JPS6032147A - 信号紀録ディスク - Google Patents

信号紀録ディスク

Info

Publication number
JPS6032147A
JPS6032147A JP58140337A JP14033783A JPS6032147A JP S6032147 A JPS6032147 A JP S6032147A JP 58140337 A JP58140337 A JP 58140337A JP 14033783 A JP14033783 A JP 14033783A JP S6032147 A JPS6032147 A JP S6032147A
Authority
JP
Japan
Prior art keywords
signal recording
protective coating
layer
track grooves
coating layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP58140337A
Other languages
English (en)
Inventor
Koichi Konishi
小西　弘一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Holdings Corp
Original Assignee
Matsushita Electric Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Industrial Co Ltd filed Critical Matsushita Electric Industrial Co Ltd
Priority to JP58140337A priority Critical patent/JPS6032147A/ja
Publication of JPS6032147A publication Critical patent/JPS6032147A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 産業上の利用分野 本発明はビデオディスク、またはオーディオディスクの
ような映像、音響、もしくは他の情報信号が面上に凸凹
の形で記録されている信号記録ディスクや、トラック溝
を有する信号記録ディスクに関するものである。信号記
録ディスクには、両面再生用のツーピースのものと、片
面再生用のツーピースのものと、片面再生用ワンピース
のものとがあるが、本発明は、特に片面再生用ワンピー
スの信号記録ディスクに関するものである。
従来例の構成とその問題点 通常、信号記録ディスクは面上に凸凹状の信号を記録し
た金型、もしくはトラック溝を形成した金型から型取り
を行ない、その形成面上に反射層を形成し、高分子コー
ド剤で保護コート層を形成している。
以下図面を参照しながら従来の信号記録ディスクについ
て説明する。第１図は従来の信号記録ディスクの断面拡
大図である。
凸凹状の信号を記録した金型、もしくはトラック溝を形
成した金型からインジェクション成型法にて、ポリカー
ボネート樹脂を媒体とし、複製媒体１を形成し、その信
号記録面、トラック溝形成面上に真空蒸着法、スパッタ
リング法にてアルミニウムの反射層２を形成し、その面
上にスピナーを用いてアクリル系、紫外線硬化型樹脂を
塗布し、厚み２０〜３０μｍの保護コート層３を形成し
ている。
しかしながら、上記のような構成には次のような問題点
がある。
１ず第一に、保護コート層の厚みが数十ミクロン以下と
薄いので、擦る力には強いが引っかく力や鋭利な物との
衝突に弱く、信号記録面、トラック溝形成面にも損傷を
与える。第二に、保護コート層が硬化する時、収縮を生
ずるので信号記録ディスクがそってしまう。第三に、保
護コート層を厚くすることが難かしい。（厚くすると硬
化時の収縮が大きくなり、捷た塗布操作が難しい）。第
四に、異物が混入した場合、突起物ができ、外観が悪く
なる。第五に、異物が混入した場合、保護コート層を通
して見えるので外観が悪くなる。
最近、信号記録ディスクの保護コート層を兼ねてラベル
を貼り付ける方法のものもでているが、このものにも次
のような問題点がある。
まず第一に、引っかく力や鋭利な物との衝突に対して弱
く、信号記録面、トラック溝形成面にも損傷を与える。
第二に、貼り付ける操作が難しい。
第三に、異物が混入した場合、突起物ができ外観が悪く
なる。第四に、反射層の上に直接貼り付けることかでき
ない。
発明の目的 本発明は、面上に凸凹状の信号、もしくはトラック溝を
形成した複製媒体のその凸凹状の信号もしくはトラック
溝の形成面上に反射層を形成し、その反射層の面上に無
機物粉末と高分子接着剤とからなる保護コート層を形成
することにより、上記諸問題点を解決した信号記録ディ
スク番提供するものである。
発明の構成 本考案の信号記録ディスクは、面上に凸凹状の信号、も
しくはトラック溝を形成した複製媒体のその凸凹状の信
号もしくはトラック溝の形成面上に反射層とその面上に
無機物粉末と高分子接着剤とから形成された保護コート
層から構成したものであり、これにより、機械的強度の
強い保護コート層を有する信号記録ディスクとなるもの
である。
実施例の説明 以下本発明の一実施例について、図面を参照しながら説
明する。
第２図は、本発明の一実施例における信号記録ディスク
の断面拡大図である。
金型より成型した凸凹状の信号、もしくはトラック溝を
形成した複製媒体１としてポリカーボネートを用い、イ
ンジェクション成型法にて成型を行ない、真空蒸着によ
り反射層２として銀層を形成した後、その面上に粒径１
μｍ以下の酸化アルミニウム粉末とエポキシ系接着剤と
を１：２の割合で混合した保護コート剤をシルク印刷し
、６０°Ｃで硬化し、厚み１００μｍの保護コート層４
を形成して信号記録ディスクを作製した。
次に、本発明の他の実施例について、図面を参照しなが
ら説明する。
第３図は、本発明の他の実施例における信号記録ディス
クの断面拡大図である。
金型より成型した凸凹状の信号、もしくはトラック溝を
形成した複製媒体１としてアクリル系紫外線硬化型樹脂
を用い、それを支持する基板６として透明アクリル基板
を用い、紫外線硬化型樹脂法にて成型を行ない、反射層
２としてスパッタリングでアルミニウム層を形成した後
、その面上に粒径１μｍ以下の酸化ケイ素粉末とアクリ
ル系接着剤とを１：２の割合で混合した保護コート剤を
ロール塗布し、常温硬化し、厚み１６０μｍの保護コー
ト層４を形成して信号記録ディスクを作製した。
発明の効果 本発明は、面上に凸凹状の信号、もしくはトラック溝を
形成した複製媒体のその凸凹状の信号もしくはトラック
溝の形成面上に反射層を形成し、さらにこの反射層の面
上に無機物粉末と高分子接着剤とからなる保護コート層
を形成しているので、保護コート面が従来に比べ非常に
強くなり、引っかく力や鋭利な物との衝突にも強くなり
、信号記録面やトラック溝形成面に損傷を与えることが
ない。また、高分子接着剤と無機物粉末との混合比の調
整によシ保護コート剤の硬化時の収縮率を小さくできる
ので、信号記録ディスクのそりをより防ぐことができる
。さらに、保護コート層を厚くすることが容易にでき、
塗布中に異物が混入しても余り突起物ができない。また
、高分子接着剤と混合する無機物粉末の選択により、い
ろいろな色を着色でき、塗布中に異物が混入しても保温
コート層の表面からは余り見えないなどの優れた効果が
ある。この他にも、反射層の上に直接塗布ができるため
塗布操作が容易である、安定に保護コート層が形成でき
る等の利点もあり、上記各利点によりコストが安くなる
などの効果もある。
【図面の簡単な説明】
第１図は従来の信号記録ディスクの断面拡大図、第２図
は本発明の一実施例の信号記録ディスクの断面拡大図、
第３図は本発明の他の実施例の信号記録ディスクの断面
拡大図である。 ６・・・・・・基板。 代理人の氏名　弁理士　中　尾　敏　男　ほか１名第２
図 第３図

Claims (1)

    【特許請求の範囲】
  1. 面上に凸凹状の信号、もしくはトラック溝を形成した複
    製媒体のその凸凹状の信号もしくは、トラック溝の形成
    面上に反射層を形成し、その反射層の面上に無機物粉末
    と高分子接着剤とからなる保護コート層を形成したこと
    を特徴とする信号記録ディスク。
JP58140337A 1983-07-29 1983-07-29 信号紀録ディスク Pending JPS6032147A (ja)