JPH04360037A - 追記型光ディスク - Google Patents

追記型光ディスク

Info

Publication number
JPH04360037A
JPH04360037A JP3134802A JP13480291A JPH04360037A JP H04360037 A JPH04360037 A JP H04360037A JP 3134802 A JP3134802 A JP 3134802A JP 13480291 A JP13480291 A JP 13480291A JP H04360037 A JPH04360037 A JP H04360037A
Authority
JP
Japan
Prior art keywords
film
substrate
optical disc
groove
write
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP3134802A
Other languages
English (en)
Inventor
Satoru Tanaka
覚 田中
Takashi Chuma
隆 中馬
Yasushi Araki
荒木　泰志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pioneer Corp
Original Assignee
Pioneer Electronic Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pioneer Electronic Corp filed Critical Pioneer Electronic Corp
Priority to JP3134802A priority Critical patent/JPH04360037A/ja
Priority to EP91311404A priority patent/EP0516907A1/en
Publication of JPH04360037A publication Critical patent/JPH04360037A/ja
Priority to US08/093,138 priority patent/US5370970A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は追記型光ディスクに関し
、さらに詳しくは反射率が向上していてＲＦ信号レベル
を高く設定することができるとともにトラッキングエラ
ー信号レベルをも高く設定することが可能で安定した性
能を発揮する追記型光ディスクに関する。
【０００２】
【従来の技術】従来、追記型光ディスクの構成としては
、たとえば図５に示すようにグルーブ１００が形成され
ている基板１０１上に色素膜１０２が設けられ、この色
素膜１０２上に反射膜１０３が形成されているものが一
般的であった。そして、色素膜１０２は、通常、基板１
０１上の全面に形成されていた。
【０００３】一方、光ディスクのトラッキングサーボ用
信号検出方法の代表的なものとしてプッシュプル法が知
られており、従来より広く採用されている。そして、こ
のプッシュプル法においては、グルーブおよびピットに
おける光の回折を利用して回折光の光量差によりトラッ
キングエラーの検出を行なっている。
【０００４】
【発明が解決しようとする課題】ところで、図５に示し
た構成の従来の追記型光ディスクにおいては、反射膜１
０３の全面下に色素膜１０２が設けられているため、基
板側から入射する光の反射膜１０３による反射率が充分
ではなく、ＲＦ信号レベルを高く設定することが困難で
あるという問題があった。また、プッシュプル法を採用
してトラッキングサーボ用信号の検出を行う場合には、
回折光強度が充分ではなかったり、ばらつきが生じたり
するという問題があった。
【０００５】さらに、従来の構成の追記型光ディスクに
おいてＲＦ信号レベルを高く設定すると相対的にトラッ
キングエラー信号レベルが低下するという欠点もあった
。本発明は、かかる事情に基づいてなされたものであり
、本発明の目的は、光の反射率が向上していてＲＦ信号
レベルを高く設定することが可能であるとともにトラッ
キングエラー信号レベルをも高く設定することが可能で
あって安定した性能を発揮する追記型光ディスクを提供
することにある。
【０００６】
【課題を解決するための手段】前記の目的を達成するた
めの本発明の構成は、基板にグルーブが形成されている
とともに該基板上に色素膜を有し、該色素膜上に反射膜
を有する追記型光ディスクにおいて、色素膜のうち、基
板のランド部上に形成されている部分とグルーブ内に形
成されている部分の一部とが退色していることを特徴と
する追記型光ディスクである。
【０００７】
【作用】本発明の追記型光ディスクにおいては、基板上
に形成されている色素膜のうち、基板における隣接する
グルーブで挾まれた部分、すなわちランド部の上に設け
られている部分とグルーブ内に形成されている部分の一
部とが退色している。したがって、色素膜のうち、基板
のランド部上に設けられている部分では色素の吸光度が
著しく低下しているので光透過率が向上し、この部分で
は反射膜からの光の反射率が向上してＲＦ信号レベルを
高く設定することが可能になる。また、グルーブ内に形
成されている色素膜の一部が退色しているため、グルー
ブの深さを光学的に浅くすることが可能であり、回折光
強度を高くすることができるためトラッキングエラー信
号レベルをも高くすることが可能である。
【０００８】
【実施例】以下に本発明の一実施例について図面を参照
して説明する。図１は本発明の光ディスクの概略を示す
斜視断面図であり、図２は断面説明図である。なお、図
１においては反射膜４の厚さを省略してある。図２に示
すように、この光ディスクにおいては、光透過性を有す
る基板１の片面にグルーブ２が形成され、このグルーブ
２を有する基板１の全面に色素膜３が形成されていると
ともに、色素膜３上には反射膜４が形成されている。
【０００９】基板１の形成材料としては、光透過性を有
しているものであればよく、たとえばポリカーボネート
（ＰＣ）、ポリメタクリル酸メチル（ＰＭＭＡ）等の樹
脂、光学ガラスなどが挙げられる。これらのなかでも、
ポリカーボネート（ＰＣ）、ポリメタクリル酸メチル（
ＰＭＭＡ）などの樹脂が好ましい。ここで、基板１の形
成材料が光学ガラスである場合には、この基板１上に、
予めグルーブ２が形成されている転写層（図示せず）を
設けてもよい。転写層の形成材料としては、たとえばホ
ルムアルデヒドにより芳香族ジアゾニウム塩を縮合させ
たジアゾレジンまたはこのジアゾレジンとポバール、フ
ェノール樹脂等が組合わされた芳香族ジアゾニウム塩系
の光分解型感光性樹脂；例えばケイ皮酸基をポバール、
アクリル樹脂等の線状ポリマーの側鎖に導入してなる光
二量型感光性樹脂；不飽和ポリエステル、エポキシアク
リレート、ウレタンアクリレートなどのプレポリマーも
しくはバインダーポリマーとしてのポバール、ポリアミ
ド、ポリメタクリレート等と各種のアクリレートやメタ
クリレートモノマーおよび光重合開始剤を加えてなる光
ラジカル重合系樹脂組成物等の光重合型感光性樹脂等の
紫外線硬化形樹脂（Ｐｈｏｔｏ　Ｐｏｌｙｍｅｒ　；２
Ｐ）などが挙げられる。
【００１０】グルーブ２の深さは、通常、０．０４〜０
．４μｍ程度である。色素膜３の形成に用いられる色素
としては、たとえばシアニン色素、ナフトキノン系色素
、フタロシアニン系色素などが挙げられる。これらのな
かでも、好ましいのはシアニン色素であり、インドリン
形シアニン色素は特に好ましい。このインドリン形シア
ニン色素は、２個の含窒素複素環をメチン基あるいはそ
の連鎖で結合した陽イオン構造を有し、低沸点の有機溶
剤に所定量溶解した溶液状態のときには６４０〜７００
ｎｍの波長付近に最大吸収をもっているが、薄膜化した
場合には長波長側に光吸収特性のピークがシフトして高
出力半導体レーザの波長（７８０ｎｍ）に近くなるとい
う性質を有する。このような性質を有するインドリン形
シアニン色素の具体例としては、たとえば次の式１、式
２で表されるものなどが挙げられる。
【００１１】
【化１】
【００１２】
【化２】
【００１３】なお、これらの式中、Ｒ１　〜Ｒ４　はア
ルキル基である。たとえばこれらのインドリン形シアニ
ン色素は、図２に示すように、基板１に形成されている
グルーブ２内およびランド部５上で色素膜３を形成する
。色素膜３は、グルーブ２内の一部とランド部５上の部
分とで退色している。ここで、グルーブ２内の一部とラ
ンド部５上の部分とで退色している色素膜３を形成する
ためには、たとえば、図３に示すように、基板１上の全
面にわたって色素膜３を塗設し（図３参照）、その後、
図４に示すように、色素膜３のうち、グルーブ２内の一
部とランド部５上の部分とが退色するまで例えばＵＶ光
のような色素を退色させることのできる光を照射する方
法を好適に採用することができる。なお、この方法にお
いては、ＵＶ光等の光の照射条件を適宜に設定すること
により、グルーブ２内の未退色色素量を決定することが
できる。
【００１４】この色素膜３上には反射膜４が設けられて
いる。反射膜４の形成材料としては、たとえば金（Ａｕ
）が好適に用いられ、反射膜４は、たとえば蒸着法、ス
パッタリング法等により色素膜３上に形成される。この
反射膜の厚さは、０．０３〜３μｍ程度である。
【００１５】
【発明の効果】本発明によれば、以上の構成としたので
、反射膜による光の反射率が向上していてＲＦ信号レベ
ルを高く設定することができるとともに、トラッキング
エラー信号レベルをも高くすることが可能であり、安定
した性能を発揮する追記型光ディスクを提供することが
できる。
【図面の簡単な説明】
【図１】本発明の追記形光ディスクの一例の概略を示す
斜視断面図である。
【図２】図１に示した追記形光ディスクの断面説明図で
ある。
【図３】本発明の追記形光ディスクにおける色素膜の形
成過程の一例を示す断面説明図である。
【図４】本発明の追記形光ディスクにおける色素膜の形
成状態の一例を示す断面説明図である。
【図５】従来の追記形光ディスクの一例を示す断面説明
図である。
【符号の説明】
１…基板 ２…グルーブ ３…色素膜 ４…反射膜 ５…ランド部

Claims (1)

    【特許請求の範囲】
  1. 【請求項１】　　基板にグルーブが形成されているとと
    もに該基板上に色素膜を有し、該色素膜上に反射膜を有
    する追記型光ディスクにおいて、色素膜のうち、基板の
    ランド部上に形成されている部分とグルーブ内に形成さ
    れている部分の一部とが退色していることを特徴とする
    追記型光ディスク。
JP3134802A 1991-06-06 1991-06-06 追記型光ディスク Pending JPH04360037A (ja)