WO2020032287A1 - 感圧接着層形成性オルガノポリシロキサン組成物およびその使用 - Google Patents

感圧接着層形成性オルガノポリシロキサン組成物およびその使用 Download PDF

Info

Publication number
WO2020032287A1
WO2020032287A1 PCT/JP2019/031810 JP2019031810W WO2020032287A1 WO 2020032287 A1 WO2020032287 A1 WO 2020032287A1 JP 2019031810 W JP2019031810 W JP 2019031810W WO 2020032287 A1 WO2020032287 A1 WO 2020032287A1
Authority
WO
WIPO (PCT)
Prior art keywords
sensitive adhesive
component
adhesive layer
pressure
organopolysiloxane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/031810
Other languages
English (en)
French (fr)
Inventor
伊藤　真樹
昭宏 中村
通孝 須藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Toray Co Ltd
Original Assignee
Dow Toray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Toray Co Ltd filed Critical Dow Toray Co Ltd
Priority to CN201980058011.6A priority Critical patent/CN112654687B/zh
Priority to JP2020535942A priority patent/JP7046198B2/ja
Priority to KR1020217006971A priority patent/KR102532824B1/ko
Priority to US17/267,379 priority patent/US12509614B2/en
Priority to EP19846409.1A priority patent/EP3835387A4/en
Publication of WO2020032287A1 publication Critical patent/WO2020032287A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

［課題］低温において貯蔵弾性率(G')を幅広い範囲で設計可能であり、かつ、硬化性に優れ、実用上十分な粘着力を有する感圧接着層を形成する、硬化反応性のオルガノポリシロキサン組成物およびその用途を提供する。 ［解決手段］（Ａ）アルケニル基を有する鎖状オルガノポリシロキサン、（Ｂ）水酸基等の含有量が９モル％以下のオルガノポリシロキサンレジンであって、(b1) 分子量（Ｍｗ）が４５００以上のもの、（ｂ２）分子量（Ｍｗ）が４５００未満のものの混合物、（Ｃ）オルガノハイドロジェンポリシロキサン、および（Ｄ）ヒドロシリル化反応触媒を含有してなり、（Ａ）成分に対する（Ｂ）成分の質量比が０．９～３．０の範囲にあり、当該組成物の硬化により得られる感圧接着層の－２０℃におけるせん断貯蔵弾性率G'が０．７７～５０．００ＭＰａの範囲にある感圧接着層形成性オルガノポリシロキサン組成物。

Description

感圧接着層形成性オルガノポリシロキサン組成物およびその使用
本発明は、感圧接着層を形成する硬化反応性のオルガノポリシロキサン組成物に関する。詳細には、本発明は、実用上十分な硬化性および粘着を有し、かつ、低温を含む幅広い温度領域において、せん断貯蔵弾性率G’が０．７７以上の幅広い領域で弾性率を設計することができる、硬化反応性のオルガノポリシロキサン組成物に関するものである。また、本発明は、当該組成物を用いる感圧接着剤組成物、当該組成物を用いた積層体、電子部品または表示装置（フレキシブルディスプレイやタッチパネル等含む）等の用途に関する。
ポリシロキサン系感圧接着剤組成物は、アクリル系やゴム系の感圧接着剤組成物と比較して、電気絶縁性、耐熱性、耐寒性、各種被着体に対する粘着性に優れるので、耐熱性粘着テープ、電気絶縁性粘着テープ、ヒートシールテープ、メッキマスキングテープ等に使用されている。これらのポリシロキサン系感圧接着剤組成物は、その硬化機構により、付加反応硬化型、縮合反応硬化型、パーオキサイド硬化型などに分類される。室温放置もしくは加熱によって速やかに硬化し、副生物を発生しないので、付加反応硬化型の感圧接着剤組成物が汎用されている。
ポリシロキサン系感圧接着剤の上記特性および必要に応じて高い透明性を実現できる性質を生かし、近年、スマートデバイス等の先端エレクトロニクス材料および表示素子分野への応用が検討されている。このようなデバイスは、電極層、表示層を含む複数層からなるフィルムを透明基材の間に挟みこんだ構造をとっており、電極層、表示層の保護および層間の接着性改良を目的に、耐熱・耐寒性に優れるポリシロキサン系感圧接着剤が有効に作用することが期待される。
特に近年の材料開発においては、－２０℃等の低温を含む幅広い温度領域において、貯蔵弾性率(たとえばせん断貯蔵弾性率G’)の設計の自由度が高く、かつ、硬化性に優れ、実用上十分な粘着力を有するポリシロキサン系感圧接着剤組成物が求められているが、公知の文献等に記載された感圧接着剤組成物はこれらの特性を十分に満足するものではなく、未だ、改善の余地を残している。
例えば、特許文献１には、粘着ゴムシートが開示されているが、そのレジン成分およびシロキサンポリマー成分の比率においてレジン成分の含有量が少なく、分子量や水酸基の含有量等の特定の性質を備えたレジン成分を組み合わせて使用することはなんら記載も示唆もされていない。さらに、当該粘着ゴムシートは微粉末シリカ等を使用しており、本発明の目的とする貯蔵弾性率(G’)を充足するものではない。
同様に、特許文献２には、数平均分子量９５０～１６００のオルガノポリシロキサンレジンを用いるシリコーン感圧接着剤が開示されているが、特に分子量において異なり、かつ、水酸基の含有量等の特定の性質を備えたレジン成分を組み合わせて使用することはなんら記載も示唆もされていない。さらに、当該シリコーン感圧接着剤は、一定の粘着力を有するものであるが、本発明の目的とする貯蔵弾性率(G’)を充足するものではない。
一方、特許文献３には、ポリマー成分に対するレジン成分の物質量比が０．５～１．０の範囲であり、低温および室温における貯蔵弾性率G’の差が小さいことを特徴とする透明樹脂接着層を備えた積層体が提案されている。しかしながら、当該透明樹脂接着層は縮合反応性のものしか具体的に開示されておらず、工業的に利用するには硬化反応が遅過ぎるという問題がある。さらに、当該透明樹脂接着層は、本発明の目的とする貯蔵弾性率(G’)および実用上十分な粘着力を充足するものではない。
ここで、本件出願人らは、特許文献４においてフレキシブル積層体用途において、十分な弾性率と損失係数（tanδ）を有する硬化層を形成可能な硬化性シリコーン組成物を提案している。しかしながら、その実施例等で具体的に開示された組成は、その一部において、重量平均分子量の異なるレジン成分の組み合わせを開示するものであるが、本発明の課題を十分に解決できるものではない。
特開２００６－２２５４２０号公報 特開平０５－２１４３１６号公報 国際特許公開２０１７－０８２６５４号公報 国際特許公開２０１７－１８８３０８号公報
本発明は上記課題を解決すべくなされたものであり、貯蔵弾性率(G’)の設計の自由度が高く、かつ、硬化性に優れ、実用上十分な粘着力を有する感圧接着層を形成する、硬化反応性のオルガノポリシロキサン組成物を提供することを目的とする。さらに、本発明は、当該硬化反応性のオルガノポリシロキサン組成物またはその硬化物の、感圧接着層としての使用、広汎な用途における弾性粘着部材としての使用およびそれらを備えた機器または装置を提供することを目的とする。
本発明者らは上記課題について鋭意検討した結果、本発明に到達した。すなわち、本発明の目的の一つは、ヒドロシリル化反応硬化性の感圧接着層形成性オルガノポリシロキサン組成物において、分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、分子量範囲の異なる２種類以上のオルガノポリシロキサンレジンを併用し、鎖状オルガノポリシロキサンに対するオルガノポリシロキサンレジンの質量比を０．９～３．０の範囲に調整し、かつ、当該組成物の硬化により得られる感圧接着層の－２０℃におけるせん断貯蔵弾性率G’が０．７７～５０．００ＭＰａの範囲にある感圧接着層形成性オルガノポリシロキサン組成物により達成される。また、上記課題は、当該硬化反応性のオルガノポリシロキサン組成物またはその硬化物の、感圧接着層としての使用、電子材料または表示装置用部材としての使用およびそれらを備えた電子部品または表示装置により達成されうる。
すなわち、本発明は、
「［１］（Ａ）分子内に平均して１を超える数のアルケニル基を有する鎖状オルガノポリシロキサン、
（Ｂ）以下の（ｂ１）成分および（ｂ２）成分を１：９９～９９：１の質量比で含む、オルガノポリシロキサンレジン混合物：
（ｂ１）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００以上であるオルガノポリシロキサンレジン、
（ｂ２）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００未満であるオルガノポリシロキサンレジン
（Ｃ）分子内に少なくとも２個のＳｉ－Ｈ結合を有するオルガノハイドロジェンポリシロキサン、および
（Ｄ）有効量のヒドロシリル化反応触媒
を含有してなり、（Ａ）成分に対する（Ｂ）成分の質量比が０．９～３．０の範囲にあり、当該組成物の硬化により得られる感圧接着層の－２０℃におけるせん断貯蔵弾性率G’が０．７７～５０．００ＭＰａの範囲にある感圧接着層形成性オルガノポリシロキサン組成物
［２］当該組成物の硬化により得られる厚み５０μｍの感圧接着層の、厚み２ｍｍのポリメチルメタクリレートシートに対する、ＪＩＳ Ｚ ０２３７に従う１８０°引き剥がし試験方法を用いて引張速度300ｍｍ/minにより測定された粘着力が９００～４０００ｇｆ／ｉｎｃｈの範囲であることを特徴とする、［１］に記載の感圧接着層形成性オルガノポリシロキサン組成物。

［３］（Ａ）成分の少なくとも一部が、（Ａ１）２５℃において１００，０００ｍＰａ・ｓ以上の粘度を有するか、ＪＩＳ　Ｋ６２４９に規定される方法に準じて測定された可塑度が５０～２００の範囲にある生ゴム状のアルケニル基含有オルガノポリシロキサンであり、そのアルケニル基中のビニル（ＣＨ２＝ＣＨ）部分の含有量が０．００５～０．４００質量％の範囲にある鎖状オルガノポリシロキサンであり、
（Ｂ）成分であるオルガノポリシロキサンレジン混合物が、Ｒ３ＳｉＯ１／２単位（式中、Ｒは一価有機基であり、Ｒの９０モル％以上が炭素数１～６のアルキル基またはフェニル基である；Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）から実質的になるオルガノポリシロキサンレジン混合物であり
（Ｃ）成分の量が、上記の（Ａ）成分中および（Ｂ）成分中のアルケニル基の物質量の和に対する（Ｃ）成分中のＳｉＨ基の物質量の比（モル比）が０．１～１００となる量であり、
（Ｄ）成分の量が、組成物中の固形分中の白金系金属の含有量が０．１～２００ｐｐｍの範囲である、［１］または［２］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物。
［４］（Ｃ）成分の量が、上記の（Ａ）成分中および（Ｂ）成分中のアルケニル基の物質量の和に対する（Ｃ）成分中のＳｉＨ基の物質量の比（モル比）が２０～６０となる量である［１］～［３］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物。
［５］さらに、（Ａ´）分子内に炭素－炭素二重結合含有反応性基を含まない鎖状オルガノポリシロキサンを含む、［１］～［４］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物
［６］［１］～［５］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる感圧接着剤層。
［７］フィルム状基材上に、［１］～［５］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる感圧接着剤層を備えた積層体。
［８］１または２以上のフィルム状基材に当該感圧接着剤層に対する剥離層が設けられている、［７］に記載の積層体。
［９］フィルム状基材、
該フィルム状基材上に形成された第１剥離層、
該剥離層上に［１］～［５］のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を塗工し硬化させて形成された感圧接着層、及び
該感圧接着層上に積層された第２剥離層
を含む、［７］または［８］の積層体。
［１０］［１］～［５］のいずれか１項記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる、弾性粘着部材。
［１１］［１０］に記載の弾性粘着部材を含む電子機器または電気的装置。」
である。
本発明の感圧接着層形成性オルガノポリシロキサン組成物は、ヒドロシリル化反応による硬化性に優れ、硬化して、実用上十分な接着力を備え、かつ、貯蔵弾性率(G’) の設計の自由度が高く、－２０℃におけるせん断貯蔵弾性率G’が０．７７以上の幅広い領域で弾性率を設計することができ、実用上十分な接着性を有する感圧接着層を形成することができる。さらに、当該硬化反応性のオルガノポリシロキサン組成物またはその硬化物は、感圧接着層、電子材料または表示装置用部材として好適に使用することができ、それらを備えた電気・電子部品または表示装置は、上記の要求特性を充足して硬化不良の問題、低温を含めた幅広い温度領域における接着層の粘弾性が十分と成るので、低温から室温を含む温度領域において、電子部品等の基材に対する密着不良の問題を生じにくい感圧接着層を形成することができるため、工業化が容易であり、かつ、得られる表示デバイス等の積層体の性能改善が期待されるという利点を有する。
［感圧接着層形成性オルガノポリシロキサン組成物］
まず、本発明にかかる感圧接着層形成性オルガノポリシロキサン組成物について説明する。当該組成物は、ヒドロシリル化反応を含む硬化反応により速やかに硬化し、貯蔵弾性率(G’) の設計の自由度が高く、－２０℃におけるせん断貯蔵弾性率G’が０．７７以上の幅広い領域で弾性率を設計することができ、実用上十分な粘着力を有する感圧接着層を形成するものである。以下、その各構成成分、技術的特徴であるオルガノポリシロキサンレジン混合物の範囲、その鎖状オルガノポリシロキサンに対するオルガノポリシロキサンレジンの質量比、および感圧接着層の特性について説明する。
本発明のオルガノポリシロキサン組成物は、上記のとおり、ヒドロシリル化反応により硬化して一定の粘着力を有する感圧接着層を形成するものであり、当該組成において、分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、分子量範囲の異なるオルガノポリシロキサンレジンの混合物を使用し、かつ、主剤であるアルケニル基を有する鎖状オルガノポリシロキサンに対するオルガノポリシロキサンレジンの配合の範囲が特定の範囲にある。当該特徴を有する組成物の硬化により得られる感圧接着層は、－２０℃におけるせん断貯蔵弾性率G’が０．７７～５０．００ＭＰａの範囲であり、好適には、さらに、一定の粘着力を有するものである。
具体的には、本発明のオルガノポリシロキサン組成物は、
（Ａ）分子内に平均して１を超える数のアルケニル基を有する鎖状オルガノポリシロキサン、
（Ｂ）以下の（ｂ１）成分および（ｂ２）成分を１：９９～９９：１の質量比で含む、オルガノポリシロキサンレジン混合物：
（ｂ１）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００以上であるオルガノポリシロキサンレジン、
（ｂ２）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００未満であるオルガノポリシロキサンレジン
（Ｃ）分子内に少なくとも２個のＳｉ－Ｈ結合を有するオルガノハイドロジェンポリシロキサン、および
（Ｄ）有効量のヒドロシリル化反応触媒
を含有してなる。また、当該組成物は、ヒドロシリル化反応触媒を含むので、取扱作業性の見地から、さらに、（Ｅ）硬化遅延剤を含有してもよく、本発明の目的に反しない範囲で、その他の添加剤を含むものであってよい。以下、各成分について説明する。
（Ａ）成分のアルケニル基含有オルガノポリシロキサンは、鎖状のポリシロキサン分子であり、この組成物の主剤（ベースポリマー）であり、１分子中に平均して１を超える数のケイ素原子に結合したアルケニル基を含有し、好適なアルケニル基の個数は、１分子中に１．５個以上である。（Ａ）成分のオルガノポリシロキサンのアルケニル基としては、例えば、ビニル基、アリル基、ブテニル基、ペンテニル基、ヘキセニル基、ヘプテニル基などの炭素数２～１０のアルケニル基が挙げられ、特にビニル基またはヘキセニル基であることが好ましい。（Ａ）成分のアルケニル基の結合位置としては、例えば、分子鎖末端及び／又は分子鎖側鎖が挙げられる。なお、（Ａ）成分は、単一の成分のみを含んでいてもよく、２種以上の異なった成分の混合物であってもよい。
（Ａ）成分のオルガノポリシロキサンにおいて、アルケニル基以外のケイ素原子に結合した有機基としては、例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基等のアルキル基；フェニル基、トリル基、キシリル基、ナフチル基等のアリール基；ベンジル基、フェネチル基等のアラルキル基；クロロメチル基、３－クロロプロピル基、３，３，３－トリフロロプロピル基等のハロゲン化アルキル基などが挙げられ、特に、メチル基、フェニル基であることが好ましい。
（Ａ）成分は（Ｂ）成分と異なり、鎖状のポリシロキサン分子構造を有する。例えば、（Ａ）成分は、直鎖状、一部分岐を有する直鎖状（分岐鎖状）であることが好ましく、一部に環状、三次元網状を含んでいても良い。好適には、主鎖がジオルガノシロキサン単位の繰り返しからなり、分子鎖両末端がトリオルガノシロキシ基で封鎖された、直鎖状または分岐鎖状のジオルガノポリシロキサンであることが好ましい。なお、分岐鎖状のオルガノポリシロキサンを与えるシロキサン単位は後述するＴ単位またはＱ単位である。
（Ａ）成分の室温における性状はオイル状または生ゴム状であってもよく、（Ａ）成分の粘度は２５℃において５０ｍＰａ・ｓ以上、特に１００ｍＰａ・ｓ以上であることが好ましい。特に、本発明にかかるオルガノポリシロキサン組成物が溶剤型である場合には、（Ａ）成分の少なくとも一部は、（Ａ１）２５℃において１００，０００ｍＰａ・ｓ以上の粘度を有するか、ＪＩＳ　Ｋ６２４９に規定される方法に準じて測定された可塑度（２５℃、４.２ｇの球状試料に１ｋｇｆの荷重を３分間かけたときの厚さを1/100mmまで読み、この数値を100倍したもの）が５０～２００の範囲にある、さらに好ましくは８０～１８０の範囲にある生ゴム状のアルケニル基含有オルガノポリシロキサンであることが好ましい。
なお、これらのアルケニル基含有オルガノポリシロキサンは、接点障害防止等の見地から、揮発性または低分子量のシロキサンオリゴマー（オクタメチルテトラシロキサン（Ｄ４）、デカメチルペンタシロキサン（Ｄ５）等）が低減ないし除去されていることが好ましい。その程度は所望により設計可能であるが、成分（Ａ）全体の１質量％未満、各シロキサンオリゴマーについて０．１質量％未満としてもよく、必要に応じ、検出限界付近まで低減してもよい。
前記の（Ａ１）成分中のアルケニル基の含有量は特に限定されるものではないが、本発明の技術的効果の見地から、（Ａ１）成分中のアルケニル基中のビニル（ＣＨ２＝ＣＨ）部分の含有量（以下、「ビニル含有量」という）が、０．００５～０．４００質量％の範囲が好ましく、０．００５～０．３００質量％の範囲が特に好ましい。
本発明の（Ａ）成分として、前記の（Ａ１）成分より低粘度の（Ａ）成分であっても、利用可能であり、具体的には、（Ａ２）２５℃における粘度が１００，０００ｍＰａ・ｓ未満のアルケニル基含有オルガノポリシロキサンが利用可能である。ここで、（Ａ２）成分の粘度以外の例示は、（Ａ１）成分と同様である。
本発明の技術的効果の見地から、（Ａ）成分の５０質量％以上が、（Ａ１）成分である高重合度のアルケニル基含有オルガノポリシロキサンであることが好ましく、７５～１００質量％が（Ａ１）成分であることが特に好ましい。すなわち、本発明の（Ａ）成分として前記の（Ａ１）成分（＝高重合度のアルケニル基含有オルガノポリシロキサン）と（Ａ２）成分（＝より低重合度のアルケニル基含有オルガノポリシロキサン）を併用する場合には、両者の質量比が５０：５０～１００：０、より好適には７５：２５～１００：０または７５：２５～９０：１０の範囲である。
（Ｂ）オルガノポリシロキサンレジン混合物は、本発明の特徴的な構成の一つであり、基材への粘着力を付与する粘着付与成分であると同時に、（Ａ）成分と一定の比率で使用することにより、本発明の目的である低温における貯蔵弾性率および実用的な粘着力範囲を実現する成分である。より具体的には、（Ｂ）成分は、水酸基または加水分解性基の含有量が抑制された、平均分子量の異なるオルガノポリシロキサンレジンの混合物であり、（Ｂ）成分間での加水分解／重合反応が起こりにくく、かつ、平均分子量の異なるレジンを組み合わせて使用することで、その硬化物である感圧接着層における所定の貯蔵弾性率および実用的な粘着力範囲を実現する。
詳細には、（Ｂ）成分は、以下の（ｂ１）成分および（ｂ２）成分を１：９９～９９：１の質量比で含む、オルガノポリシロキサンレジン混合物である。
（ｂ１）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００以上であるオルガノポリシロキサンレジン、
（ｂ２）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００未満であるオルガノポリシロキサンレジン
本発明における（Ｂ）成分、すなわち、（ｂ１）成分および（ｂ２）成分は、共通する性質として、その分子内における水酸基および加水分解性基の含有量の和が、当該オルガノポリシロキサンレジン分子中の全ケイ素原子に対して９モル％以下の範囲であり、分子中の全ケイ素原子に対して７モル％以下であることが好ましい。なお、（Ｂ）成分において、かかる水酸基および加水分解性基の含有量は、これらの官能基を全て水酸基に換算して表現することもできる。この場合、当該オルガノポリシロキサンレジン分子中の水酸基以外の加水分解性基を全て水酸基（ＯＨ）であると仮定してその質量％を計算すると、上記の水酸基および加水分解性基の含有量の和は、当該オルガノポリシロキサンレジン分子中における水酸基および水酸基に換算したこれらの加水分解性基の含有量の和が２．０質量％以下であり、１．６質量％以下が好ましいと表現することもできる。水酸基または加水分解性基は、後述するレジン構造中のシロキサン単位のうち、Ｔ単位またはＱ単位などのケイ素に直接結合しており、原料となるシラン由来またはシランが加水分解した結果、生じた基であるので、合成したオルガノポリシロキサンレジンをトリメチルシラン等のシリル化剤で加水分解処理することで水酸基または加水分解性基の含有量を低減することができる。
（ｂ１）成分および（ｂ２）成分において、当該水酸基または加水分解性基の量が前記の上限を超えると、オルガノポリシロキサンレジン分子間の縮合反応が進行して、硬化物中において分子量の大きいオルガノポリシロキサンレジン構造が形成されやすくなる。このような分子量の大きいオルガノポリシロキサンレジンは、組成物全体の硬化性を損なう傾向があり、当該組成物の低温における硬化性が不十分となったり、得られる感圧接着層が実用上十分な貯蔵弾性率を有しなくなる場合がある。
（ｂ１）成分および（ｂ２）成分は、共にオルガノポリシロキサンレジンであり、三次元構造を有するオルガノポリシロキサンである。例えば、Ｒ２ＳｉＯ２／２単位（Ｄ単位）及びＲＳｉＯ３／２単位（Ｔ単位）（式中、Ｒは互いに独立した一価有機基を表す）からなり、水酸基または加水分解性基の含有量が上記範囲にあるレジン、Ｔ単位単独からなり、水酸基または加水分解性基の含有量が上記範囲にあるレジン、並びにＲ３ＳｉＯ１／２単位（Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）からなり、水酸基または加水分解性基の含有量が上記範囲にあるレジンなどを挙げることができる。特に、Ｒ３ＳｉＯ１／２単位（Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）からなり、分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が０～７モル％（これらの官能基を全て水酸基に換算した場合、０．０～１．６質量％であることが好ましい）の範囲であるレジン（ＭＱレジンとも呼ばれる）を使用することが好ましい。
Ｒの一価有機基は、好ましくは炭素数１～１０の一価炭化水素基であり、炭素数１～１０のアルキル基、炭素数２～１０のアルケニル基、炭素数６～１０のアリール基、炭素数６～１０のシクロアルキル基、ベンジル基、フェニルエチル基、及びフェニルプロピル基が例示される。特に、Ｒの９０モル％以上が炭素数１～６のアルキル基またはフェニル基であることが好ましく、Ｒの９５～１００モル％がメチル基またはフェニル基であることが特に好ましい。
（ｂ１）成分および（ｂ２）成分が、Ｒ３ＳｉＯ１／２単位（Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）からなるレジンである場合、Ｍ単位対Ｑ単位のモル比は、０．５～２．０であることが好ましい。このモル比が０．５未満である場合には基材への粘着力が低下することがあり、２．０より大きい場合には粘着層を構成する物質の凝集力が低下するからである。また、本発明の特性を損なわない範囲で、Ｄ単位及びＴ単位を（Ｂ）成分中に含有させることも可能である。さらに、これらのオルガノポリシロキサンレジンは、接点障害防止等の見地から、低分子量のシロキサンオリゴマーが低減ないし除去されていても良い。
（ｂ１）成分および（ｂ２）成分であるオルガノポリシロキサンレジンは、その重量平均分子量（Ｍｗ）において互いに異なる。ここで、重量平均分子量（Ｍｗ）は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される各々のオルガノポリシロキサンレジンにおいて、個々の分子が全体に占める割合を考慮した平均分子量である。
（ｂ１）成分は、分子量の大きいオルガノポリシロキサンレジンであり、その重量平均分子量（Ｍｗ）は、４５００以上であり、５０００以上が好ましく、５５００以上が特に好ましい。実用上、（ｂ１）成分は、重量平均分子量（Ｍｗ）が５０００～１００００の範囲にある、上述のＲ３ＳｉＯ１／２単位（Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）からなるレジンが特に好適である。
（ｂ２）成分は、分子量の小さいオルガノポリシロキサンレジンであり、その重量平均分子量（Ｍｗ）は、４５００未満であり、４０００以下が好ましく、３７５０以下が特に好ましい。実用上、（ｂ１）成分は、重量平均分子量（Ｍｗ）が５００～３７５０の範囲にある、上述のＲ３ＳｉＯ１／２単位（Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）からなるレジンが特に好適である。
（Ｂ）成分は、上記の（ｂ１）成分および（ｂ２）成分を１：９９～９９：１の質量比で含む、オルガノポリシロキサンレジン混合物であり、その混合比は、特に制限されるものではないが、組成や粘弾性の設計に応じて、５：９５～９５：５の範囲であってよく、１０：９０～９０：１０の範囲であってよく、１５：８５～８５：１５となる範囲であってもよい。一方、本発明は、２種以上の分子量の異なるレジン成分を実質的に組み合わせて使用することに特徴があり、（Ｂ）成分がこれらの分子量の異なるオルガノポリシロキサンレジンの混合物でなかったり、混合比が前記の上下限の外側であると、仮にレジン成分の水酸基または加水分解性基の含有量が２．０質量％以下であっても、本発明の目的とする硬化性、粘着力および貯蔵弾性率等の特性が実現できない場合がある。
［（Ａ）成分に対する（Ｂ）成分の質量比］
本発明に係る感圧接着層形成性オルガノポリシロキサン組成物は、鎖状の反応性シロキサン成分である（Ａ）成分に対する、オルガノポリシロキサンレジンである（Ｂ）成分の質量比が０．９～３．０の範囲にあることを特徴とする。（Ｂ）成分として、上記の特徴的なオルガノポリシロキサンレジン混合物を選択し、かつ、鎖状のシロキサンポリマー成分に対して上記のレジン成分が前記範囲となるように配合されていると、本発明の目的とする硬化性、粘着力および貯蔵弾性率等の特性が好適に実現されるためである。特に、（Ａ）成分に対する、（Ｂ）成分の質量比は１．１～３．０の範囲であってよく、所望の
粘着力および貯蔵弾性率を実現するために、１．５以上、あるいは２．０以上であってもよい。一方、（Ａ）成分に対する、（Ｂ）成分の質量比が前記範囲外であると、他の構成を調整しても本発明の目的とする硬化性、粘着力および貯蔵弾性率等の特性が実現できない場合がある。
（Ｃ）成分は、Ｓｉ－Ｈ結合を分子中に２個以上有するオルガノハイドロジェンポリシロキサンであり、本発明にかかるオルガノポリシロキサン組成物の架橋剤である。成分（Ｃ）の分子構造は限定されず、例えば、直鎖状、一部分岐を有する直鎖状、分岐鎖状、環状、あるいはオルガノポリシロキサンレジンであることが挙げられ、好ましくは、直鎖状、一部分岐を有する直鎖状、あるいはオルガノポリシロキサンレジンである。ケイ素原子結合水素原子の結合位置は特に限定されず、分子鎖末端，側鎖，これら両方が例示される。
ケイ素原子結合水素原子の含有量は０.１～２．０質量％であることが好ましく、０.５～１.７質量％であることがより好ましい。
ケイ素原子に結合する有機基として、メチル基，エチル基，プロピル基，ブチル基，オクチル基等の炭素原子数１～８のアルキル基；フェニル基，トリル基などのアリール基；ベンジル基、フェネチル基などのアラルキル基；３－クロロプロピル基、３,３,３－トリフロロプロピル基等のハロゲン化アルキル基が例示されるが、それらの合計数の５０モル％以上が炭素原子数１～８のアルキル基またはフェニル基であることが好ましい。製造容易性および前記した好ましい（Ａ）成分、（Ｂ）成分との相溶性の点で他の有機基はメチル基またはフェニル基が好ましい。
本発明にかかる（Ｃ）成分がオルガノポリシロキサンレジンであるオルガノハイドロジェンポリシロキサンである場合は、一般式：Ｒ'３ＳｉＯ１/２で表されるシロキサン単位と一般式：Ｒ'２ＨＳｉＯ１/２で表されるシロキサン単位と式：ＳｉＯ４/２で表されるシロキサン単位からなるオルガノポリシロキサン共重合体、一般式：Ｒ'２ＨＳｉＯ１/２で表されるシロキサン単位と式：ＳｉＯ４/２で表されるシロキサン単位からなるオルガノポリシロキサン共重合体、一般式：Ｒ'２ＨＳｉＯ１/２で表されるシロキサン単位と式：R’ＳｉＯ３/２で表されるシロキサン単位からなるオルガノポリシロキサン共重合体、一般式：Ｒ'ＨＳｉＯ２/２で表されるシロキサン単位と一般式：Ｒ'ＳｉＯ３/２で表されるシロキサン単位または式：ＨＳｉＯ３/２で表されるシロキサン単位からなるオルガノポリシロキサン共重合体、およびこれらのオルガノポリシロキサンの二種以上の混合物が例示される。なお、式中のＲ'は炭素数１～８のアルキル基、アリール基、アラルキル基、またはハロゲン化アルキル基であり、上記同様の基が例示される。
（Ｃ）成分として、具体的には、トリス（ジメチルハイドロジェンシロキシ）メチルシラン，テトラ（ジメチルハイドロジェンシロキシ）シラン、両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン，両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体，両末端ジメチルハイドロジェンシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体，環状メチルハイドロジェンオリゴシロキサン，環状メチルハイドロジェンシロキサン・ジメチルシロキサン共重合体，分子鎖両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン・ジメチルシロキサン共重合体、トリメトキシシランの加水分解縮合物、(ＣＨ３)２ＨＳiＯ１/２単位とＳiＯ４/２単位とからなる共重合体、(ＣＨ３)２ＨＳiＯ１/２単位とＳiＯ４/２単位と(Ｃ６Ｈ５)ＳiＯ３/２単位とからなる共重合体、(ＣＨ３)２ＨＳiＯ１/２単位とＣＨ3ＳiＯ３/２単位とからなる共重合体、およびこれらの２種以上の混合物が例示される。
直鎖状の場合は特に、分子構造式：RTMe2SiO (Me 2SiO)q (H Me SiO)r Si Me2RT   （７）
（式中、Meはメチル基であり、RTはメチル基または水素原子であり、ｑ，ｒは０.３≦r/(q+r)≦１、５≦ (q+r)≦２００の関係を満たす数である。）で示されるメチルハイドロジェンポリシロキサンが好ましい。なお、上記（Ｃ）成分は異なるもの２種以上を併用してもよい。
同様に、次のようなオルガノシロキサンも例示される。なお、式中、Ｍe、Ｐhは、それぞれ、メチル基、フェニル基を示し、ｍは１～１００の整数であり、ｎは１～５０の整数であり、ｂ、ｃ、ｄ、ｅはそれぞれ正の数であり、ただし、一分子中のｂ、ｃ、ｄ、ｅの合計は１である。
ＨＭe２ＳiＯ(Ｐh２ＳiＯ)ｍＳiＭe２Ｈ
ＨＭeＰhＳiＯ(Ｐh２ＳiＯ)ｍＳiＭeＰhＨ
ＨＭeＰhＳiＯ(Ｐh２ＳiＯ)ｍ(ＭeＰhＳiＯ)ｎＳiＭeＰhＨ
ＨＭeＰhＳiＯ(Ｐh２ＳiＯ)ｍ(Ｍe２ＳiＯ)ｎＳiＭeＰhＨ
(ＨＭe２ＳiＯ１/２)ｂ(ＰhＳiＯ３/２)ｃ
(ＨＭeＰhＳiＯ１/２)ｂ(ＰhＳiＯ３/２)ｃ
(ＨＭeＰhＳiＯ１/２)ｂ(ＨＭe２ＳiＯ１/２)ｃ(ＰhＳiＯ３/２)ｄ
(ＨＭe２ＳiＯ１/２)ｂ(Ｐh２ＳiＯ２/２)ｃ(ＰhＳiＯ３/２)ｄ
(ＨＭeＰhＳiＯ１/２)ｂ(Ｐh２ＳiＯ２/２)ｃ(ＰhＳiＯ３/２)ｄ
(ＨＭeＰhＳiＯ１/２)ｂ(ＨＭe２ＳiＯ１/２)ｃ(Ｐh２ＳiＯ２/２)ｄ(ＰhＳiＯ３/２)ｅ
［ＳｉＨ／Ｖｉ比］
本発明の組成物は、ヒドロシリル化反応硬化性であり、（Ｃ）成分の使用量は、組成物がヒドロシリル化反応により十分に硬化することができれば特に制限されるものではないが、組成物中の（Ａ）成分中のアルケニル基の量（物質量）および（Ｂ）成分中のアルケニル基の量（物質量）の和に対する（Ｃ）成分中のケイ素原子結合水素原子（ＳｉＨ）基の物質量、すなわちモル比が０．１～１００の範囲であることが好ましく、０．５～６０の範囲、１．０～５０の範囲、または１．０～４０の範囲であっても良い。
一方、ガラス等の基材に対する密着性を改善する目的で、ＳｉＨ基の量を１０以上、または２０以上に設計することができ、かつ、２０を超えることが好ましく、２２以上であることがより好ましい。例えば、組成物中の（Ａ）成分中のアルケニル基の量（物質量）および（Ｂ）成分中のアルケニル基の量（物質量）の和に対する（Ｃ）成分中のケイ素原子結合水素原子（ＳｉＨ）基の物質量は、２０～６０の範囲、２２～５０の範囲に設計することができる。ＳｉＨ基の量が前記下限を下回ると、基材への密着性の改善という技術的効果が実現できない場合がある。一方、ＳｉＨ基の量が前記上限を超えると、反応せずに残存する硬化剤の量が多くなってしまい、硬化物が脆くなる等の硬化物性における悪影響やガスの発生等の問題が生じる場合がある。ただし、組成物のＳｉＨ／Ｖｉ比が上記範囲外でも実用上十分な感圧接着層を形成することができる。
［ヒドロシリル化反応触媒］
本発明にかかるオルガノポリシロキサン組成物は、ヒドロシリル化反応触媒を含む。ヒドロシリル化反応触媒としては、白金系触媒、ロジウム系触媒、パラジウム系触媒が例示され、本組成物の硬化を著しく促進できることから白金系触媒が好ましい。この白金系触媒としては、白金微粉末、塩化白金酸、塩化白金酸のアルコール溶液、白金－アルケニルシロキサン錯体、白金－オレフィン錯体、白金－カルボニル錯体が例示され、特に、白金－アルケニルシロキサン錯体が好ましい。このアルケニルシロキサンとしては、１,３－ジビニル－１,１,３,３－テトラメチルジシロキサン、１,３,５,７－テトラメチル－１,３,５,７－テトラビニルシクロテトラシロキサン、これらのアルケニルシロキサンのメチル基の一部をニトリル類、アミド類、ジオキソラン類、及びスルホラン類からなる群から選択される基、エチル基、フェニル基等で置換したアルケニルシロキサン、これらのアルケニルシロキサンのビニル基をアリル基、ヘキセニル基等で置換したアルケニルシロキサンが例示される。特に、この白金－アルケニルシロキサン錯体の安定性が良好であることから、１,３－ジビニル－１,１,３,３－テトラメチルジシロキサンであることが好ましい。なお、ヒドロシリル化反応を促進する触媒としては、鉄、ルテニウム、鉄／コバルトなどの非白金系金属触媒を用いてもよい。
本発明において、ヒドロシリル化反応触媒の含有量は特に制限されるものではないが、組成物中の固形分の合計量に対し、白金系金属量が０．１～２００ｐｍの範囲となる範囲であり、０．１～１５０ｐｐｍ、０．１～１００ｐｐｍの範囲であってよく、０．１～５０ｐｐｍの範囲であってもよい。ここで、白金系金属は、白金、ロジウム、パラジウム、ルテニウム、イリジウムからなるVIII族の金属元素であるが、実用上、ヒドロシリル化反応触媒の配位子を除いた白金金属の含有量が上記範囲であることが好ましい。なお、固形分とは、本発明にかかるオルガノポリシロキサン組成物を硬化反応させた場合に、硬化層を形成する成分（主として主剤、接着付与成分、架橋剤、触媒およびその他の不揮発性成分）であり、加熱硬化時に揮発する溶媒等の揮発性成分を含まない。
本発明にかかるオルガノポリシロキサン組成物中の白金系金属の含有量が５０ｐｐｍ以下（４５ｐｐｍ以下，３５ｐｐｍ以下，３０ｐｐｍ以下，２５ｐｐｍ以下または２０ｐｐｍ以下）である場合、硬化後、あるいは加熱や紫外線等の高エネルギー線に暴露した場合、特に、透明な感圧接着層の変色や着色を抑制できる場合がある。一方、オルガノポリシロキサン組成物の硬化性の見地から、白金系金属の含有量は、０．１ｐｐｍ以上であり、当該下限を下回ると硬化不良の原因となる場合がある。
（Ｅ）成分は硬化遅延剤であり、組成物中のアルケニル基と（Ｃ）成分中のＳｉＨ基の架橋反応を抑制して、常温での可使時間を延長し、保存安定性を向上するために配合するものである。したがって、実用上は、本発明の感圧接着層形成性オルガノポリシロキサン組成物にとって、必須に近い成分である。
具体的には、（Ｅ）成分はアセチレン系化合物、エンイン化合物、有機窒素化合物、有機燐化合物、オキシム化合物が例示される。具体的には、３－メチル－１－ブチン－３－オール、３,５－ジメチル－１－ヘキシン－３－オール、３－メチル－１－ペンチン－３－オール、１－エチニル－１－シクロヘキサノール、フェニルブチノール等のアルキンアルコール；３－メチル－３－ペンテン－１－イン、３,５－ジメチル－１－ヘキシン－３－イン等のエンイン化合物；２－エチニル－４－メチル－２－ペンテン、１,３,５,７－テトラメチル－１,３,５,７－テトラビニルシクロテトラシロキサン、１,３,５,７－テトラメチル－１,３,５,７－テトラヘキセニルシクロテトラシロキサン等のメチルアルケニルシクロシロキサン；ベンゾトリアゾールが例示される。
組成物の硬化挙動の見地から、本発明の感圧接着層形成性オルガノポリシロキサン組成物は、組成物の調製後室温で８時間後に粘度の増大が１．５倍以内であり、８０～２００℃で硬化可能であることが好ましい。増粘が抑制されていることは、取扱作業性、ポットライフ、硬化後の特性の見地から重要であり、大過剰の（Ｃ）成分を含み、任意で白金系金属量の含有量が低くとも、一定以上の高温（８０～２００℃）で硬化させることで硬化性を確保することができるためである。なお、このような組成物は上記の各成分およびヒドロシリル化触媒と（Ｅ）成分の好適な組み合わせおよび配合量を選択することで、実現可能である。
本発明にかかるオルガノポリシロキサン組成物は、上記の好適な（Ａ）成分および（Ｂ）成分に加えて、溶媒として有機溶剤を含んでもよい。有機溶剤は、塗工作業性などを考慮してその種類及び配合量を調整する。有機溶剤としては、例えばトルエン、キシレン、ベンゼンなどの芳香族炭化水素系溶剤、ヘプタン、ヘキサン、オクタン、イソパラフィンなどの脂肪族炭化水素系溶剤、酢酸エチル、酢酸イソブチルなどのエステル系溶剤、ジイソプロプルエーテル、１，４－ジオキサンなどのエーテル系溶剤、トリクロロエチレン、パークロロエチレン、塩化メチレンなどの塩素化脂肪族炭化水素系溶剤、溶剤揮発油などが挙げられ、シート状基材への濡れ性などに応じて２種以上を組み合わせても良い。有機溶剤配合量は、（Ａ）成分～（Ｃ）成分の混合物をシート状基材表面に均一に塗工できるような量がよく、例えば、（Ａ）成分と（Ｂ）成分と（Ｃ）成分の合計１００質量部当たり、５～３０００質量部である。
本発明にかかるオルガノポリシロキサン組成物は、本発明の技術的効果を損なわない範囲で、任意で、上記成分以外の成分を含むことができる。例えば、接着促進剤；ポリジメチルシロキサンまたはポリジメチルジフェニルシロキサンなどの非反応性のオルガノポリシロキサン；フェノール系、キノン系、アミン系、リン系、ホスファイト系、イオウ系、またはチオエーテル系などの酸化防止剤；トリアゾール系またはベンゾフェノン系などの光安定剤；リン酸エステル系、ハロゲン系、リン系、またはアンチモン系などの難燃剤；カチオン系界面活性剤、アニオン系界面活性剤、または非イオン系界面活性剤などからなる１種類以上の帯電防止剤などを含むことができる。なお、これらの成分のほか、顔料、染料、無機微粒子（補強性フィラー、誘電性フィラー、導電性フィラー、熱伝導性フィラー）などを任意で配合することもできる。
［（Ａ´）分子内に炭素－炭素二重結合含有反応性基を含まない鎖状オルガノポリシロキサン］
本発明にかかるオルガノポリシロキサン組成物には、アルケニル基、アクリル基、メタクリル基等の炭素－炭素二重結合含有反応性基を含まないポリジメチルシロキサンまたはポリジメチルジフェニルシロキサンなどの非反応性のオルガノポリシロキサンを配合することができ、これにより、後述する感圧接着層の損失係数（ｔａｎδ）、貯蔵弾性率（Ｇ’）および損失弾性率（Ｇ’’）を改善することができる場合がある。例えば、水酸基末端を有するポリジメチルシロキサンまたはポリジメチルジフェニルシロキサンの使用により、感圧接着層の損失係数を増加させることができ、そのような組成物は、本発明の範囲に包含される。
本発明にかかるオルガノポリシロキサン組成物の調製方法は特に限定されず、それぞれの成分を均質に混合することによって行われる。必要に応じて溶剤を加えてもよく、公知の攪拌機または混練機を用いて、０～２００℃の温度で混合して調製してもよい。
本発明のオルガノポリシロキサン組成物は、基材上に塗工することによって塗膜を形成し、８０～２００℃の温度条件下、好適には、９０～１９０℃の温度条件下で加熱することによって硬化物とする。塗工方法としては、グラビアコート、オフセットコート、オフセットグラビア、ロールコート、リバースロールコート、エアナイフコート、カーテンコート、及びコンマコートが例示される。
［感圧接着性および粘着力の範囲］
本発明のオルガノポリシロキサン組成物は、ヒドロシリル化反応により当該組成物を硬化させてなる硬化層が感圧接着性であることを特徴とする。本発明の感圧接着層は、上記の構成を有し、実用上十分な粘着力を発現することから、公知のシリコーン感圧接着剤を所望により置き換えて利用可能である。
具体的には、本発明のオルガノポリシロキサン組成物を硬化させてなる厚み５０μｍの感圧接着層の、厚み２ｍｍのポリメチルメタクリレートシートに対する、ＪＩＳ Ｚ ０２３７に従う１８０°引き剥がし試験方法を用いて引張速度300ｍｍ/minにより測定された粘着力が９００～４０００ｇｆ／ｉｎｃｈの範囲にある感圧接着層を設計可能であり、１０００～３５００ｇｆ／ｉｎｃｈの範囲にある感圧接着層が好適である。なお、上記の厚み（５０μｍ）は、本発明にかかる硬化層の粘着力を客観的に定義するための基準となる硬化層自体の厚みであり、本発明のオルガノポリシロキサン組成物は厚み５０μｍに限らず、任意の厚みの硬化層または感圧接着層として利用することができることは言うまでもない。
［貯蔵弾性率およびその他の粘弾性］
本発明の感圧接着層形成性オルガノポリシロキサン組成物は、その硬化により得られる感圧接着層の－２０℃におけるせん断貯蔵弾性率G’が０．７７～５０．００ＭＰａの範囲にあり、当該貯蔵弾性率G’が０．７７～３０．００ＭＰａの範囲であってよく、０．８１～３０．００ＭＰａの範囲であってよく、０．８５～２９．００ＭＰａの範囲であるものも好適に本発明の範囲に含まれる。このような低温における貯蔵弾性率G’を有し、かつ、上記の実用的な粘着力を有することから、本発明における感圧接着層形成性オルガノポリシロキサン組成物は、弾性粘着部材の形成を目的として、スピーカー、トランスデューサー等の電子機器、電気的装置の部材として、また、スマートデバイス等の先端エレクトロニクス材料および表示素子分野への応用に適する。
本発明に係る感圧接着層の貯蔵弾性率（Ｇ’）は、公知の測定方法によって測定することができる。例えば、貯蔵弾性率（Ｇ’）ＭＣＲ３０１粘弾性測定装置（Ａｎｔｏｎ　Ｐａａｒ社製）を使用して測定することができ、直径８ｍｍ厚み０．５～１ｍｍ程度の円盤状の試料を用い、８ｍｍパラレルプレート、周波数１Ｈｚ、ひずみ０．１％、昇温速度３℃／分で、使用温度である－４０℃から１００℃の範囲において、－２０℃における値として測定することができる。
本発明に係る感圧接着層は、－２０℃での１．０Ｈｚにおける貯蔵弾性率Ｇ’が２５℃での１．０Ｈｚにおける貯蔵弾性率Ｇ’の３倍以上あってもよい。
［感圧接着層の透明性、色調または着色・変色に関する特性］
本発明のオルガノポリシロキサン組成物は、実質的に透明、半透明または不透明のいずれであってもよく、当該感圧接着層の用途に応じてその透明性を設計することができる。例えば、表示装置用の感圧接着層として、本発明のオルガノポリシロキサン組成物を硬化させてなる厚さ１０～１０００μｍのフィルム状の硬化物は、目視で透明であることが好ましく、カーボンブラック等の着色性の添加剤を含まないことが好ましい。なお、目視で透明である場合、より客観的には、厚み１００μｍの硬化層からなる表示装置用の感圧接着層の波長４５０ｎｍの光の透過率が空気の値を１００％とした場合に８０％以上であり、好適には９０％以上であり、９５％以上に設計してもよい。一方、光透過性が求められない電気・電子部品の接着等においては、半透明～不透明な感圧接着層であってもよく、光透過性以外の要求特性に応じて、着色性あるいは光透過性を損なうようなフィラー成分または添加剤を利用しても良い。
本発明のオルガノポリシロキサン組成物は、任意で硬化層中の白金系金属の含有量を低減等することにより、上記の透明性に加えて、硬化物が着色していないように設計することが可能である。具体的には、本発明のオルガノポリシロキサン組成物を硬化させてなる厚み１００μｍの硬化層を、その硬化直後にＪＩＳ Ｚ ８７２９に規定されるＬ＊ａ＊ｂ＊表色系で測定したｂ＊値が、０．１５以下であり、さらに０．１０以下であるように設計可能である。かかるｂ＊値を有することは、硬化層が実質的に透明であり、かつ、黄色に着色していないことを意味する。
本発明の硬化層は、高温や紫外線等の高エネルギー線に長時間暴露した場合であっても、その色調が大きく変化せず、特に、黄変の問題を生じないように設計可能である。具体的には、以下のいずれの評価を行った場合であっても、本発明のオルガノポリシロキサン組成物を硬化させてなる厚み１００μｍの硬化層について、評価の前後におけるＪＩＳ Ｚ ８７２９に規定されるＬ＊ａ＊ｂ＊表色系で測定したｂ＊値の変化（Δｂ＊）が０．２０以下であり、０．１５以下であるように設計可能である。なお、Δｂ＊は数値変化の絶対値である。

（１）加熱エージング評価：硬化層を１０５℃－３００時間エージングする

（２）高エネルギー線照射：硬化層に対し、３６５ｎｍでの強度が１２ｍＷ／ｃｍ２、２５４ｎｍでの強度が３．５ｍＷ／ｃｍ２である水銀灯（例えば、ウシオ電機製Ｏｐｔｉｃａｌ　ＭｏｄｕｌｅＸなど）を用いた紫外光を、室温において試料上に75時間照射する
［感圧接着剤層としての使用］
本発明の硬化物は、特に、感圧接着剤層として使用することができる。また、被着体との密着性を向上させるために、感圧接着剤層または基材の表面に対してプライマー処理、コロナ処理、エッチング処理、プラズマ処理等の表面処理を行ってもよい。ただし、本発明の感圧接着剤層は、上記のとおり、表示デバイス等の基材への密着性に優れることから、必要に応じ、これらの工程を加えてさらに被着体との密着性を向上させてもよく、これらの工程を省くことにより、より高い生産効率を実現してもよい。
本発明に係る硬化性オルガノポリシロキサン組成物は、剥離ライナーに塗工した後、上記の温度条件下で加熱することにより硬化させ、剥離ライナーを剥がしてフィルム状基材、テープ状基材、またはシート状基材（以下、「フィルム状基材」という）と貼り合せたり、フィルム状基材に塗工した後、上記の温度条件下で加熱することにより硬化させ、前記基材の表面に感圧接着剤層を形成することができる。これらのフィルム状基材上に本発明に係るオルガノポリシロキサン組成物を硬化してなる硬化層、特にフィルム状の感圧接着剤層を備えた積層体は、粘着テープ、絆創膏、低温支持体、転写フィルム、ラベル、エンブレム及び装飾又は説明用の標示に使用してもよい。更に、本発明に係るオルガノポリシロキサン組成物を硬化してなる硬化層は、自動車部品、玩具、電子回路、又はキーボードの組み立てに使用してもよい。あるいは、本発明に係るオルガノポリシロキサン組成物を硬化してなる硬化層、特にフィルム状の感圧接着剤層は、積層タッチスクリーン又はフラットパネルディスプレイの構築及び利用に使用してもよい。
基材の種類として、板紙，ダンボール紙，クレーコート紙，ポリオレフィンラミネート紙，特にはポリエチレンラミネート紙，合成樹脂フィルム・シート，天然繊維布，合成繊維布，人工皮革布，金属箔が例示される。特に、合成樹脂フィルム・シートが好ましく、合成樹脂として、ポリイミド、ポリエチレン、ポリプロピレン、ポリスチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリカーボネート、ポリエチレンテレフタレート、シクロポリオレフィン、ナイロンが例示される。特に耐熱性が要求される場合には、ポリイミド、ポリエーテルエーテルケトン、ポリエチレンナフタレート（ＰＥＮ）、液晶ポリアリレート、ポリアミドイミド、ポリエーテルスルフォン等の耐熱性合成樹脂のフィルムが好適である。一方、表示デバイス等視認性が求められる用途においては、透明基材、具体的にはポリプロピレン、ポリスチレン、ポリ塩化ビニリデン、ポリカーボネート、ポリエチレンテレフタレート、ＰＥＮ等の透明材料が好適である。
上記基材はフィルム状またはシート状であることが好ましい。その厚さは特に制限されず、用途に応じて所望の厚さで設計することができる。さらに、支持フィルムと感圧接着層の密着性を向上させるために、プライマー処理、コロナ処理、エッチング処理、プラズマ処理された支持フィルムを用いてもよい。また、フィルム状基材の感圧接着層面と反対面には、傷つき防止、汚れ防止、指紋付着防止、防眩、反射防止、帯電防止などの処理などの表面処理されたものであってもよい。
基材への塗工方法としては、グラビアコート、オフセットコート、オフセットグラビア、オフセット転写ロールコーター等を用いたロールコート、リバースロールコート、エアナイフコート、カーテンフローコーター等を用いたカーテンコート、コンマコート、マイヤーバー、その他公知の硬化層を形成する目的で使用される方法が制限なく使用できる。
塗工量は表示装置等の用途に応じて所望の厚さで設計することができ、一例として、硬化したあとの感圧接着層の厚みとして１～１，０００μｍであり、５～９００μｍであってよく、１０～８００μｍであってよいが、これらに限定されるものではない。
本発明に係る感圧接着層は、その要求特性に応じて単層であっても２層以上の感圧接着層を積層してなる複層であってもよい。複層の感圧接着層は、一層ずつ作成した感圧接着剤フィルムを貼り合わせても良く、剥離層を備えたフィルム基材上等で、感圧接着層形成性オルガノポリシロキサン組成物を塗工して硬化させる工程を複数回行ってもよい。
本発明に係る感圧接着層は、部材間の接着ないし粘着機能のほか、誘電層、導電層、放熱層、絶縁層、補強層等から選ばれる他の機能層としての役割を付与されていても良い。
本発明のオルガノポリシロキサン組成物を硬化してなる硬化層が感圧接着層、特に、感圧接着剤フィルムである場合、当該硬化層は、剥離コーティング能を有する剥離層を備えたフィルム基材上に、剥離可能な状態で粘着した積層体フィルムとして取り扱うことが好ましい。剥離層は剥離ライナー、セパレーター、離型層あるいは剥離コーティング層と呼ばれることもあり、好適には、シリコーン系剥離剤、フッ素系剥離剤、アルキド系剥離剤、またはフルオロシリコーン系剥離剤等の剥離コーティング能を有する剥離層、基材表面に物理的に微細な凹凸を形成させたり、本発明の感圧接着層と付着しにくい基材それ自体であってもよい。特に本発明にかかる積層体においては、剥離層として、フルオロシリコーン系剥離剤を硬化させてなる剥離層の使用が好ましい。
本発明のオルガノポリシロキサン組成物を硬化してなる硬化物は、上記のような粘弾性と接着力を併せ持つため、弾性粘着部材として、各種の電子機器または電気的装置の部材として有用である。特に、電子材料、表示装置用部材またはトランスデューサー用部材（センサ、スピーカー、アクチュエーター、およびジェネレーター用を含む）として有用であり、当該硬化物の好適な用途は、電子部品または表示装置の部材である。本発明にかかる硬化物は透明でも不透明であってもよいが、フィルム形状の硬化物、特に実質的に透明な感圧接着剤フィルムは、表示パネルまたはディスプレイ用の部材として好適であり、特に、画面を指先等で接触することにより機器、特に電子機器を操作可能な所謂タッチパネル用途に特に有用である。また、不透明な弾性粘着層は、透明性が要求されず、粘着層自体に一定の伸縮性または柔軟性が求められるセンサ、スピーカー、アクチュエーター等に用いられるフィルム状またはシート状部材の用途に特に有用である。
特に、本発明のオルガノポリシロキサン組成物を硬化してなる感圧接着層は、従来のシリコーン感圧接着層と同等の感圧接着特性を実現可能であり、かつ、硬化不良や硬化性の低下の問題を生じることなく、表示デバイス等の基材への密着性を改善できる。
［表示パネルまたはディスプレイ用の部材］
本発明のオルガノポリシロキサン組成物を硬化してなる硬化物は、積層タッチスクリーン又はフラットパネルディスプレイの構築及び利用に使用することができ、その具体的な使用方法は、感圧接着剤層（特に、シリコーンＰＳＡ）の公知の使用方法を特に制限なく用いることができる。
例えば、本発明のオルガノポリシロキサン組成物を硬化してなる硬化物は、前記の特表２０１４－５２２４３６号または特表２０１３－５１２３２６等で開示された光学的に透明なシリコーン系感圧接着剤フィルムあるいは粘着剤層として、タッチパネル等の表示デバイスの製造に用いることができる。具体的には、本発明のオルガノポリシロキサン組成物を硬化してなる硬化物は、特表２０１３－５１２３２６に記載の粘着層または粘着フィルムとして、特に制限なく用いることができる。
一例として、本発明にかかるタッチパネルは、一面に導電層が形成されている伝導性プラスチックフィルム等の基材、及び当該導電層が形成された側またはその反対側の面に付着されている本発明の硬化性オルガノポリシロキサン組成物を硬化してなる硬化層を含むタッチパネルであってよい。当該基材は、シート状またはフィルム状基材であることが好ましく樹脂フィルムまたはガラス板が例示される。また、前記伝導性プラスチックフィルムは、一面にＩＴＯ層が形成されている樹脂フィルムまたはガラス板、特に、ポリエチレンテレフタレートフィルムであってよい。これらは、前記の特表２０１３－５１２３２６等に開示されている。
その他、本発明のオルガノポリシロキサン組成物を硬化してなる硬化物は、タッチパネル等の表示デバイスの製造に用いる偏光板用接着フィルムとして用いてもよく、特開２０１３－０６５００９号公報に記載のタッチパネルとディスプレイモジュール間の貼合に用いる感圧接着層として用いてもよい。
本発明の硬化反応性のオルガノポリシロキサン組成物、それを硬化してなる硬化物の用途としては、上記に開示した他に何ら制約はなく、当該組成物を硬化してなる硬化物を備えてなる感圧接着フィルムはテレビ受像機、コンピューター用モニター、携帯情報端末用モニター、監視用モニター、ビデオカメラ、デジタルカメラ、携帯電話、携帯情報端末、自動車などの計器盤用ディスプレイ、種々の設備・装置・機器の計器盤用ディスプレイ、自動券売機、現金自動預け払い機、車載用表示装置、車載用透過型スクリーンなど、文字や記号、画像を表示するための種々の表示装置に利用可能である。このような表示装置の表面形状は、平面ではなく曲面状ないし湾曲した形状であってもよく、各種フラットパネルディスプレイ（ＦＰＤ）のほか、自動車（電気自動車含む）や航空機等に利用される曲面ディスプレイまたは曲面透過型スクリーンが例示される。さらに、これらの表示装置は、スクリーンやディスプレイ上に機能またはプログラムを実行するためのアイコンや、電子メール・プログラム等の通知表示、カーナビゲーション装置、オーディオ装置、空調装置などの各種装置の操作ボタンを表示することができ、これらのアイコンや通知表示、操作ボタンに指を触れることで、入力操作が可能となるタッチパネル機能が付加されていてもよい。装置としては、ＣＲＴディスプレイ、液晶ディスプレイ、プラズマディスプレイ、有機ＥＬディスプレイ、無機ＥＬディスプレイ、ＬＥＤディスプレイ、表面電解ディスプレイ（ＳＥＤ）、電界放出型ディスプレイ（ＦＥＤ）などの表示装置や、これらを利用したタッチパネルに応用が可能である。また、当該組成物を硬化してなる硬化物は、接着性と粘弾特性に優れるため、スピーカー用のメンブレン等のトランスデューサー用部材（センサ、スピーカー、アクチュエーター、およびジェネレーター用を含む）であるフィルム又はシート状部材として利用できるほか、さらに、二次電池、燃料電池または太陽電池モジュールに用いる封止層または接着剤層として利用することができる。
本発明のオルガノポリシロキサン組成物を硬化してなる感圧接着層は、実質的に透明であってよく、硬化不良や硬化性の低下の問題を生じることなく、かつ、各種表示デバイス等の基材への密着性に優れることから、長期間にわたって表示内容の視認性および操作性が良好な車両用表示装置、特に、曲面スクリーンまたは曲面ディスプレイを備え、任意でタッチパネル機能を有する車両用表示装置に好適に利用できる。例えば、特開2017-047767号公報、特開2014-182335号公報、特開2014-063064号公報、特開2013-233852号公報等には曲面状の表示面を備えた車両用表示装置が開示されているが、本発明にかかる感圧接着層は、これらの文献中の透明性が求められる接着層または粘着層の一部又は全部として好適に適用乃至置き換えが可能である。さらに、本発明の感圧接着層形成性オルガノポリシロキサン組成物は、他の公知の曲面状の表示装置についても、現在使用されている透明性が求められる接着層または粘着層を置き換えて利用できることは言うまでもなく、本発明の感圧接着剤の利点をさらに活用するために表示装置の設計や部材の厚みを公知の手法により調整することが好ましい。
なお、本発明の感圧接着層を備えた透明なフィルム状基材を、これらの、ディスプレイ表面の傷つき防止、汚れ防止、指紋付着防止、帯電防止、反射防止、のぞき見防止などの目的で使用してもよい。
　以下に、本発明の実施例及び比較例を記す。なお、各実施例・比較例・参考例において「硬化させた」とは、各々の硬化条件により、各組成物が完全に硬化したことを意味するものである。
（硬化反応性のオルガノポリシロキサン組成物の調製）
　表１に示す各成分を用いて、各実施例・比較例・参考例に示す硬化反応性のオルガノポリシロキサン組成物を調製した。なお、表１における％は全て質量％である。
（オルガノポリシロキサン成分の分子量の測定）
Waters社製ゲルパーミエーションクロマトグラフィー（GPC）を用い、テトラヒドロフラン（ＴＨＦ）を溶媒として、標準ポリスチレン換算で、オルガノポリシロキサンレジン等のオルガノポリシロキサン成分の重量平均分子量（Mw）、数平均分子量（Mn）を求めた。

（オルガノポリシロキサンレジン中の水酸基（ＯＨ）含有量の測定）
ガラスフリープローブを備えたブルカー製ＡＣＰ－３００２９Si NMRスペクトロメーターを用い、テトラメチルシランの化学シフトを0 ppmとしたときに、-93から-103.5 ppmに現れるSi(OH)O2/3単位の全シリコンに対する存在比率からモル含量を得、さらに、オルガノポリシロキサンレジン中の水酸基（ＯＨ）の質量％にも換算した。なお、以下の実施例におけるオルガノポリシロキサンレジン中に水酸基以外の加水分解性官能基は含まれていなかった。

（粘着力測定）
　各組成物を、ＰＥＴフィルム（株式会社東レ製、製品名ルミラー（登録商標）S１０、厚さ５０μｍ）に硬化後の厚みが５０μｍとなるように塗工し、１５０℃で３分間硬化させた。1日放置後、同試料を幅２０ｍｍに切断し、粘着層面をＰＭＭＡ板（パルテック製、アクリライトＬ００１，５０ｘ１２０ｘ２ｍｍ）にローラーを用いて貼り合せて試験片とした。ＰＭＭＡ板を用いた試験片は、オリエンテック社製ＲＴＣ－１２１０引っ張り試験機を用いてＪＩＳ　Ｚ０２３７に準じて１８０°引き剥がし試験方法を用いて引張速度３００ｍｍ/ｍｉｎにて粘着力（２０ｍｍ幅での測定を表示単位ｇｆ/インチに換算）を測定した。

（動的粘弾性：－２０℃における貯蔵弾性率Ｇ’）
　各組成物を硬化後の厚みが約１００μｍになるようにフロロシリコーン剥離コーティングを塗工した剥離ライナーに塗工し、１５０℃で３分間硬化させた。この感圧接着剤フィルムを５枚以上重ね合わせ、厚さ５００μｍ以上である、両面を剥離ライナーに挟まれたフィルムサンプルを得た。当該フィルムを直径８ｍｍにくりぬき、動的粘弾性装置（Ａｎｏｔｏｎ　Ｐａａｒ社製、ＭＣＲ３０１）のパラレルプレートプローブに貼り付けて、貯蔵弾性率Ｇ’を測定した。測定条件は、－７０℃～２００℃の範囲であり、周波数１Ｈｚ、昇温速度３℃／分にて測定し、損失係数、貯蔵弾性率Ｇ’、損失弾性率Ｇ’’を測定し、－２０℃における貯蔵弾性率Ｇ’を記録した。

（引張試験）
　上記の動的粘弾性試験用サンプルと同じようにして得た厚さ５００μｍ以上である、両面を剥離ライナーに挟まれたフィルムサンプルを、幅約５ｍｍ、長さ約７０ｍｍに切断し、粘着剤表面にベビーパウダーを塗りながら剥離ライナーを剥がして、引張試験サンプルとした。引張試験は島津社製Ａｕｔｏｇｒａｐｈ　ＡＧＳ－Ｘを用い、サンプルの上下約２５ｍｍを掴んで、３００ｍｍ／分の速度で行った。応力およびひずみは各サンプルごとの正確なサンプルの幅と厚さ、クロスヘッド間距離から求めた。
　表１に硬化反応性のオルガノポリシロキサン組成物の材料を示す。なお、各成分の粘度または可塑度は以下の方法により、室温において測定した。

［粘度］
　粘度（ｍＰａ・ｓ）は、ＪＩＳ　Ｋ７１１７－１に準拠した回転粘度計を使用して測定した値であり、動粘度（ｍｍ２／ｓ）は、ＪＩＳ　Ｚ８８０３に準拠したウベローデ型粘度計によって測定した値である。

［可塑度］
　可塑度は、ＪＩＳ　Ｋ　６２４９に規定される方法に準じて測定された値（２５℃、４.２ｇの球状試料に１ｋｇｆの荷重を３分間かけたときの厚さを1/100mmまで読み、この数値を100倍したもの）で示した。
表１　硬化反応性のオルガノポリシロキサン組成物の成分 
Figure JPOXMLDOC01-appb-T000001
（実施例１）
　成分ａのビニル官能性ポリジメチルシロキサン３２．９重量部、成分ｂ１のＭＱシリコーン樹脂５２．６重量部、成分ｂ２のＭＱシリコーン樹脂４４．４重量部、トルエン９２．３重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．７５６重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は３４．９、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（実施例２）
　成分ａのビニル官能性ポリジメチルシロキサン３２．２重量部、成分ｂ１のＭＱシリコーン樹脂４１．６重量部、成分ｂ２のＭＱシリコーン樹脂５４．７重量部、トルエン９３．７重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．７４５重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は３５．１、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（実施例３）
　成分ａのビニル官能性ポリジメチルシロキサン３１．６重量部、成分ｂ１のＭＱシリコーン樹脂２６．８重量部、成分ｂ２のＭＱシリコーン樹脂６８．０重量部、トルエン９５．８重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．７３７重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ２の白金系ヒドロシリル化反応触媒０．５７７重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は３５．４、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（実施例４）
　成分ａのビニル官能性ポリジメチルシロキサン３４．７重量部、成分ｂ１のＭＱシリコーン樹脂２．３７重量部、成分ｂ２のＭＱシリコーン樹脂８４．５重量部、トルエン４５．１重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．６５６重量部、成分ｅの硬化遅延剤２０％溶液０．４０９重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．３５５重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。（a）成分中のアルケニル基の量に対する（c1）成分中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は２８．７、白金金属の固形分に対する含量は２２ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（参考例１）
　次の組成を組むことができる。成分ａのビニル官能性ポリジメチルシロキサン２５．７重量部、成分a’の無官能性ポリジメチルシロキサン６．４３重量部、成分ｂ１のＭＱシリコーン樹脂４１．６重量部、成分ｂ２のＭＱシリコーン樹脂５４．７重量部、トルエン３８．２重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．５８２重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は３４．４、白金金属の固形分に対する含量は３０ｐｐｍであった。
（比較例１）
　成分ａのビニル官能性ポリジメチルシロキサン４９．０重量部、成分ｂ１のＭＱシリコーン樹脂７９．９重量部、トルエン９３．３重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．９１９重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は２８．４、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（比較例２）
　成分ａのビニル官能性ポリジメチルシロキサン４９．０重量部、成分ｂ１のＭＱシリコーン樹脂７９．９重量部、トルエン９３．３重量部、成分ｃ２の両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン０．４３３重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ２中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は２８．４、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（比較例３）
　成分ａのビニル官能性ポリジメチルシロキサン３１．６重量部、成分ｂ１のＭＱシリコーン樹脂２６．８重量部、成分ｂ２のＭＱシリコーン樹脂６８．０重量部、トルエン９５．８重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．７３７重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ２の白金系ヒドロシリル化反応触媒０．５７７重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は３５．４、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
（比較例４）
　成分ａのビニル官能性ポリジメチルシロキサン４８．３重量部、成分ｂ１のＭＱシリコーン樹脂８１．０重量部、トルエン９２．９重量部、成分ｃ１の両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体０．９１０重量部、成分ｅの硬化遅延剤２０％溶液０．５７７重量部、を室温でよく混合し、混合物に成分ｄ１の白金系ヒドロシリル化反応触媒０．４８４重量部を加えて硬化反応性のオルガノポリシロキサン組成物とした。成分ａ中のアルケニル基の量に対する成分ｃ１中のＳｉＨ基のモル比（ＳｉＨ／Ｖｉ比）は２８．６、白金金属の固形分に対する含量は３０ｐｐｍであった。
　当該組成物を上記の方法で硬化させ、上記に示す方法によりＰＭＭＡ板に対する粘着力、粘弾性、応力歪を測定し、その評価結果等を表２に示した。
Figure JPOXMLDOC01-appb-T000002
表２に示すとおり、実施例１～４に係る感圧接着層形成性オルガノポリシロキサン組成物は十分な硬化性を有し、－２０℃における貯蔵弾性率G’が０．７７ＭＰａ以上の良好な範囲（０．９０４，８．６７，９．３２，１３．００ＭＰａ）にあり、実用上十分な粘着力を備える。
一方、比較例１～４では、－２０℃における貯蔵弾性率G’が低く、一定以上のG’の値という本発明の要求特性を達成できないものであった。

Claims (11)

  1. （Ａ）分子内に平均して１を超える数のアルケニル基を有する鎖状オルガノポリシロキサン、
    （Ｂ）以下の（ｂ１）成分および（ｂ２）成分を１：９９～９９：１の質量比で含む、オルガノポリシロキサンレジン混合物：
    （ｂ１）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００以上であるオルガノポリシロキサンレジン、
    （ｂ２）分子内の全ケイ素原子に対する水酸基および加水分解性基の含有量の和が９モル％以下であり、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により標準ポリスチレン換算で測定される重量平均分子量（Ｍｗ）が４５００未満であるオルガノポリシロキサンレジン
    （Ｃ）分子内に少なくとも２個のＳｉ－Ｈ結合を有するオルガノハイドロジェンポリシロキサン、および
    （Ｄ）有効量のヒドロシリル化反応触媒
    を含有してなり、（Ａ）成分に対する（Ｂ）成分の質量比が０．９～３．０の範囲にあり、当該組成物の硬化により得られる感圧接着層の－２０℃におけるせん断貯蔵弾性率G’が０．７７～５０．００ＭＰａの範囲にある、感圧接着層形成性オルガノポリシロキサン組成物。
  2. 当該組成物の硬化により得られる厚み５０μｍの感圧接着層の、厚み２ｍｍのポリメチルメタクリレートシートに対する、ＪＩＳ Ｚ ０２３７に従う１８０°引き剥がし試験方法を用いて引張速度300ｍｍ/minにより測定された粘着力が９００～４０００ｇｆ／ｉｎｃｈの範囲であることを特徴とする、請求項１に記載の感圧接着層形成性オルガノポリシロキサン組成物。
  3. （Ａ）成分の少なくとも一部が、（Ａ１）２５℃において１００，０００ｍＰａ・ｓ以上の粘度を有するか、ＪＩＳ　Ｋ６２４９に規定される方法に準じて測定された可塑度が５０～２００の範囲にある生ゴム状のアルケニル基含有オルガノポリシロキサンであり、そのアルケニル基中のビニル（ＣＨ２＝ＣＨ）部分の含有量が０．００５～０．４００質量％の範囲にある鎖状オルガノポリシロキサンであり、
    （Ｂ）成分であるオルガノポリシロキサンレジン混合物が、Ｒ３ＳｉＯ１／２単位（式中、Ｒは一価有機基であり、Ｒの９０モル％以上が炭素数１～６のアルキル基またはフェニル基である；Ｍ単位）及びＳｉＯ４／２単位（Ｑ単位）から実質的になるオルガノポリシロキサンレジン混合物であり
    （Ｃ）成分の量が、上記の（Ａ）成分中および（Ｂ）成分中のアルケニル基の物質量の和に対する（Ｃ）成分中のＳｉＨ基の物質量の比（モル比）が０．１～１００となる量であり、
    （Ｄ）成分の量が、組成物中の固形分中の白金系金属の含有量が０．１～２００ｐｐｍの範囲である、請求項１または請求項２に記載の感圧接着層形成性オルガノポリシロキサン組成物。
  4. （Ｃ）成分の量が、上記の（Ａ）成分中および（Ｂ）成分中のアルケニル基の物質量の和に対する（Ｃ）成分中のＳｉＨ基の物質量の比（モル比）が２０～６０となる量である請求項１～３のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物。

  5. さらに、（Ａ´）分子内に炭素－炭素二重結合含有反応性基を含まない鎖状オルガノポリシロキサンを含む、請求項１～４のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物
  6. 請求項１～５のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる感圧接着剤層。
  7. フィルム状基材上に、請求項１～５のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる感圧接着剤層を備えた積層体。
  8. １または２以上のフィルム状基材に当該感圧接着剤層に対する剥離層が設けられている、請求項７に記載の積層体。
  9. フィルム状基材、
    該フィルム状基材上に形成された第１剥離層、
    該剥離層上に請求項１～５のいずれか１項に記載の感圧接着層形成性オルガノポリシロキサン組成物を塗工し硬化させて形成された感圧接着層、及び
    該感圧接着層上に積層された第２剥離層
    を含む、請求項７または請求項８の積層体。
  10. 請求項１～５のいずれか１項記載の感圧接着層形成性オルガノポリシロキサン組成物を硬化してなる、弾性粘着部材。
  11. 請求項１０に記載の弾性粘着部材を含む電子機器または電気的装置。
PCT/JP2019/031810 2018-08-10 2019-08-13 感圧接着層形成性オルガノポリシロキサン組成物およびその使用 Ceased WO2020032287A1 (ja)