KR20170077153A - 광활성 섬유 및 직물 매질 - Google Patents

광활성 섬유 및 직물 매질 Download PDF

Info

Publication number
KR20170077153A
KR20170077153A KR1020177012621A KR20177012621A KR20170077153A KR 20170077153 A KR20170077153 A KR 20170077153A KR 1020177012621 A KR1020177012621 A KR 1020177012621A KR 20177012621 A KR20177012621 A KR 20177012621A KR 20170077153 A KR20170077153 A KR 20170077153A
Authority
KR
South Korea
Prior art keywords
photoactive
fibers
agent
eosin
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
KR1020177012621A
Other languages
English (en)
Inventor
레미지오 피에르갈리니
니콜라오스 루피스
데이비드 오해이온
Original Assignee
클록스 테크놀로지스 인크.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 클록스 테크놀로지스 인크. filed Critical 클록스 테크놀로지스 인크.
Publication of KR20170077153A publication Critical patent/KR20170077153A/ko
Ceased legal-status Critical Current

Abstract

다양한 측면에서, 본 발명은 광활성제를 포함하는 섬유 및 직물 매질, 및 광활성제의 광활성화에 의해 광활성화될 수 있는 섬유 및 직물 매질에 관한 것이다. 일부 예에서, 섬유 및 직물 매질은 표면 상에 존재하는 광활성제를 갖는다 (예를 들어, 섬유/직물이 광활성제로 코팅 또는 분무되거나 섬유/직물이 광활성제를 포함하는 조성물 또는 제제에 침지된다). 다른 경우에, 광활성제는 섬유를 만드는 물질 내로 혼입된다 (예를 들어, 광활성제가 섬유를 만드는 물질과 혼합/화합된다). 본 발명의 광활성 섬유는 적어도 하나의 열가소성 중합체, 및 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는 적어도 하나의 광활성제를 포함한다.

Description

광활성 섬유 및 직물 매질{PHOTOACTIVATABLE FIBERS AND FABRIC MEDIA}
관련 출원에 대한 상호참조
본 출원은 그의 내용이 여기에 참조로 포함되는 2014년 10월 31일자로 출원된 미국 가특허출원 제62/073,795호의 이익 및 우선권을 주장한다.
본 발명은 일반적으로 광활성제를 포함하는 광활성 섬유 및 직물 매질, 이러한 광활성 섬유 및 직물 매질을 형성하는 방법, 및 이들의 잠재적 사용에 관한 것이다.
광선치료(phototherapy)는 수술, 치료 및 진단을 비롯한 의료 및 미용 분야 모두에서 광범위한 응용 범위를 갖는 것으로 인지되어 왔다. 예를 들어, 광선치료는 침습을 적게 하면서 암 및 종양을 치료하고, 항균 치료로서 표적 부위를 소독하고, 피부 상태를 치료하고, 상처 치유를 촉진하기 위해 사용되었다.
이들 용도에 대해, 광선치료는 전형적으로 광을 흡수 및/또는 방출할 수 있는 광활성제를 포함하는 광활성 제형(photoactivatable formulations) 및/또는 조성물을 사용하여 이루어졌다. 이들 광활성 제형 및/또는 조성물은 전형적으로 액체 또는 반(semi)-액체(예컨대 겔, 페이스트, 크림 등)로서 제조 및/또는 사용되었다. 그것들의 액체 및/또는 반-액체 텍스처로 인해, 이들 광활성 제형 및/또는 조성물 중 일부는 제형 및/또는 조성물 밖으로의 광활성제의 누출을 나타낸다. 또한, 이들 제형 및/또는 조성물은 그것들이 적용될 수 있는 지지체/표면을 필요로 한다. 그것들은 유체와 접촉시 확산 및/또는 희석되려는 경향이 있기 때문에, 일부 액체 및 반-액체 광활성 제형 및/또는 조성물은 원하는 효과를 얻기 위해 표면 위로 다중 적용될 것을 필요로 한다.
그러므로, 본 발명은 지금까지 알려져 있는 광활성 제형을 능가하는 추가의 장점들을 나타낼 수 있는 특징들을 가지는 광활성 제형에 관한 것이다. 이러한 특징들은 광선치료에 유용할 수 있고 광활성 제형의 보다 폭넓은 산업상 이용가능성에 기여할 수 있다.
다양한 측면에 따르면, 본 발명은 적어도 하나의 열가소성 중합체, 및 적어도 하나의 광활성제를 포함하는 광활성 섬유에 관련되고, 이때 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출한다.
다양한 측면에 따르면, 본 발명은 적어도 하나의 열가소성 중합체로 구성된 복수의 섬유; 및 적어도 하나의 광활성제를 포함하는 광활성 직물에 관련되며, 이때 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출한다.
다양한 측면에 따르면, 본 발명은 광활성 직물을 포함하는 제조 물품에 관련되는데, 광활성 직물은: a) 적어도 하나의 열가소성 중합체로 구성된 복수의 섬유; 및 b) 적어도 하나의 광활성제를 포함하며, 이때 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출한다.
다양한 측면에 따르면, 본 발명은 대상에 대해 광선치료를 실시하는 방법에 관련되며, 그 방법은 본원에서 정의된 광활성 섬유를 대상에게 적용하는 단계; 및 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 광활성 섬유를 조사하는 단계를 포함한다.
다양한 측면에 따르면, 본 발명은 대상에 대해 광선치료를 실시하는 방법에 관련되며, 그 방법은 본원에서 정의된 광활성 직물을 대상에게 적용하는 단계; 및 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 광활성 직물을 조사하는 단계를 포함한다.
다양한 측면에 따르면, 본 발명은 대상에 대해 광선치료를 실시하는 방법에 관련되며, 그 방법은 본원에서 정의된 제조 물품을 대상에게 적용하는 단계; 및 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 제조 물품을 조사하는 단계를 포함한다.
다양한 측면에 따르면, 본 발명은 대상에게 광선치료를 실시하기 위해 사용되는, 본원에서 정의된 광활성 섬유의 용도에 관련된다.
다양한 측면에 따르면, 본 발명은 대상에게 광선치료를 실시하기 위해 사용되는, 본원에서 정의된 광활성 직물의 용도에 관련된다.
다양한 측면에 따르면, 본 발명은 대상에게 광선치료를 실시하기 위해 사용되는, 본원에서 정의된 제조 물품의 용도에 관련된다.
다양한 측면에 따르면, 본 발명은 제1 광활성 직물; 및 제2 광활성 직물을 포함하는 제조 물품에 관련되며; 이때 제1 및 제2 광활성 직물은 서로 연결되어 있고 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는 적어도 하나의 광활성제를 포함한다.
본 발명의 내용 중에 포함되어 있다.
도 1a 내지 1c. 도 1a는 본 발명의 광활성 섬유의 제조에 사용된 압출기 공정의 개략도를 도시한다. 도 1b는 본 발명의 일 실시예에 따른 압출 공정에 의해 제조된 섬유들의 횡단면도를 도시한다 (도 1b는 섬유의 코어를 보여준다). 도 1c는 본 발명의 다른 실시예에 따른 압출 공정에 의해 제조된 섬유의 횡단면도를 도시하고, 이때 섬유는 덮개와 코어를 가진다.
도 2a 내지 2d는 나일론 섬유 (도 2a), PBT 섬유 (도 2b) 및 PMMA 섬유 (도 2c)에 존재하는 광활성제의 시간경과에 따른 형광 방출을 나타내는 그래프를 도시한다. 도 2d는 광활성제의 시간 경과에 따른 형광 방출에 대한 시험된 중합체들의 효과를 비교하는 그래프를 도시한다.
도 3은 본 발명의 일 실시예에 따른 표시된 광활성 섬유들 밖으로의 에오신의 누출을 비교하는 그래프를 도시한다.
도 4는 용액 중의 에오신 Y에 의한 형광 방출에 윤활제의 첨가가 미치는 효과를 나타내는 그래프를 도시한다.
도 5a 및 5b. 도 5a는 상이한 농도의 에오신 Y의 형광 방출에 대한 윤활제의 존재의 효과를 나타내는 그래프를 도시한다. 도 5b는 에오신 Y의 형광 방출에 대한 윤활제의 존재의 효과를 플루오레세인의 형광 방출에 대한 윤활제의 존재의 효과와 비교하는 그래프를 도시한다.
도 6a 및 6b. 도 6a는 표면에 2, 4 또는 6 층의 에오신:플루오레세인 조성물을 가지는 본 발명에 따른 광활성 폴리프로필렌 섬유의 시간 경과에 따른 형광 방출을 비교하는 그래프를 도시한다. 도 6b는 표면에 2, 4 또는 6층의 플루오레세인 조성물을 가지는 본 발명의 실시예에 따른 광활성 나일론 섬유의 시간 경과에 따른 형광 방출을 비교하는 그래프를 도시한다.
도 7은 광활성 나일론 섬유의 안쪽에 (내부) 또는 표면에 (외부) 존재하는 광활성제를 가지는 본 발명의 일 실시예에 따른 광활성 나일론 섬유의 시간 경과에 따른 형광 방출을 비교하는 그래프를 도시한다.
도 8a 내지 8f는 에오신 Y의 용액에 침지된 (0.1g/L) 본 발명의 일 실시예에 따른 광활성 폴리프로필렌 섬유의 형광 방출 사진들을 도시한다. 도 8a 및 8b는 1일 후 청색 램프 아래에서의 형광 방출을 도시하며, 이때 섬유는 물에서 드러나지 않았다. 도 8c 및 8d는 3일 후 청색 램프 아래에서의 형광 방출을 도시하며, 이때 섬유는 물에서 드러나지 않았다 도 8e 및 8f는 물에서 드러난 3일 후 청색 램프 아래에서의 형광 방출을 도시한다.
도 9a 내지 9p는 광활성제 용액에 침지된 섬유들, 즉 에오신 Y 50g/L 중의 시판중인 치섬유 (dental fibers) (도 9a 및 9b); 에오신 Y 0.1g/L 중의 시판중인 치섬유 (도 9c및 9d); 플루오레세인 50g/L 중의 시판중인 치섬유 (도 9e 및 19f); 플루오레세인 0.1g/L 중의 시판중인 치섬유 (도 9g 및 9h); 플루오레세인:에오신 Y 50g/L 중의 시판중인 치섬유 (도 9i 및 9j); 플루오레세인:에오신 Y 0.1g/L 중의 시판중인 치섬유 (도 9k 및 9l); 플루오레세인 50g/L 중의 폴리프로필렌 섬유 (도 9m 및 9n); 및 플루오레세인 0.1g/L 중의 폴리프로필렌 섬유 (도 9o 및 9p)의 청색 램프 아래에서의 형광 방출 사진들을 도시한다.
도 10은 본 발명의 일 실시예에 따른 광활성 직물들의 제조 공정의 개략도를 도시한다.
도 11a 및 11b. 도 11a는 본 발명의 일 실시예에 따른, 수트-형 의상의 발생시, 제조 물품의 개략도를 도시한다. 도 11b는 본 발명의 일 실시예에 따른 광활성 직물로 제조된 수트-형 의상의 사진을 도시한다.
다양한 측면에서, 본 발명은 광활성제를 포함하는 섬유 및 직물 매질, 및 광활성제의 광활성화에 의해 광활성화될 수 있는 섬유 및 직물 매질에 관한 것이다. 일부 경우에, 섬유 및 직물 매질은 표면 상에 존재하는 광활성제를 갖는다 (예를 들어, 섬유/직물이 광활성제로 코팅 또는 분무되거나 섬유/직물이 광활성제를 포함하는 조성물 또는 제제에 침지된다). 다른 경우에, 광활성제는 섬유를 만드는 물질 내로 혼입된다 (예를 들어, 광활성제가 섬유를 만드는 물질과 혼합/화합된다). 일부 다른 구현예에서, 광활성제는 섬유/직물의 표면 모두 위에 존재하고 섬유를 만드는 물질 내로 혼입/화합된다.
일부 경우에, 섬유는 합성 섬유, 천연 섬유 및 텍스타일 섬유를 포함하지만 이에 한정되지는 않는다. 예를 들어, 합성 섬유는 중합체 또는 상이한 중합체들의 조합으로 제조될 수도 있다. 일부 경우에, 중합체는 열가소성 중합체이다.
본원에 사용된 바와 같이, "섬유"라는 용어는 복합 재료의 구성요소로 사용되는 스트링 또는 실 또는 필라멘트에 관한 것이다. 섬유는 예를 들어 직물에 국한되지 않는 다른 물질의 제조에 사용될 수도 있다.
일부 경우에, 중합체는 아크릴, 아크릴로니트릴 부타디엔 스티렌 (ABS), 폴리벤즈이미다졸 (PBI), 폴리카보네이트, 폴리에테르 술폰 (PES), 폴리에테르에테르 케톤 (PEEK), 폴리에테르이미드 (PEI), 폴리에틸렌 (PE), 폴리페닐렌 옥사이드 (PPO), 폴리페닐렌 설파이드 (PPS), 폴리프로필렌 (PP), 폴리스티렌, 폴리 염화비닐 (PVC), 테플론, 폴리부틸렌, 폴리에틸렌 테레프탈레이트 (PET), 폴리부틸렌 테레프탈레이트 (PBT), 나일론, 폴리락트산 (PLA), 폴리메틸 메타크릴레이트 폴리에스테르, 폴리우레탄, 레이온, 폴리(메틸 메타크릴레이트) (PMMA), 또는 이들의 임의의 혼합물이다.
일부의 다른 예에서, 섬유는 글리콜산, 공중합체 락타이드/글리콜라이드, 폴리에스테르 중합체, 공중합체 폴리글리콜산/트리메틸렌 카보네이트, 천연 단백질 섬유, 셀룰로오스 섬유, 폴리아미드 중합체, 폴리프로필렌의 중합체, 폴리에틸렌의 중합체, 나일론, 폴리락트산의 중합체, 폴리부틸렌 테레프탈레이트의 중합체, 폴리에스테르, 공중합체 폴리글리콜, 폴리부틸렌, 폴리 메틸 메타크릴레이트의 중합체, 또는 이들의 임의의 혼합물로부터 만들어질 수도 있다.
일부 구현예에서, 본 발명의 섬유는 섬유를 형성하는 두 개의 별개의 중합체를, 보통 코어-외피 또는 나란한 배열로 가지는 공압출 섬유일 수도 있다.
일부 구현예에서, 섬유는 단일 가닥(모노-필라멘트)로 구성될 수도 있고 복수의 가닥(멀티-필라멘트)로 구성될 수도 있다. 멀티 필라멘트인 광활성 섬유(photoactivatable fiber)는 또한 얽히거나 또는 편조되거나 꼬여질 수도 있다 (즉, 멀티 필라멘트가 얽히고, 편조되거나 또는 꼬여져서 섬유를 형성한다).
일부 구현예에서, 본원에서 정의된 광활성 섬유(개별적으로 취함, 모노필라멘트)의 직경은 약 15 내지 약 500㎛, 약 25㎛ 내지 약 500㎛, 약 50㎛ 내지 400㎛, 약 50㎛ 내지 약 300㎛, 바람직하게는 약 50㎛ 내지 약 250㎛, 바람직하게는 약 75㎛ 내지 약 300㎛, 가장 바람직하게는 약 75㎛ 내지 약 250㎛ 사이에서 다양하다. 일부 구현예에서, 본원에서 정의된 광활성 섬유의 직경은 약 15㎛, 약 20㎛, 약 25㎛, 약 50㎛, 약 75㎛, 약 100㎛, 약 125㎛, 약 150㎛, 약 175㎛, 약 200㎛, 약 225㎛, 약 250㎛, 약 250㎛, 약 275㎛, 약 300㎛, 약 325㎛, 약 350㎛, 약 375㎛, 약 400㎛, 약 425㎛, 약 450㎛, 약 475㎛, 약 500㎛이다. 일부 경우에, 본원에서 정의된 광활성 섬유(개별적으로 취함)의 직경은 약 31㎛이다.
일부 구현예에서, 본원에서 정의된 광활성 섬유는 기계적 견인력 및 신장력에 대한 중간 내지 높은 저항을 나타낸다. 일부 구현예에서, 본원에서 정의된 광활성 섬유는 탄력성이 있으며, 원래의 크기 및 형상으로 신장 및 재형성할 수 있다.
일부 구현예에서, 광활성 섬유는 약 400 내지 약 480 데니어, 약 410 내지 약 470 데니어, 약 420 내지 약 460 데니어, 약 420 및 약 450 데니어 또는 약 428 데니어의 선형 질량 밀도를 가진다. 본원에서 사용된 바와 같이, 용어 "데니어"는 섬유의 선형 질량 밀도에 대한 측정 단위를 지칭하며, 9000 미터 당 질량으로 정의된다.
일부 구현예에서, 본원에서 정의된 섬유는 그 길이 및 유연성 및 권취성 정도를 유지한다. 다른 구현에서, 스트레치 섬유는 감기 및 풀기 공정으로 인해 섬유에 손상을 입히지 않고 감기거나 풀리도록 윤활될 수도 있다. 일부 예에서, 섬유는 원래 직경의 적어도 반, 1/3, 1/4, 1/5, 1/6, 1/7, 1/8, 1/9 또는 1/10의 최소 직경에 도달하도록 섬유가 신장될 수 있게 하는 인장 강도를 갖는다.
도 1a는 본 발명의 일 실시예에 따른 광활성 섬유를 제조하기 위한 공정의 일례의 개략도이다. 이 예에서, 압출 공정이 사용되며, 여기서 중합체 펠릿이 용융 및 압출되고 이어서 여전히 뜨거울 때 섬유로 인출된다. 이 공정 도중에 물과 기름 속의 광활성제 용액이 여전히 뜨거울 때 중합체 상으로 분무된다. 그런 다음 섬유는 보관 및 사용 편의를 위한 보빈 상으로 방사된다. 일부 경우에, 본 발명의 광활성 섬유는 TEM 동시 회전식 트윈 스크류 압출기를 사용하여 제조된다.
일부 구현예에서, 광활성제는 광에 노출될 때 광여기되고 나서 그 에너지를 다른 분자로 전달하거나 예를 들어 형광과 같이 광으로서 방출할 수 있는 화학 화합물이다. 예를 들어, 일부 경우에, 광활성제는 광에 의해 광여기될 때 광 분산을 강화 또는 가속시키기 위해 그 에너지를 전달할 수 있거나 산소 라디칼을 방출하기 위해 산화제와 같은 다른 분자에 전달할 수도 있다. 광활성제의 예로는 형광 화합물 (또는 얼룩) ("형광크롬" 또는 "형광단" 또는 "발색단"으로도 알려져 있음)이 있으나 이에 한정되지는 않는다. 기타 염료 그룹 또는 염료들(생물학적이고 조직학적인 염료, 식용 착색제, 카로티노이드류 및 기타 염료)이 사용될 수도 있다. 적절한 광 활성제는 일반적으로 안전하다고 인정되는 물질(Generally Regarded As Safe; GRAS)일 수 있다.
특정 구현예에서, 본 발명의 광활성 섬유는 제1 광활성제(photoactivatable agent)를 포함한다. 일부 구현예에서, 제1 광활성제는 예를 들어 약 380nm 내지 약 800nm, 약 380nm 내지 약 700, 약 400nm 내지 약 800, 또는 약 380nm 내지 약 600nm인 파장과 같은, 가시 스펙트럼의 범위에서의 파장에서 흡수한다. 다른 실시예에서, 제1 광활성제는 약 200nm 내지 약 800nm, 약 200nm 내지 약 700nm, 약 200nm 내지 약 600nm, 또는 약 200nm 내지 약 500nm인 파장에서 흡수한다. 일 실시예에서, 상기 제1 광활성제는 약 200nm 내지 약 600nm의 파장에서 흡수한다. 일부 실시예에서, 상기 제1 광활성제는 약 200nm 내지 약 300nm, 약 250nm 내지 약 350nm, 약 300nm 내지 약 400nm, 약 350nm 내지 약 450nm, 약 400nm 내지 약 500nm, 약 450nm 내지 약 650nm, 약 600nm 내지 약 700nm, 약 650nm 내지 약 750nm 또는 약 700nm 내지 약 800nm의 파장에서 흡수한다.
일부 구현예에서, 광활성제는 약 400nm 내지 약 800nm 범위 이내인 광을 방출한다.
본원에 개시된 광활성 섬유들은 적어도 하나의 추가의 광활성제를 포함할 수 있다. 광활성제 조합은 조합된 염료 분자들에 의해 광 흡수를 증가시키고 흡수 및 광-생물조절 선택성을 향상시킬 수도 있다. 그러므로, 특정 실시예에서, 본 발명의 광활성 섬유는 하나 이상의 광활성제를 포함한다.
광활성 섬유들이 표면 (즉 섬유의 주변 환경과 접촉하는 섬유들의 표면)에 광활성화제를 가지는 경우의 구현예에서, 이러한 광활성 섬유들은 하나 이상의 광활성제 및 담체 물질, 예컨대 그것에 한정되는 것은 아니지만 물을 포함하는 광활성제 조성물에 침지됨으로써 제조될 수 있다.
광활성 섬유들이 표면 (즉 섬유의 주변 환경과 접촉하는 섬유들의 표면)에 광활성제를 가지는 경우의 다른 구현예에서, 이러한 광활성 섬유들은 하나 이상의 광활성제 및 담체 물질을 포함하는 광활성제 조성물로 분무됨으로써 제조될 수 있다.
일부 구체적인 예에서, 광활성제 조성물은 섬유가 그 조성물에 침지되는 것을 허용하는 농도를 가진다. 일부 구체적인 실시예에서, 광활성제 조성물은 액체 또는 반-액체 형태로 존재한다.
담체 물질은 광활성제의 광활성 특성에 영향을 미치지 않는 임의의 물질인, 광활성제와 부합하는 임의의 액체 또는 반 액체 물질, 예컨대, 예를 들면 물일 수 있다. 일부 다른 구체적인 실시예에서, 광활성제 조성물은 광활성제 조성물이 섬유 위로 분무되는 것을 허용하는 농도를 가진다.
광활성 섬유들이 섬유 안으로 통합된 광활성제를 가지는 경우의 구현예에서, 광활성 섬유들은 광활성제를 섬유 조성물에 통합시킴으로써 제조된다. 일부 실시예에서, 광활성 섬유들은 압출에 의해 제조된다. 일부 구체적인 구현예에서, 광활성 섬유들은 방적을 사용하는 공정에 의해 제조된다. 방적은 습식, 건식, 건식 제트-습식, 용융, 겔 또는 전기 방적일 수 있다. 방적되는 중합체는 유체 상태로 전환될 수 있다. 만약 중합체가 열가소성이면 용융될 수 있고, 그렇지 않으면 용매에 녹거나 또는 화학적으로 처리되어 가용성 또는 열가소성 유도체를 형성할 수 있다. 그런 다음 용융 중합체는 방적돌기를 통해 가압되고, 그런 후 고무 상태로, 그런 다음에는 고체 상태로 냉각된다. 만약 중합체 용액이 사용된다면, 용매는 방적돌기를 통해 가압된 후에 제거된다. 광활성제의 조성물은 유체 상태로 또는 용융 중합체에 또는 용매에 녹아 있는 중합체에 첨가될 수 있다. 용융 방적은 용융될 수 있는 중합체에 사용될 수 있다. 그 안에 분산되어 있는 광활성제를 가진 중합체는 방적돌기로부터 압출된 후에 냉각시킴으로써 굳어진다.
광활성제는 광활성 섬유 내에 균일하게 또는 균일하지 않게 분포될 수 있다. 광활성 성분이 광활성 섬유들에 균일하게 분포된 때, 광활성 섬유들 중의 광활성제의 농도는 광활성 섬유들이 분해됨에 따라 꾸준한 한편, 광활성제가 광활성 섬유들에 균일하지 않게 분포된 때, 광활성 섬유들 중의 광활성제의 농도는 광활성 섬유들이 분해됨에 따라 달라진다.
사용될 광활성제의 농도는 광활성 섬유로부터의 방출될 광활성에 대해 원하는 강도 및 지속 시간에 기초하여 선택하고, 원하는 생체 치료, 의료 또는 미용 효과에 기초하여 선택할 수 있다. 예를 들면, 크산텐 염료 등의 일부 염료는, 이후에 추가 농도 증가가 실질적으로 더 높은 방출된 형광을 제공하지 않는, '포화 농도'에 도달한다. 또한 포화 농도 위로 광활성제 농도 증가로 인해 광활성 섬유를 통과하는 광을 활성화하는 양을 줄일 수 있다. 따라서, 더 많은 형광이 광을 활성화하는 것보다 특정한 적용분야에 필요한 경우, 광활성제의 높은 농도가 사용될 수 있다. 하지만, 방출된 형광 및 활성화 광 사이에 균형이 필요한 경우, 포화 농도에 가깝거나 그보다 낮은 농도가 선택될 수 있다.
본 발명의 광활성 섬유에 사용될 수 있는 적합한 광활성제로는 하기의 것들이 있지만, 이에 한정되지 않는다:
클로로필 염료 - 클로로필 염료는 클로로필 a; 클로로필 b; 클로로필린; 박테리오클로로필 a; 박테리오클로로필 b; 박테리오클로로필 c; 박테리오클로로필 d; 프로토클로로필; 프로토클로로필 a; 양친매성 클로로필 유도체 1; 및 양친매성 클로로필 유도체 2를 포함하나, 이들로 제한되지 않는다.
크산텐 유도체 - 크산텐 염료는 에오신, 에오신 B (4',5'-디브로모,2',7'-디니트로-플루오레세인, 2음이온); 에오신 Y; 에오신 Y (2',4',5',7'-테트라브로모-플루오레세인, 2음이온); 에오신 (2',4',5',7'-테트라브로모-플루오레세인, 2음이온); 에오신 (2',4',5',7'-테트라브로모-플루오레세인, 2음이온) 메틸 에스테르; 에오신 (2',4',5',7'-테트라브로모-플루오레세인, 1음이온) p-이소프로필벤질 에스테르; 에오신 유도체 (2',7'-디브로모-플루오레세인, 2음이온); 에오신 유도체 (4',5'-디브로모-플루오레세인, 2음이온); 에오신 유도체 (2',7'-디클로로-플루오레세인, 2음이온); 에오신 유도체 (4',5'-디클로로-플루오레세인, 2음이온); 에오신 유도체 (2',7'-디요오도-플루오레세인, 2음이온); 에오신 유도체 (4',5'-디요오도-플루오레세인, 2음이온); 에오신 유도체 (트리브로모-플루오레세인, 2음이온); 에오신 유도체 (2',4',5',7'-테트라클로로-플루오레세인, 2음이온); 에오신 디세틸피리디늄 클로라이드 이온쌍; 에리트로신 B (2',4',5',7'-테트라요오도-플루오레세인, 2음이온); 에리트로신; 에리트로신 2음이온; 에리트로신 B; 플루오레세인; 플루오레세인 2음이온; 플록신 B (2',4',5',7'-테트라브로모-3,4,5,6-테트라클로로-플루오레세인, 2음이온); 플록신 B (테트라클로로-테트라브로모-플루오레세인); 플록신 B; 로즈 벵갈 (3,4,5,6-테트라클로로-2',4',5',7'-테트라요오도플루오레세인, 2음이온); 피로닌 G, 피로닌 J, 피로닌 Y; 4,5-디브로모-로다민 메틸 에스테르; 4,5-디브로모-로다민 n-부틸 에스테르; 로다민 101 메틸 에스테르; 로다민 123; 로다민 6G; 로다민 6G 헥실 에스테르; 테트라브로모-로다민 123; 및 테트라메틸-로다민 에틸 에스테르를 포함하는 로다민과 같은 로다민 염료를 포함하나, 이들로 제한되지 않는다.
메틸렌 블루 염료 - 메틸렌 블루 유도체는 1-메틸 메틸렌 블루; 1,9-디메틸 메틸렌 블루; 메틸렌 블루; 메틸렌 블루(16 μM); 메틸렌 블루 (14 μM); 메틸렌 바이올렛; 브로모메틸렌 바이올렛; 4-요오도메틸렌 바이올렛; 1,9-디메틸-3-디메틸-아미노-7-디에틸-아미노-페노티아진; 및 1,9-디메틸-3-디에틸아미노-7-디부틸-아미노-페노티아진을 포함하나, 이들로 제한되지 않는다.
아조 염료 - 아조 (또는 디아조-) 염료는 메틸 바이올렛, 뉴트럴 레드, 파라 레드(피그먼트 레드 1), 아마란스 (아조루빈 S), 카르모이신 (아조루빈, 식용 적색 3호, 애시드 레드 14), 알루라 레드 AC(FD&C 40), 타르트라진 (FD&C 황색 5호), 오렌지 G (애시드 오렌지 10), 폰소 4R(식용 적색 7호), 메틸 레드(애시드 레드 2), 및 무렉시드-푸르푸르산 암모늄을 포함하나, 이들로 제한되지 않는다.
본 발명의 몇몇 측면에서, 본원에 개시된 광활성 섬유의 하나 이상의 광활성제는 애시드 블랙 1, 애시드 블루 22, 애시드 블루 93, 애시드 푹신(Acid fuchsin), 애시드 그린, 애시드 그린 1, 애시드 그린 5, 애시드 마젠타(Acid magenta), 애시드 오렌지 10, 애시드 레드 26, 애시드 레드 29, 애시드 레드 44, 애시드 레드 51, 애시드 레드 66, 애시드 레드 87, 애시드 레드 91, 애시드 레드 92, 애시드 레드 94, 애시드 레드 101, 애시드 레드 103, 애시드 로제인(Acid roseine), 애시드 루빈(Acid rubin), 애시드 바이올렛 19, 애시드 옐로우 1, 애시드 옐로우 9, 애시드 옐로우 23, 애시드 옐로우 24, 애시드 옐로우 36, 애시드 옐로우 73, 애시드 옐로우 S, 아크리딘 오렌지, 아크리플라빈(Acriflavine), 알시안 블루(Alcian blue), 알시안 옐로우, 알코올 용해성 에오신, 알리자린(Alizarin), 알리자린 블루 2RC, 알리자린 카르민, 알리자린 시아닌 BBS, 알리자롤 시아닌(Alizarol cyanin) R, 알리자린 적색 S, 알리자린 퍼퓨린(Alizarin purpurin), 알루미논(Aluminon), 아미도 블랙 10B, 아미도슈워즈(Amidoschwarz), 아닐린 블루 WS, 안트라센 블루 SWR, 아우라민(Auramine) O, 아조카민(Azocarmine) B, 아조카민 G, 아조익 디아조 5, 아조익 디아조 48, 아주어(Azure) A, 아주어 B, 아주어 C, 베이직 블루 8, 베이직 블루 9, 베이직 블루 12, 베이직 블루 15, 베이직 블루 17, 베이직 블루 20, 베이직 블루 26, 베이직 브라운 1, 베이직 푹신, 베이직 그린 4, 베이직 오렌지 14, 베이직 레드 2, 베이직 레드 5, 베이직 레드 9, 베이직 바이올렛 2, 베이직 바이올렛 3, 베이직 바이올렛 4, 베이직 바이올렛 10, 베이직 바이올렛 14, 베이직 옐로우 1, 베이직 옐로우 2, 비브리히 스칼렛(Biebrich scarlet), 비스마르크 브라운(Bismarkck brown) Y, 브릴리언트 크리스탈 스칼렛(Brilliant crystla scarlet) 6R, 칼슘 레드, 카르민(Carmine), 카르민산, 셀레스틴 블루(Celestine blue) B, 차이나 블루(China blue), 코치닐(Cochineal), 코엘레스틴 블루(Coelestine blue), 크롬 바이올렛 CG, 크로모트로프(Chromotrope) 2R, 크로목산 시아닌(Chromoxane cyanin) R, 콩고 코린트(Congo corinth), 콩고 레드, 코튼 블루, 코튼 레드, 크로세인 스칼렛(Croceine scarlet), 크로신(Crocin), 크리스탈 폰소 6R, 크리스탈 바이올렛, 달리아(Dahlia), 다이아몬드 그린 B, 다이렉트 블루 14, 다이렉트 블루 58, 다이렉트 레드, 다이렉트 레드 10, 다이렉트 레드 28, 다이렉트 레드 80, 다이렉트 옐로우 7, 에오신 B, 에오신 블루이쉬(Eosin Bluish), 에오신, 에오신 Y, 에오신 옐로위쉬(Eosin yellowish), 에오신올(Eosinol), 이리 가넷(Erie garnet) B, 에리오크롬 시아닌(Eriochrome cyanin) R, 에리트로신 B, 에틸 에오신, 에틸 녹색, 에틸 바이올렛, 에반스 블루(Evans blue), 패스트 블루(Fast blue) B, 패스트 그린 FCF, 패스트 레드 B, 패스트 옐로우, 플루오레세인, 식용 녹색 3, 갈레인(Gallein), 갈라민 블루(Gallamine blue), 갈로시아닌(Gallocyanin), 겐티안 바이올렛(Gentian violet), 헤마테인(Haematein), 헤마틴(Haematine), 헤마톡실린(Haematoxylin), 헬리오 패스트 루빈(Helio fast rubin) BBL, 헬베티아 블루(Helvetia blue), 헤마테인(Hematein), 헤마틴(Hematine), 헤마톡실린(Hematoxylin), 호프만 바이올렛(Hoffman's violet), 임페리얼 레드(Imperial red), 인도시아닌 녹색(Indocyanin green), 인그레인 블루(Ingrain blue), 인그레인 블루 1, 인그레인 옐로우 1, INT, 커메즈(Kermes), 커메직산(Kermesic acid), 커네크트로트(Kernechtrot), 랙(Lac), 랙카인산(Laccaic acid), 라우쓰 바이올렛(Lauth's violet), 라이트 그린, 리사민 그린(Lissamine green) SF, 룩솔 패스트 블루(Luxol fast blue), 마젠타 0, 마젠타 I, 마젠타 II, 마젠타 III, 말라카이트 그린(Malachite green), 맨체스터 브라운(Manchester brown), 마티우스 옐로우(martius yellow), 메르브로민(Merbromin), 머큐로크롬(Mercurochrome), 메타닐 옐로우(Metanil yellow), 메틸렌 아주어 A, 메틸렌 아주어 B, 메틸렌 아주어 C, 메틸렌 블루, 메틸 블루, 메틸 녹색, 메틸 바이올렛, 메틸 바이올렛 2B, 메틸 바이올렛 10B, 모던트 블루(Mordant blue) 3, 모던트 블루 10, 모던트 블루 14, 모던트 블루 23, 모던트 블루 32, 모던트 블루 45, 모던트 레드 3, 모던트 레드 11, 모던트 바이올렛 25, 모던트 바이올렛 39, 나프톨 블루 블랙(Naphthol blue black), 나프톨 그린 B, 나프톨 옐로우 S, 내츄럴 블랙 1, 내츄럴 그린 3(클로로필린), 내츄럴 레드, 내츄럴 레드 3, 내츄럴 레드 4, 내츄럴 레드 8, 내츄럴 레드 16, 내츄럴 레드 25, 내츄럴 레드 28, 내츄럴 옐로우 6, NBT, 뉴츄럴 레드, 뉴 푹신(New fuchsin), 니아가라 블루(Niagara blue) 3B, 나이트 블루, 나일 블루(Nile blue), 나일 블루 A, 나일 블루 옥사존(oxazone), 나일 블루 설페이트, 나일 레드, 니트로 BT, 니트로 블루 테트라졸륨, 뉴클리어 패스트 레드(Nuclear fast red), 오일 레드 O, 오렌지 G, 오르세인(Orcein), 파라로사닐린(Pararosanilin), 플록신 B, 피크르산(Picric acid), 폰소 2R, 폰소 6R, 폰소 B, 폰소 데 크실리딘(Ponceau de Xylidine), 폰소 S, 프리뮬러(Primula), 퍼퓨린, 피로닌(Pyronin) B, 피코빌린류, 피코시아닌(Phycocyanin)류, 피코에리트린(Phycoerythrin)류. 피코에리트린시아닌 (PEC), 프탈로시아닌류, 피로닌 G, 피로닌 Y, 퀴닌(Quinine), 로다민 B, 로사닐린, 로즈 벵갈, 샤프론, 사프라닌(Safranin) O, 스칼렛 R, 스칼렛 레드, 샤라크(Scharlach) R, 쉘락(Shellac), 시리우스 레드(Sirius red) F3B, 솔로크롬 시아닌(Solochrome cyanin) R, 솔루블 블루(Soluble blue), 솔벤트 블랙 3, 솔벤트 블루 38, 솔벤트 레드 23, 솔벤트 레드 24, 솔벤트 레드 27, 솔벤트 레드 45, 솔벤트 옐로우 94, 주정용 에오신(Spirit soluble eosin), 수단(Sudan) III, 수단 IV, 수단 블랙 B, 설퍼 옐로우(Sulfur yellow) S, 스위스 블루(Swiss blue), 테트라진, 티오플라빈(Thioflavine) S, 티오플라빈 T, 티오닌(Thionin), 톨루이딘 블루(Toluidine blue), 톨루일린 레드, 트로페올린(Tropaeolin) G, 트리파플라빈(Trypaflavine), 트리판 블루(Trypan blue), 우라닌(Uranin), 빅토리아 블루(Victoria blue) 4R, 빅토리아 블루 B, 빅토리아 그린 B, 비타민 B, 워터 블루(Water blue) I, 수용성 에오신, 크실리딘 폰소, 또는 옐로위쉬 에오신(Yellowish eosin) 중 임의의 것으로부터 독립적으로 선택될 수 있다.
소정의 실시예들에서, 본 발명의 광활성 섬유는 생체 광자성 상승 효과를 제공하도록, 상기에서 나열된 임의의 광활성제, 또는 이의 조합을 포함할 수도 있다. 예를 들어, 광활성제의 하기 상승적 조합이 사용될 수도 있다: 에오신 Y 및 플루오레세인; 플루오레세인 및 로즈 벵갈; 에오신 Y, 로즈 벵갈 또는 플루오레세인과 함께 에리트로신; 에오신 Y, 로즈 벵갈, 플루오레세인 및 에리트로신 중 하나 이상과 함께 플록신 B; 에오신 Y, 플루오레세인 및 로즈 벵갈.
일부 예에서, 광활성제는 전체 부피의 약 100g/L, 약 50g/L, 약 10g/L, 약 5g/L, 약 1g/L 또는 약 0.1g/L의 농도로 광활성제 조성물에 존재한다. 바람직하게는, 광활성제는 약 10g/L 내지 약 100g/L의 농도로 광활성제 조성물에 존재한다. 일부 예에서, 광활성제는 0.1g/L 미만의 농도로 광활성제 조성물에 존재하며, 예를 들어, 광활성제는 mg/L의 농도 또는 ㎍/L 농도로 광활성제 조성물에 존재한다.
일부 실시예에서, 본 발명의 광활성 섬유는 윤활제를 포함한다. 일부 예에서, 윤활제는 본 발명의 광활성 섬유 상에 코팅된다. 일부 예에서, 윤활제는 Lurol Oil™과 같은 처리제 오일이지만, 이제 한정되지 않는다. 이론에 구속되고자 하지 않고, 섬유의 표면에 윤활제를 첨가하면 섬유 상으로 광활성제의 조성물의 보유가 개선된다. 예를 들어, 윤활제는 중합체의 친수성을 향상시켜 광활성제 용액의 흡수를 증가시킨다.
일부 구현예에서, 본 발명의 광활성 섬유 밖으로 광활성제의 약 15% 미만, 더욱 바람직하게는 10% 미만, 더욱 바람직하게는 5% 미만, 더욱 바람직하게는 4% 미만, 더욱 바람직하게는 3% 미만, 더욱 바람직하게는 2% 미만, 더욱 바람직하게는 1% 미만의 누출이 있으며, 또는 더욱 더 바람직하게는 광활성 섬유 밖으로 광활성제의 누출이 사실상 없다. 본 발명의 광활성 섬유 밖으로 광활성제의 누출은 0.1g의 광활성 섬유를 10ml의 물에 1일 동안 놓은 다음 물 속의 광활성제의 양을 측정함으로써 평가할 수도 있다.
일부 구현예에서, 본원에서 정의된 광활성 섬유들은 직물 물질로 짜여져서 복수의 광활성 섬유들을 포함하는 광활성 직물이 생성될 수 있다. 일부 구현예에서, 광활성 섬유들을 포함하는 광활성 직물은 실질적으로 광활성제의 누출을 나타내지 않는다.
본원에서 사용되는 용어 "직물"은 섬유들의 네트워크로 구성된 직조된 물질 또는 섬유들로 구성된 부직포 (예컨대 스펀본드 (spunbound)) 물질을 나타낸다. 위빙은 두 개의 구별되는 세트의 원사 또는 실이 직각으로 꼬아져서 직물 또는 천이 형성되는 옷감의 제조 방법이다. 유사한 공정은 편직(knitting), 펠팅 (felting) 및 편조(braiding) 또는 땋기(plaiting)이다. 부직포 직물은 섬유 또는 필라멘트를 기계적으로, 열적으로 또는 화학적으로 얽음으로써 함께 결합되어 있는 시트 또는 웹 구조로서 광범위하게 정의된다. 그것들은 별도의 섬유, 용융 플라스틱 또는 플라스틱 필름으로부터 직접 만들어진 평평한 또는 촘촘한 다공성 시트이다. 그것들은 위빙이나 편직에 의해 제조되지 않고 섬유를 원사로 전환시킬 필요가 없다.
일부 예에서, 직물 물질은 예컨대, 그것들에 한정되는 것은 아니지만, 의상, 의류, 상처용 드레싱, 타월, 침구 등과 같은 제조 물품의 제작에 사용될 수 있다. 일부 구현예에서, 의상은 셔츠, 바지, 장갑, 마스크, 양말 등일 수 있다. 일부 경우에, 본 발명의 광활성 섬유들은 수트 또는 수트-형 의상인 직물 물질로 직조된다.
광활성제가 섬유들의 중합체와 합성되는 구현예에서, 이러한 섬유로부터 만들어진 직물 또한 광활성이다. 반면 광활성제가 섬유들의 중합체와 합성되지 않는 구현예에서, 이러한 섬유들로부터 만들어진 직물은 직물을 광활성으로 만들기 위해 광활성제 조성물로 코팅되거나 침지되거나 또는 분무될 수 있다.
일부 다른 실시예에서, 광활성 직물은 그것들에 한정되는 것은 아니지만 스펀본드 직물과 같은 부직포 광활성 직물일 수 있다. 스펀본드 직물은 압출된, 방적 필라멘트를 수집 벨트 상에 균일한 무작위 방식으로 놓고 이어서 섬유들을 결합시킴으로써 제조될 수 있다. 섬유들은 공기 분사 또는 정전기 교환에 의해 웹 레잉 공정 중에 분리될 수 있다. 수집 표면은 통상적으로 섬유를 조절되지 않은 방식으로 편향시키고 이동시킴으로써 기류가 발생하는 것을 방지하기 위하여 천공되어 있다. 결합은 가열된 롤 또는 고온 바늘을 부분적으로 용융된 중합체에 적용하고 섬유들을 함께 융합시킴으로써 웹에 강도 및 무결성을 제공한다. 일반적으로, 고분자량 및 넓은 분자량 분포를 가진 중합체, 예컨대, 그것들에 한정되는 것은 아니지만, 폴리프로필렌, 폴리에스테르, 폴리에틸렌, 폴리에틸렌 테레프탈레이트, 나일론, 폴리우레탄 및 레이온이 스펀본드 직물의 제조에 사용될 수 있다. 일부 경우에, 스펀본드 직물은 중합체들의 혼합물로 구성될 수 있다. 저융점 중합체가 고융점 섬유들과 산재된 별도의 섬유일 수 있는 결합제로서 작용할 수 있거나, 또는 두 개의 중합체가 단일 섬유 유형으로 조합될 수 있다. 후자의 경우에 소위 이중-성분 섬유들은 저융점 성분을 가지며, 그것은 고융점 코어를 덮는 덮개로서 작용한다. 이중성분 섬유들은 또한 두 개의 인접한 중합체의 압출에 의해 방적될 수 있다.
일부 경우에, 방적 결합은 결합 장치를 방적과 일직선상에 배치함으로써 섬유 방적을 웹 형성과 조합시킬 수 있다. 일부 배열에서 웹은 별도의 단계로 결합될 수 있다. 방적 공정은 연속적인 필라멘트 원사의 제조와 유사할 수 있고 주어진 중합체에 대해 유사한 압출기 조건을 이용할 수 있다. 섬유들은 방적돌기를 빠져나가서 저온 공기에 의해 급속 냉각되는 용융 중합체로서 형성된다. 공정의 목적은 와이드 웹을 제조하는 것으로, 따라서 많은 방적돌기가 전체 폭을 가로지르기에 충분한 섬유들을 생성하기 위해 나란히 배치된다.
움직이는 벨트 또는 스크린에 놓이기 전에, 방적돌기의 생산량은 보통 섬유 강도를 증가시키고 신장성을 감소시키기 위하여 섬유들 내에서 분자 사슬을 지향하도록 약화되어야 하는 복수의 개별적인 필라멘트를 포함한다. 이것은 방적돌기를 빠져나온 직후에 플라스틱 섬유들을 신속하게 연신시킴으로써 이루어진다. 실제로 섬유들은 기계적으로 또는 공압식으로 가속된다. 웹은 이동하는 벨트 위로의 필라멘트 번들의 공압 증착에 의해 형성된다. 공압 건(gun)은 제한된 저압 영역을 통하여 필라멘트를 이동시키기 위하여 고압 공기, 그러나 벤튜리관에서와 같은 고속을 사용한다. 웹이 최대 균일성 및 커버를 이루기 위해서는, 개별적인 필라멘트가 벨트에 도달하기 전에 분리된다. 이것은 정전기 전하를 번들 위에, 한편으로는 장력 하에 및 증착 전에 유도함으로써 이루어진다. 전하는 마찰 전기적으로 또는 고전압 전하를 적용함으로써 유도될 수 있다. 벨트는 통상 전기적으로 접지된 전도성 와이어로 제조된다. 증착시, 벨트는 필라멘트를 방출한다. 방적에 의해 제조된 웹은 이러한 번들 분리 장치에 대한 요구를 제거하는 소위 슬롯 다이를 통해 필라멘트를 선형으로 배열하였다.
방적 웹에서 섬유들을 결합시키기 위해 많은 방법들이 사용될 수 있다. 이것들로는 기계적 니들링, 열적 결합 및 화학적 결합을 포함한다. 마지막 두 가지는 섬유들의 융합 또는 접착에 의해 웹의 큰 영역 (구역 결합) 또는 작은 영역 (포인트 결합)을 결합시킬 수 있다. 포인트 결합은 포인트에서 섬유들의 융합을 초래하는데, 포인트 결합들 사이에 섬유가 있고 나머지는 상대적으로 비어 있다. 스테이플 섬유 웹과 함께 사용된, 그러나 관례적으로는 연속적인 필라멘트 웹과 함께 사용되지 않는 다른 방법들로는 스티치 결합, 초음파 융합 및 수압식 얽힘을 포함한다.
본 발명의 광활성 직물은 바람직하게 직물의 섬유들에 삽입된 광활성제에 광이 도달하는 것과 광활성제에 의해 방출된 광이 직물을 빠져나가는 것을 허용하는 두께를 가진다.
일부 실시예들에서, 본 발명의 광활성 섬유와 광활성 직물은 미용 및/또는 의료적 이익을 나타낼 수 있다.
이들 실시예의 일부 구현예에서, 광활성 섬유와 광활성 직물은 광선치료가 필요한 대상의 조직 및/또는 기관의 예방 및/또는 치료를 촉진하고 및/또는 조직 또는 기관을 치료하기 위하여 사용될 수 있다.
일부 경우에, 본 발명의 광활성 섬유 및/직물은 여드름, 습진, 피부염 또는 건선과 같은 피부 장애의 치료를 촉진하고, 조직 회복을 촉진하며, 염증을 조절하고, 콜라겐 합성을 조절하고, 성형술의 경우 흉터를 감소시키거나 피하고, 또는 상처 치유를 촉진하기 위해 사용될 수 있다. 그것들은 급성 염증을 치료하기 위해 사용될 수 있다. 급성 염증은 그 자체가 통증, 발열, 홍조, 부기 및 기능의 손실로서 제시할 수 있고, 예컨대 벌레 물린데 대한 반응, 예컨대 모기, 꿀벌, 말벌, 덩굴 옻나무 또는 후-삭마 (post-ablative) 치료 같은 알레르기 반응에서 볼 수 있는 것과 같은 염증성 반응을 포함한다.
특정 경우에, 본 발명의 광활성 섬유 및/직물은 피부 장애의 치료, 흉터의 예방 또는 치료, 및/또는 상처 치유 및/또는 조직 회복의 가속화를 제공할 수 있다.
소정의 실시예들에서, 광활성 섬유 또는 직물은 상처 치유를 촉진하기 위해 사용될 수 있다. 이런 경우, 광활성 섬유 또는 직물은 적절한 것으로 보이는 상처 부위에 의사 또는 다른 의료인에 의해 적용될 수 있다. 소정의 실시예들에서, 광활성 섬유 또는 직물은 흉터 교정을 최적화하기 위해 상처 봉합 이후에 사용될 수 있다. 이러한 경우, 상기 광활성 섬유 또는 직물은 1주에 1회의 규칙적인 간격, 또는 의사나 다른 건강 관리 제공자가 적절하다고 간주하는 간격으로 적용될 수 있다.
소정의 실시예들에서, 광활성 섬유 또는 직물은 치료된 피부의 상태를 유지하기 위해 여드름 치료 후에 사용될 수 있다. 이러한 경우, 상기 광활성 섬유 또는 직물은 1주에 1회의 규칙적인 간격, 또는 의사나 다른 건강 관리 제공자가 적절하다고 간주하는 간격으로 적용될 수 있다.
소정의 실시예들에서, 상기 광활성 섬유 또는 직물은 치료된 피부의 상태를 유지하기 위해 박피성 피부 치료 후에 사용될 수 있다.
본 발명의 광활성 섬유 또는 직물은 홍반, 모세혈관확장증, 광선 모세혈관확장증, 기저세포 암종, 접촉성 피부염, 융기성 피부섬유 육종증, 생식기 사마귀, 화농성 한선염, 흑색종, 메르켈 세포 암종, 화폐상 피부염, 전염성 연속증, 건선, 건선 관절염, 주사, 옴, 두피 건선, 피지성 암종, 편평상피 세포 암종, 지루성 피부염, 지루성 각화증, 대상 포진, 백선 백반, 사마귀, 피부암, 천포창, 햇볕 화상, 피부염, 습진, 발진, 농가진, 만성 단순태선, 비류, 구강 홍반, 수발가성 모낭염, 약물 발진, 다형 홍반, 홍반 결절, 환상 육아종, 광선 각화증, 자반병, 원형 탈모, 아프타 구내염, 건성 피부, 튼살, 건조증, 심상 어린증, 곰팡이 감염, 단순 포진, 간질, 켈로이드, 각화증, 비립종, 전염성 연속증, 장미색 비강증, 가려움증, 두드러기 및 혈관 종양 및 기형을 포함하지만, 이들에만 한정되지 않는 피부 질환을 치료하는 데에 이용될 수도 있다. 피부염으로는 접촉성 피부염, 아토피성 피부염, 지루성 피부염, 화폐상 피부염, 전신성 박탈 피부염(generalized exfoliative dermatitis) 및 정체 피부염(stasis dermatitis)을 들 수 있다. 피부암으로는 흑색종, 기저세포 암종, 및 편평세포 암종(squamous cell carcinoma)을 들 수 있다.
본 발명의 광활성 섬유 또는 직물은 여드름을 치료하기 위해 사용될 수 있다. 본원에서 사용된 바와 같이, "여드름"은 피부샘 또는 모낭의 염증에 의해 야기된 피부 질환을 의미한다. 본 발명의 광활성 섬유 또는 직물은 발생 초기 단계, 또는 여드름으로부터 병소가 보이는 후기 단계에 여드름을 치료하기 위해 사용될 수 있다. 경증, 중등도 및 중증 여드름은 광활성 섬유 또는 직물의 실시예들로 치료할 수 있다. 여드름의 발생 초기 단계는 일반적으로 털피지샘 기관(pilosebaceous apparatus)에 위치한 피지샘으로부터 피지 또는 진피유(dermal oil)의 과량 분비와 함께 시작한다. 피지는 모낭관을 통해 피부 표면에 도달한다. 모낭관 내 및 피부 상에 과량의 피지의 존재는 모낭관(follicular duct)으로부터의 정상적인 피지의 흐름을 차단하거나 지체하게 하는 경향이 있으며, 따라서 면포반(comedone)으로 공지된 고형 플러그(solid plug)를 생성하기 위해 피지의 농후화 및 고형화를 초래한다. 여드름이 생기는 정상적인 순서에서, 모공의 과각화(hyperkeratiniazation)가 자극되며, 따라서 모낭관의 차단을 완성한다. 일반적인 결과는 구진(papule), 농포(pustule), 또는 낭포(cyst)이며, 종종 박테리아에 의해 감염되어, 2차 감염을 야기한다. 여드름은 특히 면포반, 염증성 구진, 또는 낭포의 존재를 특징으로 한다. 여드름의 발생은 경미한 피부 자극 내지 피팅(pitting), 심지어는 흉한 흉터의 발생에 이를 수 있다. 따라서 본 발명의 광활성 섬유 또는 직물은 피부 자극, 피팅(pitting), 흉터 발생, 면포반, 염증성 구진, 낭포, 과각화, 및 여드름과 연관된 피지의 농후화 및 경화 중 하나 이상을 치료하기 위해 사용될 수 있다.
몇몇 피부 질환은 발적(redness), 홍조, 화상, 박피, 뾰루지, 구진, 농포, 면포반, 반점, 결절, 물집, 수포, 모세관 확장증, 거미 정맥, 창, 표면 자극 또는 통증, 가려움증, 염증, 적색, 자주색 또는 청색 패치(patch) 또는 변색, 사마귀(mole), 및/또는 종양을 포함한 다양한 증상을 나타낸다.
본 발명의 광활성 섬유 또는 직물은 다양한 유형의 여드름을 치료하기 위해 사용될 수 있다. 여드름의 몇몇 유형으로는, 예를 들어 심상성 여드름(acne vulgaris), 낭포성 여드름, 응괴성 여드름(acne atrophica), 브롬 여드름(bromide acne), 염소 여드름(chlorine acne), 집족성 여드름(acne conglobata), 화장품성 여드름(acne cosmetica), 세제성 여드름(acne detergicans), 전염성 여드름, 하계 여드름(acne estivalis), 전격성 여드름(acne fulminans), 할로겐 여드름, 인투라타성 여드름(acne indurata), 요오드 여드름, 켈로이드성 여드름(acne keloid), 기계적 여드름(acne mechanica), 구진성 여드름(acne papulosa), 적창(pomade acne), 월경전 여드름(premenstrual acne), 농포성 여드름(acne pustulosa), 괴혈성 여드름(acne scorbutica), 선병성 여드름(acne scrofulosorum), 두드러기성 여드름(acne urticata), 두창성 여드름(acne varioliformis), 독물성 여드름(acne venenata), 프로피온산 여드름, 찰상 여드름(acne excoriee), 그람-음성 여드름, 스테로이드성 여드름, 및 결정낭포성 여드름(nodulocystic acne)을 들 수 있다.
소정의 실시예들에서, 본 발명의 광활성 섬유 또는 직물은 전신 또는 국소 항생제 치료와 함께 사용된다. 예를 들어, 여드름 치료에 사용되는 항생제에는 테트라사이클린, 에리스로마이신, 미노사이클린, 독시사이클린이 있다. 일부 구현예에서, 본원의 광활성 직물로 구성된 제조 물품은 예를 들어 박테리아 또는 다른 감염성 약제에 의해 상처의 감염 및/또는 재-감염을 방지하기 위해 상처의 치료에 사용될 때 항-감염 효과를 가질 수도 있다.
본 발명의 광활성 섬유 또는 직물은 상처 치료, 상처 치유 촉진, 조직 수복 촉진 및/또는 운동 기능(예, 관절 운동) 개선을 비롯한 미용술 감소에 사용될 수도 있다. 본 발명의 광활성 섬유 또는 직물에 의해 치료될 수 있는 상처로는, 예를 들어 서로 상이한 방식으로 개시된 피부 및 피하 조직에 대한 부상(예를 들어, 장기 요양으로 인한 압박 궤양, 트라우마 또는 수술에 의해 유도된 상처, 화상, 당뇨병 또는 정맥 부전에 연결된 궤양)을 들 수 있으며, 상기 부상은 다양한 특징을 갖는다. 소정의 실시예들에서, 본 발명은, 예를 들어 화상, 절개, 절제, 병변, 열상, 찰과상, 천공 또는 관통창, 외과적 창상, 타박상, 혈종, 압착 손상, 총상, 창(sore) 및 궤양을 치료하고 및/또는 이들의 치유를 촉진하기 위한 광활성 섬유 또는 직물을 제공한다.
일부 실시예에서, 본 발명의 광활성 섬유 및 직물은 대상에 대해, 예컨대 대상의 조직 및/또는 기관에 대해 광선치료를 실시하는 방법에 사용될 수 있다. 이러한 방법은 본원에서 정의된 광활성 섬유 및 직물을 광선치료를 필요로 하는 대상에 또는 조직 또는 기관에 적용하는 단계 및 광활성제의 흡수 스펙트럼과 중첩하는 그것과 중첩하는 파장을 가지는 광으로 광활성 섬유 및 직물을 조사하는 단계를 포함한다.
특정 경우에, 본 발명의 광활성 섬유 및 직물은 광선치료에 및/또는 생체광자 치료에 사용될 수 있다. 특정 경우에, 본 발명의 광활성 섬유 및 직물은 생체광자 의료 장치로서 사용될 수 있다.
특정 경우에, 본 발명의 광활성 섬유 및 직물은 봉합 재료, 스텐트, 카테터, 풍선, 상처 드레싱 등과 같은 의료 장치의 제조에 사용될 수 있다. 일부 다른 실시예에서, 광활성 섬유는 칫솔, 치실, 치아 교정기 등의 제작에서와 같이 치아 보호 장치의 제작에 사용될 수 있다.
본 발명의 방법은 본 발명의 광활성 섬유 또는 광활성 직물을 광선치료를 필요로 하는 조직 또는 기관에 적용하는 단계 및 광활성 섬유 또는 광활성 직물에 존재하는 광활성제(들)의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 광활성 섬유 또는 광활성 직물을 조사하여 광활성제(들)의 방출을 유도하는 단계를 포함한다.
본 발명의 방법들에서, 임의의 활성 광원이 사용될 수 있다. 임의의 종류의 할로겐, LED 또는 플라즈마 아크 램프, 또는 레이저가 적절할 수 있다. 활성 광의 적절한 소스의 주요 특성은, 이들 소스들이 조성물에 존재하는 하나 이상의 광활성제를 활성시키기에 적절한 파장(또는 파장들)으로 발광한다는 점일 것이다. 일 실시예에서, 아르곤 레이저가 사용된다. 다른 실시예에서, 칼륨-티타늄-인산염(KTP) 레이저(예, GreenLight™ 레이저)가 사용된다. 또 다른 실시예에서, LED 램프, 예컨대 광경화 장치가 활성 광원이다. 여전히 또 다른 실시예에서, 상기 활성 광원은 약 200 nm 내지 800 nm의 파장을 갖는 광원이다. 다른 실시예에서, 상기 활성 광원은 400nm 및 600nm의 파장을 갖는 가시광선원이다. 다른 실시예에서, 상기 활성 광원은 400nm 및 700nm의 파장을 갖는 가시광선원이다. 또 다른 실시예에서, 활성 광원은 청색광이다. 또 다른 실시예에서, 활성 광원은 적색광이다. 또 다른 실시예에서, 활성 광원은 녹색광이다. 게다가, 활성 광의 소스는 적절한 출력 밀도를 가져야 한다. 비-시준(collimation)된 광원(LED, 할로겐 또는 플라즈마 램프)에 적합한 출력 밀도는 약 0.1mW/cm2 내지 약 200mW/cm2의 범위이다. 레이저 광원에 적합한 출력 밀도는 약 0.5 mW/cm2 내지 약 0.8 mW/cm2의 범위이다.
일부 구현예들에서, 광은 대상의 피부 표면에서 약 0.1mW/cm2 내지 약 500mW/cm2, 또는 0.1 내지 300mW/cm2, 또는 0.1 내지 200mW/cm2의 에너지를 갖되, 상기 인가된 에너지는 적어도 처리되는 상태, 광의 파장, 광원에서 피부까지의 거리, 및 상기 광활성 섬유 또는 직물의 두께에 의존한다. 소정의 실시예들에서, 대상의 피부에서의 광은 약 1내지 40mW/cm2, 또는 20 내지 60mW/cm2, 또는 40 내지 80mW/cm2, 또는 60 내지 100mW/cm2, 또는 80 내지 120mW/cm2, 또는 100 내지 140mW/cm2, 또는 30 내지 180mW/cm2, 또는 120 내지 160mW/cm2, 또는 140 내지 180mW/cm2, 또는 160 내지 200mW/cm2, 또는 110 내지 240mW/cm2, 또는 110 내지 150mW/cm2, 또는 190 내지 240mW/cm2이다.
광활성제의 활성화는 조사(펨토- 또는 피코 초) 시에 거의 즉시 일어날 수 있다. 장시간의 노출 기간은 본 발명의 광활성 섬유 및 직물 및 그것의 치료되는 조직과의 상호 작용의 흡수, 반사 및 재방출 광의 상승 효과를 이용하는 데에 유익할 수 있다. 일 실시예에서, 광활성 섬유 또는 직물의 활성 광에 대한 노출 시간은 0.01분 내지 90분의 기간이다. 다른 실시예에서, 광활성 섬유 또는 직물의 활성 광에 대한 노출 시간은 1분 내지 5분의 기간이다. 몇몇 기타 실시예에서, 상기 광활성 섬유 또는 직물은 1분 내지 3분의 기간 동안 조사된다. 소정의 실시예들에서, 광은 1초 내지 30초, 15초 내지 45초, 30초 내지 60초, 0.75분 내지 1.5분, 1분 내지 2분, 1.5분 내지 2.5분, 2분 내지 3분, 2.5분 내지 3.5분, 3분 내지 4분, 3.5분 내지 4.5분, 4분 내지 5분, 5분 내지 10분, 10분 내지 15분, 15분 내지 20분, 또는 20분 내지 30분의 기간 동안 적용된다. 상기 치료 시간은 약 90분, 약 80분, 약 70분, 약 60분, 약 50분, 약 40분 또는 약 30분까지의 범위일 수 있다. 상기 치료 시간은 치료 영역으로 유도된 플루엔스의 비율을 조정함으로써 선량(dosage)을 유지하기 위해서 조정될 수 있음을 이해해야 할 것이다. 예를 들면, 전달되는 플루엔스는 약 4 내지 약 60J/cm2, 약 4 내지 약 90J/cm2, 약 10 내지 약 90J/cm2, 약 10 내지 약 60J/cm2, 약 10 내지 약 50J/cm2, 약 10 내지 약 40J/cm2, 약 10 내지 약 30J/cm2, 약 20 내지 40J/cm2, 약 15J/cm2 내지 약 25J/cm2, 또는 약 10 내지 약 20J/cm2일 수 있다.
소정의 실시예들에서, 광활성 섬유 및 광활성 직물은 소정의 간격으로 재-조사될 수도 있다. 또 다른 실시예에서, 활성 광원은 적절한 노출 시간 동안 치료 영역 위로 연속 동작하고 있다. 또 다른 실시예에서, 광활성 섬유 또는 광활성 직물은 광활성 섬유 또는 광활성 직물이 적어도 부분적으로 광표백되거나 완전히 광표백될 때까지 조사될 수도 있다.
소정의 실시예들에서, 광활성 섬유 또는 직물 중의 광활성제는 태양 및 천정 조명을 포함하여 주변광에 의하여 광여기될 수 있다. 소정의 실시예들에서, 광활성제는 전자기 스펙트럼의 가시 범위 내에서 광에 의해 광 활성화될 수 있다. 상기 광은 태양광, 백열 전구, LED 장치, 텔레비전, 컴퓨터, 전화, 모바일 기기 등에서와 같은 전자 디스플레이 화면들, 모바일 기기 상의 플래시라이트와 같은 임의의 광원에 의해 방출될 수 있다. 본 발명의 방법들에서, 임의의 광원이 사용될 수 있다. 예를 들어, 주변 광과 직사광 또는 직접 인공광의 조합이 사용될 수도 있다. 주변 광은 LED 전구, 형광등 등의 머리 위의 조사, 및 간접 태양광을 포함할 수 있다.
본 발명의 방법들에서, 상기 광활성 섬유 또는 직물은 광의 적용 이후에 조직이나 기관에서 제거될 수 있다. 다른 실시예들에서, 상기 광활성 섬유 또는 직물은 연장된 기간 동안 조직이나 기관 상에 남겨지고 적절한 시점들에서 직접 또는 주변 광으로 재-활성화되어서 상태를 치료한다.
실시예
실시예 1
광활성 섬유 및 광활성 직물의 준비
발색단을 중합체 재료 (발색단과 화합된 중합체 재료)로 만들어진 섬유에 혼입시켰다. 화합에는 중합체 용융물을 취하여 고체 형태로 발색단을 중합체에 직접 첨가한 다음, 용융물이 냉각될 수 있게 하는 것이 관여했다. 이 과정은 발색단이 중합체 섬유와 혼입될 수 있게 했다. 중합체 섬유는 섬유, 부직포, 튜브 및 필름으로부터 선택되었다. 발색단 대 중합체 비율을 사용된 발색단에 따라 달라지도록 선택했다, 예를 들어: 에오신 Y의 경우, 20% w/w 비율 (물 속)을 마스터 발색단 배치에 사용했으며, 플루오레세인의 경우, 5% w/w 비율을 마스터 발색단 배치에 사용했다. 순수 에오신 Y 섬유를 만들고 에오신 Y 및 플루오레세인의 4 : 1 혼합물 (중량 기준 (또는 섬유 중량 기준 1 : 1))을 제조하였다.
섬유의 준비: 폴리프로필렌, 폴리에틸렌, 나일론 또는 이들의 조합으로 제조된 섬유를 준비하였다. 에오신 Y 또는 플루오레세인 또는 에오신 Y과 플루오레세인의 조합을 광활성제로서 사용했다. 하나의 유형의 중합체를 사용하여 제조한 섬유의 단면도가 도 1b에 도시되어 있다. 폴리에틸렌은 폴리프로필렌 외피를 갖는 50/50 폴리에틸렌 코어로 제조되었다. 이들 섬유의 단면도가 도 1c에 도시되어 있다.
다음과 같은 조성의 섬유를 고려하였다:
A) 폴리프로필렌 중합체 및 5% 에오신 Y,
B) 폴리프로필렌 중합체 및 10% 에오신 Y,
C) 폴리프로필렌 중합체 및 15% 에오신 Y,
D) 폴리프로필렌 중합체 및 20% 에오신 Y,
E) 폴리프로필렌 중합체 및 5% 에오신 Y
F) 폴리프로필렌 중합체 및 10% 플루오레세인,
G) 폴리프로필렌 중합체 및 15% 에오신 Y;
H) 폴리프로필렌 중합체 및 20% 에오신 Y
I) 폴리에틸렌 중합체 및 5% 에오신 Y,
J) 폴리에틸렌 중합체 및 10% 에오신 Y,
K) 폴리에틸렌 중합체 및 15% 에오신 Y,
L) 폴리에틸렌 중합체 및 20% 에오신 Y,
M) 폴리에틸렌 중합체 및 5% 플루오레세인,
N) 나일론 및 5% 에오신 Y,
O) 나일론 및 10% 에오신 Y,
P) 나일론 및 15% 에오신 Y,
Q) 나일론 및 20% 에오신 Y,
R) 나일론 및 5% 플루오레세인.
부직포: 폴리프로필렌 섬유를 부직포 샘플로 사용하였다. 다음 섬유를 준비하였다:
S) 폴리프로필렌 중합체 및 0.5g/L 에오신 Y,
T) 폴리프로필렌 중합체 및 0.5g/L 에오신 Y 및 0.25g/L 플루오레세인.
실시예 2
윤활제가 포함된 광활성 섬유의 준비
섬유를 발색단 및 윤활제의 배스(1:6 오일:물) (즉, 루롤 오일)에 침지시켜서 착색되고 형광을 띠는 섬유를 생성시켰다. 섬유는 두 가지 발색단, 에오신 Y 및 플루오레세인/에오신 Y 혼합물(1/4)을 모두 포함했다. 폴리에틸렌을 폴리프로필렌 외피를 갖는 50/50 폴리에틸렌 코어로 제조하였다.
다음과 같은 조성의 섬유를 고려하였다:
AA) 폴리프로필렌 (코어)를 갖는 폴리메틸 메타크릴레이트 (외피), 에오신 Y:플루오레세인 각각 10g/L, 150㎛ 모노필라멘트,
BB) 폴리프로필렌 (코어)를 갖는 폴리메틸 메타크릴레이트 (외피), 에오신 Y:플루오레세인 각각 20g/L, 150㎛ 모노필라멘트,
CC) 폴리프로필렌 (코어)를 갖는 폴리메틸 메타크릴레이트 (외피), 에오신 Y:플루오레세인 각각 30g/L, 150㎛ 모노필라멘트,
DD ) 나일론, 에오신 Y:플루오레세인 각각 10g/L, 150㎛ 멀티필라멘트,
EE ) 나일론, 에오신 Y:플루오레세인 각각 20g/L, 150㎛ 멀티필라멘트,
FF) 나일론, 에오신 Y: 플루오레세인 각각 50g/L, 150㎛ 멀티필라멘트,
GG ) 폴리프로필렌, 에오신 Y 발색단 20%, 2 파운드,
HH ) 폴리프로필렌, 플루오레세인 발색단 5%, 1 파운드와 혼합된
폴리프로필렌, 에오신 Y 발색단 20%, 1 파운드 (1:1 비율)
폴리프로필렌 코어 블랭크, 블랭크, 1 파운드로 도핑된 폴리에틸렌 외피, 에오신 Y 발색단 20%, 1 파운드,
II) 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리에틸렌 외피와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리에틸렌 외피 (1:1 비율),
JJ ) 폴리프로필렌 코어 블랭크, 블랭크, 1 파운드,
KK ) 에오신 Y 발색단 20%, 1 파운드로 도핑된 폴리에틸렌 외피 및 에오신 Y 발색단 20%, 1 파운드로 도핑된 폴리프로필렌 코어,
LL ) 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리에틸렌 외피와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리에틸렌 외피 (1:1 비율) 및 에오신 Y 발색단 20%, 1 파운드로 도핑된 폴리프로필렌 코어,
MM) 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리에틸렌 외피와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리에틸렌 외피 (1:1 비율) 및 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리프로필렌 코어와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리프로필렌 코어 (1:1 비율),
NN ) 에오신 Y 발색단 20%, 1 파운드로 도핑된 폴리프로필렌 코어를 갖는 폴리에틸렌 외피 블랭크, 블랭크, 1 파운드,
OO) 폴리에틸렌 외피 블랭크, 블랭크, 1 파운드 및 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리프로필렌 코어와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리프로필렌 코어 (1:1 비율),
PP) 에오신 Y 발색단 20%, 1 파운드로 도핑된 폴리에틸렌 외피 및 플루오레세인 발색단 5%, 0.5 파운드로 도핑된 폴리프로필렌 코어와 혼합된 에오신 Y 발색단 20%, 0.5 파운드로 도핑된 폴리프로필렌 코어 (1:1 비율),
QQ ) 나일론, 에오신 Y 발색단 20%, 2 파운드,
RR) 나일론, 플루오레세인 발색단 5%, 1 파운드와 혼합된 나일론, 에오신 Y 발색단 20%, 1 파운드 (1:1 비율).
실시예 3
광활성 섬유에 의한 형광 방출
표 1, 5, 9, 14, 19 및 25에 개략된 광활성 섬유를 준비하였다; 광활성제의 조성물을 일부 섬유 상에 분무하였다. 이 섬유 각각은 Thera™ 램프를 사용하여 5cm에서 5분간 조사한 후 형광을 방출하는 능력을 평가했다. 결과가 도 2a (나일론 섬유), 도 2b (PBT 섬유) 및 도 2c (PMMA 섬유) 및 표 2, 3, 4, 6, 7, 8, 10, 11, 12, 13, 15, 16, 17, 18, 20, 21, 22, 23, 24, 26, 27, 28, 29, 30, 31, 32 및 33에 제시되어 있다.
에오신과 화합된 폴리에틸렌을 포함하는 광활성 섬유
섬유 조성물 형광 방출
1 0.5% 에오신 함유 폴리에틸렌 + 루롤 오일 코팅 표 2
2 0.5% 에오신 함유 폴리에틸렌 + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 3
3 0.5% 에오신 함유 폴리에틸렌 + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 4
4 0.5% 에오신 함유 폴리에틸렌 + 10g/L 에오신 Y 코팅 + 루롤 오일 코팅 -
섬유 1 - 폴리에틸렌 + 에오신 내부, 루롤 오일 외부
섬유 1 - 폴리에틸렌 + 에오신 내부, 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 37.73 37.83 37.89 37.91 38.04 38.18 38.28 38.36 38.44 38.56 38.61 11.44 99.9%
형광 519-760 0.03 0.03 0.03 0.03 0.03 0.03 0.02 0.03 0.03 0.02 0.02 0.01 0.1%
합계 400-760 37.76779 37.85432 37.9151 37.94457 38.06825 38.2112 38.30258 38.38788 38.4684 38.58573 38.6291 11.45 100.0%
형광% 　 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.0% 0.00 0.1%
퍼플 (400)-450 25.7413 25.4023 25.1707 24.9117 24.7605 24.6212 24.4817 24.3537 24.2225 24.1625 24.0604 7.43 65.0%
블루 450-500 11.9843 12.4069 12.6914 12.9768 13.2592 13.5382 13.7734 13.9839 14.1869 14.3716 14.5227 4.00 34.9%
그린 500-570 0.0117 0.0197 0.0307 0.0279 0.0259 0.0267 0.0338 0.0334 0.0415 0.0349 0.0313 0.01 0.1%
옐로우 570-591 0.0065 0.0067 0.0092 0.0102 0.0093 0.0092 0.0056 0.0071 0.0108 0.0064 0.0058 0.00 0.0%
오렌지 591-610 0.0054 0.0098 0.0088 0.0110 0.0091 0.0096 0.0064 0.0074 0.0064 0.0072 0.0056 0.00 0.0%
레드 610-760 0.0188 0.0094 0.0047 0.0075 0.0047 0.0068 0.0019 0.0026 0.0005 0.0035 0.0035 0.00 0.0%
합계 (400-700) 37.77 37.85 37.92 37.95 38.07 38.21 38.30 38.39 38.47 38.59 38.63 11.45 100.0%
섬유 2 - 루롤 오일 중 과산화 요소 함유
섬유 2 - 루롤 오일 중 과산화 요소 함유 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 44.34 43.56 43.60 43.59 43.53 43.48 43.45 43.47 43.48 43.60 43.69 13.08 99.9%
형광 519-760 0.03 0.03 0.03 0.03 0.03 0.04 0.03 0.03 0.03 0.04 0.04 0.01 0.1%
합계 400-760 44.364 43.59121 43.63011 43.62437 43.55596 43.52089 43.48319 43.49531 43.50617 43.63938 43.72855 13.09 100.0%
형광% 　 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.00 0.1%
퍼플 (400)-450 28.7823 27.7839 27.6486 27.3997 27.1146 26.9311 26.7372 26.5918 26.4659 26.4030 26.3381 8.16 62.3%
블루 450-500 15.5221 15.7414 15.9171 16.1574 16.3843 16.5173 16.6797 16.8401 16.9717 17.1625 17.3136 4.92 37.6%
그린 500-570 0.0376 0.0415 0.0369 0.0431 0.0308 0.0436 0.0389 0.0393 0.0406 0.0504 0.0474 0.01 0.1%
옐로우 570-591 0.0091 0.0094 0.0112 0.0094 0.0083 0.0111 0.0072 0.0093 0.0083 0.0115 0.0076 0.00 0.0%
오렌지 591-610 0.0076 0.0087 0.0106 0.0103 0.0099 0.0111 0.0107 0.0100 0.0107 0.0092 0.0114 0.00 0.0%
레드 610-760 0.0055 0.0069 0.0060 0.0049 0.0085 0.0072 0.0101 0.0051 0.0096 0.0031 0.0110 0.00 0.0%
합계 (400-700) 44.36 43.59 43.63 43.62 43.56 43.52 43.48 43.50 43.51 43.64 43.73 13.09 100.0%
섬유 3 - 루롤 오일 중 중탄산 나트륨 함유
섬유 3 - 루롤 오일 중 중탄산 나트륨 함유 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 45.77 45.38 45.39 45.41 45.38 45.46 45.53 45.55 45.53 45.53 45.64 13.65 99.9%
형광 519-760 0.03 0.03 0.03 0.02 0.03 0.03 0.02 0.03 0.04 0.02 0.03 0.01 0.1%
합계 400-760 45.79708 45.4078 45.42176 45.43369 45.40676 45.48801 45.55223 45.58 45.56858 45.554 45.66506 13.66 100.0%
형광% 　 0.1% 0.1% 0.1% 0.0% 0.1% 0.1% 0.0% 0.1% 0.1% 0.1% 0.1% 0.00 0.1%
퍼플 (400)-450 30.4595 29.6024 29.2516 28.8436 28.6273 28.4034 28.2416 28.0332 27.8598 27.6870 27.6032 8.61 63.0%
블루 450-500 15.2759 15.7454 16.1074 16.5308 16.7115 17.0158 17.2490 17.4738 17.6294 17.7953 17.9823 5.03 36.8%
그린 500-570 0.0356 0.0341 0.0350 0.0419 0.0480 0.0437 0.0514 0.0500 0.0491 0.0580 0.0645 0.01 0.1%
옐로우 570-591 0.0075 0.0081 0.0062 0.0067 0.0080 0.0068 0.0031 0.0094 0.0100 0.0052 0.0053 0.00 0.0%
오렌지 591-610 0.0107 0.0106 0.0104 0.0063 0.0071 0.0089 0.0040 0.0090 0.0116 0.0060 0.0060 0.00 0.0%
레드 610-760 0.0082 0.0076 0.0117 0.0046 0.0051 0.0098 0.0035 0.0049 0.0091 0.0026 0.0041 0.00 0.0%
합계 (400-700) 45.80 45.41 45.42 45.43 45.41 45.49 45.55 45.58 45.57 45.55 45.67 13.66 100.0%
에오신과 화합된 폴리락트산(PLA)을 포함하는 광활성 섬유
섬유 조성물 형광 방출
5 0.5% 에오신 함유 PLA + 루롤 오일 코팅 표 6
6 0.5% 에오신 함유 PLA + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 7
7 0.5% 에오신 함유 PLA + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 8
섬유 5 - 폴리락트산 + 에오신 내부, 루롤 오일 외부
섬유 5 - 폴리락트산 + 에오신 내부, 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 14.94 14.93 14.85 14.75 14.71 14.67 14.65 14.66 14.62 14.61 14.61 4.42 93.9%
형광 519-760 1.12 1.02 0.98 0.95 0.94 0.92 0.91 0.90 0.87 0.87 0.85 0.28 6.0%
합계 400-760 16.05383 15.94828 15.82929 15.69884 15.6478 15.58449 15.56786 15.55919 15.48759 15.48833 15.46502 4.71 99.9%
형광% 　 6.9% 6.4% 6.2% 6.1% 6.0% 5.9% 5.9% 5.8% 5.6% 5.6% 5.5% 0.06 6.0%
퍼플 (400)-450 10.4182 10.2214 10.0756 9.9133 9.8031 9.7045 9.6358 9.5792 9.5010 9.4528 9.4132 2.95 62.6%
블루 450-500 4.5199 4.7079 4.7777 4.8335 4.9048 4.9608 5.0190 5.0769 5.1140 5.1618 5.1980 1.47 31.3%
그린 500-570 0.1184 0.1103 0.1017 0.0982 0.0979 0.0945 0.0947 0.0931 0.0908 0.0913 0.0890 0.03 0.6%
옐로우 570-591 0.2998 0.2848 0.2731 0.2668 0.2631 0.2578 0.2561 0.2523 0.2461 0.2436 0.2386 0.08 1.7%
오렌지 591-610 0.3337 0.3119 0.3002 0.2939 0.2891 0.2839 0.2806 0.2780 0.2700 0.2688 0.2626 0.09 1.9%
레드 610-760 0.3793 0.3265 0.3152 0.3070 0.3035 0.2965 0.2949 0.2929 0.2784 0.2828 0.2761 0.09 2.0%
합계 (400-700) 16.07 15.96 15.84 15.71 15.66 15.60 15.58 15.57 15.50 15.50 15.48 4.71 100.0%
섬유 6 - 폴리락트산 + 에오신 내부, UP + 루롤 오일 외부
섬유 6 - 폴리락트산 + 에오신 내부, UP + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 15.27 15.32 15.33 15.31 15.29 15.28 15.26 15.22 15.18 15.14 15.11 4.58 94.4%
형광 519-760 1.05 0.94 0.91 0.90 0.89 0.86 0.85 0.83 0.83 0.80 0.79 0.27 5.5%
합계 400-760 16.32258 16.26344 16.24112 16.20668 16.17224 16.14035 16.10769 16.05246 16.00419 15.94197 15.8982 4.84 99.9%
형광% 　 6.4% 5.8% 5.6% 5.6% 5.5% 5.3% 5.3% 5.2% 5.2% 5.0% 5.0% 0.05 5.5%
퍼플 (400)-450 10.6935 10.4773 10.3672 10.2573 10.1656 10.0862 10.0081 9.9236 9.8464 9.7768 9.7092 3.05 62.9%
블루 450-500 4.5788 4.8458 4.9628 5.0482 5.1215 5.1921 5.2499 5.2948 5.3311 5.3629 5.3990 1.53 31.6%
그린 500-570 0.0972 0.0853 0.0822 0.0826 0.0797 0.0787 0.0778 0.0752 0.0752 0.0741 0.0737 0.02 0.5%
옐로우 570-591 0.2906 0.2567 0.2470 0.2436 0.2380 0.2330 0.2287 0.2254 0.2223 0.2162 0.2132 0.07 1.5%
오렌지 591-610 0.3265 0.2930 0.2836 0.2786 0.2726 0.2664 0.2618 0.2578 0.2549 0.2474 0.2433 0.08 1.7%
레드 610-760 0.3516 0.3193 0.3121 0.3097 0.3079 0.2968 0.2942 0.2880 0.2866 0.2764 0.2715 0.09 1.9%
합계 (400-700) 16.34 16.28 16.25 16.22 16.19 16.15 16.12 16.06 16.02 15.95 15.91 4.85 100.0%
섬유 7 - 폴리락트산 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부
섬유 7 - 폴리락트산 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 16.07 16.04 16.01 15.90 15.79 15.77 15.72 15.66 15.65 15.70 15.75 4.75 94.3%
형광 519-760 1.12 0.99 0.96 0.93 0.92 0.92 0.91 0.89 0.87 0.87 0.84 0.28 5.6%
합계 400-760 17.18991 17.03564 16.96755 16.83133 16.71217 16.69256 16.62935 16.55821 16.5202 16.56995 16.59658 5.03 99.9%
형광% 　 6.5% 5.8% 5.7% 5.5% 5.5% 5.5% 5.4% 5.4% 5.2% 5.2% 5.1% 0.06 5.6%
퍼플 (400)-450 11.1705 10.9276 10.8025 10.6200 10.4800 10.3930 10.2891 10.1908 10.1298 10.1080 10.0959 3.15 62.6%
블루 450-500 4.9016 5.1169 5.2034 5.2792 5.3112 5.3811 5.4351 5.4730 5.5252 5.5922 5.6575 1.60 31.7%
그린 500-570 0.1197 0.1019 0.0951 0.0932 0.0913 0.0929 0.0918 0.0894 0.0859 0.0890 0.0858 0.03 0.6%
옐로우 570-591 0.3141 0.2730 0.2662 0.2585 0.2557 0.2532 0.2495 0.2454 0.2382 0.2381 0.2313 0.08 1.5%
오렌지 591-610 0.3475 0.3054 0.2967 0.2881 0.2847 0.2817 0.2778 0.2740 0.2670 0.2655 0.2586 0.09 1.7%
레드 610-760 0.3529 0.3253 0.3178 0.3062 0.3028 0.3042 0.2994 0.2988 0.2868 0.2898 0.2799 0.09 1.8%
합계 (400-700) 17.21 17.05 16.98 16.85 16.73 16.71 16.64 16.57 16.53 16.58 16.61 5.04 100.0%
에오신과 화합된 폴리프로필렌을 포함하는 광활성 섬유
섬유 조성물 형광 방출
8 0.5% 에오신 함유 폴리프로필렌 + 루롤 오일 코팅 표 10
9 0.5% 에오신 함유 폴리프로필렌 + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 11
10 0.5% 에오신 함유 폴리프로필렌 + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 12
11 0.5% 에오신 함유 폴리프로필렌 + 10g/L 에오신 Y 코팅 + 루롤 오일 코팅 표 13
섬유 8 - 폴리프로필렌 + 에오신 내부, 루롤 오일 외부

섬유 8 - 폴리프로필렌 + 에오신 내부, 루롤 오일 외부		 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 38.79 38.50 38.31 38.11 37.91 37.60 37.37 37.23 36.98 36.89 36.70 11.33 99.9%
형광 519-760 0.10 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.02 0.02 0.01 0.1%
합계 400-760 38.88797 38.51682 38.31451 38.11967 37.91618 37.60603 37.37597 37.24258 36.99724 36.90971 36.7173 11.34 100.0%
형광% 　 0.2% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.1% 0.1% 0.00 0.1%
퍼플 (400)-450 26.2136 25.6104 25.2140 24.8144 24.4722 24.0801 23.7486 23.5275 23.2268 23.0455 22.8148 7.32 64.6%
블루 450-500 12.5662 12.8714 13.0711 13.2695 13.4083 13.4929 13.5901 13.6822 13.7305 13.8151 13.8517 4.00 35.3%
그린 500-570 0.0130 0.0223 0.0221 0.0249 0.0289 0.0253 0.0293 0.0257 0.0272 0.0345 0.0339 0.01 0.1%
옐로우 570-591 0.0002 0.0003 0.0006 0.0053 0.0014 0.0036 0.0021 0.0010 0.0023 0.0053 0.0030 0.00 0.0%
오렌지 591-610 0.0002 0.0029 0.0044 0.0049 0.0026 0.0031 0.0030 0.0033 0.0045 0.0032 0.0054 0.00 0.0%
레드 610-760 0.0948 0.0096 0.0026 0.0008 0.0029 0.0012 0.0029 0.0029 0.0061 0.0060 0.0087 0.00 0.0%
합계 (400-700) 38.89 38.52 38.31 38.12 37.92 37.61 37.38 37.24 37.00 36.91 36.72 11.34 100.0%
섬유 9 - 폴리프로필렌 + 에오신 내부, UP + 루롤 오일 외부
섬유 9 - 폴리프로필렌 + 에오신 내부, UP + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 38.22 37.85 37.66 37.36 37.11 36.88 36.72 36.64 36.51 36.43 36.37 11.14 99.9%
형광 519-760 0.12 0.00 0.02 0.00 0.01 0.01 0.02 0.01 0.01 0.01 0.01 0.01 0.1%
합계 400-760 38.33982 37.8572 37.67632 37.36189 37.1219 36.89308 36.73885 36.64907 36.52148 36.44165 36.37409 11.15 100.0%
형광% 　 0.3% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.00 0.1%
퍼플 (400)-450 25.9945 25.2982 24.9107 24.4318 24.0608 23.7143 23.4416 23.2361 23.0084 22.8281 22.6777 7.23 64.8%
블루 450-500 12.2258 12.5352 12.7280 12.9008 13.0307 13.1446 13.2552 13.3760 13.4809 13.5761 13.6610 3.91 35.1%
그린 500-570 0.0032 0.0220 0.0210 0.0265 0.0273 0.0230 0.0278 0.0285 0.0241 0.0321 0.0306 0.01 0.1%
옐로우 570-591 0.0007 0.0001 0.0038 0.0005 0.0004 0.0048 0.0034 0.0005 0.0029 0.0011 0.0009 0.00 0.0%
오렌지 591-610 0.0005 0.0003 0.0053 0.0021 0.0014 0.0052 0.0048 0.0033 0.0033 0.0025 0.0023 0.00 0.0%
레드 610-760 0.1152 0.0014 0.0078 0.0002 0.0014 0.0014 0.0062 0.0048 0.0020 0.0019 0.0017 0.00 0.0%
합계 (400-700) 38.34 37.86 37.68 37.36 37.12 36.89 36.74 36.65 36.52 36.44 36.37 11.15 100.0%
섬유 10 - 폴리프로필렌 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부
섬유 10 - 폴리프로필렌 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 36.92 36.59 36.47 36.29 36.17 36.04 35.91 35.83 35.76 35.70 35.67 10.85 100.0%
형광 519-760 0.00 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.00 0.0%
합계 400-760 36.92294 36.59499 36.47866 36.30052 36.18347 36.04749 35.91653 35.84232 35.77078 35.70893 35.67485 10.85 100.0%
형광% 　 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.00 0.0%
퍼플 (400)-450 24.9566 24.3430 24.0409 23.6970 23.4067 23.1523 22.8998 22.7089 22.5307 22.3735 22.2601 7.02 64.7%
블루 450-500 11.9414 12.2264 12.4073 12.5720 12.7439 12.8609 12.9852 13.1015 13.2040 13.3008 13.3833 3.82 35.2%
그린 500-570 0.0226 0.0177 0.0253 0.0257 0.0262 0.0254 0.0258 0.0244 0.0253 0.0297 0.0281 0.01 0.1%
옐로우 570-591 0.0012 0.0030 0.0017 0.0041 0.0026 0.0015 0.0031 0.0012 0.0039 0.0036 0.0006 0.00 0.0%
오렌지 591-610 0.0010 0.0035 0.0012 0.0015 0.0027 0.0031 0.0023 0.0031 0.0046 0.0013 0.0012 0.00 0.0%
레드 610-760 0.0001 0.0015 0.0022 0.0002 0.0014 0.0043 0.0004 0.0033 0.0024 0.0000 0.0015 0.00 0.0%
합계 (400-700) 36.92 36.60 36.48 36.30 36.18 36.05 35.92 35.84 35.77 35.71 35.67 10.85 100.0%
섬유 11 - 폴리프로필렌 + 에오신 내부, 에오신 + 루롤 오일 외부
섬유 11 - 폴리프로필렌 + 에오신 내부, 에오신 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 34.92 34.27 34.10 33.96 33.80 33.65 33.52 33.43 33.36 33.23 33.16 10.15 99.9%
형광 519-760 0.04 0.02 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.01 0.1%
합계 400-760 34.96027 34.29043 34.12328 33.98972 33.83178 33.67762 33.55483 33.45521 33.38872 33.26012 33.18787 10.16 100.0%
형광% 　 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.00 0.1%
퍼플 (400)-450 24.0092 23.0633 22.6970 22.3805 22.0694 21.8103 21.5672 21.3650 21.1855 20.9851 20.8562 6.63 65.3%
블루 450-500 10.9008 11.1891 11.3868 11.5594 11.7112 11.8201 11.9385 12.0429 12.1567 12.2284 12.2886 3.51 34.5%
그린 500-570 0.0173 0.0173 0.0143 0.0207 0.0223 0.0225 0.0194 0.0232 0.0196 0.0235 0.0199 0.01 0.1%
옐로우 570-591 0.0118 0.0090 0.0071 0.0088 0.0095 0.0102 0.0076 0.0079 0.0079 0.0075 0.0085 0.00 0.0%
오렌지 591-610 0.0114 0.0076 0.0097 0.0112 0.0104 0.0078 0.0109 0.0081 0.0096 0.0079 0.0085 0.00 0.0%
레드 610-760 0.0102 0.0044 0.0088 0.0097 0.0095 0.0069 0.0117 0.0082 0.0098 0.0081 0.0065 0.00 0.0%
합계 (400-700) 34.96 34.29 34.12 33.99 33.83 33.68 33.56 33.46 33.39 33.26 33.19 10.16 100.0%
에오신과 화합된 나일론을 포함하는 광활성 섬유
섬유 조성물 형광 방출
12 0.5% 에오신 함유 나일론 + 루롤 오일 코팅 표 15
13 0.5% 에오신 함유 나일론 + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 16
14 0.5% 에오신 함유 나일론 + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 17
15 0.5% 에오신 함유 나일론 + 10g/L 에오신 Y 코팅 + 루롤 오일 코팅 표 18
섬유 12 - 나일론 + 에오신 내부, 루롤 오일 외부
섬유 12 - 나일론 + 에오신 내부, 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 8.45 9.13 10.34 11.38 12.24 13.06 13.83 14.52 15.24 15.82 16.38 3.72 69.9%
형광 519-760 7.55 6.46 5.97 5.54 5.23 4.91 4.64 4.40 4.25 4.03 3.90 1.59 29.9%
합계 400-760 15.99847 15.59112 16.31268 16.92697 17.46969 17.96796 18.46997 18.92674 19.48819 19.84828 20.28261 5.31 99.8%
형광% 　 47.2% 41.4% 36.6% 32.7% 29.9% 27.3% 25.1% 23.3% 21.8% 20.3% 19.2% 0.30 29.9%
퍼플 (400)-450 6.8019 6.9690 7.5393 7.9927 8.3430 8.6685 8.9554 9.2182 9.4951 9.6972 9.8883 2.51 47.2%
블루 450-500 1.6408 2.1589 2.7965 3.3803 3.8857 4.3748 4.8527 5.2897 5.7259 6.0989 6.4642 1.21 22.7%
그린 500-570 2.0031 1.7498 1.6586 1.5746 1.5063 1.4374 1.3732 1.3144 1.2775 1.2280 1.2009 0.45 8.5%
옐로우 570-591 2.2768 1.9007 1.7088 1.5559 1.4441 1.3456 1.2576 1.1845 1.1207 1.0606 1.0133 0.45 8.4%
오렌지 591-610 1.4927 1.2519 1.1345 1.0406 0.9709 0.9120 0.8536 0.8080 0.7702 0.7336 0.7040 0.30 5.6%
레드 610-760 1.8387 1.6080 1.5182 1.4229 1.3568 1.2651 1.2106 1.1433 1.1291 1.0584 1.0397 0.41 7.6%
합계 (400-700) 16.05 15.64 16.36 16.97 17.51 18.00 18.50 18.96 19.52 19.88 20.31 5.32 100.0%
섬유 13 - 나일론 + 에오신 내부, UP + 루롤 오일 외부(25-30분)
섬유 13 - 나일론 + 에오신 내부, UP + 루롤 오일 외부(25-30 분) mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 24.96 25.05 25.19 25.29 25.42 25.49 25.61 25.68 25.78 25.90 25.99 7.63 93.0%
형광 519-760 1.98 1.93 1.93 1.95 1.91 1.90 1.89 1.84 1.88 1.86 1.84 0.57 7.0%
합계 400-760 26.93968 26.98401 27.11688 27.24167 27.32461 27.38227 27.49843 27.52573 27.66029 27.7626 27.83434 8.20 99.9%
형광% 　 7.4% 7.2% 7.1% 7.2% 7.0% 6.9% 6.9% 6.7% 6.8% 6.7% 6.6% 0.07 7.0%
퍼플 (400)-450 13.4292 13.4647 13.5354 13.5872 13.6501 13.6725 13.7437 13.7672 13.8125 13.8662 13.9151 4.10 49.9%
블루 450-500 11.4229 11.4809 11.5418 11.5944 11.6551 11.7014 11.7509 11.8032 11.8555 11.9193 11.9667 3.50 42.7%
그린 500-570 0.7422 0.7341 0.7330 0.7372 0.7289 0.7264 0.7299 0.7229 0.7323 0.7294 0.7230 0.22 2.7%
옐로우 570-591 0.4073 0.3998 0.3982 0.3978 0.3923 0.3909 0.3853 0.3833 0.3793 0.3786 0.3737 0.12 1.4%
오렌지 591-610 0.3298 0.3235 0.3230 0.3212 0.3183 0.3170 0.3128 0.3103 0.3079 0.3066 0.3036 0.10 1.2%
레드 610-760 0.6231 0.5954 0.5999 0.6183 0.5943 0.5883 0.5899 0.5528 0.5867 0.5762 0.5659 0.18 2.2%
합계 (400-700) 26.95 27.00 27.13 27.26 27.34 27.40 27.51 27.54 27.67 27.78 27.85 8.21 100.0%
섬유 14 - 나일론 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부(25-30분)
섬유 14 - 나일론 + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부(25-30 분) mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 27.04 27.10 27.20 27.13 27.12 27.21 27.30 27.37 27.49 27.58 27.53 8.18 94.4%
형광 519-760 1.72 1.70 1.69 1.65 1.61 1.59 1.59 1.57 1.54 1.56 1.49 0.49 5.6%
합계 400-760 28.7625 28.80483 28.88949 28.77401 28.72682 28.79745 28.89051 28.94176 29.02669 29.14196 29.0172 8.66 100.0%
형광% 　 6.0% 5.9% 5.8% 5.7% 5.6% 5.5% 5.5% 5.4% 5.3% 5.3% 5.1% 0.06 5.6%
퍼플 (400)-450 14.7774 14.7599 14.7845 14.7271 14.6997 14.7221 14.7524 14.7707 14.8138 14.8509 14.7998 4.43 51.1%
블루 450-500 12.1575 12.2336 12.3042 12.2857 12.3044 12.3716 12.4369 12.4876 12.5577 12.6191 12.6099 3.71 42.8%
그린 500-570 0.7817 0.7752 0.7711 0.7525 0.7403 0.7425 0.7407 0.7376 0.7291 0.7282 0.7190 0.22 2.6%
옐로우 570-591 0.3552 0.3522 0.3484 0.3332 0.3294 0.3225 0.3216 0.3195 0.3133 0.3150 0.3054 0.10 1.1%
오렌지 591-610 0.2653 0.2623 0.2593 0.2496 0.2476 0.2397 0.2398 0.2385 0.2326 0.2365 0.2263 0.07 0.9%
레드 610-760 0.4370 0.4330 0.4333 0.4369 0.4162 0.4097 0.4097 0.3982 0.3904 0.4027 0.3666 0.13 1.4%
합계 (400-700) 28.77 28.82 28.90 28.78 28.74 28.81 28.90 28.95 29.04 29.15 29.03 8.67 100.0%
섬유 15 - 나일론 + 에오신 내부, 에오신 + 루롤 오일 외부 - 시도 2 (25-30분)
섬유 15 - 나일론 + 에오신 내부, 에오신 + 루롤 오일 외부 - 시도 2 (25-30 분) mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 18.95 19.06 19.19 19.29 19.41 19.49 19.61 19.74 19.83 19.94 20.05 5.84 89.8%
형광 519-760 2.25 2.23 2.24 2.19 2.20 2.17 2.18 2.19 2.15 2.15 2.13 0.66 10.1%
합계 400-760 21.20136 21.28697 21.42811 21.48191 21.60579 21.66376 21.78431 21.92765 21.98483 22.08331 22.17704 6.49 99.9%
형광% 　 10.6% 10.5% 10.4% 10.2% 10.2% 10.0% 10.0% 10.0% 9.8% 9.7% 9.6% 0.10 10.1%
퍼플 (400)-450 10.4090 10.4463 10.5206 10.5657 10.6302 10.6576 10.7182 10.7853 10.8302 10.8776 10.9295 3.19 49.1%
블루 450-500 8.4999 8.5673 8.6248 8.6759 8.7348 8.7871 8.8430 8.9077 8.9536 9.0093 9.0661 2.63 40.4%
그린 500-570 0.5179 0.5198 0.5227 0.5133 0.5139 0.5128 0.5124 0.5241 0.5177 0.5155 0.5159 0.16 2.4%
옐로우 570-591 0.5174 0.5138 0.5096 0.5043 0.5029 0.4997 0.4990 0.4989 0.4941 0.4892 0.4894 0.15 2.3%
오렌지 591-610 0.4525 0.4474 0.4439 0.4396 0.4384 0.4349 0.4342 0.4322 0.4282 0.4264 0.4245 0.13 2.0%
레드 610-760 0.8250 0.8123 0.8263 0.8028 0.8053 0.7911 0.7970 0.7988 0.7803 0.7846 0.7707 0.24 3.7%
합계 (400-700) 21.22 21.31 21.45 21.50 21.63 21.68 21.80 21.95 22.00 22.10 22.20 6.50 100.0%
에오신과 화합된 폴리부틸렌 테레프탈레이트(PBT)를 포함하는 광활성 섬유
섬유 조성물 형광 방출
16 순수 PBT + 루롤 오일 코팅 표 20
17 1% 에오신 함유 PBT + 루롤 오일 코팅 표 21
18 1% 에오신 함유 PBT + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 22
19 1% 에오신 함유 PBT + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 23
20 1% 에오신 함유 PBT + 10g/L 에오신 Y 코팅 + 루롤 오일 코팅 표 24
섬유 16 - PBT 블랭크
섬유 16 - PBT 블랭크 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 69.78 69.35 69.24 68.90 68.53 68.16 68.04 67.72 67.51 67.29 67.15 20.54 99.9%
형광 519-760 0.05 0.07 0.06 0.05 0.05 0.06 0.05 0.07 0.06 0.05 0.04 0.02 0.1%
합계 400-760 69.82895 69.4195 69.30044 68.95217 68.5783 68.21259 68.09006 67.79068 67.56456 67.3467 67.19618 20.55 100.0%
형광% 　 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.1% 0.00 0.1%
퍼플 (400)-450 42.9096 42.0190 41.5394 40.9650 40.4537 39.9428 39.6390 39.2507 38.9616 38.6804 38.4675 12.13 59.0%
블루 450-500 26.7852 27.2232 27.5890 27.8149 27.9591 28.0905 28.2822 28.3575 28.4216 28.4878 28.5608 8.37 40.7%
그린 500-570 0.1043 0.1571 0.1564 0.1587 0.1566 0.1574 0.1648 0.1639 0.1680 0.1621 0.1529 0.05 0.2%
옐로우 570-591 0.0000 0.0052 0.0084 0.0098 0.0050 0.0067 0.0040 0.0110 0.0079 0.0106 0.0061 0.00 0.0%
오렌지 591-610 0.0000 0.0088 0.0059 0.0033 0.0035 0.0087 0.0001 0.0069 0.0049 0.0058 0.0060 0.00 0.0%
레드 610-760 0.0299 0.0066 0.0016 0.0006 0.0006 0.0071 0.0000 0.0010 0.0006 0.0001 0.0032 0.00 0.0%
합계 (400-700) 69.83 69.42 69.30 68.95 68.58 68.21 68.09 67.79 67.56 67.35 67.20 20.55 100.0%
섬유 17 - PBT + 에오신 내부, 루롤 오일 외부
섬유 17 - PBT + 에오신 내부, 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 2.63 2.57 2.41 2.18 2.06 1.99 2.26 2.34 2.30 2.28 2.24 0.69 47.1%
형광 519-760 2.83 2.73 2.71 2.64 2.58 2.51 2.45 2.40 2.36 2.34 2.33 0.77 52.3%
합계 400-760 5.463108 5.298557 5.120492 4.828287 4.644863 4.504063 4.707606 4.736382 4.659129 4.616988 4.571799 1.46 99.4%
형광% 　 51.8% 51.5% 53.0% 54.8% 55.6% 55.8% 52.1% 50.6% 50.7% 50.7% 50.9% 0.53 52.6%
퍼플 (400)-450 1.8166 1.7553 1.6450 1.5014 1.4223 1.3755 1.5282 1.5655 1.5335 1.5147 1.4931 0.47 32.0%
블루 450-500 0.8139 0.8126 0.7602 0.6817 0.6405 0.6139 0.7270 0.7718 0.7606 0.7591 0.7499 0.22 15.0%
그린 500-570 0.0536 0.0543 0.0575 0.0548 0.0545 0.0552 0.0543 0.0554 0.0537 0.0556 0.0561 0.02 1.1%
옐로우 570-591 0.5284 0.4851 0.4763 0.4619 0.4510 0.4395 0.4304 0.4193 0.4146 0.4093 0.4090 0.14 9.2%
오렌지 591-610 0.7208 0.6774 0.6674 0.6502 0.6344 0.6149 0.5997 0.5842 0.5764 0.5684 0.5648 0.19 12.9%
레드 610-760 1.5646 1.5467 1.5464 1.5100 1.4731 1.4350 1.3972 1.3685 1.3481 1.3375 1.3262 0.44 29.7%
합계 (400-700) 5.50 5.33 5.15 4.86 4.68 4.53 4.74 4.76 4.69 4.64 4.60 1.47 100.0%
섬유 18 - PBT + 에오신 내부, UP + 루롤 오일 외부
섬유 18 - PBT + 에오신 내부, UP + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 0.42 0.46 1.12 0.91 0.91 0.96 0.99 0.99 0.99 1.08 1.07 0.26 32.0%
형광 519-760 2.32 2.04 1.90 1.84 1.81 1.78 1.76 1.72 1.69 1.66 1.63 0.56 67.2%
합계 400-760 2.740057 2.495696 3.021197 2.744473 2.727173 2.740978 2.744468 2.71341 2.678671 2.743669 2.696495 0.82 99.3%
형광% 　 84.6% 81.8% 63.0% 66.9% 66.5% 65.1% 64.0% 63.4% 63.1% 60.6% 60.3% 0.68 67.7%
퍼플 (400)-450 0.3091 0.3171 0.7094 0.5882 0.5908 0.6157 0.6325 0.6333 0.6306 0.6807 0.6734 0.17 20.7%
블루 450-500 0.1126 0.1379 0.4059 0.3184 0.3210 0.3396 0.3549 0.3580 0.3572 0.3990 0.3955 0.09 11.3%
그린 500-570 0.0497 0.0412 0.0447 0.0430 0.0441 0.0444 0.0452 0.0456 0.0463 0.0471 0.0470 0.01 1.6%
옐로우 570-591 0.4315 0.3609 0.3414 0.3298 0.3247 0.3202 0.3163 0.3103 0.3053 0.3009 0.2959 0.10 12.1%
오렌지 591-610 0.5479 0.4794 0.4456 0.4291 0.4212 0.4130 0.4054 0.3958 0.3873 0.3800 0.3715 0.13 15.6%
레드 610-760 1.3154 1.1822 1.0955 1.0564 1.0456 1.0277 1.0096 0.9893 0.9704 0.9539 0.9309 0.32 38.6%
합계 (400-700) 2.77 2.52 3.04 2.76 2.75 2.76 2.76 2.73 2.70 2.76 2.71 0.83 100.0%
섬유 19 - PBT + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부
섬유 19 - PBT + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 0.55 0.56 1.00 1.17 1.25 1.08 1.05 1.05 1.09 1.11 1.13 0.30 34.4%
형광 519-760 2.40 2.11 1.94 1.86 1.78 1.76 1.74 1.71 1.69 1.66 1.64 0.56 64.9%
합계 400-760 2.954142 2.667009 2.942724 3.028633 3.035268 2.841185 2.787107 2.766328 2.777914 2.770098 2.774827 0.86 99.3%
형광% 　 81.4% 79.1% 65.9% 61.5% 58.7% 62.1% 62.4% 61.9% 60.9% 60.1% 59.2% 0.65 65.3%
퍼플 (400)-450 0.3923 0.3886 0.6557 0.7512 0.7970 0.6904 0.6687 0.6707 0.6870 0.6962 0.7091 0.19 22.2%
블루 450-500 0.1566 0.1676 0.3467 0.4136 0.4562 0.3852 0.3775 0.3828 0.3989 0.4086 0.4225 0.10 12.1%
그린 500-570 0.0504 0.0408 0.0409 0.0416 0.0404 0.0425 0.0432 0.0441 0.0449 0.0453 0.0460 0.01 1.5%
옐로우 570-591 0.4400 0.3607 0.3312 0.3199 0.3066 0.3023 0.2983 0.2935 0.2904 0.2869 0.2834 0.10 11.2%
오렌지 591-610 0.5668 0.4937 0.4519 0.4318 0.4119 0.4049 0.3978 0.3895 0.3835 0.3768 0.3705 0.13 15.0%
레드 610-760 1.3750 1.2394 1.1382 1.0913 1.0431 1.0353 1.0207 1.0044 0.9917 0.9744 0.9612 0.33 37.9%
합계 (400-700) 2.98 2.69 2.96 3.05 3.06 2.86 2.81 2.79 2.80 2.79 2.79 0.86 100.0%
섬유 20 - PBT + 에오신 내부, 에오신 + 루롤 오일 외부
섬유 20 - PBT + 에오신 내부, 에오신 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 3.25 3.82 3.91 4.14 4.19 4.39 4.35 4.30 4.27 4.27 4.24 1.23 62.9%
형광 519-760 2.72 2.62 2.54 2.42 2.36 2.30 2.27 2.23 2.20 2.17 2.16 0.72 36.7%
합계 400-760 5.966188 6.441835 6.450766 6.557832 6.549098 6.694657 6.622601 6.520864 6.46933 6.436219 6.394325 1.94 99.6%
형광% 　 45.6% 40.7% 39.4% 36.9% 36.0% 34.4% 34.3% 34.1% 34.1% 33.7% 33.8% 0.37 36.8%
퍼플 (400)-450 2.1823 2.5014 2.5369 2.6563 2.6642 2.7716 2.7308 2.6852 2.6568 2.6469 2.6211 0.78 40.1%
블루 450-500 1.0644 1.3131 1.3703 1.4781 1.5245 1.6190 1.6181 1.6076 1.6056 1.6155 1.6114 0.44 22.8%
그린 500-570 0.0508 0.0554 0.0585 0.0551 0.0556 0.0568 0.0560 0.0546 0.0576 0.0569 0.0567 0.02 0.9%
옐로우 570-591 0.4800 0.4340 0.4202 0.4071 0.3951 0.3860 0.3797 0.3738 0.3682 0.3644 0.3631 0.12 6.2%
오렌지 591-610 0.6916 0.6422 0.6186 0.5936 0.5743 0.5586 0.5488 0.5387 0.5300 0.5229 0.5176 0.17 9.0%
레드 610-760 1.5314 1.5275 1.4769 1.3971 1.3637 1.3304 1.3163 1.2875 1.2773 1.2554 1.2499 0.41 21.2%
합계 (400-700) 6.00 6.47 6.48 6.59 6.58 6.72 6.65 6.55 6.50 6.46 6.42 1.95 100.0%
에오신과 화합된 폴리(메틸) 메타크릴레이트(PMMA)를 포함하는 광활성 섬유
섬유 조성물 형광 방출
21 1% 에오신 함유 PMMA + 루롤 오일 코팅 표 26
22 1% 에오신 함유 PMMA + 1% 과산화 요소 코팅 + 루롤 오일 코팅 표 27
23 1% 에오신 함유 PMMA + 중탄산 나트륨 코팅 + 루롤 오일 코팅 표 28
24 1% 에오신 함유 PMMA + 10g/L 에오신 Y 코팅 + 루롤 오일 코팅 표 29
섬유 21 - PMMA + 에오신 내부, 루롤 오일 외부
섬유 21 - PMMA + 에오신 내부, 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 10.26 10.12 10.08 10.02 9.98 9.96 9.88 9.90 9.83 9.79 9.82 2.99 93.9%
형광 519-760 0.73 0.67 0.65 0.64 0.63 0.63 0.61 0.60 0.60 0.60 0.59 0.19 6.0%
합계 400-760 10.99377 10.79335 10.72893 10.65819 10.61231 10.58607 10.49542 10.50296 10.43348 10.39166 10.41602 3.19 99.9%
형광% 　 6.7% 6.2% 6.0% 6.0% 5.9% 5.9% 5.9% 5.7% 5.8% 5.8% 5.7% 0.06 6.0%
퍼플 (400)-450 7.8615 7.6370 7.5561 7.4510 7.3697 7.3017 7.2094 7.1832 7.1110 7.0489 7.0420 2.21 69.4%
블루 450-500 2.3995 2.4856 2.5276 2.5694 2.6118 2.6571 2.6720 2.7161 2.7200 2.7422 2.7821 0.78 24.6%
그린 500-570 0.0096 0.0069 0.0050 0.0043 0.0038 0.0033 0.0028 0.0026 0.0025 0.0023 0.0020 0.00 0.0%
옐로우 570-591 0.1304 0.1195 0.1128 0.1092 0.1063 0.1037 0.1003 0.0978 0.0963 0.0953 0.0928 0.03 1.0%
오렌지 591-610 0.2326 0.2175 0.2105 0.2074 0.2043 0.2022 0.1977 0.1949 0.1934 0.1922 0.1889 0.06 1.9%
레드 610-760 0.3732 0.3388 0.3284 0.3283 0.3277 0.3293 0.3241 0.3193 0.3211 0.3215 0.3190 0.10 3.1%
합계 (400-700) 11.01 10.81 10.74 10.67 10.62 10.60 10.51 10.51 10.44 10.40 10.43 3.19 100.0%
섬유 22 - PMMA + 에오신 내부, UP + 루롤 오일 외부
섬유 22 - PMMA + 에오신 내부, UP + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 15.69 14.95 14.74 14.59 14.47 14.42 14.39 14.36 14.33 14.28 14.27 4.39 95.7%
형광 519-760 0.75 0.67 0.66 0.64 0.64 0.63 0.63 0.63 0.62 0.61 0.60 0.19 4.2%
합계 400-760 16.4387 15.62283 15.39582 15.23084 15.11069 15.05078 15.01809 14.98481 14.95077 14.89236 14.87711 4.58 99.9%
형광% 　 4.6% 4.3% 4.3% 4.2% 4.3% 4.2% 4.2% 4.2% 4.1% 4.1% 4.1% 0.04 4.2%
퍼플 (400)-450 11.0082 10.3866 10.1416 9.9691 9.8076 9.7133 9.6369 9.5602 9.5019 9.4261 9.3807 2.97 64.9%
블루 450-500 4.6795 4.5640 4.5964 4.6207 4.6597 4.7054 4.7496 4.7990 4.8327 4.8559 4.8920 1.41 30.8%
그린 500-570 0.0004 0.0004 0.0002 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.00 0.0%
옐로우 570-591 0.0950 0.0842 0.0818 0.0763 0.0759 0.0727 0.0720 0.0703 0.0683 0.0664 0.0642 0.02 0.5%
오렌지 591-610 0.2189 0.2031 0.1987 0.1947 0.1933 0.1901 0.1884 0.1865 0.1828 0.1805 0.1789 0.06 1.3%
레드 610-760 0.4494 0.3965 0.3888 0.3815 0.3856 0.3805 0.3825 0.3799 0.3760 0.3743 0.3721 0.12 2.5%
합계 (400-700) 16.45 15.63 15.41 15.24 15.12 15.06 15.03 15.00 14.96 14.90 14.89 4.58 100.0%
섬유 23 - PMMA + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부
섬유 23 - PMMA + 에오신 내부, 중탄산 나트륨 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 13.15 13.50 13.34 13.26 13.22 13.13 12.89 12.80 12.69 12.59 12.51 3.92 95.4%
형광 519-760 0.68 0.64 0.63 0.62 0.61 0.61 0.61 0.60 0.60 0.59 0.59 0.19 4.5%
합계 400-760 13.83246 14.1425 13.97107 13.88749 13.82635 13.73764 13.49795 13.40275 13.28483 13.18373 13.09997 4.10 99.9%
형광% 　 4.9% 4.5% 4.5% 4.5% 4.4% 4.4% 4.5% 4.5% 4.5% 4.5% 4.5% 0.05 4.5%
퍼플 (400)-450 9.3441 9.4130 9.2256 9.1099 9.0173 8.9034 8.7126 8.6168 8.5063 8.4182 8.3422 2.68 65.2%
블루 450-500 3.8100 4.0877 4.1181 4.1541 4.1999 4.2260 4.1747 4.1828 4.1792 4.1748 4.1704 1.24 30.2%
그린 500-570 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.00 0.0%
옐로우 570-591 0.0804 0.0695 0.0664 0.0646 0.0623 0.0606 0.0604 0.0597 0.0591 0.0576 0.0565 0.02 0.5%
오렌지 591-610 0.2044 0.1888 0.1839 0.1819 0.1782 0.1759 0.1761 0.1742 0.1728 0.1704 0.1683 0.05 1.3%
레드 610-760 0.4057 0.3948 0.3881 0.3880 0.3795 0.3824 0.3847 0.3798 0.3780 0.3732 0.3729 0.12 2.8%
합계 (400-700) 13.84 14.15 13.98 13.90 13.84 13.75 13.51 13.41 13.30 13.19 13.11 4.11 100.0%
섬유 24 - PMMA + 에오신 내부, 에오신 + 루롤 오일 외부
섬유 24 - PMMA + 에오신 내부, 에오신 + 루롤 오일 외부 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 13.69 13.11 13.01 12.84 12.64 12.72 12.91 12.48 12.70 12.93 13.08 3.87 96.6%
형광 519-760 0.49 0.47 0.46 0.45 0.44 0.44 0.44 0.43 0.43 0.43 0.43 0.13 3.4%
합계 400-760 14.1806 13.57408 13.46488 13.29157 13.08745 13.16511 13.35073 12.91267 13.13371 13.35688 13.50934 4.01 99.9%
형광% 　 3.5% 3.4% 3.4% 3.4% 3.4% 3.4% 3.3% 3.4% 3.3% 3.2% 3.2% 0.03 3.4%
퍼플 (400)-450 9.6291 9.0682 8.9211 8.7398 8.5535 8.5459 8.6049 8.2940 8.3781 8.4711 8.5391 2.62 65.3%
블루 450-500 4.0575 4.0408 4.0850 4.1040 4.0914 4.1746 4.3091 4.1839 4.3231 4.4581 4.5427 1.25 31.3%
그린 500-570 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.0000 0.00 0.0%
옐로우 570-591 0.0456 0.0374 0.0362 0.0350 0.0332 0.0325 0.0312 0.0309 0.0308 0.0294 0.0296 0.01 0.3%
오렌지 591-610 0.1404 0.1264 0.1243 0.1215 0.1201 0.1197 0.1158 0.1154 0.1157 0.1133 0.1139 0.04 0.9%
레드 610-760 0.3167 0.3091 0.3061 0.2989 0.2969 0.3000 0.2972 0.2959 0.2933 0.2922 0.2913 0.09 2.3%
합계 (400-700) 14.19 13.58 13.47 13.30 13.10 13.17 13.36 12.92 13.14 13.36 13.52 4.01 100.0%
나일론 섬유의 형광 방출에 대한 색상 구분
색상 섬유 12 섬유 13 섬유 14 섬유 15
퍼플 2.51 2.25 2.47 2.44
블루 1.21 1.05 1.07 1.07
그린 0.45 0.46 0.41 0.27
옐로우 0.45 0.45 0.38 0.42
오렌지 0.30 0.30 0.25 0.32
레드 0.41 0.42 0.35 0.42
PBT 섬유의 형광 방출에 대한 색상 구분
색상 섬유 16 섬유 17 섬유 18 섬유 19 섬유 20
퍼플 12.13 0.47 0.17 0.19 0.78
블루 8.37 0.22 0.09 0.10 0.44
그린 0.05 0.02 0.01 0.01 0.02
옐로우 0.00 0.14 0.10 0.10 0.12
오렌지 0.00 0.19 0.13 0.13 0.17
레드 0.00 0.44 0.32 0.33 0.41
PMMA 섬유의 형광 방출에 대한 색상 구분
색상 섬유 21 섬유 22 섬유 23 섬유 24
퍼플 2.21 2.97 2.68 2.62
블루 0.78 1.41 1.24 2.25
그린 0.00 0.00 0.00 0.00
옐로우 0.03 0.02 0.02 0.01
오렌지 0.06 0.06 0.05 0.04
레드 0.10 0.12 0.12 0.09
섬유가 방출한 형광에 대한 중합체의 영향을 측정하고 준비된 다양한 섬유 사이에서 비교했다. 결과는 도 2d에 제시되어 있다. 이 데이터는 폴리에틸렌과 PBT로 만든 섬유가 가장 많이 형광을 내는 것을 보여준다.
상기 표시된 섬유의 형광 방출에 대한 색상 분류
색상 폴리에틸렌 폴리락트산 폴리프로필렌 나일론 PBT PMMA
퍼플 8.81 2.95 7.32 2.51 0.47 2.21
블루 5.08 1.47 4.00 1.21 0.22 0.78
그린 0.01 0.03 0.01 0.45 0.02 0.00
옐로우 0.00 0.08 0.00 0.45 0.14 0.03
오렌지 0.00 0.09 0.00 0.30 0.19 0.06
레드 0.01 0.09 0.00 0.41 0.44 0.10
실시예 4
광활성 섬유 밖으로 광활성화제의 누출
이 실험의 목적은 중합체가 광활성 섬유 밖으로 광활성화제의 누출에 영향을 미치는지 여부를 결정하는 것이었다. 누출은 0.1g의 섬유를 10ml의 물에 1일 동안 둔 다음 광활성화제의 존재에 대해 물을 평가함으로써 측정하였다. 도 3은 실시예 3에 정의된 바와 같이 광활성 섬유로부터 에오신의 누출을 도시한다. 도 4의 샘플에 대한 검출 한계는 0.0095 μg/ml이었다. 표 34는 이 실험 동안 얻어진 데이터를 개략적으로 나타낸 것이다. 표 34에 제시되고 도 3에 도시된 데이터는 폴리에틸렌으로 제조된 광활성 섬유 및 PBT로 제조된 광활성 섬유가 시험된 중합체들 중에서 에오신의 최소 누출을 나타낸다는 것을 제시하였다. 데이터는 또한 광활성화제를 섬유의 중합체와 화합하는 것이 광활성 섬유 밖으로 광활성화제의 누출을 실질적으로 일으키지 않는 것을 나타낸다.
광활성 섬유 광활성화제 용액 중 농도 (ppm) 누출%
1 화합됨 0.103 0.454
2 화합됨 0.116 0.510
3 화합됨 0.154 0.676
4 화합되고 코팅됨 0.351 1.544
5 화합됨 0.046 0.102
6 화합됨 0.046 0.102
7 화합됨 0.041 0.090
8 화합됨 0.048 0.211
9 화합됨 0.041 0.183
10 화합됨 0.049 0.214
11 화합되고 코팅됨 0.546 2.404
12 화합됨 0.022 0.099
13 화합됨 0.017 0.074
14 화합됨 0.065 0.286
15 화합되고 코팅됨 0.899 3.957
17 화합됨 BDL N/A
18 화합됨 BDL N/A
19 화합됨 BDL N/A
20 화합되고 코팅됨 0.184337 0.4055414
21 화합됨 0.102 0.224
22 화합됨 0.118 0.261
23 화합됨 0.184 0.405
24 화합되고 코팅됨 1.495 3.290
실시예 5
광활성 섬유에 의해 방출되는 형광에 대한 다양한 램프 높이의 영향
이 실험의 목적은 광활성 섬유의 형광 방출에 대한 청색 램프 높이를 변화시키는 효과를 결정하는 것이었다. 측정 값은 아래 표 35-38에 제시되어 있다.
청색 램프 출력
높이 (cm) 에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율
5 30.43
3.75 39.15 -1.25 8.72 22.28
2.5 49.78 -1.25 10.63 21.35
형광 방출에 대한 나일론 광활성 섬유로부터의 청색 램프 높이의 영향
높이
(cm) 		0-5 분 5-10 분
에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율 에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율
5 1.59 1.02
3.75 1.64 -1.25 0.05 3.19 0.96 -1.25 -0.06 -6.60
2.5 1.90 -1.25 0.26 15.66 1.09 -1.25 0.13 13.83
형광 방출에 대한 PBT 광활성 섬유로부터의 청색 램프 높이의 영향
높이
(cm) 		0-5 분 5-10 분
에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율 에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율
5 0.77 0.67
2.5 1.04 -2.50 0.28 26.54 0.80 -2.50 0.13 19.88
형광 방출에 대한 PLA 광활성 섬유로부터의 청색 램프 높이의 영향
높이
(cm) 		0-5 분 5-10 분
에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율 에너지 (J/cm 2 ) 높이 변화 에너지 변화 에너지 증가율
5 0.28 0.24
2.5 0.39 -2.50 0.11 27.25 0.25 -2.50 0.01 2.83
청색 램프 높이가 감소함에 따라, 광활성 섬유에 의해 생성된 형광 및 에너지는 비-선형 양상으로 증가한다. 나일론 섬유의 경우, 그 효과는 처음 5분 안에 나타난다. 형광 및 에너지는 형광의 경우 12.95 mW/cm2이고 에너지의 경우 1.90 J/cm2이다. 5분 후에는, 형광 및 에너지가 유사한 것으로 관찰되었다. PBT 섬유의 경우, 램프 높이를 감소시킴으로써 형광 및 에너지 둘 다 증가한다. 그러나, 광표백이 보다 빠르게 일어난다. PLA 섬유의 경우, 램프 높이를 감소시킴으로써 처음에는 형광이 증가한다. 광표백이 7분 후에 형광이 램프를 닫았을 때보다 낮게 되는 속도로 일어난다.
실시예 6
에오신 Y로부터 방출된 형광에 미치는 윤활제 첨가의 효과
이 실험의 목적은 윤활제의 첨가가 에오신 Y의 용액의 형광의 방출에 영향을 미치는지 평가하는 것이었다. 루롤 오일이 물 중의 에오신 Y의 용액에 첨가된 때 그 용액은 즉시 오렌지색으로부터 핑크색으로 바뀌었다. 또한 약간 거품이 발생할 수도 있다. 루롤 오일을 사용한 용액의 빠른 조사는 용액이 한 층이고, 완전히 혼화 가능하며, 가시적인 침전물은 없음을 나타낸다. 루롤 오일의 효과를 320 μL을 2mL의 109 μg/g 에오신 Y 용액에 첨가함으로써 비교하였다. 이들 두 가지 용액의 형광을 측정하여 루롤 오일이 어떠한 효과를 나타냈는지를 측정하였다 (도 4). 그 결과는, 루롤 오일 용액이 거의 2배의 형광이었고 거의 광분해되지 않는 것으로 보아, 루롤 오일이 에오신 Y 용액의 효과를 가졌음을 나타냈다. 또한, 루롤 오일의 형광은 적색 천이되어서, 일부 황색 및 오렌지색이 관찰되었다. 청색 램프 아래에서는 루롤 오일 용액은 거의 오렌지색으로 보이는 한편, 루롤 오일이 없는 용액은 녹색이었다.
실시예 7
광활성 섬유의 형광 방출에 미치는 윤활제 첨가의 효과
윤활제의 존재는 도핑된 섬유 및 그것들의 형광에 영향을 미치는 것으로 나타났다. 저농도의 발색단의 경우 그것은 약간 적색 천이될 수 있고, 표백 시간을 상당히 감소시킨다. 고농도의 발색단에서는, 적색 천이될 뿐 아니라, 형광도 증가시킨다. 가장 큰 효과는 10 g/L의 루롤 오일 근처인 것으로 나타난다. 초기에 에오신 Y 도핑된 섬유의 형광은 0.01이었지만 (도 5a), 루롤 오일의 첨가로 형광은 0.7로 부스팅되었다. 에오신 Y와 루롤 오일을 첨가한 동일한 농도의 플루오레세인에 대해 비교를 시행하였다. 그것들은 유사한 형광으로 출발한 한편, 플루오레세인 광분해가 더 빠른 것으로 나타났다 (도 5b).
실시예 8
다중 층의 광활성제를 가진 광활성 섬유의 제조
이 실험의 목적은 광활성제의 하나 이상의 층을 중합체 섬유 위에 첨가하는 것이 형광 방출에 영향을 미치는 지를 측정하는 것이었다. 이 목적을 위해, 다음의 광활성 섬유들을 제조하였다. 폴리프로필렌 중합체를 광활성제 (에오신 Y:플루오레세인)와 0.8 내지 1.0% w/w 근처에서 혼합한 다음 그 중합체를 경화시키고 작은 조각으로 잘랐다. 이 중합체를 호퍼 안으로 처리하고, 특정 ㎛ 크기의 섬유로 압출시켰다 (도 6a: 31㎛) (도 6b: 93㎛). 기계 헤드로부터 빠져나감에 따라, 그것은 루롤 오일 단독의 조성물로, 또는 루롤 오일과 광활성제의 조성물로, 또는 루롤 오일과 과산화 요소의 조성물로, 또는 루롤 오일과 중탄산 나트륨의 조성물로 분무되었다.
형광단의 양은 광활성 섬유의 전체 형광에 대한 결정요인이다. 층 수준이 증가함에 따라 전체 형광 또한 증가한다. 증가는 선형이지 않아서, 섬유 함량의 배가는 형광을 배가시키지 않는다. 그러나 6개 층이 동일 물질의 4 및 2층 둘 다보다 먼저 형성되는 것은 분명하다.
실시예 9
형광 방출에 미치는 광활성제의 다중 층의 영향
발색단이 중합체 섬유의 표면상에 위치할 때, 층의 수의 증가는 또한 중합체 섬유의 형광을 증가시킨다. 발색단이 내부에 있을 때, 반대현상이 일어나는데, 층의 수의 증가는 전체 형광을 감소시킨다. 광활성 섬유를 실시예 8에서 기술한 것과 같이 제조하였다. 광표백은 발색단이 내부에 있을 때 보다 빠르게 일어난다 (도 7). 4층 50 g/L 에오신 Y 외부를 시도 2와 비교하고 4층 0.5% 에오신 Y 내부를 시도 3과 비교할 때, 광표백 속도는 에오신 Y를 나일론과 합성할 때보다 더 빠르다. 나일론 시도 3이 나일론 시도 2보다 더 성공적이었다. 섬유 내에 발색단이 더 적고 층이 더 적으면, 섬유를 발색단으로 코팅할 때보다 더 형광을 나타냈다. 그러나, 광표백은 훨씬 더 빠른 속도로 일어난다. 10분 후 그것들 사이에 2 mW/cm2의 차이가 관찰된다.
방출된 형광의 색상 구분
색상 시도 2
4 층
50g/L 에오신 Y 		시도 2
2 층
50g/L E:F 		시도 2
4 층
50g/L E:F 		시도 3
2 층
0,5% 에오신 내부
루롤 오일 외부 		시도 3
4 층
0,5% 에오신 내부
루롤 오일 외부
퍼플 2.63 6.21 1.87 2.51 0.29
블루 1.27 3.49 0.90 1.21 0.08
그린 0.22 0.32 0.31 0.45 0.21
옐로우 0.56 0.47 0.66 0.45 0.35
오렌지 0.44 0.34 0.51 0.30 0.26
레드 0.50 0.27 0.60 0.41 0.41
나일론 실행 1-103㎛ E/F 10g/L- 4 층 0-5분
나일론 실행 1-103㎛ E/F 10g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 21.47 24.99 25.79 26.31 26.83 27.22 27.44 27.69 27.95 28.21 28.36 7.92 87.0%
형광 519-760 3.12 5.17 4.70 4.34 4.03 3.85 3.68 3.53 3.49 3.32 3.17 1.18 12.9%
합계 400-760 24.58338 30.15935 30.49297 30.65144 30.85972 31.07188 31.11921 31.21439 31.43356 31.52938 31.53128 9.09 99.9%
형광% 　 12.7% 17.1% 15.4% 14.2% 13.1% 12.4% 11.8% 11.3% 11.1% 10.5% 10.0% 0.13 12.9%
퍼플 (400)-450 14.2387 15.8609 16.1645 16.2767 16.4031 16.5001 16.5381 16.5781 16.6734 16.7323 16.7269 4.86 53.4%
블루 450-500 7.2285 8.9835 9.4986 9.9158 10.3133 10.6121 10.7933 11.0066 11.1705 11.3788 11.5401 3.03 33.3%
그린 500-570 1.2302 2.1414 1.9567 1.7172 1.5957 1.5291 1.4669 1.4155 1.3995 1.3350 1.2853 0.47 5.2%
옐로우 570-591 1.1034 1.4359 1.3037 1.1519 1.0679 1.0119 0.9749 0.9367 0.9109 0.8637 0.8309 0.32 3.5%
오렌지 591-610 0.6207 0.8740 0.7901 0.7554 0.7005 0.6657 0.6391 0.6134 0.5987 0.5662 0.5442 0.20 2.2%
레드 610-760 0.1814 0.8965 0.8084 0.8645 0.8071 0.7795 0.7324 0.6883 0.7045 0.6760 0.6255 0.21 2.4%
합계 (400-700) 24.60 30.19 30.52 30.68 30.89 31.10 31.14 31.24 31.46 31.55 31.55 9.10 100.0%
나일론 실행 1-103㎛ E/F 20g/L- 4 층 0-5분
나일론 실행 1-103㎛ E/F 20g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 19.40 21.27 22.67 22.77 23.13 23.67 24.11 24.51 24.92 25.30 25.57 6.95 80.2%
형광 519-760 7.72 6.40 5.79 5.81 5.63 5.45 5.18 5.03 4.87 4.75 4.66 1.70 19.6%
합계 400-760 27.12141 27.67375 28.45756 28.58048 28.76461 29.12852 29.29128 29.53686 29.79402 30.04862 30.22247 8.65 99.9%
형광% 　 28.5% 23.1% 20.4% 20.3% 19.6% 18.7% 17.7% 17.0% 16.4% 15.8% 15.4% 0.20 19.6%
퍼플 (400)-450 12.6847 13.4080 14.0379 14.1004 14.2567 14.5022 14.6514 14.8214 14.9772 15.1395 15.2521 4.28 49.4%
블루 450-500 6.6370 7.7965 8.5687 8.6018 8.8139 9.1072 9.4021 9.6311 9.8833 10.0927 10.2565 2.66 30.7%
그린 500-570 2.2366 1.8797 1.6972 1.7004 1.6593 1.6050 1.5366 1.4934 1.4625 1.4331 1.4059 0.50 5.8%
옐로우 570-591 2.4298 1.9811 1.7822 1.7786 1.7244 1.6595 1.5891 1.5402 1.4879 1.4429 1.4163 0.52 6.0%
오렌지 591-610 1.5572 1.2861 1.1626 1.1594 1.1250 1.0824 1.0351 1.0043 0.9687 0.9394 0.9180 0.34 3.9%
레드 610-760 1.6340 1.3711 1.2534 1.2832 1.2280 1.2135 1.1167 1.0842 1.0517 1.0368 1.0080 0.37 4.2%
합계 (400-700) 27.18 27.72 28.50 28.62 28.81 29.17 29.33 29.57 29.83 30.08 30.26 8.66 100.0%
나일론 실행 7 플루오레세인 35g/L- 4 층 0-5분
나일론 실행 7 플루오레세인 35g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 10.68 11.92 12.89 13.63 14.33 14.95 15.60 16.21 16.71 17.21 17.61 4.32 65.4%
형광 519-760 10.30 9.13 8.49 8.01 7.59 7.16 6.83 6.42 6.17 5.88 5.65 2.28 34.5%
합계 400-760 20.98009 21.05839 21.38843 21.64094 21.92016 22.11076 22.42923 22.63264 22.88359 23.0868 23.25756 6.60 99.9%
형광% 　 49.1% 43.4% 39.7% 37.0% 34.6% 32.4% 30.4% 28.4% 27.0% 25.5% 24.3% 0.35 34.5%
퍼플 (400)-450 6.7401 7.2458 7.6859 8.0035 8.3020 8.5583 8.8489 9.0966 9.3179 9.5100 9.6820 2.50 37.8%
블루 450-500 3.5037 4.2174 4.7250 5.1256 5.5065 5.8505 6.2007 6.5468 6.8184 7.1173 7.3422 1.67 25.2%
그린 500-570 6.4483 5.8166 5.4777 5.2332 5.0226 4.8153 4.6339 4.4415 4.3017 4.1459 4.0237 1.51 22.8%
옐로우 570-591 1.8820 1.6354 1.4990 1.3971 1.3096 1.2236 1.1540 1.0778 1.0244 0.9718 0.9246 0.40 6.0%
오렌지 591-610 1.0807 0.9469 0.8767 0.8197 0.7732 0.7270 0.6870 0.6431 0.6127 0.5811 0.5564 0.23 3.5%
레드 610-760 1.3665 1.2324 1.1575 1.0932 1.0361 0.9634 0.9312 0.8515 0.8318 0.7831 0.7505 0.31 4.6%
합계 (400-700) 21.02 21.09 21.42 21.67 21.95 22.14 22.46 22.66 22.91 23.11 23.28 6.61 100.0%
나일론 실행 9C-103㎛ E/F 30/7.5/7.5- 4 층 0-5분
나일론 실행 9C-103㎛ E/F 30/7.5/7.5- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 20.92 21.07 21.36 21.56 21.77 21.82 21.92 22.02 22.17 22.33 22.48 6.51 94.0%
형광 519-760 1.54 1.41 1.39 1.36 1.36 1.34 1.34 1.33 1.29 1.31 1.30 0.41 5.9%
합계 400-760 22.45942 22.48255 22.74403 22.9241 23.12528 23.16169 23.26146 23.35004 23.46191 23.64257 23.78278 6.92 99.9%
형광% 　 6.9% 6.3% 6.1% 5.9% 5.9% 5.8% 5.8% 5.7% 5.5% 5.5% 5.5% 0.06 5.9%
퍼플 (400)-450 14.2461 14.0180 14.0744 14.0780 14.0611 14.0484 14.0565 14.0161 14.0168 14.0343 14.0449 4.22 60.9%
블루 450-500 6.6739 7.0542 7.2817 7.4833 7.7090 7.7720 7.8656 8.0056 8.1532 8.3002 8.4356 2.29 33.1%
그린 500-570 0.0700 0.0640 0.0625 0.0652 0.0690 0.0682 0.0698 0.0715 0.0696 0.0761 0.0801 0.02 0.3%
옐로우 570-591 0.3880 0.3600 0.3510 0.3480 0.3480 0.3455 0.3465 0.3454 0.3405 0.3456 0.3501 0.11 1.5%
오렌지 591-610 0.5250 0.4839 0.4742 0.4657 0.4584 0.4548 0.4544 0.4491 0.4407 0.4421 0.4408 0.14 2.0%
레드 610-760 0.5830 0.5270 0.5243 0.5075 0.5028 0.4956 0.4916 0.4848 0.4631 0.4663 0.4531 0.15 2.2%
합계 (400-700) 22.49 22.51 22.77 22.95 23.15 23.18 23.28 23.37 23.48 23.66 23.80 6.93 100.0%
폴리프로필렌 실행 10 플루오레세인 35g/L- 4 층 0-5분
폴리프로필렌 실행 10 플루오레세인 35g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 34.75 35.18 35.26 35.19 35.26 35.20 35.11 35.10 34.95 34.88 34.86 10.53 98.7%
형광 519-760 0.58 0.63 0.60 0.46 0.45 0.41 0.38 0.37 0.31 0.30 0.29 0.13 1.3%
합계 400-760 35.32948 35.80934 35.85791 35.65735 35.70358 35.60884 35.48748 35.47158 35.25517 35.18271 35.15384 10.66 100.0%
형광% 　 1.6% 1.8% 1.7% 1.3% 1.3% 1.1% 1.1% 1.0% 0.9% 0.9% 0.8% 0.01 1.3%
퍼플 (400)-450 21.5860 21.4518 21.3402 20.8147 20.7911 20.6313 20.4316 20.3492 20.1362 20.0194 19.9225 6.23 58.4%
블루 450-500 13.0286 13.5733 13.7616 14.2367 14.3212 14.4363 14.5448 14.6194 14.6803 14.7432 14.8173 4.26 39.9%
그린 500-570 0.5551 0.5656 0.5458 0.4488 0.4390 0.4082 0.3877 0.3818 0.3440 0.3258 0.3198 0.13 1.2%
옐로우 570-591 0.1004 0.1011 0.0941 0.0763 0.0704 0.0666 0.0622 0.0591 0.0486 0.0467 0.0454 0.02 0.2%
오렌지 591-610 0.0477 0.0609 0.0577 0.0443 0.0441 0.0397 0.0369 0.0364 0.0289 0.0289 0.0273 0.01 0.1%
레드 610-760 0.0132 0.0590 0.0608 0.0382 0.0396 0.0282 0.0258 0.0271 0.0182 0.0197 0.0226 0.01 0.1%
합계 (400-700) 35.33 35.81 35.86 35.66 35.71 35.61 35.49 35.47 35.26 35.18 35.15 10.66 100.0%
폴리프로필렌 실행 12 에오신 y 25g/L- 4 층 0-5분
폴리프로필렌 실행 12 에오신 y 25g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 20.35 20.29 20.27 20.23 20.19 20.17 20.12 20.13 20.09 20.11 20.09 6.06 96.2%
형광 519-760 0.84 0.81 0.80 0.79 0.78 0.78 0.77 0.77 0.76 0.76 0.76 0.24 3.7%
합계 400-760 21.1856 21.09802 21.06914 21.02316 20.96994 20.94642 20.8899 20.89411 20.85018 20.8722 20.85232 6.29 100.0%
형광% 　 4.0% 3.8% 3.8% 3.8% 3.7% 3.7% 3.7% 3.7% 3.6% 3.7% 3.7% 0.04 3.7%
퍼플 (400)-450 13.7608 13.4286 13.2875 13.1247 12.9928 12.8698 12.7363 12.6547 12.5548 12.4838 12.4130 3.90 61.9%
블루 450-500 6.5846 6.8630 6.9810 7.1075 7.1948 7.2987 7.3816 7.4711 7.5354 7.6239 7.6759 2.16 34.3%
그린 500-570 0.1434 0.1414 0.1371 0.1356 0.1310 0.1287 0.1287 0.1258 0.1257 0.1261 0.1258 0.04 0.6%
옐로우 570-591 0.2980 0.2976 0.2957 0.2925 0.2902 0.2867 0.2854 0.2838 0.2835 0.2843 0.2841 0.09 1.4%
오렌지 591-610 0.2576 0.2460 0.2432 0.2400 0.2387 0.2383 0.2366 0.2356 0.2336 0.2341 0.2328 0.07 1.1%
레드 610-760 0.1509 0.1306 0.1338 0.1319 0.1314 0.1333 0.1302 0.1320 0.1260 0.1290 0.1295 0.04 0.6%
합계 (400-700) 21.20 21.11 21.08 21.03 20.98 20.96 20.90 20.90 20.86 20.88 20.86 6.30 100.0%
폴리프로필렌 실행 15B E/F/RB 20/5/5 (g/L)- 4 층 0-5분
폴리프로필렌 실행 15B E/F/RB 20/5/5 (g/L)- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 25.41 25.50 25.59 25.65 25.72 25.76 25.80 25.82 25.85 25.91 25.94 7.71 97.2%
형광 519-760 0.83 0.78 0.76 0.74 0.73 0.72 0.71 0.70 0.69 0.68 0.68 0.22 2.8%
합계 400-760 26.23634 26.28132 26.34717 26.39618 26.44999 26.4881 26.5104 26.51969 26.5395 26.5943 26.62222 7.93 100.0%
형광% 　 3.2% 3.0% 2.9% 2.8% 2.8% 2.7% 2.7% 2.6% 2.6% 2.6% 2.6% 0.03 2.8%
퍼플 (400)-450 16.5085 16.3661 16.2357 16.1308 16.0312 15.9348 15.8525 15.7523 15.7119 15.6652 15.6041 4.81 60.6%
블루 450-500 8.8967 9.1325 9.3518 9.5209 9.6896 9.8291 9.9452 10.0682 10.1388 10.2448 10.3347 2.90 36.6%
그린 500-570 0.0424 0.0335 0.0338 0.0317 0.0318 0.0339 0.0339 0.0342 0.0351 0.0372 0.0380 0.01 0.1%
옐로우 570-591 0.2430 0.2265 0.2220 0.2187 0.2144 0.2158 0.2143 0.2133 0.2104 0.2097 0.2118 0.07 0.8%
오렌지 591-610 0.2914 0.2797 0.2711 0.2657 0.2593 0.2577 0.2525 0.2497 0.2456 0.2409 0.2387 0.08 1.0%
레드 610-760 0.2676 0.2562 0.2455 0.2408 0.2358 0.2289 0.2237 0.2135 0.2088 0.2076 0.2058 0.07 0.9%
합계 (400-700) 26.25 26.29 26.36 26.41 26.46 26.50 26.52 26.53 26.55 26.61 26.63 7.93 100.0%
폴리에틸렌 외피 포함 폴리프로필렌 코어, 플루오레세인, 30g/L- 4 층 0-5분
폴리에틸렌 외피 포함 폴리프로필렌 코어, 플루오레세인, 30g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 23.10 24.18 24.29 24.54 24.89 25.20 25.33 25.54 25.68 25.76 25.83 7.46 95.1%
형광 519-760 1.91 1.56 1.52 1.43 1.27 1.16 1.06 0.99 0.96 0.88 0.84 0.38 4.9%
합계 400-760 25.01102 25.73662 25.8135 25.97069 26.16178 26.35745 26.39481 26.52577 26.64275 26.64462 26.66904 7.84 100.0%
형광% 　 7.6% 6.0% 5.9% 5.5% 4.9% 4.4% 4.0% 3.7% 3.6% 3.3% 3.1% 0.05 4.9%
퍼플 (400)-450 14.4848 14.7578 14.8113 14.8620 14.9236 14.9942 14.9548 14.9895 14.9871 14.9555 14.9339 4.46 56.9%
블루 450-500 8.4257 9.2502 9.3024 9.5154 9.8149 10.0590 10.2412 10.4189 10.5712 10.6820 10.7803 2.95 37.6%
그린 500-570 1.2588 1.0645 1.0456 0.9803 0.8771 0.8112 0.7264 0.6795 0.6468 0.6059 0.5693 0.26 3.3%
옐로우 570-591 0.3698 0.3003 0.2976 0.2783 0.2503 0.2278 0.2113 0.1983 0.1879 0.1763 0.1669 0.07 1.0%
오렌지 591-610 0.2250 0.1784 0.1778 0.1635 0.1457 0.1334 0.1285 0.1196 0.1159 0.1082 0.1014 0.04 0.6%
레드 610-760 0.2560 0.1919 0.1862 0.1777 0.1555 0.1368 0.1378 0.1247 0.1385 0.1210 0.1213 0.05 0.6%
합계 (400-700) 25.02 25.74 25.82 25.98 26.17 26.36 26.40 26.53 26.65 26.65 26.67 7.84 100.0%
폴리프로필렌 코어/폴리에틸렌 외피, E:F:RB, 20g/:5g/L:5g/L- 4 층 0-5분
폴리프로필렌 코어/폴리에틸렌 외피, E:F:RB, 20g/:5g/L:5g/L- 4 층 0-5분 mW/cm2 5cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 23.53 23.65 23.69 23.72 23.77 23.77 23.83 23.87 23.92 23.96 23.99 7.13 96.5%
형광 519-760 0.98 0.94 0.89 0.87 0.85 0.83 0.82 0.82 0.80 0.79 0.78 0.26 3.5%
합계 400-760 24.50132 24.58279 24.58891 24.59305 24.62182 24.6087 24.65408 24.69701 24.72073 24.74822 24.7711 7.39 99.9%
형광% 　 4.0% 3.8% 3.6% 3.5% 3.4% 3.4% 3.3% 3.3% 3.2% 3.2% 3.1% 0.03 3.5%
퍼플 (400)-450 15.7772 15.6065 15.4681 15.3450 15.1697 15.0644 15.0060 14.9231 14.8477 14.7970 14.7369 4.56 61.7%
블루 450-500 7.7480 8.0411 8.2265 8.3771 8.6030 8.7102 8.8288 8.9500 9.0729 9.1644 9.2549 2.57 34.8%
그린 500-570 0.0396 0.0323 0.0291 0.0276 0.0286 0.0265 0.0275 0.0271 0.0281 0.0282 0.0282 0.01 0.1%
옐로우 570-591 0.2661 0.2586 0.2495 0.2456 0.2394 0.2338 0.2327 0.2335 0.2282 0.2260 0.2240 0.07 1.0%
오렌지 591-610 0.3425 0.3369 0.3225 0.3156 0.3047 0.3008 0.2960 0.2944 0.2866 0.2829 0.2797 0.09 1.3%
레드 610-760 0.3442 0.3234 0.3087 0.2973 0.2910 0.2873 0.2772 0.2830 0.2709 0.2632 0.2605 0.09 1.2%
합계 (400-700) 24.52 24.60 24.60 24.61 24.64 24.62 24.67 24.71 24.73 24.76 24.78 7.39 100.0%
Royal Carolina 매질, 에오신:플루오레세인, 1 층
Royal Carolina 매질, 에오신:플루오레세인, 1 층 mW/cm2 5 cm 　
　 0 0, 5 분 1 분 1, 5 분 2 분 2, 5 분 3 분 3, 5 분 4 분 4, 5 분 5 분 J/cm2 　
램프 400-518 45.18 44.92 44.87 44.82 44.75 44.69 44.66 44.59 44.59 44.57 44.54 13.43 98.4%
형광 519-760 0.78 0.79 0.78 0.75 0.73 0.72 0.70 0.68 0.67 0.66 0.65 0.22 1.6%
합계 400-760 45.96064 45.70756 45.64751 45.57463 45.4783 45.41009 45.36403 45.26928 45.2666 45.23608 45.19001 13.65 100.0%
형광% 　 1.7% 1.7% 1.7% 1.7% 1.6% 1.6% 1.5% 1.5% 1.5% 1.5% 1.4% 0.02 1.6%
퍼플 (400)-450 27.0635 26.5869 26.4423 26.2921 26.1306 25.9930 25.8850 25.7933 25.7023 25.6407 25.5755 7.85 57.5%
블루 450-500 18.1148 18.3232 18.4223 18.5199 18.6103 18.6862 18.7644 18.7845 18.8782 18.9181 18.9484 5.58 40.9%
그린 500-570 0.2912 0.2955 0.2929 0.2800 0.2687 0.2667 0.2642 0.2519 0.2550 0.2530 0.2491 0.08 0.6%
옐로우 570-591 0.2904 0.2976 0.2912 0.2858 0.2791 0.2745 0.2699 0.2593 0.2589 0.2526 0.2481 0.08 0.6%
오렌지 591-610 0.1584 0.1609 0.1572 0.1555 0.1516 0.1508 0.1445 0.1426 0.1381 0.1355 0.1327 0.04 0.3%
레드 610-760 0.0470 0.0485 0.0466 0.0461 0.0425 0.0436 0.0404 0.0421 0.0382 0.0404 0.0403 0.01 0.1%
합계 (400-700) 45.97 45.71 45.65 45.58 45.48 45.41 45.37 45.27 45.27 45.24 45.19 13.65 100.0%
실시예 10
재- 침지된 광활성 섬유의 형광 방출
물 중의 에오신 Y의 용액을 0.1 g/L의 농도로 제조하였고, 두 개의 폴리프로필렌 섬유를 발색단으로 섬유를 도핑하기 위해 그 용액에 침지하였다. 그런 다음 섬유를 제1 일에 볼 수 있는 그것들의 형광에 대해 조사하여 그것들이 물에 침지되는 경우 얼마나 많은 발색단이 보유되는지 뿐만 아니라 시간 경과에 따라 형광을 얼마나 잘 보유하는지를 측정하였다. 이 실험으로부터, 섬유의 팁이 3일 후에 형광을 보유하고 있음을 알 수 있다.
도 8a 및 8b는 1일 후 청색 램프 아래에서의 형광 방출을 도시하며, 이때 섬유는 물에서 드러나지 않았다. 도 8c 및 8d는 3일 후 청색 램프 아래에서의 형광 방출을 도시하며, 이때 섬유는 물에서 드러나지 않았다. 도 8e 및 8f는 물에서 드러난 3일 후 청색 램프 아래에서의 형광 방출을 나타낸다.
실시예 11
치섬유 도핑의 정성 분석
시판중인 치섬유를 에오신 Y의 용액 (300 g/L, 200 g/L, 100 g/L, 50 g/L, 10 g/L, 1 g/L 또는 0.1 g/L)에 10초 동안 침지하였다. 섬유를 꺼내어 색을 관찰한 후, 청색 램프 아래 두고 형광을 정성적으로 관찰하였다. 300 내지 100 g/L의 에오신 Y 용액은 거의 형광을 나타내지 않은 한편, 50 g/L의 에오신 Y 용액은 형광을 나타냈다. 형광의 유의미한 증가가 10 g/L의 에오신 Y 용액을 사용했을 때 관찰되었다.
치섬유를 플루오레세인 용액 (50 g/L, 10 g/L, 1 g/L, 0.1 g/L)에 10초 동안 침지하였다. 그런 다음 섬유를 꺼내어 색을 관찰한 후, 청색 램프 아래 두고 형광을 정성적으로 관찰하였다. 50 g/L의 플루오레세인 용액이 형광을 나타냈다.
치섬유를 플루오레세인의 용액에 침지하였다: 10초 동안 다시 에오신 Y 1:1 ((50 g/L, 10 g/L, 1 g/L, 0.1 g/L의 총 발색단) 용액. 그런 다음 섬유를 꺼내어 색을 관찰한 후, 청색 램프 아래 두고 형광을 정성적으로 관찰하였다. 50 g/L의 플루오레세인: 에오신 Y 1:1 용액은 거의 형광을 나타내지 않았다. 형광의 유의미한 증가가 10 g/L의 플루오레세인일 때 관찰되었다: 에오신 Y 1:1 용액을 사용하였다.
도 9a 내지 9p는 광활성제의 용액에 침지된 섬유들, 즉 에오신 Y 50 g/L 중의 시판중인 치섬유 (도 9a 및 9b); 에오신 Y 0.1 g/L 중의 시판중인 치섬유 (도 9c및 9d); 플루오레세인 50 g/L 중의 시판중인 치섬유 (도 9e 및 19f); 플루오레세인 0.1 g/L 중의 시판중인 치섬유 (도 9g 및 9h); 플루오레세인:에오신 Y 50 g/L 중의 시판중인 치섬유 (도 9i 및 9j); 플루오레세인:에오신 Y 0.1 g/L 중의 시판중인 치섬유 (도 9k 및 9l); 플루오레세인 50 g/L 중의 폴리프로필렌 섬유 (도 9m 및 9n); 플루오레세인 0.1 g/L 중의 폴리프로필렌 섬유 (도 9o 및 9p)의 청색 램프 아래에서의 형광 방출 사진들을 도시한다.
폴리프로필렌 섬유를 플루오레세인 용액 (50 g/L, 10 g/L, 1 g/L, 0.1 g/L의 총 발색단)에 10초 동안 침지한 후, 꺼내어 색을 관찰한 다음, 청색 램프 아래 두고 형광을 정성적으로 관찰하였다. 50 g/L 플루오레세인 용액은 거의 형광을 나타내지 않았다. 형광의 증가는 10 g/L의 플루오레세인 용액을 사용하였을 때 관찰되었다.
실시예 12
광활성 직물의 제조
광활성 직물의 제조에 사용된 폴리프로필렌 섬유를 Midwest Filtration (West Chester Township, 미국 오하이오주.)으로부터 얻었다. 시험한 직물은 0.45 oz/yd2 내지 2.50 oz/yd2 범위의 밀도의 폴리프로필렌으로 구성되었다. 2.00 oz/yd2의 밀도의 폴리프로필렌 직물이 상당한 양의 발색단을 흡수한 한편, 높은 두께보다 적은 광을 차단한 것으로 (데이터는 제시하지 않음) 관찰되었다. 직물 조각을 루롤 오일 PP-3771이 없는 작은 발색단 배스에 침지한 한편 다른 직물 조각을 루롤 오일 PP-3771을 포함한 작은 발색단 배스에 침지하였다. 그런 다음 침지된 직물을 롤 건조시키고 오븐에서 가열하였다. 광활성 직물의 제조 공정을 도 10에 도시한다.
실시예 13
광활성 제조 물품의 제조
광활성 직물을 포함하는 제조 물품을 구상하였다. 특히, 제조 물품은 섬유를 포함하는 직물로 만들어진 수트다 (도 11a). 일부 경우에, 직물의 조성물에 들어가는 섬유들은 순수 중합체, 즉 말하자면 광활성제를 포함하지 않은 중합체로 만들어질 수 있다. 일부 다른 경우에, 직물의 조성물에 들어가는 섬유들은 광활성제를 포함하는 광활성 섬유로 만들어질 수 있다. 직물이 순수 중합체로 만들어진 섬유를 포함하는 경우에, 그 직물 또는 이러한 직물로 만들어진 제조 물품은 광활성제를 직물 위로 및 직물의 섬유들 사이에 생성된 작은 틈 안으로 증착시키기 위하여 광활성제 조성물로 코팅되거나, 침지되거나 또는 분무될 수 있다 윤활제 조성물이 또한 직물의 섬유들 사이에 생성된 작은 틈 안으로 광활성제의 삽입을 촉진하기 위해 직물 위에 놓일 수 있다. 이 특정 예에서 제조 물품은 광선치료를 필요로 하는 대상이 입게 되는 수트이다 (도 11a). 수트의 제작에 포함시키기에 바람직한 광활성 섬유는 하나 이상의 광활성제를 포함하는 나일론 및 폴리에틸렌을 포함한다. 그 결과의 제조 물품 (예컨대 수트-형 의상)을 그런 다음 광 아래에서 광활성화시키는 한편 광선치료를 필요로 하는 대상이 입도록 하였다.
수트-형 의상을 다음의 조성을 가지는 2가지 광활성 직물을 연결시킴으로써 제조하였다:
(1) 광활성 직물 #1을 폴리프로필렌 섬유로부터 만들었다. 그 결과의 직물을 0.50 g/L 에오신 Y + 루롤 오일의 조성물에 침지하였다.
(2) 광활성 직물 #2를 폴리프로필렌 섬유로부터 만들었다. 그 결과의 직물을 0.25 g/L 에오신 Y + 0.25 g/L 플루오레세인 + 루롤 오일의 조성물에 침지하였다.
나란히 놓은 광활성 직물을 도 11b에 도시된 수트-형 의상으로 재단하였다. 2개의 직물을 연결시키고, 꿰매고, 접착시키고, 부착시키고, 융합시키고, 바느질하고, 또는 결합시키는 등등, 그런 다음 따라서 재단하였다.
실시예 14
광활성 직물을 사용한 사이토킨 및 성장 인자 조정
이 실험의 목적은 사이토킨 및 성장 인자의 분비에 미치는 본 발명의 광활성 섬유의 효과를 평가하는 것이었다. 이 목적을 위해, 청색 램프 (129.53mW/cm2)를 인간 피부 섬유아세포 (계대 #3 (70,000 세포/웰)) 샘플 단계의 상부 또는 바닥 어느 한 쪽에 5 cm 간격으로 배치하였다. 아래의 표 50에서 확인한 광활성 직물을 관례대로 만들어진 플라스틱 프레임 주위에 랩핑하였다 (1 내지 3회 회전). 슬라이드를 ~1 내지 1.4 ml의 PBS로 채우고 섬유 바로 위 단계에 직접 배치하였다. 조사를 바닥으로부터 상부로 옮겼다. 세포를 대부분의 섬유 및 매질에 대해 13-15J/cm2 동안 또는 5 J/cm2 동안 조사하였다. 그런 다음 세포를 24시간 동안 정상 매질/IFNg에서 인큐베이션하고 상층액을 수집하여 -80에서 저장하였다. 수집한 상층액에 대해 항체 어레이 분석을 수행하였고 사이토킨 및 성장 인자의 발현 수준을 분석하고 IFNg 자극된 세포에 표준화하였다. 그 결과를 표 51에 나타내는데, 그것은 미처리된 대조와만 비교한 발현 수준의 적어도 50% 차이를 기준으로 한다.
광활성 섬유/직물의 조성
광활성 섬유/직물 조성물
36 직물 1 - 폴리프로필렌 섬유 (블랭크 - 광활성화제 없음)
37 직물 2 - 폴리프로필렌 섬유 + 에오신 Y
38 직물 3 - 폴리프로필렌 섬유 + 에오신 y 및 플루오레세인
39 직물 1+1 (2 층)
40 직물 2+3 (2 층)
광활성 직물의 생물학적 효과
샘플 직물 1 (블랭크) 직물 2 (E) 직물 3 (E/F) 직물 2+3 (E+E/F)
광자 평가 P=10.11, B=6.70, G=0.04, Y=0.00, O=0.00, R=0.00 P=7.41, B=4.37, G=0.09, Y=0.16, O=0.11, R=0.05 P=6.69, B=4.25, G=0.13, Y=0.15, O=0.09, R=0.03 P=5.30, B=2.86, G=0.14, Y=0.26, O=0.20, R=0.10
투여량 15 J/cm2 15 J/cm2 15 J/cm2 15 J/cm2
조정 ↓ ↑ ↓ ↑ ↓ ↑ ↓ ↑
사이토킨 , 케모카인 및 성장 인자 --------- -------- ---------- IL-6, GM-CSF, MCP-2 ---------- GM-SCF, IL-2, IL-13, GROα, MCP-2, MCP-3, ANG G-SCF, I-309, IL-15, IL-7, MDC, TGFβ1, GROα, IGF-1 ANG
P= 퍼플, B= 블루, G= 그린, Y = 옐로우, O = 오렌지, R = 레드
위에 표시된 결과는 각 매질에 대해 최소 두 개의 독립적인 실험에서 나온 결과이다.
결과는 조합된 (층상) 매질 2 (에오신) 및 매질 3 (에오신/플루오레세인)의 조사가 I-309, IL-15, IL-7, MDC, TGFβ1, GROα 및 IGF-1의 하향 조절에 긍정적인 영향을 미칠 수 있다. 이들 사이토킨 및 케모카인은 접촉 알레르기성 피부염 (I-309, IL-7), 건선 (GROα, IL-15, IGF-1), 아토피성 피부염 (MDC) 및 흉터 (TGFβ1)와 같은 상태에 포함된다. 그러나, 이들 병리학은 복합적이고 통상적으로 더 많은 단백질의 조정이 바람직할 것이다.
본 발명을 검토한 후에 당 기술분야의 숙련자에게 변형예들 및 변경예들이 떠오를 것이다. 개시된 특징부들은 본원에서 설명된 하나 이상의 다른 특징부와 임의의 조합 및 하위 조합(다수의 의존형 조합 및 하위 조합을 포함함)으로 구현될 수 있다. 임의의 구성요소들을 포함하는, 상기에서 설명 또는 도시된 다양한 특징부는 다른 시스템들에 조합되거나 일체화될 수 있다. 또한, 소정의 특징부들이 생략될 수 있거나 구현되지 않는다. 변경, 치환, 및 변형의 예는 당업자에 의해 확인가능하며 본원에 개시된 내용의 범위를 벗어나지 않고 이루어질 수 있다. 본원에서 인용된 모든 참조는 그들 전체가 참조로 포함되며, 본원의 일부를 이룬다.

Claims (84)

  1. 광활성 섬유로서,
    - 적어도 하나의 열가소성 중합체, 및
    - 적어도 하나의 광활성제를 포함하고;
    여기서 상기 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는, 광활성 섬유.
  2. 제1항에 있어서,
    상기 적어도 하나의 광활성제는 상기 적어도 하나의 열가소성 중합체와 화합되는, 광활성 섬유.
  3. 제2항에 있어서,
    상기 적어도 하나의 광활성제는 상기 광활성 섬유 전반에 균일하게 분산되어 있는, 광활성 섬유.
  4. 제2항에 있어서,
    상기 적어도 하나의 광활성제는 상기 광활성 섬유 전반에 불균일하게 분산되어 있는, 광활성 섬유.
  5. 제1항 또는 제2항에 있어서,
    상기 적어도 하나의 광활성제는 상기 광활성 섬유의 표면 상에 적층되어 있는, 광활성 섬유.
  6. 제1항 또는 제2항에 있어서,
    상기 적어도 하나의 광활성제의 제1 부분은 상기 적어도 하나의 열가소성 중합체와 화합되고, 상기 적어도 하나의 광활성제의 제2 부분은 상기 광활성 섬유의 표면 상에 적층되어 있는, 광활성 섬유.
  7. 제5항 또는 제6항에 있어서,
    상기 광활성 섬유는 그 표면 상에 상기 적어도 하나의 광활성제의 적어도 하나의 층을 포함하는, 광활성 섬유.
  8. 제5항 또는 제6항에 있어서,
    상기 광활성 섬유는 그 표면 상에 상기 적어도 하나의 광활성제의 둘 이상의 층을 포함하는, 광활성 섬유.
  9. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 아크릴, 아크릴로니트릴 부타디엔 스티렌 (ABS), 폴리벤즈이미다졸 (PBI), 폴리카보네이트, 폴리에테르 술폰 (PES), 폴리에테르에테르 케톤 (PEEK), 폴리에테르이미드 (PEI), 폴리에틸렌 (PE), 폴리페닐렌 옥사이드 (PPO), 폴리페닐렌 설파이드 (PPS), 폴리프로필렌 (PP), 폴리스티렌, 폴리 염화비닐 (PVC), 테플론, 폴리부틸렌, 폴리에틸렌 테레프탈레이트 (PET), 폴리부틸렌 테레프탈레이트 (PBT), 나일론, 폴리락트산 (PLA), 폴리메틸 메타크릴레이트 폴리에스테르, 폴리우레탄, 레이온, 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 광활성 섬유.
  10. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 나일론, 폴리에틸렌 (PE), 폴리프로필렌 (PP), 폴리락트산 (PLA), 폴리부틸렌 테레프탈레이트 (PBT), 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 광활성 섬유.
  11. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 나일론인, 광활성 섬유.
  12. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리에틸렌인, 광활성 섬유.
  13. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리프로필렌인, 광활성 섬유.
  14. 제1항 내지 제13항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 에오신 Y, 에오신 B, 에리트로신, 플루오레세인, 로즈 벵갈 및 이들의 혼합물로 이루어진 군으로부터 선택되는, 광활성 섬유.
  15. 제1항 내지 제13항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 i) 에오신 Y; ii) 플루오레세인; iii) 에오신 Y 및 플루오레세인; 또는 iv) 에오신 Y 및 플루오레세인 및 로즈 벵갈인, 광활성 섬유.
  16. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 나일론이고 상기 적어도 하나의 광활성제는 에오신 Y인, 광활성 섬유.
  17. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 나일론이고 상기 적어도 하나의 광활성제는 에오신 Y 및 플루오레세인인, 광활성 섬유.
  18. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리에틸렌이고 상기 적어도 하나의 광활성제는 에오신 Y인, 광활성 섬유.
  19. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리에틸렌이고 상기 적어도 하나의 광활성제는 에오신 Y 및 플루오레세인인, 광활성 섬유.
  20. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리프로필렌이고 상기 적어도 하나의 광활성제는 에오신 Y인, 광활성 섬유.
  21. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리프로필렌이고 상기 적어도 하나의 광활성제는 에오신 Y 및 플루오레세인인, 광활성 섬유.
  22. 제1항 내지 제21항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 형광을 방출하는, 광활성 섬유.
  23. 제1항 내지 제22항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 약 400nm 내지 약 800nm 사이의 파장을 갖는 광을 방출하는, 광활성 섬유.
  24. 제1항 내지 제23항 중 어느 한 항에 있어서,
    상기 광활성 섬유는 400 데니어 내지 480 데니어 사이의 선형 질량 밀도를 가지는, 광활성 섬유.
  25. 제1항 내지 제23항 중 어느 한 항에 있어서,
    상기 광활성 섬유는 420 데니어 내지 450 데니어 사이의 선형 질량 밀도를 가지는, 광활성 섬유.
  26. 제1항 내지 제25항 중 어느 한 항에 있어서,
    윤활제를 더 포함하는, 광활성 섬유.
  27. 제26항에 있어서,
    상기 윤활제는 루롤 오일인, 광활성 섬유.
  28. 복수의 광활성 섬유들을 포함하는 광활성 직물로, 여기서 상기 광활성 섬유들은 i) 적어도 하나의 열가소성 중합체, 및 ii) 적어도 하나의 광활성제를 포함하고, 여기서 상기 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는, 광활성 직물.
  29. 제28항에 있어서,
    상기 광활성 섬유들의 적어도 하나의 광활성제는 상기 적어도 하나의 열가소성 중합체와 화합되는, 광활성 직물.
  30. 제29항에 있어서,
    상기 광활성 섬유들의 적어도 하나의 광활성제는 상기 광활성 섬유 전반에 균일하게 분산되어 있는, 광활성 직물.
  31. 제29항에 있어서,
    상기 광활성 섬유들의 적어도 하나의 광활성제는 상기 광활성 섬유 전반에 불균일하게 분산되어 있는, 광활성 직물.
  32. 제28항에 있어서,
    상기 적어도 하나의 광활성제는 상기 광활성 섬유의 적어도 일부의 표면 상에 적층되어 있는, 광활성 직물.
  33. 제28항 내지 제32항 중 어느 한 항에 있어서,
    상기 광활성 섬유는 400 데니어 내지 480 데니어 사이의 선형 질량 밀도를 가지는, 광활성 직물.
  34. a) 적어도 하나의 열가소성 중합체로 구성된 복수의 섬유; 및
    b) 적어도 하나의 광활성제를 포함하는 광활성 직물로, 여기서 상기 적어도 하나의 광활성제는 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는, 광활성 직물.
  35. 제34항에 있어서,
    상기 적어도 하나의 광활성제는 상기 복수의 광활성 섬유의 적어도 일부의 표면 상에 적층되어 있는, 광활성 직물.
  36. 제34항에 있어서,
    상기 적어도 하나의 광활성제는 상기 적어도 하나의 열가소성 중합체와 화합되는, 광활성 직물.
  37. 제34항에 있어서,
    상기 적어도 하나의 광활성제의 제1 부분은 상기 복수의 광활성 섬유의 적어도 일부의 표면 상에 적층되어 있고, 상기 적어도 하나의 광활성제의 제2 부분은 상기 적어도 하나의 열가소성 중합체와 화합되는, 광활성 직물.
  38. 제28항 내지 제37항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 아크릴, 아크릴로니트릴 부타디엔 스티렌 (ABS), 폴리벤즈이미다졸 (PBI), 폴리카보네이트, 폴리에테르 술폰 (PES), 폴리에테르에테르 케톤 (PEEK), 폴리에테르이미드 (PEI), 폴리에틸렌 (PE), 폴리페닐렌 옥사이드 (PPO), 폴리페닐렌 설파이드 (PPS), 폴리프로필렌 (PP), 폴리스티렌, 폴리 염화비닐 (PVC), 테플론, 폴리부틸렌, 폴리에틸렌 테레프탈레이트 (PET), 폴리부틸렌 테레프탈레이트 (PBT), 나일론, 폴리락트산 (PLA), 폴리메틸 메타크릴레이트 폴리에스테르, 폴리우레탄, 레이온, 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 광활성 직물.
  39. 제28항 내지 제37항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 나일론, 폴리에틸렌 (PE), 폴리프로필렌 (PP), 폴리락트산 (PLA), 폴리부틸렌 테레프탈레이트 (PBT), 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 광활성 직물.
  40. 제28항 내지 제37항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 에오신 Y, 에오신 B, 에리트로신, 플루오레세인, 로즈 벵갈 및 이들의 임의의 혼합물로 이루어진 군으로부터 선택되는, 광활성 직물.
  41. 제28항 내지 제40항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 형광을 방출하는, 광활성 직물.
  42. 제28항 내지 제41항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 약 400nm 내지 약 800nm 사이의 파장을 갖는 광을 방출하는, 광활성 직물.
  43. 제34항 내지 제42항 중 어느 한 항에 있어서,
    상기 섬유는 400 데니어 내지 480 데니어 사이의 선형 질량 밀도를 가지는, 광활성 직물.
  44. 제28항 내지 제43항 중 어느 한 항에 있어서,
    윤활제를 더 포함하는, 광활성 직물.
  45. 제44항에 있어서,
    상기 윤활제는 루롤 오일인, 광활성 직물.
  46. 제28항에 있어서,
    상기 윤활제는 상기 복수의 광활성 섬유의 적어도 일부분 상에 코팅되는, 광활성 직물.
  47. 제34항에 있어서,
    상기 윤활제는 상기 복수의 섬유의 적어도 일부분 상에 코팅되는, 광활성 직물.
  48. 제26항에 있어서,
    상기 복수의 광활성 섬유는 직조된 것인, 광활성 직물.
  49. 제28항에 있어서,
    상기 복수의 광활성 섬유는 스펀본드인, 광활성 직물.
  50. 제34항에 있어서,
    상기 복수의 섬유는 직조된 것인, 광활성 직물.
  51. 제34항에 있어서,
    상기 복수의 섬유는 스펀본드인, 광활성 직물.
  52. a) 적어도 하나의 열가소성 중합체로 구성된 복수의 섬유를 포함하는 광활성 직물; 및 b) 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는 적어도 하나의 광활성제를 포함하는 광활성 직물을 포함하는 제조 물품.
  53. 제52항에 있어서,
    상기 적어도 하나의 광활성제는 상기 복수의 광활성 섬유의 적어도 일부의 표면 상에 적층되어 있는, 제조 물품.
  54. 제52항에 있어서,
    상기 적어도 하나의 광활성제는 상기 적어도 하나의 열가소성 중합체와 화합되는, 제조 물품.
  55. 제52항에 있어서,
    상기 적어도 하나의 광활성제의 제1 부분은 상기 복수의 광활성 섬유의 적어도 일부의 표면 상에 적층되어 있고, 상기 적어도 하나의 광활성제의 제2 부분은 상기 적어도 하나의 열가소성 중합체와 화합되는, 제조 물품.
  56. 제52항 내지 제55항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 아크릴, 아크릴로니트릴 부타디엔 스티렌 (ABS), 폴리벤즈이미다졸 (PBI), 폴리카보네이트, 폴리에테르 술폰 (PES), 폴리에테르에테르 케톤 (PEEK), 폴리에테르이미드 (PEI), 폴리에틸렌 (PE), 폴리페닐렌 옥사이드 (PPO), 폴리페닐렌 설파이드 (PPS), 폴리프로필렌 (PP), 폴리스티렌, 폴리 염화비닐 (PVC), 테플론, 폴리부틸렌, 폴리에틸렌 테레프탈레이트 (PET), 폴리부틸렌 테레프탈레이트 (PBT), 나일론, 폴리락트산 (PLA), 폴리메틸 메타크릴레이트 폴리에스테르, 폴리우레탄, 레이온, 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 제조 물품.
  57. 제52항 내지 제55항 중 어느 한 항에 있어서,
    상기 적어도 하나의 열가소성 중합체는 폴리에틸렌 (PE), 폴리프로필렌 (PP), 폴리락트산 (PLA), 폴리부틸렌 테레프탈레이트 (PBT), 폴리(메틸 메타크릴레이트) (PMMA) 중 하나 이상인, 제조 물품.
  58. 제52항 내지 제57항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 에오신 Y, 에오신 B, 에리트로신, 플루오레세인, 로즈 벵갈 및 이들의 임의의 혼합물로 이루어진 군으로부터 선택되는, 제조 물품.
  59. 제52항 내지 제58항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 형광을 방출하는, 제조 물품.
  60. 제52항 내지 제59항 중 어느 한 항에 있어서,
    상기 적어도 하나의 광활성제는 활성 광에 반응하여 약 400nm 내지 약 800nm 사이의 파장을 갖는 광을 방출하는, 제조 물품.
  61. 제52항 내지 제60항 중 어느 한 항에 있어서,
    상기 섬유는 400 데니어 내지 480 데니어 사이의 선형 질량 밀도를 가지는, 제조 물품.
  62. 제52항 내지 제61항 중 어느 한 항에 있어서,
    상기 광활성 직물은 윤활제를 더 포함하는, 제조 물품.
  63. 제62항에 있어서,
    상기 윤활제는 루롤 오일인, 제조 물품.
  64. 제62항에 있어서,
    상기 윤활제는 상기 복수의 광활성 섬유의 적어도 일부분 상에 코팅되는, 제조 물품.
  65. 제62항에 있어서,
    상기 윤활제는 상기 복수의 섬유의 적어도 일부분 상에 코팅되는, 제조 물품.
  66. 제52항에 있어서,
    상기 광활성 섬유는 직조된 것인, 제조 물품.
  67. 제52항에 있어서,
    상기 복수의 광활성 섬유는 스펀본드인, 제조 물품.
  68. 제52항 내지 제67항 중 어느 한 항에 있어서,
    대상에 의해 착용될 의복인, 제조 물품.
  69. 제68항에 있어서,
    상기 대상은 광선치료를 필요로 하는, 제조 물품.
  70. 대상에 대해 광선치료를 실시하는 방법으로서, 상기 방법은
    - 제1항 내지 제27항 중 어느 한 항에 정의된 광활성 섬유를 상기 대상에게 적용하는 단계; 및
    - 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 상기 광활성 섬유를 조사하는 단계를 포함하는, 방법.
  71. 대상에 대해 광선치료를 실시하는 방법으로서, 상기 방법은
    - 제28항 내지 제51항 중 어느 한 항에 정의된 광활성 직물을 상기 대상에게 적용하는 단계; 및
    - 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 상기 광활성 직물을 조사하는 단계를 포함하는, 방법.
  72. 대상에 대해 광선치료를 실시하는 방법으로서, 상기 방법은
    - 제52항 내지 제69항 중 어느 한 항에 정의된 제조 물품을 상기 대상에게 적용하는 단계; 및
    - 광활성제의 흡수 스펙트럼과 중첩하는 파장을 가지는 광으로 상기 제조 물품을 조사하는 단계를 포함하는, 방법.
  73. 대상에게 광선치료를 실시하기 위해 사용되는, 제1항 내지 제27항 중 어느 한 항에 정의된 광활성 섬유의 용도.
  74. 대상에게 광선치료를 실시하기 위해 사용되는, 제28항 내지 제51항 중 어느 한 항에 정의된 광활성 직물의 용도.
  75. 대상에게 광선치료를 실시하기 위해 사용되는, 제52항 내지 제69항 중 어느 한 항에 정의된 제조 물품의 용도.
  76. - 제1 광활성 직물; 및
    - 제2 광활성 직물을 포함하는 제조 물품으로서,
    여기서 상기 제1 및 제2 광활성 직물은 서로 연결되어 있고 약 400nm 내지 약 800nm 사이의 광을 흡수하고 방출하는 적어도 하나의 광활성제를 포함하는, 제조 물품.
  77. 제76항에 있어서,
    상기 제1 광활성 직물은 폴리프로필렌으로 구성된 광활성 섬유를 포함하는, 제조 물품.
  78. 제76항에 있어서,
    상기 제1 광활성 직물 및 상기 제2 광활성 직물은 폴리프로필렌으로 구성된 광활성 섬유를 포함하는, 제조 물품.
  79. 제76항 내지 제78항 중 어느 한 항에 있어서,
    상기 제1 광활성 직물은 제1 광활성제를 포함하는, 제조 물품.
  80. 제76항 내지 제79항 중 어느 한 항에 있어서,
    상기 제2 광활성 직물은 제2 광활성제를 포함하는, 제조 물품.
  81. 제79항에 있어서,
    상기 제1 광활성제는 에오신 Y인, 제조 물품.
  82. 제80항에 있어서,
    상기 제2 광활성제는 에오신 Y 및 플루오레세인인, 제조 물품.
  83. 제76항 내지 제82항 중 어느 한 항에 있어서,
    상기 제1 광활성 직물 및 상기 제2 광활성 직물은 서로 연결되고, 꿰매지고, 접착되고, 부착되고, 융합되고, 바느질되거나, 또는 결합된, 제조 물품.
  84. 제76항에 있어서,
    상기 제1 광활성 직물 및/또는 상기 제2 광활성 직물과 연관된 적어도 하나의 추가적인 광활성 직물을 포함하되, 상기 적어도 하나의 추가적인 광활성 직물은 적어도 하나의 추가의 광활성제를 포함하는, 제조 물품.
KR1020177012621A 2014-10-31 2015-10-30 광활성 섬유 및 직물 매질 Ceased KR20170077153A (ko)