JPS6233686A - 光記録材料 - Google Patents

光記録材料

Info

Publication number
JPS6233686A
JPS6233686A JP60175137A JP17513785A JPS6233686A JP S6233686 A JPS6233686 A JP S6233686A JP 60175137 A JP60175137 A JP 60175137A JP 17513785 A JP17513785 A JP 17513785A JP S6233686 A JPS6233686 A JP S6233686A
Authority
JP
Japan
Prior art keywords
recording
volume content
tin
over
recording layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP60175137A
Other languages
English (en)
Other versions
JPH0523197B2 (ja
Inventor
Masaki Ito
雅樹 伊藤
Akio Morimoto
昭男 森本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NEC Corp
Original Assignee
NEC Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NEC Corp filed Critical NEC Corp
Priority to JP60175137A priority Critical patent/JPS6233686A/ja
Priority to US06/893,040 priority patent/US4763139A/en
Priority to DE8686110786T priority patent/DE3679249D1/de
Priority to EP86110786A priority patent/EP0211435B1/en
Publication of JPS6233686A publication Critical patent/JPS6233686A/ja
Publication of JPH0523197B2 publication Critical patent/JPH0523197B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 （産業上の利用分野） 本発明はレーザ光によって情報を記録再生することので
きる光記録媒体に関し、さらζこ詳しくは集光したレー
ザ光の熱作用により薄膜にピットを形成して記録する光
記録媒体に関するものである。
（従来の技術） レーザ光によって情報を媒体に記録し、かつ再生する追
記型光ティスフメモリは、配備密度が高いことから大容
量記録装置として優れた特徴を有している。このような
追記型光ディスクメモリの記録媒体とじては、低融点金
属であるＴｅ、Ｂｉあるいにそれらを含有する合金が使
用されている（例えば、特公昭５４−１５４８３号）。
（発明が解決しようとする問題点） しかし、低融点金属（とくｌこ高感度であるＳｎ）は、
記録再生信号の品質が悪く実用番こ供することはできな
かった。
本発明の目的は、記録感度が高く、かつ信号品質の良好
な光記録媒体に用いる光記録材料を提供することにある
。
（問題点を解決するための手段） 本発明の光記録材料は光記録媒体の記録層に用いる光記
録材料であってスズを体積率で３０％以上含有し、加え
て、ニッケル酸化物を体積率で２０−以上含有して構成
されることを特徴とする特（作用） 本発明による記録＠は体積率で３０チ以上のスズに加え
て体積率で２０チ以上のニッケル酸化物を不可欠な構成
要素として含んでいる。スズに低融点の半金属のため高
い記録感度を有している。
しかし、材料の結晶性に起因して表面性が悲いので、未
記録ノイズが大きく問題であり実用に供することにでき
ない。本発明者らは体積率で２０％以上のニッケル酸化
物をスズに含有させること番こより記録層の表面性が著
しく改善されることを見出し１本発明に致ったものであ
る。
記録層の膜厚は１００〜１０（ＩＯＡ程度が記録感度。
信号品質の点で望ましく、とくに１５０〜５０００Ａが
望ましい。
記録層はスズとニッケル酸化物のみの混合物でも充分に
優れた光記録媒体特性を有するが、更に耐候性を向上さ
せたり１反射率を所定の値に調整する１こめには第３物
質等を含有させてもよい。第３物質とじてに、炭素、ア
ルミニウム、チタン、りＣ１ム、　鉄、　ニアハルト、
ニッケル、ｍ、亜鉛、ゲルマニウム、ジルコニウム、ニ
オブ、モｌＪブｆン、ロジウム、パラジウム、銀、タン
タル、タングステン、白金、金のうち１以上が望ましい
。これらは体積率で約ｌＯ〜１５チ以下で効果を示すも
のが多いが、物理によってはこれらより多く含ませるこ
ともある。
図に光記録媒体の一例を示す断面図である。ｌは基板、
２は記録層を表わす。
基板としては洩々のものを使用できるが、一致ｔこは合
成樹脂Ｊガラス、磁器が望ましい。合成樹脂としては、
ポリメチルメタクリレート等のアクリル樹脂、ポリカー
ボネート、ボワエーテルイミド、ポリサルホン、エポキ
シ樹脂、塩化ビニル樹脂等がある。基板ｌこはその上に
断熱層やスムージング層を設けてもよい。基板の形状に
円板状、シート状、テープ状とすることができる。
記録層への情報の記録は、記録層にビットを形成するこ
とによりなされる。円板状の基板を用いるディスク媒体
では、ビットニ同心円状又にスパイラル状の多数のトラ
ック形成するように記録される。多数のトラックを一定
間隔で精度よく記録するには１通常基板上に光の案内溝
が設けられる。
ビーム径程度の溝ｌこ光が入射すると光が回折される。
ビーム中Ｉｖが溝からずれるにつれて回折光強度の空間
分布が異なり、これを検出してビームを溝の中心ｌこ入
射させるよう番こサーボ系を構成できる。通常溝の幅に
０．３〜１．２μｍ、その深さは使用する記録再生レー
ザ波長のｌ／１２〜１／４の範囲ζこ設定される。
（実施例１） 以下１本発明の実施例について説明する。
内径１５ｍｍ、外径１２０ｍｍ、厚さ１．２ｍｍ　の案
内溝付きアクリル樹脂ディスク基板を真空蒸着装置内に
入れ、　　２ＸＩＯＴｏｒｒ以下に排気した。蒸発源と
しては、抵抗加熱用ボートｆこＳｎを入れ、電子ビーム
加熱用るつほにＮｉＯを入れた。水晶扱動子式膜厚モニ
ターを用いてそれぞれの蒸着物質の蒸着速度を制御しな
から共蒸着することにより、ディスク基板上に記録層を
形成した。
第１表に、　３ｓｏ４の記録層のＮｉＯの体積含有率を
変化させた場合に、基板入射反射率（波長８３００Ａ）
、未記録ノイズレベル、信号対雑音比（Ｃ／Ｎ　）がど
のようζこ変化するかを示す。ここで。
記録再生に用いた半導体レーザの波長は８３００Ｘであ
り、信号周波数は１．２ＭＨｚ、ハンド＠は３０ＫＨｚ
、媒体の線速度は５ｍ／ｓｅｃ　である。反射率はＮｉ
Ｏの含有率が増大するｆこしたがって低下する傾向とな
り、スズの含有率が３０％未満では反射率が１０１４こ
達しないのでフォーカスサーボに悪影響を与え実用上問
題となる。未記録ノイズレベルｉ、ＮｉＯを添加するこ
とにより急激に低下し、２０％以上のＮｉＯの含有で実
用の域に達する。
したがって、ＮｉＯの体積含有率が２０チ以上でかつＳ
ｎの体積含有率が３０％以上が実用可能な組成範囲であ
る。
膜厚が３５ＯＡ　以外の場合の実施例を第２表に示す。
この場合においても上記組成範囲が良好であることがわ
かる。
第２表 ＼＼、＋ （実施例２） 抵抗加熱用ボートにＳｎを入れ、を子ビーム加熱用るつ
ぼにＮｉＯを入れもう一つの電子ビーム加熱用るつぼに
Ｃｎを入れ、体積率で６０％、３５チ、５％で共蒸着し
てアクリルディスク基板上に記録層を形成した、実施例
１と同様ｌこして記録再生したところＣ／Ｎ　約５０ｄ
Ｂと良好な記録ができた。
（実施例３） 抵抗加熱用ボートにＳｎ　を入れ、電子ヒーム加熱用る
つぼｌこＮｉＯを入れ、もう一つの電子ビーム加熱用る
つほに重−ｌφで８０対２０のへ１−Ｃｒ合金を入れ、
体積率で５５鴫、４０％、５％テ共蒸着してアクリルデ
ィスク基板上ｌこ記録層を形成した。実施例１と同様ｌ
こして記録再生したところＣ／Ｎ　約５０　ｄＢと良好
な記録ができた。
（実施例４） 抵抗加熱用ボートにＳｎを入れ、電子ビーム加熱用るつ
ぼにＮｉＯを入れ、もう一つの電子ビーム加熱用るつほ
に重ｔ％で７０対２５対５のＦｅｌＩＣｒ−ＡＡ！合金
を入れ１体ａｔｉで５５％、４０％。
５％で共蒸着してポリカーボネート基板上ｆこ記録層を
形成した。実施例１と同様番こして記録再生したところ
、Ｃ／Ｎ　約４ｆｌｄ　Ｂ　　と良好な記録ができた。
（発明の効果） 上記実施例から明らかなように１本発明により記録感度
が烏くかつ毎号品質の良好な光記録材料が得られる。
【図面の簡単な説明】
図に元記鋒媒体の断面図である。 図１こおいて、１は基板、２ｔ／′ｉ記録層を示す。 −二゛ 、゛そＩダ一 代野人弁理士　内ｗＣ層Ｊハｊ］′： ＼＼〜− 手続補正書（自発） ６１．１０．２８ 昭和　　年　　月　　日

Claims (1)

    【特許請求の範囲】
  1. 　光記録媒体の記録層に用いる光記録材料であって、ス
    ズを体積率で３０％以上含有し、加えてニッケル酸化物
    を体積率で２０％以上含有してなることを特徴とする光
    記録材料。
JP60175137A 1985-08-08 1985-08-08 光記録材料 Granted JPS6233686A (ja)