JPH09320116A - 光ディスク - Google Patents

光ディスク

Info

Publication number
JPH09320116A
JPH09320116A JP8160803A JP16080396A JPH09320116A JP H09320116 A JPH09320116 A JP H09320116A JP 8160803 A JP8160803 A JP 8160803A JP 16080396 A JP16080396 A JP 16080396A JP H09320116 A JPH09320116 A JP H09320116A
Authority
JP
Japan
Prior art keywords
adhesive
recording layer
information recording
optical disk
transparent substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP8160803A
Other languages
English (en)
Inventor
Takashi Daiko
高志 大胡
Junichi Iimura
純一 飯村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Victor Company of Japan Ltd
Original Assignee
Victor Company of Japan Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Victor Company of Japan Ltd filed Critical Victor Company of Japan Ltd
Priority to JP8160803A priority Critical patent/JPH09320116A/ja
Priority to EP97108635A priority patent/EP0810591B1/en
Priority to DE1997627726 priority patent/DE69727726T2/de
Priority to US08/866,361 priority patent/US6037099A/en
Publication of JPH09320116A publication Critical patent/JPH09320116A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】 【課題】 反りの発生を最小限に抑えた光ディスクを提
供する。 【解決手段】 ディスク基板１ａと１ｂまたはディスク
基板１ａと１ａを貼り合わせる際に、接着剤層３のヤン
グ率と膜厚を掛け合わせた数値、ヤング率と熱膨張係数
とを掛け合わせた数値、熱膨張係数と膜厚を掛け合わせ
た数値を所定の範囲に設定すること、接着剤のガラス転
移点を２０℃〜８０℃の範囲に設定し且つ膜厚を１０μ
ｍ以上１００μｍ以下の範囲に設定すること、更に、接
着剤のガラス転移点を２０℃〜８０℃の範囲に設定し且
つ膜厚を１０μｍ以上１００μｍ以下の範囲に設定す
る。

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、光ディスクに関し、特
に保存安定性の優れた貼り合わせ型光ディスクに関する
ものである。
【０００２】
【従来の技術】基板の表面に記録層または反射層を有す
る基板２枚を貼り合わせてなる光ディスクは、記録容量
が大きいという利点を持ち、ビデオディスクやデジタル
オーディオディスク、文書やデータのファイル用のディ
スクとして利用されている。図９は従来の貼り合わせ型
光ディスクの概略を示す断面斜視図であり、図１０のａ
とｂはその貼り合わせ面の概略を示す断面図である。従
来の貼り合わせ型光ディスク３０は、片面に信号ピット
やトラッキング用のグルーブが形成されている厚さ１．
２ｍｍ程度の光透過性を有する基板９の信号ピットある
いはグルーブ側に記録層１０が設けられ、必要に応じて
保護膜１１が設けられている２枚の記録層付き基板の記
録層１０同士が対向する状態で接着剤層１２を介して貼
り合わされている両面記録再生タイプ（ａ）と、一方の
基板には記録層の無い片面記録再生タイプ（ｂ）があ
る。
【０００３】基板９の形成材料としては、光透過性を有
しているものであればよく、例えば光学ガラス、アクリ
ル樹脂、ポリカーボネート樹脂およびアモルファスポリ
オレフィン樹脂などが挙げられる。記録層１０の材料と
しては、例えばＴｂＦｅ、ＧｄＣｏ、ＧｄＴｂＦｅ、Ｍ
ｎＣｕＢｉ等の光磁気記録材料やＡｓ−Ｔｅ−Ｇｅ系、
Ｓｎ−Ｔｅ−Ｓｅ系等の相変化記録材料などの書き換え
可能な種々の材料や、シアニン系やフタロシアニン系に
代表される追記型の材料や、あらかじめ基板に信号ピッ
トが形成されている再生専用型の場合はアルミニウム
系，Ｃｕ系，Ａｇ系，Ａｌ系材料反射層などにより形成
される。保護膜１１の材料としては主に紫外線硬化型樹
脂が用いられ、接着剤層１２の材料としては主にホット
メルト型接着剤と紫外線硬化型接着剤（以下ＵＶ接着
剤）が用いられる。
【０００４】
【発明が解決しようとする課題】ところで、光ディスク
を取り扱う上で必ず発生するのが反りの問題であり、貼
り合わせ型光ディスクも例外ではない。従来の貼り合わ
せ型光ディスクは、１．２ｍｍ厚の基板をスペーサーを
介して、あるいは直接貼り合わせた構造であったが、最
近では高密度化の流れにともない、基板の厚さが薄くな
る方向にある。従って、基板厚が薄くなるとディスクの
剛性が弱くなるため反りやすくなり、特にディスクが片
面記録再生タイプ（ｂ）の場合は、その構造的なアンバ
ランスからより反りが発生し易くなっているのである。
また反りの発生の原因として、接着剤の物性も大きく起
因している。従来の貼り合わせ型光ディスクに使用され
ている接着剤であるＰＳ４５０−２０（エイ・シー・ア
イ・ジャパン・リミテッド製、商品名）を用いて０．６
ｍｍ厚のポリカーボネート基板を貼り合わせた片面記録
再生型光ディスクを温度５５℃、湿度９５％、９６時間
の環境試験にかけ、取り出し直後からの反り角の経時変
化を測定した結果を図８に示すが、環境試験前後で反り
角が１．０ｄｅｇ．近く変化してしまう。他のホットメ
ルト型接着剤としては、ＰＳ４５０−５６（エイ・シー
・アイ・ジャパン・リミテッド製、商品名）、ＰＰＥＴ
−２１０１（東亜合成（株）製、商品名）、あるいは他
のＥＶＡ系やポリオレフィン系の接着剤が使用されてい
るが、同様に反り角の変化が大きい。またＵＶ接着剤に
おいても、アロニックスＵＶ−３６１０、３８１０、Ｍ
−２１０、Ｍ−２４０、Ｍ−１１００、Ｍ−１２００、
Ｍ−１４００、Ｍ−６１００、Ｍ−６２００、Ｍ−６２
５０、Ｍ−６３００（以上東亜合成（株）製、商品名）
や、シクロヘキシル（メタ）アクリレート、ポリエチレ
ングリコールジ（メタ）アクリレート、１，６−ヘキサ
ンジオールジ（メタ）アクリレート、ネオペンチルグリ
コールジアクリレート、ヒドロキシピバリン酸ネオペン
チルグリコールジ（メタ）アクリレート、ＥＯ変性ビス
フェノールＡジアクリレート、イソボルニル（メタ）ア
クリレートなどが用いられるが、ホットメルトの場合と
同様に反り角の変化が大きい。このように従来の貼り合
わせ型光ディスクでは、使用環境条件に急激な変化があ
った場合反り角が大きく変化してしまう。高密度化に伴
い、プレーヤー側のディスクの反りに対するマージンも
少なくなり、環境変化による反り角の変化量は０．２ｄ
ｅｇ．以下であることが要求されている。しかもコンピ
ューターの周辺機器に光ディスクを使用する傾向にある
ので、光ディスクの耐環境性は、従来よりも更に厳しい
使用環境条件に対応できるよう更なる向上が望まれてい
る。
【０００５】そこで、本発明は上記の点に着目してなさ
れたものであり、高温多湿といった厳しい環境下でも反
りの発生を抑えた保存安定性の優れた貼り合わせ型光デ
ィスクを提供することを目的とするものである。
【０００６】
【課題を解決するための手段】上述した問題点を解決す
るために、本発明による光ディスクは、上面に金属膜あ
るいは有機色素からなる情報記録層を有する透明基板
と、情報記録層のない透明基板、又は、上面に金属膜あ
るいは有機色素からなる情報記録層を有する透明基板同
士を情報記録層が内側になるように接着剤層を介して貼
り合わせてなる光ディスクにおいて、前記基板の貼り合
わせに用いる接着剤のヤング率と前記接着剤層の膜厚を
掛け合わせた数値が、１．０×１０-2ｋｇ／ｍｍ以上
３．０ｋｇ／ｍｍ以下であることを特徴とするものであ
る。
【０００７】また、本発明による光ディスクは、上面に
金属膜あるいは有機色素からなる情報記録層を有する透
明基板と、情報記録層のない透明基板、又は、上面に金
属膜あるいは有機色素からなる情報記録層を有する透明
基板同士を情報記録層が内側になるように接着剤層を介
して貼り合わせてなる光ディスクにおいて、前記基板の
貼り合わせに用いる接着剤の熱膨張係数とヤング率を掛
け合わせた数値が、１．５×１０-2ｋｇ・ｍｍ-2・℃-1
以下であることを特徴とするものである。
【０００８】更に、本発明による光ディスクは、上面に
金属膜あるいは有機色素からなる情報記録層を有する透
明基板と、情報記録層のない透明基板、又は、上面に金
属膜あるいは有機色素からなる情報記録層を有する透明
基板同士を情報記録層が内側になるように接着剤層を介
して貼り合わせてなる光ディスクにおいて、前記基板の
貼り合わせに用いる接着剤の熱膨張係数と前記接着剤層
の膜厚を掛け合わせた数値が、２．０×１０-5ｍｍ／℃
以下であることを特徴とするものである。
【０００９】更にまた、本発明による光ディスクは、上
面に金属膜あるいは有機色素からなる情報記録層を有す
る透明基板と、情報記録層のない透明基板、又は、上面
に金属膜あるいは有機色素からなる情報記録層を有する
透明基板同士を情報記録層が内側になるように接着剤層
を介して貼り合わせてなる光ディスクにおいて、前記基
板の貼り合わせに用いる接着剤のガラス転移点が２０℃
以上８０℃以下であり、且つ、前記接着剤層の膜厚が１
０μｍ以上１００μｍ以下であることを特徴とするもの
であり、接着剤のヤング率の温度変化の平均傾きが−
１．０ｋｇ／ｍｍ2/℃以上であることを特徴とするもの
を含む。
【００１０】
【発明の実施の形態】
【実施例１】以下、添付図面を参照して本発明の一実施
例を説明する。図１は本発明の一実施例における光記録
ディスクの断面図を示すものである。射出成形により成
形された信号ピットの記録された０．６ｍｍ厚の透明な
ポリカーボネート基板１ａの信号ピット側に約７００オ
ングストロームの厚さのアルミニウムの反射層２をスパ
ッタリング法により形成したディスクを準備し、その反
射層側の半径４０ｍｍ付近に円形に接着剤を約３ｇ滴下
し、その上に反射層も保護膜も無い透明な基板１ｂを乗
せ、直後に５００〜４０００ｒｐｍの回転数で２〜６０
秒間回転させることによりディスク全面を接着剤で被覆
させた後、基板１ｂ側から１００Ｗ／ｃｍの高圧水銀灯
により５秒間紫外線照射することにより接着剤を硬化さ
せ、再生専用の貼り合わせ型光ディスク１０を得た。
【００１１】
【表１】
【００１２】接着剤として表１に示すような材質及び温
度によってヤング率の異なるＵＶ硬化型接着剤Ａ１〜Ｈ
１を準備し、それぞれの接着剤を用いて膜厚をパラメー
タにして図１のような構造の貼り合わせ型光ディスクを
作製した。室温（２０℃）にて反り角を測った後、それ
ぞれのディスクを表１に示した条件温度５５℃、湿度
９５％、９６時間，条件温度７０℃、湿度９０％、９
６時間，条件温度８０℃、湿度８５％、９６時間とい
う３種類の条件の下環境試験にかけた。そして環境試験
の終了後、温度２５℃、湿度５０％の環境下に２４時間
放置した後の反り角を測定し、環境試験前後の反り角の
変化量を測定した。なお反り角はＪＩＳＳ ８６０５で
規定された反り角のレベルを測定できる専用の測定機
（アドモントサイエンス社製ＳＨ−３ＤＬ−１２Ｎ）を
用いて行い、測定径は反り角の変化が最大になる最外周
（半径５８ｍｍ）で行った。またヤング率は、接着剤を
幅４ｍｍ、長さ３０ｍｍ、厚さ５０μｍの短冊状に形成
し、熱応力歪測定装置（型式ＴＭＡ／ＳＳ１０、セイコ
ー電子工業株式会社製）を用いて、この試料に温度をか
けながら１５±５ｇの引っ張り応力をかけた時の応力と
歪の関係から求め、膜厚のコントロールはスピンの回転
数と時間を調整することによって行なった。
【００１３】反り角の変化量の結果を表１及び図３に示
す。図３は表１の結果をグラフ化したものである。前述
したように環境変化に伴う反り角の変動は０．２ｄｅ
ｇ．以下が望ましい。図３から、接着剤の特性値として
ヤング率×膜厚の値は１．０×１０-2ｋｇ／ｍｍ以上
３．０ｋｇ／ｍｍ以下の範囲において反り角の変動が
０．２ｄｅｇ．以下の要求を満足することが確認され
た。
【００１４】
【実施例２】図２は本発明の一実施例における光記録デ
ィスクの断面図を示すものである。射出成形によりトラ
ッキンググルーブの記録された０．６ｍｍ厚の透明なポ
リカーボネート基板４ａのトラッキンググルーブ側に第
一誘電体保護層５として窒化ケイ素の薄膜をスパッタリ
ング法により約９００オングストロームの厚さに成膜
し、その上に記録層６としてＴｂＦｅＣｏの薄膜を１０
００オングストロームの膜厚で成膜されている。そして
さらにその上に第二誘電体保護層７として窒化ケイ素の
薄膜を９００オングストロームの厚さで成膜し、その上
にＵＶ保護層８としてＳＤ−１７（大日本インキ株式会
社製、商品名）をスピンコート法により１０μｍの厚さ
で形成した。この記録層の形成された基板４ａと記録層
も保護層も無い透明な基板４ｂとを実施例１と同様にス
ピンコート法により接着剤層３を介して貼り合わせるこ
とによって、記録再生可能な貼り合わせ型光ディスク２
０を得た。そして実施例１と同様に表１の接着剤につい
て検討したところ、実施例１と同様に接着剤の特性値と
してヤング率×膜厚の値を１．０×１０-2ｋｇ／ｍｍ以
上３．０ｋｇ／ｍｍ以下に設定することによって反り角
の変動を０．２ｄｅｇ．以下に抑えられることが確認で
きた。
【００１５】
【実施例３】実施例３は先に説明した貼り合わせ型光デ
ィスク１０に適用する接着剤の特性に関する。
【００１６】
【表２】
【００１７】接着剤として表２に示すような物性を持つ
ＵＶ硬化型接着剤Ａ２〜Ｈ２を準備し、それぞれの接着
剤を用いて図１のような構造の貼り合わせ型光ディスク
１０を作製した。室温（２０℃）にて反り角を測った
後、それぞれのディスクを表２に示した条件温度５５
℃、湿度９５％、９６時間条件温度７０℃、湿度９０
％、９６時間，条件温度８０℃、湿度８５％、９６時
間という３種類の条件の下、環境試験にかけた。そして
環境試験の終了後、温度２５℃、湿度５０％の環境下に
２４時間放置した後の反り角を測定し、環境試験前後の
反り角の変化量を測定した。なお反り角はＪＩＳ Ｓ
８６０５で規定された反り角のレベルを測定できる専用
の測定機（アドモントサイエンス社製ＳＨ−３ＤＬ−１
２Ｎ）を用いて行い、測定径は反り角の変化が最大にな
る最外周（半径５８ｍｍ）で行った。またヤング率は、
接着剤を幅４ｍｍ、長さ３０ｍｍ、厚さ５０μｍの短冊
状に形成し、熱応力歪測定装置（型式ＴＭＡ／ＳＳ１
０、セイコー電子工業株式会社製）を用いて、この試料
に温度をかけながら１５±５ｇの引っ張り応力をかけた
時の応力と歪の関係から求めた。そして熱膨張係数も上
記熱応力歪測定装置を用いて、１ｍｍ厚の試料に３ｇの
一定圧縮加重を掛けながら昇温させたときの膨張量から
求めた。
【００１８】図４に接着剤の特性値と反り角の変化量の
結果を示す。前述したように環境変化に伴う反り角の変
動は０．２ｄｅｇ．以下が望ましい。図４から、接着剤
の特性値として熱膨張係数×ヤング率が１．５×１０-2
ｋｇ・ｍｍ-2・℃-1以下の範囲において反り角の変動が
０．２ｄｅｇ．以下の要求を満足することが確認され
た。
【００１９】
【実施例４】実施例２と同様に図２のような構造の光デ
ィスク２０を作製した。そして表２に示す接着剤につい
て検討したところ、実施例３と同様に接着剤の特性値と
して熱膨張係数×ヤング率を１．５×１０-2ｋｇ・ｍｍ
-2・℃-1以下に設定することによって反り角の変動を
０．２ｄｅｇ．以下に抑えられることが確認できた。
【００２０】
【実施例５】実施例５も先に説明した貼り合わせ型光デ
ィスク１０に適用する接着剤の特性に関する。
【００２１】
【表３】
【００２２】接着剤として表３に示すような熱膨張係数
の異なるＵＶ硬化型接着剤Ａ３〜Ｃ３を準備し、それぞ
れの接着剤を用いて膜厚をパラメータにして図１のよう
な構造の貼り合わせ型光ディスク１０を作製した。室温
（２０℃）にて反り角を測った後、それぞれのディスク
を表３に示した条件温度５５℃、湿度９５％、９６時
間，条件温度７０℃、湿度９０％、９６時間，条件
温度８０℃、湿度８５％、９６時間という３種類の条件
の下、環境試験にかけた。そして環境試験の終了後、温
度２５℃、湿度５０％の環境下に２４時間放置した後の
反り角を測定し、環境試験前後の反り角の変化量を測定
した。なお反り角はＪＩＳ Ｓ ８６０５で規定された
反り角のレベルを測定できる専用の測定機（アドモント
サイエンス社製ＳＨ−３ＤＬ−１２Ｎ）を用いて行い、
測定径は反り角の変化が最大になる最外周（半径５８ｍ
ｍ）で行った。また熱膨張係数は、熱応力歪測定装置
（型式ＴＭＡ／ＳＳ１０、セイコー電子工業株式会社
製）を用いて、１ｍｍ厚に硬化させた試料に３ｇの一定
圧縮加重を掛けながら昇温させたときの膨張量から求め
た。膜厚のコントロールはスピンの回転数と時間を調整
することによって行なった。
【００２３】図５に反り角の変化量の結果を示す。前述
したように環境変化に伴う反り角の変動は０．２ｄｅ
ｇ．以下が望ましい。図５から、接着剤の特性値として
熱膨張係数×膜厚が２．０×１０-5mｍ／℃以下の範囲
において反り角の変動が０．２ｄｅｇ．以下の要求を満
足することが確認された。
【００２４】
【実施例６】実施例２と同様に図２のような構造の光デ
ィスク２０を作製した。そして表３に示す接着剤につい
て検討したところ、実施例５と同様に接着剤の特性値と
して熱膨張係数×膜厚を２．０×１０-5ｍｍ／℃以下に
設定することによって反り角の変動を０．２ｄｅｇ．以
下に抑えられることが確認できた。
【００２５】
【実施例７】実施例７も先に説明した貼り合わせ型光デ
ィスク１０に適用する接着剤の特性に関する。
【００２６】
【表４】
【００２７】接着剤として表４に示されるようなガラス
転移点（以下Ｔｇという）の異なる数種類の硬化型接着
剤Ａ４〜Ｆ４を準備し、それぞれの接着剤を用いて膜厚
をパラメータにして図１のような構造の貼り合わせ型光
ディスク１０を作製した。室温（２０℃）にて反り角を
測った後、それぞれのディスクを温度８０℃、湿度８５
％、９６時間の条件の下、環境試験にかけた。そして環
境試験の終了後、温度２０℃、湿度５０％の環境下に２
４時間放置した後の反り角を測定し、環境試験前後の反
り角の変化量を測定した。なお反り角はＪＩＳ Ｓ ８
６０５で規定された反り角のレベルを測定できる専用の
測定機を用いて行い、測定径は反り角の変化が最大にな
る最外周（半径５８ｍｍ）で行った。またＴｇはＤＳＣ
法によって求め、ヤング率の温度変化は、接着剤を幅４
ｍｍ、長さ３０ｍｍ、厚さ５０μｍの短冊状に形成し、
熱応力歪測定装置（型式ＴＭＡ／ＳＳ１０、セイコー電
子工業株式会社製）を用いて、この試料に温度をかけな
がら１５±５ｇの引っ張り応力をかけたときの応力と歪
の関係から求め、膜厚はスピンの回転数と時間を調整す
ることによって行なった。
【００２８】反り角の変化量の結果を表４及び図６に示
す。前述したように環境変化に伴う反り角の変動は０．
２ｄｅｇ．以下が望ましい。図６から、接着剤のＴｇが
２０℃以上８０℃以下であり、且つ膜厚が１０μｍ以上
１００μｍ以下の範囲において反り角の変動が０．２ｄ
ｅｇ．以下の要求を満足することが確認された。
【００２９】
【実施例８】Ｔｇが約４０℃でヤング率の温度変化の平
均傾き（以下γ値という）が異なる接着剤およびＴｇが
約６０℃でγ値が異なる接着剤を準備し、実施例７と同
様な実験を行った。図７にその結果を示す。図７からγ
値が−１．０ｋｇ／ｍｍ2／℃以上になると反り角の変
化がさらに小さくなることが確認された。
【００３０】
【実施例９】実施例２と同様に図２のような構造の光デ
ィスク２０を作製した。そして表４に示す接着剤につい
て検討したところ、実施例７と同様に接着剤のＴｇが２
０℃以上８０℃以下であり、且つ膜厚が１０μｍ以上１
００μｍ以下に設定することによって反り角の変動を
０．２ｄｅｇ．以下に抑えられ、更に、実施例８と同様
な試験を行なったところγ値を−１．０ｋｇ／ｍｍ2／
℃以上に設定することによって更に反り角の変化が小さ
くなることが確認された。
【００３１】なお、本発明における貼り合わせ光ディス
クの構成については従来のものと特に変わりはなく、基
板としてはポリカーボネート、ポリメチルメタクリレー
ト（ＰＭＭＡ）、エポキシ、アモルファスポリオレフィ
ン等の透明なプラスチックやガラスが用いられる。記録
層の構成は、再生専用型の場合は射出成形等により基板
上に形成された信号ピットの上にＡｌ、Ａｕ、Ｐｔ、Ｃ
ｕ、Ａｇ等の金属反射膜およびその合金膜が成膜され、
追記型の場合はグルーブと呼ばれる案内溝の上にシアニ
ン系あるいはフタロシアニン系の有機色素膜を形成しそ
の上にＡｌ、Ａｕ、Ｃｕ、Ａｇ系金属反射膜およびその
合金系反射膜が形成される。そして記録再生型の場合
は、グルーブの上に第一誘電体層、記録層、第二誘電体
層、必要に応じて反射層、有機樹脂保護層がこの順で積
層されている。誘電体層に用いられる誘電体としてはＡ
ｌＮｘ、ＳｉＯ２、ＳｉＮｘ、ＺｎＳ等が用いられ、記
録層にはＦｅＴｂ、ＦｅＴｂＣｏ、ＦｅＴｂＧｄ、Ｇｄ
Ｃｏ、ＭｎＣｕＢｉ等の光磁気記録材料やＡｓ−Ｔｅ−
Ｇｅ系、Ｓｎ−Ｔｅ−Ｓｅ系等の相変化記録材料が用い
られる。そして有機樹脂保護層としては主にエポキシア
クリレート、ウレタンアクリレート、ポリエステルアク
リレート等の紫外線硬化型樹脂が用いられる。成膜方法
についてもスパッタリング、真空蒸着、イオンプレーテ
ィング、プラズマ蒸着、無電解メッキあるいはスピンコ
ート等、任意の薄膜形成手段を用いることができる。以
上の様にして作製した記録層付き基板同士あるいは記録
層付き基板と記録層の付いていない基板とを接着剤によ
って貼り合わせることによって作製される。接着剤の種
類に特に限定はなく、ホットメルト型や紫外線硬化型な
どの一般的な接着剤を用いることができる。ホットメル
ト型ではポリアミド系、ポリエステル系、ポリウレタン
系、ポリオレフィン系や湿気硬化などの反応性を付与し
たタイプを用いることができるがこれに限定されるもの
ではない。また紫外線硬化型では分子中に少なくとも１
つのエチレン性不飽和結合を有する付加重合可能な化合
物、例えばポリエステル（メタ）アクリレート、ポリエ
ーテル（メタ）アクリレート、ポリウレタン（メタ）ア
クリレート、エポキシ（メタ）アクリレートなどの架橋
性オリゴマーや、３官能以上あるいは単官能や２官能の
（メタ）アクリル酸エステル、具体的には３官能以上で
はトリメチロールプロパントリ（メタ）アクリレート、
ジペンタエリスリトールヘキサアクリレート、２官能で
はカプロラクトン変性ヒドロキシピバリン酸ネオペンチ
ルグリコールジアクリレート、ジシクロペンタニルジア
クリレート、単官能では２−ヒドロキシ−３−フェノキ
シプロピルアクリレートなどを単独で、あるいは適当な
割合でブレンドして用いることができる。もちろんこれ
もこれに限られるものではなく、上記物性値を満たす材
料であれば良い。また貼り合わせ方法についても特に限
定は無く、ホットメルト型の場合はロールコート法、紫
外線硬化型の場合はスピンコート法、スクリーン印刷
法、ロールコート法などの公知の製法を用いることがで
きる。
【００３２】また、実施例においては、３種類の使用温
度範囲を想定した結果（２０℃〜５５℃、２０℃〜７０
℃、２０〜８０℃）を示したが、当然のことながらこの
使用温度範囲はこれに限定されるものではなく、例えば
気温が氷点下の地域での使用や、温度が８０℃以上にも
なる真夏の車の中などあらゆる使用環境に対して品質を
保証するために、接着剤のヤング率と膜厚はその使用温
度範囲に応じて設定されるべきものであることは言うま
でもない。更に接着剤の種類についてもホットメルト型
や紫外線硬化型に限定されるものではなく、例えば２液
性のエポキシ系接着剤や嫌気性接着剤、プライマー硬化
型接着剤、シアノアクリレート系接着剤など上記範囲を
満たすものであればよいということは、本発明の趣旨か
ら明らかである。更にまた、実施例では記録層が片面に
存在する場合についてのみ説明したが、これに限ること
はなく、情報記録層を有する２枚の透明基板を情報記録
層が互いに内側になるように接着剤層を介して貼り合わ
せてなる光ディスクにも適用して良いことは勿論であ
る。
【００３３】
【発明の効果】以上説明したように本発明の光記録ディ
スクによれば、接着剤の使用温度におけるヤング率と膜
厚を掛け合わせた数値を１．０×１０-2ｋｇ／ｍｍ以上
３．０ｋｇ／ｍｍ以下の範囲に設定すること、ヤング率
と熱膨張係数とを掛け合わせた数値を１．５×１０-2ｋ
ｇ・ｍｍ・℃-1以下の範囲に設定すること、熱膨張係数
と膜厚を掛け合わせた数値を２．０×１０-5ｍｍ／℃以
下設定すること、接着剤のガラス転移点を２０℃〜８０
℃の範囲に設定し且つ膜厚を１０μｍ以上１００μｍ以
下の範囲に設定することによって反りの発生を最小限に
抑えることが可能となり、物理的精度の高い高品質な光
記録ディスクを提供することができる。更に、接着剤の
ガラス転移点を２０℃〜８０℃の範囲に設定し且つ膜厚
を１０μｍ以上１００μｍ以下の範囲に設定したとき、
接着剤のヤング率の温度変化の平均傾きを−１．０ｋｇ
／ｍｍ2／℃以上にすることによって反りの発生を更に
抑えることができる。
【図面の簡単な説明】
【図１】本発明の光記録ディスクの一実施例を示す断面
図である。
【図２】本発明の光記録ディスクの一実施例を示す断面
図である。
【図３】貼り合わせ型光ディスクの接着剤のヤング率×
膜厚と反り角の変化量の関係を示す図である。
【図４】貼り合わせ型光ディスクの接着剤のヤング率×
熱膨張係数と反り角の変化量の関係を示す図である。
【図５】貼り合わせ型光ディスクの接着剤の熱膨張係数
×膜厚と反り角の変化量の関係を示す図である。
【図６】貼り合わせ型光ディスクの接着剤層の膜厚と反
り角の関係を示す図である。
【図７】貼り合わせ型光ディスクのγ値と反り角の関係
を示す図である。
【図８】従来の貼り合わせ型光ディスクの反り角の変化
量を示す図である。
【図９】従来の貼り合わせ型光ディスクの概略を示す断
面斜視図である。
【図１０】従来の貼り合わせ型光ディスクの概略を示す
断面図である。
【符号の説明】
１０ 再生専用型貼り合わせ光ディスク ２０ 記録再生型貼り合わせ光ディスク ３０ 貼り合わせ光ディスク １ａ，１ｂ，４ａ，４ｂ，９ 透光性ディスク基板 ２ 反射層 ３，１２ 接着層 ５ 第一誘電体層 ６，１０ 記録層 ７ 第二誘電体層 ８，１１ 保護膜

Claims (5)

    【特許請求の範囲】
  1. 【請求項１】上面に金属膜あるいは有機色素からなる情
    報記録層を有する透明基板と、情報記録層のない透明基
    板、又は、上面に金属膜あるいは有機色素からなる情報
    記録層を有する透明基板同士を情報記録層が内側になる
    ように接着剤層を介して貼り合わせてなる光ディスクに
    おいて、前記基板の貼り合わせに用いる接着剤のヤング
    率と前記接着剤層の膜厚を掛け合わせた数値が、１．０
    ×１０-2ｋｇ／ｍｍ以上３．０ｋｇ／ｍｍ以下であるこ
    とを特徴とする光ディスク。
  2. 【請求項２】上面に金属膜あるいは有機色素からなる情
    報記録層を有する透明基板と、情報記録層のない透明基
    板、又は、上面に金属膜あるいは有機色素からなる情報
    記録層を有する透明基板同士を情報記録層が内側になる
    ように接着剤層を介して貼り合わせてなる光ディスクに
    おいて、前記基板の貼り合わせに用いる接着剤の熱膨張
    係数とヤング率を掛け合わせた数値が、１．５×１０-2
    ｋｇ・ｍｍ-2・℃-1以下であることを特徴とする光ディ
    スク。
  3. 【請求項３】上面に金属膜あるいは有機色素からなる情
    報記録層を有する透明基板と、情報記録層のない透明基
    板、又は、上面に金属膜あるいは有機色素からなる情報
    記録層を有する透明基板同士を情報記録層が内側になる
    ように接着剤層を介して貼り合わせてなる光ディスクに
    おいて、前記基板の貼り合わせに用いる接着剤の熱膨張
    係数と前記接着剤層の膜厚を掛け合わせた数値が、２．
    ０×１０-5ｍｍ／℃以下であることを特徴とする光ディ
    スク。
  4. 【請求項４】上面に金属膜あるいは有機色素からなる情
    報記録層を有する透明基板と、情報記録層のない透明基
    板、又は、上面に金属膜あるいは有機色素からなる情報
    記録層を有する透明基板同士を情報記録層が内側になる
    ように接着剤層を介して貼り合わせてなる光ディスクに
    おいて、前記基板の貼り合わせに用いる接着剤のガラス
    転移点が２０℃以上８０℃以下であり、且つ、前記接着
    剤層の膜厚が１０μｍ以上１００μｍ以下であることを
    特徴とする光ディスク。
  5. 【請求項５】前記接着剤のヤング率の温度変化の平均傾
    きが−１．０ｋｇ／ｍｍ2/℃以上であることを特徴とす
    る請求項４記載の光ディスク。
JP8160803A 1996-05-31 1996-05-31 光ディスク Pending JPH09320116A (ja)