JPH0657695A - 紙塗工液用薬剤 - Google Patents
紙塗工液用薬剤Info
- Publication number
- JPH0657695A JPH0657695A JP23309492A JP23309492A JPH0657695A JP H0657695 A JPH0657695 A JP H0657695A JP 23309492 A JP23309492 A JP 23309492A JP 23309492 A JP23309492 A JP 23309492A JP H0657695 A JPH0657695 A JP H0657695A
- Authority
- JP
- Japan
- Prior art keywords
- water
- molecular weight
- average molecular
- paper coating
- glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【目的】 保水性に優れた紙塗工液用薬剤を得る。
【構成】 ポリエチレングリコールなどの水溶性ポリオ
キシアルキレン化合物とジフェニルメタンジイソシアネ
ートなどのポリイソシアネートとの反応により得られる
水溶性ポリウレタン樹脂からなる紙塗工液用薬剤。
キシアルキレン化合物とジフェニルメタンジイソシアネ
ートなどのポリイソシアネートとの反応により得られる
水溶性ポリウレタン樹脂からなる紙塗工液用薬剤。
Description
【０００１】
【産業上の利用分野】本発明は紙塗工液用薬剤に関す
る。更に詳しくは、保水性に優れた紙塗工液用薬剤に関
する。
る。更に詳しくは、保水性に優れた紙塗工液用薬剤に関
する。
【０００２】
【従来の技術】従来紙塗工液として、クレイ、重質炭酸
カルシュム等の顔料、ラテックス、酸化デンプン等のバ
インダー、分散剤等と水からなるスラリー状のものが一
般的に用いられている。そして、この紙塗工液の保水
性、粘度、流動性等の性状を調整するために、アルギン
酸ナトリウム、カルボキシメチルセルロース（ＣＭＣ）
等の高分子化合物が少量添加される。しかしこれらの高
分子化合物はこれらの目的を満たすには不十分であっ
た。例えば、アルギン酸ナトリウムやＣＭＣは、保水性
を高めるに十分な量を添加すると紙塗工液の流動性が著
しく悪くなり、一方、流動性が適切となるような量で使
用した場合には、紙塗工液の保水性が不十分となるとい
う欠点があった。この欠点を克服するため種々の方策が
提案されている。例えば、特開平２−５３９９６号公報
記載の特定のアクリル酸系共重合体を用いる方法、特開
平２−２８９１９６号公報記載のスルホン化芳香族ポリ
マーを用いた方法、特開平３−１２４８９９号公報記載
の特定のアニオン変性ポリビニルアルコールを用いる方
法、等が試みられているがいずれも十分とは言えない。
カルシュム等の顔料、ラテックス、酸化デンプン等のバ
インダー、分散剤等と水からなるスラリー状のものが一
般的に用いられている。そして、この紙塗工液の保水
性、粘度、流動性等の性状を調整するために、アルギン
酸ナトリウム、カルボキシメチルセルロース（ＣＭＣ）
等の高分子化合物が少量添加される。しかしこれらの高
分子化合物はこれらの目的を満たすには不十分であっ
た。例えば、アルギン酸ナトリウムやＣＭＣは、保水性
を高めるに十分な量を添加すると紙塗工液の流動性が著
しく悪くなり、一方、流動性が適切となるような量で使
用した場合には、紙塗工液の保水性が不十分となるとい
う欠点があった。この欠点を克服するため種々の方策が
提案されている。例えば、特開平２−５３９９６号公報
記載の特定のアクリル酸系共重合体を用いる方法、特開
平２−２８９１９６号公報記載のスルホン化芳香族ポリ
マーを用いた方法、特開平３−１２４８９９号公報記載
の特定のアニオン変性ポリビニルアルコールを用いる方
法、等が試みられているがいずれも十分とは言えない。
【０００３】
【発明が解決しようとする課題】本発明の目的は、従来
の塗工液に見られる上記欠点を改善し保水性、流動性等
にすぐれた紙塗工液用薬剤を提供することにある。
の塗工液に見られる上記欠点を改善し保水性、流動性等
にすぐれた紙塗工液用薬剤を提供することにある。
【０００４】
【課題を解決するための手段】本発明者らは、上記問題
点を解決すべく鋭意検討した結果、特定の水溶性ポリウ
レタン樹脂を保水剤として用いることにより、分散性、
保水性にすぐれるとともに、流動性にもすぐれた紙塗工
液が得られることを見いだし本発明に到達した。すなわ
ち本発明は、ヒドロキシル基を有する化合物（ａ）にエ
チレンオキサイド（ＥＯ）、またはＥＯとプロピレンオ
キサイド（ＰＯ）を付加した水溶性ポリオキシアルキレ
ン化合物（Ａ）およびポリイソシアネート（Ｂ）から誘
導され、重量平均分子量が２万〜５０万で、オキシエチ
レン単位の含有重量が６０％以上である水溶性ポリウレ
タン樹脂（１）からなる紙塗工液用薬剤である。
点を解決すべく鋭意検討した結果、特定の水溶性ポリウ
レタン樹脂を保水剤として用いることにより、分散性、
保水性にすぐれるとともに、流動性にもすぐれた紙塗工
液が得られることを見いだし本発明に到達した。すなわ
ち本発明は、ヒドロキシル基を有する化合物（ａ）にエ
チレンオキサイド（ＥＯ）、またはＥＯとプロピレンオ
キサイド（ＰＯ）を付加した水溶性ポリオキシアルキレ
ン化合物（Ａ）およびポリイソシアネート（Ｂ）から誘
導され、重量平均分子量が２万〜５０万で、オキシエチ
レン単位の含有重量が６０％以上である水溶性ポリウレ
タン樹脂（１）からなる紙塗工液用薬剤である。
【０００５】ヒドロキシル基を有する化合物（ａ）とし
ては、例えば、脂肪族一価アルコール類（メタノール、
エタノール、オクチルアルコール、ドデシルアルコー
ル、トリデシルアルコール、ステアリルアルコール、オ
レイルアルコールなど）；一価フェノール類（フェノー
ル、クレゾール、エチルフェノール、イソブチルフェノ
ール、オクチルフェノール）、多価フェノール類（ヒド
ロキノン、カテコールなど）；ビスフェノール類（ビス
フェノールＡ、ビスフェノールＳ、テトラメチルビスフ
ェノールＡ、テトラメチルビスフェノールＳなど）；多
価アルコール類（エチレングリコール、プロピレングリ
コール、ヘキシレングリコール、ジメチロールプロピオ
ン酸（塩）、グリセリン、トリメチロールプロパン、ト
リメチロールエタン、ペンタエリスリトール、ソルビト
ール、ショ糖など）；並びに、水が挙げられる。これら
のうち好ましいものはエチレングリコール、プロピレン
グリコール及び水である。
ては、例えば、脂肪族一価アルコール類（メタノール、
エタノール、オクチルアルコール、ドデシルアルコー
ル、トリデシルアルコール、ステアリルアルコール、オ
レイルアルコールなど）；一価フェノール類（フェノー
ル、クレゾール、エチルフェノール、イソブチルフェノ
ール、オクチルフェノール）、多価フェノール類（ヒド
ロキノン、カテコールなど）；ビスフェノール類（ビス
フェノールＡ、ビスフェノールＳ、テトラメチルビスフ
ェノールＡ、テトラメチルビスフェノールＳなど）；多
価アルコール類（エチレングリコール、プロピレングリ
コール、ヘキシレングリコール、ジメチロールプロピオ
ン酸（塩）、グリセリン、トリメチロールプロパン、ト
リメチロールエタン、ペンタエリスリトール、ソルビト
ール、ショ糖など）；並びに、水が挙げられる。これら
のうち好ましいものはエチレングリコール、プロピレン
グリコール及び水である。
【０００６】水溶性ポリオキシアルキレン化合物（Ａ）
は（ａ）にＥＯ、またはＥＯとＰＯを付加して得られ
る。このときＥＯ、またはＥＯとＰＯに加え、必要によ
り他のアルキレンオキサイド（１，２−ブチレンオキサ
イド、テトラヒドロフラン、α−オレフィンオキサイ
ド、アルキレンオキサイド置換体（エピクロロヒドリ
ン、スチレンオキサイド等）を付加してもよい。ＥＯと
ともに他のアルキレンオキサイドを用いる場合の付加様
式は、ランダム付加でもブロック付加でもよい。但し、
（Ａ）を構成するポリオキシアルキレン鎖の末端部分
は、ポリイソシアネートとの反応性の点からＥＯが付加
しているものが好ましい。ＥＯとＥＯ以外のアルキレン
オキサイドを併用する場合は、（Ａ）が水溶性である範
囲内であればよく、（Ａ）中のオキシエチレン単位の割
合は通常６０重量％以上、好ましくは７０重量％以上と
すればよい。（Ａ）の数平均分子量は通常１，０００〜
３０，０００、好ましくは２，０００〜２５，０００で
ある。１，０００未満では、ウレタン樹脂（１）が水に
難溶性となり、３０，０００を越えるとポリイソシアネ
ート（Ｂ）との反応性が乏しくなり目的とする性能を有
する高分子化合物を得ることが困難となる。
は（ａ）にＥＯ、またはＥＯとＰＯを付加して得られ
る。このときＥＯ、またはＥＯとＰＯに加え、必要によ
り他のアルキレンオキサイド（１，２−ブチレンオキサ
イド、テトラヒドロフラン、α−オレフィンオキサイ
ド、アルキレンオキサイド置換体（エピクロロヒドリ
ン、スチレンオキサイド等）を付加してもよい。ＥＯと
ともに他のアルキレンオキサイドを用いる場合の付加様
式は、ランダム付加でもブロック付加でもよい。但し、
（Ａ）を構成するポリオキシアルキレン鎖の末端部分
は、ポリイソシアネートとの反応性の点からＥＯが付加
しているものが好ましい。ＥＯとＥＯ以外のアルキレン
オキサイドを併用する場合は、（Ａ）が水溶性である範
囲内であればよく、（Ａ）中のオキシエチレン単位の割
合は通常６０重量％以上、好ましくは７０重量％以上と
すればよい。（Ａ）の数平均分子量は通常１，０００〜
３０，０００、好ましくは２，０００〜２５，０００で
ある。１，０００未満では、ウレタン樹脂（１）が水に
難溶性となり、３０，０００を越えるとポリイソシアネ
ート（Ｂ）との反応性が乏しくなり目的とする性能を有
する高分子化合物を得ることが困難となる。
【０００７】水溶性ポリオキシアルキレン化合物（Ａ）
としては、例えば、ポリエチレングリコール、ポリオキ
シエチレンノニルフェニルエーテル、ポリオキシエチレ
ンオキシプロピレングリコール（ＥＯ含有重量８０
％）、グリセリン、トリメチロールプロパンなどの多価
アルコールのＥＯ単独付加物、同様の多価アルコールに
ＰＯについでＥＯを付加した化合物（ＥＯ含有重量８０
％）およびこれらの２種以上の混合物があげられる。こ
れらのうち、好ましいものはポリエチレングリコールお
よびポリオキシエチレンオキシプロピレングリコールで
ある。
としては、例えば、ポリエチレングリコール、ポリオキ
シエチレンノニルフェニルエーテル、ポリオキシエチレ
ンオキシプロピレングリコール（ＥＯ含有重量８０
％）、グリセリン、トリメチロールプロパンなどの多価
アルコールのＥＯ単独付加物、同様の多価アルコールに
ＰＯについでＥＯを付加した化合物（ＥＯ含有重量８０
％）およびこれらの２種以上の混合物があげられる。こ
れらのうち、好ましいものはポリエチレングリコールお
よびポリオキシエチレンオキシプロピレングリコールで
ある。
【０００８】また、（Ａ）とともに必要に応じて、該水
溶性ポリウレタン樹脂（１）の水溶性を阻害しない程度
であれば他のヒドロキシル基を有する化合物を使用する
ことができる。この他のヒドロキシル基を有する化合物
としては（Ａ）の前駆物質として例示したヒドロキシル
基を有する化合物（但し、水を除く。）が挙げられる。
この化合物の使用量は、（Ａ）に対して通常１０重量％
以下である。
溶性ポリウレタン樹脂（１）の水溶性を阻害しない程度
であれば他のヒドロキシル基を有する化合物を使用する
ことができる。この他のヒドロキシル基を有する化合物
としては（Ａ）の前駆物質として例示したヒドロキシル
基を有する化合物（但し、水を除く。）が挙げられる。
この化合物の使用量は、（Ａ）に対して通常１０重量％
以下である。
【０００９】本発明において、ポリイソシアネート
（Ｂ）としては、例えば、エチレンジイソシアネート、
ヘキシレンジイソシアネート、1,5−ナフチレンジイソ
シアネート、4,4'−ジフェニルメタンジイソシアネー
ト、4,4'−ジフェニルジメチルメタンジイソシアネー
ト、ジもしくはテトラアルキルジフェニルメタンジイソ
シアネート、4,4'−ジベンジルジイソシアネート、1,3
−フェニレンジイソシアネート、1,4−フェニレンジイ
ソシアネート、トリレンジイソシアネート（2,4および
2,6などの各異性体）、イソホロンジイソシアネート、
キシリレンジイソシアネートなどのジイソシアネート
類、トリレンジイソシアネートとトリメチロールプロパ
ンとの反応物、アニリンを塩酸の存在下でホルムアルデ
ヒドを反応させて得たポリアミンをホスゲン化して得ら
れるポリフェニルメタンポリイソシアネート、これらの
製造工程で得られる粗製ポリイソシアネートおよびこれ
らの２種以上の混合物を挙げることができる。これらの
うち好ましいものは、ジイソシアネート類および粗製ジ
フェニルメタンジイソシアネートである。
（Ｂ）としては、例えば、エチレンジイソシアネート、
ヘキシレンジイソシアネート、1,5−ナフチレンジイソ
シアネート、4,4'−ジフェニルメタンジイソシアネー
ト、4,4'−ジフェニルジメチルメタンジイソシアネー
ト、ジもしくはテトラアルキルジフェニルメタンジイソ
シアネート、4,4'−ジベンジルジイソシアネート、1,3
−フェニレンジイソシアネート、1,4−フェニレンジイ
ソシアネート、トリレンジイソシアネート（2,4および
2,6などの各異性体）、イソホロンジイソシアネート、
キシリレンジイソシアネートなどのジイソシアネート
類、トリレンジイソシアネートとトリメチロールプロパ
ンとの反応物、アニリンを塩酸の存在下でホルムアルデ
ヒドを反応させて得たポリアミンをホスゲン化して得ら
れるポリフェニルメタンポリイソシアネート、これらの
製造工程で得られる粗製ポリイソシアネートおよびこれ
らの２種以上の混合物を挙げることができる。これらの
うち好ましいものは、ジイソシアネート類および粗製ジ
フェニルメタンジイソシアネートである。
【００１０】ポリウレタン樹脂（１）を構成する（Ａ）
中のＯＨ基と（Ｂ）中のイソシアネート基との当量比
（ＯＨ／ＮＣＯ）は、通常（０．８〜１．２）：１であ
る。上記の範囲内では、紙塗工液の保水性および流動性
が優れる。ポリウレタン樹脂（１）の重量平均分子量
は、通常２０，０００〜５００，０００、好ましくは３
０，０００〜４００，０００である。分子量分布（重量
平均分子量／数平均分子量）は、通常１．３〜６．０、
好ましくは１．５〜４．０である。ポリウレタン樹脂
（１）中のオキシエチレン単位の含有量は通常６０重量
％以上、好ましくは７０重量％以上である。オキシエチ
レン単位がこれ未満では水溶性が不十分である。
中のＯＨ基と（Ｂ）中のイソシアネート基との当量比
（ＯＨ／ＮＣＯ）は、通常（０．８〜１．２）：１であ
る。上記の範囲内では、紙塗工液の保水性および流動性
が優れる。ポリウレタン樹脂（１）の重量平均分子量
は、通常２０，０００〜５００，０００、好ましくは３
０，０００〜４００，０００である。分子量分布（重量
平均分子量／数平均分子量）は、通常１．３〜６．０、
好ましくは１．５〜４．０である。ポリウレタン樹脂
（１）中のオキシエチレン単位の含有量は通常６０重量
％以上、好ましくは７０重量％以上である。オキシエチ
レン単位がこれ未満では水溶性が不十分である。
【００１１】ポリウレタン樹脂（１）の製法を例示する
と、通常のウレタンプレポリマーを作成する方法で
（Ａ）および（Ｂ）を反応させることにより（１）が得
られる。反応温度は通常３０〜２００℃、好ましくは５
０〜１８０℃である。反応時間は、通常０．１〜３０時
間、好ましくは０．１〜８時間である。この反応は、溶
剤中で行ってもよい。溶剤としては、アセトン、テトラ
ヒドロフラン、ジメチルホルムアミド、ジメチルスルホ
キサイド、トルエン、ジオキサン等が挙げられる。これ
ら溶剤を用いる場合は、反応後、溶剤を除去して（１）
を得る。
と、通常のウレタンプレポリマーを作成する方法で
（Ａ）および（Ｂ）を反応させることにより（１）が得
られる。反応温度は通常３０〜２００℃、好ましくは５
０〜１８０℃である。反応時間は、通常０．１〜３０時
間、好ましくは０．１〜８時間である。この反応は、溶
剤中で行ってもよい。溶剤としては、アセトン、テトラ
ヒドロフラン、ジメチルホルムアミド、ジメチルスルホ
キサイド、トルエン、ジオキサン等が挙げられる。これ
ら溶剤を用いる場合は、反応後、溶剤を除去して（１）
を得る。
【００１２】本発明の薬剤使用量（固形分換算）は顔料
１００部に対して通常０．１〜１０部、好ましくは０．
５〜５部である。０．１未満では保水性が不足し１０部
以上では流動性が悪くなる。本発明の薬剤を用いた塗工
液は通常水性分散液の形で使用される。必要に応じてそ
の他の添加剤、例えば分散剤（ポリアクリル酸ナトリウ
ム、ピロリン酸ナトリウム、ヘキサメタリン酸ナトリウ
ムなど）、消泡剤（脂肪酸エステル、リン酸エステル、
シリコーン化合物など）、潤滑剤（ステアリン酸カルシ
ウム、ワックスなど）、耐水化剤（エポキシ系樹脂、尿
素樹脂、メラミン樹脂、グリオキザールなど）、蛍光染
料などが添加される。また他の保水剤、例えばアルギン
酸ナトリウム、ＣＭＣ、酸化デンプン、ポリアクリ酸
塩、スチレンー無水マレイン酸共重合体などを併用する
することもできる。紙塗工塗料は公知の方法で、例えば
エアナイフコーター、ビルブレードコーター、インパー
ティドブレードコーター、トランスファーロールコータ
ー、ロッドコーターなどにより紙に塗工することができ
る。塗工後、乾燥し必要に応じカレンダーリングまたは
スーパーカレンダーリング仕上げを行う。塗工の温度は
通常１０〜６０℃、乾燥温度は通常９０〜１３０℃、カ
レンダーリング、スーパーカレンダーリングの温度は通
常６０〜１００℃である。
１００部に対して通常０．１〜１０部、好ましくは０．
５〜５部である。０．１未満では保水性が不足し１０部
以上では流動性が悪くなる。本発明の薬剤を用いた塗工
液は通常水性分散液の形で使用される。必要に応じてそ
の他の添加剤、例えば分散剤（ポリアクリル酸ナトリウ
ム、ピロリン酸ナトリウム、ヘキサメタリン酸ナトリウ
ムなど）、消泡剤（脂肪酸エステル、リン酸エステル、
シリコーン化合物など）、潤滑剤（ステアリン酸カルシ
ウム、ワックスなど）、耐水化剤（エポキシ系樹脂、尿
素樹脂、メラミン樹脂、グリオキザールなど）、蛍光染
料などが添加される。また他の保水剤、例えばアルギン
酸ナトリウム、ＣＭＣ、酸化デンプン、ポリアクリ酸
塩、スチレンー無水マレイン酸共重合体などを併用する
することもできる。紙塗工塗料は公知の方法で、例えば
エアナイフコーター、ビルブレードコーター、インパー
ティドブレードコーター、トランスファーロールコータ
ー、ロッドコーターなどにより紙に塗工することができ
る。塗工後、乾燥し必要に応じカレンダーリングまたは
スーパーカレンダーリング仕上げを行う。塗工の温度は
通常１０〜６０℃、乾燥温度は通常９０〜１３０℃、カ
レンダーリング、スーパーカレンダーリングの温度は通
常６０〜１００℃である。
【００１３】
【実施例】以下実施例により本発明をさらに説明する
が、本発明はこれに限定されるものではない。なお実施
例中、部は重量部を表す。 実施例１ ポリエチレングリコール（数平均分子量８，０００）１
６部、ポリオキシエチレンオキシプロピレングリコール
［ポリプロピレングリコール（数平均分子量１，６０
０）にＥＯを付加したもの；数平均分子量８，０００、
ＥＯ＝８０重量％］１６部、4,4'−ジフェニルメタンジ
イソシアネート１部（ＯＨ／ＮＣＯ＝１．００）を１５
０℃で３時間反応させ、本発明の薬剤［１］を得た。重
量平均分子量は５７，０００、分子量分布は２．４であ
った。 実施例２ ポリエチレングリコール（数平均分子量６，０００）９
０部、ポリオキシエチレンオキシプロピレングリコール
［ポリプロピレングリコール（数平均分子量１，７０
０）にＥＯを付加したもの；数平均分子量８，５００、
ＥＯ＝８０重量％］１２０部、4,4'−ジフェニルメタン
ジイソシアネート７部（ＯＨ／ＮＣＯ＝１．０４）を１
６０℃で２．５時間反応させ、本発明の薬剤［２］を得
た。重量平均分子量は４７，０００、分子量分布は２．
２であった。 実施例３ ポリエチレングリコール（数平均分子量２０，０００）
６４部、ポリオキシエチレンオキシプロピレングリコー
ル［ポリプロピレングリコール（数平均分子量１，６０
０）にＥＯを付加したもの；数平均分子量８，０００、
ＥＯ＝８０重量％］２２部、トリレンジイソシアネート
１部（ＯＨ／ＮＣＯ＝１．０１を１８０で℃２時間反応
させ、本発明の薬剤［３］を得た。重量平均分子量は５
２，０００、分子量分布は２，８であった。
が、本発明はこれに限定されるものではない。なお実施
例中、部は重量部を表す。 実施例１ ポリエチレングリコール（数平均分子量８，０００）１
６部、ポリオキシエチレンオキシプロピレングリコール
［ポリプロピレングリコール（数平均分子量１，６０
０）にＥＯを付加したもの；数平均分子量８，０００、
ＥＯ＝８０重量％］１６部、4,4'−ジフェニルメタンジ
イソシアネート１部（ＯＨ／ＮＣＯ＝１．００）を１５
０℃で３時間反応させ、本発明の薬剤［１］を得た。重
量平均分子量は５７，０００、分子量分布は２．４であ
った。 実施例２ ポリエチレングリコール（数平均分子量６，０００）９
０部、ポリオキシエチレンオキシプロピレングリコール
［ポリプロピレングリコール（数平均分子量１，７０
０）にＥＯを付加したもの；数平均分子量８，５００、
ＥＯ＝８０重量％］１２０部、4,4'−ジフェニルメタン
ジイソシアネート７部（ＯＨ／ＮＣＯ＝１．０４）を１
６０℃で２．５時間反応させ、本発明の薬剤［２］を得
た。重量平均分子量は４７，０００、分子量分布は２．
２であった。 実施例３ ポリエチレングリコール（数平均分子量２０，０００）
６４部、ポリオキシエチレンオキシプロピレングリコー
ル［ポリプロピレングリコール（数平均分子量１，６０
０）にＥＯを付加したもの；数平均分子量８，０００、
ＥＯ＝８０重量％］２２部、トリレンジイソシアネート
１部（ＯＨ／ＮＣＯ＝１．０１を１８０で℃２時間反応
させ、本発明の薬剤［３］を得た。重量平均分子量は５
２，０００、分子量分布は２，８であった。
【００１４】評価 表１に記載した割合で配合しスラリー状の紙塗工液を調
整した
整した
【００１５】
【表１】
【００１６】塗工液の物性および塗工紙の物性を表２に
示した。塗工液についてローシェアー粘度（６０ｒｐ
ｍ）とハイシェアー粘度（４４００ｒｐｍ）を測定し、
過マンガン酸カリウム法にて保水性を測定した。その結
果を表２に示した。本発明の薬剤を使用した評価例１〜
４は比較評価例１〜３に比べ流動性を落とさずに優れた
保水効果が得られている。
示した。塗工液についてローシェアー粘度（６０ｒｐ
ｍ）とハイシェアー粘度（４４００ｒｐｍ）を測定し、
過マンガン酸カリウム法にて保水性を測定した。その結
果を表２に示した。本発明の薬剤を使用した評価例１〜
４は比較評価例１〜３に比べ流動性を落とさずに優れた
保水効果が得られている。
【００１７】
【表２】
【００１８】（注） ローシェア粘度（ｃｐｓ）：Ｂ型粘度計により測定し
た。（回転数６０ｒｐｍ） ハイシェア粘度（ｃｐｓ）：ハイシェア粘度計により
（日本精機（株）製）測定した。（回転数４４００ｒｐ
ｍ） 保水性：ＫＭｎＯ4法（塗工液の上にＫＭｎＯ4を乗せた
濾紙を浮かべたとき、ＫＭｎＯ4が変色するまでの時間
（秒）を測定する。時間が長い程保水性が良い。
た。（回転数６０ｒｐｍ） ハイシェア粘度（ｃｐｓ）：ハイシェア粘度計により
（日本精機（株）製）測定した。（回転数４４００ｒｐ
ｍ） 保水性：ＫＭｎＯ4法（塗工液の上にＫＭｎＯ4を乗せた
濾紙を浮かべたとき、ＫＭｎＯ4が変色するまでの時間
（秒）を測定する。時間が長い程保水性が良い。
【００１９】また、塗工液を上質紙（坪６５ｇ／ｍ2）
に固形分付着量が１７ｇ／ｍ2になるように塗布乾燥し
て塗工紙を作り、その塗工紙の性状を測定した。その結
果を表３に示す。
に固形分付着量が１７ｇ／ｍ2になるように塗布乾燥し
て塗工紙を作り、その塗工紙の性状を測定した。その結
果を表３に示す。
【００２０】
【表３】
【００２１】（注） 平滑度：ＪＩＳ Ｐ８１１９−１９７６により測定。 光沢度：ＪＩＳ Ｐ８１４２−１９６５により測定。 白色度：ＪＩＳ Ｐ８１２３−１９６１により測定。 ドライピック、ウェットピック：ＲＩ印刷機を用いて塗
工液の表面に印刷し、ピッキング発生状態を観察し判
定。 評価方法：５点法で評価を行う。その値が大きいほど良
好。
工液の表面に印刷し、ピッキング発生状態を観察し判
定。 評価方法：５点法で評価を行う。その値が大きいほど良
好。
【００２２】
【発明の効果】本発明の紙塗工液用薬剤は、保水性、流
動性が優れており、また、印刷性、耐ピッキング性、光
沢性、平滑性に優れた塗工紙が得られる。
動性が優れており、また、印刷性、耐ピッキング性、光
沢性、平滑性に優れた塗工紙が得られる。
Claims (4)
- 【請求項１】 ヒドロキシル基を有する化合物（ａ）に
エチレンオキサイド（ＥＯ）、またはＥＯとプロピレン
オキサイド（ＰＯ）を付加した水溶性ポリオキシアルキ
レン化合物（Ａ）およびポリイソシアネート（Ｂ）から
誘導され、重量平均分子量が２万〜５０万で、オキシエ
チレン単位の含有重量が６０％以上である水溶性ポリウ
レタン樹脂（１）からなる紙塗工液用薬剤。 - 【請求項２】 ヒドロキシル基を有する化合物（ａ）が
エチレングリコール、プロピレングリコールおよび水か
らなる群より選ばれる１種以上である請求項１記載の紙
塗工液用薬剤。 - 【請求項３】 ポリオキシアルキレン化合物（Ａ）の数
平均分子量が１，０００〜３０，０００である請求項１
または２記載の紙塗工液用薬剤。 - 【請求項４】 ポリオキシアルキレン化合物（Ａ）が、
ポリオキシエチレングリコールまたはポリオキシエチレ
ンオキシプロピレングリコールである請求項１〜３のい
ずれか記載の紙塗工液用薬剤。