JPS5915465A - カ−ペツト裏打ち用接着剤組成物 - Google Patents
カ−ペツト裏打ち用接着剤組成物Info
- Publication number
- JPS5915465A JPS5915465A JP12652382A JP12652382A JPS5915465A JP S5915465 A JPS5915465 A JP S5915465A JP 12652382 A JP12652382 A JP 12652382A JP 12652382 A JP12652382 A JP 12652382A JP S5915465 A JPS5915465 A JP S5915465A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- compd
- adhesive composition
- carpet backing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は接着強度および粘度安定性に優れたカーペット
バッキング用接着剤組成物に関するものである。
バッキング用接着剤組成物に関するものである。
現在の代表的なカーペットであるタフテッドカーヘット
は、麻の織布又はポリプロピレン等合成繊維の織布、不
織布等の一次基布にナイロン、アクリル、羊毛等のパイ
ルを植込んだものであるが、パイルの脱落防止の為にそ
の裏面に接着剤を塗布し、ジーート等の二次基布を貼り
合わせ熱風乾燥することにより製造されている。
は、麻の織布又はポリプロピレン等合成繊維の織布、不
織布等の一次基布にナイロン、アクリル、羊毛等のパイ
ルを植込んだものであるが、パイルの脱落防止の為にそ
の裏面に接着剤を塗布し、ジーート等の二次基布を貼り
合わせ熱風乾燥することにより製造されている。
接着剤として共重合体ラテックス等に炭酸カルシウム等
の充填剤およびポリアクリル酸等の増粘剤を加え、作業
に適した粘度に調整された水性の接着剤組成物が広く使
用されている。
の充填剤およびポリアクリル酸等の増粘剤を加え、作業
に適した粘度に調整された水性の接着剤組成物が広く使
用されている。
従来これら接着剤組成物の接着強度向上を目的として種
々改良検討が加えられてきた。しかしながらこれらの接
着剤組成物は充分満足のいく接着強度を有しておらず使
用条件が限定されていた。
々改良検討が加えられてきた。しかしながらこれらの接
着剤組成物は充分満足のいく接着強度を有しておらず使
用条件が限定されていた。
本発明者らは接着剤組成物の接着強度を向上させること
を目的として鋭意研死した結果、従来の接着剤組成物よ
りもはるかに優れた接着強度を有する組成物を見出し本
発明を完成した。
を目的として鋭意研死した結果、従来の接着剤組成物よ
りもはるかに優れた接着強度を有する組成物を見出し本
発明を完成した。
すなわち、本発明は共重合体ラテックス１００重量部（
固形分）、エポキシ化合物ｏ、ｏｉ−ｔ。
固形分）、エポキシ化合物ｏ、ｏｉ−ｔ。
重量部および倉シリジン環を有する化合物０．０１〜１
０重量部を含有することを特徴とするカーペット裏打ち
用接着剤組成物である。
０重量部を含有することを特徴とするカーペット裏打ち
用接着剤組成物である。
本発明において用いられる共重合体ラテックスとしては
スチレン−ブタジェンゴムラテックス、メチルメタクリ
レート−ブタジェンゴムラテックス、アクリロニトリル
−シタジエンゴムラテックス、塩化ビニル重合体ラテッ
クス、塩化ビニル−アクリレート共重合体ラテックスな
どカーペット裏打ち処理に使用可能な一般の共重合体ラ
テックスをあげることができる、なお、これらの共重合
体ラテックスはカルボキシル基、アマイド基、グリシジ
ル基又はスルホン酸基などを含んでいてもよい。特にカ
ルボキシル基で変性された共重合体ラテックスが好まし
い。
スチレン−ブタジェンゴムラテックス、メチルメタクリ
レート−ブタジェンゴムラテックス、アクリロニトリル
−シタジエンゴムラテックス、塩化ビニル重合体ラテッ
クス、塩化ビニル−アクリレート共重合体ラテックスな
どカーペット裏打ち処理に使用可能な一般の共重合体ラ
テックスをあげることができる、なお、これらの共重合
体ラテックスはカルボキシル基、アマイド基、グリシジ
ル基又はスルホン酸基などを含んでいてもよい。特にカ
ルボキシル基で変性された共重合体ラテックスが好まし
い。
本発明において用いられるエポキシ化合物はその分子中
に２個以上のエポキシ基を有するものであって、好適な
ものとしては、グリセリン、プロピレングリコール、エ
チレングリコール、ヘキサントリオール、ソルビトール
、トリメチｏ −／ｌ／ ７’ロパン、３−メチルペン
タントリオール、ポリエチレングリコール、ポリプロピ
レングリコール等の脂肪族多価アルコール類とエピクロ
ルヒドリンの如きノ為ロヒドリンとの反応生成物、レゾ
ルシン、カテコール、ノ・イドロキノン１．３．５）リ
ヒドロキシベンゼン、ビス（４−ヒドロキンフェニル）
メタン、ビス（４−ヒドロキシフェニル）ジメチルメタ
ン、４゜４′−ビヒドロキシフェニル等の芳香族多価ア
ルコールとエピクロルヒドリンの如キハロヒドリンとの
反応生成物、ジグリシジルエーテル、−カルボキシレー
ト等の過酢１等で不飽和結合部を酸化して得られるエポ
キシ化合物があげられる。
に２個以上のエポキシ基を有するものであって、好適な
ものとしては、グリセリン、プロピレングリコール、エ
チレングリコール、ヘキサントリオール、ソルビトール
、トリメチｏ −／ｌ／ ７’ロパン、３−メチルペン
タントリオール、ポリエチレングリコール、ポリプロピ
レングリコール等の脂肪族多価アルコール類とエピクロ
ルヒドリンの如きノ為ロヒドリンとの反応生成物、レゾ
ルシン、カテコール、ノ・イドロキノン１．３．５）リ
ヒドロキシベンゼン、ビス（４−ヒドロキンフェニル）
メタン、ビス（４−ヒドロキシフェニル）ジメチルメタ
ン、４゜４′−ビヒドロキシフェニル等の芳香族多価ア
ルコールとエピクロルヒドリンの如キハロヒドリンとの
反応生成物、ジグリシジルエーテル、−カルボキシレー
ト等の過酢１等で不飽和結合部を酸化して得られるエポ
キシ化合物があげられる。
これらは、共重合体ラテックス１００重量部（固形分）
当９０．０１−１０重量部で用いられる。０．０１１重
部未満では接着強度の向上は認められず１０重量部を超
えると接着強度のより以上の向上は認められない。
当９０．０１−１０重量部で用いられる。０．０１１重
部未満では接着強度の向上は認められず１０重量部を超
えると接着強度のより以上の向上は認められない。
好ましくＶｉｏ、０５〜５重量部で用いられる０アジリ
ジン環を有する化合物としては、フェニルイソシアネー
ト、ジクロルフェニルイソシアネート等のモノイソシア
ネート類、トリレンジイソシアネート、ジフェニルメタ
ン−４，４１−ジインシアネート等のジイソシアネート
類、トリフェニルメタントリイソシアネート、ジフェニ
ルメタントリイノシアネート等のトリイソシアネート類
、一般式 で表わさｒＬ、ｎ＝ｏ、１．２．３．４などの混合体で
あるポリメチレンポリフェニルイソシアネート等の多官
能イソシアネート類、等とエチレンイミンとを公知の方
法で反応させて得られた化合物があげられる。。
ジン環を有する化合物としては、フェニルイソシアネー
ト、ジクロルフェニルイソシアネート等のモノイソシア
ネート類、トリレンジイソシアネート、ジフェニルメタ
ン−４，４１−ジインシアネート等のジイソシアネート
類、トリフェニルメタントリイソシアネート、ジフェニ
ルメタントリイノシアネート等のトリイソシアネート類
、一般式 で表わさｒＬ、ｎ＝ｏ、１．２．３．４などの混合体で
あるポリメチレンポリフェニルイソシアネート等の多官
能イソシアネート類、等とエチレンイミンとを公知の方
法で反応させて得られた化合物があげられる。。
これらは共重合体ラテックス１００重量部（固形分）当
り０．０１〜１０重量部で用いられる。
り０．０１〜１０重量部で用いられる。
０．０１重量部未満では接着強度の向上は認められず、
ｉｏ重量部を超えてももはやそれ以上の接着強度の向上
は認められない。好ましくは０．０５〜５重量部で用い
られる。
ｉｏ重量部を超えてももはやそれ以上の接着強度の向上
は認められない。好ましくは０．０５〜５重量部で用い
られる。
本発明の接着剤組成物は必要に応じて分散剤、安定剤、
架橋剤、充填剤、着色剤、増粘剤等を加えることができ
る。
架橋剤、充填剤、着色剤、増粘剤等を加えることができ
る。
次に実施例をあげて本発明を具体的に説明するが、本発
明は実施例により限定されるものではない。
明は実施例により限定されるものではない。
以下余白
実施例
ブタジェン４５重量部、スチレン５２重量部、アクリル
酸２重量部、イタコン酸１重量部を重合して共重合体ラ
テックスを得た。
酸２重量部、イタコン酸１重量部を重合して共重合体ラ
テックスを得た。
これらの接着剤組成物を用いて、基布がポリプロピレン
、パイルがナイロンのタフテッドカーペットに１．２に
９／イｄの割合で均一に塗布し、次いで □ジュート（
二次基布）を圧着して貼りあわせ、１２０℃において２
０分間乾燥し、ＪＩＳ−Ｌ−１０２１に従って接着強度
を測定した。
、パイルがナイロンのタフテッドカーペットに１．２に
９／イｄの割合で均一に塗布し、次いで □ジュート（
二次基布）を圧着して貼りあわせ、１２０℃において２
０分間乾燥し、ＪＩＳ−Ｌ−１０２１に従って接着強度
を測定した。
結果を第１表に示す。
以下余白
第１表
特許出願人
住友ノーガタック株式会社
Claims (1)
- 【特許請求の範囲】 １、 共重合体ラテックス１００重量部（固形分〕エポ
キシ化合物０．０１〜１０重量部およびアジリジン環を
有する化合物０．０１〜１０重量部を含有することを特
徴とするカーペット裏打ち用接着剤組成物。 ２、 エポキシ化合物が０．０５〜５重量部である特許
請求の範囲第１項記載のカーペット裏打ち用接着剤組成
物。 ３、 アジリジン環を有する化合物が０．０５〜５重量
部である特許請求の範囲第１項または第２項記載のカー
ペット裏打ち用接着剤組成物。