JPS6232553B2 - - Google Patents

Info

Publication number
JPS6232553B2
JPS6232553B2 JP51088201A JP8820176A JPS6232553B2 JP S6232553 B2 JPS6232553 B2 JP S6232553B2 JP 51088201 A JP51088201 A JP 51088201A JP 8820176 A JP8820176 A JP 8820176A JP S6232553 B2 JPS6232553 B2 JP S6232553B2
Authority
JP
Japan
Prior art keywords
pigment
leader
resins
tape
magnetic tape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP51088201A
Other languages
English (en)
Other versions
JPS5313907A (en
Inventor
Masaaki Fujama
Masahiro Uchiumi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujifilm Holdings Corp
Original Assignee
Fuji Photo Film Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Photo Film Co Ltd filed Critical Fuji Photo Film Co Ltd
Priority to JP8820176A priority Critical patent/JPS5313907A/ja
Priority to US05/816,183 priority patent/US4146031A/en
Priority to DE19772733541 priority patent/DE2733541A1/de
Publication of JPS5313907A publication Critical patent/JPS5313907A/ja
Publication of JPS6232553B2 publication Critical patent/JPS6232553B2/ja
Granted legal-status Critical Current

Description

【発明の詳細な説明】
本発明はビデオテープ、メモリーテープ、オー
デイオ等の磁気記録用長尺帯の頭部、尾部、必要
に応じて中間部に位置する。リーダーまたはトレ
ーラーテープの新規な構成に関するものである。 従来、磁気テープ部のドロツプアウトは磁気テ
ープ自体の問題でリーダーテープには殆んど関係
しないと考えられていた。しかしながら、本発明
者等の検討結果によれば磁気テープ輸送中に増加
するドロツプアウト、繰返し使用時のテープ頭部
のドロツプアウト等はリーダーの特性に支配され
ることが判明した。しかもその原因はリーダーの
塗布面側だけの問題ではなく、反塗布面側の特性
も重要であることがわかつた。更にもう１つの新
しい知見は、テープの巻きつけ角度の強い固定ガ
イドピンを有するカセツトに組込まれた場合、磁
気テープが固定ガイドピンに張りついて巻戻し不
可能になる現象が従来のリーダーで発生したが、
これも磁気テープに原因があるのではなくリーダ
ーによつて生ずることがわかつた。即ちリーダー
が適当な性能を有していないと磁気テープやガイ
ド系を汚染して、その結果ドロツプアウトの増
加、磁気テープの巻戻し不良が生ずるものと考え
られる。そしてそれは塗膜部の削れやベース面側
の削れをも惹起するものであることが判つた。 従来のリーダーまたはトレーラー用テープとし
ては次の様なものが知られている。金属蒸着膜
をストライプ状に設けたもの（実公昭46―
14349）、ベースの片面または両面をマツト化し
たもの（実公昭49―42726）、粒子サイズ４μ以
下の顔料を粘結剤100部に対して50〜800部添加し
た塗布層を設けたもの（特開昭49―40504、同49
―67603）等である。上記３者のうちのものが
性能的に最もすぐれているが、依然として次のよ
うな欠点を有している。１繰返し使用時にガイド
ポールおよび磁気ヘツドを含む走行系によつて塗
膜が損傷を受け、ドロツプアウトの増加を来たし
たり、走行性が不安定なものとなる。２ヘリカル
VTRのように高速度で回転するビデオ・ヘツド
の尖端に塵が付着して目詰りを起し、この結果ビ
デオ信号の記録再生が困難になる。３高温、高湿
下ではリーダーの摩擦係数が増大して必要とする
一定の走行速度が維持できず、走行性が不安定と
なる。４巻き戻し時、テープの巻付角度が大きく
なるにしたがつて走行が不良となる。 リーダーまたはトレーラーテープにおける上記
の欠点を解消すべく本発明者等は研究を重ねた結
果、プラスチツク支持体表面に顔料と粘結剤を主
体とする塗布層を設け、この顔料は白色顔料又は
体質顔料よりなる固体粉末であつてその平均粒子
サイズは(A)0.01〜２μ、(B)８〜25μの２群を混合
比(A)／(B)が９／１〜５／５にて混合したものから
なるもので、更に反塗布層面である支持体裏面に
0.1mg／m2以上の有機物潤滑剤層を有した構造と
すれば、その目的は達せられることを見出して本
発明を完成したものである。 本発明で用いられる支持体は磁気テープの支持
体と同一または異なつたものでよく、ポリエチレ
ンテレフタレート、ポリエチレンナフタレート等
ポリエステル類、ポリプロピレン等のポリオレフ
イン類、セルローストリアセテート、セルロース
ダイアセテート等のセルロース誘導体、ポリ塩化
ビニル等のビニル系樹脂類、ポリカーボネート等
のプラスチツク等から選ばれ、その厚さは磁気テ
ープの支持体と同じかまたはそれ以上であること
が必要である。 本発明における顔料は固体粉末であればどのよ
うなものでもよく、例えば、鉛白、鉛亜鉛華、硫
化亜鉛、塩基性硫酸鉛、アンチモン白、酸化ジル
コン、メタほう酸バリウム、パツチンソン白、マ
ンガン白、亜鉛華、リトボン、酸化チタン、硫酸
鉛、珪酸鉛、鉛酸カルシウム、酸化錫、タングス
テン白等の白色顔料や、硫酸バリウム、炭酸バリ
ウム、沈降性炭酸カルシウム、胡粉、アルミナ
白、シリカ、滑石粉、珪酸カルシウム、沈降性炭
酸マグネシウム、ペントナイト、消石灰、沈降性
硫酸バリウム、白亜、石膏、クレー、シリカ白、
アスベスチン、炭酸マグネシウム、サチン白、マ
グネシア、ストロンチウム白等の体質顔料、その
他リーダーテープに透明度を必要としなければ黒
色顔料、灰色顔料、赤色顔料、茶色顔料、緑色顔
料、青色顔料等が使用でき、特に無機顔料が好ま
しく、(A)，(B)２種類の無機顔料の混合比(A)／(B)の
範囲は９／１〜５／５である。なお平均粒子サイ
ズの範囲は(A)0.01〜２μ、(B)８〜25μであり、(B)
粒子については平板状のものが好ましく、(B)の粒
子サイズが大きすぎると粉の脱落によるドロツプ
アウトが増加する。この(B)の粗な粒子によつて塗
膜面の凹凸が生じ、その凹凸は0.3〜10μ程度が
適当である。その時の顔料の塗布層の厚さは２〜
15μが好ましい。 また、粘結剤としては熱可塑性樹脂、熱硬化性
樹脂、導電性樹脂の単独または混合物が用いられ
る。熱可塑性樹脂としては、塩化ビニル酢酸ビニ
ル共重合体、塩化ビニル塩化ビニリデン共重合
体、塩化ビニルアクリロニトリル共重合体、アク
リル酸エステルアクリロニトリル共重合体、アク
リル酸エステル塩化ビニリデン共重合体、アクリ
ル酸エステルスチレン共重合体、メタクリル酸エ
ステルアクリロニトリル共重合体、メタクリル酸
エステル塩化ビニリデン共重合体、メタクリル酸
エステルスチレン共重合体、ウレタンエラストマ
ー、ポリ弗化ビニル、塩化ビニリデンアクリロニ
トリル共重合体、ブタジエンアクリロニトリル共
重合体、ポリアミド樹脂、ポリビニルブチラー
ル、セルロース誘導体（セルロースアセテートブ
チレート、セルロースダイアセテート、セルロー
ストリアセテート、セルロースプロピオネート、
ニトロセルロース等）、スチレンブタジエン共重
合体、ポリエステル樹脂、クロロビニルエーテル
アクリル酸エステル共重合体、アミノ樹脂、各種
の合成ゴムの単独及びこれらの混合物が、熱硬化
性樹脂としては、フエノール樹脂、エポキシ樹
脂、ポリウレタン硬化型樹脂、尿素樹脂、メラミ
ン樹脂、アルキツド樹脂、シリコン樹脂、アクリ
ル系反応樹脂、エポキシ―ポリアミド樹脂、ニト
ロセルロースメラミン樹脂、高分子量ポリエステ
ル樹脂とイソシアネートプレポリマーの混合物、
メタクリル酸塩共重合体とジイソシアネートプレ
ポリマーの混合物、ポリエステルポリオールとポ
リイソシアネートの混合物、尿素ホルムアルデヒ
ド樹脂、低分子量グリコール／高分子量ジオー
ル／トリフエニルメタントリイソシアネートの混
合物、ポリアミン樹脂及びこれらの混合物等が、
また導電性樹脂としては、ポリカチオン系樹脂や
第４級アンモニウム塩樹脂等、例えば ポリ（塩化ビニルベンジルトリメチルアンモニウ
ム） ポリ（塩化―２―ヒドロキシ―３―メタクロイロ
キシプロピルトリメチルアンモニウム） ポリ（塩化―Ｎ―アクリルアミドプロピル―３―
トリメチルアンモニウム） ３，４―アイオネン ８，８―アイオネン が使用される。 顔料と粘結剤の比率（顔料／粘結剤）好ましく
は６／１〜0.5／１、特に好ましいのは3.0／１〜
1.0／１の範囲である。 支持体裏面に設ける潤滑剤層の潤滑剤としては
シリコーンオイル、脂肪族エステル、フツ化オイ
ル、密ろうの如きワツクス類等の有機物潤滑剤が
好ましく用いられ、また潤滑剤の塗布層としては
0.1〜1000mg／m2が好ましい範囲である。この有
機物潤滑剤は支持体ベースを保護すると同時に一
部が塗膜に転写して離型効果を持たせ、ヘツドの
チツピングや面荒れを防止する効果を奏するもの
であるが、有機物潤滑剤層の塗布量が多くなると
VTRの走行系を汚染する。 本発明のリーダーまたはトレーラーテープを用
いることにより次のような効果が奏せられる。 １ 繰返し使用時のリーダー塗布面の摩擦係数の
増加が極めて少なくなる。 ２ リーダーに後続する磁気テープのドロツプア
ウトの増加が極めて少ない。 ３ リーダー部にビデオ回転ヘツドが接触しても
目詰りが発生しないばかりでなくヘツドのクリ
ーニング効果がある。 ４ 高温高湿下でも走行性が優れている。 ５ 固定ガイドピンを有する走行系での磁気テー
プのハリツキが生じない。 例 １ 従来技術により製造したリーダーテープを接合
したカセツトテープNo.１と、本発明のリーダーテ
ープを接合したカセツトテープNo.２〜10について
ドロツプ・アウト増加率、巻戻し不良率、摩擦係
数増加率等に関して比較を行なつた。 まず、評価基準について説明する。 １ ドロツプアウトの増加率 三洋電機製VTC―7230型VTRのカセツトテー
プの先端に各種のリーダーをつけ、リーダーに接
続されている磁気テープの頭の部分の１分間当り
ドロツプアウトを画面上で目視計数しながら記録
再生を行ない、 ドロツプアウト増加率 ＝５０回走行再生時のドロツプアウト数／初回再生
時のドロツプアウト数 で算出した。 ２ 巻戻し不良率 １）と同様なVTRおよびカセツトを用い、テ
ープの頭の部分で早送り20秒→停止→巻戻
し１秒後→停止→巻戻し１秒後→停止、続
いて、を繰返し、テープ頭部になつたらか
らやり直す。そして停止後、巻戻し操作時に磁気
テープが走行しない場合を巻戻し不良とし、巻戻
し不良率を下式から算出した。 巻戻し不良率＝巻戻し不能回数／巻戻し、停止の繰返し
回数×100 ３ 摩擦係数増加率 直径50mmのアルマイトローラーにリーダーの顔
料塗布面が接するよう巻きつけ、荷重100ｇ、相
対速度13cm／秒で１分間測定し次のように算出し
た。 摩擦係数増加率＝ロール回転１分後の摩擦係数／ロー
ル回転５秒後の摩擦係数 Γ サンプルの製法 サンプルNo.２〜10については次の様にして製造
した。 ボールミル中に顔料(A)、粘結剤および有機溶剤
の適量を添加して約15時間分散後、顔料(B)を添加
して更に５時間分散を行なつて塗布液をつくつ
た。厚み36μのポリエチレンテレフタレートベー
スの片面に上記塗布液を塗布後乾燥し、更に上記
と反対面側のベースに潤滑剤を溶剤で希釈して塗
布し、乾燥後の塗布層が0.1mg／m2以上の値にな
るように塗布した。上記塗布面を1/2インチ巾に
スリツト後、市販されている三洋電機製VTC―
7230VTRのカセツトテープにリーダーテープの
みを入れ換えて各種リーダーを接合したカセツト
テープを製造した。上記塗布液において粘結剤と
しては、塩化ビニル酢酸ビニル共重合体41％、導
電性アクリル樹脂32％、イソシアネート22％、レ
シチン2.5％、シリコンオイル２％からなる混合
物を、溶剤としてはメチルエチルケトンを用い
た。 サンプルNo.１は顔料Ｂを添加しない点、支持体
裏面に有機物潤滑剤を塗布しない点を除いてはサ
ンプルNo.２〜10と同様にして製造した。 サンプルNo.１〜10についての前記の性能に関す
る比較を行なつた結果を第１表に示す。
【表】 第１表において、サンプルNo.１とNo.２〜５を比
較して判るように、本発明のものは従来のものに
比しドロツプアウト増加率、巻戻し不良率、摩擦
係数増加率の全てにわたつて低く、極めて優れて
いるものである。またサンプルNo.６，７からは、
有機物潤滑剤の塗布量は0.1mg／m2までは充分使
用できるが、それ以下ではその効果が少なくなる
ことが判る。サンプルNo.８〜10およびそれ以前の
サンプルを含めて考察すると、顔料(B)の粒子サイ
ズは８〜25μ、顔料(A)の粒子サイズは0.01〜２
μ、顔料／粘結剤の比率は3.0／１〜1.0／１が特
に好ましいことが判つた。Ａの粒子サイズは大き
な粒子になるほど光透過率が悪くなると、同時
に、表面電気抵抗が増大するので小さい粒子の方
が好ましいが、一方、極端に粒子サイズの小さい
ものは塗膜の耐久性が劣るから上記の範囲が適当
である。更に接合テープの粘着剤がビデオ回転ヘ
ツドに付着した場合、従来技術によるサンプルNo.
１のリーダーを通しての回復率が3/10であるのに
対して、本発明のものは高い回復率を示した。ま
た30℃、湿度90％での走行性はサンプルNo.１で速
度が低下するのに対して、本発明のものは異常が
認められなかつた。 例 ２ 塗布層 顔料(A)；炭酸カルシウム、平均粒子サイズ２μ 顔料(B)；ケイ酸マグネシウム、平均粒子サイズ
１〜40μの間で変動 粘結剤；例１と同じ組成のもの 顔料(A)／(B)＝８部／２部 顔料（(A)＋(B)）／粘結剤＝３／１ 有機物潤滑剤層 アミルステアレートを用い、含量を７mg／m2の
ものと、0.1mg／m2のものとの２種類とした。 上記の条件で顔料(B)の粒子サイズを変化させた
場合の、ヘツド目詰りに回復率とドロツプアウト
増加率について調べた。結果を添付図面の図表に
示す。該図中、横軸に顔料(B)の粒子サイズ
（μ）、縦軸(A)にヘツド目詰り回復率（％）、縦軸
(B)に50回後のドロツプアウト増加率（％）をと
り、実線はヘツド目詰り回復率を、破線は50回後
のドロツプアウト増加率を各々示すグラフで、該
グラフ中１は有機物潤滑剤含量７mg／m2のもの、
２は有機物潤滑剤0.1mg／m2のものである。 該図から明らかなように、顔料(B)の粒子は５μ
において効果が現われ、35μ以上ではむしろ悪化
する傾向がある。 例 ３ 例１において、顔料(B)を除去し、その代わりに
顔料(A)を10部用いた以外はサンプルNo.４と同様な
方法でサンプルNo.11を製造した。次に例１におい
て、潤滑剤を除去した以外はサンプルNo.４と同様
な方法でサンプルNo.12を製造した。 次に例１において、顔料(A)を除去し、その代わ
りに顔料(B)を10部用いた以外はサンプルNo.４と同
様な方法でサンプルNo.13を製造した。次に例１に
おいて顔料(A)を除去し、その代わりに顔料(B)を10
部用いかつ、潤滑剤を除去した以外はサンプルNo.
４と同様な方法でサンプルNo.14を製造した。 サンプルNo.11〜14，１（比較例）及びサンプル
No.４（実施例）について前記の性能に関する比較
を行なつた結果を第２表に示す。
【表】 第２表においてサンプルNo.４とサンプル１，11
〜14を比較して判るように、本発明は粒子サイズ
の異なる２種の顔料(A)及び顔料(B)を組み合せて用
い、かつ潤滑剤を併用することによつて本発明の
効果を発揮するものであり、これらを１つでも満
足しない組み合せでは本発明の効果が得られな
い。
【図面の簡単な説明】
添付の図面は、本発明において、顔料(B)の粒子
サイズを変化させた場合の、ヘツド目詰り回復率
とドロツプアウト増加率への影響を示す図表であ
る。

Claims (1)

    【特許請求の範囲】
  1. １ プラスチツク支持体表面に顔料と粘結剤を主
    体とする塗布層、裏面に潤滑剤層を設け、上記顔
    料は白色顔料又は体質顔料よりなる固体粉末であ
    つて、平均粒子サイズ、(A)0.01〜２μ、(B)８〜25
    μの２群を混合比(A)／(B)が９／１〜５／５にて混
    合したものから成り、上記潤滑剤層は有機潤滑剤
    が0.1mg／m2以上の割合で塗布されたものである
    ことを特徴とする磁気テープ用リーダーまたはト
    レーラー。
JP8820176A 1976-07-26 1976-07-26 Reader or trailer for magnetic tape Granted JPS5313907A (en)