CN103757732A - Algae-resistant fishing net - Google Patents
Algae-resistant fishing net Download PDFInfo
- Publication number
- CN103757732A CN103757732A CN201310669662.3A CN201310669662A CN103757732A CN 103757732 A CN103757732 A CN 103757732A CN 201310669662 A CN201310669662 A CN 201310669662A CN 103757732 A CN103757732 A CN 103757732A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- algae
- raw material
- parts
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an algae-resistant fishing net. The algae-resistant fishing net comprises, by weight, 91-100 parts of ultrahigh-molecular weight polyethylene, 12-15 parts of polyoxyethylene, 2-3 parts of cuprous thiocyanate, 0.8-1 part of zinc pyrithione, 3-4 parts of phenyltriethoxysilane and 4-5 parts of a modification plasticizer. The algae-resistant fishing net has good algae resistance, is convenient for cleaning and has a long service life.
Description
Technical field
The present invention relates generally to a kind of fishing net, relates in particular to a kind of anti-algae fishing net.
Background technology
Modern fishing net mainly adopts polyethylene, the raw materials such as nylon are processed, wherein polythene fishing net, to adopt polythene material through fusion plastification, spinning, plying is twisted thread and is made into, use Yu Haiyang trawlnet, purse seine, wind resistance sea net cage etc., there is longer life cycle, higher catching rate, but the mechanical property of polyethylene itself is general, TENSILE STRENGTH is lower, creep resistance is bad, just cause the intensity of conventional polyethylene fishing net, anti-wear performance, at the bottom of toughness is unwell to Complex Sea and wind and waves environment fishing operation, reduced the service life of fishing gear, not only waste resource, also directly affect catch.
Summary of the invention
The object of the invention is just to provide a kind of anti-algae fishing net.
The present invention is achieved by the following technical solutions:
A kind of anti-algae fishing net, it is comprised of the raw material of following weight parts:
Ultra-high molecular weight polyethylene 91-100, polyethylene glycol oxide 12-15, cuprous sulfocyanide 2-3, Zinc Pyrithione 0.8-1, phenyl triethoxysilane 3-4, modification plasticizer 4-5;
Described modification plasticizer is comprised of the raw material of following weight parts: MTES 1-1.2, dioctyl ester 2-2.3, ATBC 1.2-1.4, peanut oil 2-2.3, turpentine oil 1-1.2, eucalyptus oil 0.3-0.4, poly-different diene 1.2-1.4, morpholine 0.2-0.3, antioxidant MB 1-1.2, methyl ethyl ketone peroxide 0.2-0.3, styrene 1.2-1.4, nano titanium oxide 0.2-0.3;
Above-mentioned methyl ethyl ketone peroxide is added drop-wise in other each mixtures of materials, and stirring reaction 60-90 minute, is warming up to 120-130 ℃, and stirring reaction 2-3 hour obtains described modification plasticizer.
A preparation method for anti-algae fishing net, comprises the following steps:
The 15-20% that gets above-mentioned ultra-high molecular weight polyethylene weight mixes with polyethylene glycol oxide, insulation reaction 10-12 minute at 100-120 ℃, add cuprous sulfocyanide, reduction temperature is normal temperature, add the each raw material of residue, by extruder, melt extrude, drawing-off, sizing, spinning, obtain described anti-algae fishing net.
Advantage of the present invention is:
The fishing net that the present invention produces has good algae preventive effect, is convenient to clean, and increases the service life.
The specific embodiment
Embodiment 1
A kind of anti-algae fishing net, it is characterized in that it by following weight parts (kilogram) raw material form:
Ultra-high molecular weight polyethylene 100, polyethylene glycol oxide 15, cuprous sulfocyanide 2, Zinc Pyrithione 0.8, phenyl triethoxysilane 4, modification plasticizer 4;
Described modification plasticizer is comprised of the raw material of following weight parts: MTES 1.2, dioctyl ester 2.3, ATBC 1.4, peanut oil 2.3, turpentine oil 1.2, eucalyptus oil 0.4, poly-different diene 1.4, morpholine 0.3, antioxidant MB 1.2, methyl ethyl ketone peroxide 0.3, styrene 1.4, nano titanium oxide 0.3;
Above-mentioned methyl ethyl ketone peroxide is added drop-wise in other each mixtures of materials, and stirring reaction 90 minutes, is warming up to 120-130 ℃, and stirring reaction 2-3 hour obtains described modification plasticizer.
A preparation method for anti-algae fishing net, comprises the following steps:
Get 20% of above-mentioned ultra-high molecular weight polyethylene weight and mix with polyethylene glycol oxide, at 120 ℃, insulation reaction 12 minutes, adds cuprous sulfocyanide, reduction temperature is normal temperature, adds the each raw material of residue, by extruder, melt extrudes, drawing-off, sizing, spinning, obtain described anti-algae fishing net.
Filament properties test: elongation at break 15.1%;
Anti-tensile degree (KG) 54.6;
Knotting strength (KG) 37.49.
Claims (2)
1. an anti-algae fishing net, is characterized in that what it was comprised of the raw material of following weight parts:
Ultra-high molecular weight polyethylene 91-100, polyethylene glycol oxide 12-15, cuprous sulfocyanide 2-3, Zinc Pyrithione 0.8-1, phenyl triethoxysilane 3-4, modification plasticizer 4-5;
Described modification plasticizer is comprised of the raw material of following weight parts: MTES 1-1.2, dioctyl ester 2-2.3, ATBC 1.2-1.4, peanut oil 2-2.3, turpentine oil 1-1.2, eucalyptus oil 0.3-0.4, poly-different diene 1.2-1.4, morpholine 0.2-0.3, antioxidant MB 1-1.2, methyl ethyl ketone peroxide 0.2-0.3, styrene 1.2-1.4, nano titanium oxide 0.2-0.3;
Above-mentioned methyl ethyl ketone peroxide is added drop-wise in other each mixtures of materials, and stirring reaction 60-90 minute, is warming up to 120-130 ℃, and stirring reaction 2-3 hour obtains described modification plasticizer.
2. a preparation method for anti-algae fishing net as claimed in claim 1, is characterized in that comprising the following steps:
The 15-20% that gets above-mentioned ultra-high molecular weight polyethylene weight mixes with polyethylene glycol oxide, insulation reaction 10-12 minute at 100-120 ℃, add cuprous sulfocyanide, reduction temperature is normal temperature, add the each raw material of residue, by extruder, melt extrude, drawing-off, sizing, spinning, obtain described anti-algae fishing net.