JPH03108539A - 多層包装体用積層シート、多層包装体及び多層包装体の製造方法 - Google Patents

多層包装体用積層シート、多層包装体及び多層包装体の製造方法

Info

Publication number
JPH03108539A
JPH03108539A JP1245207A JP24520789A JPH03108539A JP H03108539 A JPH03108539 A JP H03108539A JP 1245207 A JP1245207 A JP 1245207A JP 24520789 A JP24520789 A JP 24520789A JP H03108539 A JPH03108539 A JP H03108539A
Authority
JP
Japan
Prior art keywords
layer
multilayer
surface layer
laminated sheet
container
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP1245207A
Other languages
English (en)
Other versions
JPH0694209B2 (ja
Inventor
Yukio Takada
高田　幸夫
Takeshi Shinohara
剛 篠原
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Idemitsu Petrochemical Co Ltd
Original Assignee
Idemitsu Petrochemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Idemitsu Petrochemical Co Ltd filed Critical Idemitsu Petrochemical Co Ltd
Priority to JP24520789A priority Critical patent/JPH0694209B2/ja
Publication of JPH03108539A publication Critical patent/JPH03108539A/ja
Publication of JPH0694209B2 publication Critical patent/JPH0694209B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は軽量容器分野に用いられる多層包装体用積層シ
ート、そのシートを用いた多層包装体及び多層包装体の
製造方法に関するものである。さらに詳しくいえば、本
発明は、食品、飲料等の包装用、特に加熱殺菌包装用と
して好適に用いられる密封性、開封性ともに優れている
多層包装体とその多層包装体用積層シートに関する。本
発明はまた、その多層包装体の好適な製造方法に関する
。
しかし、これらの容器では未だ容器本体の最内層の切断
時のエツジ切れ特性が不十分であり、切断ができなかっ
たり、均一に切れずに容器本体の最内層が伸びてヒゲ等
が発生しピール惑に劣り、外観上からも好ましいものと
はいえないという問題がある。
〔従来の技術〕
従来、食品類などの包装のための軽量容器分野において
、密封性に優れるとともに開封性にも優れている各種の
易開封性容器が提案されている。
例えば、容器本体を積層構造として蓋材をヒートシール
した場合、この容器を開封する際、蓋材にヒートシール
された容器本体側の最内層とそれに接する層との層間を
剥離させ、該最内層をヒートシール部内側に設けられた
薄肉部でエツジ切れにより切断させる易開封性容器が提
案されている（特開昭６３−３０７０７３号公報、実開
昭６４−３９２７３号公報、特開昭６４−７０３７４号
公報）。
〔発明が解決しようとする課題〕 エツジ切れ特性を改良するための一般法としてエツジ切
れさせる層にポリエチレンワックス、アククチツクポリ
プロピレン等の低分子量分を配合する方法があるが、こ
の方法を上記の容器に応用すると、ボイルレトルト時に
低分子量分の溶出や層の劣化が起こり、また耐内容物性
、衛生性に劣るなどの問題が生じる。
そこで、本発明は蓋材をヒートシールした容器のシール
層に凹状の弱め線を設け、シール面と剥離面を異なる面
として、開封時に剥離したシール層を該弱め線でエツジ
切れさせて開封する多層包装体容器で、そのシール層の
エツジ切れによるカット性を向上させて、シールが完全
でかつ開封が容易なボイルレトルト殺菌可能な多層包装
体とその多層包装体用積層シートを提供しようとするも
のである。本発明はまた、その多層包装体の好適な製造
方法を提供しようとするものである。
〔課題を解決するための手段〕
本発明者らは前記課題を解決するため鋭意研究を重ねた
結果、シール層を剥離性表面層としてメルトインデック
スの異なる少なくとも２種の高密度ポリエチレンを用い
て形成することにより、エツジ切れによるカット性が向
上することを見出し本発明を完成するに至った。
すなわち本発明は、少な（とも剥離性表面層とこれに接
する層とからなり、該剥離性表面層がメルトインデック
スの異なる少なくとも２種の高密度ポリエチレンからな
る厚み５μｍ以上の層であることを特徴とする多層包装
体用積層シートを提供するものである。
本発明の多層包装体用積層シートは少なくとも剥離性表
面層とこれに接する層とからなる。
剥離性表面層の厚みは、５〜１５０μｍが好ましい、特
に好ましくは８〜１１００ｕであり、更に好ましくは８
〜５０μｍである。厚みが５μｍ未満では多層包装体に
用いた場合密封力不足となり、逆に１５０μｍを超える
とエツジ切れを起こさせるための凹状の弱め線形成によ
る核層の薄肉化が不良となる。
この剥離性表面層はメルトインデックスの異なる少なく
とも２種の高密度ポリエチレンからなるが、剥離性表面
層のメルトインデックスは０．０１〜３０の間であれば
特に制限されない、メルトインデックスの異なる高密度
ポリエチレンの数は２種とするのが好ましいが、２種を
超えても良い。
高密度ポリエチレンの数が２種の場合、両者のメルトイ
ンデックスの差は２以上であることが好ましい。特に好
ましくは４以上である。この差が２未満の場合には、エ
ツジ切れによるカット性が不足する。ここで、メルトイ
ンデックスの値は、ＪＩｓ　　Ｋ−７２１０に規定され
る条件（１９０℃、２．１６ｋｇ荷重、１０分間）で測
定した。
メルトインデックスの異なる２種の高密度ポリエチレン
の配合比は、メルトインデックスの大きい高密度ポリエ
チレン：メルトインデックスの小さい高密度ポリエチレ
ンが重量比で５：９５〜９５：５であることが好ましい
、特に好ましくは２０：８０〜８０：２０である。この
範囲外では、得られる剥離性表面層のエツジ切れによる
カット性が不足する。上記の配合比でメルトインデック
スの差が２以上の高密度ポリエチレンを、得られる剥離
性表面層のメルトインデックスがｏ、ｏｉ〜３０の間と
なるようにすることが好ましい。
本発明の多層包装体用積層シートは共押出法により好適
に成形されるが、その場合にはメルトインデックスの小
さい高密度ポリエチレンの割合がメルトインデックスの
大きい高密度ポリエチレンの割合より高い方が押出上、
安定で好ましい。
剥離性表面層に接する層は、上記の眉間剥離強度の条件
を満たすものであれば特に制限はなく、ポリ−オレフィ
ン系樹脂、ポリスチレン系樹脂、ポリアミド系樹脂、ポ
リエステル系樹脂、ポリカーボネート系樹脂又はこれら
の混合物又はこれらに熱可塑性エラストマー、各種添加
剤若しくは無機充填剤を５〜７０重量％混合した樹脂あ
るいは金属箔などが挙げられる。
剥離性表面層とこれに接する層との眉間は、この多層包
装体用積層シートを容器本体に熱成形し蓋材をヒートシ
ールして多層包装体としたとき、開封時の剥離面となる
。従って、剥離性表面層とこれに接する層との眉間の剥
離強度は、シール面すなわち蓋材と剥離性表面層との層
間のヒートシール強度より小さく、蓋材を剥離する際剥
離面で剥離が開始され蓋材の開封が容易である強度範囲
とする。上記範囲であれば特に制限はないが、好ましく
は２００〜１５００ｇ／１５ｎｍ（引張速度３００■／
ｍｉｎ、以下同じ）であり、特に好ましくは３００〜１
２００ｇ／１５ｍｍ程度である。
包装体の使用分野によって適宜決定すればよい。
以上の剥離性表面層とこれに接する層とからなる本発明
の多層包装体用積層シートは共押出法により好適に形成
される。すなわち、メルトインデックスの異なる少なく
とも２種のビーズ状、ペレット状等の高密度ポリエチレ
ンは、好ましくは押出機中で混合され、押し出されて剥
離性表面層となる。同時に、共押出により、この剥離性
表面層に接する層も成形され、本発明の多層包装体用積
層シートとなる。ここで、押出機中でのメルトインデッ
クスの異なる少なくとも２種の高密度ポリエチレンが混
合される温度は１５０〜３００″Ｃが好ましい。特に好
ましくは１９０〜２５０℃である。
あるいは、メルトインデックスの異なる少なくとも２種
の高密度ポリエチレンから５μｍ以上の剥離性表面層を
成形し、これを剥離性表面層に接する層とラミネートし
て所望の多層包装体用積層シートとすることもできる。
ラミネート加工としては、例えばエキストルージョンラ
ミネート、ホットメルトラミネート、ドライラミネート
、ウェットラミネートなどの方法を用いることができる
。
本発明の多層包装体用積層シートは上記のような材料か
らなる２層のものでもよいが、ガスバリヤ−性の向上や
、容器とした場合の変形を少なくする目的で、さらに他
の材料からなる層を積層した３層以上の積層シートとし
てもよい。他の材料からなる層としては、例えばエチレ
ン−ビニルアルコール共重合体、ポリ塩化ビニリデン、
ナイロン、ポリエチレンテレフタレートなどの樹脂層や
アルミ蒸着層などのガスバリヤ−性に優れたものが挙げ
られる。これら他の材料からなる層は、１層のみでもよ
いし、２層以上からなる多層体であってもよく、また、
無機充填剤１０〜８０重量％を含有する樹脂層を有する
ものであってもよい。
本発明はまた、上記の多層包装体用積層シートを熱成形
して得られた開口部とその周縁にフランジ部を有する容
器と該容器のフランジ部にシールされた蓋材とからなり
、該フランジ部のシール部よりも開口部側の表面剥離層
に凹状の弱め線が形成されていることを特徴とする多層
包装体を提供することである。
以下、本発明の多層包装体を図面に基づいて詳細に説明
する。第１図（ａ）は本発明の多層包装体の一例を説明
する断面説明図である。
第１図（ａ）において、ｌは多層容器本体の剥離性表面
層、２はこれに接する層（外Ｎ）、３はフランジ部であ
る。容器に内容物を充填したのち蓋材４で蓋をし、この
蓋材を多層容器本体の剥離性表面層１とフランジ部３で
タイトにヒートシールする。５はヒートシール部の位置
を示し、多層容器本体と蓋材は多層容器本体のフランジ
部で難剥離ヒートシールされている。ヒートシール部の
内側端と外側端には剥離性表面層に凹状の弱め線６．７
が形成されている。
ヒートシール部外側端の剥離性表面層の凹状の弱め線７
は、開封時に多層容器本体の剥離面すなわち剥離性表面
層とこれに接する層との眉間の剥離を容易にするための
もので、多層容器の剥離性表面層の剥離を他の手段で開
始する場合には必ずしも必要ではない。なお外側端に凹
状の弱め腺を設ける場合には少なくとも開封開始部に設
ければよい。
剥離性表面層のヒートシール部の内側端の凹状の弱め線
６は蓋材を剥がす際にフランジ部内周で蓋材とともに剥
離した多層容器本体の剥離性表面層を切断し開封するた
めに必要なものである。この凹状の弱め線は蓋材を剥が
すときに剥離性表面層を容易に切断できるものであれば
どのようなものでもよい。剥離性表面層の剥離性の点か
らは、凹状の弱め線は凹状の先端が多層容器の剥離性表
面層に接する層（外層）まで接していることが好ましい
。この剥離性表面層は、本発明のメルトインデックスの
異なる少なくとも２種の高密度ポリエチレンからなる厚
みは５μｍ以上の層であり、上記の凹状の弱め線でのエ
ツジ切れによるカット性に優れている。
また、この凹状の弱め線は円、三角形、四角形など環状
にフランジ内周に全周にわたって設けてもよいし、一部
は残しておいてもよい０Ｍ材の一部がついたまま剥がす
ような場合には、そこの部分だけ凹状の弱め線を設けな
いようにする。
また、凹状の弱め線が蓋材を介して押圧形成されている
と、製造上工程が簡潔となり好ましい。
本発明の多層容器本体の形状は特に限定されるものでは
ないが、通常、円、四角などであり、この形状のフラン
ジ部に沿って蓋材が環状にヒートシールされる。また、
カップ状であっもトレー状であってもよく、フランジ部
周縁にリブまたはカールが設けられているものであって
もよい。
次に、蓋材の材料は単層フィルムであっても多層フィル
ムであってもいずれでもよく、特に制限はない。多層フ
ィルムを用いた場合について説明すると、プラスチック
の単層フィルム、多層フィルム、紙、アルミ箔又はこれ
らの複合材料等からなる基材と、ポリエチレン、ポリプ
ロピレン、エチレン−α−オレフィン共重合体、エチレ
ン−酢酸ビニル共重合体等からなる多層材料の剥離性表
面層との易ヒートシール性を有する樹脂からなるシーラ
ント層とからなっているものが好適に用いられる。
なお、本発明の多層包装体にあっては、容器本体に剥離
性表面層を存する本発明の多層包装体用積層シートを有
する限り、多層材料の剥離性表面層の内側に必要に応じ
て、シール層など他の層を有していてもよい。
更に本発明は、本発明の多層包装体用積層シートを開口
部とその周縁にフランジ部を有する容器に熱成形し、少
なくとも内側の周縁部に凸状部を有するシールリングを
用いて蓋材を該容器フランジ部にヒートシールすること
を特徴とする多層包装体の製造方法を提供するものであ
る。
本発明の多層包装体は以下の方法により容易に好適に作
製される。
本発明の多層包装体用積層シートを真空成形、圧空成形
などにより成形したり、多層射出成形、多層射出プロー
成形、多層ブロー成形などにより、開口部とその周縁に
フランジ部を有する容器に熱成形する。あるいは必要に
応じて紙などの容器の内側に多層フィルムを熱成形する
ことができる。
上記の容器のフランジ部に蓋材を設置して、少な（とも
内側の周縁部に凸状部を存するシールリングを用いて該
蓋材をヒートシールする。
第１図（ｂ）は第１図（ａ）に示す多層包装体をヒート
シールするシールリングについて説明する断面説明図で
ある。９はシールリングで、このシールリングを用いて
剥離性表面層を蓋材を介して押圧することにより剥離性
表面層に凹状の弱め線を形成する。
シールリング９には周縁部に通常１０〜５００μｍ１好
ましくは２０〜３００ｔＩｍの高さの凸状部１０が設け
られており、ヒートシール時にヒートシール部の内側端
に、さらには必要に応じてヒートシール部の外側端に凹
状の弱め線を形成する。
ヒートシールリングは、第１図（ｂ）に示すように、周
縁部に凸状部を有し、ヒートシール部の端部に剥離性表
面層の凹部を形成できるものであれば特に制限はない。
第２図は本発明に用いるヒートシールリングの他の好ま
しい態様を示すものである。ヒートシールリングの内側
周縁部の凸状部に対応する位置近傍の包装体の蓋材及び
剥離性表面層に凹状の弱め線が形成されており、ヒート
シール部の内側端の剥離性表面層の凹状の弱め線から外
側に向かって、通常１〜工０ａＩａｌ、好ましくは１．
５から５１１ｍの非ヒートシール部が形成されている。
１１はこの非ヒートシール部の位置を示している。
第３図は本発明の他の態様を示すもので、多層容器のフ
ランジ部の外側端までヒートシールされ、剥離性表面層
に外側の凹状の弱め線が設けられていない例である。
第４図は本発明のヒートシール部の形状の好ましい態様
を示す平面図で、凹状の弱め線は環状にフランジ部全周
にわたって形成されており、つまみ部付近に凸状の先端
部を有しており、開封を一層容易にしている。
以上、本発明の多層包装体及び多層包装体の製造方法に
おいて、本発明の多層包装体用積層シートが多層容器本
体に熱成形されている場合について説明したが、本発明
は多層包装体用積層シートを蓋材として用いる場合等シ
ート状のものについても包装体が袋状のものについても
適用できる。
〔作用〕
メルトインデックスの異なる少なくとも２種の高密度ポ
リエチレンからなる剥離性表面層では分子量分布に起因
する高密度ポリエチレン間の相分離によりエツジ切れ性
能が改善される一方、前記高密度ポリエチレンと同一メ
ルトインデックスを有する単一高密度ポリエチレンでは
当該性能が現れないものと推定される。
本発明の多層包装体に商品を封入し、蓋材をヒートシー
ルしたものを開封するときは以下のような動作で簡単に
開封することができる。
例えば、第１図（ａ）において、つまみ部８を上方にも
ちあげる。すると、剥離性表面層の凹状の弱め線７のと
ころから剥離性表面層１とそれに接する層２との眉間で
剥離が開始され、それに続いてヒートシール部外縁の剥
離性表面層の凹状の弱め線７が切断され、それにつれて
剥離性表面Ｎ１とこれに接する層２の間で剥離が進行し
、剥離性表面層の凹状の弱めｖＡ６のところまで剥離性
表面層が剥離し、弱め線６でのエツジ切れにより蓋材が
剥がされる。本発明の多層包装体用積層シートを用いる
ことによりこのときのエツジ切れによるカット性が優れ
ているので、蓋材と多層包装容器とが密封性よく難剥離
ヒートシールされていても容易に開封できる。また、開
封したあとの剥離面の外観も美麗である。
〔実施例］ 次に実施例により本発明をさらに詳細に説明するが、本
発明はこれらの例によってなんら限定されるものではな
い。
実施例１〜８及び比較例１〜７ 第１表に示すメルトインデックス（Ｍ　Ｉ　）を有し、
第１表に示す配合比のペレット状の高密度ポリエチレン
のベースレジンと配合物とを押出機に入れた（第２表に
使用した樹脂の特性、商品名等を示す。）。これを２３
０℃で混合しながら、これが剥離性表面層となるように
共押出成形によりこの剥離性表面層（Ａ層）とこれに接
する層（Ｂ層）の２層からなる多層包装体用積層シート
を成形した。ここで、Ａ層の厚みは３〜１５０μｍで第
１表に示す厚みとした。また、Ｂ層の厚みは８００μｍ
とし、材料はＥ−１００Ｇ／ペトロセン１７２＝８０／
２０重量％とじた。
この多層包装体用積層シートを真空、圧空成形により、
６０ｗφＸ４０ｍｍ（高さ）のフランジ付（フランジ幅
８ｍｍ）の丸型多層容器を成形した。
この容器に蓋材として、配向ナイロン／ポリ塩化ビニリ
デン／直鎖状低密度ポリエチレン（１５μ／２０μ７６
０μ）からなる多層フィルムをかぶせ、フランジ部でヒ
ートシールリングを用い温度１７０　’Ｃ１圧力５ｋｇ
／ｃｄ、　１秒でヒートシールを行った。なお、ヒート
シールリングはシリンダー径８０閣φであり、その内周
縁の直径は６３ｍｍ、ヒートシール部幅は１０ｍｍであ
り、シールリングの内周縁部には、５０μｍの環状の凸
状部が設けられており、ヒートシールはフランジ部の外
側端まで行った（第３図）、ヒートシールにより得られ
た凹状の弱め線の内側端での剥離性表面層の厚みは実質
ゼロであった。
このようにして得られた密封容器について、蓋材を剥離
したときのカット性、耐圧性、シール性、′）耐＃本訃
レトルト性（１２０°Ｃ１３０分）につい３字ｎて各々
評価を行った結果を第１表に示す。
（以下余白） 〔発明の効果〕 本発明により、開封が容易に行え剥離時のカット性に優
れ剥離面の外観が良好な、シール強度が斉く密封性に優
れたボイルやレトルト処理が可能である多層包装体及び
その多層包装体用積層シートを得ることができる。また
、その多層包装体を容易に広いシール条件範囲で製造す
ることの可能な多層包装体の製造方法を得ることができ
る。
【図面の簡単な説明】
第１図（ａ）は本発明の多層包装体の一例を示し、第１
図（ハ）は第１図（ａ）の包装体のヒートシールを行う
シールリングを示す断面説明図、第２図および第３図は
本発明の多層包装体及びシールリングの他の例を示す部
分断面図、第４図は、ヒートシール部のこのましい形状
を示す平面図である。 符号の説明 １　剥離性表面層 ２　剥離性表面層に接する層 ３　フランジ部　　　　４　Ｍ材 ヒートシール部　　６　凹状の弱め線 凹状の弱め線　　　８　つまみ部 シールリング　　　ｌＯ凸状部 毛１図

Claims (1)

  1. 【特許請求の範囲】 １、少なくとも剥離性表面層とこれに接する層とからな
    り、該剥離性表面層がメルトインデックスの異なる少な
    くとも２種の高密度ポリエチレンからなる厚み５μｍ以
    上の層であることを特徴とする多層包装体用積層シート
    。 ２、メルトインデックスの異なる少なくとも２種の高密
    度ポリエチレンが、メルトインデックスの差が２以上の
    ものである請求項１記載の多層包装体用積層シート。 ３、請求項１記載の多層包装体用積層シートを熱成形し
    て得られた開口部とその周縁にフランジ部を有する容器
    と該容器のフランジ部にシールされた蓋材とからなり、
    該フランジ部のシール部よりも開口部側の表面剥離層に
    凹状の弱め線が形成されていることを特徴とする多層包
    装体。 ４、弱め線が蓋材を介して押圧形成されたものである請
    求項３記載の多層包装体。 ５、請求項１記載の多層包装体用積層シートを開口部と
    その周縁にフランジ部を有する容器に熱成形し、少なく
    とも内側の周縁部に凸状部を有するシールリングを用い
    て蓋材を該容器フランジ部にヒートシールすることを特
    徴とする多層包装体の製造方法。
JP24520789A 1989-09-22 1989-09-22 多層包装体用積層シート、多層包装体及び多層包装体の製造方法 Expired - Lifetime JPH0694209B2 (ja)