서의 효과가 있다.
또한 본 발명의 실시예에 의한 원단은 원단으로서의 유연성과 스크린용으로서의 경직성을 동시에 만족할 수 있는 물성을 제공하여 용도별도 적절한 물성치를 갖는 특징이 있다.
또한 본 발명의 실시예에 의한 원단은 용도에 따라 융착율을 변화시켜 적절한 물성을 갖도록 할 수 있는 장점이 있다.
도 1 및 도 2는 본 발명의 바람직한 일실시예에 의한 원단의 올풀림강도 1올 기준 및 5mm 기준을 측정하는 원리를 나타낸 개념도.
도 2는 본 발명의 바람직한 다른 실시예에 의한 재생 폴리에스테르의 제조공정도.
도 3 및 4는 본 발명의 실시예에 의한 원단의 단면 SEM 사진.
도 5는 비교예에 의한 원단의 단면 SEM 사진.
이하 본 발명에 첨부된 도면을 참조하여 본 발명의 바람직한 일실시예를 상세히 설명하기로 한다. 우선, 도면들중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.
본 명세서에서 사용되는 정도의 용어 "약", "실질적으로" 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
본 명세서서에서 "원단"이라 함은 직물, 편성물, 펠트, 프레이트, 부직포, 접착직물, 몰드직물, 웹(web) 모두를 의미하는 용어로 사용된다.
본 발명에 의한 원단은 일반사와 저융점사가 혼합되어 형성될 수 있다. 우선 일반사는 제한없이 사용될 수 있으며 저융점사는 시스-코어형 또는 분할형 복합섬유가 비제한적인 예로서 사용될 수 있다. 상기 저융점사는 저융점사만으로 경사 및/또는 위사에 사용될 수 있고, 상기 저융점사와 일반사가 혼방 및/또는 합사된 사를 사용할 수 있다.
또한 상기 저융점사는 비제한적인 예로서 시스부에는 저융점 폴리에스테르계 수지가, 코어부에는 난연성 폴리에스테르계 수지가 포함된 난연성 저융점 폴리에스테르계 필라멘트일 수 있다. 이 경우 상기 폴리에스테르계 수지는 폴리에틸렌테레프탈레이트 및 폴리부틸렌테레프탈레이트 수지로 이루어진 군에서 1 이상 선택된 것일 수 있으며, 상기 저융점 폴리에스테르계 수지는 이소프탈산 성분, 테레프탈산 성분, 에틸렌글리콜 성분 및 디에틸렌글리콜 성분이 포함된 것일 수 있다.
또한 상기 폴리에스테르계 수지는 융점이 220 ℃ 내지 260 ℃일 수 있으며, 상기 저융점 폴리에스테르계 수지의 융점은 110 내지 200 ℃ 일 수 있다. 상기 범위 미만인 경우 폴리에스테르 자체의 형태안정성에 문제가 있고 상기 범위를 초과하는 경우 코어부의 수지에도 영향을 미칠 수 있다. 상기 시스부 대 코어부의 비는 10:90 내지 30:70 중량%임이 바람직한데 상기 시스부가 10 중량% 미만인 경우에는 열접착성능의 저하를 초래하며, 시스부가 30 중량%를 초과하면 심부의 함량이 너무 줄어들게 되어 폴리에스테르의 섬유 특성이 현저히 저하되고, 난연 특성 발휘가 어렵게 된다.
상기 난연성 폴리에스테르계 수지는 인계 난연제와 공중합되어 있기 것이 바람직하며, 더욱 바람직하게는 하기 화학식 1로 표시된 인계 난연제일 수 있다. 이 경우 상기 인계 난연제는 폴리에스테르계 수지 내에 인 원자(P)가 5,000 ppm 내지 10,000 ppm 포함됨이 바람직하다. 상기 인의 함량이 5,000 ppm 미만 되도록 첨가 시에는 난연 효과가 미미하고, 10,000 ppm 초과되면 폴리에스테르계 수지의 용융점도가 저하되어, 방사 시 작업성 및 물성이 저하되는 문제가 있다.
화학식 1
Figure PCTKR2009004354-appb-C000001
단, R1 및 R2는 탄소(C)수 1 내지 18 개의 알킬기, 아릴기, 모노히드록시 알킬기 또는 수소 원자이며, R3는 탄소수 1 내지 18 개의 알킬기, 아릴기이다. 또한, n은 1 내지 4 인 정수.
상기 원단을 형성할 원사가 준비되면, 미리 결정된 원단의 설계에 따라 제직 또는 제편될 수 있다. 상기 원단을 형성함에 있어서, 일반사와 저융점사는 50 : 50 내지 75 : 15 중량비로 원단에 포함될 수 있다. 한편 저융점사가 일반사와 혼방 내지 합사되어 상기 일반사와 함께 제직 또는 제편되는 경우 상기 혼방 내지 합사되는 일반사와 저융점사의 비율은 70 : 30 내지 0 :100 중량비로 포함될 수 있다. 상기 일반사와 저융점사가 0 : 100 중량비인 경우 혼방 내지 합사가 아닌 저융점사 단독으로 사용되는 것을 의미한다.
상기 제직 또는 제편을 통해 형성된 원단은 경직성으로 부여하여 위해 저융점사를 융착시키는 공정을 거치게 된다. 이 때 저융점사가 섬유간에 융착되어 원단에 경직성 내지 형태안정성을 부여하는 정도(융착율)는 직조된 원단의 단면을 수직(저융점사가 위사로 제공된 경우에는 위사방향)으로 절개하고, 이를 고정시킨 후 전자 현미경을 이용하고, 200배 배율로 직물의 단면군을 관찰하여 이 중 무작위로 200개를 추출하고 이 범위내에서 섬유간에 융착하고 있는 수를 카운팅함으로서 융착하고 있는 섬유의 수를 산출한다. 이를 백분율로 표시한다.
본 발명의 일실시예에 의한 원단의 융착율은 다양한 제품군에 제공될 수 있도록 30 내지 100%일 수 있다. 그리고 상기 범위의 융착율을 갖는 원단의 경우 실미끄러짐 정도가 0.1 내지 2.5mm이며, 올풀림강도의 경우 1올 기준 0.2 내지 3.5Kg, 5mm 기준 10 내지 35Kg일 수 있다. 또한 원단의 굽힘길이는 3 내지 10cm일 수 있다.
상기 미끄럼 길이는 원단의 경사 또는 위사가 직물의 표면 또는 이면에 가해지는 마찰 등 물리적 작용에 의하여 부분적으로 경사 또는 위사의 교차 위치가 한 쪽으로 치우치거나 밀린 상태에서의 길이를 의미한다. 일반 직물의 경우 경사 및 위사 간에 커버팩터(cover factor)에 의한 결합력이 존재하여 물리적 결합력으로서 직물의 형태안정성을 확보하지만 본 발명에 의한 원단은 이와 더불어 각각 경사 및/또는 위사의 융착율을 확보하여 직물의 형태안정성을 더 확보할 수 있다.(도 4 참조)
한편 상기 올풀림강도라 함은 원단에서 직조된 경사 또는 위사가 원단의 구성으로부터 이탈되는 때의 강도를 의미한다. 즉 올풀림강도가 크다는 것은 직조된 원사가 저융점사와 융착되는 정도가 큼을 의미한다. 이는 원단이 스크린 또는 블라인드 용도로서 장폭 또는 장길이의 사용상태에 있어서 형태안정성이 확보되는 것을 의미한다.
또한 본 발명에 의한 원단의 굽힘길이는 3 내지 10cm일 수 있다. 굽힘길이는 후술된 시험방법에 의해 평가될 수 있는데, 본 발명에 의한 원단의 굽힘길이는 통상의 원단의 굽힘길이와 일정 차이를 나타내기는 하나 굽힘성이 발현되어 원단으로서의 유연성이 확보될 수 있다. 상기 굽힘길이가 과도하게 길 경우에는 결국 원단으로서의 유연성이 결여되어 가공공정에 어려움이 있고 블라인드 등의 용도로서 부적합한 문제점이 있다.
상기 원단의 물성이 상기 범위 내에 포함되는 경우 스크린/블라인드용으로서 적절한 형태안정성이 부여되고 롤링(블라인드지로 사용되는 경우 원단이 감길 수 있어야 함)에도 큰 문제가 없다. 즉 본 발명에 의한 원단에 있어서 상기와 같은 물성의 영역은 스크린용으로서의 형태안정성과 원단으로서 유연성이란 모순된 물성을 동시에 만족할 수 있는 바람직한 영역이라 할 수 있다.
한편 본 발명의 일실시예에 의한 원단은 난연성 이외에 내광 견뢰도를 우수하게 하기 위해 벤조트리아졸계, 벤조페논계 등의 자외선 흡수제나 다른 섬유용 가공제를 사용할 수도 있다. 상기 사용될 수 있는 다른 섬유용 가공제로서 일반적으로 사용되는 대전방지제, 발수발유제, 오염방지제, 항균제, 수분 흡수제, 슬립 방지제 등이 부가적으로 사용될 수도 있으며 이러한 일반적으로 공지된 가공제가 부가된다 하더라도 본 발명의 본질적인 발명의 사상을 벗어나지 않는 한 본 발명의 범주에 포함됨은 물론이다.
한편 본 발명에 의한 원단은 난연사와 저융점사로 형성된 원단으로 제조될 수 있다. 이 경우 상기 저융점사는 경사 및 위사 또는, 경사 또는 위사에 포함되거나 상기 난연사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함될 수 있다. 기타 물성과 융착율은 상기 일반사와 저융점사로 형성된 원단과 동일할 수 있다.
이하 본 발명의 재생 폴리에스테르 섬유를 제조하기 위한 방법의 실시예를 나타내지만, 한정되는 것은 아니다.
실시예 1
제직원사로 경사를 일반 폴리에스테르로 사용하고, 위사로 심초(Sheath/Core)구조인 복합섬유로서 시드부가 저융점(Low Melting Point)을 가지는 폴리에스테르 30중량%와 일반 폴리에스테르 70중량%를 합사한 원사를 사용하여 평직으로 직조하였다. 이 때 조직밀도는 경사방향으로 100가닥/inch, 위사방향으로 100가닥/inch이다. 이후 직조된 원단을 융착율이 30%가 되도록 처리하였다.
실시예 2 내지 실시예 5
상기 실시예 1과 동일하되, 융착율이 각각 50%, 70%, 90%, 100%이 되도록 하였다.
실시예 6 내지 10
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 40중량%로 하였다.
실시예 11 내지 15
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 50중량%로 하였다.
실시예 16 내지 20
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 60중량%로 하였다.
실시예 21 내지 25
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 70중량%로 하였다.
실시예 26 내지 30
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 80중량%로 하였다.
실시예 31 내지 35
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 90중량%로 하였다.
실시예 36 내지 40
상기 실시예 1 내지 5와 동일하되, 저융점 폴리에스테르 비율을 100중량%로 하였다.
비교예 1 및 2
상기 실시예 1과 동일하되, 각각 융착율을 10% 및 20%^로 처리하였다.
비교예 3
상기 실시예 1과 동일하되, 저융점사를 사용하지 않고 일반 폴리에스테르사를 이용하여 통상의 원단을 제조하였다.
표 1
구분 원단구조 융착율(%)
경사 위사(합사율)
실시예 1 일반사 30중량% 30
실시예 2 일반사 30중량% 50
실시예 3 일반사 30중량% 70
실시예 4 일반사 30중량% 90
실시예 5 일반사 30중량% 100
실시예 6 일반사 40중량% 30
실시예 7 일반사 40중량% 50
실시예 8 일반사 40중량% 70
실시예 9 일반사 40중량% 90
실시예 10 일반사 40중량% 100
실시예 11 일반사 50중량% 30
실시예 12 일반사 50중량% 50
실시예 13 일반사 50중량% 70
실시예 14 일반사 50중량% 90
실시예 15 일반사 50중량% 100
실시예 16 일반사 60중량% 30
실시예 17 일반사 60중량% 50
실시예 18 일반사 60중량% 70
실시예 19 일반사 60중량% 90
실시예 20 일반사 60중량% 100
실시예 21 일반사 70중량% 30
실시예 22 일반사 70중량% 50
실시예 23 일반사 70중량% 70
실시예 24 일반사 70중량% 90
실시예 25 일반사 70중량% 100
실시예 26 일반사 80중량% 30
실시예 27 일반사 80중량% 50
실시예 28 일반사 80중량% 70
실시예 29 일반사 80중량% 90
실시예 30 일반사 80중량% 100
실시예 31 일반사 90중량% 30
실시예 32 일반사 90중량% 50
실시예 33 일반사 90중량% 70
실시예 34 일반사 90중량% 90
실시예 35 일반사 90중량% 100
실시예 36 일반사 100중량% 30
실시예 37 일반사 100중량% 50
실시예 38 일반사 100중량% 70
실시예 39 일반사 100중량% 90
실시예 40 일반사 100중량% 100
비교예 1 일반사 30중량% 10
비교예 2 일반사 30중량% 20
비교예 3 일반사 일반사 -
* 시험방법
1. 실미끄러짐 길이 측정 : KSK 0408
2. 올풀림 강도
(1) 한 올 풀림강도
시료 크기 7X7(cm)을 준비하고 이 중 한올을 빼서 1 cm만큼 풀어내어 인장시험기(KSK 0520)에 물린 후 나머지 6 cm에 잔존하는 시료내의 한 올이 다 풀려나갈때 까지 필요한 하중을 측정하였다. 이 때 조직밀도는 100X100(가닥/inch)으로 일치시켰다.
(2) 5mm 올풀림 강도
시료 크기 7X7(cm)을 준비하고 준비한 시료의 가운데 윗변에서 5미리 위치에 후크를 걸어 끼운다. 상기 후크는 60 Kg이상의 힘에도 형태변화가 없는 재질을 사용한다. 상기 후크를 인장시험기 윗부분에 , 원단은 아래쪽에 파지 한 후 하중을 가하면서 5 mm 만큼의 올이 원단에서 분리될 때 까지 필요한 하중 측정한다. 이 때 올이 분리되지 않고 원단 파열이 일어날 경우 파열 시점의 하중을 데이타로 간주한다. 측정 중에 가해진 하중 중 최대치를 물성 수치로 평가한다. 이 때 조직밀도는 100X100(가닥/inch)으로 일치시켰다.
3. 원단의 굽힘길이
시료 크기 7X7(cm)을 준비하고 일단을 플랫폼의 긴 방향에 대하여 평행하게 되도록 플랫폼 위에 위치시킨다. 늘어진 부분이 플랫폼에서 돌출되어 자체 하중에 의하여 굽어지도록 플랫폼의 길이 방향으로 전진시킨다. 돌출된 부분의 끝은 자유롭고 다른 쪽은 적당한 압력으로 시료가 미끄러지도록 한다. 시료의 앞 끝이 플랫폼 앞 끝에서 연속되는 선을 지나 수평면 이하 41.5°의 각도로 기울어지면, 돌출길이는 시료의 굽힘길이의 두배가 된다.
상기 실시예의 시험결과는 하기 표 2로 정리하였다. 하기 표 2에 나타난 것과 같이 본 발명에 의한 실시예들은 일반 원단(비교예 3)은 물론 비교예들에 비해 원단의 융착상태가 우수하여 직조된 원사가 탈리되지 않음을 알 수 있다. 즉 이는 원단의 경직성으로 발현되어 용도별로 선택에 따라 적절한 융착율 및 저융점사의 혼용율을 가변하여 경직성을 제어할 수 있다. 한편 도 3 및 4는 본 발명의 실시예에 의한 원단의 단면 SEM 사진이고, 도 5는 비교예에 의한 원단의 단면 SEM 사진이다.
표 2
구분 슬립(mm) 올풀림강도(Kg) 굽힘길이(cm)
1올 5mm
실시예 1 2.5 0.2 10 3
실시예 2 2.1 0.9 10.9 3.4
실시예 3 1.8 2.1 11.7 3.9
실시예 4 1.2 2.5 18.3 4.3
실시예 5 0.5 2.7 21.1 4.7
실시예 6 2.5 0.3 10.2 5
실시예 7 1.9 2.1 11.4 4.4
실시예 8 1.2 2.4 15.1 5.1
실시예 9 0.5 2.9 19.1 6
실시예 10 0.4 3.1 22.5 6.9
실시예 11 2.4 0.3 10.2 4.1
실시예 12 1.7 2.2 13.4 4.6
실시예 13 0.9 2.6 17.1 5.4
실시예 14 0.4 3.2 23.5 6.2
실시예 15 0.4 3.3 26.8 7.2
실시예 16 2.2 0.5 10.6 4.2
실시예 17 1.3 2.2 18.3 4.8
실시예 18 0.6 2.7 21.4 5.7
실시예 19 0.4 3.3 26.9 6.6
실시예 20 0.3 3.4 29.4 7.3
실시예 21 2.1 0.7 10.9 4.6
실시예 22 1.2 1.9 19.3 5.3
실시예 23 0.6 2.2 25.3 6.1
실시예 24 0.3 3.1 31 7
실시예 25 0.2 3.4 32.1 7.6
실시예 26 2 0.7 11.2 5
실시예 27 1.1 1.6 22.1 5.8
실시예 28 0.5 2.6 30.1 6.5
실시예 29 0.2 3.3 34.1 7.3
실시예 30 0.1 3.4 34.8 8
실시예 31 2.1 0.7 13.2 5.5
실시예 32 0.9 1.9 25.4 6.2
실시예 33 0.4 2.8 33.2 7.2
실시예 34 0.2 3.4 34.5 8.2
실시예 35 0.1 3.5 35 8.8
실시예 36 1.9 0.8 14.3 6.1
실시예 37 0.8 1.9 30.4 7
실시예 38 0.2 3.1 34.2 8.3
실시예 39 0.1 3.5 34.9 9.2
실시예 40 0.1 3.5 35 10
비교예 1 4.5 0.12 3.85 2.7
비교예 2 4.3 0.15 5.76 2.9
비교예 3 6.7 0.1 2.14 2.6
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.

Claims (12)

  1. 일반사와 저융점사를 포함하는 원단에 있어서,
    상기 저융점사가 경사 및 위사 또는, 경사 또는 위사에 포함되거나; 상기 일반사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함되되,
    상기 저융점사의 융착율이 30 내지 100%인 저융점사를 포함하는 원단.
  2. 제1항에 있어서,
    상기 범위의 융착율을 갖는 원단의 경우 실미끄러짐도가 0.1 내지 2.5mm인 저융점사를 포함하는 원단.
  3. 제1항 또는 제2항에 있어서,
    상기 원단의 올풀림강도(1올 기준)가 0.2 내지 3.5Kg인 저융점사를 포함하는 원단.
  4. 제1항 또는 제2항에 있어서,
    상기 원단의 올풀림강도(5mm 기준)가 10 내지 35Kg인 저융점사를 포함하는 원단.
  5. 제3항에 있어서,
    상기 원단의 올풀림강도(5mm 기준)가 10 내지 35Kg인 저융점사를 포함하는 원단.
  6. 제1항 또는 제2항에 있어서,
    상기 원단의 굽힘길이는 3 내지 10cm인 저융점사를 포함하는 원단.
  7. 제3항에 있어서,
    상기 원단의 굽힘길이는 3 내지 10cm인 저융점사를 포함하는 원단.
  8. 제5항에 있어서,
    상기 원단의 굽힘길이는 3 내지 10cm인 저융점사를 포함하는 원단.
  9. 제1항 또는 제2항에 있어서,
    상기 일반사와 저융점사는 50 : 50 내지 75 : 15 중량비로 이루어진 저융점사를 포함하는 원단.
  10. 제1항에 있어서,
    상기 원단에는 난연사가 더 포함된 저융점사를 포함하는 원단.
  11. 제1항 또는 제2항에 있어서,
    상기 저융점사는 복합섬유로서,
    시스부에는 저융점 폴리에스테르계 수지가, 코어부에는 난연성 폴리에스테르계 수지가 포함된 저융점사를 포함하는 원단.
  12. 난연사와 저융점사를 포함하는 원단에 있어서,
    상기 저융점사가 경사 및 위사 또는, 경사 또는 위사에 포함되거나; 상기 난연사와 저융점사가 혼방 또는 합사되어 경사 및 위사 또는, 경사 또는 위사에 포함되되,
    상기 저융점사의 융착율이 30 내지 100%인 저융점사를 포함하는 원단.
PCT/KR2009/004354 2009-06-12 2009-08-04 저융점사를 포함하는 원단 Ceased WO2010143777A1 (ko)