JPH04259593A - 光記録媒体 - Google Patents
光記録媒体Info
- Publication number
- JPH04259593A JPH04259593A JP3020026A JP2002691A JPH04259593A JP H04259593 A JPH04259593 A JP H04259593A JP 3020026 A JP3020026 A JP 3020026A JP 2002691 A JP2002691 A JP 2002691A JP H04259593 A JPH04259593 A JP H04259593A
- Authority
- JP
- Japan
- Prior art keywords
- recording
- recording film
- recording medium
- optical recording
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【０００１】
【産業上の利用分野】本発明は、光記録媒体、特にピッ
ト形成タイプの記録膜を有する光記録媒体に関する。
ト形成タイプの記録膜を有する光記録媒体に関する。
【０００２】
【従来の技術】光記録媒体は、一般に記憶容量が大きく
、しかも書き込みまたは読み出しが非接触で行なわれる
等、優れた特徴を備えており、その開発が従来から活発
に行なわれてきている。このような光記録媒体の１例と
して、例えば追記型光ディスクがあり、このものは、記
録膜の微少面積にレーザビームを集光させ、それを熱エ
ネルギーに変換し、記録膜の性状を変えて（ピット形成
）記録し、未記録部分との反射光量の違いによって再生
を行うようにしている。
、しかも書き込みまたは読み出しが非接触で行なわれる
等、優れた特徴を備えており、その開発が従来から活発
に行なわれてきている。このような光記録媒体の１例と
して、例えば追記型光ディスクがあり、このものは、記
録膜の微少面積にレーザビームを集光させ、それを熱エ
ネルギーに変換し、記録膜の性状を変えて（ピット形成
）記録し、未記録部分との反射光量の違いによって再生
を行うようにしている。
【０００３】このような媒体の記録膜の材質としては、
大きな反射率変化を与えるものが好ましく、また無害で
あること、そして、より高感度化する必要があること、
より製造コストを安価にする必要があることから、色素
を主とした有機材料系の記録膜を用いた光記録媒体の提
案が種々なされている（特開昭第５８−１１２７９０号
公報、同第５８−１１４９８９号公報、同第５８−１２
５２４６号公報、同第６０−７１２９５号公報等）。
大きな反射率変化を与えるものが好ましく、また無害で
あること、そして、より高感度化する必要があること、
より製造コストを安価にする必要があることから、色素
を主とした有機材料系の記録膜を用いた光記録媒体の提
案が種々なされている（特開昭第５８−１１２７９０号
公報、同第５８−１１４９８９号公報、同第５８−１２
５２４６号公報、同第６０−７１２９５号公報等）。
【０００４】
【発明が解決しようとする課題】しかしながら、従来の
記録材料のなかにはレーザビームを照射しピットを形成
した場合、形状の整ったきれいなピットが形成されない
ものがあり、ピット後尾部が融解流動し、尾を引く形状
となるという問題が生じていた。そのため、記録再生波
形において、いわゆるハンプ（ｈｕｍｐ）現象が生じ、
十分な再生特性がとれないという不都合が生じていた。
記録材料のなかにはレーザビームを照射しピットを形成
した場合、形状の整ったきれいなピットが形成されない
ものがあり、ピット後尾部が融解流動し、尾を引く形状
となるという問題が生じていた。そのため、記録再生波
形において、いわゆるハンプ（ｈｕｍｐ）現象が生じ、
十分な再生特性がとれないという不都合が生じていた。
【０００５】
【発明が解決しようとする課題】本発明は、このような
実情に鑑み、創案されたものであり、最適なピットが形
成され、十分な再生特性を有する光記録媒体を提供する
ことにある。
実情に鑑み、創案されたものであり、最適なピットが形
成され、十分な再生特性を有する光記録媒体を提供する
ことにある。
【０００６】
【課題を解決するための手段】上記課題を解決するため
、本発明は基板上に記録膜を有する光記録媒体において
、前記記録膜は、融解点と分解点との差が１００℃（度
）以下の記録材料を含有するように構成した。本発明に
用いられる基板は、光透過性であれば特に限定はないが
、生産性向上の観点から、いわゆる射出成形基板が好ま
しい。射出成形基板とは、平板状の基板と、この基板の
片面に設けられるグルーブ、アドレス等とを同一材料で
一体的にワンショットの射出成形で形成した基板をいう
。
、本発明は基板上に記録膜を有する光記録媒体において
、前記記録膜は、融解点と分解点との差が１００℃（度
）以下の記録材料を含有するように構成した。本発明に
用いられる基板は、光透過性であれば特に限定はないが
、生産性向上の観点から、いわゆる射出成形基板が好ま
しい。射出成形基板とは、平板状の基板と、この基板の
片面に設けられるグルーブ、アドレス等とを同一材料で
一体的にワンショットの射出成形で形成した基板をいう
。
【０００７】このような基板は、例えばポリカーボネー
ト樹脂（ＰＣ）、ポリメタクリル酸メチル樹脂（ＰＭＭ
Ａ）等のプラスチック材料から形成される。このような
基板上には、記録膜が成膜され、この記録膜には、融解
点と分解点との差が１００℃以下、特に、０〜７０℃の
記録材料が含有される。この差が１００℃を越えると、
レーザビームを照射しピットを形成した場合、形状の整
ったきれいなピットが形成されず、ピット後尾部が融解
流動し、尾を引く形状となり、そのため、記録再生波形
において、いわゆるハンプ（ｈｕｍｐ）現象が生じ、十
分な再生特性がとれない。なお、分解点とは、物質の熱
分解が始まる温度をいい、大気圧下で測定が行われる。
ト樹脂（ＰＣ）、ポリメタクリル酸メチル樹脂（ＰＭＭ
Ａ）等のプラスチック材料から形成される。このような
基板上には、記録膜が成膜され、この記録膜には、融解
点と分解点との差が１００℃以下、特に、０〜７０℃の
記録材料が含有される。この差が１００℃を越えると、
レーザビームを照射しピットを形成した場合、形状の整
ったきれいなピットが形成されず、ピット後尾部が融解
流動し、尾を引く形状となり、そのため、記録再生波形
において、いわゆるハンプ（ｈｕｍｐ）現象が生じ、十
分な再生特性がとれない。なお、分解点とは、物質の熱
分解が始まる温度をいい、大気圧下で測定が行われる。
【０００８】このような物性を有する記録材料の具体例
としては、シアニン系の色素に多く見出される。このよ
うな記録材料を含有する記録膜は、例えばスピンコート
法等の常用手段により塗設される。塗設される記録膜の
厚さは４０〜３００ｎｍ程度である。なお、塗布に用い
る溶媒としては、ジアセトンアルコール、エチルセロソ
ルブ、メチルセロソルブ、イソホロン、メタノール、テ
トラフルオロプロパノール等が挙げられる。
としては、シアニン系の色素に多く見出される。このよ
うな記録材料を含有する記録膜は、例えばスピンコート
法等の常用手段により塗設される。塗設される記録膜の
厚さは４０〜３００ｎｍ程度である。なお、塗布に用い
る溶媒としては、ジアセトンアルコール、エチルセロソ
ルブ、メチルセロソルブ、イソホロン、メタノール、テ
トラフルオロプロパノール等が挙げられる。
【０００９】なお、本発明の記録膜には、上記記録材料
のほかに、光劣化防止のためのクエンチャ等を含有して
もよい。本発明の記録媒体の記録再生に適用されるレー
ザ光は、例えば波長７６０〜８３０ｎｍの半導体レーザ
用いられる。本発明の記録媒体は、前述したように、い
わゆる射出成形基板上に記録膜を設けて形成されるが、
このものを２枚用意し、記録膜を対向して配置した、い
わゆるエアーサンドイッチ構造とすることも可能であり
、また反射膜等を付帯させ保護層を設ける密着型として
もよく、いずれも記録光照射に基板側から実行される。
のほかに、光劣化防止のためのクエンチャ等を含有して
もよい。本発明の記録媒体の記録再生に適用されるレー
ザ光は、例えば波長７６０〜８３０ｎｍの半導体レーザ
用いられる。本発明の記録媒体は、前述したように、い
わゆる射出成形基板上に記録膜を設けて形成されるが、
このものを２枚用意し、記録膜を対向して配置した、い
わゆるエアーサンドイッチ構造とすることも可能であり
、また反射膜等を付帯させ保護層を設ける密着型として
もよく、いずれも記録光照射に基板側から実行される。
【００１０】
【作用】本発明の媒体には、一般に回転下において、記
録光がパルス状に照射される。このとき記録膜の一部が
融解、除去されピットが形成される。このように形成さ
れたピットは、やはり媒体の回転下、読み出し光の反射
光の差を検出することによって行なわれる。
録光がパルス状に照射される。このとき記録膜の一部が
融解、除去されピットが形成される。このように形成さ
れたピットは、やはり媒体の回転下、読み出し光の反射
光の差を検出することによって行なわれる。
【００１１】
【実施例】以下、本発明の実施例を示して本発明をさら
に詳細に説明する。記録膜に含有される記録材料として
は、下記構造式で示される２種の有機色素（本発明）を
用い、これらをエチルセロソルブ溶媒中に溶解し、直径
１２ｃｍのポリカーボネート（ＰＣ）基板上に、６０ｎ
ｍの厚さに塗設し、その後、反射層として金をコートと
し、この上に保護層を設け、本発明の光記録媒体（本発
明サンプル１，２）を作製した。
に詳細に説明する。記録膜に含有される記録材料として
は、下記構造式で示される２種の有機色素（本発明）を
用い、これらをエチルセロソルブ溶媒中に溶解し、直径
１２ｃｍのポリカーボネート（ＰＣ）基板上に、６０ｎ
ｍの厚さに塗設し、その後、反射層として金をコートと
し、この上に保護層を設け、本発明の光記録媒体（本発
明サンプル１，２）を作製した。
【００１２】
【化１】
【００１３】
【化２】
【００１４】次いで、比較サンプルとして、下記構造式
で示される２種の有機色素（比較例）を用い、上記本発
明と同様の方法により作製した（比較サンプル１，２）
。
で示される２種の有機色素（比較例）を用い、上記本発
明と同様の方法により作製した（比較サンプル１，２）
。
【００１５】
【化３】
【００１６】
【化４】
【００１７】これらの各サンプルについて、以下の条件
で記録再生テストを行った。 波長：７８０ｎｍ，線速：１．４ｍ／ｓリードパワー：
０．５ｍＷ， ライトパワー：６ｍＷ これらの記録再生波形を調べたところ、本発明サンプル
１および２のものはハンプ現象が生じておらず、記録形
成されたピットは、極めて歪みが少なくきれいな形状に
形成されていることが確認された。一方、比較サンプル
１，２および３のものは全てハンプ現象が見られ、実用
上好ましくないことが確認された。
で記録再生テストを行った。 波長：７８０ｎｍ，線速：１．４ｍ／ｓリードパワー：
０．５ｍＷ， ライトパワー：６ｍＷ これらの記録再生波形を調べたところ、本発明サンプル
１および２のものはハンプ現象が生じておらず、記録形
成されたピットは、極めて歪みが少なくきれいな形状に
形成されていることが確認された。一方、比較サンプル
１，２および３のものは全てハンプ現象が見られ、実用
上好ましくないことが確認された。
【００１８】
【発明の効果】以上の結果より本発明の効果は明らかで
ある。すなわち、本発明の光記録媒体の記録膜は、融解
点と分解点との差が１００℃以下の記録材料を含有する
ように構成したので、記録時に形状の整ったきれいなピ
ットが形成され、十分な再生特性を有するという効果を
奏する。
ある。すなわち、本発明の光記録媒体の記録膜は、融解
点と分解点との差が１００℃以下の記録材料を含有する
ように構成したので、記録時に形状の整ったきれいなピ
ットが形成され、十分な再生特性を有するという効果を
奏する。
Claims (2)
- 【請求項１】 基板上に記録膜を有する光記録媒体に
おいて、前記記録膜は、融解点と分解点との差が１００
℃以下の記録材料を含有することを特徴とする光記録媒
体。 - 【請求項２】 前記記録材料は、シアニン色素である
ことを特徴とする請求項１記載の光記録媒体。