HUT68630A - Oxide-based, (very) hard grains coated with ceramics and method for producing those - Google Patents

Oxide-based, (very) hard grains coated with ceramics and method for producing those Download PDF

Info

Publication number
HUT68630A
HUT68630A HU9300365A HU9300365A HUT68630A HU T68630 A HUT68630 A HU T68630A HU 9300365 A HU9300365 A HU 9300365A HU 9300365 A HU9300365 A HU 9300365A HU T68630 A HUT68630 A HU T68630A
Authority
HU
Hungary
Prior art keywords
coated
particles
binder
glaze
oxide
Prior art date
Application number
HU9300365A
Other languages
English (en)
Other versions
HU9300365D0 (en
Inventor
Reiner Kunz
Rudolf Strittmatter
Albert Kerber
Bernhard Vierus
Original Assignee
Lonza Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lonza Ag filed Critical Lonza Ag
Publication of HU9300365D0 publication Critical patent/HU9300365D0/hu
Publication of HUT68630A publication Critical patent/HUT68630A/hu

Description

A találmány oxidbázisú, különösen korund bázisú, nagy keménységű szemcsékre vonatkozik, amelyeket színes kerámia-bevonat vesz körül. A találmány továbbá a szemcsék előállítására is vonatkozik. A találmány szerinti szemcsék színező, kopásgátló és érdesítő komponensként alkalmazhatók kerámiai mázban, zománcban, festékanyagokban és bevonatokban.
A mechanikai tulajdonságok, különösen a kopásállóság és a csúszással szembeni biztonság növelése céljából nagy terhelésnek kitett felületekbe gyakran nagy keménységű szemcséket dolgoznak be. Az ilyen felületek példájaként a kerámiai padlócsempe, ill. annak máza nevezhető meg, amely vizes blokkokban, nyilvános és privát helyiségekben egyaránt található. Ide tartoznak az egyéb anyagokból (műanyag, műkő) készült padlóburkolatok is, amelyek hasonló terheléseknek vannak kitéve. Nagy keménységű szemcseként főleg korundrészecskéket alkalmaznak, mert ezek - nem-oxidos kemény anyagokkal, pl. keményfémmel vagy sziliciumkarbiddal ellentétben - nemkívánatos kémiai reakció nélkül dolgozhatók be mázba és tűzománcba, és kedvező árak mellett kielégítő keménységet és kopásállóságot biztosítanak.
A kereskedelmi forgalomban kaphatú korundszemcsék egyik hátránya, hogy csak igen korlátozott mértékben színezhető);, illetve belőlük csak korlátozott mértékben alakítható ki díszített felület, ami főleg a belsőépítészet és a nyilvános épületek kialakítása területén korlátozást jelent. A korund szemcsék saját színe fehértől barnáig terjed árnyala faiban, vagy szürke, kékes, illetve különleges korundok esetén rózsaszín, ill. rubinpiros is lehet. A korund színe a kerámiai máz égetésekor megváltozik. Ezért kielégítő eredményt csak akkor érnek el, ha a máz színe körülbelül azonos a szemcsék színével, ami a színpalettát igen szűkíti és az összes intenzív szint kizárja. A mázban lévő szintestek (pigment) mennyiségének a szokásos érték felé történő emelése nem használ, mert egyrészt a korundszemcsék - feladatuknál fogva - a máz felületén kell, hogy helyezkedjenek el, másrészt a több szintest drágítja a terméket. Különböző színekből összetevő felület, ahol a máz és a szemcse másmás színű, például pettyezett felület kialakítása a fentiek miatt szintén alig lehetséges.
A találmány feladata ezért olyan oxidos keményszemcsék megalkotása volt, amelyek tetszőlegesen színezett mázba és egyéb felületekbe bedolgozhatok anélkül, hogy a szinhatást rontanának. Az új szemcsék bővítik a rendelkezésre álló színválasztékot emellett különleges felületképzéseket, pl. pettyezést, melírozást, márványozást és egyéb mintákat tesznek lehetővé.
A fenti feladatot a találmány szerint az 1. igénypontban igényelt, színes kerámiával bevont nagykeménységű szemcsékkel oldottuk meg.
Azt találtuk, hogy az oxidbázisú, nagy keménységű részecskék egy vagy több színes kerámiából és kötőanyagból álló burkolattal láthatók el.
így a kemény részecskék kívánó mechanikai tulajdon ságait hasznosíthatjuk anélkül, hogy az alkalmazási területen színezés vagy felületalakítás vonatkozásában korlátok volnának.
Színes kerámián itt (szervetlen) oxidokból izzítással előállított szervetlen vegyületek (pl. rutilok, spinellek, kromitok, aluminátok, ferritok stb.) értendők, amelyek kerámiai mázokban színező komponensként szerepelnek, és amelyekre jellemző, hogy kerámiai mázban nem vagy csak kevéssé oldódnak. Emellett - a felhasználási területen támasztott követelményektől függően - szervetlen pigmentet, egyfázisú vagy többfázisú fémoxidot stb., valamint színes fritteket alkalmazhatunk. Áttekintést ad például B. Römpp, Chemie-Lexikon, 9. kiadás, 4. köt, 1991, Georg Thieme Verlag Stuttgart, vagy W. Heinz, Silicat-Lexikon, 1. kiadás 1985, Akademie-Verlag Berlin, 226. old.
Az olyan felületen, amely nincs kitéve a 300 °C-ot meg-haladó hőmérsékletnek, például festék- vagy müanyagfelület, beton, a fentiekben említett színes kerámiák mindegyikét probléma nélkül lehet alkalmazni. Ha színes üvegfrittet csempék mázában alkalmazunk, a kemény részecskét körülvevő fritt részben egybeolvad a mázzal,ami - esetleg kívánatos melírizási hatást eredményez.Amennyiben szervetlen pigmentet alkalmazunk mázakban, minden egyes esetben előkisérlettel kell megvizsgálni, hogy a szervetlen pigment a máz égetési hőmérsékleten közömbösnek marad-e.
A találmány szerinti oxidbázisú, bevont kemény részecskék alapanyagaként előnyösen alumíniumoxidot, cirkó- 5 nium-oxidot, szilicium-oxidot, spinelleket vagy a felsoroltak keverékét alkalmazzuk, adott esetben a szokásos szennyezőkkel és/vagy adalékkal, például stabilizátorokkal vagy a szinterelést elősegítő anyagokkal együtt. Különösen előnyben részesítjük a korundot, főleg az olvasztott és a színtereit korundot.
A találmány értelmében burkolattal ellátott kemény részecskék szemcsemérete 0,03 mm és 3 mm, előnyösen 0,06 mm és 5 mm közötti. Különösen előnyösek a szűk tartományú szemcseméret-eloszlás, mint amilyet a 42-D-1984 és a 43-D-1984 FEPA-szabvány ismertet.
Méretüknél fogva a találmány szerinti részecskék jól dolgozhatók fel, mert ömleszthető, nem porzó, össze nem tapadó grízszerü terméket képeznek. Ezért a részecskék mind a száraz mázfelviteli eljárásban, mind a szokásos nedves felviteli eljárásban alkalmazhatók, automata berendezéssel jól szállíthatók és adagolhatok.
A bevonat nélküli szemcsék tömegére számítva a színes kerámiát 2-20 r%, előnyösen 5-10 t% mennyiségben alkalmazzuk. A konkrét mennyiség a színes kerámia szemcseméretétől, a szin kívánt erejétől, mélységétől és a kemény szemcsék szemcseméretétől függ.
Finom szemcséjű kerámia (pl. FEPA szerint F 220) esetén a kerámiai máz úgy színezhető be, hogy az optikai szinbenyomás teljesen homogén, olyan, amilyet a hagyományos mázszinezés eredményez a szintestek közvetlen adagolásával. Bebizonyosodott azonban, hogy a találmány szerinti, bevont ··«·· · ·· • · ···· ·· · • · ·· ···♦·· · ······ ·· · ·· kemény részecskék alkalmazása esetén ugyanahoz a szintelítettséghez sokkal kevesebb szintest szükséges, mint a hagyományos mázszinezés esetén. így például a száraz mázkeverék tömegére vonatkoztatva 7 t% mennyiségű színes bevonatú korundszemcséket adagolva (ezek max. 10 t% színtestet tartalmaznak, tehát a mázkeverékre vonatkoztatva összesen 0,7 t% szintest) ugyanazt a szintelítettséget érjük el, mint 5 t% szintest közvetlenül a mázkeverékhez történő adagolásával.
Ily módon a máz nehézfémtartalmát erősen csökkenthetjük anélkül, hogy más színtestekkel kelleni pótolni az elhagyott mennyiséget.
A bevonat képzésére kötőanyagként elvileg minden olyan anyag alkalmas, amely mind a kemény szemcsét, mind a szintestet kellően nedvesíti, eléggé tapadó réteget képez és a bevont részecskék tervbe vett alkalmazása során (például csempék égetése) nem fejt ki káros hatást.
Előnyös kötőanyagok az alábbiak: kovasav, kovasavsók színtelen üvegfrittel vagy enélkül, alumíniummonofosztat vagy a felsoroltak keverékei. Különösen előnyösen alkálifém-szilikátot (vízüveget), például nátronvízüveget alkalmazunk .
A találmány szerinti, bevonattal ellátott kemény szemcséket egyszerű, olcsó módon állíthatjuk elő. Például a bevonni kívánt kemény részecskéket először a kötőanyag oldatával vagy szuszpenziójával nedvesítjük, például hagyományos keverőben végzett egyszerű összekeverés, vagy a mozgatott szemcsékre való rápermetezés utján. Oldatként, • · ···« ·· · • · ·· ······ · ···· ·· ·« · ··
- 7 illetve szuszpenzióként előnyösen vízzel vagy más, könnyen párolgó folyadékkal készített oldatot vagy szuszpenziót alkalmazunk. Előnyösen nem sokkal több kötőanyagoldatot, ill. szuszpenziót alkalmazunk, mint amennyi a szemcsék egyenletes nedvesítéséhez és az adott mennyiségű szintest megkötéséhez szükséges. Ez a szükséges mennyiség a részecskék fajlagos felületétől ill. méretétől és az oldat, ill. szuszpenzió viszkozitásától függ.
A fentiek szerint nedvesített szemcséket a finom por alakú színtesttel összekeverjük, így egyenletes bevonat képződik. Előnyösen a kötőanyag és a szintest közötti tömegarányt úgy választjuk meg, hogy a kialakult bevonat külső felületén lényegében nincs felesleges kötőanyag (mert ha volna, a szemcsék könnyen összetapadnak). A szintest felvitele után a szemcséket szárítjuk. A további hőkezelés erősen a későbbi alkalmazási területtől függ, hőmérséklettartománya
- legalább 300 °C-tól (müanyag-felülettek, beton, színes üvegfrittel bevont korund alkalmazása csempemázban melírozott szinhatás eléréséhez)
- legfeljebb 1200 °C-ig terjed; ezen a hőmérsékleten a csempemáz kompionensének szánt szemcséket hőkezeljük, ha a bevont korund teljesen iners viselkedésére van szükség.
Utána adott esetben aglomeráljuk és/vagy szitázzuk az aglomerátumok eltávolítására és/vagy megszüntetésére.
A találmány szerint előállított, bevonattal ellátott • ·
- 8 kemény szemcsék egyik előnyös alkalmazási területe az, hogy kerámiai mázhoz vagy tűzzománchoz adagoljuk, elsősorban a kopásállóság növelésére és a felület érdesítésére, azaz a csúszáci veszély csökkentésére. E célból a szemcséket előnyösen a máz- ill. zománcréteg felületére szórjuk, vagy égetés előtt a por vagy vizes zagy alakjában felvitt mázvagy tűzzománc rétegre , vagy égetés közben. Emellett a részecskéket arra is használhatjuk, hogy a kész máz- vagy zománcréteg kinézését befolyásoljuk, például a felület szerkezetét megváltoztatjuk matt hatás létrehozására, vagy
- ha az alapmáz és a szemcsebevonat különböző szinű vagy szinintenzitású - pettyes mintát vagy hasonló effektusokat hozunk létre.
Ha szinezőként használjuk a találmány szerinti szemcséket, a máz, ill. zománc áttetszőségétől függően előnyös lehet, ha a szemcséket egyenletesen szétosztjuk a mázanyagban, vagy az un. máz alatti festékhez hasonlóan a szubsztrátumra helyezzük és mázzal fedjük le.
A találmány szerinti, bevont szemcséket különösen előnyösen szabad ég alatt vagy vizes blokkban elhelyezett vagy erős kopásnak kitett, főleg nyilvános épületekben és iparban felhasználásra kerülő padlócsempe mázába dolgozzuk be.
Más előnyös felhasználási terület az, hogy a találmány szerinti szemcséket műanyaghoz és bevonómasszához, például padló- és falbevonatok készítésére használható bevonómasszához adagolják. Ez esetben is a termék jó tulajdonsá• · Λ « · · • ·»·« · · * « « * »····· · ·« *· « ··
- 9 gai, így a kopásállóság és a szinadás, érvényesülnek.
A találmány szerinti bevont kemény szemcséket továbbá mechanikailag terhelt festékréteg létrehozásához használatos festékhez is adhatjuk.
Végül a találmány szerinti, bevont kemény szemcsék adalékként alkalmazható mükőmasszában, betonban vagy habarcsban.
A találmányt az alábbi példákkal közelebbről ismertetjük.
1. példa kg korundhoz (nemes korund, F-120 /= ds0 110 μπι/ szemcseméreteloszlású) 60 tf% nátronvízüveg (34,2 t% szilárdanyagtartalom, 8 t% Na2O, 26,6 t% SiO2, viszkozitás mintegy 70 mPa.mp) és 40 tf% víz elegyéből 25 ml-t adunk, és az elegyet lapátkeverőben 20 percen keresztül keverjük. Az ilyen módon egyenletesen nedvesített korundhoz 100 g például spinell típusú szintestet adunk (szemcseméret 100 % < 63 μιη) és a keverést további 20 percen át folytatjuk. A kapott korund részecskéket 150 °C-on szárítjuk 0,1 % maradéknedvességre (dobszárítóban, 4 óra meleg levegővel) Utána ellenőrzésképpen 212 μιη-θΞ szitán keresztül szitáljuk. A szitán átkerült anyagot 1000 °C-on, oxidáló légkörben (levegő) forgókemencében égetjük. Az átlagos tartózkodási idő 2 óra.
Lehűlés után a szemcséket lengőszitán, gummigolyók segítségével desagglomeráljuk és 212 μπ-es szitán át szitáljuk a megmaradt agglomerátumok eltávolítása céljából. A
termék ömleszthető szemcsékből áll, a szinbenyomás optikailag homogén.
2. példa
Az 1. példához analóg módon korund szemcséket bevonattal látunk el a korund tömegére vonatkoztatva 10 % szintest felhasználásával. Az alábbi szinü és összetételű
színtesteket használjuk:
zöld: c^2°3 95 %
a12°3 3 %
sio2 2 %
barna: ZnO 50 %
Fe2O3 25 %
Cr2O3 25 %
kék: Co304 20 %
A12O3 80 %
sárga: Pb3O4 40 %
Sb2O3 40 %
ZnO 10 %
CaO 10 %
Az alábbi táblázatban feltüntettük, hogy a hagyományos máz szinezéssel összehasonlítva a környezetszennyező anyagok mennyiségét (t%) milyen mértékben lehetett csökkenteni a ta«« * ·«« • ·
- 11 lálmány révén.
Táblázat
Szin Környezet- szennyező komponens 5 t% szintest közvetlen adagolása esetén 7 t% találmány szerinti bevont korund esetén
zöld Cr203 4,75* 0,67
barna ZnO 2,50 0,35
Cr2°3 1,25 0,18
kék Co3°4 1,00 0,14
sárga Pb3O4 2,00 0,28
Sb2O3 2,00 0,28
Zno 0,50 0,07
* A megadott 5 t%-ig hiányzó mennyiség a szintest azon komponensei, amelyek nem környezetszennyező, például AI2O3 , SiO2, Fe2O3._)

Claims (9)

1. Oxid bázisú kemény szemcse, azzal jellemezve, hogy bevonattal· rendelkezik, amely legalább egy kerámiai ^színtestből és legalább egy kötőanyagból áll.
2. Az 1. igénypont szerinti bevont kemény részecskék, azzal jellemezve, hogy az alapanyag alumíniumoxid, cirkóniumoxid, sziliciumoxid, spinell vagy a felsorolt oxidok keveréke.
3. A 2. igénypont szerinti bevont kemény részecskék, azzal jellemezve, hogy az alpanyag korund.
4. Az 1-3. igénypontok bármelyike szerinti bevont részecskék, azzal jellemezve, hogy a szemcsemérete 0,03 mm és 3 mm közötti.
z-Az 1-4. igénypontok bármelyike szerinti bevont részecskék, azzal jellemezve, hogy a kerámai szintest
.. mennyisége, a bevonat nélküli szemcsék tömegére vonatkoztatva
5-10 t%.
6. Az 1-5. igénypontok bármelyike szerinti részecskék, azzal jellemezve, hogy a kötőanyag kovasavból, kovasavsóból, színtelen üvegfrittből, alumínium-foszfátból vagy a felsoroltak keverékéből áll.
7. A 6. igénypont szerinti kemény részecskék, azzal jellemezve, hogy a kötőanyag alkálifém-szilikát.
8. Eljárás az 1-7. igénypontok bármelyike szerinti bevont részecskék előállítására, azzal jellemezve, hogy a °/G bevonni kívánt kemény részecskéket kötőanyag oldatával vagy szuszpenziójával nedvesítjük, majd a szükséges mennyiségű,
I
C° 1 finomra porított szintesttel összekeverjük és szárítjuk.
z ~ ~
9. A 8. igénypontok bármelyike szerinti eljárás, azzal jellemezve, hogy kötőanyag-oldatként vizes alkálifémszi- likát-oldatot alkalmazunk,_______.....-........— -------. A 8. vagy 9. igénypont szerinti eljárás, azzal jellemezve, hogy a keményszemcsék bevonatát szárítás után
300-1200 °C-on keményítjük ill. égetjük.
HU9300365A 1992-02-13 1993-02-12 Oxide-based, (very) hard grains coated with ceramics and method for producing those HUT68630A (en)