ES2059379T3 - Materiales compuestos tolerantes al deterioro que contienen particulas infusibles. - Google Patents

Materiales compuestos tolerantes al deterioro que contienen particulas infusibles.

Info

Publication number
ES2059379T3
ES2059379T3 ES87306010T ES87306010T ES2059379T3 ES 2059379 T3 ES2059379 T3 ES 2059379T3 ES 87306010 T ES87306010 T ES 87306010T ES 87306010 T ES87306010 T ES 87306010T ES 2059379 T3 ES2059379 T3 ES 2059379T3
Authority
ES
Spain
Prior art keywords
epoxy resin
infusible particles
prepreg
deterioration
materials containing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES87306010T
Other languages
English (en)
Inventor
Irena Nmn Gawin
Brian Joseph Swetlin
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hercules LLC
Original Assignee
Hercules LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hercules LLC filed Critical Hercules LLC
Application granted granted Critical
Publication of ES2059379T3 publication Critical patent/ES2059379T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

SE PRESENTAN MATERIALES COMPUESTOS TOLERANTES A LOS DAÑOS QUE CONTIENEN FILAMENTOS DE ALTA RESISTENCIA EN FORMA DE MADEJAS O HILOS DE FIBRA CONTINUA Y UNA MATRIZ DE RESINA EPOXI RETICULADA SEPARADA DE FASE TENAZ. LA MATRIZ DE RESINA EPOXI RETICULADA CONTIENE PARTICULAS INFUSIBLES QUE RESIDEN PRINCIPALMENTE ENTRE LAS CAPAS DEL MATERIAL COMPUESTO Y TIENEN CRITICAMENTE UN TAMAÑO MEDIO ENTRE 10 Y 75 MICRAS. TAMBIEN SE PRESENTAN PREPARACIONES PREVIAS PARA OBTENER LOS MATERIALES COMPUESTOS TOLERANTES A LOS DAÑOS Y METODOS PARA OBTENER DICHAS PREPARACIONES Y LAS COMPOSICIONES DE RESINA EPOXI DE LAS MISMAS. LAS COMPOSICIONES DE RESINA EPOXI CONTIENEN LAS PARTICULAS INFUSIBLES QUE SE SEGREGAN PARA QUEDAR, SEGUN SU TAMAÑO, SOBRE UNA CAPA SUPERFICIAL DE LA PREPARACION PREVIA DURANTE EL PROCESO DE COMBINACION DE LOS FILAMENTOS DE ALTA RESISTENCIA DE LA PREPARACION PREVIA Y LA RESINA QUE CONTIENE LA COMPOSICION DE RESINAS EPOXI. ALTERNATIVAMENTE LAS PARTICULAS INFUSIBLES PUEDEN DISPONERSE DIRECTAMENTESOBRE LA SUPERFICIE DE RESINA EPOXI DE LA PREPARACION PREVIA.
ES87306010T 1986-07-09 1987-07-08 Materiales compuestos tolerantes al deterioro que contienen particulas infusibles. Expired - Lifetime ES2059379T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US06/884,139 US4863787A (en) 1986-07-09 1986-07-09 Damage tolerant composites containing infusible particles

Publications (1)

Publication Number Publication Date
ES2059379T3 true ES2059379T3 (es) 1994-11-16

Family

ID=25384038

Family Applications (1)

Application Number Title Priority Date Filing Date
ES87306010T Expired - Lifetime ES2059379T3 (es) 1986-07-09 1987-07-08 Materiales compuestos tolerantes al deterioro que contienen particulas infusibles.

Country Status (10)

Country Link
US (1) US4863787A (es)
EP (1) EP0252725B1 (es)
AT (1) ATE96817T1 (es)
BR (1) BR8703486A (es)
CA (1) CA1300783C (es)
DE (1) DE3788007T2 (es)
DK (1) DK356587A (es)
ES (1) ES2059379T3 (es)
IL (1) IL82916A (es)
NO (1) NO872667L (es)

Families Citing this family (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2051274T3 (es) * 1986-12-25 1994-06-16 Toray Industries Materiales compuestos altamente resistentes.
US4977218A (en) * 1988-09-26 1990-12-11 Amoco Corporation Carboxylated rubber particles as tougheners for fiber reinforced composites
JPH0267331A (ja) * 1988-07-15 1990-03-07 Amoco Corp 繊維強化複合材に対する強靱化材料としてのカルボキシル化ゴム粒
EP0351025A3 (en) * 1988-07-15 1991-10-23 Amoco Corporation Fiber reinforced composites toughened with carboxylated rubber particles
EP0351028A3 (en) * 1988-07-15 1991-10-23 Amoco Corporation Resin particle-filled, fiber-reinforced composites
US5169710A (en) * 1988-07-15 1992-12-08 Amoco Corporation Fiber-reinforced composites toughened with porous resin particles
US5202390A (en) * 1988-07-28 1993-04-13 Ciba-Geigy Corporation Butadiene/polar comonomer copolymer and aromatic reactive end group-containing prepolymer
ES2068911T3 (es) * 1988-07-28 1995-05-01 Ciba Geigy Ag Combinaciones de flexibilizadores para resinas epoxi.
US4977215A (en) * 1988-09-26 1990-12-11 Amoco Corporation Carboxylated rubber particles as tougheners for fiber reinforced composites
US5037689A (en) * 1989-02-17 1991-08-06 Basf Aktiengesellschaft Toughened thermosetting structural materials
US5120823A (en) * 1989-02-17 1992-06-09 Basf Aktiengesellschaft Toughened thermosetting structural materials
US5087657A (en) * 1989-02-23 1992-02-11 Amoco Corporation Fiber-reinforced composites toughened with resin particles
EP0392348A3 (en) * 1989-04-14 1991-12-27 Cytec Technology Corp. Toughened thermosetting structural materials
US5244719A (en) * 1990-10-23 1993-09-14 Amoco Corporation Prepreg with improved room temperature storage stability
US5151471A (en) * 1990-10-23 1992-09-29 Amoco Corporation Epoxy matrix resin formulations with improved storage stability containing powdered diamine dispersions
CA2044787A1 (en) * 1990-10-31 1992-05-01 Shahid P. Qureshi Fiber-reinforced composites toughened with porous resin particles
CA2055059A1 (en) * 1990-11-16 1992-05-17 Anita N. Chan Damage tolerant composites containing infusible particles
DE4039715A1 (de) * 1990-12-13 1992-06-17 Basf Ag Epoxidharzmischungen fuer faserverbundwerkstoffe
US5268223A (en) * 1991-05-31 1993-12-07 Amoco Corporation Toughened fiber-reinforced composites
DE69232851T2 (de) * 1991-07-30 2003-09-04 Cytec Technology Corp., West Paterson Gehärtete, faserverstärkte härtbare Harzmatrixprepregs und Verbundstoffe daraus
US5532296A (en) * 1991-07-30 1996-07-02 Cytec Technology Corp. Bismaleimide resin systems toughened by addition of preformed functionalized low Tg elastomer particles
US5932635A (en) * 1991-07-30 1999-08-03 Cytec Technology Corp. Tackified prepreg systems
EP0532893A2 (en) * 1991-08-09 1993-03-24 Hercules Incorporated Depolymerization of polymers and their use in thermoset compositions and composites
EP0564235B1 (en) * 1992-03-30 1998-12-09 Toray Industries, Inc. Prepreg and composites
CA2112146A1 (en) * 1992-12-23 1994-06-24 Nitya P. Khasat Polydicyclopentadiene having improved stability and toughened with polymeric particles
US5360840A (en) * 1992-12-29 1994-11-01 Hercules Incorporated Epoxy resin compositions with improved storage stability
US5519177A (en) * 1993-05-19 1996-05-21 Ibiden Co., Ltd. Adhesives, adhesive layers for electroless plating and printed circuit boards
US5985431A (en) * 1994-12-02 1999-11-16 Toray Industries, Inc. Prepreg, and a fiber reinforced composite material
JPH0925393A (ja) * 1995-05-09 1997-01-28 Toray Ind Inc 繊維強化複合材料用エポキシ樹脂組成物、プリプレグおよび繊維強化複合材料
WO1997031052A1 (en) 1996-02-21 1997-08-28 Toray Industries, Inc. Epoxy resin composition for fiber-reinforced composite material, yarn prepreg, and process and apparatus for preparing the same
EP0820858B1 (en) * 1996-07-22 2000-11-02 Hexcel Corporation Honeycomb core materials with particulate reinforcement
US5945253A (en) * 1996-08-29 1999-08-31 Xerox Corporation High performance curable polymers and processes for the preparation thereof
US8105690B2 (en) 1998-03-03 2012-01-31 Ppg Industries Ohio, Inc Fiber product coated with particles to adjust the friction of the coating and the interfilament bonding
US6419981B1 (en) 1998-03-03 2002-07-16 Ppg Industries Ohio, Inc. Impregnated glass fiber strands and products including the same
US6593255B1 (en) 1998-03-03 2003-07-15 Ppg Industries Ohio, Inc. Impregnated glass fiber strands and products including the same
US6949289B1 (en) 1998-03-03 2005-09-27 Ppg Industries Ohio, Inc. Impregnated glass fiber strands and products including the same
US8062746B2 (en) 2003-03-10 2011-11-22 Ppg Industries, Inc. Resin compatible yarn binder and uses thereof
US7354641B2 (en) 2004-10-12 2008-04-08 Ppg Industries Ohio, Inc. Resin compatible yarn binder and uses thereof
US20070104933A1 (en) * 2005-11-04 2007-05-10 Hamid Saadatmanesh Reinforced structural member and method of forming
US8810908B2 (en) * 2008-03-18 2014-08-19 Stereo Display, Inc. Binoculars with micromirror array lenses
DE102009001855A1 (de) 2009-03-25 2010-09-30 Henkel Ag & Co. Kgaa Verfahren zur Herstellung eines faserhaltigen Verbundwerkstoffs
WO2015033998A1 (ja) * 2013-09-06 2015-03-12 ダイセル・エボニック株式会社 繊維強化樹脂およびその製造方法並びに成形品
WO2025132403A2 (en) * 2023-12-20 2025-06-26 Solvay Specialty Polymers Usa, Llc Upcycling of polyarylethersulfone to make a reactive macromer product

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3174977A (en) * 1959-09-28 1965-03-23 Flintkote Co Plastic compositions for flooring
US3837904A (en) * 1970-03-09 1974-09-24 Great Lakes Carbon Corp A method of sizing carbon fibers
US3926904A (en) * 1974-09-30 1975-12-16 United Technologies Corp Curable crack-resistant epoxy resin
US3926903A (en) * 1974-09-30 1975-12-16 United Technologies Corp Curable crack-resistant epoxy resin
US4195113A (en) * 1975-03-12 1980-03-25 Desoto, Inc. Encapsulated impregnated rovings
US4187347A (en) * 1975-03-12 1980-02-05 Desoto, Inc. Encapsulated impregnated rovings
US4220686A (en) * 1975-03-12 1980-09-02 Desoto, Inc. Encapsulated impregnated rovings
US4264655A (en) * 1976-04-05 1981-04-28 Desoto, Inc. Encapsulated impregnated rovings
US4222918A (en) * 1979-03-19 1980-09-16 Desoto, Inc. Aqueous emulsions, methods of making the same and impregnated rovings made from the emulsions
ZA84551B (en) * 1983-06-30 1985-03-27 Union Carbide Corp Epoxy compositions containing oligomeric diamine hardeners and high strength composities therefrom
US4539253A (en) * 1984-03-30 1985-09-03 American Cyanamid Co. High impact strength fiber resin matrix composites
US4656208A (en) * 1985-02-19 1987-04-07 Hercules Incorporated Thermosetting epoxy resin compositions and thermosets therefrom
US4680076A (en) * 1986-08-28 1987-07-14 Hercules Incorporated Multiphase epoxy thermosets having rubber within disperse phase

Also Published As

Publication number Publication date
EP0252725B1 (en) 1993-11-03
DE3788007D1 (de) 1993-12-09
IL82916A (en) 1990-12-23
DE3788007T2 (de) 1994-03-03
ATE96817T1 (de) 1993-11-15
NO872667D0 (no) 1987-06-25
BR8703486A (pt) 1988-03-22
DK356587A (da) 1988-01-10
EP0252725A3 (en) 1990-01-31
CA1300783C (en) 1992-05-12
NO872667L (no) 1988-01-11
US4863787A (en) 1989-09-05
IL82916A0 (en) 1987-12-20
DK356587D0 (da) 1987-07-09
EP0252725A2 (en) 1988-01-13

Similar Documents

Publication Publication Date Title
NO872667D0 (no) Skadebestandige kompositter inneholdende usmeltbare partikler.
Schinner et al. Recycling carbon-fiber-reinforced thermoplastic composites
CA2056034A1 (en) Prepregs, process for producing the same and laminates produced with the same
EP0885704A4 (en) CARBON FIBER PREPREGS AND METHOD FOR PRODUCING THE SAME
DE59906578D1 (de) Verfahren zur Herstellung eines mittels Kohlenstoffkurzfaser verstärkten Siliciumcarbid-Verbundwerkstoffes
EP0377194A3 (en) Toughened thermosetting structural materials
JPS6426651A (en) Production of prepreg
EP0133281A3 (en) Curable fibre reinforced epoxy resin composition
Chan et al. Damage tolerant composites containing infusible particles
Mantena et al. Dynamic mechanical properties of hybrid polyethylene/graphite composites
EP0297524A2 (en) Microcrack resistant composites
Poursartip et al. Intralaminar polyethylene fibre-carbon fibre hybrid laminates
DOREY et al. Carbon fibre surface treatment for adhesion to epoxy resins
Hartwig et al. Fibre Composites With Thermoplastic Matrices
MA Effect of fiber orientation and laminate thickness on the mechanical properties of PEEK/C. F. and PPS/C. F. after impact loading
MA et al. Toughening epoxy resin matrix for glass and carbon fibre composites- Effects of matrix toughness on the mechanical properties of fibre composites
Jarvie Characterization of dicyclopentadiene based cyanate ester resin mechanical and electrical properties of unreinforced resin castings and composites
Hoisington Modelling Toughening Concepts for High Performance Polymer Composites
JPH04306240A (ja) プリプレグ
Knutsson et al. Flexure tests of three fibrous composite materials
Wittich et al. Interlaminar fracture data of various continuous fiber reinforced composite laminates
Planitz-Penno New Duroplastic Matrix Resins for High-Resistance Fiber Composite Materials With Superior Properties Within the Ranges of Impact Behavior, Heat Resistance, and Resistance to Media
MORLEY The role of the matrix in the preparation and properties of carbon fibre composites
Adams et al. Electron Microscopic Study of the Morphology of Cured Epoxy Resin. Interim Report, July 1982-June 1984
LAYDEN et al. Silicon nitride whisker reinforced glass matrix composites(Patent)

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 252725

Country of ref document: ES