JPH09228169A - Polyester multilament composite yarn and woven or knitted fabric using the composite yarn - Google Patents
Polyester multilament composite yarn and woven or knitted fabric using the composite yarnInfo
- Publication number
- JPH09228169A JPH09228169A JP3832696A JP3832696A JPH09228169A JP H09228169 A JPH09228169 A JP H09228169A JP 3832696 A JP3832696 A JP 3832696A JP 3832696 A JP3832696 A JP 3832696A JP H09228169 A JPH09228169 A JP H09228169A
- Authority
- JP
- Japan
- Prior art keywords
- multifilament
- polyester
- composite yarn
- woven
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、適度なハリ、コ
シ、ドレープ性を有すると共に、優しい薄起毛調のパウ
ダータッチを有する織編物を与える新規なポリエステル
系マルチフィラメント複合糸、およびこの複合糸を用い
たポリエステル系複合織編物に関するものである。TECHNICAL FIELD The present invention relates to a novel polyester-based multifilament composite yarn that provides a woven or knitted fabric having moderate elasticity, elasticity, and drapeability, and a powder touch with a gentle thin raised tone, and a composite yarn thereof. The present invention relates to a polyester-based composite woven or knitted fabric used.
【０００２】[0002]
【従来の技術】ポリエステル系マルチフィラメント糸
は、その優れた特性を生かして衣料用途を始めとする各
種の用途で広く活用されている。特に最近では、シルク
タッチの合成繊維用としてポリエステル系フィラメント
糸の研究が盛んに進められている。ことに衣料用途で
は、絹をターゲットとしてそれを越えて合繊でしか表現
できない膨らみ、ハリ、コシ、キシミ等を持たせるた
め、熱処理により伸長するマルチフィラメントを含む異
収縮混繊糸を使用し、更にはその一部もしくは全部のフ
ィラメントを異形断面形状とし、且つフィラメント表面
にマイクロポーラスを持たせるため、ＴｉＯ2 等の微粒
子を均一分散させた後アルカリ減量したり、あるいは芯
／鞘２重構造としてそのフィラメントデニールを調整し
た複合糸も知られている。また特開平７−１１８９９１
号には、単繊維繊度０．２デニール以下の低収縮マルチ
フィラメントと、単繊維繊度１デニール以上の高収縮マ
ルチフィラメント糸からなる異収縮混繊糸を５０回／ｍ
以上に撚糸加工した複合糸を緯糸に配した織物も知られ
ている。2. Description of the Related Art Polyester-based multifilament yarns are widely used in various applications including clothing applications by taking advantage of their excellent characteristics. Particularly in recent years, research on polyester-based filament yarns for synthetic fibers for silk touch has been actively conducted. Especially for clothing applications, in order to have bulges, elasticity, stiffness, creases, etc. that can be expressed only with synthetic fibers with silk as the target, we use a different shrinkage mixed fiber containing multifilaments that expand by heat treatment. In order to make some or all of the filaments have an irregular cross-sectional shape and to have a microporous surface on the filament surface, fine particles such as TiO 2 are uniformly dispersed and then alkali weight is reduced, or as a core / sheath double structure, Composite yarns with adjusted filament denier are also known. In addition, JP-A-7-118991
The number of different shrinkage mixed filament yarns consisting of low shrinkage multifilament with single fiber fineness of 0.2 denier or less and high shrinkage multifilament yarn with single fiber fineness of 1 denier or more is 50 times / m.
A woven fabric in which a composite yarn obtained by twisting a yarn as described above is arranged on a weft is also known.
【０００３】しかしこれまでに提案されているこれらの
糸を用いた織編物は、ソフトな薄起毛調、キシミといっ
た特性は良好であっても、ソフト感やハリ、コシ、ヌメ
リのないソフトドライ感といった特性を満足し得るもの
とはいえない。ハリ、コシを改善するための手段とし
て、複合される芯糸に単繊維繊度の太いフィラメントを
使用することも知られているが、０．２デニール以下と
いった細いマルチフィラメントを鞘糸として使用する
と、複合糸が芯のある嫌なタッチとなるばかりでなく、
表面側に露出する鞘糸を構成するフィラメントが細過ぎ
るため、該鞘糸部が弾力不足によりクタッとした感じと
なってヌメリ感が強く、ソフトなドライタッチが得られ
ない。However, the woven and knitted fabrics using these yarns that have been proposed so far have a soft feeling, firmness, elasticity, and a soft dry feeling without stickiness, even if they have good characteristics such as a soft thin brushed tone and creases. It cannot be said that such characteristics can be satisfied. As a means for improving firmness and elasticity, it is also known to use a thick filament having a single fiber fineness as a core yarn to be combined, but when a thin multifilament of 0.2 denier or less is used as a sheath yarn, Not only does the composite thread have an unpleasant touch with a core,
Since the filaments constituting the sheath yarn exposed on the surface side are too thin, the sheath yarn portion feels stiff due to lack of elasticity, and the slimy feeling is strong, and a soft dry touch cannot be obtained.
【０００４】しかも、単繊維繊度が０．２デニール未満
のものは染着性が悪く、これを鞘糸として使用すると、
芯糸（高収縮糸）との間で染着性差を生じてイラツキが
目立つ様になり、高級品嗜好の現状にそぐわなくなる。Moreover, if the single fiber fineness is less than 0.2 denier, the dyeing property is poor, and if this is used as a sheath yarn,
Difficulty in dyeing with the core yarn (high shrinkage yarn) causes noticeable irritability, which makes it unsuitable for the current high-class taste.
【０００５】[0005]
【発明が解決しようとする課題】本発明は上記の様な従
来技術の問題点に着目してなされたものであって、その
目的は、優しい薄起毛調の豊かな膨らみ感、ソフトドラ
イなパウダータッチ、適度なハリ、コシ、ドレープ性な
どを全て満足する高品質の織編物を与える合成複合糸を
開発し、更には該複合糸を用いた優れた品質の織編物を
提供しようとするものである。SUMMARY OF THE INVENTION The present invention has been made in view of the problems of the prior art as described above, and its purpose is to provide a gentle fluffy, rich swelling feeling and soft dry powder. With the aim of developing a synthetic composite yarn that gives a high-quality woven or knitted fabric satisfying all of touch, moderate elasticity, firmness, drapability, etc., and further providing an excellent quality woven or knitted fabric using the composite yarn. is there.
【０００６】[0006]
【課題を解決するための手段】上記課題を達成すること
のできた本発明に係るポリエステル系マルチフィラメン
ト複合糸の構成は、下記の糸物性を有するポリエステル
系マルチフィラメントＡとポリエステル系マルチフィラ
メントＢとが、前者：２０〜８０％、後者８０〜２０％
のデニール比率で複合されると共に、それらが交絡度２
０〜１２０個／ｍで絡合した複合糸からなるところにそ
の特徴を有している。The composition of the polyester-based multifilament composite yarn according to the present invention, which has been able to achieve the above-mentioned object, has a polyester-based multifilament A and a polyester-based multifilament B having the following physical properties. , Former: 20-80%, latter 80-20%
They are compounded with a denier ratio of 2 and they are entangled 2
Its characteristic is that it is composed of a composite yarn entangled at 0 to 120 yarns / m.
【０００７】マルチフィラメントＡ：ｄｐｆA が０．２
〜０．５デニール、ＳＨＷA が７％以下で、仮撚捲縮さ
れたマルチフィラメント マルチフィラメントＢ：ｄｐｆB が２デニール以上、Ｓ
ＨＷB が５〜６０％、ＤＴB が３．５ｇ／ｄ以上、ＤＥ
B が４５％以下であるマルチフィラメント 但し、ＳＨＷB −ＳＨＷA は５％以上 上記において、ｄｐｆA およびｄｐｆB は、ポリエステ
ル系マルチフィラメントＡおよびＢの単繊維デニール、
ＳＨＷA およびＳＨＷB は、ポリエステル系マルチフィ
ラメントＡおよびＢの熱水（１００℃）収縮率、ＤＥB
はポリエステル系マルチフィラメントＢの破断伸度、Ｄ
ＴB はポリエステル系マルチフィラメントＢの破断強度
をそれぞれ表わす。Multifilament A : dpf A is 0.2
~ 0.5 denier, SHW A 7% or less, false twist crimped multifilament multifilament B: dpf B 2 denier or more, S
HW B is 5~60%, DT B is 3.5g / d or more, DE
Multifilament in which B is 45% or less However, SHW B- SHW A is 5% or more In the above, dpf A and dpf B are monofilament denier of polyester-based multifilaments A and B,
SHW A and SHW B are hot water (100 ° C.) shrinkage of polyester-based multifilaments A and B, DE B
Is the elongation at break of polyester-based multifilament B, D
T B represents the breaking strength of the polyester multifilament B, respectively.
【０００８】上記複合糸を構成するマルチフィラメント
ＢまたはこれとマルチフィラメントＡは、横断面形状に
おいて３以上の突起を有すると共に異形度が１．１以上
のフィラメントの集合体とすることにより、複合糸もし
くは織編物としてのテカリを抑えると共に染色性を高め
ることができるので好ましく、またこれらマルチフィラ
メントＡ，Ｂの全部もしくは一部をカチオン可染性ポリ
エステルとすれば、カチオン系染料を用いることによっ
て鮮明色も表現できるし、更にシャンブレー、霜降り、
杢等も表現できるので好ましく、またこれらマルチフィ
ラメントＡ，Ｂの全部又は一部として、微細孔形成剤を
０．５％以上含有するポリエステルからなるものを使用
し、紡糸・延伸時の減量加工により微細孔を現出させた
フィラメントを使用すれば、複合糸あるいは織編物とし
てのヌメリ感や光沢感（反射）が抑えられ、深色性の表
現が可能になるばかりでなくソフトドライ感も一段と高
められるので好ましい。The multifilament B or the multifilament A and the multifilament A which compose the above-mentioned composite yarn are aggregates of filaments having three or more protrusions in cross-sectional shape and having a degree of irregularity of 1.1 or more. Alternatively, it is preferable because it can suppress the glossiness of the woven and knitted fabric and enhance the dyeability. When all or a part of the multifilaments A and B are made of a cationic dyeable polyester, a bright color can be obtained by using a cationic dye. Can be expressed, and chambray, marbled,
Since it is possible to express heather and the like, it is preferable to use, as all or part of these multifilaments A and B, one made of polyester containing 0.5% or more of a micropore-forming agent, and by reducing the weight during spinning and drawing. The use of filaments with fine pores suppresses the slimy feel and glossiness (reflection) of the composite yarn or woven / knitted fabric, which not only enables the expression of bathochromic properties but also further enhances the soft dry feel. It is preferable because it is possible.
【０００９】そして、上記のポリエステル系マルチフィ
ラメント複合糸を全部もしくは一部として用いて製織も
しくは製編した後、染色および仕上げ加工を施すことに
よって得られる織編物は、上記処理工程で受ける熱処理
によりマルチフィラメントＢが収縮すると共に、収縮率
の小さいマルチフィラメントＡが織編物の表面にループ
状に膨出し、優しい薄起毛調の豊かな膨らみ感、ソフト
ドライなパウダータッチ、適度なハリ、コシ、ドレープ
性などを全て満足する高品質の織編物となる。A woven or knitted product obtained by weaving or knitting the polyester multifilament composite yarn as a whole or a part thereof, and then subjecting it to dyeing and finishing is multi-processed by the heat treatment received in the above treatment step. As filament B shrinks, multi-filament A with a low shrinkage swells like a loop on the surface of the woven or knitted fabric, giving a gentle fluffy, fluffy feel, soft dry powder touch, moderate elasticity, elasticity, and drapeability. It is a high quality woven and knitted fabric that satisfies all of the above.
【００１０】[0010]
【発明の実施の形態】以下、本発明について更に詳細に
説明する。まず、本発明のポリエステル系マルチフィラ
メント複合糸を構成するマルチフィラメントとしては、
熱水収縮率（１００℃での値：以下同じ）が７％以下で
あるマルチフィラメントＡと、熱水収縮率が５〜６０％
の範囲にあるマルチフィラメントＢをそれぞれ選択し、
且つ得られる織編物に膨らみを発現させるには、上記マ
ルチフィラメントＡとマルチフィラメントＢの熱水収縮
率差（ΔＳＨＷ）を少なくとも５％以上、好ましくは１
０％以上にしなければならない。但し、マルチフィラメ
ントＢの熱水収縮率があまりに大きくなると、織編物製
品としたときにパッカリングの問題を起こし易くなるの
で、マルチフィラメントＢの熱水収縮率は６０％以下、
より好ましくは５０％以下とすべきである。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail below. First, as the multifilament constituting the polyester-based multifilament composite yarn of the present invention,
Multifilament A having a hot water shrinkage (value at 100 ° C .: the same below) of 7% or less, and a hot water shrinkage of 5 to 60%
Select each multifilament B in the range of
In addition, in order to cause the obtained woven or knitted fabric to bulge, the difference in hot water shrinkage ratio (ΔSHW) between the multifilament A and the multifilament B is at least 5% or more, preferably 1 or more.
Must be 0% or higher. However, if the hot water shrinkage rate of the multifilament B becomes too large, the problem of puckering tends to occur in the case of a woven or knitted product. Therefore, the hot water shrinkage rate of the multifilament B is 60% or less,
It should more preferably be 50% or less.
【００１１】尚、本発明の複合糸を使用することによっ
て得られる織編物の収縮力は、該複合糸において芯糸を
構成するマルチフィラメントＢであり、後述する様にそ
の収縮によってマルチフィラメントＡを複合糸の外周側
へうまく膨出させるには、該マルチフィラメントＢの熱
収縮応力を０．３ｇ／ｄ以上、より好ましくは３．５ｇ
／ｄ以上とし、かつ収縮能を決める該熱応力の立ち上が
り温度を６５℃以上、より好ましくは８０℃以上とする
のがよい。The shrinkage force of the woven or knitted fabric obtained by using the composite yarn of the present invention is the multifilament B constituting the core yarn in the composite yarn, and as described later, the shrinkage of the multifilament A results in the multifilament A. In order to swell the composite yarn to the outer peripheral side, the heat shrinkage stress of the multifilament B is 0.3 g / d or more, more preferably 3.5 g.
/ D or more, and the rising temperature of the thermal stress that determines the shrinkability is 65 ° C. or more, and more preferably 80 ° C. or more.
【００１２】しかして熱応力の立ち上がり温度が６５℃
未満の低いものでは、撚糸セットやサイジング等の工程
で該熱応力立上り温度以上の熱を受けたときに熱セット
が固定され、その後の染色加工工程で熱処理しても織編
物が収縮し得なくなって満足な風合いが得られなくな
る。こうした問題を回避するには、熱応力が低下しない
上記熱応力立上り温度未満の温度で熱セットや乾燥を行
なわなければならなくなり、それに伴って熱セットや乾
燥に長時間を要することになって生産性が損なわれるか
らである。However, the rising temperature of thermal stress is 65 ° C.
If the value is less than less, the heat set is fixed when receiving heat above the thermal stress rising temperature in the steps such as twisting yarn setting and sizing, and the woven or knitted fabric cannot shrink even after heat treatment in the subsequent dyeing process. And a satisfactory texture cannot be obtained. In order to avoid such problems, it is necessary to perform heat setting and drying at a temperature lower than the above thermal stress rising temperature at which thermal stress does not decrease, and accordingly, it takes a long time for heat setting and drying. This is because the sex is impaired.
【００１３】また、マルチフィラメントＡの熱水収縮率
は７％以下に抑えなければならず、これは、複合糸とし
た後の熱水処理工程で、フィラメントＡ，Ｂの熱収縮差
による膨らみを発現させるうえで重要な要件となる。即
ち上記熱収縮差によってフィラメントＡを膨出させるに
は、芯糸を構成するマルチフィラメントＢを十分に熱収
縮させて糸長差を発現させることが必要であり、マルチ
フィラメントＡの熱水収縮率が大き過ぎると、それに伴
ってマルチフィラメントＢの熱水収縮率をそれ以上に大
きくしなければならなくなり、ひいては織編物の収縮量
が過度に大きくなって織編物が硬質化し、満足のいく特
性の織編物が得られなくなるからである。The hot water shrinkage rate of the multifilament A must be suppressed to 7% or less. This is because the swelling due to the heat shrinkage difference between the filaments A and B in the hot water treatment step after forming the composite yarn. It becomes an important requirement for the expression. That is, in order to swell the filament A due to the difference in heat shrinkage, it is necessary to sufficiently heat-shrink the multifilament B constituting the core yarn so as to develop a yarn length difference. Is too large, the hot water shrinkage rate of the multifilament B must be increased accordingly, and the shrinkage amount of the woven or knitted fabric becomes excessively large, so that the woven or knitted fabric is hardened. This is because a woven or knitted fabric cannot be obtained.
【００１４】次に、マルチフィラメントＡを構成する単
繊維の繊度は０．２〜０．５デニールの範囲から選択さ
れる。これは、０．２デニール未満の細いものではソフ
トなタッチは得られるものの、鞘糸成分として複合糸の
外側に膨出するマルチフィラメントＡが弾力不足でクタ
ッとした感じとなり、薄起毛調のパウダータッチが得ら
れなくなるばかりでなく、該マルチフィラメントの繊度
が細くなるほど見掛けの染着性が低下し、芯糸となるマ
ルチフィラメントＢとの染着性差が大きくなってイラツ
キが目立つ様になるからである。しかし、該マルチフィ
ラメントＡの単繊維繊度が過度に大きくなると、複合
糸、更には織編物のソフト感が著しく損なわれるので、
０．５デニール以下に抑えなければならない。Next, the fineness of the single fibers constituting the multifilament A is selected from the range of 0.2 to 0.5 denier. This is because thin filaments less than 0.2 denier provide a soft touch, but the multifilament A swelling to the outside of the composite yarn as a sheath yarn component has a lack of elasticity and feels stiff, resulting in a thin brushed powder. Not only will the touch not be obtained, but the smaller the fineness of the multifilament, the lower the apparent dyeing property, and the greater the difference in dyeing property with the multifilament B, which is the core yarn, and the more noticeable the irritability becomes. is there. However, if the monofilament fineness of the multifilament A becomes excessively large, the softness of the composite yarn and further the woven or knitted fabric is significantly impaired.
Must be kept below 0.5 denier.
【００１５】またこのマルチフィラメントＡは、仮撚加
工を施したものでなければならず、これは、芯糸として
複合されるマルチフィラメントＢの単繊維繊度との関係
で決められる。即ち、芯糸として複合されるマルチフィ
ラメントＢの単繊維繊度は後述する如く２デニール以上
のものが選択されるが、周知の様にマルチフィラメント
の見掛け染着性は単繊維繊度が太いほど濃くなる傾向が
あり、極細フィラメントと太デニールフィラメントの混
繊糸ではその染着差でイラツキが発生し易いが、マルチ
フィラメントＡに仮撚加工を施しておけば染着の濃化が
起こり、太デニールのマルチフィラメントＢとの染着差
によるイラツキが軽減されるからであり、しかも仮撚加
工によって弾力性も高められ、０．２〜０．５デニール
のフィラメントであっても非常にソフト感のある複合糸
となる。上記仮撚を行なうに当たっては、仮撚数や湿度
などの仮撚加工条件を低めに抑えた方が、マルチフィラ
メントの開繊性を高める上で好ましい。Further, the multifilament A must be a false-twisted product, which is determined in relation to the single fiber fineness of the multifilament B composited as a core yarn. That is, the monofilament fineness of the multifilament B composited as the core yarn is selected to be 2 denier or more as described later, but as is well known, the apparent dyeing property of the multifilament becomes darker as the monofilament fineness becomes thicker. There is a tendency that mixed yarns of ultrafine filaments and thick denier filaments tend to cause irregularities due to the difference in dyeing. However, if false twisting is applied to multifilament A, thickening of dyeing occurs and This is because the unevenness due to the difference in dyeing with the multi-filament B is reduced, and the elasticity is also improved by false twisting, and even a filament of 0.2 to 0.5 denier has a very soft feeling. It becomes a thread. In carrying out the above false twisting, it is preferable to suppress false twisting conditions such as the number of false twisting and humidity to keep the multifilament openability high.
【００１６】尚本発明においては、上記の様にマルチフ
ィラメントＡの断面が仮撚加工により異形化されている
ので、それによりヌメリ感がなく且つソフトドライ感を
備えたものを得ることができるが、より好ましくは、該
マルチフィラメントＡを構成する各フィラメントとして
複数の突起を有する異形横断面のものを使用したり、あ
るいは、各フィラメントを構成するポリエステル系樹脂
の製造時に無機又は有機の微細孔形成剤を０．５％以上
含ませ、織編物にした後でアルカリ減量などで微細孔を
生ぜしめる等の工夫をすれば、ソフトドライ感を一段と
改善することができるので好ましい。In the present invention, since the cross section of the multifilament A is modified by false twisting as described above, it is possible to obtain a product having no slimy feel and a soft dry feel. More preferably, each filament constituting the multifilament A has a modified cross-section having a plurality of protrusions, or the formation of inorganic or organic fine pores during the production of the polyester resin constituting each filament. It is preferable to add 0.5% or more of the agent to make a woven or knitted product and then to make fine pores by reducing alkali and the like, because the soft dry feeling can be further improved.
【００１７】本発明で用いられるポリエステル系マルチ
フィラメントＡの捲縮加工として、仮撚加工を採用する
ことによる利点をまとめると下記の通りである。 前記の様に加工後異形化してソフトドライタッチとな
る。 単糸でトルク（旋回性）を持っているので、絡合性が
向上してソフトタッチ感が助長される。 仮撚加工に引き続いてマルチフィラメントＢと混繊が
行なえる。 捲縮加工の中で最も品質が安定しており且つ高速加工
も可能である。The advantages of adopting false twisting as crimping of the polyester multifilament A used in the present invention are summarized as follows. As described above, after processing, the shape is changed to a soft dry touch. Since the single yarn has torque (turning property), the entanglement property is improved and the soft touch feeling is promoted. Following the false twisting, the multifilament B and the mixed fiber can be mixed. It has the most stable quality of crimping and can be processed at high speed.
【００１８】上記マルチフィラメントＡの鞘糸としての
特性を有効に発揮させるには、複合糸中に占める該マル
チフィラメントＡのデニール比率を２０〜８０％、より
好ましくは３０〜７０％の範囲としなければならず、２
０％未満では鞘糸としての前記特性を複合糸もしくはこ
れを用いた織編物として有効に発揮させることができ
ず、一方８０％を超えると、相対的に芯糸を構成するマ
ルチフィラメントＢの比率が少なくなり過ぎて複合糸と
しての糸強力が低下する他、混繊、撚糸、サイジング、
製繊等の後加工通過性および織編布としての物性が確保
できなくなる。尚、該マルチフィラメントＡの鞘糸とし
ての特性をより確実に発揮させるうえでは、複合糸中に
占める該マルチフィラメントＡを、フィラメントの全本
数比で８０％以上、より好ましくは８５〜９９％の範囲
とすることが望ましい。In order to effectively exhibit the characteristics of the multifilament A as a sheath yarn, the denier ratio of the multifilament A in the composite yarn must be in the range of 20 to 80%, more preferably 30 to 70%. Must be 2
If it is less than 0%, the above properties as a sheath yarn cannot be effectively exhibited as a composite yarn or a woven or knitted fabric using the same, whereas if it exceeds 80%, the ratio of the multifilament B relatively constituting the core yarn is relatively high. Is reduced too much and the yarn strength as a composite yarn is reduced, as well as mixed fiber, twisted yarn, sizing,
It becomes impossible to secure the post-processability of fiber manufacturing and the physical properties of a woven or knitted fabric. In order to more surely exhibit the characteristics of the multifilament A as a sheath yarn, the multifilament A occupying in the composite yarn is 80% or more, more preferably 85 to 99% in terms of the total number of filaments. It is desirable to set the range.
【００１９】次に、マルチフィラメントＢの単繊維繊度
は２デニール以上でなければならない。しかしてマルチ
フィラメントＢは、本発明の複合糸において芯糸を構成
するものであり、その単繊維繊度が２デニール未満で
は、複合糸あるいはこれを用いた織編物がハリ、コシの
ないものになってしまう。このマルチフィラメントＢを
構成するフィラメントは、複数の突起を有する異形横断
面のものを使用することが望ましい。これは、鞘糸を構
成する前記マルチフィラメントＡは単繊維繊度が細く、
上記の様に構成フィラメントの横断面を異形化したり微
細孔を生ぜしめても乾いたタッチが不十分になり易いの
で、こうしたドライタッチを芯糸部分で補うことが望ま
しいからである。また、マルチフィラメントＢは単繊維
繊度が太いので、いやな光沢が目立ち易く、これを防止
する為にも前記の突起を持たせる方が好ましい。こうし
た目的を有効に発現させるには、突起を３個以上とし且
つ異形度は１．１以上とするのが良い。Next, the monofilament fineness of the multifilament B must be 2 denier or more. However, the multifilament B constitutes the core yarn in the composite yarn of the present invention, and when the single fiber fineness thereof is less than 2 denier, the composite yarn or the woven or knitted fabric using the same is free from elasticity and stiffness. Will end up. It is desirable to use a filament having a modified cross section having a plurality of protrusions as the filament constituting the multifilament B. This is because the multifilament A constituting the sheath yarn has a fine single fiber fineness,
This is because the dry touch is likely to be insufficient even if the cross section of the constituent filaments is deformed or fine holes are formed as described above, and it is desirable to supplement such a dry touch with the core yarn portion. Further, since the monofilament fineness of the multifilament B is large, unpleasant luster is apt to stand out, and it is preferable to have the above-mentioned projections in order to prevent this. In order to effectively realize such an object, it is preferable that the number of protrusions is 3 or more and the degree of irregularity is 1.1 or more.
【００２０】該マルチフィラメントＢは、破断強度が
３．５ｇ／ｄ以上、より好ましくは３．８ｇ／ｄ以上
で、且つ複合糸中に占める比率はデニール比率で２０〜
８０％、より好ましくは３０〜７０％の範囲とすべきで
ある。しかして、複合糸としての糸強力は、芯糸を構成
するマルチフィラメントＢで殆んど決まってくるので、
混繊、撚糸、サイジング、製繊等の後加工通過性および
織編布としての物性を確保するには、上記の破断強度と
デニール比率が必要となるからである。勿論、複合糸中
のマルチフィラメントＢのデニール比率が８０％を超え
ても、安定した工程通過性や織編物としての強力は確保
できるが、その場合は本発明で意図するソフトで優しい
パウダータッチが得られなくなる。The multifilament B has a breaking strength of 3.5 g / d or more, more preferably 3.8 g / d or more, and the ratio of the multifilament B in the composite yarn is 20 to 20 in terms of denier.
It should be in the range of 80%, more preferably 30-70%. However, since the yarn strength of the composite yarn is almost determined by the multifilament B forming the core yarn,
This is because the above-mentioned breaking strength and denier ratio are required to secure post-processability such as mixed fibers, twisted yarns, sizing, and fiber manufacturing, and physical properties as a woven or knitted fabric. Of course, even if the denier ratio of the multifilament B in the composite yarn exceeds 80%, stable process passability and strength as a woven or knitted fabric can be secured, but in that case, the soft and gentle powder touch intended by the present invention is achieved. You won't get it.
【００２１】次にマルチフィラメントＢの破断伸度は４
５％以下でなければならない。しかして、前述の如く本
発明の複合糸及び織編物の張力の殆どはマルチフィラメ
ントＢに依存するが、破断伸度の大きい（ヤング率の小
さい）ものでは、糸加工、サイジング、撚糸、織編工程
で張力を受けた時に不均一に引っ張られてヒケ状のムラ
糸になったり、製品としたときにパッカリングが生ずる
等の問題を引き起こすからである。こうした観点から、
より好ましい破断伸度は４０％以下である。Next, the breaking elongation of the multifilament B is 4
Must be 5% or less. As described above, most of the tension of the composite yarn and the woven / knitted fabric of the present invention depends on the multifilament B, but in the case of the one having a large breaking elongation (small Young's modulus), the yarn processing, the sizing, the twisted yarn, and the woven / knitted fabric. This is because when tension is applied during the process, it is pulled unevenly to form a sink-like uneven yarn, and when a product is produced, problems such as puckering occur. From this perspective,
A more preferable breaking elongation is 40% or less.
【００２２】上記のマルチフィラメントＡ，Ｂを複合し
て糸状に加工するに当たっては、実質的に同じ長さのも
のを使用し、それらを交絡処理されるが、このときの交
絡度は２０〜１２０個／ｍ、より好ましくは３０〜１０
０個／ｍの範囲に設定しなければならない。交絡度が２
０個／ｍ未満では、芯糸と鞘糸との染着差によるイラツ
キが生じ易くなるばかりでなく、複合糸がばらけ易くな
って後工程通過性を阻害する。逆に交絡度が１２０個／
ｍを超えると、毛羽が発生し易くなるばかりでなく、ま
たインターレースマークによるイラツキが生じ易く、い
ずれも本発明の目的にそぐわなくなる。When the above-mentioned multifilaments A and B are combined and processed into a thread shape, those having substantially the same length are used and they are entangled. The degree of entanglement at this time is 20 to 120. Pieces / m, more preferably 30 to 10
It must be set in the range of 0 pieces / m. Degree of confounding is 2
When the number is less than 0 / m, not only the unevenness due to the difference in dyeing between the core yarn and the sheath yarn is liable to occur, but also the composite yarn is liable to be scattered and the post-process passability is impaired. Conversely, the degree of confounding is 120 /
If it exceeds m, not only fluffing is likely to occur, but also irregularity due to interlaced marks is likely to occur, which is not suitable for the purpose of the present invention.
【００２３】本発明で使用する前記マルチフィラメント
Ａ，Ｂの構成素材は、ポリエステル系である限り格別の
制限はないが、中でも特に好ましいのは、５−ナトリウ
ムスルホン酸金属塩等を分子中に含むカチオン可染性ポ
リエステルであり、この様なポリエステル系樹脂からな
るマルチフィラメントを選択使用すれば、単繊維繊度の
細かいものであっても、カチオン系染料を用いることに
よって鮮明色も表現できるし、さらにシャンブレー、霜
降り、杢等も表現できるので好ましい。The constituent material of the multifilaments A and B used in the present invention is not particularly limited as long as it is a polyester type, but among them, particularly preferred is to include 5-sodium sulfonic acid metal salt in the molecule. It is a cationic dyeable polyester, and if a multifilament made of such a polyester resin is selectively used, even if the single fiber fineness is fine, it is possible to express a clear color by using a cationic dye. Chambray, marbled, heather and the like can be expressed, which is preferable.
【００２４】またこれらマルチフィラメントＡ，Ｂを構
成するフィラメントとして、原料ポリエステル系樹脂中
にカオリン、メタカオリン、酸化チタン等の微細孔形成
剤を適量（好ましくは０．５重量％程度以上）含有さ
せ、紡糸・延伸時の減量加工により微細孔を現出させた
フィラメントを使用すれば、複合糸としてのヌメリ感や
光沢感（反射）が抑えられ、深色性の表現が可能になる
ばかりでなくソフトドライ感も一段と高められるので好
ましい。Further, as filaments constituting these multifilaments A and B, an appropriate amount (preferably about 0.5% by weight or more) of a fine pore forming agent such as kaolin, metakaolin and titanium oxide is contained in the raw material polyester resin, By using filaments that have fine pores exposed by weight reduction processing during spinning and drawing, the slimy feel and glossiness (reflection) of the composite yarn can be suppressed, and not only the deep color property can be expressed but also the softness. It is preferable because the dry feeling can be further enhanced.
【００２５】本発明の複合糸は、上記の様に適度の交絡
処理によって収斂されているが、これを更に加撚処理す
ることは、イラツキ防止や後工程通過性を高める上で好
ましい。しかし、あまり強撚されているとフィラメント
の移動が阻害され、マルチフィラメントＡ，Ｂの熱収縮
差による鞘糸の膨出が起こり難くなるので、好ましくは
２０，０００／√Ｄ（Ｔ／Ｍ）程度以下、より好ましく
は１，８００／√Ｄ（Ｔ／Ｍ）程度以下に抑えるべきで
ある。The composite yarn of the present invention is converged by a proper entanglement treatment as described above, but it is preferable to further twist the twisted yarn in order to prevent flicker and improve the post-process passability. However, if it is twisted too much, the movement of the filament is hindered, and the bulging of the sheath yarn due to the difference in heat shrinkage between the multifilaments A and B is less likely to occur. Therefore, 20,000 / √D (T / M) is preferable. It should be suppressed to below about 1,800 / √D (T / M).
【００２６】本発明で芯糸および鞘糸として用いるマル
チフィラメントＡ，Ｂを構成する各フィラメントの横断
面が、複合糸にソフトドライタッチを持たせる為に複数
の突起を有し且つ異形度１．１以上が好ましいことは先
に述べたが、この他、必要によっては、マルチフィラメ
ントＢを構成するフィラメントを中空構造（異形を含
む）とすることにより、ハリ、コシを一段と強調したり
軽量感を高めることも可能である。細デニールであるマ
ルチフィラメントＡについてはその効果が少ないが、中
空断面のフィラメントを使用することも勿論可能であ
る。更にマルチフィラメントＡ，Ｂのいずれか一方又は
両方とも所謂シックアンドシンヤーンとし、自然なタッ
チと外観を与えることも、好ましい態様として推奨され
る。The cross section of each filament constituting the multifilaments A and B used as the core yarn and the sheath yarn in the present invention has a plurality of protrusions for imparting a soft dry touch to the composite yarn, and the degree of irregularity 1. As described above, one or more is preferable, but in addition, if necessary, the filament constituting the multi-filament B is made to have a hollow structure (including a variant) to further emphasize elasticity and stiffness, and to reduce the weight. It is possible to raise it. The effect is small for the multi-filament A having a fine denier, but it is of course possible to use a filament having a hollow cross section. Furthermore, it is also recommended as a preferred embodiment that either or both of the multifilaments A and B be so-called thick and thin yarns to give a natural touch and appearance.
【００２７】次に、本発明に係るポリエステル系マルチ
フィラメント複合糸の製造方法について、好ましい例を
示して具体的に説明するが、本発明はもとより下記の製
法によって制限を受けるものではない。Next, the method for producing the polyester-based multifilament composite yarn according to the present invention will be specifically described by showing preferred examples, but the present invention is not limited by the following production method.
【００２８】図１は、マルチフィラメントＡの仮撚とマ
ルチフィラメントＢとの交絡・複合を一連の工程で連続
的に実施する場合の説明図である。図１において、Ｘは
（延伸）仮撚加工後の状態で単繊維繊度が０．２〜０．
５デニールとなる原糸であり、これをガイド１を経てフ
ィードローラー２により送り出し、該ローラー２と第１
デリベリーローラー５の間でヒーター３により加撚状態
の糸を適度の温度に加熱してから仮撚ツイスターで加熱
・解撚し、仮撚加工されたマルチフィラメントＡとす
る。引き続いて、第２デリベリーローラー７との間に設
けられたインターレーサー６でボビンＹから繰り出され
てくるマルチフィラメントＢと合わせて交絡処理し、交
絡度２０〜１２０個／ｍとなる様に絡合してからチーズ
９に巻き取る。８はテークアップローラである。このと
き仮撚に用いられるスピンドルとしてはピンタイプのも
のが好ましいが、３軸ディスクタイプやベルトニップタ
イプであっても、各フィラメントへの損傷の少ない条件
を選定すれば適用可能である。FIG. 1 is an explanatory view of the case where the false twist of the multifilament A and the entanglement / composite of the multifilament B are continuously carried out in a series of steps. In FIG. 1, X has a single fiber fineness of 0.2 to 0. after being (stretched) false twisted.
A yarn having a denier of 5 denier, which is sent out by a feed roller 2 via a guide 1 and the roller 2 and the first yarn.
The twisted yarn is heated to an appropriate temperature by the heater 3 between the delivery rollers 5 and then heated and untwisted by a false twist twister to obtain a false twisted multifilament A. Subsequently, an interlacer 6 provided between the second delivery roller 7 and the second delivery roller 7 performs an entanglement process together with the multifilament B fed from the bobbin Y so that the entanglement degree becomes 20 to 120 pieces / m. After combining, roll it up on cheese 9. 8 is a take-up roller. At this time, a pin type is preferable as the spindle used for false twisting, but a triaxial disk type or a belt nip type can be applied if conditions that cause less damage to each filament are selected.
【００２９】仮撚加工条件は特に限定はないが、マルチ
フィラメントＢとの交絡を阻害しない様適度の開繊性を
保つため、仮撚数は28,000／√Ｄ以下、加工温度もやや
低めの１６０〜２００℃、加工張力はやや高めの０．４
〜０．６ｇ／ｄに設定するのが好ましい。ただし複合糸
の用途によっては、開繊性に問題ない範囲で且つ仮撚機
の操業性に悪影響を及ぼさない範囲でマルチフィラメン
トＡ，Ｂの一部に毛羽を生じさせることも可能である
が、その場合は、カット毛羽端が糸条に巻き付いたり未
解撚になって交絡が入り難くなることがあるので注意し
なければならない。The conditions for false twisting are not particularly limited, but in order to maintain an appropriate spreadability so as not to hinder the entanglement with the multifilament B, the number of false twists is 28,000 / √D or less, and the processing temperature is slightly lower than 160. ~ 200 ℃, processing tension is slightly higher 0.4
It is preferably set to ˜0.6 g / d. However, depending on the use of the composite yarn, it is possible to cause fluff to occur in a part of the multifilaments A and B within a range where there is no problem in openability and a range in which the operability of the false twisting machine is not adversely affected. In that case, care must be taken because the cut fluff ends may become wrapped around the yarn or become untwisted, making it difficult for entanglement to occur.
【００３０】上記の様にして得られる本発明のマルチフ
ィラメント複合糸を使用し、常法に従って製織若しくは
製編してから、染色および仕上げ加工を施すと、該織編
物を構成する複合糸内のマルチフィラメントＢが上記処
理工程で受ける熱処理により収縮すると共に、収縮率の
小さいマルチフィラメントＡが織編物の表面にループ状
に膨出し、優しい薄起毛調の豊かな膨らみ感、ソフトド
ライなパウダータッチ、適度なハリ、コシ、ドレープ性
などを全て満足する高品質の織編物を得ることができ
る。When the multifilament composite yarn of the present invention obtained as described above is used for weaving or knitting according to a conventional method and then subjected to dyeing and finishing, the inside of the composite yarn constituting the woven or knitted fabric is The multifilament B shrinks due to the heat treatment received in the above treatment step, and the multifilament A having a small shrinkage swells in a loop shape on the surface of the woven or knitted fabric, and a gentle fluffy rich swelling feeling, a soft dry powder touch, It is possible to obtain a high-quality woven or knitted fabric satisfying all of appropriate elasticity, elasticity and drape.
【００３１】[0031]
【実施例】以下、実施例を挙げて本発明をより具体的に
説明するが、本発明はもとより下記実施例によって制限
を受けるものではなく、前後記の趣旨に適合し得る範囲
で適当に変更を加えて実施することも勿論可能であり、
それらはいずれも本発明の技術的範囲に含まれる。な
お、実施例で採用した各物性の測定方法は以下の通りで
ある。The present invention will be described in more detail with reference to the following examples. However, the present invention is not limited to the following examples, and can be appropriately modified within the range that can meet the gist of the preceding and following description. Of course, it is also possible to add
All of them are included in the technical scope of the present invention. In addition, the measuring method of each physical property adopted in the examples is as follows.
【００３２】（１）破断強度、破断伸度 ＪＩＳ−Ｌ−１０１３（１９９２）に準じ、東洋ボール
ドウィン社製「テンシロン」を用いて試料長（ゲージ
長）２００ｍｍ、引張速度２００ｍｍ／分でＳ−Ｓ曲線
を測定し、破断強度および破断伸度を算出した。(1) Breaking Strength and Breaking Elongation According to JIS-L-1013 (1992), using "Tensilon" manufactured by Toyo Baldwin Co., Ltd., sample length (gauge length) 200 mm, tensile speed 200 mm / min S-S The curve was measured and the breaking strength and breaking elongation were calculated.
【００３３】（２）熱水収縮率（ＳＨＷ） ＪＩＳ−Ｌ−１０１３（１９９２）に準じ、次の方法に
よって測定した。即ち、適当な枠周のラップリールで初
荷重１／１０ｇ／デニールで８回捲のカセをとり、カセ
に１／３０ｇ／デニールの荷重をかけてその長さＩ0
（ｍｍ）を測定する。次いでその荷重を取り除き、１／
１０００ｇ／デニールの荷重をかけた状態でカセを沸騰
水中に３０分間浸漬する。その後カセを沸騰水から取り
出し、冷却後再び１／３０ｇ／デニールの荷重をかけて
その時の長さＩ1 （ｍｍ）を測定し、下記式によって熱
水収縮率（ＳＨＷ）を算出する。 ＳＨＷ＝（Ｉ0 −Ｉ1 ）×１００÷Ｉ0 （％）(2) Hot water shrinkage (SHW) According to JIS-L-1013 (1992), the shrinkage was measured by the following method. That is, a wrap reel having an appropriate frame circumference is used to take a casks wound 8 times with an initial load of 1/10 g / denier, and a load of 1/30 g / denier is applied to the casks to obtain its length I 0.
(Mm) is measured. Then remove the load and
The mold is immersed in boiling water for 30 minutes while applying a load of 1000 g / denier. After that, the haze was taken out from the boiling water, and after cooling, a load of 1/30 g / denier was applied again to measure the length I 1 (mm) at that time, and the hot water shrinkage ratio (SHW) was calculated by the following formula. SHW = (I 0 −I 1 ) × 100 ÷ I 0 (%)
【００３４】（３）交絡度 適当な長さの糸を取り出し、下端に１／１０ｇ／デニー
ルの荷重をかけて垂直に吊り下げる。次いで適当なニー
ドルを糸に突き刺して静かに持ち上げ、ニードルが停止
した距離（ｃｍ）を１００回測定して平均値Ｉ（ｃｍ）
を求め、次式により交絡度を算出する。 交絡度＝１００÷（２×Ｉ）(3) Degree of entanglement A thread of an appropriate length is taken out and vertically suspended by applying a load of 1/10 g / denier to the lower end. Then, a suitable needle is pierced into the thread and gently lifted, and the distance (cm) at which the needle stops is measured 100 times and the average value I (cm) is measured.
And the degree of confounding is calculated by the following equation. Entanglement degree = 100 ÷ (2 × I)
【００３５】（４）ウースターノルマル（ＵＲｎ） ツェルベガー社製「ウースターイーブネステスターＣ
型」を使用し、糸速度５０ｍ／分で走行させて仮撚を付
与しつつ試料のデニールに応じたスロットによりノーマ
ルで２分間、２．５ｃｍ／分で測定チャートを描く。次
いでチャートを２．５ｃｍで２分割し、それぞれの最高
値（Ｍ１，２）／最低値（Ｌ１，２）を読み取り、その
値から次式によって算出する。 ＵＲｎ＝［（Ｍ１＋Ｍ２）＋（｜Ｌ１｜＋｜Ｌ２｜）］
／２ （５）異形度 適当な倍率で断面を撮影し内接円と外接円の比から算出
する。(4) Wooster Normal (URn) "Wooster Eve Nestester C" manufactured by Zellveger
Using a "mold", while running at a yarn speed of 50 m / min to give false twist, a measurement chart is drawn at 2.5 cm / min for 2 minutes in a normal manner with a slot corresponding to the denier of the sample. Then, the chart is divided into two at 2.5 cm, the maximum value (M1,2) / minimum value (L1,2) of each is read, and the value is calculated by the following formula. URn = [(M1 + M2) + (| L1 | + | L2 |)]
/ 2 (5) Deformedness The cross section is photographed at an appropriate magnification and calculated from the ratio of the inscribed circle and the circumscribed circle.
【００３６】実施例１〜３，比較例１〜９ 三菱重工（株）製「ＬＳ−６」仮撚機を一部改造した図
１の仮撚機を使用し、表１に示す諸元のマルチフィラメ
ントＡ，Ｂを同表に示す比率および交絡度で複合して複
合糸を製造し、その物性、風合い、外観、操業性を評価
すると共に総合品質を評価し、結果を表２に示した。Examples 1 to 3 and Comparative Examples 1 to 9 Using the false twisting machine of FIG. 1 obtained by partially modifying the "LS-6" false twisting machine manufactured by Mitsubishi Heavy Industries, Ltd., the specifications shown in Table 1 are used. The multifilaments A and B were compounded in the ratio and the degree of entanglement shown in the same table to produce a composite yarn, and the physical properties, texture, appearance and operability thereof were evaluated and the overall quality was evaluated. The results are shown in Table 2. .
【００３７】[0037]
【表１】 [Table 1]
【００３８】[0038]
【表２】 [Table 2]
【００３９】表１，２より次の様に考察される。実施例
１〜３は本発明の規定要件を全て満足する実施例であ
り、風合い、外観、操業性のいずれにおいても良好な結
果が得られている。特に実施例１は、マルチフィラメン
トＢにカオリナイトが含まれているので光沢が抑えら
れ、また実施例３では、マルチフィラメントＢがカチオ
ン染料可染性であるため、シャンブレー効果が見られて
好ましい。The following is considered from Tables 1 and 2. Examples 1 to 3 are examples that satisfy all the requirements of the present invention, and good results are obtained in terms of texture, appearance, and operability. In particular, in Example 1, since the multifilament B contains kaolinite, the gloss is suppressed, and in Example 3, the multifilament B is dyeable with a cationic dye, so that the chambray effect is observed, which is preferable.
【００４０】これに対し比較例１は、マルチフィラメン
トＡのＳＨＷA が大き過ぎるため、マルチフィラメント
ＢとのΔＳＨＷは十分大きい値となっているが、膨らみ
に欠けており、またマルチフィラメントＢのＳＨＷB が
大き過ぎるため、製品でのパッカリングが発生した。On the other hand, in Comparative Example 1, since the SHW A of the multifilament A is too large, the ΔSHW with the multifilament B is a sufficiently large value, but the bulge is lacking and the SHW of the multifilament B is also large. Since B is too large, puckering occurred on the product.
【００４１】また比較例２は、マルチフィラメントＢの
破断強度が不足すると共に破断伸度が大き過ぎるため、
撚糸や製繊工程で糸切れが発生し、しかも不均一に伸長
されてヒケ状の欠点が発生しており、更に織物としての
引裂強力も低かった。比較例３は、マルチフィラメント
Ａの単繊維繊度が規定範囲を超えているため、ソフト感
に欠け外観も単調な物となった。In Comparative Example 2, the breaking strength of the multifilament B is insufficient and the breaking elongation is too large.
Thread breakage occurred in the twisting and fiber-making processes, and the yarn was unevenly stretched to cause a sink-like defect, and the tear strength as a woven fabric was low. In Comparative Example 3, since the single fiber fineness of the multifilament A exceeds the specified range, the soft feeling was lacking and the appearance was monotonous.
【００４２】比較例４は、マルチフィラメントＡの単繊
維繊度が細か過ぎるため、染着度差が大きくなってイラ
ツキが目立つ。しかも複合糸の外側に膨出するフィラメ
ントＡがソフト過ぎてクタットした物となっている。In Comparative Example 4, since the single fiber fineness of the multifilament A is too fine, the difference in the degree of dyeing becomes large and the irregularity is noticeable. Moreover, the filament A bulging to the outside of the composite yarn is too soft and is cut.
【００４３】比較例５は、マルチフィラメントＡとして
丸断面のフラットヤーンを用いた例であるが、仮撚捲縮
加工が施されていないため柔軟さが不足し、ヌメリの強
い物となっている。Comparative Example 5 is an example in which a flat yarn having a round cross section is used as the multifilament A, but since the false twist crimping process is not applied, the flexibility is insufficient and the product has a strong slime. .
【００４４】比較例６は、マルチフィラメントＡの複合
比率が不足（マルチフィラメントＢの複合比率が過大）
するため、ソフト感に欠けるものであった。またマルチ
フィラメントＢの横断面も丸であるため、ややドライ感
が不足している。比較例７は、マルチフィラメントＢの
ＳＨＷB が低く、マルチフィラメントＡとのΔＳＨＷも
小さいために膨らみが不足する。In Comparative Example 6, the composite ratio of multifilament A is insufficient (the composite ratio of multifilament B is excessive).
Therefore, it lacked in softness. Further, since the cross section of the multifilament B is also round, the dry feeling is slightly insufficient. In Comparative Example 7, the SHW B of the multifilament B is low and the ΔSHW of the multifilament A is also small, so that the bulge is insufficient.
【００４５】比較例８は、交絡度（Ｄｉ）が不足するた
め染着差がそのまま木目状となって表われ、しかもフィ
ラメントＢが分離し操業性が著しく害される。比較例８
は、逆にＤｉが大き過ぎる比較例であり、操業性に問題
はなかったが、一部のフィラメントが切断して毛羽立ち
を起こし、またインターレースマークが目立った。In Comparative Example 8, since the degree of entanglement (Di) is insufficient, the difference in dyeing appears in the form of wood grain as it is, and the filament B is separated, and the operability is significantly impaired. Comparative Example 8
On the contrary, in Comparative Example where Di was too large, there was no problem in operability, but some filaments were cut to cause fuzz, and interlaced marks were conspicuous.
【００４６】[0046]
【発明の効果】本発明は以上の様に構成されており、複
合糸の鞘糸を構成するポリエステル系マルチフィラメン
トＡと芯糸を構成するポリエステル系マルチフィラメン
トＢの単繊維デニールや熱水収縮率、収縮率差、破断強
度などを規定すると共に、それらの複合比率と交絡度を
適正に設定することにより、従来のポリエステル系複合
糸に比べて、優れた工程通過性のもとで、優しい薄起毛
調のパウダータッチを有すると共に、適度なハリ、コ
シ、ドレープ性を備えた織編物を与える複合糸を提供
し、更にはこの複合糸を使用することによって、優れた
品質・特性を備えた織編物を提供し得ることになった。The present invention is constituted as described above, and the single fiber denier and the hot water shrinkage of the polyester multifilament A constituting the sheath yarn of the composite yarn and the polyester multifilament B constituting the core yarn. , Shrinkage ratio difference, breaking strength, etc., and by appropriately setting their composite ratio and degree of entanglement, compared to conventional polyester-based composite yarn, it has excellent process passability and is gentle and thin. We provide a composite yarn that gives a woven and knitted fabric with a raised-powder-like powder touch and appropriate elasticity, stiffness, and drape, and by using this composite yarn, weave with excellent quality and characteristics. Knitting can be provided.
【図１】本発明に係る複合糸の製造装置を例示する説明
図である。FIG. 1 is an explanatory view illustrating a device for manufacturing a composite yarn according to the present invention.
Ａ マルチフィラメントＡ Ｂ マルチフィラメントＢ Ｃ 複合糸 ２ フィードローラー ３ ヒーター ４ 仮撚ツイスター ５ 第１デリベリーローラー ６ インターレーサー ７ 第２デリベリーローラー ９ チーズ A multi-filament A B multi-filament B C composite yarn 2 feed roller 3 heater 4 false twist twister 5 1st deliberry roller 6 interlacer 7 2nd deliberry roller 9 cheese
Claims (5)
ルチフィラメントＡとポリエステル系マルチフィラメン
トＢとが、前者：２０〜８０％、後者８０〜２０％のデ
ニール比率で複合されると共に、それらが交絡度２０〜
１２０個／ｍで絡合した複合糸からなることを特徴とす
るポリエステル系マルチフィラメント複合糸。 マルチフィラメントＡ：ｄｐｆA が０．２〜０．５デニ
ール、ＳＨＷA が７％以下で、仮撚捲縮されたマルチフ
ィラメント マルチフィラメントＢ：ｄｐｆB が２デニール以上、Ｓ
ＨＷB が５〜６０％、ＤＴB が３．５ｇ／ｄ以上、ＤＥ
B が４５％以下であるマルチフィラメント 但し、ＳＨＷB −ＳＨＷA は５％以上 上記において、ｄｐｆA およびｄｐｆB は、ポリエステ
ル系マルチフィラメントＡおよびＢの単繊維デニール、
ＳＨＷA およびＳＨＷB は、ポリエステル系マルチフィ
ラメントＡおよびＢの熱水（１００℃）収縮率、ＤＥB
はポリエステル系マルチフィラメントＢの破断伸度、Ｄ
ＴB はポリエステル系マルチフィラメントＢの破断強度
をそれぞれ表わす。1. A polyester-based multifilament A and a polyester-based multifilament B having the following physical properties are compounded at a denier ratio of the former: 20 to 80% and the latter 80 to 20%, and they are entangled. 20 ~
A polyester-based multifilament composite yarn comprising a composite yarn entangled at 120 yarns / m. Multifilament A: dpf A of 0.2 to 0.5 denier, SHW A of 7% or less, false-twist crimped multifilament B: dpf B of 2 denier or more, S
HW B is 5~60%, DT B is 3.5g / d or more, DE
Multifilament in which B is 45% or less However, SHW B- SHW A is 5% or more In the above, dpf A and dpf B are monofilament denier of polyester-based multifilaments A and B,
SHW A and SHW B are hot water (100 ° C.) shrinkage of polyester-based multifilaments A and B, DE B
Is the elongation at break of polyester-based multifilament B, D
T B represents the breaking strength of the polyester multifilament B, respectively.
断面形状において３以上の突起を有すると共に異形度が
１．１以上のフィラメントの集合体である請求項１に記
載の複合糸。2. The composite yarn according to claim 1, wherein at least the multifilament B is an aggregate of filaments having three or more protrusions in a cross-sectional shape and having a degree of irregularity of 1.1 or more.
ントＢの全部又は一部がカチオン可染性ポリエステルか
らなる請求項１または２に記載の複合糸。3. The composite yarn according to claim 1, wherein all or part of the multifilament A and the multifilament B are made of cationic dyeable polyester.
ントＢの全部又は一部が、微細孔形成剤を０．５％以上
含有するポリエステルからなるものである請求項１〜３
のいずれかに記載の複合糸。4. The multifilament A and the multifilament B are wholly or partly made of polyester containing 0.5% or more of a micropore forming agent.
7. The composite yarn according to any one of 1.
リエステル系マルチフィラメント複合糸を全部もしくは
一部として用いて製織もしくは製編した後、染色および
仕上げ加工を施し、織編物表面に前記ポリエステル系マ
ルチフィラメントＡをループ状に膨出させたものである
ことを特徴とするポリエステル系複合織編物。5. A polyester-based multifilament composite yarn according to any one of claims 1 to 4 is used as a whole or a part of the fabric, which is woven or knitted, and then dyed and finished, and the surface of the woven or knitted fabric is subjected to A polyester-based composite woven or knitted fabric, wherein the polyester-based multifilament A is swelled in a loop shape.