JPS6086145A - 含ハロゲン系難燃剤含有スチレン系樹脂組成物の熱安定化法 - Google Patents
含ハロゲン系難燃剤含有スチレン系樹脂組成物の熱安定化法Info
- Publication number
- JPS6086145A JPS6086145A JP19578183A JP19578183A JPS6086145A JP S6086145 A JPS6086145 A JP S6086145A JP 19578183 A JP19578183 A JP 19578183A JP 19578183 A JP19578183 A JP 19578183A JP S6086145 A JPS6086145 A JP S6086145A
- Authority
- JP
- Japan
- Prior art keywords
- halogen
- styrene resin
- retardant
- resin composition
- containing flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は難燃剤として含ハロゲン化合物を含有するスチ
レン系樹脂組成物の熱安定化に関するものである。
レン系樹脂組成物の熱安定化に関するものである。
スチレン系樹脂は、電気絶縁性、寸法安定性、加工性等
に優れた特性を有しており電気機器部品をはじめ各種用
途に使用されている。しかし可燃性であることが用途拡
大の障害となっており、この障害を克服するために該樹
脂の難燃化が行なわれている。
に優れた特性を有しており電気機器部品をはじめ各種用
途に使用されている。しかし可燃性であることが用途拡
大の障害となっており、この障害を克服するために該樹
脂の難燃化が行なわれている。
この難燃化をす°るためには、一般に含ノ・ロゲン化合
物、リン化合物、三酸化アンチモン等のいわゆる難燃剤
または難燃助剤を添加する方法が従来より行なわれてお
りこれら難燃剤のなかでも含ハロゲン化合物、特に臭素
化合物が有効である。
物、リン化合物、三酸化アンチモン等のいわゆる難燃剤
または難燃助剤を添加する方法が従来より行なわれてお
りこれら難燃剤のなかでも含ハロゲン化合物、特に臭素
化合物が有効である。
しかしながら、一般的に、スチレン系樹脂に含ハロゲン
系難燃剤を添加した場合、該樹脂組成物の熱安定性が著
しく低下することが知られており、該熱安定性の低下を
抑制するためには、従来より、有機錫化合物、エポキシ
化合物、リン化合物、抗酸化剤等を添加したり、マレイ
ン酸金属塩を添加する方法（特公昭５６−５４０２３号
）等があるが、該添加剤の熱安定化効果はまだ満足され
るものではなく更に熱安定化効果の優れる安定剤の開発
が待たれていた。
系難燃剤を添加した場合、該樹脂組成物の熱安定性が著
しく低下することが知られており、該熱安定性の低下を
抑制するためには、従来より、有機錫化合物、エポキシ
化合物、リン化合物、抗酸化剤等を添加したり、マレイ
ン酸金属塩を添加する方法（特公昭５６−５４０２３号
）等があるが、該添加剤の熱安定化効果はまだ満足され
るものではなく更に熱安定化効果の優れる安定剤の開発
が待たれていた。
本発明者等はかかる観点から、スチレン系樹脂に、含ノ
・ロゲン系難燃剤を添加した樹脂組成物に対し、熱安定
化効果の優れる安定剤につき鋭意研究を重ねた結果、含
ノ・ロゲン系難燃斉１含有スチレン系樹脂組成物に対し
、一般式〔Ｉ〕（式中Ｍは２価の金属を示す。） で示されるエチレンジアミンテトラ酢酸金属塩を添加す
ることにより該樹脂組成物の熱安定性が格段に向上する
ことを見出し本発明を完成した。
・ロゲン系難燃剤を添加した樹脂組成物に対し、熱安定
化効果の優れる安定剤につき鋭意研究を重ねた結果、含
ノ・ロゲン系難燃斉１含有スチレン系樹脂組成物に対し
、一般式〔Ｉ〕（式中Ｍは２価の金属を示す。） で示されるエチレンジアミンテトラ酢酸金属塩を添加す
ることにより該樹脂組成物の熱安定性が格段に向上する
ことを見出し本発明を完成した。
本発明に使用されるスチレン系樹脂とは、スチレン並び
にα−メチルスチレンの如きα置換スチレン、ビニルト
ルエン、０−クロルスチレンの如き核置換スチレンなど
のビニル芳香族イし金物単量体の重合体、これらビニル
芳香族（ヒ合物単量体を主として、これと共重合可能な
他の単量体、例えばアクリロニトリル、アクリル酸並び
にメタクリル酸、それらのブチルあるいはエチルエステ
ルの如きビニル化合物、ビニルピリジン、ビニルカルバ
ゾーンの如きビニル複素環化合物等との共重合体、その
ほかブタジェン、１−クロルブタジェン、２−クロルブ
タジェン、イソプレンの如き共役ジエン化合物、及びＥ
ｉＰＤＭ。
にα−メチルスチレンの如きα置換スチレン、ビニルト
ルエン、０−クロルスチレンの如き核置換スチレンなど
のビニル芳香族イし金物単量体の重合体、これらビニル
芳香族（ヒ合物単量体を主として、これと共重合可能な
他の単量体、例えばアクリロニトリル、アクリル酸並び
にメタクリル酸、それらのブチルあるいはエチルエステ
ルの如きビニル化合物、ビニルピリジン、ビニルカルバ
ゾーンの如きビニル複素環化合物等との共重合体、その
ほかブタジェン、１−クロルブタジェン、２−クロルブ
タジェン、イソプレンの如き共役ジエン化合物、及びＥ
ｉＰＤＭ。
ブチルゴムなどの如き飽和ゴムにビニル芳香族化合物単
量体単独、またはこれと上記の様なビニル化合物とをグ
ラフトさせたグラフト重合体等を挙げることができる。
量体単独、またはこれと上記の様なビニル化合物とをグ
ラフトさせたグラフト重合体等を挙げることができる。
本発明に使用される含ハロゲン系難燃剤として通常この
分野において使用されるものを限定なく使用することが
できるが例えば、トリス（β−クロルエチル）フォスフ
ェート、トリス（ジクロルプロピル）フォスフェート、
トリス（２，３−ジブロムプロピル）フォスフェート、
トリス（ブロムクロルプロピル〕フォスフェート、塩素
化パラフィン、塩素化ポリエチレン、塩素化ポリフェニ
ル、パークロルペンタシクロデカン、臭素化ポリフェニ
ル、テトラブロムエタン、テトラ７”ロムブタン、ヘキ
サプロムシクロト０デカン、テトラブロムベンゼン、ビ
ニルクロルアセテート、ブロムスチレン、ブロムフェニ
ルアリルエーテル、クロルエンド酸シアリル、へ゛ノド
酸、無水ヘット酸、テトラクロル無水フタル酸、テトラ
ブロム無水フタル酸、クロルプロｔＪ！ンジオール、テ
トラブロムビスフェノールＡ１デカブロムジフエニルエ
ーテル、トリス（２，３−ジブロムプロピル）イン７ア
スレート、テトラブロムビスフェノールＡのカーボネー
トオリゴマー等を挙げることができる。
分野において使用されるものを限定なく使用することが
できるが例えば、トリス（β−クロルエチル）フォスフ
ェート、トリス（ジクロルプロピル）フォスフェート、
トリス（２，３−ジブロムプロピル）フォスフェート、
トリス（ブロムクロルプロピル〕フォスフェート、塩素
化パラフィン、塩素化ポリエチレン、塩素化ポリフェニ
ル、パークロルペンタシクロデカン、臭素化ポリフェニ
ル、テトラブロムエタン、テトラ７”ロムブタン、ヘキ
サプロムシクロト０デカン、テトラブロムベンゼン、ビ
ニルクロルアセテート、ブロムスチレン、ブロムフェニ
ルアリルエーテル、クロルエンド酸シアリル、へ゛ノド
酸、無水ヘット酸、テトラクロル無水フタル酸、テトラ
ブロム無水フタル酸、クロルプロｔＪ！ンジオール、テ
トラブロムビスフェノールＡ１デカブロムジフエニルエ
ーテル、トリス（２，３−ジブロムプロピル）イン７ア
スレート、テトラブロムビスフェノールＡのカーボネー
トオリゴマー等を挙げることができる。
これら含ノ・ロゲン系難燃剤の添カロ量は、特男１］な
制限はなく、要求される難燃化度により適宜変量すれば
よいが、一般にスチレン系樹月旨１００重量部に対して
５〜３５重量部を単独またか１２種以上併用することが
好ましい。また更に三酸化アンチモン等の難燃助剤を併
用するとより難燃効果が優れ、その添加駄は通常スチレ
ン系樹脂１００重量部に対して１〜２０重量部力Ｉ好ま
しいＯ 本発明に使用される一般式［１）で示されるエチレンジ
アミンテトラ酢酸金属塩は、等である。
制限はなく、要求される難燃化度により適宜変量すれば
よいが、一般にスチレン系樹月旨１００重量部に対して
５〜３５重量部を単独またか１２種以上併用することが
好ましい。また更に三酸化アンチモン等の難燃助剤を併
用するとより難燃効果が優れ、その添加駄は通常スチレ
ン系樹脂１００重量部に対して１〜２０重量部力Ｉ好ま
しいＯ 本発明に使用される一般式［１）で示されるエチレンジ
アミンテトラ酢酸金属塩は、等である。
本発明に使用される一般式［１）で示されるエチレンジ
アミンテトラ酢酸金属塩の添加量は１難燃化のために使
用される含ハロゲン系難燃剤の種類によって適宜法めら
れるものであるが含ハロゲン系難燃剤１００重量部に対
して０．５〜５０重量部、通常は１〜２０重量部である
。
アミンテトラ酢酸金属塩の添加量は１難燃化のために使
用される含ハロゲン系難燃剤の種類によって適宜法めら
れるものであるが含ハロゲン系難燃剤１００重量部に対
して０．５〜５０重量部、通常は１〜２０重量部である
。
本発明を実施するに当っては、スチレン系樹脂に、含ハ
ロゲン系難燃剤を添加し、更に、エチレンジアミンテト
ラ酢酸金属塩を添加し、ヘンシェルミキサー、バンバリ
ーミキサ−等の混合機で配合すればよい。また含ハロゲ
ン系難燃剤とエチレンジアミンテトラ酢酸金属塩とをあ
らかじめ混合したものをスチレン系樹脂に添加し配合し
てもよい。
ロゲン系難燃剤を添加し、更に、エチレンジアミンテト
ラ酢酸金属塩を添加し、ヘンシェルミキサー、バンバリ
ーミキサ−等の混合機で配合すればよい。また含ハロゲ
ン系難燃剤とエチレンジアミンテトラ酢酸金属塩とをあ
らかじめ混合したものをスチレン系樹脂に添加し配合し
てもよい。
本発明の安定剤以外に必要に応じて、有機錫化合物、エ
ポキシ化合物、有機亜リン酸エステル、抗酸化剤、各種
金属石ケン、難燃助剤、顔料、充填剤、滑剤、発泡剤等
を添加することができる。
ポキシ化合物、有機亜リン酸エステル、抗酸化剤、各種
金属石ケン、難燃助剤、顔料、充填剤、滑剤、発泡剤等
を添加することができる。
以下実施例によって本発明を具体的に説明するが、本発
明はこれらによって限定されるものではない。これらの
例において部とは重量部を意味する。
明はこれらによって限定されるものではない。これらの
例において部とは重量部を意味する。
実施例１゜
アクリロニトリル−ブタジェン−スチレン樹脂〔日本合
成ゴム（株）製、Ｊ８ＲＡＥ８すｌｏＮＰｌｌｏｏ部、
テトラブロムビスフェノールＡのカーボネートオリゴマ
ー〔奇人化成（株）製ファイヤーガード７５０Ｇ）２０
部に〔表−１〕に示す安定剤１，０部を添加した配合物
を１３０℃に調節した８インチ試験ロールで５分間混練
し、厚さＯ，Ｓ Ｗのシートを作製した。得られたシー
トを裁断後８枚積み重ね、２６５℃で３０分、６０分及
び９０分プレスを行ない、プレス後の゛試験片を取り出
しその着色度を肉眼で判定した。〔表−１〕で判るよう
に本発明に用いたエチレンジアミンテトラ酢酸金属塩が
熱安定化効果に優れていることが判る。
成ゴム（株）製、Ｊ８ＲＡＥ８すｌｏＮＰｌｌｏｏ部、
テトラブロムビスフェノールＡのカーボネートオリゴマ
ー〔奇人化成（株）製ファイヤーガード７５０Ｇ）２０
部に〔表−１〕に示す安定剤１，０部を添加した配合物
を１３０℃に調節した８インチ試験ロールで５分間混練
し、厚さＯ，Ｓ Ｗのシートを作製した。得られたシー
トを裁断後８枚積み重ね、２６５℃で３０分、６０分及
び９０分プレスを行ない、プレス後の゛試験片を取り出
しその着色度を肉眼で判定した。〔表−１〕で判るよう
に本発明に用いたエチレンジアミンテトラ酢酸金属塩が
熱安定化効果に優れていることが判る。
実施例２゜
スチレン樹脂［旭化成（株）製、スタイロン４９２］１
００部、テトラブロムビスフェノールＡ〔奇人化成（株
）製、ファイヤガード２０００３１５部、三酸化アンチ
モン１部に〔表−２〕に示す安定剤１．０部を添加した
配合物を１１５℃に調節した８インチ試験ロールで５分
間混練し、厚さ０．７關のシートを作製した。得られた
シートを裁断後８枚積重ね２６０℃で４０分、８０分及
び１２０分プレスを行ない、プレス後の試験片を取り出
しその着色度を肉眼で判定した。
００部、テトラブロムビスフェノールＡ〔奇人化成（株
）製、ファイヤガード２０００３１５部、三酸化アンチ
モン１部に〔表−２〕に示す安定剤１．０部を添加した
配合物を１１５℃に調節した８インチ試験ロールで５分
間混練し、厚さ０．７關のシートを作製した。得られた
シートを裁断後８枚積重ね２６０℃で４０分、８０分及
び１２０分プレスを行ない、プレス後の試験片を取り出
しその着色度を肉眼で判定した。
〔表−２〕から判るように本発明で用いたエチレンジア
ミンテトラ酢酸金属塩が熱安定化効果に優れていること
が判る。
ミンテトラ酢酸金属塩が熱安定化効果に優れていること
が判る。
〔表−２〕
手続補正書（自発）
１、事件の表示
昭和５８年特許願第１９５７８１号
２、発明の名称
３、補正をする者
代表輯役古用清太部
４、代理人
居所 東京部品用区広町１丁目２番５８号６、補正の対
象 「明細書の発明の詳細な説明の橋」 ７゜補正の内容 別紙の通り （１）明細書第４頁第２行目の「メチン」を「メチル」
と訂正。
象 「明細書の発明の詳細な説明の橋」 ７゜補正の内容 別紙の通り （１）明細書第４頁第２行目の「メチン」を「メチル」
と訂正。
以上
Claims (1)
- 【特許請求の範囲】 １、 含ハロゲン系難燃剤含有スチレン系樹脂組成物に
対し、一般式 （式中Ｍは２価の金属を示す。） で示されるエチレンジアミンテトラ酢酸金属塩を添加す
ることを特徴とする含ハロゲン系難燃剤含有スチレン系
樹脂組成物の熱安定化法。