WO2016190403A1 - 高速鉄道車両用焼結摩擦材とその製造方法 - Google Patents

高速鉄道車両用焼結摩擦材とその製造方法 Download PDF

Info

Publication number
WO2016190403A1
WO2016190403A1 PCT/JP2016/065648 JP2016065648W WO2016190403A1 WO 2016190403 A1 WO2016190403 A1 WO 2016190403A1 JP 2016065648 W JP2016065648 W JP 2016065648W WO 2016190403 A1 WO2016190403 A1 WO 2016190403A1
Authority
WO
WIPO (PCT)
Prior art keywords
friction material
sintered friction
volume
powder
speed railway
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2016/065648
Other languages
English (en)
French (fr)
Inventor
耕嗣 大藪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Akebono Brake Industry Co Ltd
Original Assignee
Akebono Brake Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Akebono Brake Industry Co Ltd filed Critical Akebono Brake Industry Co Ltd
Priority to EP16800107.1A priority Critical patent/EP3305927B1/en
Priority to CN201680031128.1A priority patent/CN107614720B/zh
Publication of WO2016190403A1 publication Critical patent/WO2016190403A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、３００ｋｍ／ｈを超える高速域においても高い摩擦係数を安定して維持することができる高速鉄道車両用焼結摩擦材を提供することを目的とする。本発明の高速鉄道車両用焼結摩擦材は、Ｃｕを基材とし、１体積％～２０体積％のＦｅＣｒと、５体積％～２０体積％の金属酸化物と、３０体積％～６０体積％の潤滑材を含む。

Description

高速鉄道車両用焼結摩擦材とその製造方法
　本発明は、新幹線などの高速鉄道車両に用いられる焼結摩擦材とその製造方法に関する。
　新幹線などの高速鉄道車両は、１車両当たりの重量が４０ｔを超え、３００ｋｍ／ｈを超える走行速度で運行される。このため、このような高速で運行される車両を、確実に停止可能なブレーキが必要不可欠である。特に、緊急時において、安全かつ短距離で停止可能なブレーキが求められている。
　従来、高速鉄道車両用ブレーキとしては、一般的に、モータを発電機として使用することによって制動をかける電気ブレーキと、車軸とともに回転するブレーキロータに、摩擦材を押し付けることによって制動をかける基礎ブレーキ（ディスクブレーキ）とが併用されている。このうち、ディスクブレーキを構成する摩擦材は、通常、銅や鉄などの基材に、摩擦調整材、研摩材および潤滑材などを添加することによって製造される。
　たとえば、日本国特開２００６－１６６８０号公報には、スズ粉末；０．５ｗｔ％～１５ｗｔ％、亜鉛粉末；０．１ｗｔ％～３０ｗｔ％、ニッケル粉末；５ｗｔ％～２５ｗｔ％、鉄粉末；５ｗｔ％～２５ｗｔ％、ステンレス鋼粉末；０．１ｗｔ％～２０ｗｔ％、銅粉末；残部、のマトリックス金属成分が５５ｗｔ％～８０ｗｔ％、潤滑材、摩擦調整材などのフィラー成分が２０ｗｔ％～４５ｗｔ％、の焼結体からなり、（１）鉄粉末とステンレス鋼粉末の合計量が８ｗｔ％～２８ｗｔ％、（２）鉄粉末が、水素ガスまたはアンモニアガス雰囲気中で６００℃～１２００℃の温度で熱処理した粒径範囲が４０μｍ～１５０μｍの電解鉄粉末であることを特徴とする銅系焼結摩擦材が開示されている。
　また、日本国特開２００７－１２６７３８号公報には、金属材料をマトリックスとし、研削材と潤滑材とを含む焼結摩擦材において、マトリックスの金属材料として、鋳鉄２５体積％～５０体積％と、銅１体積％～７体積％とを含む焼結摩擦材が開示されている。
　しかしながら、これらの文献に記載の焼結摩擦材は、高速域における摩擦係数や耐摩耗性に問題がある。具体的には、日本国特開２００６－１６６８０号公報に記載の焼結摩擦材は、電解鉄粉末とステンレス鋼粉末を併用することで、鉄成分の焼結を阻害する作用を利用して、摩擦材中に空隙を生じさせ、この空隙によってもたらされる研削作用によって摩擦係数を確保しようとするものであるため、高速鉄道車両のさらなる高速化（３５０ｋｍ／ｈ以上）に対応することができない。一方、日本国特開２００７－１２６７３８号公報に記載の技術は、基材に鉄系合金を使用しているため、銅系焼結摩擦材と比べて熱伝導性に劣り、減速時に急激な温度上昇を伴うという問題がある。また、相手材（ブレーキロータ）との関係で、減速時における摩耗量が大きく、十分な耐摩耗性を確保することが困難であるという問題がある。
　これらの焼結摩擦材に対して、日本国特開２０１２－２０７２８９号公報には、７．５質量％以上のＦｅ、５０質量％以上のＣｕ、５質量％～１５質量％の黒鉛、０．３質量％～７質量％の二硫化モリブデンおよび０．５質量％～１０質量％のシリカを含有し、Ｆｅ／Ｃｕが０．１５～０．４０であることを特徴とする高速鉄道車両用焼結摩擦材料が開示されている。この焼結摩擦材は、銅系の焼結摩擦材に添加されたＦｅが相手材に含まれるＦｅと反応し、両者が凝着することにより高い摩擦係数を実現している。また、基材に、熱伝導性に優れる銅を使用しており、減速時における急激な温度上昇を防止している。
　しかしながら、このような焼結摩擦材であっても、減速時に生じた摩擦熱によって、その表面は１０００℃を超えるような高温となる。このため、摩擦調整材として添加したＦｅが酸化され、焼結摩擦材の表面に酸化鉄層が形成されると、十分な凝着力を発揮することができなくなる。したがって、この文献に記載の技術では、長期間にわたって、高い摩擦係数を安定して維持することは困難である。
　なお、日本国特開昭６０－２００９３２号公報には、銅系の焼結摩擦材に、ＦｅＣｒを１質量％～２０質量％添加することにより、耐熱フェード特性および耐水フェード特性を高め、特に高温域における摩擦係数および耐摩耗性の改善を図る技術が記載されている。
　しかしながら、この文献に記載の焼結摩擦材は、二輪車を対象としたものであり、高速鉄道車両を対象としたものではない。すなわち、この文献に記載の技術は、シリカやアルミナなどの金属酸化物のひっかき作用によって摩擦係数を確保しており、ＦｅＣｒは、基材の溶着（凝着）や塑性流動を防止し、耐摩耗性を向上させるために添加されているにすぎない。したがって、この文献に記載の技術では、上述した日本国特開２００６－１６６８０号公報に記載の技術と同様に、高速鉄道車両のさらなる高速化に対応することはきわめて困難である。
日本国特開２００６－１６６８０号公報 日本国特開２００７－１２６７３８号公報 日本国特開２０１２－２０７２８９号公報 日本国特開昭６０－２００９３２号公報
　本発明は、３００ｋｍ／ｈを超える高速域においても、高い摩擦係数を安定して維持できる高速鉄道車両用焼結摩擦材を提供することを目的とする。また、本発明は、このような高速鉄道車両用焼結摩擦材を、工業規模の製造において容易に製造可能な方法を提供することを目的とする。
　本発明の高速鉄道車両用焼結摩擦材は、Ｃｕを基材とし、１体積％～２０体積％のＦｅＣｒと、５体積％～２０体積％の金属酸化物と、３０体積％～６０体積％の潤滑材とを含むことを特徴とする。
　前記Ｃｕを２０体積％以上含むことが好ましい。
　前記金属酸化物は、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３から選択される１種以上であることが好ましく、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の３種であることがより好ましい。この場合、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の体積比が、ＭｇＯ：ＺｒＯ２：Ａｌ２Ｏ３＝１．５～２．５：１．５～２．５：１．０であることがさらに好ましい。
　なお、本発明の高速鉄道車両用焼結摩擦材は、１５体積％以下のＳｎおよびＺｎのうちの少なくとも１つをさらに含むことができる。
　また、本発明の高速鉄道車両用焼結摩擦材の製造方法は、
　基材となるＣｕ粉末に、１体積％～２０体積％のＦｅＣｒ粉末と、５体積％～２０体積％の金属酸化物粉末と、３０体積％～６０体積％の潤滑材とを混合することにより混合粉末を得る、混合工程と、
　前記混合粉末を成形型に投入し、加圧成形することにより予備成形体を得る、成形工程と、
　前記予備成形体とプレッシャプレートとを重ね合わせて焼成することにより、焼結体を得る、焼結工程と、
を備えることを特徴とする。
　前記焼結体を、常温、５０ＭＰａ～９０ＭＰａで、２秒間～５秒間サイジングした後、所定の厚さに研摩する、加工工程をさらに備えることが好ましい。
　前記金属酸化物として、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３から選択される１種以上を用いることが好ましく、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の３種を用いることがより好ましい。この場合、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の体積比を、ＭｇＯ：ＺｒＯ２：Ａｌ２Ｏ３＝１．５～２．５：１．５～２．５：１．０とすることがより好ましい。
　前記混合工程において、１５体積％以下のＳｎおよびＺｎのうちの少なくとも１つをさらに混合してもよい。
　前記ＦｅＣｒ粉末として、平均粒径が１０μｍ～３００μｍであるＦｅＣｒ粉末を用いることが好ましい。また、前記金属酸化物粉末として、平均粒径が５０μｍ～４００μｍである金属酸化物粉末を用いることが好ましい。
　本発明によれば、３００ｋｍ／ｈを超える高速域においても、高い摩擦係数を安定して維持できる高速鉄道車両用焼結摩擦材を提供することができる。また、このような高速鉄道車両用焼結摩擦材を、工業規模の製造において容易に製造可能な方法を提供することができる。このため、本発明の工業的意義はきわめて大きい。
図１は、本発明の高速鉄道車両用焼結摩擦材の一実施態様を示す、概略平面図である。
　上述したように、焼結摩擦材中のフェロクロム（ＦｅＣｒ）には、高速域からの減速時における基材の凝着を防止する効果があることが知られていたものの、摩擦調整材としての鉄と異なり、それ自体によって、直接的に摩擦係数を向上させる効果はないと考えられていた。
　本発明者は、この点について研究を重ねた結果、自動車や二輪車よりもはるかに高重量物である高速鉄道車両を、３００ｋｍ／ｈを超える高速域から減速させる場合には、焼結摩擦材の表面温度は１０００℃を超える高温となるため、ＦｅＣｒが相手材と凝着し、高い摩擦係数を発揮することができるとの知見を得た。また、ＦｅＣｒは耐酸化性に優れるため、このような高温にさらされた場合であっても、焼結摩擦材の表面に酸化鉄層が形成されることはないとの知見を得た。
　一方、焼結摩擦材と相手材との凝着力によって高い摩擦係数を確保する場合、相手材の表面に移着物や反応生成物が生じることが問題となる。特に、高速鉄道車両の用途では、減速時に要するエネルギが膨大となるため、これらの移着物や反応生成物の影響は大きく、長期間にわたって、高い摩擦係数を安定して維持することが困難となる場合がある。本発明者は、この点を踏まえて、さらに研究を重ねた結果、摩擦調整材として添加する研削材および潤滑材の添加量や種類などを最適化することにより、移着物や反応生成物の影響を効果的に排除できるとの知見を得た。本発明は、これらの知見に基づき完成されたものである。
　以下、本発明の高速鉄道車両用焼結摩擦材（以下、「焼結摩擦材」という）について、「１．高速鉄道車両用焼結摩擦材」と「２．高速鉄道車両用焼結摩擦材の製造方法」に分けて説明する。なお、本発明は、焼結摩擦材の形状や寸法によって制限されることはないが、以下では、図１に示すような、厚さが１５ｍｍ～５５ｍｍ、短手方向の長さが１００ｍｍ～２００ｍｍ、長手方向の長さが３５０ｍｍ～５５０ｍｍの範囲にあるブレーキライニングを例に挙げて説明する。
　１．高速鉄道車両用焼結摩擦材
　（１）組成
　本発明の焼結摩擦材は、Ｃｕを基材とし、１体積％～２０体積％のフェロクロム（ＦｅＣｒ）と、５体積％～２０体積％の金属酸化物と、３０体積％～６０体積％の黒鉛とを含むことを特徴とする。
　［基材］
　本発明の焼結摩擦材では、基材としてＣｕを使用する。これは、Ｃｕは熱伝導性に優れるため、ＦｅやＦｅ合金を基材とする焼結摩擦材に比べて、表面温度の急激な上昇を防止することができるからである。
　Ｃｕの含有量は、特に制限されることはなく、焼結摩擦材の基礎となるマトリックスを構成可能な程度であればよい。具体的には、Ｃｕの含有量は、２０体積％以上とすることが好ましく、３０体積％以上とすることがより好ましい。Ｃｕの含有量が２０体積％未満では、他の構成成分との関係で、焼結摩擦材の成形性や強度が低下するばかりでなく、十分な熱伝導性を確保することができない場合がある。一方、Ｃｕの含有量の上限は、後述する摩擦調整材や研削材などの添加成分との関係で定められるべきものであるが、概ね、５０体積％以下とすることが好ましく、４５体積％以下とすることがより好ましい。
　なお、本発明の焼結摩擦材においては、Ｃｕに、焼結助剤として、微量のスズ（Ｓｎ）および亜鉛（Ｚｎ）のうちの少なくとも１つを添加し、基材をＣｕ－Ｓｎ合金、Ｃｕ－Ｚｎ合金またはＣｕ－Ｓｎ－Ｚｎ合金により構成することもできる。基材をこれらのＣｕ合金で構成することにより、焼結摩擦材の低温焼結が可能となる。ただし、これらの焼結助剤の含有量は、１５体積％以下とすることが好ましい。焼結助剤の含有量が１５体積％を超えると、液相温度が下がり、焼結摩擦材の耐熱温度が低下してしまうおそれがある。
　［摩擦調整材］
　本発明では、摩擦調整材としてフェロクロム（ＦｅＣｒ）を用いる。ＦｅＣｒは、融点が１４００℃～１５００℃の範囲にあり、Ｃｕの融点（１０８３℃）と比べて高温である。このため、高速鉄道車両を３００ｋｍ／ｈを超える高速域から減速させる際に、摩擦材の表面が１０００℃を超えるような高温となった場合においても、相手材との凝着が可能であり、高い摩擦係数を発揮することができる。しかも、ＦｅＣｒは耐酸化性に優れ、減速時に生じた摩擦熱により酸化することはないため、このような高い摩擦係数を安定して維持することができる。
　なお、ＦｅＣｒとしては、高炭素ＦｅＣｒ、中炭素ＦｅＣｒおよび低炭素ＦｅＣｒのいずれも用いることができるが、ＦｅＣｒの耐熱温度の観点から、低炭素ＦｅＣｒを用いることが好ましい。
　ＦｅＣｒの含有量は、１体積％～２０体積％、好ましくは２体積％～１０体積％、より好ましくは４体積％～８体積％とすることが必要となる。ＦｅＣｒの含有量が１体積％未満では、その添加効果を得ることができない。一方、ＦｅＣｒは、固体状態では硬度が高いため、その含有量が２０体積％を超えると、相手材の摩耗量が著しく増加してしまう。
　［研削材］
　研削材は、摩擦係数を高めるとともに、その研削作用により相手材（ディスクロータ）の摩擦面に生じた移着物や反応生成物を削り取り、摩擦面をクリーンな状態に保つために添加する成分である。本発明の焼結摩擦材では、高速域における高い摩擦係数を確保するために相手材との凝着力を利用しているため、このような研削材および次述する潤滑材の含有量や種類の選択も重要となる。
　本発明の焼結摩擦材では、研削材として、金属酸化物を使用することができ、その含有量を、５体積％～２０体積％、好ましくは６体積％～１５体積％、より好ましくは７体積％～１３体積％とすることが必要となる。金属酸化物の含有量が５体積％未満では、上述した機能を十分に発揮することができない。一方、金属酸化物の含有量が２０体積％を超えると、相手材に対する攻撃性が過度に大きくなってしまう。
　このような金属酸化物としては、焼結摩擦材に要求される性能に応じて種々のものを選択することができる。しかしながら、本発明のような高速鉄道車両での用途では、相手材であるディスクロータの寿命を確保する観点から、マグネシア（ＭｇＯ）、ジルコニア（ＺｒＯ２）およびアルミナ（Ａｌ２Ｏ３）から選択される１種以上を使用することが好ましく、これら３種の金属酸化物を組み合わせて使用することがより好ましい。
　金属酸化物として、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３を使用する場合、これらの体積比を、ＭｇＯ：ＺｒＯ２：Ａｌ２Ｏ３＝１．５～２．５：１．５～２．５：１．０とすることが好ましく、１．８～２．３：１．８～２．３：１．０とすることがより好ましく、２：２：１とすることがさらに好ましい。これにより、焼結摩擦材に適度な研削作用を付与し、高速域からの減速時における摩擦係数を、さらに安定させることができる。
　［潤滑材］
　潤滑材は、相手材との焼き付きを防止するとともに、焼結摩擦材の寿命（耐久性）を向上させるために添加する成分である。本発明の焼結摩擦材では、このような潤滑材として、従来技術と同様に、黒鉛、二硫化モリブデン（ＭｏＳ２）、二硫化タングステン（ＷＳ２）、フッ化カルシウム（ＣａＦ２）などから選択される少なくとも１種を使用することができる。これらの中でも、環境に対する負荷が少ない、黒鉛を使用することが好ましい。
　潤滑材として黒鉛を使用する場合、天然黒鉛のほか、膨張黒鉛や人造黒鉛も使用することができるが、これらの中でも天然黒鉛や人造黒鉛を使用することが好ましく、天然黒鉛と人造黒鉛を組み合わせて使用することがより好ましい。なお、天然黒鉛としては、鱗状黒鉛を使用することが好ましい。
　鱗状黒鉛と人造黒鉛を組み合わせて使用する場合、鱗状黒鉛と人造黒鉛の体積比を、２．５～３．５：１．０とすることが好ましく、２．８～３．２：１．０とすることがより好ましい。これにより、高速域からの減速時における耐摩耗性を改善することができる。
　潤滑材の含有量は、合計で、３０体積％～６０体積％、好ましくは３５体積％～５０体積％、より好ましくは３７体積％～４８体積％とすることが必要となる。潤滑材の含有量が３０体積％未満では、その添加効果を十分に得ることができない。一方、潤滑材の含有量が６０体積％を超えると、焼結摩擦材の強度を十分に確保することができなくなる。
　（２）特性
　［摩擦係数］
　上述したように、本発明の焼結摩擦材は、摩擦調整材としてＦｅＣｒを使用しているため、高速域においても、高い摩擦係数を発揮することができる。また、減速時に生じた摩擦熱により酸化鉄層が形成されることがなく、かつ、研削材や潤滑材の含有量および種類を適切に規制することにより、相手材の表面に生じた移着物や反応生成物を除去することが可能であるため、このような高い摩擦係数を、長期間にわたって安定して維持することができる。
　具体的には、本発明の焼結摩擦材を用いて、以下の条件でダイナモ試験（非常ブレーキ相当）を行った場合において、３６５ｋｍ／ｈにおける摩擦係数の平均値（平均摩擦係数）μａｖｅを０．３０以上、好ましくは０．３３以上とすることができる。また、この速度における瞬間の摩擦係数の最小値（最小摩擦係数）μｍｉｎを０．２５以上、好ましくは０．３０以上とすることができる。
　　（ダイナモ試験の条件）
　　・慣性モーメント　：１２１ｋｇ・ｍ２
　　・初速度　　　　　：３６５ｋｍ・ｈ－１
　　・試験回数　　　　：３回
　　・相手材　　　　　：新幹線用鍛鋼ディスクロータ
　［摩耗量］
　上述のように、ＦｅＣｒは、固体状態においては硬質であるため、その含有量が増加するほど、焼結摩擦材の攻撃性が高くなり、相手材の摩耗量が大きくなるおそれがある。このような問題に対して、本発明の焼結摩擦材では、ＦｅＣｒの含有量を適宜調整することで、高い摩擦係数を維持したまま、相手材の摩耗量を抑制することが可能である。なお、相手材の摩耗量は、たとえば、断面測定機を用いて測定することができる。
　２．高速鉄道車両用焼結摩擦材の製造方法
　本発明の焼結摩擦材の製造方法は、基材となるＣｕ粉末に、１体積％～２０体積％のＦｅＣｒ粉末と、５体積％～２０体積％の金属酸化物粉末と、３０体積％～６０体積％の潤滑材とを混合することにより混合粉末を得る、混合工程と、この混合粉末を成形型に投入し、加圧成形することにより予備成形体を得る、成形工程と、この予備成形体とプレッシャプレートとを重ね合わせて焼成することにより、焼結体を得る、焼結工程とを備えることを特徴とする。以下、工程ごとに、本発明の焼結摩擦材の製造方法を説明する。
　（１）混合工程
　混合工程は、基材となるＣｕ粉末に、１体積％～２０体積％のＦｅＣｒ粉末と、５体積％～２０体積％の金属酸化物粉末と、３０体積％～６０体積％の潤滑材とを混合し、混合粉末を得る工程である。
　ａ）原料粉末
　本発明の製造方法において使用することができる原料粉末は、特に制限されることはないが、以下で説明するものを使用することが好ましい。なお、各原料粉末の混合比や、金属酸化物粉末としてＭｇＯ粉末、ＺｒＯ２粉末およびＡｌ２Ｏ３粉末を使用する場合の体積比などについては、上述した焼結摩擦材における組成比と同様であるため、ここでの説明は省略する。
　［Ｃｕ粉末］
　Ｃｕ粉末としては、平均粒径が１０μｍ～２００μｍのものを用いることが好ましく、３０μｍ～１００μｍのものを用いることがより好ましい。これにより、混合工程において、混合粉末中に各原料粉末を均一に分散させることができ、得られる焼結摩擦材を均一な組成とすることが可能となる。
　なお、ＳｎやＺｎなどの焼結助剤を使用する場合、平均粒径が５μｍ～１００μｍのものを用いることが好ましく、１０μｍ～８０μｍのものを用いることがより好ましい。
　また、本発明の製造方法においては、Ｃｕ粉末に代えて、Ｃｕ－Ｓｎ合金粉末、Ｃｕ－Ｚｎ合金粉末あるいはＣｕ－Ｓｎ－Ｚｎ合金粉末などのＣｕ合金粉末を用いることも可能である。この場合、Ｃｕ合金粉末として、平均粒径が５μｍ～１００μｍのものを用いることが好ましく、１０μｍ～８０μｍのものを用いることがより好ましい。
　［ＦｅＣｒ粉末］
　ＦｅＣｒ粉末としては、平均粒径が１０μｍ～３００μｍのものを用いることが好ましく、３０μｍ～１００μｍのものを用いることがより好ましい。ＦｅＣｒ粉末の平均粒径が１０μｍ未満では、焼結摩擦材の表面に露出するＦｅＣｒの割合が減少し、摩擦性能が低下するおそれがある。一方、ＦｅＣｒ粉末の平均粒径が３００μｍを超えると、焼結摩擦材の表面に露出するＦｅＣｒに偏りが生じるため、局所的に、高摩擦領域が形成されるおそれがある。
　［金属酸化物粉末］
　金属酸化物粉末としては、平均粒径が５０μｍ～４００μｍのものを用いることが好ましい。金属酸化物粉末の平均粒径が５０μｍ未満では、ディスクロータの摩擦面に対するクリーニング性が不足する場合がある。一方、金属酸化物粉末の平均粒径が４００μｍを超えると、焼結摩擦材の表面に露出する金属酸化物に偏りが生じるため、局所的に、高摩擦領域が形成されるおそれがある。
　なお、本発明において、Ｃｕ粉末、ＦｅＣｒ粉末および金属酸化物粉末の平均粒径は、レーザー回折式粒度分布計により測定される値（メジアン径）を意味する。
　［潤滑材］
　潤滑材として、黒鉛粉末を用いる場合、平均粒径が１０μｍ～２０００μｍのものを用いることが好ましい。ただし、黒鉛粉末として人造黒鉛を用いる場合には、平均粒径が５００μｍ以上２０００μｍ以下の範囲にある大粒径の人造黒鉛（ＣＬ）と、平均粒径が５０μｍ以上５００μｍ未満の範囲にある小粒径の人造黒鉛（Ｃｓ）とを、体積比（ＣＬ／ＣＳ）が、１．５～２．５となるように混合して用いることが好ましく、１．８～２．４となるように混合して用いることがより好ましい。これにより、潤滑特性が優れるばかりでなく、黒鉛を比較的多く含む場合であっても、高強度の焼結摩擦材を得ることができる。
　なお、本発明において、黒鉛の平均粒径は、ふるい分け法やレーザー回折式粒度分布計により測定される値（メジアン径）を意味する。
　ｂ）混合方法
　混合方法は、上述した原料粉末が均一に混合される限り、特に制限されることはなく公知の方法を利用することができる。具体的には、上述した原料粉末に適量の有機溶剤を添加し、これらの原料粉末が均一に分散するように回転混合機などを用いて湿式混合する方法を利用することができる。
　（２）成形工程
　成形工程は、混合工程で得られた混合粉末を成形型に投入し、加圧成形することにより予備成形体を得る工程である。なお、成形工程では、成形型を加熱する必要はなく、常温（１５℃～２５℃程度）で加圧成形する。
　成形工程における加圧力は、２５０ＭＰａ～３５０ＭＰａとすることが好ましい。また、加圧時間は、２秒間～５秒間とすることが好ましい。このような条件で加圧成形することにより、成形密度が十分に高い予備成形体を、効率的に得ることができる。
　（３）焼成工程
　焼成工程は、成形工程で得られた予備成形体とプレッシャプレートとを重ね合わせて焼成することにより、焼結体を得る工程である。
　この際、焼結温度を８００℃～１０００℃とすることが好ましい。また、加圧力を０．１ＭＰａ～２．０ＭＰａとすることが好ましい。さらに、焼成時間（焼成温度での保持時間）を１０分間～４００分間とすることが好ましい。このような条件で焼成することにより、焼結摩擦材の機械的強度を高め、制動時に生じる接線力に対する耐性を向上させることが可能となる。
　（４）加工工程
　焼成工程で得られた焼結体は、加工工程を経て、所定のサイズに調整される。この際、焼結体の加工方法は、特に制限されることはないが、たとえば、焼結体を、常温、５０ＭＰａ～９０ＭＰａ、２秒間～５秒間、サイジングした後、所定の厚さに研摩する方法が好ましい。これにより、焼結体を所定の寸法に矯正するばかりでなく、その機械的強度をさらに改善することが可能となる。
　以下、実施例および比較例を用いて本発明を具体的に説明する。
　［焼結摩擦材］
　原料粉末として表１に示すものを用意し、これらの原料粉末を表２に示すように混合することにより混合粉末を得た。この混合粉末を成形型に投入し、常温、３００ＭＰａで３秒間加圧成形することにより予備成形体を得た。次に、この予備成形体を、銅めっきした金属板（プレッシャプレート）と重ね合わせた上で、焼結炉に投入し、８００℃～１０００℃、１ＭＰａで６０分間焼成し、焼結体を得た。この焼結体を室温まで冷却し、常温、７０ＭＰａで３秒間サイジングした後、焼結体の表面を研摩し、厚さが２０ｍｍ、外形が６０ｍｍの焼結摩擦材を得た。その後、トルク受けプレートにリベットで取り付け、図１に示すようなブレーキライニング１を得た。
　［摩擦材の評価］
　上述のようにして得られたブレーキライニングを用いて、以下の条件でダイナモ試験（非常ブレーキ相当）を実施した。この結果、平均摩擦係数μａｖｅが０．３３以上かつ最小摩擦係数μｍｉｎが０．３０以上のものを「優（◎）」と、μａｖｅが０．３０以上かつμｍｉｎが０．２５以上のもの（ただし、μａｖｅが０．３３以上かつμｍｉｎが０．３０以上のものを除く）を「良（○）」と、μａｖｅが０．３０未満またはμｍｉｎが０．２５未満のものを「不良（×）」と評価した。以上の結果を表３に示す。
　また、ダイナモ試験後、断面測定機（株式会社小坂研究所製、ＳＰ－４６Ｄ）を用いて、相手材の摩耗量を測定した。この結果、相手材の摩耗量が１０μｍ未満であったものを「優（◎）」、１０μｍ以上３０μｍ未満であったものを「良（○）」、３０μｍ以上であったものを「不良（×）」と評価した。以上の結果を表３に示す。
　　（ダイナモ試験の条件）
　　・慣性モーメント　：１２１ｋｇ・ｍ２
　　・初速度　　　　　：３６５ｋｍ・ｈ－１
　　・試験回数　　　　：３回
　　・相手材　　　　　：新幹線用鍛鋼ディスクロータ
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　［総合評価］
　表１～３より、実施例１～５の焼結摩擦材は、高速域における平均摩擦係数μａｖｅを０．３０以上、かつ、摩耗量を３０μｍ未満とすることが可能であることが確認できる。特に、実施例２および３の焼結摩擦材は、相手材の摩耗量を抑制しつつ、高い摩擦特性を発揮していることが確認できる。
　これに対して、摩擦調整材としてＦｅを使用した比較例２～５の焼結摩擦材は、高速域における平均摩擦係数μａｖｅが低下していることが確認できる。これは、高速域からの減速時に発生した熱によりＦｅが酸化し、焼結摩擦材の表面に酸化鉄層が形成され、摩擦力が低下したためと考えられる。
　本発明を詳細にまた特定の実施形態を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。本出願は、２０１５年５月２８日出願の日本特許出願（特願２０１５－１０９２１４）に基づくものであり、その内容はここに参照として取り込まれる。
　１　ブレーキライニング

Claims (14)

  1. 　Ｃｕを基材とし、１体積％～２０体積％のＦｅＣｒと、５体積％～２０体積％の金属酸化物と、３０体積％～６０体積％の潤滑材とを含む、高速鉄道車両用焼結摩擦材。
  2. 　前記Ｃｕを２０体積％以上含む、請求項１に記載の高速鉄道車両用焼結摩擦材。
  3. 　前記金属酸化物は、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３から選択される１種以上である、請求項１または請求項２に記載の高速鉄道車両用焼結摩擦材。
  4. 　前記金属酸化物は、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３である、請求項３に記載の高速鉄道車両用焼結摩擦材。
  5. 　前記ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の体積比が、ＭｇＯ：ＺｒＯ２：Ａｌ２Ｏ３＝１．５～２．５：１．５～２．５：１．０である、請求項４に記載の高速鉄道車両用焼結摩擦材。
  6. 　１５体積％以下のＳｎおよびＺｎのうちの少なくとも１つをさらに含む、請求項１～５のいずれか１項に記載の高速鉄道車両用焼結摩擦材。
  7. 　基材となるＣｕ粉末に、１体積％～２０体積％のＦｅＣｒ粉末と、５体積％～２０体積％の金属酸化物粉末と、３０体積％～６０体積％の潤滑材とを混合することにより混合粉末を得る、混合工程と、
    　前記混合粉末を成形型に投入し、加圧成形することにより予備成形体を得る、成形工程と、
    　前記予備成形体とプレッシャプレートとを重ね合わせて焼成することにより、焼結体を得る、焼結工程と、
    を備える、高速鉄道車両用焼結摩擦材の製造方法。
  8. 　前記焼結体を、常温、５０ＭＰａ～９０ＭＰａで、２秒間～５秒間サイジングした後、所定の厚さに研摩する、加工工程をさらに備える、請求項７に記載の高速鉄道車両用焼結摩擦材の製造方法。
  9. 　前記金属酸化物として、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３から選択される１種以上を用いる、請求項７または８に記載の高速鉄道車両用焼結摩擦材の製造方法。
  10. 　前記金属酸化物として、ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３を用いる、請求項９に記載の高速鉄道車両用焼結摩擦材の製造方法。
  11. 　前記ＭｇＯ、ＺｒＯ２およびＡｌ２Ｏ３の体積比を、ＭｇＯ：ＺｒＯ２：Ａｌ２Ｏ３＝１．５～２．５：１．５～２．５：１．０とする、請求項１０に記載の高速鉄道車両用焼結摩擦材の製造方法。
  12. 　前記混合工程において、１５体積％以下のＳｎおよびＺｎのうちの少なくとも１つをさらに混合する、請求項７～１１のいずれか１項に記載の高速鉄道車両用焼結摩擦材の製造方法。
  13. 　前記ＦｅＣｒ粉末として、平均粒径が１０μｍ～３００μｍであるＦｅＣｒ粉末を用いる、請求項７～１２のいずれか１項に記載の高速鉄道車両用焼結摩擦材の製造方法。
  14. 　前記金属酸化物粉末として、平均粒径が５０μｍ～４００μｍである金属酸化物粉末を用いる、請求項７～１３のいずれか１項に記載の高速鉄道車両用焼結摩擦材の製造方法。
PCT/JP2016/065648 2015-05-28 2016-05-26 高速鉄道車両用焼結摩擦材とその製造方法 Ceased WO2016190403A1 (ja)