JPS6096578A - 温度平衡材の製法 - Google Patents

温度平衡材の製法

Info

Publication number
JPS6096578A
JPS6096578A JP59212749A JP21274984A JPS6096578A JP S6096578 A JPS6096578 A JP S6096578A JP 59212749 A JP59212749 A JP 59212749A JP 21274984 A JP21274984 A JP 21274984A JP S6096578 A JPS6096578 A JP S6096578A
Authority
JP
Japan
Prior art keywords
temperature
oxide
balancing material
temperature balancing
material according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP59212749A
Other languages
English (en)
Other versions
JPH0217508B2 (ja
Inventor
フリツツ・アルデインガー
ヴアルトラウト・ヴエルデツカー
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WC Heraus GmbH and Co KG
Original Assignee
WC Heraus GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WC Heraus GmbH and Co KG filed Critical WC Heraus GmbH and Co KG
Publication of JPS6096578A publication Critical patent/JPS6096578A/ja
Publication of JPH0217508B2 publication Critical patent/JPH0217508B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明はセラミック拐料からなる温度平衡材に関する。
温度平衡材（Ｔｅｍｐｅｒ＆ｔｕｒｅａｕｓｇｌｅｉｃ
ｈｋｉ；ｒｐａｒ　）とは所定の体積内にできるだけ一
定の温度を維持するために使用されるか、或は所定の表
面上に均一の温度伝導性全付与するのに使用する材料で
あると理解されたい。このような温度平衡材はできるだ
け少ない温度勾配が要求される場所に一般に使用される
。温度平衡材は例えば融解／単結晶引上げ法操作に際し
て適当な融解るつばのまわりの管の形態すなわち外側の
るつぼの形態で使用されるか、熱分析装置では炉のブロ
ックの形態で使用されるか、熱処理操作や焼結操作や加
圧焼結操作では炉の２イニングまたは挿入材の形態で使
用される。
〔従来の技術〕
低温度領域＜＜１ｏｏｏ℃）では温度平衡材として通常
使用温度に応じて銅、銀ｔたはアルミニウムからなる全
域熱伝導体が使用される。これらの金桟熱伝導体は融解
温度が低く、再結晶温度が低く、低温度で既にクリープ
する傾向、すなわち口取によシすでに変形する傾向があ
るという欠点をもつ。高温度用には酸化ベリリウムから
なる温度平衡材を使用することができる。
しかし、温度平衡材として酸化ベリリウムの使用は、酸
化ベリリウムの毒性のためにその取扱いが極めて容易で
はなく、また酸化ベリリウムは低温度においては極めて
熱伝導度が良好であるが、高温度では熱伝導度が大きく
低下するために、はとんど考慮されない。
ヨーロッパ特許Ｉ＠７５ｇ５ｔ号明ｍ召には窒化アルミ
ニウムの焼結によって得らｆ′Ｌ、た、高密度及び高熱
伝導性をもつ成形体が記載されている。
窒化アルミニウムの焼結助剤として希土類金属酸化物、
例えは酸化イツトリウムまたは酸化ランタン、酸化カル
シウム、酸化バリウム及び酸化ストロンチウムが既知で
ある。
〔発明が解決しようとする問題点〕
本発明の課題は熱の均−且つ迅速な熱の吸収−放出のた
めに高温度においても使用できるセラミック材からなる
温度平衡材を見出すにある。
〔問題を解決するための手段〕
上述の課題は本発明により少くとも／　００　Ｗ／ｍＫ
の熱伝導度をもつ緻密に焼結された蟹化アルミニウムに
より解決される。
〔作　用〕
本発明による緻密に焼結した依化アルミニクムからなる
温度平衡材は約ｉ’ｔｏθ℃までの温度で使用される。
上記窒化アルミニウムは高強度と温度変化に対する良好
な安定性をもち、且つ毒性がないために加工の際に＊扱
いが簡単であるという点ですぐれている。本発明による
緻密に焼結した輩化アルミニウム材は高温度のガスに対
しても良好な安定性をもつ。
本発明の温度平衡材の製造用原料は好適には窒化アルミ
ニウム、窒化アルミニウムの重量の０．０３−２重量Ｍ
％の、１μｍ以下の粒度のアルミニウム粉末と、０．／
−１０重量％の酸化物添加物を含有する窒化アルミニウ
ムの粉末状混合物である。
この混合物を冷間圧縮して素地成形体に加工し、この成
形体を不活性雰囲気中、好適には窒素算囲気下で緻密に
焼結する。
緻密に焼結した窒化アルミニウムの熱膨張係数と熱伝導
度とは酸化物添加物の種類及び量によって所望のように
左右させることができる。
約コ０θＷ　／　ｍ　Ｋ　までの熱伝導度が達成される
。
酸化物添加物としてはアルカリ土類金属の酸化物、希土
類金属〔スヵ／ジウム、イツトリウム及びう／タンない
しルテシウム（Ｌｕ））の酸化物、元素周期表バ族、Ｖ
族及びＶｌ族の遷移元素の酸化物、酸化アルミニウム及
び二酸化ケイ素を単独または２独以上を０．／　−／　
０重量％使用する。
特に、酸化イツトリウムを好適にはＯ，Ｓ〜ｌ爪Ｍ％の
ｈ；、で使用するのが有利であることが判明した。
本発明による温度平衡材は例えば高温度分析（約／７０
０℃までの）用熱分析装置における炉ブロック材として
、単結晶引上げ法における温度均一化材として、及び加
熱管の形で使用される０ 本発明による温度平衡材の製造は下記実施例に記載のよ
うにして慣用の仕方で行われる。
実施例 ／　ｆｉｍ以下の粒度のアルミニウム粉末１重量％を含
む窒化アルミニウム粉末９９重量％と酸化イツトリウム
粉末／重量％との混合物ｓｏ　ｏ。
Ｉ全ボールミル中で化２ミック磨砕材を用いて保賎雰囲
気ガスとしてのアルゴン下でｑｏ時間磨砕し、次いでｉ
ｏｏμｍのふるい目寸法のふるいにかけた。
ふるい処理して得た１００μｍ以下の粒度の粉末を冷間
等圧圧縮（圧力、ｚｓｏｏパ゛−ル）して圧縮体を遺り
、これを電気加熱焼結炉に入れた。
／θ−５ミリバールに減圧後に３００　”Ｑに加熱し、
この温度に７時間維持した後、焼結炉に窒素を５ミリバ
ールの圧力まで導入した。この圧力を保ちながら焼結炉
を加熱して３時間以内に／、２θｏ°０まで昇温させ、
次いで窒素圧を／グＯミリバールに高め、温度を７時間
以内に／ｇｓＯ′Ｃに高めたところ、窒素圧は／ざＯミ
リバールとなった。
この温度と圧力とｆ！：、２時間維持した後、冷却した
。焼結炉に通気した後、緻密焼結体を炉から取出した。
こうして造った温度子＠例は３．ｌ、×７０”−６ｘ−
ｚの熱膨張係数、コ００　Ｗ／　ｍ　Ｋ　の熱伝導率、
３２ＯＮ　／１１１１　ノ曲は強度及び、？、２７９１
ｃｍ　ｖＶｆｊ度（理論密度）のものであった。
特許出順人代理人　曾　我　道　照

Claims (1)

  1. 【特許請求の範囲】 ｌ　少くとも１０θＷ／　ｍ　、Ｅｌ、の熱伝導度をも
    つ緻密に焼粉ｉした窒化アルミニウムからなることを特
    徴とする、セラミック伺Ｆｌからなる温度平衡材。 ユ　温度平衡材が／独または、２種以上の酸化物添加物
    を含有してなる、特許請求の範囲第７項記載の温度平衡
    材。 、３．　酸化物添加物がアルカリ土類金属、希土類金属
    、元素周期表■族、Ｖ族及び■族の遷移全綱の酸化物、
    酸化アルミニウム及び二酸化ケイ素である特Ｎ／Ｉ〜請
    求の範囲第一項記載の温度平衡材。 ダ　酸化物添加物の含量が０．１〜１０重量％である特
    許請求の範囲第２項または第３項記載の温度平衡相。 Ｓ　酸化物添加物が酸化イツトリウムである特許請求の
    範囲第３項または第７項記載の温度平衡材。
JP59212749A 1983-10-15 1984-10-12 温度平衡材の製法 Granted JPS6096578A (ja)