JPS609896B2 - 防水シ−トの接合方法 - Google Patents

防水シ−トの接合方法

Info

Publication number
JPS609896B2
JPS609896B2 JP56186569A JP18656981A JPS609896B2 JP S609896 B2 JPS609896 B2 JP S609896B2 JP 56186569 A JP56186569 A JP 56186569A JP 18656981 A JP18656981 A JP 18656981A JP S609896 B2 JPS609896 B2 JP S609896B2
Authority
JP
Japan
Prior art keywords
adhesive
tape
waterproof sheets
rubber
joining
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP56186569A
Other languages
English (en)
Other versions
JPS5887033A (ja
Inventor
定 池田
雅典 筧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsuboshi Belting Ltd
Original Assignee
Mitsuboshi Belting Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsuboshi Belting Ltd filed Critical Mitsuboshi Belting Ltd
Priority to JP56186569A priority Critical patent/JPS609896B2/ja
Publication of JPS5887033A publication Critical patent/JPS5887033A/ja
Publication of JPS609896B2 publication Critical patent/JPS609896B2/ja
Expired legal-status Critical Current

Description

【発明の詳細な説明】 本発明は屋根、貯水池、地下鉄構内等の防水施工を施す
べき部分に使用される防水シートの接合方法に関し、更
に詳しくは大気中、あるいは水中等の水分の存在下にお
いて外気温〜９０ｑｏ範囲の比警舞霊害毒事霊需要憲三
率馨を接合する方法に関する。
従釆、防水シートの接合には、重ね合せ部に溶剤型接着
剤を塗布して貼合せる工法が通常、採用されている。
この場合、使用する接着剤により若干、差異があるが、
なおかつ次のような問題がある。‘１） 水みちを充填
するに充分なだけの塗布厚が確保しにくいこと‘２１
接着剤の塗布条件、乾燥条件の選択に熟練を要すること
、｛３’温度、転圧などの変化で接着力が不均一になる
こと‘４｝ 有機溶剤を多量に使用しているため、その
毒性により作業環境を汚染し、また火災の危険性がある
こと風 袋着剤塗布後、乾燥する間に砂ほこり等が付着
して接着不良を起すことがあること等である。
そのため、接着剤を使用する方法においては、防水シー
ト間の接着力、そして遮水機能を保証することは非常に
困難である。
一方、前記方法に対抗し接着剤を使用しない工法として
はホットメルト型の接着剤を用いるものや感圧性接着剤
を用いる方法があるが、これらの方法は特別なアプリケ
ーターが必要であったり、夏場等防水シートの表面温度
が５０℃以上になると接着力が著しく低下するなど、種
々の欠点を持っている状況であり、未だ充分実用に適し
ていない。
本発明は上述のような従来法の欠点に着目し、これを改
善するもので、水分の存在する環境下において低温で短
時間に防水シート同志を接合して遮水効果をあげ、また
接合部分の接着力の向上、作業性そして水みちをなくし
た防水シートの接合方法を提供することを目的とするも
のである。
すなわち、本発明は防水シート端部相互の重ね合せ部を
接合するに当り、ハロゲン化ブチルゴムにシランカップ
リング剤、粘着付与剤を配合した低温架橋可能で粘着性
を有するテープ状粘着材を上記重ね合せ部に介在させて
、該重ね合せ部を転圧した後、放置して該テープ接着材
を自然架橋させて防水シート同志を接合することをその
特徴とする。以下、更に前記本発明接合方法の具体的態
様について詳述する。
第１図は本発明による接合態様の一例を示し「防水シー
ト亀，１′の端部の重ね合せ部２の間に接合中と同中の
低温架橋可能で粘着性をもつテープ状接着材３を介在さ
せ、重ね合せ部２の上下を。
ーラ等により転圧した後の状態を図示している。しかし
て、このようにテープ状接着材３を介在させた防水シー
ト１，１′は水分の存在する環境下に放置されると、こ
のテープ状接着材３は水分の影響によって自然架橋をし
始め、放置時間の経過と共に防水シート同志を強固に接
着するのである。
本発明に使用する上記テープ状接着材はハロゲン化ブチ
ルゴムにシランカツプリング剤、粘着剤、その他適宜配
合剤を必要に応じて配合したものであり、そのうちハロ
ゲン化ブチルゴムとしては、臭素化ブチルゴム、塩素化
ブチルゴム等が含まれ、ハロゲンの含有量は通常、０．
１〜２肌ｔ％の範囲で、好ましくは０．５〜４Ｍ％であ
る。
この場合、ハロゲン含有量が２肌ｔ％を越える場合には
ポリマーのモジュラスが高くなりすぎてゴム弾性を失う
ため適当でなく、また０．１ｗｔ％以下では架橋点の数
が少なくなりすぎ良好な結果を期待し得なくなる。また
、架橋剤であるシランカップリング剤としては、その分
子中にハロゲンの反応可能な有機官能機、即ちアミノ基
、メルカプト基「 ゥレィド基などを少くとも１つ以上
有し、かつシランに結合した加水分解可能な基、例えば
アルコキシ基、アセトキシ基などを少なくとも１つ以上
有するものが適当であり、例えばｙーアミノプロピルト
リメトキシシラン、ｙ−アミノプロピルトリエトキシシ
ラン、８−アミノエチルトリメトキシシラン、８ーアミ
ノエチルトリエトキシシラン、Ｎ一Ｂ（アミノエチル）
ｙーアミノプロピルトリメトキシシラン、Ｎ一８（アミ
ノエチル）ｙーアミノプロピルメチルジメトキシシラン
、ｙ−メルカプトプロピルトリメトキシシラン、ｙーウ
レイドプロピルトリェトキシシラン等が挙げられる。こ
のシランカップリング剤は前記ハ。
ゲン化ブチルゴム中のハロゲン１モルに対し、通常０．
１〜５モル「好ましくは０．５〜２モルの割合で使用さ
れる。また「本発明に用いるテープ状接着材に粘着性（
ｔａｃｋ）を付与するための粘着付与剤としては、クマ
ロン樹脂〜 フェノール、テルベン樹脂、石油系炭化水
素樹脂、ロジン誘導体など、通常のゴム用粘着付与剤が
ゴム１０の重量部に対して通常５〜２０の重量部、好ま
しくは２０〜１０の重量部配合され使用される。
かくして叙上のようなゴム配合物からなるテープ状接着
材は粘着性を有するところから防水シートとよく接着し
、かつ９０ｑｏ以下の低温領域で水分と反応して架橋し
始めて防水シート同志を接合する。
この架橋反応は、シランカップＩＪング剤の有機官能基
がハロゲン原子と反応して化学結合を形成し、さらにハ
ロゲン化ブチルゴムに結合したシランカップリング剤の
加水分解性の基が周囲の水分により加水分解されてシラ
ノール基となり、他のハロゲン化ブチルゴムに結合した
シランカップリング剤において同様に生じたシラノール
基と縮合反応を生じて架橋すると考えられる。この場合
、架橋反応速度を早めて接着力を上げるには、ジブチル
錫ジラウレートのような縮合反応用触媒を配合すること
が効果的である。
なお、本発明に使用する前記テープ状接着材には、シラ
ンカップリング剤の架橋と共に従来、ハロゲン化ブチル
ゴムを架橋するに用いられている硫黄系加硫剤、キノン
オキシム系架橋剤、樹脂加硫剤等の架橋剤を適宜、併用
しても差支えないし、又、カーボンブラック等の補強剤
、炭酸カルシウム等の充填剤、軟化剤、可塑剤、老化防
止剤等を加えてもよい。
又、ブチルゴムやエチレン−プロピレンゴムなどの合成
ゴムや天然ゴムとハロゲン化ブチルゴムをブレンドして
もよい。更に、本発明において使用可能な防水シートと
しては、ブチルゴム、エチレンープロピレンゴムなどの
ゴム類を手体とするゴムシート、または該ゴム類に均一
に分散し得るポリエチレン、エチレン一酢酸ビニル共重
合体などの合成樹脂類およびアスファルトなどの騒音物
とを混和してなる浪合シートが挙げられ、これらが利用
目的に対応して使用される。
以下、本発明の実施例を示す。
＊実施例 後記第１表の配合により調合したテープ状接着材と、後
記第２表の配合で得た加硫ゴムシートとを用いて、互い
に接着し、下記接着テスト及び保持テストにより剥離接
着力ならびに保持力を測定した。
テープ状接着剤配合； 第 １ 表 単位；重量部 注１ ボリサーブｏモブチル×２ 注２ エッソＨＴプチル１０−６８ 注３ ｒ−メルカゾトブロピルトリェトキシンフン任４
ジプチル錫ジラゥレート注５ ｐ−ｔ−ブチルフェノ
ール＝ァセトン樹脂注６ パラフィン系プロセスオイル
被着体ゴムシート配合； 第２表 単位；重量部 ＥＰＤＭ ＩＯＯ
ｚｎｏ ５ステアリ
ン酸 １ＳＲＦカーボンブラック
５０ＭＡＦカーボンブラック
２０炭酸カルシウム粉
２０パラフィン系プロセスオイル ２０
ジベンゾチアジルスルフイド ０．５テト
ラメチルチウラムジスルフイド １．０硫 黄
１．０加硫条件 １６０℃×
３企分 接着テスト； 上記第２表に示した加硫ゴムシートを被着体とし、バフ
がけ、トルェン脱脂後、前記第１表の配合で得た厚さ１
．０吻のテープ状接着材を該加硫シートに介在し、庄着
後、２５側中の短冊状に切った。
このようにして得た試料を５０午０で一定の相対湿度に
保った密閉容器内に、１，４及び７日間放置した後、５
仇舷／ｍｉｎの速度、室温で剥離強度を測定した。その
結果を第２図、第３図に示す。図中、イは実施例１、口
は比較例１、ハは実施例２、二は比較例２の場合であり
、ＲＨは各相対湿度である。保持力テスト ＪＩＳＺ１５２４に準じて１０００夕の荷重下で試験を
行った。
但し、テープ状接着材は２５豚×２５肌×１．０柳のも
のを用い、彼着体は前記第２表の配合で得た加硫ゴムシ
ートで、試験温度は室温（１９ｏｏ）である。その結果
を第４，５図に示す。以上の各テスト結果により、ハロ
ゲン化プチルゴムにシランカップリング剤、粘着付与剤
等を加えてなるテープ状接着材はそれ自身被着体との接
着が良好であり、また水分の存在下であれば約９０℃以
下の低温領域で自然架橋するところから、上記テープ状
接着材を防水シート間に介在すれば、時間の経過に伴っ
て防水シート同志を強固に接合でき、極めて優れた防水
シートの接合方法であることが理解される。
【図面の簡単な説明】
第１図は本発明の接合方法に係る防水シート接合部の１
例を示す断面図、第２図は実施例１と比較例１のテープ
状接着材を用いた場合の放置時間と剥離強さの関係を示
す図表、第３図は実施例２と比較例２のテープ状接着材
を用いた場合の放置時間と剥離強さの関係を示す図表、
第４図は実施例１と比較例１のテープ状接着材を用いた
場合の放置時間とずれの長さとの関係を示す図表、第５
図は実施例２と比較例２のテープ状接着材を用いた場合
の放置時間とずれの長さの関係を示す図表である。 多′図 姿Ｚ図 多３図 多ィ図 多ク図

Claims (1)

    【特許請求の範囲】
  1. １ 防水シート端部相互の重ね合せ部を接合するに際し
    、ハロゲン化ブチルゴムにシランカツプリング剤、粘着
    付与剤等を配合した低温架橋可能で粘着性を有するテー
    プ状接着材を上記重ね合せ部に介在させて、該重ね合せ
    部を転圧した後、放置して該テープ状接着材を自然架橋
    させて防水シート同志を接合することを特徴とする防水
    シートの接合方法。
JP56186569A 1981-11-19 1981-11-19 防水シ−トの接合方法 Expired JPS609896B2 (ja)