JPS6057882B2 - 分離用支持体 - Google Patents
分離用支持体Info
- Publication number
- JPS6057882B2 JPS6057882B2 JP7608877A JP7608877A JPS6057882B2 JP S6057882 B2 JPS6057882 B2 JP S6057882B2 JP 7608877 A JP7608877 A JP 7608877A JP 7608877 A JP7608877 A JP 7608877A JP S6057882 B2 JPS6057882 B2 JP S6057882B2
- Authority
- JP
- Japan
- Prior art keywords
- separation
- support
- porous
- porous support
- bacteria
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は新しい分離用支持体に関するものであり、更に
詳しく言えば高分子多孔質材料の細孔内壁に小糖類また
は多糖類をコーティングして分離能力を飛躍的に向上さ
せた分離用支持体に関するものてある。
詳しく言えば高分子多孔質材料の細孔内壁に小糖類また
は多糖類をコーティングして分離能力を飛躍的に向上さ
せた分離用支持体に関するものてある。
従来バクテリヤや異物の分離、分析などに使用される高
分子多孔質材料よりなる支持体は酢酸センイ素樹脂、ナ
イロン樹脂、ビニル樹脂などの多孔状のものが使用され
ているが、孔径に対し大きな寸法の菌や異物の脱漏があ
り、孔径の小さな支持体材料を使用すると分離速度が著
しく遅くなり処理時間が余分にかかり非能率であるばか
りでなく、僅かでも菌のもれがあると後で菌が繁殖し、
分隣した効果が皆無となり労力や材料、時間などの無駄
な消費が大きくなり多大の損失をしばしば招来していた
。
分子多孔質材料よりなる支持体は酢酸センイ素樹脂、ナ
イロン樹脂、ビニル樹脂などの多孔状のものが使用され
ているが、孔径に対し大きな寸法の菌や異物の脱漏があ
り、孔径の小さな支持体材料を使用すると分離速度が著
しく遅くなり処理時間が余分にかかり非能率であるばか
りでなく、僅かでも菌のもれがあると後で菌が繁殖し、
分隣した効果が皆無となり労力や材料、時間などの無駄
な消費が大きくなり多大の損失をしばしば招来していた
。
本発明者等は細菌などの分離を確実に行わせるための工
夫を行つた結果、多孔質材料の内壁に炭水化物をコーテ
ィングすることにより被ろ週休の分離を容易かつ確実に
行うことが出来て分離、分析操作に適する高分子多孔質
支持体の得られることを見出した。
夫を行つた結果、多孔質材料の内壁に炭水化物をコーテ
ィングすることにより被ろ週休の分離を容易かつ確実に
行うことが出来て分離、分析操作に適する高分子多孔質
支持体の得られることを見出した。
本発明の高分子多孔質支持体によれば分離能力を非常に
向上させることが出来る。
向上させることが出来る。
すなわち、従来の多孔質材料の細孔表面は何もコーティ
ングされていないので材料そのものがむき出しになつて
いるが、これに対し本発明の多孔質支持体においては細
孔の内側が高分子ゲル物質、例えば炭水化物でコーティ
ングされている結果ろ過原液中の微粒子や細菌や異物な
どが著しく除去し易くなり、除去率が著しく向上するこ
とがわかつた。小糖類または多糖類のコーティング処理
により多孔質の平均孔径はコーティング層の厚さの分だ
け小さくなるので除去率の比較は処理品と、コーティン
グ処理後の平均孔径に等しい平均粒径を持つ未処理品と
について行つた。
ングされていないので材料そのものがむき出しになつて
いるが、これに対し本発明の多孔質支持体においては細
孔の内側が高分子ゲル物質、例えば炭水化物でコーティ
ングされている結果ろ過原液中の微粒子や細菌や異物な
どが著しく除去し易くなり、除去率が著しく向上するこ
とがわかつた。小糖類または多糖類のコーティング処理
により多孔質の平均孔径はコーティング層の厚さの分だ
け小さくなるので除去率の比較は処理品と、コーティン
グ処理後の平均孔径に等しい平均粒径を持つ未処理品と
について行つた。
本発明に於て高分子多孔質材料としては酢酸セＩソー素
樹脂、ポリアミド樹脂、塩化ビニル樹脂、スチレン樹脂
などに使用することが出来る。
樹脂、ポリアミド樹脂、塩化ビニル樹脂、スチレン樹脂
などに使用することが出来る。
本発明で用いられる単糖類、二糖類、三糖類などの小糖
類及び多糖類としては次のようなものがあげられる。単
糖類としてはジオース（Ｃ２Ｈ４Ｏ２）のアルドースで
あるグリコールアルデヒド、グリセルアルデヒド（アル
ドース）、ジヒドロキシアセトン（ケトース）などのト
リオース（Ｃ３Ｈ６Ｏ３）、エリスロース（アルドース
）、エリスリユロース（ケトース）などのテトロース（
Ｃ４Ｈ８Ｏ，）、リボース、キシロース、アラビノース
、アラビヌロース、キシリユロースなどがある。
類及び多糖類としては次のようなものがあげられる。単
糖類としてはジオース（Ｃ２Ｈ４Ｏ２）のアルドースで
あるグリコールアルデヒド、グリセルアルデヒド（アル
ドース）、ジヒドロキシアセトン（ケトース）などのト
リオース（Ｃ３Ｈ６Ｏ３）、エリスロース（アルドース
）、エリスリユロース（ケトース）などのテトロース（
Ｃ４Ｈ８Ｏ，）、リボース、キシロース、アラビノース
、アラビヌロース、キシリユロースなどがある。
二糖類としてはラクトース、マルトース、トレハロース
、メリビオースなどがある。三糖類としてはラフィノー
ス、メリチトース、ゲンチアノースなどがある。多糖類
としてはデキストリン、デンプン、グリコーゲン、イヌ
リン、マンナン、アラパン、キシラン、デキストラン、
ガラクタン、アラビアガム、タマリンドガム、ペクチン
などがある。
、メリビオースなどがある。三糖類としてはラフィノー
ス、メリチトース、ゲンチアノースなどがある。多糖類
としてはデキストリン、デンプン、グリコーゲン、イヌ
リン、マンナン、アラパン、キシラン、デキストラン、
ガラクタン、アラビアガム、タマリンドガム、ペクチン
などがある。
又これ等のうちから２種以上の混合物を混入したものも
用いることが出来る。本発明に於て高分子多孔質支持体
の微細孔は連続気泡体で、空孔率は通常３０％以上から
９５％以下で、好ましくは７０〜９０％の範囲内にあつ
て、厚味が２５μ以上から５ｒｒＬ１ＷＬ以下で、好ま
しくは１００μ〜３ｍＩｍの範囲内にあるシート状のも
のが使用出来る。
用いることが出来る。本発明に於て高分子多孔質支持体
の微細孔は連続気泡体で、空孔率は通常３０％以上から
９５％以下で、好ましくは７０〜９０％の範囲内にあつ
て、厚味が２５μ以上から５ｒｒＬ１ＷＬ以下で、好ま
しくは１００μ〜３ｍＩｍの範囲内にあるシート状のも
のが使用出来る。
高分子多孔質支持体の一般的な製造法としては、高分子
材料に適当な可塑剤その他の添加剤を加え、親溶剤、及
び適当量の非溶剤を加えて溶解し、粘度約１〜１０ポイ
ズの溶液としてこれを薄板上にキャストし、親溶剤を蒸
発乾燥させ、相分離を行わせ、次いで非溶剤を蒸発乾燥
させて得る方法がある。
材料に適当な可塑剤その他の添加剤を加え、親溶剤、及
び適当量の非溶剤を加えて溶解し、粘度約１〜１０ポイ
ズの溶液としてこれを薄板上にキャストし、親溶剤を蒸
発乾燥させ、相分離を行わせ、次いで非溶剤を蒸発乾燥
させて得る方法がある。
微細孔の平均寸法は１０ｍμ〜１００μ程度のものが使
用され、高分子ゲル物質のコーティング厚さは微細孔平
均寸法の０．１％〜５０％未満の範囲に調節が可能であ
る。
用され、高分子ゲル物質のコーティング厚さは微細孔平
均寸法の０．１％〜５０％未満の範囲に調節が可能であ
る。
本発明の支持体は工場や実験室において除菌、分離、分
析、分画などの目的に使用することが出来る。
析、分画などの目的に使用することが出来る。
添付図面において、第１図は実施例１において比較に使
用した平均孔径（ｄ１）が０．５０μのセルロースアセ
テート樹脂よりなる多孔質支持体の拡大断面図である。
用した平均孔径（ｄ１）が０．５０μのセルロースアセ
テート樹脂よりなる多孔質支持体の拡大断面図である。
第３図に示すような平均孔径（Ｄ３）が０．５５μのセ
ルロースアセテート樹脂よりなる多孔質支持体にタマリ
ンドガムをコーティング処理して厚さ（Δｄ）０．０２
５μのコーティング層を細孔内側面に設けると第２図に
示すような平均孔径（Ｄ２）が０．５０μのコーティン
グ処理した多孔質支持体が得られる。以下の実施例によ
つて本発明を更に具体的に説明する。
ルロースアセテート樹脂よりなる多孔質支持体にタマリ
ンドガムをコーティング処理して厚さ（Δｄ）０．０２
５μのコーティング層を細孔内側面に設けると第２図に
示すような平均孔径（Ｄ２）が０．５０μのコーティン
グ処理した多孔質支持体が得られる。以下の実施例によ
つて本発明を更に具体的に説明する。
実施例１セルロースアセテート樹脂よりなる平均孔径（
Ｄ３）が０．５５μの多孔質支持体（第３図）に対しタ
マリンドガムの３０℃の２．５％水溶液に２０分浸漬し
、引き上げ後８０℃で３紛間乾燥し、多孔質支持体細孔
の内壁にタマリンドガムのコーティングを行つた。
Ｄ３）が０．５５μの多孔質支持体（第３図）に対しタ
マリンドガムの３０℃の２．５％水溶液に２０分浸漬し
、引き上げ後８０℃で３紛間乾燥し、多孔質支持体細孔
の内壁にタマリンドガムのコーティングを行つた。
コーティング処理後の平均孔径（Ｄ２）は０．５０μで
あつた（第２図）。未処理の平均孔径（ｄ１）が０．５
０μの支持体（第１図）との分離能力を比較した。これ
らの多孔質支持体にセラチア菌（長径約１μ、短径約０
．５μ）を含有する原水をそれぞれ通してセラチア菌を
分離したところ未処理の多孔質支持体の分離率は８０％
であるのに対して、処理済の多孔質支持体の分離率は１
００％であつて、本発明によるタマリンドガムのコーテ
ィングによる顕著な分離能力向上の効果が見られた。実
施例２ポリアミド樹脂よりなる多孔質支持体（平均孔径
：０．９０μ）に対しデキストランの２５℃の０．１％
水溶液に３紛浸漬し、引き上げ後６０Ｃで５時間乾燥し
多孔質の内壁にデキストランのコーティングを行い、平
均孔径０．８０μの多孔質支持体を得た。
あつた（第２図）。未処理の平均孔径（ｄ１）が０．５
０μの支持体（第１図）との分離能力を比較した。これ
らの多孔質支持体にセラチア菌（長径約１μ、短径約０
．５μ）を含有する原水をそれぞれ通してセラチア菌を
分離したところ未処理の多孔質支持体の分離率は８０％
であるのに対して、処理済の多孔質支持体の分離率は１
００％であつて、本発明によるタマリンドガムのコーテ
ィングによる顕著な分離能力向上の効果が見られた。実
施例２ポリアミド樹脂よりなる多孔質支持体（平均孔径
：０．９０μ）に対しデキストランの２５℃の０．１％
水溶液に３紛浸漬し、引き上げ後６０Ｃで５時間乾燥し
多孔質の内壁にデキストランのコーティングを行い、平
均孔径０．８０μの多孔質支持体を得た。
この支持体に対し径０．８０μの酵母菌を含有する水を
通して菌を分離したところ未処理支持体では菌の除去率
が６０％であるのに対し、処理済支持体では９０％の除
去率に著しく向上した。
通して菌を分離したところ未処理支持体では菌の除去率
が６０％であるのに対し、処理済支持体では９０％の除
去率に著しく向上した。
第１図および第３図は未処理の多孔質支持体の拡大断面
図であり、第２図は処理済の多孔質支持体の拡大断面図
である。
図であり、第２図は処理済の多孔質支持体の拡大断面図
である。
Claims (1)
- １ 高分子多孔質材料の連続微細孔の内壁に小糖類また
は多糖類をコーティングしたことを特徴とする分離用支
持体。